CEB-FIP Model Code 2010-Draft-reinf

232

6 Interface characteristics

Explicit consideration of the influence of bond on performance at the serviceability limit state and on rotation capacity is not normally required for members reinforced with conventional plain or deformed steel bars. The influence is instead represented by a modification of the tension stiffening from surrounding concrete.

6

Interface characteristics

6.1

Bond of embedded steel reinforcement

Bond is the term used to denote the interaction and transfer of force  between reinforcement and concrete. Bond influences performance of concrete structures in several ways. At the serviceability limit state, bond influences width and spacing of transverse cracks, tension stiffening and curvature. At the ultimate limit state, bond is responsible for strength of end anchorages and lapped joints of reinforcement, and influences rotation capacity of plastic hinge regions.

6.1.1

Local bond-slip relationship

The bond stress-slip relationship depends on a considerable number of influencing factors like rib geometry (related rib area), concrete strength,  position and orientation of the bar during casting, state of stress, boundary conditions and concrete cover.

Under well-defined conditions, it is possible to consider that there is an average 'Local bond' versus 'Local slip' relationship, for short anchorage lengths, statistically acceptable.

Therefore the bond stress-slip curves for confined and unconfined concrete, presented in Figure 6.1-1, can be considered as statistical mean curves, applicable as an average formulation for a broad range of cases. Further reliability handling would be needed to derive design bond stress-slip curves.

For monotonic loading the bond stresses between concrete and reinforcing  bar for pull-out and splitting failure can be calculated as a function of the relative displacement s according to Eqs. (6.1-1) to (6.1-4) (see Figure 6.1-1).

The first curved part refers to the stage in which the ribs penetrate into the mortar matrix, characterized by local crushing and micro-cracking. The horizontal level occurs only for confined concrete, referring to advanced crushing and shearing off of the concrete between the ribs. This level represents a residual bond capacity, which is maintained by virtue of a large concrete cover or a minimum transverse reinforcement, keeping a certain degree of integrity intact. The decreasing branch refers to the reduction of  bond resistance due t o sheari ng o f the concrete co rbels between th e ribs . In case of unconfined concrete splitting failure occurs which is reflected by a sudden drop of the bond strength before the horizontal level is reached.

! 0 = ! max ( s/s 1)

!

! 0 = ! max   ! 0 = ! max !  f

(! max - !  f ) ( s - s2)/( s3- s2)

for

0 ! s ! s1 

(6.1-1)

for

 s1 ! s ! s2 

(6.1-2)

for

 s2 ! s ! s3 

(6.1-3)

for

 s3 < s 

(6.1-4)

With regard to the generation of bond stresses, the following considerations apply. Reinforcement and concrete have the same strain ( "  s = " c) in those areas of the structure where the steel is under compression and in uncracked parts of the structure under tension. In cracked cross-sections the tension forces in the crack are transferred by the reinforcing steel. In general, the absolute displacements of the steel u s and of the concrete uc  between two cracks or along the transmission length l t are different. Due to the relative displacement  s = u s-uc  bond stresses are generated  between th e concrete and the reinforcing steel. The magnitude of these bond stresses depends predominantly on the surface of the reinforcing steel, the slip s, the concrete strength f ck  and the position of the reinforcing steel during concreting. Between cracks or along the transmission length l t   a part of the tension force of the reinforcing steel, acting in the crack, is transferred into the concrete by bond (tension stiffening effect). The local decrease of the relative displacement along the transmission length l t,  is characterized by the strain difference: ds/dx = "  s - " c Depending on the selection of the coefficient # (0 ! #  ! 1) in Eq. (6.1-1) all usual forms of a bond stress-slip relationship can be modelled, starting from a bond characteristic with a constant stress ( #   = 0) up to a bond stressslip relationship with linear increasing bond stress ( #  = 1). The parameters given in Table 6.1-1 are valid for ribbed reinforcing steel with a related rib area  A sr  "  A sr,min  according to relevant international standards. Depending on the failure mode, pull-out or splitting, different  parameters are applied. In order to take other bond conditions into consideration a further distinction of the parameters is made.

 fib Bulletin 55: Mode l Code 201 0, First com plete dra ft – Volume 1

233

234

6 Interface characteristics

Table 6.1-1:

1

Parameters for defining the mean bond stress-slip relationship of deformed bars (acc. to Eqs. (6.1-1) to (6.1-4)) 2

3

4

6

Pull-Out (PO)

Splitting (SP)

"  s < "  s,y

"  s < "  s,y

Good bond cond.

