ASTM DS67D-16 Ed 5
Short Description
ASTM DS67D-16 Ed 5...
Description
Download From http://bbs.infoeach.com
Bringas
Handbook of
Comparative World Steel Standards
The book editor, John E. Bringas, P.Eng., is president and founder of Codes and Standards Training Institute (CASTI), headquartered in Edmonton, Alberta, Canada. A metallurgical and materials engineer, he is an engineering codes and standards information specialist with over 40 years of experience. He understands the needs of the users of this handbook because he is one himself. Mr. Bringas also authored the ASTM Handbook of Steel Data: American and European and is the principle developer of the ASTM Passport to Steel Online Database. Mr. Bringas has been teaching codes and standards related courses worldwide through CASTI (www.casti.ca) since 1989. Mr. Bringas has been a codes and standards committee member since 1982 and currently serves on:
ASTM INTERNATIONAL DS67D
Handbook of
Comparative World Steel Standards
ͽ ASTM Steels (Chair of Steel Terminology), Coated Steels, Nonferrous Alloys (Chair of Nonferrous Terminology), Metallography, Mechanical Testing; ͽ ISO TC17/SC4 Steels, Canadian delegate; and ͽ NACE Oil and Gas Corrosion and Metallurgy, Petroleum Refining and Gas Processing, Pipelines, Tanks, and Well Casings, and Process Industries—Materials. Mr. Bringas is also a long-time member of the American Welding Society (AWS), ASME International, and ASM International.
5th Edition John E. Bringas, Editor
5th Edition
www.astm.org ISBN 978-0-8031-7077-3 ASTM Stock #: DS67D
ASTM AFNOR
Download From http://bbs.infoeach.com
API
ASME
BSI
CSA
DIN
EN
GB
ISO
JIS
SAE
John E. Bringas, Editor
Handbook of Comparative World Steel Standards—5th Edition ASTM Stock No. DS67D
ASTM International 100 Barr Harbor Drive PO Box C700 West Conshohocken, PA 19428-2959 Printed in the U.S.A.
Library of Congress Cataloging-in-Publication Data Names: Bringas, John E., 1953Title: Handbook of comparative world steel standards / John E. Bringas, editor. Description: Fifth edition. | West Conshohocken, PA : ASTM International, [2016] | “ASTM Stock No.: DS67D.” | Includes bibliographical references and index. ,GHQWL¿HUV /&&1_,6%1 DONSDSHU Subjects: LCSH: Steel—Standards—Handbooks, manuals, etc. | Steel alloys—Standards—Handbooks, manuals, etc. &ODVVL¿FDWLRQ /&&7$+_''&²GF/&UHFRUGDYDLODEOHDWKWWS OFFQORFJRY Copyright © 2016 ASTM International, West Conshohocken, PA. All rights reserved. This material may not be reproduced or copied, in whole or in part, in any printed, PHFKDQLFDOHOHFWURQLF¿OPRURWKHUGLVWULEXWLRQDQGVWRUDJHPHGLDZLWKRXWWKHZULWWHQFRQVHQWRIWKHSXEOLVKHU Photocopy Rights $XWKRUL]DWLRQWRSKRWRFRS\LWHPVIRULQWHUQDOSHUVRQDORUHGXFDWLRQDOFODVVURRPXVHRUWKHLQWHUQDOSHUVRQDORUHGXFDWLRQFODVVURRPXVHRIVSHFL¿FFOLHQWVLVJUDQWHGE\WKH $PHULFDQ6RFLHW\IRU7HVWLQJDQG0DWHULDOV $670,QWHUQDWLRQDO SURYLGHGWKDWWKHDSSURSULDWHIHHLVSDLGWRWKH&RS\ULJKW&OHDUDQFH&HQWHU5RVHZRRG'ULYH'DQYHUV 0$ 7HO RQOLQH KWWS ZZZFRS\ULJKWFRP 0D\¿HOG3$ March, 2016
iii
Table of Contents
Preface
1
Acknowledgments
3
Getting Started with This Book
5
1.
Introduction to Comparing World Steel Standards
7
0\WKDQG0HWKRGRORJ\:KHQ&RPSDULQJ6WHHO6WDQGDUGV
&RPSDUDWLYHDQG&ORVHVW0DWFK
Organization Definitions of Steel Terms
2.
10 10
Cautionary Note
12
4XHVWLRQV5HJDUGLQJWKH5XOHVRI&RPSDULVRQ
Noncomparable Steels
12
Criteria for Comparing Steels
12
/LVWRI&RPSDULVRQ5XOHV
%ULHI,QWURGXFWLRQWR6WHHO6WDQGDUGVDQG'HVLJQDWLRQ6\VWHPV
$670'HVLJQDWLRQ6\VWHP
$6705HIHUHQFHG6WDQGDUGVDQG6XSSOHPHQWDU\5HTXLUHPHQWV
6$('HVLJQDWLRQ6\VWHPDQG5HODWHG$,6,'HVLJQDWLRQ6\VWHP
UNS Designation System
16
&DQDGLDQ6WDQGDUGV$VVRFLDWLRQ &6$
,QWURGXFWLRQWR(XURSHDQ (1 6WDQGDUG6WHHO'HVLJQDWLRQ6\VWHP
EN 10027 Standard Designation System for Steels
17
Steel Names
17
Numerical System
17
Former National Standards Superseded by CEN Standards
17
Indexes in this Handbook
17
Carbon and Alloy Steels for General Use
19
2.1 Chemical Composition of Carbon Steels for General Use
21
&KHPLFDO&RPSRVLWLRQRI+LJK0DQJDQHVH&DUERQ6WHHOVIRU*HQHUDO8VH
2.3 Chemical Composition of Alloy Steels for General Use
36
iv
Contents
&KURPLXP &U 6WHHOV
&KURPLXP0RO\EGHQXP &U0R 6WHHOV
&KURPLXP1LFNHO &U1L 6WHHOV
1LFNHO&KURPLXP0RO\EGHQXP 1L&U0R 6WHHOV
&KURPLXP0RO\EGHQXP$OXPLQXP &U0R$O 6WHHOV
%RURQ % 6WHHOV
&KURPLXP9DQDGLXP &U9 6WHHOV
6WUXFWXUDO6WHHO3ODWHV 3.1 Carbon Steels for Structural Steel Plates
51
3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates
51
3.1B Chemical Composition of Carbon Steels for Structural Steel Plates
66
$OOR\6WHHOVIRU6WUXFWXUDO6WHHO3ODWHV
$ 0HFKDQLFDO3URSHUWLHVRI+LJK6WUHQJWK/RZ$OOR\6WUXFWXUDO6WHHO3ODWHV
% &KHPLFDO&RPSRVLWLRQRI+LJK6WUHQJWK/RZ$OOR\6WUXFWXUDO6WHHO3ODWHV
$ 0HFKDQLFDO3URSHUWLHVRI$OOR\6WHHOVIRU6WUXFWXUDO6WHHO3ODWHV
3.2.2B Chemical Composition of Alloy Steels for Structural Steel Plates
92
6WUXFWXUDO6WHHOVZLWK,PSURYHG$WPRVSKHULF&RUURVLRQ5HVLVWDQFH
$ 0HFKDQLFDO3URSHUWLHVRI6WUXFWXUDO6WHHOVZLWK,PSURYHG$WPRVSKHULF&RUURVLRQ5HVLVWDQFH
% &KHPLFDO&RPSRVLWLRQRI6WUXFWXUDO6WHHOVZLWK,PSURYHG$WPRVSKHULF&RUURVLRQ5HVLVWDQFH
3UHVVXUH9HVVHO6WHHO3ODWHV &DUERQ6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ 0HFKDQLFDO3URSHUWLHVRI&DUERQ6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% &KHPLFDO&RPSRVLWLRQRI&DUERQ6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
&DUERQ6WHHOVIRU3UHVVXUH9HVVHO3ODWHV:LWK,PSDFW7HVWLQJ%HORZ&
$ 0HFKDQLFDO3URSHUWLHVRI&DUERQ6WHHOVIRU3UHVVXUH9HVVHO3ODWHV:LWK,PSDFW7HVWLQJ%HORZ& % &KHPLFDO&RPSRVLWLRQRI&DUERQ6WHHOVIRU3UHVVXUH9HVVHO3ODWHV:LWK,PSDFW7HVWLQJ%HORZ& ò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
&U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIô&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIô&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIó&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIó&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIó&U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
Download From http://bbs.infoeach.com
Contents
v
% 0HFKDQLFDO3URSHUWLHVRIó&U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI&U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI&U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI&Uò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI &U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI &U0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIò1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIò1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIò1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIò1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIó1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIó1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIò1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIò1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI 1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI 1L$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
1L0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIò1Lò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIò1Lò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRIô1Lò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRIô1Lò0R$OOR\6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
)HUULWLFDQG0DUWHQVLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI)HUULWLFDQG0DUWHQVLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI)HUULWLFDQG0DUWHQVLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
3UHVVXUH9HVVHO6WHHO3ODWHV &RQWLQXHG $XVWHQLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI$XVWHQLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI$XVWHQLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
$ &KHPLFDO&RPSRVLWLRQRI'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
% 0HFKDQLFDO3URSHUWLHVRI'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHOVIRU3UHVVXUH9HVVHO3ODWHV
6WHHO7XEHVDQG3LSHV &DUERQ6WHHO7XEHVIRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
vi
Contents
$ 0HFKDQLFDO3URSHUWLHVRI&DUERQ6WHHO7XEHVIRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications
213
$OOR\6WHHO7XEHVIRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
$ &KHPLFDO&RPSRVLWLRQRI$OOR\6WHHO7XEHVIRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
5.2B Mechanical Properties of Alloy Steel Tubes for General and Structural Applications
225
5.3 Stainless Steel Tubes for General and Structural Applications
