Understanding Refractory API 936 Reading VI

Understanding REFRACTORY For API936 Personnel Certification Examination Reading 6 My Pre-exam Self Study Notes 2nd October 2015

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

http://www.pointfourltd.com/documents/industrialphotog_new.html

Iron Treatment Station in Basic Oxygen Furnace

Iron Treatment Station in Basic Oxygen Furnace

Charlie Chong/ Fion Zhang

http://www.pointfourltd.com/documents/industrialphotog_new.html

BOF Tapping

Charlie Chong/ Fion Zhang

http://www.pointfourltd.com/documents/industrialphotog_new.html

BOF Tapping

Charlie Chong/ Fion Zhang

http://www.pointfourltd.com/documents/industrialphotog_new.html

BODY OF KNOWLEDGE FOR API936 REFRACTORY PERSONNEL CERTIFICATION EXAMINATION API certified 936 refractory personnel must have knowledge of installation, inspection, testing and repair of refractory linings. The API 936 Personnel Certification Examination is designed to identify applicants possessing the required knowledge. The examination consists of 75 multiple-choice questions; and runs for 4 hours; no reference information is permitted on the exam. The examination focuses on the content of API STD 936 and other referenced publications.

Charlie Chong/ Fion Zhang

REFERENCE PUBLICATIONS: A. API Publications:  API Standard 936; 3rd Edition, Nov 2008 - Refractory Installation Quality Control Guidelines - Inspection and Testing Monolithic Refractory Linings and Materials.

B. ACI (American Concrete Institute) Publications:  547R87 - State of the art report: Refractory Concrete  547.1R89 - State of the art report: Refractory plastic and Ramming Mixes

C. ASTM Publications:  C113-02 - Standard Test Method for Reheat Change of Refractory Brick  C133-97 - Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories  C181-09 - Standard Test Method for Workability Index of Fireclay and High Alumina Plastic Refractories  C704-01 - Standard Test Method for Abrasion Resistance of Refractory Materials at Room Temperatures

Charlie Chong/ Fion Zhang

闭门练功

Charlie Chong/ Fion Zhang

闭门练功

http://www.gentside.com/star-wars/wallpaper/page_2.html

Charlie Chong/ Fion Zhang

http://independent.academia.edu/CharlieChong1 http://www.yumpu.com/zh/browse/user/charliechong http://issuu.com/charlieccchong

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

http://greekhouseoffonts.com/

Charlie Chong/ Fion Zhang

The Magical Book of Refractory

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Fion Zhang at Shanghai 2nd October 2015

Charlie Chong/ Fion Zhang

Reading VI Content:  Reading 1 : Introduction to the Characteristics of Refractories and Refractory materials  Reading 2 : Refractory manufacturing Refractory testing and Refractory properties  Reading 3 : AP 42, Fifth Edition, Volume I Chapter 11: Mineral Products Industry Refractory Manufacturing  Reading 4 : The Fundamentals of Refractory Inspection with Infrared Thermography

Charlie Chong/ Fion Zhang

Reading 1: Introduction to the Characteristics of Refractories and Refractory materials

Charlie Chong/ Fion Zhang

http://ispatguru.com/introduction-to-the-characteristics-of-refractories-and-refractory-materials/

Reading 1: Introduction to the Characteristics of Refractories and Refractory materials A suitable selection of the refractory lining material for a furnace can only be made with an accurate knowledge of the chemical (mineralogical) and physical properties of the refractories and refractory materials, and of the stresses of the materials during service. There are four types of stresses which refractories face during their period of service. These are given below:  Thermal (effects) – The important properties for thermal stresses are pyrometric cone equivalent (PCE), refractoriness under load (RUL), Thermal expansion under load (creep), hot modulus of rupture, thermal expansion, reheat change (after-shrinkage and after-expansion) and thermal shock resistance.  Thermo-technical – The important properties for thermo-technical stresses are thermal conductivity, specific heat, bulk density, melting point, thermal capacity and temperature conductivity. (physical properties?)

Charlie Chong/ Fion Zhang

http://ispatguru.com/introduction-to-the-characteristics-of-refractories-and-refractory-materials/

 Mechanical – The important properties for mechanical stresses are cold modulus of rupture and deformation modulus, crushing strength, abrasion resistance, porosity and density. (physical properties and forms)  Chemical – The important properties for chemical stresses are chemical composition, mineralogical composition and crystal formation, pore size distribution and types of pores, gas permeability and resistance to slag, glass melts, gases and vapours.