All other bond cond.

Good bond cond.

2.5$ f ck 

1.25$f ck 

stirrups

All other bond cond.

stirrups

unconfined 0.25

0 .25

stirrups

#f 0. 25

&  f  ck  #  7.0 ' $ !  %  20 " 

&  f  ck  #  8.0 ' $ !  %  20 " 

&  f  ck  #  5.0 ' $ !  %  20 " 

&  f  ck  #  5.5 ' $ !  %  20 " 

1.0mm

1.8mm

 s(! max)

 s(! max)

 s(! max)

 s(! max)

s2

2.0mm

3.6mm

 s1

 s1

 s1

 s1

s3

cclear 

cclear 

1.2 s1

0.5cclear 

1.2 s1

0.5cclear 

0.4

0.4

0.4

0.4

0.4

0

0.4! max

0

0.4! max

0.4  f

1)

1)

0.40! max  0.40! max

Splitting

#u,split1

s1

1)

Pull-Out

unconfined

unconfined 0. 25

max 

5

#max #u,split 2

1)

Slip s s1

 Figure 6.1-1: 1)

cclear  is the clear distance between ribs

The values in Table 6.1-1, columns 1 and 2 (pull-out failure) are valid for well confined concrete (concrete cover #  5 Ø, clear spacing between bars # 10Ø). The values in Table 6.1-1, columns 3 to 6 (splitting failure) are valid for Ø " 20mm, cmax/cmin = 2.0, cmin = Ø and  K tr = 2% in case of sti rrups. For definition of K tr  see Eq. (6.1-5).

s2

s3

Analytical bond stress-slip relationship (monotonic loading)

0.1 0.25 0.33 0.2   f # 20 $  ) !%# cmin $  ) # c max $  + 8K "& 'u,split = (2 ) 6.54 ) #* ck $  ) +  tr +  * + * +   * &0 - 20 .  - , .  %/- , .  - cmin . 

  

(6.1-5)

where:

$2

= 1.0 for good bond conditions, = 0.7 for all other bond conditions

 f ck  is characteristic cylinder concrete compressive strength (N/mm%) Ø

is diameter of the bar (mm)

cmin = min{c x,cy,c si} cmax = max{cx, csi} and

 K tr  = nl Asv/(n b Ø sv) where: nl

is number of legs of confining reinforcement at a section

 Asv is cross sectional area of one leg of a confining bar [mm%] sv

= longitudin al spacing of confining reinforcement [mm]

n b

= number of anchored bars or pairs of lapped bars

Ø

is diameter of the anchored bar or of the smaller of a pair of lapped  bars [mm]

For those parts of the reinforcing bar which are at a distance  x ! 2 Ø from a transverse crack, the bond stress #  and the slip  s  are to be reduced by the factor %  where:

% = 0.5 x/ Ø ! 1

 fib Bulletin 55: Mode l Code 201 0, First com plete dra ft – Volume 1

(6.1-6)

235

236

6 Interface characteristics

The bond stress-slip curve is considerably influenced by reinforcement yielding and by transverse pressure. Taking into account these phenomena the bond stress according to Eqs. (6.1-1) to (6.1-4) should be modified by the factor & y in case of bar yielding and & p,tr  in case of lateral pressure: ! bm = ! 0 '

& y ' & p,tr  

(6.1-7)

where: ! bm

is bond stress according to the modified bond stress-slip curve

! 0

is bond stress according to the bond stress – slip curve defined by Eq. (6.1-1) to (6.1-4)

If yielding of reinforcement occurs along the embedment length, the corresponding reduction of the bond stress is given by the factor &y according to Eq. (6.1-8). !  y

=

# y

=

1.0   b

1.0 ! [0.85 " (1 ! e !5a )  

for "  s " "  sy 

(6.1-8a)

for "  sy < "  s " "  su 

(6.1-8b)

with 2

a

 Figure 6.1-2:

Influence of steel strains on local bond-stress slip relationship in case of pull-out failure

!  s

" ! 