227
5.3.1A Chemical Composition of Ferritic and Martensitic Stainless Steel Tubes for General and Structural Applications
227
5.3.1B Mechanical Properties of Ferritic and Martensitic Stainless Steel Tubes IRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
5.3.2A Chemical Composition of Austenitic Stainless Steel Tubes for General and Structural Applications
232
5.3.2B Mechanical Properties of Austenitic Stainless Steel Tubes for General and Structural Applications
235
5.3.3A Chemical Composition of Duplex Stainless Steel Tubes and Pipes IRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
5.3.3B Mechanical Properties of Duplex Stainless Steel Tubes and Pipes IRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
&DUERQ6WHHO7XEHVDQG3LSHVIRU/RZ7HPSHUDWXUH6HUYLFH
$ 0HFKDQLFDO3URSHUWLHVRI&DUERQ6WHHO7XEHVDQG3LSHV²:LWK,PSDFW7HVWLQJ%HORZ&
% &KHPLFDO&RPSRVLWLRQRI&DUERQ6WHHO7XEHVDQG3LSHV²:LWK,PSDFW7HVWLQJ%HORZ&
5.5 Alloy Steel Tubes and Pipes for Low-Temperature Service
251
5.5A Chemical Composition of Alloy Steel Tubes and Pipes for Low-Temperature Service
251
5.5B Mechanical Properties of Alloy Steel Tubes and Pipes for Low-Temperature Service
252
5.6 Carbon Steel Tubes and Pipes for Pressure Purposes
255
5.6A Mechanical Properties of Carbon Steel Tubes and Pipes for Pressure Purposes
255
% &KHPLFDO&RPSRVLWLRQRI&DUERQ6WHHO7XEHVDQG3LSHVIRU3UHVVXUH3XUSRVHV
5.7 Carbon Steel Tubes and Pipes for Pressure Purposes at High Temperatures
260
5.7A Mechanical Properties of Carbon Steel Tubes and Pipes for Pressure Purposes at High Temperatures
260
5.7B Chemical Composition of Carbon Steel Tubes and Pipes for Pressure 3XUSRVHVDW+LJK7HPSHUDWXUHV
$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
$ &KHPLFDO&RPSRVLWLRQRIó0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
267
% 0HFKDQLFDO3URSHUWLHVRIó0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
267
$ &KHPLFDO&RPSRVLWLRQRIò0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH 3XUSRVHVDW+LJK7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRIò0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
269
Download From http://bbs.infoeach.com
Contents
vii
$ &KHPLFDO&RPSRVLWLRQRIò&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
271
% 0HFKDQLFDO3URSHUWLHVRIò&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
272
$ &KHPLFDO&RPSRVLWLRQRIò&U0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
273
% 0HFKDQLFDO3URSHUWLHVRIò&U0R$OOR\6WHHO7XEHVDQG3LSHVIRU3UHVVXUH Purposes at High Temperatures
273
$ &KHPLFDO&RPSRVLWLRQRI&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU 3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRI&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU Pressure Purposes at High Temperatures
275
$ &KHPLFDO&RPSRVLWLRQRIó&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU Pressure Purposes at High Temperatures
276
% 0HFKDQLFDO3URSHUWLHVRIó&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU Pressure Purposes at High Temperatures
277
$ &KHPLFDO&RPSRVLWLRQRIó&U0R$OOR\6WHHO7XEHVDQG3LSHVIRU 3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRIó&U0R$OOR\6WHHO7XEHVDQG3LSHVIRU Pressure Purposes at High Temperatures
279
$ &KHPLFDO&RPSRVLWLRQRI&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU 3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRI&Uò0R$OOR\6WHHO7XEHVDQG3LSHVIRU 3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
$ &KHPLFDO&RPSRVLWLRQRI &U0R$OOR\6WHHO7XEHVDQG3LSHVIRU 3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRI &U0R$OOR\6WHHO7XEHVDQG3LSHVIRU 3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
6WDLQOHVV6WHHO7XEHVDQG3LSHVIRU3UHVVXUH3XUSRVHVDQG+LJK7HPSHUDWXUHV
5.9.1A Chemical Composition of Ferritic and Martensitic Stainless Steel Tubes and Pipes for Pressure Purposes and +LJK7HPSHUDWXUHV
5.9.1B Mechanical Properties of Ferritic and Martensitic Stainless Steel Tubes DQG3LSHVIRU3UHVVXUH3XUSRVHVDQG+LJK7HPSHUDWXUHV
5.9.2A Chemical Composition of Austenitic Stainless Steel Tubes and Pipes IRU3UHVVXUH3XUSRVHVDQG+LJK7HPSHUDWXUHV
5.9.2B Mechanical Properties of Austenitic Stainless Steel Tubes and Pipes for 3UHVVXUH3XUSRVHVDQG+LJK7HPSHUDWXUHV
5.10 Line Pipe Steels
316
$ 0HFKDQLFDO3URSHUWLHVRI/LQH3LSH6WHHOV:LWKRXW1RWFK7RXJKQHVV5HTXLUHPHQWV
% &KHPLFDO&RPSRVLWLRQRI/LQH3LSH6WHHOV:LWKRXW1RWFK7RXJKQHVV5HTXLUHPHQWV
$ 0HFKDQLFDO3URSHUWLHVRI/LQH3LSH6WHHOV:LWK1RWFK7RXJKQHVV5HTXLUHPHQWV
% &KHPLFDO&RPSRVLWLRQRI/LQH3LSH6WHHOV:LWK1RWFK7RXJKQHVV5HTXLUHPHQWV
6. Steel Forgings
329
Download From http://bbs.infoeach.com
viii
Contents
6.1 Carbon Steel Forgings
333
6.1.1A Mechanical Properties of Carbon Steel Forgings for General Use
333
6.1.1B Chemical Composition of Carbon Steel Forgings for General Use
339
6.1.2A Mechanical Properties of Carbon Steel Forgings for Piping, Pressure Vessel, and &RPSRQHQWV
6.1.2B Chemical Composition of Carbon Steel Forgings for Piping, Pressure 9HVVHODQG&RPSRQHQWV
$OOR\6WHHO)RUJLQJV
$ &KHPLFDO&RPSRVLWLRQRIó&Uó0R$OOR\6WHHO)RUJLQJVIRU*HQHUDO8VH
% 0HFKDQLFDO3URSHUWLHVRIó&Uó0R$OOR\6WHHO)RUJLQJVIRU*HQHUDO8VH
$OOR\6WHHO)RUJLQJVIRU3LSLQJ3UHVVXUH9HVVHODQG&RPSRQHQWV
6.2.2.1A Chemical Composition of Mo Alloy Steel Forgings for Piping, 3UHVVXUH9HVVHODQG&RPSRQHQWV
6.2.2.1B Mechanical Properties of Mo Alloy Steel Forgings for Piping, 3UHVVXUH9HVVHODQG&RPSRQHQWV
$ &KHPLFDO&RPSRVLWLRQRIò&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ 3UHVVXUH9HVVHODQG&RPSRQHQWV
% 0HFKDQLFDO3URSHUWLHVRIò&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ 3UHVVXUH9HVVHODQG&RPSRQHQWV
$ &KHPLFDO&RPSRVLWLRQRI&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
350
% 0HFKDQLFDO3URSHUWLHVRI&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
350
$ &KHPLFDO&RPSRVLWLRQRIó&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
351
% 0HFKDQLFDO3URSHUWLHVRIó&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
351
$ &KHPLFDO&RPSRVLWLRQRIó&U0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
352
% 0HFKDQLFDO3URSHUWLHVRIó&U0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
353
6.2.2.6A Chemical Composition of 3Cr-1Mo Alloy Steel Forgings for Piping, 3UHVVXUH9HVVHODQG&RPSRQHQWV
6.2.2.6B Mechanical Properties of 3Cr-1Mo Alloy Steel Forgings for Piping, 3UHVVXUH9HVVHODQG&RPSRQHQWV
$ &KHPLFDO&RPSRVLWLRQRI&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
355
% 0HFKDQLFDO3URSHUWLHVRI&Uò0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
356
$ &KHPLFDO&RPSRVLWLRQRI &U0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
356
% 0HFKDQLFDO3URSHUWLHVRI &U0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
356
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Contents
ix
$ &KHPLFDO&RPSRVLWLRQRI&Uò1L0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
357
% 0HFKDQLFDO3URSHUWLHVRI&Uò1L0R$OOR\6WHHO)RUJLQJVIRU3LSLQJ Pressure Vessel and Components
357
6.2.2.10A Chemical Composition of Ni Alloy Steel Forgings for Piping, Pressure Vessel and Components
357
6.2.2.10B Mechanical Properties of Ni Alloy Steel Forgings for Piping, 3UHVVXUH9HVVHODQG&RPSRQHQWV
6.2.2.11A Chemical Composition of Ni-Mn Alloy Steel Forgings for Piping, Pressure Vessel and Components
359
6.2.2.11B Mechanical Properties of Ni-Mn Alloy Steel Forgings for Piping, Pressure Vessel and Components
359
$ &KHPLFDO&RPSRVLWLRQRIô1Lò&U0R$OOR\6WHHO)RUJLQJVIRU Piping, Pressure Vessel and Components
361
% 0HFKDQLFDO3URSHUWLHVRIô1Lò&U0R$OOR\6WHHO)RUJLQJVIRU Piping, Pressure Vessel and Components
361
$ &KHPLFDO&RPSRVLWLRQRIô1Lò0R$OOR\6WHHO)RUJLQJVIRU Piping, Pressure Vessel and Components
362
% 0HFKDQLFDO3URSHUWLHVRIô1Lò0R$OOR\6WHHO)RUJLQJVIRU Piping, Pressure Vessel and Components
362
$ &KHPLFDO&RPSRVLWLRQRIó1Lô&Uò0R$OOR\6WHHO)RUJLQJVIRU Piping, Pressure Vessel and Components
363
% 0HFKDQLFDO3URSHUWLHVRIó1Lô&Uò0R$OOR\6WHHO)RUJLQJVIRU Piping, Pressure Vessel and Components
363
6WDLQOHVV6WHHO)RUJLQJV
$ &KHPLFDO&RPSRVLWLRQRI0DUWHQVLWLF6WDLQOHVV6WHHO)RUJLQJV
6.3.1B Mechanical Properties of Martensitic Stainless Steel Forgings
365
6.3.2A Chemical Composition of Ferritic Stainless Steel Forgings
366
6.3.2B Mechanical Properties of Ferritic Stainless Steel Forgings
366
6.3.3A Chemical Composition of Austenitic Stainless Steel Forgings
367
6.3.3B Mechanical Properties of Austenitic Stainless Steel Forgings
373
$ &KHPLFDO&RPSRVLWLRQRI3UHFLSLWDWLRQ+DUGHQLQJ6WDLQOHVV6WHHO)RUJLQJV