Charlie Chong/ Fion Zhang

Some of the important physical and chemical properties are given below: 1. Melting point – Melting point (melting temperatures) specify the ability of materials to withstand high temperatures without chemical change and physical destruction. The melting points of major elements that constitute refractory composition in pure state vary from 1700 deg C to 3480 deg C. The melting point serves as a sufficient basis for considering the thermal stability of refractory mixtures and is an important characteristic indicating the maximum temperature of use. 2. Size and dimensional stability – The size and shape of the refractories is an important feature in design since it affects the stability of any structure. Dimensional accuracy and size is extremely important to enable proper fitting of the refractory shape and to minimize the thickness and joints in construction.

Charlie Chong/ Fion Zhang

3. Porosity – Porosity is a measure of the effective open pore space in the refractory and is expressed as the average percentage of open pore space in the overall refractory volume. The mechanical strength of a refractory material is largely determined by the true porosity which is composed of closed pores and open pores, the latter being either permeable or impermeable. For higher mechanical strength, low porosity of the refractory bricks is aimed. The important properties with respect to porosity is its behaviour during chemical attack by molten metal, slag, fluxes and vapour which can penetrate and thereby contribute to degradation of the refractory structure. High porosity materials tend to be highly insulating as a result of high volume of air they trap. The content of open pores of a brick is calculated from the water absorption. By using the water air displacement method, the open pores are classified either as permeable or effective or as impermeable pores.

Charlie Chong/ Fion Zhang

4. Bulk density – The bulk density (BD) is generally considered in conjunction with apparent porosity. It is a measure of the weight of a given volume including the pore space of the refractory. It is one of the important characteristic and provides a general indication of the product quality. An increase in bulk density increases the volume stability, the heat capacity, the resistance to abrasion and slag penetration. The bulk density is determined by means of a (1) hydrostatic scale, according to the (2) mercury displacement method or (3) by measurement.

Charlie Chong/ Fion Zhang

5. Cold crushing strength – It is a measure of the mechanical strength of the refractory brick. In furnaces, cold crushing strength (CCS) is of importance, because of bricks with high crushing strength is more resistant to impact from rods or during removal of slag than a brick with a low CCS. It is a useful indicator to the adequacy of firing and abrasion resistance in consonance with other properties such as bulk density and porosity. Comments: Typical CCS Values: Brick grade Silica Fire clay Corundum Magnesia Magnesia chromite Magnesia spinel Insulating Brick

Charlie Chong/ Fion Zhang

CCS (N /mm2) 15 -20 12 - 70 35 - 80 50 - 110 30 - 70 > 40 3 - 20

6. Pyrometric cone equivalent – It is the measurement of the refractoriness. Pyrometric cone eqquivalent (PCE) is the ability to withstand exposure to elevated temperature without undergoing appreciable deformation. Refractories due to their chemical complexity melt progressively over a range of temperature. This softening behaviour of the refractories is determined by PCE which consists of comparing ceramic specimen of known softening behaviour (seger or orton cones) with the cone of the refractory. Pyrometric cones are small triangular ceramic prisms that when set at a slight angle bend over in an arc so that the tip reaches the level of the base at a (1) particular temperature if heated (2) at a particular rate. The bending of the cones is caused by the formation of a viscous liquid within the cone body, so that the cone bends as a result of viscous flow.

Charlie Chong/ Fion Zhang

PCE is measured by making a cone of the refractory and firing it until it bends and comparing it with standard cone. PCE is useful for the quality control purpose to detect variations in batch chemistry that changes or errors in the raw material formulation. Refractoriness points to the resistance of the refractory to the extreme conditions of heat (> 1000 deg C) and corrosion when hot and molten materials are contained while being transported and/or processed. PCE cones before and after firing is shown at Fig. 1

Charlie Chong/ Fion Zhang

Fig 1 PCE cones before and after firing

Charlie Chong/ Fion Zhang

PCE cones after firing

Charlie Chong/ Fion Zhang

The Wiki: Pyrometric cones Equivalent Pyrometric cones are pyrometric devices that are used to gauge heatwork during the firing of ceramic materials. The cones, often used in sets of three as shown in the illustration, are positioned in a kiln with the wares to be fired and provide a visual indication of when the wares have reached a required state of maturity, a combination of time and temperature. Thus, pyrometric cones give a temperature equivalent; they are not simple temperaturemeasuring devices.