!  su

" ! 

 sy

=

 sy

 ; b

=

&  f  t  # $2 ' !    f   y "! %$

(6.1-8c)

If transverse pressure is present the bond stress slip curve for pull-out failure should be modified by the factor & p,tr  according to Eq. (6.1-9).

" p,tr " p,tr

=

1, 0

=

1, 0 ) tanh , 0.2 * .

%

where

 Figure 6.1-3:

Influence of transverse pressure on local bond-stress  slip relationshi p in case of pull-out fail ure

The parameters given in Table 6.1-2 are valid for smooth reinforcing steel, depending on the main influencing factors: roughness of the bar surface, bond conditions and concrete strength. They are valid for confined and unconfined concrete. They are applicable only in loading states for which the concrete is not subjected to lateral tension, in the elastic range of the reinforcement and for those parts of the reinforcing bar with the distance x > 2Ø from a transverse crack. For those parts of the reinforcing bars with a distance x " 2Ø from a transverse crack, the bond stress !  and the slip s are to be reduced  by the factor $  according to Eq. (6.1-6)

2

"!

#c $ 0

(6.1-9a)

for

#c + 0

(6.1-9b)

is the mean compressive stress (orthogon al to the bar axis) averaged over a volume around the bar with a diameter of 3 Ø.  f c is the mean concrete compressive strength.

If there is any tension stress around the bar then &c=1,0.

!max

Unloading branch

!

=

(s/s 1)

!max

"

S !f 

s1

 Figure 6.1-4:

 fib Bulletin 55: Mode l Code 201 0, First com plete dra ft – Volume 1

' #! ( & / 0 0,1* f c 1 3

for

s2

s3 Slip, s

Unloading branch of t he ! -s relationship

237

238

6 Interface characteristics

Table 6.1-2:

Parameters for defining the bond stress-slip relationship of smooth bars (according to Eqs (6.1.-1) to (6.1.-4)) Cold drawn wire

 s1 = s2 = s3 # 

! max=#f 

Hot rolled bars

Good bond conditions

All other  bond con d.

Good bond conditions

0.01mm

0.01mm

0.1mm

0.1mm

0.5

0.5

0.5

0.5

0.1$ f ck  

0.05$ f ck 

0.3$ f ck  

0.15$ f ck 

The unloading branch of the bond stress-slip relationship is linear and valid for the increasing and horizontal part of the diagram. The slope S   (see Figure 6.1-4) is independent of the slip value  s, and has an average value of S = 200 N/mm &.

All other  bond con d.

The parameters given in Tables 6.1-1 and 6.1-2 are mean values. It has to be kept in mind that the scatter of different test series is considerable, especially for small values of slip. For a given value of the slip the coefficient of variation of the bond stresses may amount to approx. 30%. The scatter is due to the use of different test specimens and the resulting differences in the state of stress in the concrete surrounding the reinforcing  bar, to the different measuring techniques, and to the different loading and deformation velocities. The heterogeneity of the concrete and the geometry of the reinforcing bars (related rib area, diameters) also have a significant influence on the !  - s  relationship. The designer should take account of this scatter as far as possible, at least in the cases where a more accurate design is necessary.

6.1.2 Rules for serviceability behaviour have been derived for ribbed bars with a relative rib area f r  within the range 0.05-0.07. More highly ribbed bars may  be capable of developing higher bond stiffness, while coatings may cause a reduction. Coefficients '  representing the influence of bond in Eqs. (7.6-5) and (7.6-17) in clause 7.6 may be modified in proportion to measured bond stiffness. In the absence of test data, the ' coefficient for plain round and for epoxy coated ribbed bars should be taken as 50% of that for a ‘normal’ ribbed bar.

Influence on serviceability

The influence of bond on crack control and tension stiffening may be estimated from the secant modulus of local bond-slip behaviour measured in accordance with RILEM pullout test procedures at a free end slip of 0.01mm.