% 0HFKDQLFDO3URSHUWLHVRI3UHFLSLWDWLRQ+DUGHQLQJ6WDLQOHVV6WHHO)RUJLQJV
$ &KHPLFDO&RPSRVLWLRQRI'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHO)RUJLQJV
% 0HFKDQLFDO3URSHUWLHVRI'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHO)RUJLQJV
6WHHO&DVWLQJV &DVW&DUERQ6WHHOV
$ 0HFKDQLFDO3URSHUWLHVRI&DVW&DUERQ6WHHOIRU*HQHUDODQG6WUXFWXUDO$SSOLFDWLRQV
7.1.1B Chemical Composition of Cast Carbon Steel for General and Structural Applications
392
7.1.2A Mechanical Properties of Cast Carbon Steel for Pressure Purposes at High Temperatures
396
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
x
Contents
7.1.2B Chemical Composition of Cast Carbon Steel for Pressure Purposes at High Temperatures
397
$ 0HFKDQLFDO3URSHUWLHVRI&DVW&DUERQ6WHHOIRU3UHVVXUH3XUSRVHVDW/RZ7HPSHUDWXUHV
7.1.3B Chemical Composition of Cast Carbon Steel for Pressure Purposes at Low Temperatures
399
&DVW0DQJDQHVH6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI&DVW0DQJDQHVH6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI&DVW0DQJDQHVH6WHHOV
&DVW$OOR\6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI&DVW$OOR\6WHHOVIRU*HQHUDODQG6WUXFWXUDO3XUSRVHV
% 0HFKDQLFDO3URSHUWLHVRI&DVW$OOR\6WHHOVIRU*HQHUDODQG6WUXFWXUDO3XUSRVHV
$ &KHPLFDO&RPSRVLWLRQRI&DVW$OOR\6WHHOVIRU3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRI&DVW$OOR\6WHHOVIRU3UHVVXUH3XUSRVHVDW+LJK7HPSHUDWXUHV
$ &KHPLFDO&RPSRVLWLRQRI&DVW$OOR\6WHHOVIRU3UHVVXUH3XUSRVHVDW/RZ7HPSHUDWXUHV
% 0HFKDQLFDO3URSHUWLHVRI&DVW$OOR\6WHHOVIRU3UHVVXUH3XUSRVHVDW/RZ7HPSHUDWXUHV
&DVW6WDLQOHVV6WHHOV &DVW6WDLQOHVV6WHHOVIRU*HQHUDODQG&RUURVLRQ5HVLVWDQW$SSOLFDWLRQV
$ &KHPLFDO&RPSRVLWLRQRI0DUWHQVLWLFDQG)HUULWLF6WDLQOHVV6WHHOVIRU *HQHUDODQG&RUURVLRQ5HVLVWDQW$SSOLFDWLRQV
% 0HFKDQLFDO3URSHUWLHVRI0DUWHQVLWLFDQG)HUULWLF6WDLQOHVV6WHHOVIRU *HQHUDODQG&RUURVLRQ5HVLVWDQW$SSOLFDWLRQV
$ &KHPLFDO&RPSRVLWLRQRI$XVWHQLWLF6WDLQOHVV6WHHOVIRU*HQHUDODQG &RUURVLRQ5HVLVWDQW$SSOLFDWLRQV
% 0HFKDQLFDO3URSHUWLHVRI$XVWHQLWLF6WDLQOHVV6WHHOVIRU*HQHUDODQG &RUURVLRQ5HVLVWDQW$SSOLFDWLRQV
&DVW6WDLQOHVV6WHHOVIRU3UHVVXUH3XUSRVHV
$ &KHPLFDO&RPSRVLWLRQRI0DUWHQVLWLFDQG)HUULWLF6WDLQOHVV6WHHOV IRU3UHVVXUH3XUSRVHV
% 0HFKDQLFDO3URSHUWLHVRI0DUWHQVLWLFDQG)HUULWLF6WDLQOHVV6WHHOVIRU 3UHVVXUH3XUSRVHV
$ &KHPLFDO&RPSRVLWLRQRI$XVWHQLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH3XUSRVHV
% 0HFKDQLFDO3URSHUWLHVRI$XVWHQLWLF6WDLQOHVV6WHHOVIRU3UHVVXUH3XUSRVHV
&DVW+HDW5HVLVWDQW6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI&DVW+HDW5HVLVWDQW6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI&DVW+HDW5HVLVWDQW6WHHOV
:URXJKW6WDLQOHVV6WHHOV 6WDLQOHVV6WHHOV 3ODWH6KHHWDQG6WULS
$ &KHPLFDO&RPSRVLWLRQRI0DUWHQVLWLF6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI0DUWHQVLWLF6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI)HUULWLF6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI)HUULWLF6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI$XVWHQLWLF6WDLQOHVV6WHHOV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Contents
% 0HFKDQLFDO3URSHUWLHVRI$XVWHQLWLF6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI3UHFLSLWDWLRQ+DUGHQLQJ6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI3UHFLSLWDWLRQ+DUGHQLQJ6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI'XSOH[ )HUULWLF$XVWHQLWLF 6WDLQOHVV6WHHOV
6WDLQOHVV6WHHOV %DU
9.
xi
$ &KHPLFDO&RPSRVLWLRQRI0DUWHQVLWLF6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI0DUWHQVLWLF6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI)HUULWLF6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI)HUULWLF6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI$XVWHQLWLF6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI$XVWHQLWLF6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI3UHFLSLWDWLRQ+DUGHQLQJ6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI3UHFLSLWDWLRQ+DUGHQLQJ6WDLQOHVV6WHHOV
$ &KHPLFDO&RPSRVLWLRQRI'XSOH[6WDLQOHVV6WHHOV
% 0HFKDQLFDO3URSHUWLHVRI'XSOH[6WDLQOHVV6WHHOV
Steels for Special Use
607
9.1 Free-Machining Steels
611
9.1.1 &KHPLFDO&RPSRVLWLRQRI5HVXOIXUL]HG&DUERQ6WHHOVIRU)UHH0DFKLQLQJ$SSOLFDWLRQV
&KHPLFDO&RPSRVLWLRQRI5HSKRVSKRUL]HGDQG5HVXOIXUL]HG&DUERQ6WHHOV for Free-Machining Applications
613
&KHPLFDO&RPSRVLWLRQRI5HVXOIXUL]HGDQG/HDGHG&DUERQ6WHHOVIRU )UHH0DFKLQLQJ$SSOLFDWLRQV
&KHPLFDO&RPSRVLWLRQRI5HSKRVSKRUL]HG5HVXOIXUL]HGDQG/HDGHG &DUERQ6WHHOVIRU)UHH0DFKLQLQJ$SSOLFDWLRQV
9.1.5 Chemical Composition of Free-Machining Stainless Steels
615
9.2 Spring Steels &KHPLFDO&RPSRVLWLRQRI&ROG5ROOHG&DUERQ6SULQJ6WHHOV
615
&KHPLFDO&RPSRVLWLRQRI&ROG5ROOHG&DUERQ:LUH6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI&ROG5ROOHG&DUERQ6WULS6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG$OOR\6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG6L$OOR\6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG&U$OOR\6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG&U6L$OOR\6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG&U0R$OOR\6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG&U9$OOR\6SULQJ6WHHOV
&KHPLFDO&RPSRVLWLRQRI+RW5ROOHG&U%$OOR\6SULQJ6WHHOV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
xii
Contents
9.2.3 Chemical Composition of Stainless Spring Steels 9.3 Tool Steels
621 622
9.3.1 Chemical Composition of Carbon Tool Steels
622
9.3.2 Chemical Composition of High-Speed Tool Steels
623
9.3.2.1 Chemical Composition of Tungsten Type High Speed Tool Steels
623
&KHPLFDO&RPSRVLWLRQRI0RO\EGHQXP7\SH+LJK6SHHG7RRO6WHHOV
9.3.3 Chemical Composition of Cold Work Tool Steels
625
&KHPLFDO&RPSRVLWLRQRI+RW:RUN7RRO6WHHOV
9.3.5 Chemical Composition of Special Purpose Tool Steels
627
%HDULQJ6WHHOV &KHPLFDO&RPSRVLWLRQRI%HDULQJ6WHHOV
Appendix 1 ASTM Ferrous Metal Standards
629
$SSHQGL['LVFRQWLQXHG)HUURXV0HWDO6WDQGDUGV
$SSHQGL[-,66WHHODQG5HODWHG6WDQGDUGV
$SSHQGL[(1&XUUHQW6WHHO6WDQGDUGV
Appendix 5 EN ISO Current Steel Standards
677
Appendix 6 ISO Iron and Steel Product Standards
679
$SSHQGL[$670$ ±6WDQGDUG7HUPLQRORJ\5HODWLQJWR6WHHO6WDLQOHVV6WHHO 5HODWHG$OOR\VDQG)HUURDOOR\V
$SSHQGL[$670(±6WDQGDUG3UDFWLFHIRU1XPEHULQJ0HWDOVDQG$OOR\VLQWKH8QLILHG 1XPEHULQJ6\VWHP 816
$SSHQGL[ 6,4XLFN5HIHUHQFH*XLGH
Steel Grade/Name Index
711
UNS Number Index
773
6WHHO1XPEHU,QGH[
6SHFLILFDWLRQ'HVLJQDWLRQ,QGH[
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Preface
This is the book I never wanted to write but always wanted to own. As a metallurgical engineer and longtime user of steel standards, author of the four CASTI Metals Data Books, and as a member of ASTM, ISO, and SAE steel standard committees, I knew all too well the many pitfalls and challenges of writing such a handbook. There were many steel standards from around the world that were new to me and that created many surprises, including the Chinese GB steel standards, which were translated into English by the metallurgical engineers of CASTI Publishing, Inc. Comparing steel standards is not an exact science, so the biggest challenge in preparing such a book was deciding on the “rules of comparison.” Of the similar books on the market today, none explain in detail why one steel is comparable to another. They simply appear together in a list of steels. I kept a daily diary to help construct a workable set of comparison rules that I could share with other users to assist them in understanding how and why one steel is comparable to another. :KHQZULWLQJWKH¿UVWHGLWLRQRIWKLVERRN '6$ WKHVHUXOHVFKDQJHGIURPFKDSWHUWRFKDSWHU while the book was being written. It was not until the last chapter and the appendix were completed that I ZDVDEOHWR¿QDOL]HWKHUXOHVRIFRPSDULVRQ,QWKHHQGDFRPSOHWHUHYLHZRIWKHERRNZDVSHUIRUPHG UHVXOWLQJLQWKHUHRUJDQL]DWLRQRIVRPHFKDSWHUVDQGWKH¿QHWXQLQJRIRWKHUV7KHUHZHUHWRRPDQ\RFFDVLRQVZKHQ,WKRXJKWWKHERRNZDV¿QLVKHGRQO\WRKDYHWRFKDQJHDGGRUGHOHWHDUXOHWKDWPDGH\HW another review of the book necessary. 0\ZULWLQJRIWKLV¿IWKHGLWLRQ '6' ZDVJUHDWO\DVVLVWHGE\XVLQJWKH$6703DVVSRUWWR6WHHO database. Without it, the handbook would be much smaller. The addition of data from Chinese GB and $60(VWHHOVWDQGDUGVKDVVLJQL¿FDQWO\LPSURYHGWKLVHGLWLRQ:LWKWKHXVHRIWKH$6703DVVSRUWWR6WHHO database, many new comparable steels were also added to this edition. I hope you enjoy using this handbook as much as I have. Tie a chain to it and anchor it to your desk because once others see it, you may never see the book again. I am interested in your comments and suggestions for improving this handbook and encourage you to send your feedback directly to ASTM.