Definition The pyrometric cone is "A pyramid with a triangular base and of a defined shape and size; the "cone" is shaped from a carefully proportioned and uniformly mixed batch of ceramic materials so that when it is heated under stated conditions, it will bend due to softening, the tip of the cone becoming level with the base at a definitive temperature. Pyrometric cones are made in series, the temperature interval between the successive cones usually being 20 degrees Celsius. The best known series are Seger Cones (Germany), Orton Cones (USA) and Staffordshire Cones (UK).

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Self-supporting cones prior to firing (top) and after (bottom)

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Seger cones after use

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

History In 1782, Josiah Wedgwood created accurately scaled pyrometric beads, which led him to be elected a fellow of the Royal Society. The modern form of the pyrometric cone was developed by Hermann Seger and first used to control the firing of porcelain wares at the Königliche Porzellanmanufaktur (Royal Porcelain Works) in Berlin, in 1886. Seger cones are to this day made by a small number of companies and the term is often used as a synonym for pyrometric cones. The Standard Pyrometric Cone Company was founded in Columbus, Ohio, by Edward J. Orton, Jr. in 1896 to manufacture pyrometric cones, and following his death a charitable trust was established to operate the company, now known as the Edward Orton Jr. Ceramic Foundation (also known as the Orton Ceramic Foundation or simply "Orton") in suburban Westerville, Ohio.

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Glaze cones were made by evaporating water from a liquid glaze until the resulting mass reached the consistency of a plastic clay. The plastic mixture was then formed into cones that were dried and set in a soft pad of clay in a kiln. When observed through the viewing port of a kiln, the potter could see when a glaze cone had reached its melting point. The rings were removed from the kiln through special loopholes in the kiln walls using metal rods and examined for signs of melting in the glaze.

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Usage For some products, such as porcelain and lead-free glazes, it can be advantageous to fire within a two-cone range. The three-cone system can be used to determine temperature uniformity and to check the performance of an electronic controller. The three-cone system consists of three consecutively numbered cones: ■ Guide cone – one cone number cooler than firing cone. ■ Firing cone – the cone recommended by manufacturer of glaze, slip, etc. ■ Guard cone – one cone number hotter than firing cone. Additionally, most kilns have temperature differences from top to bottom. The amount of difference depends on the design of the kiln, the age of the heating elements, the load distribution in the kiln, and the cone number to which the kiln is fired. Usually, kilns have a greater temperature difference at cooler cone numbers. Cones should be used on the lower, middle and top shelves to determine how much difference exists during firing. This will aid in the way the kiln is loaded and fired to reduce the difference. Downdraft venting will also even out temperatures variance.

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Both temperature and time and sometimes atmosphere affect the final bending position of a cone. Temperature is the predominant variable. The temperature is referred to as an equivalent temperature, since actual firing conditions may vary somewhat from those in which the cones were originally standardized. Observation of cone bending is used to determine when a kiln has reached a desired state. Additionally, small cones or bars can be arranged to mechanically trigger kiln controls when the temperature rises enough for them to deform. Precise, consistent placement of large and small cones must be followed to ensure the proper temperature equivalent is being reached. Every effort needs to be made to always have the cone inclined at 8° from the vertical. Large cones must be mounted 2 inches above the plaque and small cones mounted 15/16 inches. With the cones having their own base, "self-supporting cones" eliminate errors with their mounting.

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Quoted: Additionally, small cones or bars can be arranged to mechanically trigger kiln controls when the temperature rises enough for them to deform.

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

Control of variability Pyrometric cones are sensitive measuring devices and it is important to users that they should remain consistent in the way that they react to heating. Cone manufacturers follow procedures to control variability (within batches and between batches) to ensure that cones of a given grade remain consistent in their properties over long periods. A number of national standards and an ISO standard have been published regarding pyrometric cones. Even though cones from different manufacturers can have relatively similar numbering systems, they are not identical in their characteristics. If a change is made from one manufacturer to another, then allowances for the differences can sometimes be necessary.

