Laporan Praktikum Sifat Mekanik Material
July 7, 2019 | Author: Ardiyan Cakra | Category: N/A
Short Description
Hasil Praktikum Sifat Mekanik Material...
Description
Laporan Praktikum Sifat Mekanik Material
“
”
MODUL 2 LBM 4
1. Adam Reza Pahlevi 2. Adinda Nur Atiqah 3. Ainan Salsabila Rosyada 4. Anfasa Isnurhakim 5. Ardiyan Cakra Patrilia I 6. Farah Amara Digrayusa 7. Nabella Devyanna Putri Putri 8. Hasna Salsabiel 9. Regilia shinta Mayangsari 10. Suprayogi Yoga Prakasa
(31101700001) (31101700006) (31101700008) (31101700009) (31101700012) (31101700029) (31101700059) (31101700040) (31101700069) (31101700082)
FAKULTAS KEDOKTERAN GIGI UNIVERSITAS ISLAM SULTAN AGUNG SEMARANG 2017 LEMBAR PERSETUJUAN
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
LEMBAR PERSETUJUAN LAPORAN PRAKTIKUM
SIFAT FISIK DAN SIFAT MEKANIK BAHAN
Telah Disetujui oleh
Tutor
Drg. Fabia Astiawati, M.HKes
Semarang, Semarang, 2 Juni 2018
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
BAB I Dasar Teori Dasar Teori A. Sifat Fisik Fisik Dental Dental Material Sifat fisik adalah sifat yang didasarkan pada mekanika, akustik, optik, termodinamika, kelistrikan, magnet, radiasi, struktur atom, atau gejala nuklir.
Contoh sifat Fisik, yaitu : Berdasarkan Optik adalah yang berhubungan dengan fenomena cahaya, seperti : corak, translusensi (kebeningan), warna. Berdasarkan dalil termodinamika : konduktifitas termal, koefisien termal Berdasarkan ilmu materi dan mekanika : kekentalan
# Abrasi dan dan Ketahanan Abrasi Kekerasan adalah sifat yang digunakan untuk memperkirakan ketahanan aus suatu bahan dan kemampuannya untuk mengikis struktur gigi l awan. Kekerasan salah satu faktor penyebab pengikisan pada email gigi dan permukaan gigi tiruan. Faktor yang mempengaruhi keausan :
Tekanan gigitan. Frekuensi pengunyahan. Sifat abrasif makanan. Komposisi cairan. Perubahan temperatur. Kekerasan tiap permukaan. Ketidakteraturan permukaan gigi. Kekentalan / viskositas Ketahanan untuk bergerak Dipengaruhi oleh gaya friksi internal di dalam cair an Bahan kedokteran gigi kebanyakan dalam bentuk padat tapi tahap tertentu berupa cairan. Contoh : malam dan resin adalah cairan yang didinginkan di bawah titik normal. Kekentalan cairan meningkat dengan meningkatnya temperatur Kekentalan tergantung pada perubahan wujud sebelumnya dari cairan. Cairan jenis ini menjadi kurang kental dan lebih cair di bawah tekanan disebut
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Struktur dan Relaksasi Tekanan Perubahan bentuk senyawa secara permanen akan menyebabkan tekanan internal sehingga atom-atom dalam ruang geometrik akan berubah tempat. Akibatnya beberapa molekul menjadi terlalu berdekatan atau terlalu berjauhan. Atom-atom berada pada posisi tidak seimbang Energi thermal pada proses difusi wujud padat menyebabkan atom-atom kembali ke posisi seimbang. Perubahan kontur merupakan manifestasi pengaturan kembali posisi atom dan molekul. Pelepasan tekanan dikenal sebagai relaksasi. Kecepatan relaksasi dipercepat dengan meningkatnya temperatur. Creep dan Aliran Creep adalah deseran plastik yang bergantung waktu dari suatu bahan dibawah muatan statis atau tekanan konstan. Massa yang lebih tinggi mengalami tekanan fleksural yang lebih besar, fleksural creep lebih besar. Aliran logam terjadi begitu temperatur mendekati beberapa ratus derajat temperatur lebur. Warna dan Persepsi Warna Tujuan perawatan gigi adalah merestorasi warna dan penampilan gigi asli Dentistry estetika mementingkan kemampuan artistik dokter gigi dan teknisi Mata sensitif terhadap panjang gelombang 400 nm (ungu) sampai 700 nm (merah gelap). Diruang praktek dan laboratorium gigi, penyesuaian warnamenggunakan petunjuk warna.