John E. Bringas, P.Eng. President and Metallurgical Engineer CASTI Publishing, Inc.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Acknowledgments
The author gratefully acknowledges the assistance of Michael Ling, P.Eng., and Toan Huynh, P.Eng., whose work in compiling and organizing the data was of particular importance. A special acknowledgment is made to Yin Huang, Ph.D., who was the lead metallurgical engineering translator of the Chinese GB steel standards. Without his dedicated work, the GB data included here would not have maintained the KLJKTXDOLW\VWDQGDUGIRUZKLFKWKLVKDQGERRNLVNQRZQZRUOGZLGH7KHDGYLFHJLYHQE\WKHVHLQGLYLGXDOV ZKHQGLI¿FXOWWHFKQLFDOGHFLVLRQVKDGWREHPDGHLVDSSUHFLDWHG 6HYHUDOFROOHDJXHVIURP$6706RFLHW\RI$XWRPRWLYH(QJLQHHUV 6$( DQG,QWHUQDWLRQDO6WDQGDUGV 2UJDQL]DWLRQ ,62 FRPPLWWHHV ZHUH FRQWDFWHG IRU WKHLU LQSXW GXULQJ WKH SURJUHVV RI WKLV KDQGERRN LQFOXGLQJ $670 FRPPLWWHH PHPEHUV 5DOSK 'DYLVRQ )UDQN &KULVWHQVHQ DQG -RKQ 0DKDQH\ *QWHU Briefs and Baoshi Liu from the ISO; and Mel Head of the SAE. They added valuable insights into the history and technical aspects of the standards data found in this handbook. The ASTM publishing staff, most notably John Pace, David Von Glahn, Kathy Dernoga, and 0RQLFD6LSHUNRZHUHYHU\VXSSRUWLYHRIP\UHTXHVWVWRREWDLQDFFHVVWRWKHKXQGUHGVRIVWDQGDUGVQHHGHG WRZULWHWKLVKDQGERRN7KHLUSDWLHQFHDQGFRQ¿GHQFHLQP\DELOLW\WRFRPSOHWHWKHZRUNLVDSSUHFLDWHG Thank you all. The author also acknowledges the dedicated assistance of the Codes and Standards Training Institute &$67, VWDII ZKR DVVLVWHG LQ WKH UHVHDUFK HQWHUHG GDWD DQG ZKR XSGDWHG WKH ERRN ZLWK FDUH DQG diligence. $VSHFLDOWKDQNVLVH[WHQGHGWR,QIRUPDWLRQ+DQGOLQJ6HUYLFH ,+6 (QJLQHHULQJ3URGXFWVIRUSHUPLWWLQJWKHXVHRIWKHLU(QJLQHHULQJ5HVRXUFH&HQWHU (5& One person could not have produced this handbook. It took a dedicated team of professionals. These DFNQRZOHGJPHQWVFDQQRWDGHTXDWHO\H[SUHVVWKHDXWKRU¶VVLQFHUHDSSUHFLDWLRQDQGJUDWLWXGHIRUHYHU\RQH¶V assistance. Without it, this handbook would never have been completed.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Getting Started With This Book
The intent of this handbook is to allow the user to identify comparable steels that are found in standards from around the world and then to evaluate each complete standard on its own merit to ensure that the selected steel is suited for the intended application. This handbook is not designed to be the sole source of information for selecting a comparative steel and is not intended to be used as a replacement for steel standards. This handbook is one tool in the process of comparing steel standards from around the world. Comparing steel standards is not an exact science, and there is no foolproof method. When you begin WRXVHWKLVKDQGERRN\RXZLOOTXLFNO\GLVFRYHUWKDWWKHUHLVQRVXFKWKLQJDV³HTXLYDOHQW´VWHHOVWDQGDUGV The user must also be aware that not all steels have comparative counterparts. Before proceeding directly to the contents of this handbook, it is strongly recommended that you read Chapter 1, which includes a detailed explanation of the “rules of comparison” used in this handbook. %HFDXVHWKHUHZDVRIWHQLQVXI¿FLHQWVSDFHRQRQHSDJHWRSODFHERWKWKHFKHPLFDOFRPSRVLWLRQDQG mechanical properties tables, they were split into two separate tables. To assist the user in keeping track of ZKLFKFRPSDULVRQFULWHULDZHUHXVHGIRUDJLYHQVWHHOHDFKWDEOHZLWKLQDFKDSWHUZDVVHTXHQWLDOO\QXPbered and appended with either the letter A or B. Table numbers ending in the letter A designate that the table was the main criterion used for comparison; whereas table numbers ending with the letter B were “mirrored” from the A table. Each group of steel data in the tables is separated by two types of horizontal lines: black and gray. Black lines separate groups of steels that are more closely comparable to each other; whereas gray lines separate steel data within a comparative group. Caution: The pages of this handbook are formatted to keep comparative groups together as much as possible. However, when a group of comparative steels extends to more than one page, a note is placed at WKHERWWRPRIWKHSDJHWRLQGLFDWHWKDWWKHFRPSDUDWLYHJURXSFRQWLQXHVRQWKHIROORZLQJSDJH LH³127( 7KLVVHFWLRQFRQWLQXHVRQWKHQH[WSDJH´ $SSHQGL[DQG$SSHQGL[LQFOXGHOLVWVRIZLWKGUDZQDQGUHSODFHGVWDQGDUGVWKDWVKRXOGDOZD\VEH FKHFNHGZKHQWU\LQJWR¿QGFRPSDUDEOHVWHHOV7KLVKDQGERRNXQOLNHPDQ\RWKHUVLQFOXGHVWKH\HDUGDWH of each standard, which is critical when trying to identify the status of a standard.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter
1 INTRODUCTION TO COMPARING WORLD STEEL STANDARDS
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
8
Introduction to Comparing World Steel Standards
Chapter 1
Myth and Methodology When Comparing Steel Standards
When comparing steel standards from different national and interQDWLRQDOVWDQGDUGGHYHORSPHQWRUJDQL]DWLRQV 6'2V WKHUHLVQR such thing as equivalent steel standards. At best, one may be able to group comparable steel standards together based on some GH¿QHG VHW RI UXOHV ZKLFK KDV EHHQ GRQH LQ WKLV KDQGERRN )RU example, ASTM A516/A516M Grade 70 is comparable to JIS *V\PERO6*9DQGWR(1VWHHOQDPH3 *+ based on chemical compositions, mechanical properties, and application. Yet they are not equivalent because there are differences in all three standards. Comparing steel standards is not an exact sciHQFHDQGFDQQRWEHPDGHLQWRDPDWKHPDWLFDOHTXDWLRQZKHUHWZR VLGHVRIDQHTXDWLRQDUHHTXDOWRRQHDQRWKHUEHFDXVHWKHUHZLOO always be differences among standards. 7KHVHGLIIHUHQFHVPD\EHVLJQL¿FDQWWRRQHXVHUEXWQRWVLJQL¿cant to another. Therefore, this handbook uses the term comparative to denote similar standards that have been compared to each other. Comparative is a relative word that is inevitably dependent upon the UHTXLUHPHQWVRIWKHHQGXVHUWKHRQHZKRLVXOWLPDWHO\UHVSRQVLEOHIRU VHOHFWLQJWKHDSSURSULDWHVWHHOIRUDVSHFL¿FDSSOLFDWLRQ There are some steel standards that are shared by multiple SDOs. )RU H[DPSOH (1 ,62 ±7RRO 6WHHOV LV D VWDQGDUG WKDW LV VKDUHG ZLWKLQ WKH (XURSHDQ &RPPLWWHH IRU 6WDQGDUGL]DWLRQ &(1 DQG WKH ,QWHUQDWLRQDO6WDQGDUGV2UJDQL]DWLRQ ,62 V\VWHPV&RQVHTXHQWO\ WKHGDWDDUHHTXLYDOHQWLQERWKV\VWHPVEXWWKHUHLVRQO\RQHVWDQGDUG There are also different standards that share the same grades RI VWHHO )RU H[DPSOH $670 $ DQG ,62 VKDUH VHYHQ identical bearing steel grade chemical compositions, yet there are differences in grain size, hardenability, microstructure, hardness, inspection, testing, and in other details of both standards. As a result, the seven bearing steels within these two standards are not HTXLYDOHQWEXWWKH\DUHFRPSDUDEOH Comparative and Closest Match
There is also a difference between comparative and closest match when evaluating steel standards. While gathering the data for this KDQGERRNLWZDVGLI¿FXOWWRGHFLGHZKHWKHUWRLQFOXGHGDWDRQD
technically comparative basis or on a closest match basis as both KDYHWKHLUPHULWVDQGOLPLWDWLRQV 6HHUXOHLQ(1RQ SDJHIRUDPRUHGHWDLOHGGLVFXVVLRQ A technically comparative group of steels can assist the user with making a material selection based on technical merit. However, this may severely limit the number of steels that would be comparable. On the other hand, displaying the closest match data will usually increase the number of comparative steels for the user to consider but at the risk of widening the technical comparison criteria. Likewise, a strict technical comparison will provide more accurate results, but a closest match comparison will provide more data to assist the user in searching for similar steels. There are many instances in the handbook where it would be a disservice to the reader not to include the closest match steels because there would be no comparisons otherwise. Because this broadens the technical comparison criteria, the user is warned that the data herein cannot substitute for education, experience, and VRXQGHQJLQHHULQJMXGJPHQWDIWHUHYDOXDWLQJDOORIWKHVSHFL¿FDtions within each comparable standard. ,QWKHHQGWKHUHDUHQRGH¿QLWLYHUXOHVWKDWFDQEHIRUPXODWHG to distinguish between comparative steels and closest match steels. &RQVHTXHQWO\DWWKHHGLWRU¶VGLVFUHWLRQERWKW\SHVRIFRPSDULVRQV are used in this handbook. Table 1.1 is one example of the comparison process, with respect to technically comparative steels and closest match steels. Table 1.1 lists the chemical compositions of four grades of cast DOOR\FKURPLXPQLFNHOPRO\EGHQXP &U1L0R VWHHOV,IDVWULFW technical comparison was made based on their chemical composition, none of these alloys would be comparable because their chemical compositions would differ; although there are similarities in WKHLUFDUERQ & &U0RDQG1LFRQWHQWV Table 1.2 shows how these four steels were divided into two separate comparative groups based on the differing Cr and Mo contents. The thin black line in Table 1.2 is the separator between the two comparative groups. Displaying the two groups side by side also assists the user in seeing the differences and similarities among these four cast alloy steels.
Table 1.1 List of Chemical Compositions of Cr-Ni-Mo Alloy Cast Steels Before Comparison
Specification
Designation
Weight, % max, Unless Otherwise Specified*
Steel No.
UNS No.