Charlie Chong/ Fion Zhang

https://en.wikipedia.org/wiki/Pyrometric_cone

7. Refractoriness under load – Refractoriness under load (RUL) evaluates the softening behaviour of fired refractory bricks at rising temperature and constant load conditions. RUL gives an indication of the temperature at which the brick will collapse in service condition with similar load. However, under actual service conditions the bricks are heated only on one face and most of the load is carried by the relatively cooler rigid portion of the refractory bricks. Hence, the RUL test gives only an index of refractory quality, rather than a figure which can be used in a refractory design. Under service conditions, where the refractory used is heating from all sides such as checkers, partition walls etc. the RUL test data is quite significant. For RUL, samples in cylindrical shape of 50 mm height and 50 mm diameter are heated at a constant rate under a load of 0.2 N/mm2 (0.2Mpa) and the change in height includes the thermal expansion and also the expansion of test equipment. The test results are taken from the recording. The initial temperature is taken at 0.6 % compression while the final temperature is taken at 20 % compression or when the specimen has collapsed. RUL curves of different refractories are at Fig 2

Charlie Chong/ Fion Zhang

Fig 2 – RUL curves of different refractories

50 x Ф50 mm

0.2 N/mm2

Charlie Chong/ Fion Zhang

RUL Testing Set-up

Charlie Chong/ Fion Zhang

RUL

Charlie Chong/ Fion Zhang

8. Thermal expansion under load (Creep) – Thermal expansion under load (Creep) is a time dependent property which determines the deformation in a given time and at a given temperature by a refractory under stress. Refractory material must maintain dimensional stability under extreme temperatures (including repeated thermal cycling) and constant corrosion from hot liquid and gases. In the creep test, specimen of 50 mm diameter and 50 mm height with an internal bore for the measuring rod is heated at constant rate and under a given load (generally at 0.2 N/mm2). After the required temperature is reached, the samples is held for 10 -50 hours. The compression of the specimen, after maximum expansion has been attained, is given in relation to the test time as a measure of creep at a specified test temperature. Creep curves of refractories are at Fig 3

Charlie Chong/ Fion Zhang

Fig 3 Creep curves of refractories

Charlie Chong/ Fion Zhang

Creep curves of refractories

Charlie Chong/ Fion Zhang

Softening under load

Charlie Chong/ Fion Zhang

9. Volume stability, expansion and shrinkage at high temperature Permanent change in the dimension of a refractory due to contraction and expansion during service can take place due to:  The changes in the allotropic forms which cause a change in specific gravity.  A chemical reaction which produces a new material of altered specific gravity.  The formation of a liquid phase  Sintering reactions  Due to fluxing by dust and slag or by the action of alkalis in case of fireclay refractories. After heating to high temperatures and subsequent cooling, a permanent change in dimensions often occurs. This can cause either loosening of bricks during service or the destruction of brickwork due to the pressure. Permanent linear change (PLC) on heating and cooling of the refractory bricks give an indication of volume stability of the brick as well as the adequacy of the processing parameters during manufacture. It is particularly significant as a measure of conversion achieved in the manufacture of silica refractories. Charlie Chong/ Fion Zhang

10. Reversible thermal expansion – Refractories like any other materials expands when heated and contracts when cooled. The reversible thermal expansion is a reflection on the phase transformation (?) that occurs during heating and cooling. The PLC and the reversible expansion are followed in the design of refractory lining for provision of expansion joints. As a rule, those with a lower thermal expansion co-efficient are less susceptible to spalling.

Charlie Chong/ Fion Zhang

Fig 4 Thermal expansion of different refractories

Charlie Chong/ Fion Zhang

11. Thermal conductivity – Thermal conductivity is defined as the quantity of heat that will flow through a unit area in direction normal to the surface area in a defined time with a known temperature gradient under steady state conditions. It indicates general heat flow characteristics of the refractory and depends upon the chemical and mineralogical composition as well as the application temperature. High thermal conductivity refractories are needed for some applications such as coke ovens, regenerators etc. On the other hand refractories with lower thermal conductivity are preferred in most application since they help in conserving heat energy. Porosity is an important factor in heat flow through refractories. The thermal conductivity of a refractory decreases on increasing its porosity. Although it is one of the least important properties as far as service performance is concerned, it evidently determines the thickness of the brickwork.