Sifat termofisika, yaitu : 1. Konduktivitas termal Konduktivitas termal adalah pengukuran termofisika mengenai seberapa baik panas disalurkan melalui suatu bahan dengan dengan aliran konduksi. Bahan yang mempunyai konduktivitas tinggi ti nggi disebut konduktor. Bahan yang mempunyai konduktivitas rendah disebut isolator. Komposit berbasis resin mempunyai konduktivitas termal rendah dibanding logam. Konduktivitas email dan dentin yang rendah membantu mencegah syok termal dan sakit pulpa apabila makanan dingin atau panas masuk ke dalam mulut. 2. Difusi termal Difusi termal adalah pengendalian perubahan temperatur begitu panas melewati suatu bahan (kemampuan isolator). Oksida Seng-Eugenol mempunyai difusi termal dua kali dentin. 3. Koefesien ekspansi termal Koefisien ekspansi termal adalah perubahan panjang per unit panjang asal
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
direparasi, akan berkontraksi apabila diagkat dari gigi pada suasana panas dan kemudian disimpan pada suasana yang lebih dingin. B. Sifat Mekanik Dental Material Sifat mekanik adalah ilmu fisika yang berhubungan berhubungan dengan gaya dan energi serta perubahan pada benda yang disebabkan oleh gaya tersebut. Gaya dasar meliputi gaya tarik, gaya tekan dan gaya menggunting. Adapun sifat mekanik dari dental material, meliputi :
1. Gaya Tarik Gaya tarik (tensile) tensile) adalah dua gaya yang bekerja saling menjauhi satu sama lain pada satu garis lurus yang sama sehingga terjadi pemanjangan. 2. Gaya Tekan Gaya tekan (compressive (compressive)) adalah dua gaya bekerja mendekati satu sama lain pada satu garis lurus yang sama sehingga terja di pemendekan. 3. Gaya Menggunting Gaya menggunting ( shear ) adalah dua gaya yang bekerja sejajar satu s atu sama lain tetapi berlawanan arah 4. Tekanan (Stress) (Stress) Tekanan (Stress (Stress)) adalah daya dari dalam benda yang sama besarn ya tetapi berlawanan arah dengan gaya yang diberikan (gaya dari luar). Gaya per luas permukaan suatu benda. S = F /A F : gaya yang diberiakan (N) A : luas permukaan benda (m 2) Satuannya : 1 Pa = 1 N / m 2 = 1 MN / mm 2
Macam-macam Stress, yaitu : Tekanan Tarik (Tensile (Tensile Stress) Stress ) Tekanan tarik (Tensile (Tensile Stress) Stress ) adalah daya dari dalam benda yang sama besarnya tetapi berlawanan arah dengan ga ya tensile yang diberikan dari luar Tekanan Tekan (Compressive (Compressive Stress) Stress ) Tekanan tekan (Compressive (Compressive Stress) Stress ) adalah daya dari dalam benda yang sama besarnya tetapi berlawanan arah dengan gaya compressive yang diberikan dari luar. Tekanan Gunting (Shear (Shear Stress) Stress ) Tekanan gunting (Shear (Shear Stress) Stress ) adalah daya dari dalam yang sama besarnya tetapi berlawanan arah dengan gaya shear gaya shear yang yang diberiakan dari luar.
5. Ketegangan (Strain) Strain)
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Strain : € = ∆ | / | O ∆│ : Perubahan ukuran panjang │O : Panjang semula bahan
2.
Elongasi : Persentasi perubahan panjang Elongasi = Strain X 100% Elastis : Perubahan bentuk benda yang dapat kembali ke bentuk semula bila beban dilepaskan ( Reversible). Reversible). Plastis : Perubahan bentuk benda yang tidak dapat kembai ke bentuk semula walaupun beban dilepaskan ( Irreversible). Irreversible). Macam-macam Strain , yaitu : Tensile Strain (Tegangan tarik) Perubahan dimensi benda berupa pemanjangan (yang selalu diikuti dengan pengecilan diameter) disebabkan bekerjanya gaya tensile dari luar. Compressive Strain (Tegangan tekan) Perubahan dimensi benda berupa pemendekan (yang selalu diikuti dengan pembesaran diameter) disebabkan bekerjanya gaya compressive dari luar. Shear Strain (Tegangan gunting) Perubahan dimensi yang berupa sliding (tergelincirnya) (tergeli ncirnya) bidang pertama terhadap bidang kedua sesuai dengan arah gaya shear dari luar.
Modulus Elastisitas Modulus Elastisitas adalah ukuran keelatisan suatu bahan Stress =
Satuannya = Stress = Mpa atau Gpa 1 GPa = 1000 MPa
3.
Resilience Ketahanan suatu bahan terhadap perubahan bentuk secara permanen. Pengukurannya sama dengan dengan luas daerah elastis pada kurva stress dan strain. Dan satuannya adalah mMN/m 3
4.
Toughness Ketahanan suatu bahan terhadap patah. Daerah dibawah kurva stress dan
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Kemampuan sebuah benda untuk berubah bentuk tanpa patah dibawah gaya tekan. 6.
Ductility Kemampuan sebuah benda untuk berubah bentuk tanpa patah dibawah gaya tarik.