C
Mn
Si
P
S
Cr
Ni
Mo
Others
ASTM A958/ A958M-14
SC 4330
---
J23259
0.28– 0.33
0.60– 0.90
0.30– 0.60
0.035
0.040
0.70– 0.90
1.65– 2.00
0.20– 0.30
—
JIS G5111:1991
SCNCrM 2
---
---
0.25– 0.35
0.90– 1.50
0.30– 0.60
0.040
0.040
0.30– 0.90
1.60– 2.00
0.15– 0.35
—
EN 10293:2015
G32NiCrMo8-5-4
1.6570
---
0.28– 0.35
0.60– 1.00
0.60
0.020
0.015
1.00– 1.40
1.60– 2.10
0.30– 0.50
V 0.05 Cu 0.30
ISO 14737:2003
Grade G32NiCrMo8-5-4
---
---
0.28– 0.35
0.60– 1.00
0.60
0.020
0.015
1.00– 1.40
1.60– 2.10
0.30– 0.50
V 0.05 Cu 0.30
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 1
Introduction to Comparing World Steel Standards
9
Table 1.2 List of Chemical Compositions of Cr-Ni-Mo Cast Alloy Steels After Comparison
Specification
Steel No.
Designation
Weight, %, max, Unless Otherwise Specified
UNS No.
C
Mn
Si
0.60– 0.90
0.30– 0.60
S
Cr
Ni
Mo
Others
0.035
0.040
0.70– 0.90
1.65– 2.00
0.20– 0.30
---
0.300.60
0.040
0.040
0.300.90
1.602.00
0.150.35
---
0.60– 1.00
0.60
0.020
0.015
1.00– 1.40
1.60– 2.10
0.30– 0.50
V 0.05 Cu 0.30
0.60– 1.00
0.60
0.020
0.015
1.00– 1.40
1.60– 2.10
0.30– 0.50
V 0.05 Cu 0.30
ASTM A958/ A958M-14
SC 4330
---
J23259
0.28– 0.33
JIS G5111:1991
SCNCrM 2
---
---
0.250.35
0.901.50
EN 10293:2015
G32NiCrMo8-5-4
1.6570
---
0.28– 0.35
ISO 14737:2003
Grade G32NiCrMo8-5-4
---
---
0.28– 0.35
A classic closest match example is shown in Table 1.3, where WKHIRXUJUDGHVZLWKLQ(1DUHGLIIHUHQW RQWKLVEDVLVWKH\ may not belong to this comparative group. However, the Cr-Al-Mo alloys in this group typically are used as nitriding steels, and the (1 VWHHOV DUH WKH FORVHVW PDWFK IRU WKLV JURXS ([FOXGLQJ them would be a disservice to the user because they belong to the same application family, and its inclusion in this group will direct the user to other similar nitriding alloys. There are many opportunities to make technical errors that may lead to inappropriate steel comparisons. For example, there are many technical decisions to make when comparing stainless VWHHOVEHFDXVH¿QGLQJLGHQWLFDOFKHPLFDOFRPSRVLWLRQVZLWKLQVWDQGDUGVIURPGLIIHUHQWFRXQWULHVLVQRWFRPPRQ7DEOHVKRZVD list of comparative Cr-Ni-Mo wrought austenitic stainless steels from the United States, Europe, China, Japan, and other internaWLRQDOORFDWLRQV1RWHWKHGLIIHUHQFHVLQWKHVLOLFRQ 6L &U1LDQG
P
QLWURJHQ 1 7KH86&KLQHVHDQG-DSDQHVHFKHPLFDOFRPSRVLtions are more closely matched, whereas the European and internaWLRQDO ,62 VWDQGDUGVDUHLGHQWLFDO7KHVHGLIIHUHQFHVPD\DIIHFW the corrosion resistance performance in many applications, such that the user must be very careful when selecting a comparative steel based solely on data in this handbook. In summary, if strict technical comparison is made to this type of data, few relationships among the various grades of steel would be established, and the comparison would serve no purpose. %\ZLGHQLQJWKHWHFKQLFDOFRPSDULVRQFULWHULDWR¿QGWKHFORVHVW match steels, the user must understand that these steels are not HTXLYDOHQWDQGFDQQRWEHLQGLVFULPLQDWHO\VXEVWLWXWHGZLWKRXW¿UVW reviewing the complete current standards and securing competent technical advice prior to any decision making. 7R¿QGDEDODQFHIRUFRPSDULVRQRIVWHHOVE\SURGXFWIRUPXVH DSSOLFDWLRQ PHFKDQLFDO SURSHUWLHV FKHPLFDO FRPSRVLWLRQV
Table 1.3 Chromium-Molybdenum-Aluminum (Cr-Mo-Al) Steels for Nitriding UNS No.
Steel No.
K24065
32CrAlMo7-10
Specification
Designation
Weight, %, max, Unless Otherwise Specified C
Mn
Si
P
S
Cr
Ni
Mo
Others
---
0.38– 0.43
0.50– 0.70
0.15– 0.35
0.035
0.040
1.40– 1.80
---
0.30– 0.40
Al 0.95–1.30
---
1.8505
0.28– 0.35
0.40– 0.70
0.40
0.025
0.035
1.50– 1.80
---
0.20– 0.40
Al 0.80–1.20
34CrAlMo5-10
---
1.8507
0.30– 0.37
0.40– 0.70
0.40
0.025
0.035
1.00– 1.30
---
0.15– 0.25
Al 0.80–1.20
34CrAlNi7-10
---
1.8550
0.30– 0.37
0.40– 0.70
0.40
0.025
0.035
1.50– 1.80
0.85– 1.15
0.15– 0.25
Al 0.80–1.20
41CrAlMo7-10
---
1.8509
0.38– 0.45
0.40– 0.70
0.40
0.025
0.035
1.50– 1.80
---
0.20– 0.35
Al 0.80–1.20
GB/T 3077-1999
Grade 38CrMoAl
---
---
0.35– 0.42
0.30– 0.60
0.20– 0.45
0.035
0.035
1.35– 1.65
0.30
0.15– 0.25
Al 0.70–1.10; Cu 0.30
GB/T 3078-94
Grade 38CrMoAlA
---
---
0.35– 0.42
0.30– 0.60
0.20– 0.45
0.025
0.025
1.35– 1.65
0.30
0.15– 0.25
Al 0.70–1.10; Cu 0.25
ISO 683-10:1987
41 CrAlMo 7 4
---
---
0.38– 0.45
0.50– 0.80
0.50
0.030
0.035
1.50– 1.80
---
0.25– 0.40
Al 0.8–1.20
JIS G4053:2008
Symbol SACM 645
---
---
0.40– 0.50
0.60
0.15– 0.50
0.030
0.030
1.30– 1.70
0.25
0.15– 0.30
Al 0.70–1.20; Cu 0.30
ASTM A355-89 (2012)
A
EN 10085:2001
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
10
Introduction to Comparing World Steel Standards
Chapter 1
Table 1.4 List of Comparative Cr-Ni-Mo Wrought Austenitic Stainless Steels
Specification
Designation
UNS
Steel
Weight, %, max, Unless Otherwise Specified
No.
No.
C
Mn
Si
P
S
Cr
Ni
Mo
ASME SA-240/SA-240M
Type 317L
S31703
---
0.030
2.00
0.75
0.045
0.030
18.0–20.0
11.0– 15.0
3.0– 4.0
N 0.10
ASTM A240/A240M-15a
Type 317L
S31703
---
0.030
2.00
0.75
0.045
0.030
18.0–20.0
11.0– 15.0
3.0– 4.0
N 0.10
EN 10028-7:2007
X2CrNiMo18-15-4
---
1.4438
0.030
2.00
1.00
0.045
0.015
17.5–19.5
13.0– 16.0
3.0– 4.0
N 0.10
EN 10088-2:2014
X2CrNiMo18-15-4
---
1.4438
0.030
2.00
1.00
0.045
0.015
17.5–19.5
13.0– 16.0
3.0– 4.0
N 0.10
GB 4237-92
Grade 00Cr19Ni13Mo3
---
---
0.030
2.00
1.00
0.035
0.030
18.00– 20.00
11.00– 15.00
3.00– 4.00
---
GB 4239-91
Grade 00Cr19Ni13Mo3
---
---
0.030
2.00
1.00
0.035
0.030
18.00– 20.00
11.00– 15.00
3.00– 4.00
---
ISO 9328-7:2004
Grade X2CrNiMo18-15-4
---
---
0.030
2.00
1.00
0.045
0.015
17.5–19.5
13.0– 16.0
3.00– 4.0
N 0.11
JIS G 4304:2012
Symbol SUS317L
---
---
0.030
2.00
1.00
0.045
0.030
18.00– 20.00
11.00– 15.00
3.00– 4.00
---
JIS G 4305:2012
Symbol SUS317L
---
---
0.030
2.00
1.00
0.045
0.030
18.00– 20.00
11.00– 15.00
3.00– 4.00
---
SAE J405 JUN98
Type 317L
S31703
---
0.030
2.00
0.75
0.045
0.030
18.00– 20.00
11.00– 15.00
3.00– 4.00
N 0.10
UHODWHGPDQXIDFWXULQJSURFHVVHV LQFOXGLQJKHDWWUHDWPHQW DQGVR forth, a methodology had to be put in place and rules had to be established. However, as much as methodology and rules were essential in preparing this handbook, there were many instances where they would not cover every variable and circumstance. 7KHUHIRUHGLI¿FXOWFRPSDULVRQGHFLVLRQV²VXFKDVWKRVHGHVFULEHG previously—had to be made. There were literally hundreds, if not more than a thousand, such decisions made in this handbook. In these cases, the closest match comparison decisions were made at the discretion of the editor. Organization
7ZRRIWKHPDLQYDULDEOHVLQVHOHFWLQJDVSHFL¿FJUDGHRIVWHHODUH LWVLQWHQGHGDSSOLFDWLRQ XVH DQGSURGXFWIRUPZKLFKXVXDOO\QDUrows the selection to a family of steels. Therefore, the remaining data chapters in this handbook were organized by product form and use, as follows. Chapter No.
2. 3. 5. 6. 7.
Title Carbon and Alloy Steels for General Use Structural Steel Plates 3UHVVXUH9HVVHO6WHHO3ODWHV Steel Tubes and Pipes Steel Forgings Steel Castings
9.