Charlie Chong/ Fion Zhang

12. Thermal shock resistance – It characterizes the behaviour of refractories to sudden temperature shocks. Temperature fluctuations can reduce the strength of the brick structure to a high degree and can lead to disintegrtaion or spalling in layers There are several methods of determining the thermal shock resistance each having its own advantages and disadvantages. 13. Specific heat – The specific heat is a material and temperature related energy factor and is determined with the help of calorimeters. The factor indicates the amount of energy (calories) needed to raise the temperature of one gram of material by 1 deg C. Compared to water, the specific heats of refractory materials are very low. These values are less than one fourth (¼) of value of specific heat of water.

Charlie Chong/ Fion Zhang

14. Abrasion resistance – The mechanical stress of refractory bricks is not caused by pressure alone, but also the abrasive attack of the solid raw materials as it slowly pass over the brickwork and by the impingement of the fast moving gases with fine dust particles. Therefore the cold crushing strength is not alone sufficient to characterize the wear of the refractories. There is no approved method for testing abrasion resistance but there are some methods available to give reference values such as Bohme grinding machine method and sand blast method etc. Note: ASTM C704-01 Standard Test Method for Abrasion Resistance of Refractory Materials at Room Temperature

Charlie Chong/ Fion Zhang

15. Modulus of Rupture or Modulus of deformation – During thermal stress, generally combined with altered physical-chemical conditions because of infiltration, strain conditions occur in refractory brickwork which can lead to brick rupture or crack formation. In order to determine the magnitude of rupture stress, the resistance to deformation under bending stress (rupture strength) is measured. Determination of the modulus of deformation in the cold state is carried out, together with modulus of rupture, on a test bar resting on two bearing edges. In general, a high ductility is looked for in refractory bricks,i.e. a large deformation region without rupture, which means a high value of the ratio of modulus of rupture to modulus of deformation. The modulus of rupture is defined as the maximum stress of a rectangular test piece of specific dimensions which can withstand maximum load until it breaks, expressed in N/mm2. For hot modulus of rupture (HMOR) load is applied at a high temperature. The international standard test method is described in ISO 5013 with test piece dimensions of 150 mm x 25 mm x 25 mm. Note: ASTM C133-97 Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories Charlie Chong/ Fion Zhang

16. Mineralogical composition and crystal formation – The behaviour of refractories of identical composition also depends on the type of raw materials used and on the reactions achieved during firing of the bricks. A glassy phase is more susceptible to attack by slag than a tightly interlocked crystal lattice structure. Two methods are used to identify mineralization composition. In the first method polarizing microscope or scanning electron microscope (SEM) is used. In the second method X-ray diffraction analysis is done.

Charlie Chong/ Fion Zhang

End of Reading 1. Charlie Chong/ Fion Zhang

Reading 2: Refractory manufacturing Refractory testing and Refractory properties

Charlie Chong/ Fion Zhang

http://ispatguru.com/introduction-to-the-characteristics-of-refractories-and-refractory-materials/

Refractory manufacturing Refractory testing and Refractory properties What is refractory ? Is it a material which should withstand high temperature only ? The right definition is that it should withstand high temperature,resistance to thermal and thermo chemical load, posses high volume stability, resistant to erosion and abrasion, be tough , and resistant to chemical corrosion etc. Or otherwise it should have high RUL, high PCE, low conductivity , high hot MOR, high creep resistance and optimum CCS etc. There is no refractory material which posses all the above properties 100 % Overall it is a compromise with all the above properties. Choice of refractories depend on the operating and mechanical conditions of the kiln.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

CCS testing machine

Charlie Chong/ Fion Zhang

Cold crushing equipment and CCS values Brick grade Silica Fire clay Corundum Magnesia Magnesia chromite Magnesia spinel Insulating Brick

Charlie Chong/ Fion Zhang

CCS ( N / mm2) 15 -20 12 - 70 35 - 80 50 - 110 30 - 70 > 40 3 - 20

PCE

Charlie Chong/ Fion Zhang

Creep test equipments

Charlie Chong/ Fion Zhang

Refractoriness under load RUL This is a measure of the resistance of a refractory body to the combined effects of heats of load.This test helps to study the behavior of a refractory product when subjected to a constant load under conditions of progressively rising temperature. The ground mass / matrix helps to bond the entire mass of a refractory brick strongly together. The amount and the strength of the glass is fixed by the alumina - silica ratio, fluxing oxide content and the temperature of firing. It is an important parameter to decide upon the safer limit of service temperature in a given situation. Contributing factors to the increased resistance to the pressure are: a) More thorough distribution of liquid throughout the brick b) The growth of crystals through the influence of heat c) Crystallization of a portion of the liquid during cooling.