BAB II Tahapan Pekerjaan
A. Uji Tarik (Tesile Test) 1. Siapka klamer dengan beberapa macam diameter sepanjang kurang lebih 15 cm 2. Pasangkan kedua ujung klamer pada alat uji tensile. Putar tuas pada ala t uji hingga klamer kencang 3. Putar tuas alat uji hingga klamer tersebut terputus 4. Catat berapa putaran yang diperlukan hingga klamer tersebut putus 5. Catat pula tegangan yang dirasakan selama proses pengujian 6. Tiap diameter klamer dilakukan pengujian sebanyak 3 kali 7. Lakukan langkah 1-6 pada klamer dengan diameter yang berbeda 8. Bandingkan hasil percobaan pada tiap diameter klamer 9. Apabila memungkinkan, amati permukaan ujung klamer yang terputus dibawah mikroskop B. Uji Fleksural (Uji Bengkok) 1. Siapkan 2 buah penggaris dan alat uji flexural 2. Sisipkan penggaris pada alat uji, bagian tengah penggaris berada pada penunjuk o derajat alat uji 3. Bengkokkan penggaris tersebut secara perlahan dengan memperhatikan sudut
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
C. Fatigue Test 1. Kalmer ditahan dengan menggunakan tang 2. Bengkokkan klamer dengan sudut kurang lebih 30 derajat 3. Bengkokkan kembali sejauh 30 derajat kearah berlawanan 4. Lakukan tahapan nomor 2 dan 3 hingga klamer putus 5. Rasakan perubahan tekanan saat membengkokkan klamer 6. Ulangi lagi dengan menggunakan diameter yang sama sebanyak 3 kali percobaan 7. Lakukan tahapan tersebut menggunakan klamer diameter lain D. Hardness test (Uji Kekerasan Permukaan) 1. Siapkan spesimen yang akan diuji, bersihkan permukaannya 2. Uji kekerasan hanya dapat dilakukan pada permukaan yang datar 3. Nyalakan Durometer Shore D hardness tester dengan menekan tombol on 4. Letakkan Durometer Shore D hardness tester tegak lurus dengan spesimen yang akan diuji 5. Tekan secara perlahan hingga ujung dan angka pengukuran stabil. Tekan tombol hold 6. Catat hasil pengukura 7. Setelah selesai melakukan pengukuran, Durometer Shore D hardness tester dikembalikan ke angka nol dengan menekan tombol zero 8. Lakukan engukuran sebanyak 3 kali untuk tiap spesim en 9. Lakukan tahapan tersebut terhadap spesimen lain 10. Gores permukaan sampe menggunakan sonde dengan tekanan r ingan, bandingkan hasil goresan sonde pada semua spesimen, kaitkan dengan angka kekerasan
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
BAB III Hasil Pengamatan Uji Tensile
Diameter Klamer
0,3 mm
No Spesimen
Banyak Putaran
1
33
2
31
3
30
Rata Rata
32
Tegangan yang dirasakan
Cenderung lebih mudah patah karena lebih tipis
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Tebal
40o
Membengkok
50o
Membengkok
60o
Membengkok
70o
Sangat Membengkok
80o
Patah
Hasil pengamatan dengan mikroskop
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
3
0,5 mm
1
4
Putus
2
5
Putus
1
3
Putus
2
3.5
Putus
3
0,6 mm
3 Hasil Pengamatan Mikroskop
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Uji Kekerasan Spesimen
Blok Dental Plaster
Pengukuran Ke
Shore D Hardness Value
1
44
2
58
3
54
Rata – Rata Rata 52
1
50
Blok Dental
2
56
Stone
3
72
Goresan Sonde
Goresan cenderung lebih dalam karena kekerasan permukaan < dari Blok Dental Stone Goresan cenderung lebih dangkal karena kekerasan
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
BAB IV Pembahasan
Uji tensile
1. Percobaan klamer 0,33mm Percobaan 1 Percobaan 2 Percobaan 3
32 putaran 36 putaran 35 putaran
Pada uji tensile dengan diameter klamer 0,3 mm rata-rata putarannya adalah 34.39 putaran. Pada awal putaran tegangan yang dirasakan pada luas alat uji ringan kmudian semakin bertambahnya putaran makin berat dan akhirnya klamer terputus. Jadi tegangan makasimun yang dapat ditahan oleh klamer dengan diameter 0,3 mm rata-ratan ya 34,33 putaran. 2. Percobaan 0,4 mm Percobaan 1 Percobaan 2 Percobaan 3
34 putaran 38 putaran 36 putaran
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
0,6 mm
1 2 3
4 5 4
0,8 mm
1 2 3
3 3,5 3
Klamer denan diameter 0,4 mm membutuhkan rata rata 12 gerakan untuk membuat klamer terputus. Pada klamer dengan diameter 0,6 mm membutuhkan rata rata 4,33 gerakan untuk membuat klamer terputus. Pada klamer dengan diamter 0,8 mm membutuhkan rata rata 3,17 gerakan untuk membuat klamer terputus. Jadi semakin tebal diameter klamer maka ketika dibengkokkan sejauh 30° akan semakin muduh terputus
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
Trusted by over 1 million members
Try Scribd FREE for 30 days to access over 125 million titles without ads or interruptions! Start Free Trial Cancel Anytime.
2. Van Noort, Richard. 2007. Introduction to Dental Materials. London: Elsevier 3. Anusavice, K.J. 2003. Phillips Science of Dental Materials. 11th ed. W.B. Saunders Company. Philadelphia