Others
:URXJKW6WDLQOHVV6WHHOV Steels for Special Use
$OWKRXJK WKLV OLVW RI FKDSWHU WLWOHV DW ¿UVW JODQFH ORRNV UDWKHU VWUDLJKWIRUZDUGWKHUHZHUHGLI¿FXOWGHFLVLRQVUHJDUGLQJWKHVWHHO FRPSDULVRQVZLWKLQHDFKFKDSWHU)RUH[DPSOH$670KDV GH¿nitions for pipeDQGGH¿QLWLRQVIRUtube, depending on the stanGDUG¶V VXEMHFW PDWWHU DQG DSSOLFDWLRQ VHH ASTM Dictionary of Engineering Science & TechnologyWKHGLWLRQ ,QFRQWUDVW,62 6WHHO 3URGXFWV IRU 3UHVVXUH 3XUSRVHV²4XDOLW\ 5HTXLUHPHQWV²3DUW ,, :URXJKW 6HDPOHVV 7XEHV QRWHV WKDW “The word tube is synonymous with pipe.” Each standard is typically listed only in one chapter, but there DUHH[FHSWLRQV)RUH[DPSOH$670$$0±D6WDQGDUG 6SHFL¿FDWLRQ IRU &KURPLXP DQG &KURPLXP1LFNHO 6WDLQOHVV Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications, appears in more than one chapter due to its dual role IRU SUHVVXUH YHVVHO DQG JHQHUDO DSSOLFDWLRQV LH &KDSWHU ² 3UHVVXUH 9HVVHO 6WHHO 3ODWHV DQG &KDSWHU ²:URXJKW 6WDLQOHVV 6WHHOV 6LPLODUO\ WKH -DSDQHVH ,QGXVWULDO 6WDQGDUGV -,6 DQG &KLQHVH *XRMLD%LDR]KXQRU*% VWDLQOHVVVWHHOÀDWSURGXFWVWDQGDUGVZHUHDOVRLQFOXGHGLQ&KDSWHUVDQG Definitions of Steel Terms
,WLVFRPPRQWR¿QGWHUPLQRORJ\VWDQGDUGVIRUVWHHOVZLWKLQPRVW EXW QRW DOO VWDQGDUG GHYHORSPHQW RUJDQL]DWLRQV 6'2V 7KHVH
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 1
Introduction to Comparing World Steel Standards
11
standards are very useful when working with steel standards, parWLFXODUO\ZKHQLQWHUSUHWLQJVSHFL¿FWHUPV7DEOHFRQWDLQVDOLVW of steel terminology standards. It is important to note that these standards differ in the terms used to describe the different types of steel. The user of comparative steel standards data must take into account that each national 6'2KDVWKHLURZQVHWRIWHUPVDQGGH¿QLWLRQVIRUVWHHOVDQGUHODWHG SURGXFWV DQG LQ VRPH FDVHV PD\ KDYH PXOWLSOH GH¿QLWLRQV )RU H[DPSOHWKUHHGLIIHUHQWGH¿QLWLRQVIRUFDUERQVWHHOFDQEHIRXQGLQ $670VWDQGDUGV$ E$ DQG) D $VXPPDU\RIWKHFKHPLFDOHOHPHQWOLPLWVIRU$670$ 13b alloy steel and EN 10020:2000 non-alloy steel is shown in Table 1.6. Although the limits seem to be the same, it is important WRQRWHWKHUXOHLQ(13DUDJUDSKZKLFKVWDWHV
,QVRPHFDVHVWKLVUXOHUHVXOWHGLQVHYHUDOVWHHOVEHLQJQRQFRPSDUDEOH)RUH[DPSOH(1± )ODW3URGXFWV0DGH of Steels for Pressure Purposes—Part 3: Weldable Fine Grain 6WHHOV1RUPDOL]HGFRQWDLQVVWHHOVZLWKDQLFNHOFRQWHQWRI PD[LPXP LH WKHUH LV QR PLQLPXP QLFNHO UHTXLUHPHQW 8VLQJ WKHUXOHWKLVZRXOGGH¿QHWKHVHVWHHOVWRFRQWDLQ1L ZKLFKLVRYHUWKHPD[LPXPOLPLWIRUQRQDOOR\VWHHOV FDUERQVWHHOV WKHUHE\PDNLQJWKHPDOOR\VWHHOVDQGWKXVEHFRPLQJ noncomparable with non-alloy steels. $670$ EDQG(1 VKDUHWKHVDPHGH¿QLtion for stainless steel, as follows.
Where for elements other than manganese a maximum value only LV VSHFL¿HG LQ WKH SURGXFW VWDQGDUG RU VSHFL¿FDWLRQ IRU WKH ODGOH DQDO\VLVDYDOXHRIRIWKLVPD[LPXPYDOXHVKDOOEHWDNHQIRU FODVVL¿FDWLRQDVVHWRXWLQWDEOHVDQG)RUPDQJDQHVHVHHQRWHa of table 1.
In this handbook, steels have been divided into three main categories:
6WDLQOHVV VWHHO²D VWHHO WKDW FRQIRUPV WR D VSHFL¿FDWLRQ WKDW UHTXLUHVE\PDVVSHUFHQWDPLQLPXPFKURPLXPFRQWHQWRIRU more, and a maximum carbon content of less than 1.20.
1. &DUERQ6WHHOV 1RQ$OOR\6WHHOV 2. Alloy Steels 3. Stainless Steels
Table 1.5 List of Steel Terminology Standards ASTM A941-13b
Standard Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
ASTM A644-14
Standard Terminology Relating to Iron Castings
ASTM A751-14a
Standard Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
ASTM A902-15
Standard Terminology Relating to Metallic Coated Steel Products
EN 10020:2000
Definition and Classification of Grades of Steel
EN 10027-1:2005
Designation systems for steels—Part 1: Steel names
EN 10052:1993
Vocabulary of Heat Treatment Terms for Ferrous Products
EN 10079:2007
Definition of Steel Products
EN 10169-1:2003
Continuously Organic Coated (Coil Coated) Steel Flat Products—Part 1: General Information (Definitions, Materials, Tolerances, Test Methods)
EN 10266:2003
Steel tubes, fittings and structural hollow sections—Symbols and definitions of terms for use in product standards
GB/T 13304-1991
Steels—Classification
GB/T 15574-1995
Steel products classification and definitions
GB/T 15575-1995
Steel products standard designation
GB/T 341-1989
Steel wire—Classification and vocabulary
JIS G 0201:2000
Glossary of terms used in iron and steel (Heat treatment)
JIS G 0202:2013
Glossary of terms used in iron and steel (Testing)
JIS G 0203:2009
Glossary of terms used in iron and steel (Products and quality)
ISO 6929:1987
Steel products—Definitions and classification
ISO 2532:1974
Steel wire ropes—Vocabulary
ISO 3252:2000
Powder metallurgy—Vocabulary
ISO 4885:1996
Ferrous products—heat treatments—Vocabulary
ISO 8954-1:1990
Ferroalloys—Vocabulary—Part 1: Materials
ISO 8954-2:1990
Ferroalloys—Vocabulary—Part 2: Sampling and sample preparation
ISO 8954-3:1990
Ferroalloys—Vocabulary—Part 3 Sieve analysis
ISO 17893:2004
Steel wire ropes—Vocabulary, designation, and classification
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
12
Introduction to Comparing World Steel Standards
Chapter 1
Table 1.6 Limits for EN 10020:2000 and ASTMA 941-13b Between Carbon Steels/Non-Alloy Steel and Alloy Steela (% by mass) Symbol
Name
Al
Aluminum
B
Boron
Bi
Bismuth
EN 10020:2000b
ASTM A941-13b
0.30
0.30
0.0008
0.0008
0.10
---
Co
Cobalt
0.30
0.30
Cr
Chromium
0.30
0.30
Cu
Copper
0.40
0.40
La
Lanthanides
0.10
---
Mn
Manganese
1.65b
1.65
Mo
Molybdenum
0.08
0.08
Nb
Niobium
0.06
0.06
Ni
Nickel
0.30
0.30
Pb
Lead
0.40
0.40
Se
Selenium
0.10
---
Si
Silicon
0.60
0.60
Te
Tellurium
0.10
---
Ti
Titanium
0.05
0.05
V
Vanadium
0.10
0.10
W
Tungsten
0.30
0.30
Zr
Zirconium
0.05
0.05
Other (except C, P, S, N)
0.10
0.10
aAlloy steel when equal to or greater than the limit. bWhere manganese is specified only as a maximum, the limit value is 1.80 % and the 70 % rule does not apply (see 3.1.2 of EN 10020:2000).
standard to establish appropriate safety and health practices and GHWHUPLQHWKHDSSOLFDELOLW\RIUHJXODWRU\UHTXLUHPHQWVSULRUWRXVH Questions Regarding the Rules of Comparison
:KHQFRPSDULQJWZRRUPRUHVWHHOVWDQGDUGVWKHIROORZLQJTXHVtions must be asked: 1. Should mechanical properties or chemical composition be the main criteria? If mechanical properties are compared, which SURSHUW\VKRXOGEHWKH¿UVWFULWHULDIRUFRPSDULVRQWKDWLV\LHOG strength, tensile strength, elongation, impact strength, hardness, and so on? Once having selected a primary criterion, say tensile strength, should there be a secondary criterion for ranking the comparative steels within this group, for example, yield strength, hardness, and so on? When mechanical properties or chemical compositions vary with section thickness for a given steel grade, which section thickness data should be selected as the criteria for comparison? When two steels have the same minimum tensile strength values but have different yield strength values, are they no longer similar? 2. 6KRXOG FRPSDULVRQV EH EDVHG RQ WKH GDWD¶V PLQLPXP YDOXHV maximum values, or average values of their minimum/maximum ranges? Should alloy steels and stainless steels be compared based on their mechanical properties when they generally are VHOHFWHGIRUXVHEDVHGRQWKHLUDOOR\LQJHOHPHQWV¶DELOLWLHVWRSURvide satisfactory service in their intended applications? 3. Is it reasonable to compare steels based only on their chemical compositions, regardless of their product form? That is, should forging steels be compared to steel plates or tubes because they have similar chemical compositions, and is this type of comparative data useful in engineering practice? Noncomparable Steels
$670$ EDQG(1 ZHUHXVHGDVJXLGHOLQHVLQ developing these categories. Where practical, these steel categories were further divided into subcategories based on their product IRUP LQWHQGHG DSSOLFDWLRQ VHUYLFH UHTXLUHPHQW RU RWKHU VLPLODU criteria.
It is fundamental to understand that not all steels have comparative counterparts. Knowing that a steel is noncomparable can be just as important as knowing that there are comparative steels. Otherwise, valuable time could be wasted searching for something that does not exist.
Cautionary Note
Criteria for Comparing Steels
0DQ\ VWDQGDUG VSHFL¿FDWLRQV LQFOXGH FDXWLRQDU\ SDUDJUDSKV WKDW ZDUQXVHUVDERXWWKHLUUHVSRQVLELOLWLHV HJVHH3DUDJUDSKIURP $670 $$0 TXRWHG KHUH $FFRUGLQJO\ LW LV WKH XVHU¶V responsibility when comparing steel standards to perform an engineering review of each standard to ensure that it is suitable for their intended application.