Charlie Chong/ Fion Zhang

High temperature creep In a brick held at constant temperature and pressure, gradual solution of solid material up to the limits of its solubility in the liquid may cause some increase in the viscosity of the liquid. This increase is dependent on the nature of ground mass, glass content. Higher glass content will result higher deformation in this situation. This property of refractoriness is called high temperature creep. Lower deformation will ensure rigidity under the service condition. The creep is the measurement of deformation of a refractory product as a function of time when it is subjected to a constant load and heated at a specified temperature.

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Creep Curve

Charlie Chong/ Fion Zhang

Softening under load

Charlie Chong/ Fion Zhang

Linear expansion (Permanent linear change) High temperature reheat test may be used to reveal 1) if a brick has been fired long enough or at a high temperature 2) whether a brick has adequate refractoriness and volume stability It is expressed as a percentage , preferably by the ratio of the length of the test piece after heating and the original value of the length

Charlie Chong/ Fion Zhang

Equipments used to determine Thermal expansion

Charlie Chong/ Fion Zhang

Thermal expansion or refractory materials

Charlie Chong/ Fion Zhang

Equipments for thermal shock resistance test

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang

MOP- The resistance to bending stress of refractory products provide information on their deformation behavior at high temperature.

Charlie Chong/ Fion Zhang

HMOP

Charlie Chong/ Fion Zhang

Chemical composition By quantifying all the constituents present in refractory, it is possible to assess the chemical properties and melting behavior of a given refractory.As it is important to know the % Al2O3 in high alumina brick, % MgO in magnesite brick , and % SiO2 in silica brick etc.,the determination of minor constituents has also been recognized as controlling factors in the performance of many refractories. The chemical composition is of great importance with respect to attack by slag , glass melts , flue dusts and vapors. In general the principle applies that a brick is more resistant the lower the rate of chemical reaction gradient between the slag and brick is. Therefore, where the acid slag is expected , acid bricks are preferably used , and basic bricks where basic slag is expected.

Charlie Chong/ Fion Zhang

According to the behavior during contact reaction, the following groups of bricks can be differentiated.  Acid group - fused (99% SiO2), Silicon carbide bricks, Zircon crystobalite . Zircon silicate  Basic group - dolomite, magnesia, magnesia chrome, chrome magnesia ,forsterite  Inert or neutral - carbon , high alumina chromite group

Charlie Chong/ Fion Zhang

Cup corrosion test Alkali test of a high alumina brick with K2CO3

Charlie Chong/ Fion Zhang

Alkali test of a sic containing high alumina brick with K2CO3

Mineralogical investigations by X-ray diffraction Determination of the mineral phases composition of material X-ray diffraction diagram of a used magnesia –spinel brick grade, salt infiltrated.

Charlie Chong/ Fion Zhang

Microscopically techniques ( micrologies)  Light micoscopy ( transmitted light and reflected light microscopy  Microprobe analysis ( WDS, EDS)  Scanning electron microscopy Advantages of these micrlogies opposite other investigation methods  Diagnosis of mineral phases composition in raw materials , refractory products etc and their configuration ( textural/ structural criterions, pore shape and size etc

Charlie Chong/ Fion Zhang

Mineralogical investigations- Reflected light microscopy Pictures of magnesia - spinel brick grades with different raw material composition

Charlie Chong/ Fion Zhang

Mineralogical investigations- Reflected light microscopy Pictures of magnesia - spinel brick grades with different raw material composition

Charlie Chong/ Fion Zhang

Mineralogical investigations- Reflected light microscopy Pictures of magnesia - spinel brick grades with different raw material composition

Charlie Chong/ Fion Zhang

Microprobe Analysis- Chemical – mineralogical composition in mm Boundary between slag and corundum brick Polished section image (reflected light microscope)

Charlie Chong/ Fion Zhang

Back scattered electron image (microprobe)

Mineralogical investigations- Scanning electron microscopy (SEM) Hydration of Magnesia . crack formation ,caused by formation of brucite(Mg(OH)2

Charlie Chong/ Fion Zhang

Minerological investigations

Charlie Chong/ Fion Zhang

End of Reading 2. Charlie Chong/ Fion Zhang

Reading 3: AP 42, Fifth Edition, Volume I Chapter 11: Mineral Products IndustryRefractory Manufacturing

