MAT 1100 MCGB - DATA SHEET FOR SUPPLIERS
Old MAT Nos.: 110, 130, 100 Structural Steel, Carbon Steel, Killed
For more information contact FLSmidth
PROPERTIES: Carbon steel in hot rolled and normalised or similar condition: shape, plate, tube, bar and forging of structural quality in the killed condition.
STANDARDS: General requirements: When reference to this MAT NO appears on FLS Drawing or FLS Parts List or in FLS Purchase Order the data from the Primary Standard is used as acceptance criteria. Specific deviations in requirements made in the FLS Parts List, the FLS Purchase Order or a FLS Instruction always overrules this data sheet. Alternatively accepted International Standards listed in this sheet may be used if the suppliers documentation covers at least the documentation required in the Primary Listed Standard. This means that supplementary tests in some cases will be necessary. Primary Standard:
EN 10025 (1993), MATERIAL: S 235 JRG 2 FN, MATERIAL No.: 1.0038 Hot rolled products of non-alloyed structural steels - technical delivery conditions
CHEMICAL COMPOSITION: Dim. mm
% C max or range
% Si max or range
% Mn max or range
% P max or range
% S max or range
% N max or range
% Al min or range
0-16
0.17
-
1.4
0.045
0.045
0.009
-
16-40
0.17
-
1.4
0.045
0.045
0.009
-
40-
0.20
-
1.4
0.045
0.045
0.009
-
MECHANICAL PROPERTIES AT ROOM TEMPERATURE: Condition
Rev_No
Tensile Strength MPa
Yield Strength MPa
Elong. %
Rm
Re
A5
Z
Z
E
HRc
HB
HV
°C
J
0-3
360-510
235 -
21 -
-
-
206
-
-
-
20
27
3-16
340-470
235 -
26 -
-
-
206
-
-
-
20
27
16-40
340-470
225 -
26 -
-
-
206
-
-
-
20
27
40-63
340-470
215 -
25 -
-
-
206
-
-
-
20
27
63-100
340-470
215 -
24 -
-
-
206
-
-
-
20
27
100-150
340-470
195 -
22 -
-
-
206
-
-
-
20
27
150-200
320-470
185 -
21 -
-
-
206
-
-
-
20
23
200-250
320-470
175 -
21 -
-
-
206
-
-
-
20
23
Dim. mm
: 1,0
Issue Date: Revision Date:
Area Reduction
01-06-1998 08-06-2005
M.Elas GPa
Prepared by: Approved by:
Imp. Energy KV, Min
Hardness
AsK ESJ
Page 1 of 3
MAT 1100 MCGB - DATA SHEET FOR SUPPLIERS
Old MAT Nos.: 110, 130, 100 Structural Steel, Carbon Steel, Killed
For more information contact FLSmidth
ALTERNATIVE INTERNATIONAL STANDARDS TO MAT 1100 Standard ASTM A 1011/A 1011Ma (2004) ASTM A 283/A 283M (2003) ASTM A 36/A 36M (2004) ASTM A 576/A 576M (2000) ASTM A 668/A 668M (2004) EN 10025 (1993) ISO 630 (1995) JIS G 3101 (2004) JIS G 4051 (1979) ASTM: BS: DS:
Type of Material Sheet & Strip hot rolled Plates General Bars Forgings Plates & Bars Plates & Bars Plates & Bars Forgings & Hot rollings
American Society of Testing Materials British Standard Dansk Standard
DIN: EN: ISO: JIS:
Name of Material SS Grade36[250]type 1 Gr. B or C A36 Gr. 1015 - 1018 Cl. C S 235 JRG 2 FN Fe 630 B SS 400 S 15 C
Material No. . . . . . 1.0038 . . .
Deutsche Industrie-Norm European Norm International Organisation of Standardization Japanese Industrial Standard
DELIVERY CONDITIONS: The steel shall be delivered in the killed condition. Rimmed steel is not permitted. Products supplied according to the Primary Standard will be delivered at the manufacturer's discretion unless otherwise agreed upon.
Rev_No
: 1,0
Issue Date: Revision Date:
01-06-1998 08-06-2005
Prepared by: Approved by:
AsK ESJ
Page 2 of 3
MAT 1100 MCGB - DATA SHEET FOR SUPPLIERS
Old MAT Nos.: 110, 130, 100 Structural Steel, Carbon Steel, Killed
For more information contact FLSmidth
Revisions: Rev. No.
Rev. Date
Change
Responsible
0,70
31-01-2002
AnJo
0,80
12-03-2003
0,90 0,91 1,0
15-01-2004 31-01-2005 08-06-2005
Text editions Prepared & Approved changed References to Alternative Standards added to supplier version. Welding electrode number changed by adding 9000. Welding electrodes are transferred to Purchase Parts. Standards updated. Standards updated. ASTM A 668/ASTM A 668M material class changed to C Rev. no. changed to 1,0
Rev_No
: 1,0
Issue Date: Revision Date:
01-06-1998 08-06-2005
Prepared by: Approved by:
AsK ESJ
AsK AsK AsK AsK
Page 3 of 3
MAT 1105 MCGB - DATA SHEET FOR SUPPLIERS
Old MAT Nos.: -, -, Structural Steel, Carbon Steel, Killed
For more information contact FLSmidth
PROPERTIES: Carbon steel in hot rolled and normalised or similar condition: shape, plate, tube, bar and forging of structural quality in killed condition.
STANDARDS: General requirements: When reference to this MAT NO appears on FLS Drawing or FLS Parts List or in FLS Purchase Order the data from the Primary Standard is used as acceptance criteria. Specific deviations in requirements made in the FLS Parts List, the FLS Purchase Order or a FLS Instruction always overrules this data sheet. Alternatively accepted International Standards listed in this sheet may be used if the suppliers documentation covers at least the documentation required in the Primary Listed Standard. This means that supplementary tests in some cases will be necessary. Primary Standard:
EN 10025 (1993), MATERIAL: S 235 J2G3, MATERIAL No.: 1.0116 Hot rolled products of non-alloyed structural steels - technical delivery conditions
CHEMICAL COMPOSITION: % C max or range
Dim. mm
% Si max or range
% Mn max or range
% P max or range
% S max or range
0.03
0.03
0.17-0.25
% N max or range
% Al min or range
MECHANICAL PROPERTIES AT ROOM TEMPERATURE: Tensile Strength MPa
Yield Strength MPa
Elong. %
Rm
Re
A5
Z
Z
E
HRc
HB
HV
°C
J
360-510
235 -
21 -
-
-
206
-
-
-
-20
27
Annealed 16-40
340-470
225 -
26 -
-
-
206
-
-
-
-20
27
Annealed 40-63
340-470
215 -
25 -
-
-
206
-
-
-
-20
27
Annealed 63-100
340-470
215 -
24 -
-
-
206
-
-
-
-20
27
Annealed 100-150
340-470
195 -
22 -
-
-
206
-
-
-
-20
27
Annealed 150-200
320-470
185 -
21 -
-
-
206
-
-
-
-20
27
Annealed 200-250
320-470
175 -
21 -
-
-
206
-
-
-
-20
27
Condition
Annealed
Dim. mm
0-3
Area Reduction
M.Elas GPa
Imp. Energy KV, Min
Hardness
Structural steel tested for Impact Energy at -20° C. For materials supplied according to alternative ASTM standards the impact energy measured according to ASTM A 662/A 662 M (1997) shall be minimum 27 J at a testing temperature of -20° C.
Rev_No
:
1,0
Issue Date: Revision Date:
19-12-2003 08-06-2005
Prepared by: Approved by:
AsK ESJ
Page 1 of 3