The two major criteria for comparing steels in this type of handbook are mechanical properties and chemical compositions. For each given standard steel grade, there is typically only one chemical composition, which makes it ideal as a comparison criterion. However, there are several mechanical properties that can be used to compare standard steel grades and, to be consistent throughout a handbook of this type, only one property can be choVHQ7KHGHFLVLRQZDVWRXVHDVWHHO¶VWHQVLOHVWUHQJWKDVWKHVHFRQG comparison criterion. Having settled on chemical composition and tensile strength as the two main comparison criteria, the next step was to decide
The following precautionary caveat pertains only to the test method SRUWLRQ6HFWLRQV DQGRIWKLVVSHFL¿FDWLRQ 7KLV standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 1
when to apply one or the other, or both. Because carbon steels typically are selected based on mechanical properties, it was GHFLGHGWKDWWHQVLOHVWUHQJWKZRXOGEHWKH¿UVWFULWHULRQXVHGIRU comparing carbon steels. Likewise, because alloy steels and stainless steels generally are selected based on their chemistry, it was decided that chemical composition would be used to compare them. An exception to this methodology is made for the structural steels data in Chapter 3, where the tensile strength was used as the main comparison criterion for carbon and alloy steels. This exception was made because structural steels generally are selected based on their mechanical properties. Also in this same chapter, high-strength, low-alloy steels are treated as a subcategory to DOOR\VWHHOVDOWKRXJK$670$ GH¿QHVWKHPVHSDUDWHO\ %HFDXVHWKHUHZDVLQVXI¿FLHQWVSDFHRQDSDJHWRSODFHERWK the chemical composition and mechanical properties tables, they were split into two separate tables. To assist the user in keeping track of the comparison criteria used for a given steel, each table ZLWKLQDFKDSWHUZDVVHTXHQWLDOO\QXPEHUHGDQGDSSHQGHGZLWK the letter A or B. Table numbers ending in the letter A designate that it was the main criterion used for comparison, whereas table numbers ending with the letter B were “mirrored” from the A WDEOHV,QWKLVPDQQHUWKHXVHUPXVW¿UVWFRQVLGHUWKHGDWDLQWKH A table, and then see how well the data in the B table match the steels that are being compared. This is not a foolproof methodology of comparison. For examSOH$670$ *UDGH6&KDVRQHFKHPLFDOFRPSRVLWLRQEXW KDV GLIIHUHQW VWUHQJWK FODVVHV EDVHG RQ KHDW WUHDWPHQW VHH &KDSWHU 6R MXVW EHFDXVH WZR VWHHO JUDGHV KDYH FRPSDUDWLYH chemical compositions does not mean that they are comparable in mechanical properties and vice versa. Using data found in this KDQGERRNLVRQO\RQHVWHSLQ¿QGLQJVXLWDEOHFRPSDUDEOHVWHHOIRU the intended application. With this basic methodology in place, the following is a list of the comparison rules that were established to produce this handbook. List of Comparison Rules
1. 7 KH¿UVWFULWHULRQRIRUGHUIRUFDUERQ QRQDOOR\ VWHHOVLVEDVHG on tensile strength, followed by yield strength; that is, if two steels have the same tensile strength, then they are placed in ascending order by yield strength, and if yield strength is not UHTXLUHGLWLVSODFHGDWWKHWRSRIWKHRUGHU 2. Typically, comparative groups are made for every 50 MPa 1PP2 RU NVL LQ WHQVLOH VWUHQJWK WKDW LV D EODFN line divides comparative groups every 50 Mpa [50 N/mm2 or 7.25 NVL@ :KHQDQDEXQGDQFHRIGDWDLVDYDLODEOHWKLVOLPLWPD\EH reduced to improve the comparison accuracy. 3. Mechanical property subcategories, such as steels with impact WHVWLQJEHORZí& í) DUHXVHGWRIXUWKHUQDUURZWKHFRPparison process. ,IDFDUERQVWHHO¶VWHQVLOHVWUHQJWKYDULHVZLWKVHFWLRQWKLFNQHVV the tensile strength of the lowest section thickness will be used as
Introduction to Comparing World Steel Standards
13
the governing comparison factor. There is no technical reason for choosing the lowest section thickness; it is just that one had to be chosen. 5. If a carbon steel standard does not contain mechanical properties, such as those found in Chapter 2, Carbon and Alloy Steels for General Use, then the steels will be compared based on their carbon content. 6. The major criterion for alloy steel and stainless steel comparisons is chemical composition. Once these steels are placed in a comparative group by chemical composition, they are then arranged in ascending order within these groups by their tensile strength. Where possible, subcategories of alloy and stainless steel groups are made to further narrow the comparison process. 7. &KHPLFDOFRPSRVLWLRQVOLVWHGDUHWKHKHDWDQDO\VLVUHTXLUHPHQWV LQWKHVWDQGDUGV DOVRFDOOHGODGOHRUFDVWDQDO\VLV 3URGXFWDQDOyses are not listed. The chemical composition and mechanical properties data for the same steel grades are typically not listed on the same page GXHWRVSDFHOLPLWDWLRQV&RQVHTXHQWO\DVDPHDQVRINHHSLQJ the data consistent between these two sets of tables, each table is numbered, and each table number ends with either the letter A or B. 9. Each set of steel data in the tables is divided by two types of horizontal lines: black and gray. Black lines separate groups of steels that are more closely comparable to each other, whereas gray lines separate steel data within a comparative group. This does not mean that steels outside of these groups cannot be compared because these horizontal lines are dependent upon all of the comparison rules in this list and can be subjective at times. Caution: Do not confuse the thinner dividing black line within a table with the thicker black rule that borders the table. To assist in this regard, the pages were formatted to keep comparative groups together as much as practicable. However, when a group of comparative steels appears on more than one page, a note is placed at the bottom of the page to indicate that the comparative JURXSFRQWLQXHVRQWKHIROORZLQJSDJH ³1RWH 7KLVJURXSFRQWLQXHVRQWKHQH[WSDJH´ /LNHZLVHZKHQDVSHFL¿FDWLRQZLWKLQ DJURXSRIFRPSDUDWLYHVWHHOVFDQQRW¿WRQWRMXVWRQHSDJHDQRWH LVSODFHGDWWKHERWWRPRIWKHSDJHWRLQGLFDWHWKDWWKHVSHFL¿FDtion within the comparative group continues on the following SDJH ³1RWH 7KLV VSHFL¿FDWLRQ FRQWLQXHV RQ WKH QH[W SDJH ZLWKLQWKHVDPHJURXS´ 10. Steel data in standards are not always mandatory. Some data are listed as typical values or informative values or are found in supSOHPHQWDU\ UHTXLUHPHQWV 7KLV W\SH RI GDWD LV VWLOO YHU\ XVHIXO and has been included in this handbook whenever possible. This W\SHRIGDWDLVLGHQWL¿HGZLWKDQH[SODQDWRU\QRWHWKDWDSSHDUVLQ the list of standards at the beginning of the related chapter. 11. 6RPHVWDQGDUGVLQFOXGHGPXOWLSOHUHTXLUHPHQWVIRULPSDFWWHVWLQJVXFKDVGLIIHULQJWHVWWHPSHUDWXUHVRUUHTXLUHPHQWVIRUVXEsize specimens. Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
14
Introduction to Comparing World Steel Standards
Chapter 1
12. Where space permitted, as much data as possible were included. However, there are occasions when the phrase “see standard for impact test data” was used to indicate that more data could be found in the standard. 13. The phrase “see standard for impact test data” was also used when the standard did not specify a test temperature but did specify an absorbed energy value. Impact testing values listed in the tables are typically for full-size specimens and for the minimum average result at the testing temperature but do not include the minimum individual test piece UHTXLUHPHQWLIDQ\ 15. For the purpose of this handbook, phrases found in standards such as “may be applied if necessary” or “may be applied by agreement between the purchaser and supplier” or “the manuIDFWXUHUPD\¿QGLWQHFHVVDU\WR´RU³ZKHQVSHFL¿HG´RU³PD\ be added if necessary” are not a part of the comparison process. 16. Data from footnotes in the chemical composition and mechanical properties tables of steel standards were considered during the comparison process but were not always reported in the handbook due to lack of space in the tables or because they represented technical issues that were too complex to be represented in a tabular format. In these cases, the note “see standard” was used. 17. The same heat treatment terms used in each standard are listed at the beginning of each chapter. Abbreviations in the tables were made based on the terms used in the standards. A concerted effort was made to make the abbreviations consistent from chapter to chapter, although there are exceptions because each heat treatment abbreviation must be referred to in the list of heat treatment terms at the beginning of each chapter. There are many LQVWDQFHVZKHQWKHKHDWWUHDWPHQWUHTXLUHPHQWVZLWKLQDVWDQGDUG became very cumbersome to include in a small cell within a table. &RQVHTXHQWO\WKHSKUDVH³VHHVWDQGDUG´LVXVHGWRGLUHFWWKHXVHU to the standard to read all of the heat treatment details involved. A determined effort was made to enter the data in this handbook in a manner identical to that listed in the related standard, includLQJWKHXVHRIQLRELXP 1E RUFROXPELXP &E ,WVKRXOGEHQRWHG that even within the same SDO, data were not always entered in WKHVDPHPDQQHUIURPVWDQGDUGWRVWDQGDUG IRUH[DPSOH73 YHUVXV73ZKHUHDVSDFHEHWZHHQWKHOHWWHU3DQGWKHQXPEHU 3 is listed in the data. Brief Introduction to Steel Standards and Designation Systems
In the world of standardization, metals were at the forefront at the WXUQRIWKHWZHQWLHWKFHQWXU\,Q WKH,QWHUQDWLRQDO$VVRFLDWLRQ IRU7HVWLQJ0DWHULDOV ,$70 KHOGWKHLU¿UVWFRQIHUHQFHLQ=XULFK and the standardization of metals began. The IATM encouraged PHPEHUVWRIRUPQDWLRQDOFKDSWHUVDQGRQ-XQH ,$70 members met in Philadelphia to form the American section of the
,QWHUQDWLRQDO $VVRFLDWLRQ IRU 7HVWLQJ 0DWHULDOV ZKLFK LQ EHFDPHWKH$PHULFDQ6RFLHW\IRU7HVWLQJ0DWHULDOV $670 %\UHYLHZLQJVRPHH[DPSOHVRIWKHPRUHSURPLQHQWPHWDOV¶ designation systems, a direction is offered to assist those who use metal standards as a part of their work or study. This section is not all-inclusive. The amount of information on this topic could easily make up a complete book. ASTM Designation System
$670¶VGHVLJQDWLRQV\VWHPIRUPHWDOVFRQVLVWVRIDOHWWHU $IRU IHUURXVPDWHULDOV IROORZHGE\DQDUELWUDU\VHTXHQWLDOO\DVVLJQHG QXPEHU 7KHVH GHVLJQDWLRQV RIWHQ DSSO\ WR VSHFL¿F SURGXFWV IRU H[DPSOH$LVDSSOLFDEOHWRVHDPOHVVFROGGUDZQFDUERQVWHHO tubing for hydraulic system service. Metric ASTM standards have DVXI¿[OHWWHU0 Examples of the ASTM ferrous metal designation system, GHVFULELQJ LWV XVH RI VSHFL¿FDWLRQ QXPEHUV DQG OHWWHUV DUH DV follows: $670 $$0D *UDGH ²3UHVVXUH 9HVVHO Plates, Alloy Steel and High-Strength Low-Alloy Steel, Quenched-and-Tempered: A describes a ferrous metal but does not subclassify it as cast iron, carbon steel, alloy steel, tool steel, or stainless steel. 334LVDVHTXHQWLDOQXPEHUZLWKRXWDQ\UHODWLRQVKLSWRWKHPHWDO¶V properties. 0LQGLFDWHVWKDWWKHVWDQGDUG$0LVZULWWHQLQUDWLRQDOL]HG6, XQLWV WKH ³0´ FRPHV IURP WKH ZRUG ³PHWULF´ KHQFH WRJHWKHU $$0LQFOXGHVERWKLQFKSRXQGDQG6,XQLWV LQGLFDWHVWKH\HDURIDGRSWLRQRUODVWUHYLVLRQDQGDOHWWHUa followLQJWKH\HDULQGLFDWHVWKHVHFRQGUHYLVLRQRIWKHVWDQGDUGLQ ( , a number in parentheses, indicates the year of last reapproval. Grade 1 indicates the type of steel.