Charlie Chong/ Fion Zhang

http://www3.epa.gov/ttn/chief/ap42/ch11/

AP42.VI-11.5 Refractory Manufacturing 11.5.1 Process Description Refractories are materials that provide linings for high-temperature furnaces and other processing units. Refractories must be able to withstand physical wear, high temperatures (above 538°C [1000°F]), and corrosion by chemical agents. There are two general classifications of refractories, clay and nonclay. The six-digit source classification code (SCC) for refractory manufacturing is 3-05-005. Clay refractories are produced from fireclay (hydrous silicates of aluminum) and alumina (57 to 87.5 percent). Other clay minerals used in the production of refractories include kaolin, bentonite, ball clay, and common clay. Nonclay refractories are produced from a composition of alumina (180°F): Indicates high concern & warrants monitoring & corrective measures.

Charlie Chong/ Fion Zhang

This Delta-T repair criteria is very conservative and is only used as a guideline for plant engineers to determine what actions are warranted. Ultimately, the deciding factor as to exactly “How Hot is Too Hot” is unique for every type of equipment. It is recommended that accurate Absolute temperatures be documented in order to reference with the maximum allowable shell temperature for that particular piece of equipment. It is only from these Absolute temperatures that an effective course of action can be taken.

Charlie Chong/ Fion Zhang

Identification of Refractory Problems When inspecting refractory lined piping such as a transfer line, locating and identifying problems due to refractory failure is fairly simple as there are usually no internal structures within the piping that may confuse the thermographer.

Charlie Chong/ Fion Zhang

Refractory Problems on a Typical Transfer Line Piping

Charlie Chong/ Fion Zhang

However, when inspecting vessels such as steam reformers, boilers, heaters, etc., it is important to know what the internal make-up of each vessel is. Internal supports and structures such as brackets, beams, trays, tubes and bolts that are attached to the shell of the vessel may actually be thermally visible during the inspection. This is because of heat conduction. So, knowing what is inside a vessel can help you in your analysis and diagnosis of your inspection.

Charlie Chong/ Fion Zhang

Top of Convection Box Showing Effects of Heat Conduction from Internal Anchors

Charlie Chong/ Fion Zhang

There are also certain areas within every vessel that are prone to refractory failure. Vessels are mainly designed by their functional or operational characteristics. Although the design of a vessel does accommodate refractory installation, there is no costeffective way to design a vessel to be fully refractory failure-proof. Some areas on vessels that are prone to refractory failure are: · · · · · · ·

Welded joint sections Corners and seams Man-way sections Top 180° of piping Roofs Opening areas such as sight-ways and ports Burner areas

Charlie Chong/ Fion Zhang

Although these are the most common places where refractory failure occurs, it is not uncommon to have problems and failures on the vertical wall sections and bottom flooring. It is important to inspect every accessible part of a vessel and piping in order to perform an effective refractory inspection. That is why it is important to take your time and inspect in a systematic way, making sure everything is inspected because the area you missed will quite often be the area that fails. It’s good practice to first perform a walkthrough of the entire vessel or piping system before turning on your imager. By doing this before your survey you benefit from: · Knowing how and where to start the inspection and what route to take · Identifying potentially unsafe and hazardous conditions · Identifying visibly noticeable problems and flagging them for your IR inspection

Charlie Chong/ Fion Zhang

Conclusion With the highly competitive markets out there, it is important to keep your production costs down as well as try to prevent equipment failures. By using Infrared Thermography actively and frequently on refractory lined equipment, you are in a better position to “predict” problems, keep your equipment running during problem times and also properly schedule repairs and estimate the total materials needed for these repairs. The notions that refractory inspections should only be performed just before a scheduled plant turnaround in order to estimate repairs or be performed only when a visible problem is evident should be reviewed. Most refractory lined equipment is critical to your plant’s operation and should therefore be monitored on a regular basis.

Charlie Chong/ Fion Zhang

Point Lisas Industrial Estate Trinidad

Charlie Chong/ Fion Zhang

http://www.tdlir.com/

Point Lisas Industrial Estate Trinidad

Charlie Chong/ Fion Zhang

http://www.tdlir.com/

End of Reading 4. Charlie Chong/ Fion Zhang

Charlie Chong/ Fion Zhang