In the steel industry, the terms grade, type, and class generally are GH¿QHGDVIROORZVGrade is used to describe chemical composition; typeLVXVHGWRGH¿QHGHR[LGDWLRQSUDFWLFH DQGclass is used to LQGLFDWHRWKHUFKDUDFWHULVWLFVVXFKDVVWUHQJWKOHYHORUVXUIDFH¿Qish. However, within ASTM standards, these terms were adapted for use to identify a particular metal within a metal standard and DUH XVHG ZLWKRXW DQ\ ³VWULFW´ GH¿QLWLRQ EXW HVVHQWLDOO\ PHDQ WKH same thing, although some loose rules do exist, as follows. $670 $$0 *UDGH $ *UDGH % *UDGH &² Seamless Carbon Steel Pipe for High-Temperature Service: 7\SLFDOO\DQLQFUHDVHLQDOSKDEHW VXFKDVWKHOHWWHUV$%& UHVXOWV in higher tensile or yield strength steels and, if it is an unalloyed carbon steel, an increase in carbon content. ,QWKLVFDVH *UDGH$ & PD[ NVLWHQVLOHVWUHQJWK PLQ *UDGH% & PD[ NVLWHQVLOHVWUHQJWK PLQ *UDGH& & PD[ NVLWHQVLOHVWUHQJWK PLQ
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 1
$670$$07\SH²6WDLQOHVV6WHHO%DUV and Shapes: 7\SHVDQGRWKHUVDUHEDVHGRQWKH6$(GHVLJQDWLRQ V\VWHPIRUVWDLQOHVVVWHHOV VHH6$(DQGIRUPHU$PHULFDQ,URQDQG 6WHHO,QVWLWXWH>$,6,@GHVFULSWLRQWKDWIROORZV
Another use of ASTM grade designators is found in pipe, tube, and IRUJLQJSURGXFWVZKHUHWKH¿UVWOHWWHU³3´UHIHUVWRSLSH³7´UHIHUV to tube, “TP” may refer to tube or pipe, and “F” refers to forging. ([DPSOHVDUHIRXQGLQWKHIROORZLQJ$670VSHFL¿FDWLRQV ASTM A335/A335M-15, Grade P22, Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service ASTM A213/A213M-15a, Grade T22, Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes
Introduction to Comparing World Steel Standards
15
)RUDOOR\VWHHOVWKH¿UVWWZRGLJLWVRIWKH6$(V\VWHPGHVFULEH WKHPDMRUDOOR\LQJHOHPHQWVSUHVHQWLQWKHPDWHULDOWKH¿UVWGLJLW JLYLQJWKHDOOR\JURXS)RUH[DPSOHWKH;;VHULHVRIVWHHOVFRQWDLQ±1L±&UDQG±0RDORQJ with composition ranges for manganese and silicon and the maximums for sulfur and phosphorus. Additional letters added between the second and third digits LQFOXGH³%´ZKHQERURQLVDGGHG EHWZHHQDQG IRUHQKDQFHGKDUGHQDELOLW\DQG³/´ZKHQOHDGLVDGGHG EHWZHHQ DQG IRUHQKDQFHGPDFKLQDELOLW\7KHSUH¿[³0´LV XVHGWRGHVLJQDWHPHUFKDQWTXDOLW\VWHHO WKHOHDVWUHVWULFWLYHTXDOity descriptor for hot-rolled steel bars used in noncritical parts of VWUXFWXUHVDQGPDFKLQHU\ 7KHSUH¿[³(´ HOHFWULFIXUQDFHVWHHO DQG WKH VXI¿[ ³+´ KDUGHQDELOLW\ UHTXLUHPHQWV DUH PDLQO\
$670 $$0 *UDGH 73 6HDPOHVV :HOGHG DQG Heavily Cold Worked Austenitic Stainless Steel Pipes ASTM A336/A336M-10a, Grade F91, Alloy Steel Forgings for Pressure and High-Temperature Parts
ASTM Referenced Standards and Supplementary Requirements
ASTM standards contain a “referenced documents” section, which lists other ASTM standards that are referenced in the text and that either become a part of the original standard or its supplementary UHTXLUHPHQWV6XSSOHPHQWDU\UHTXLUHPHQWVDUHOLVWHGDWWKHHQGRI WKH$670VWDQGDUGVDQGGRQRWDSSO\XQOHVVVSHFL¿HGLQWKHSXUchase order—that is, they are optional. SAE Designation System and Related AISI Designation System
For many years, certain grades of carbon and alloy steels have been designated by a four-digit AISI/SAE numbering system that idenWL¿HG WKH JUDGHV DFFRUGLQJ WR VWDQGDUG FKHPLFDO FRPSRVLWLRQV %HFDXVHWKH$,6,GRHVQRWZULWHPDWHULDOVSHFL¿FDWLRQVWKHUHODtionship between AISI and grade designations has been discontinued. Beginning with the 1995 edition of the Iron and Steel Society ,66 6WULS6WHHO0DQXDOWKHIRXUGLJLWGHVLJQDWLRQVDUHUHIHUUHGWR solely as SAE designations. The SAE system uses a basic four-digit system to designate the chemical composition of carbon and alloy steels. Throughout the system, the last two digits give the carbon content in hundredths of a percent. Carbon steels are designated 10XX. For example, a carbon VWHHOFRQWDLQLQJFDUERQLVGHVLJQDWHGLQWKLVV\VWHP 5HVXOIXUL]HG FDUERQ VWHHOV DUH GHVLJQDWHG ZLWKLQ WKH VHULHV 11XX, resulfurized and rephosphorized carbon steels within ;;DQGVWHHOVKDYLQJPDQJDQHVHFRQWHQWVEHWZHHQ DQG EXW QR RWKHU DOOR\LQJ HOHPHQWV DUH GHVLJQDWHG ;; Composition ranges for manganese and silicon and maximum perFHQWDJHVIRUVXOIXUDQGSKRVSKRUXVDUHDOVRVSHFL¿HG
Table 1.7 Types and Identifying Elements in Standard SAE Carbon and Alloy Steels Carbon Steels
Description
10XX
Non-resulfurized, 1.00 manganese maximum
11XX
Resulfurized
12XX
Rephosphorized and resulfurized
15XX
Non-resulfurized, over 1.00 manganese maximum
Alloy Steels
Description
13XX
1.75 manganese
40XX
0.20 or 0.25 molybdenum or 0.25 molybdenum and 0.042 sulfur
41XX
0.50, 0.80, or 0.95 chromium and 0.12, 0.20, or 0.30 molybdenum
43XX
1.83 nickel, 0.50 to 0.80 chromium, and 0.25 molybdenum
46XX
0.85 or 1.83 nickel and 0.20 or 0.25 molybdenum
47XX
1.05 nickel, 0.45 chromium, 0.20 or 0.35 molybdenum
48XX
3.50 nickel and 0.25 molybdenum
51XX
0.80, 0.88, 0.93, 0.95, or 1.00 chromium
51XXX
1.03 chromium
52XXX
1.45 chromium
61XX
0.60 or 0.95 chromium and 0.13 or 0.15 vanadium minimum
86XX
0.55 nickel, 0.50 chromium, and 0.20 molybdenum
87XX
0.55 nickel, 0.50 chromium, and 0.25 molybdenum
88XX
0.55 nickel, 0.50 chromium, and 0.35 molybdenum
92XX
2.00 silicon or 1.40 silicon and 0.70 chromium
50BXX
0.28 or 0.50 chromium
51BXX
0.80 chromium
81BXX
0.30 nickel, 0.45 chromium, and 0.12 molybdenum
94BXX
0.45 nickel, 0.40 chromium, and 0.12 molybdenum
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
16
Introduction to Comparing World Steel Standards
Chapter 1
DSSOLFDEOHWRDOOR\VWHHOV7KHIXOOVHULHVRIFODVVL¿FDWLRQJURXSVLV shown in Table 1.7. UNS Designation System
7KH8QL¿HG1XPEHULQJ6\VWHP 816 LVDQDOSKDQXPHULFGHVLJQDWLRQV\VWHPFRQVLVWLQJRIDOHWWHUIROORZHGE\¿YHQXPEHUV7KLV system represents only the chemical composition for an individual PHWDORUDOOR\DQGLVQRWDPHWDOVWDQGDUGRUVSHFL¿FDWLRQ)RUWKH most part, existing systems such as the SAE designations were incorporated into the UNS so that some familiarity was given to the system where possible. )RUH[DPSOHWKH816SUH¿[OHWWHUIRUFDUERQDQGDOOR\VWHHOV LV³*´DQGWKH¿UVWIRXUGLJLWVDUHWKH6$(GHVLJQDWLRQ IRUH[DPSOH6$(LV816*7KHLQWHUPHGLDWHOHWWHUV³%´DQG ³/´RIWKH6$(V\VWHPDUHUHSODFHGE\PDNLQJWKH¿IWKGLJLWRIWKH 816GHVLJQDWLRQDQGUHVSHFWLYHO\ZKLOHWKHSUH¿[OHWWHU³(´ for electric furnace steels is designated in the UNS system by PDNLQJWKH¿IWKGLJLW³´7KH6$(VWHHOVZKLFKKDYHDKDUGHQDELOLW\UHTXLUHPHQWLQGLFDWHGE\WKHVXI¿[OHWWHU³+´DUHGHVLJnated by the Hxxxxx series in the UNS system. Carbon and alloy steels not referred to in the SAE system are categorized under the SUH¿[OHWWHU³.´ :KHUH SRVVLEOH WKH ¿UVW OHWWHU LQ WKH V\VWHP GHQRWHV WKH metal group; for instance, “S” designates stainless steels. Of the ¿YHGLJLWVRIWKH816GHVLJQDWLRQIRUVWDLQOHVVVWHHOVWKH¿UVW WKUHH DUH WKH 6$( DOOR\ FODVVL¿FDWLRQ IRU H[DPSOH 6;; 7KH¿QDOWZRGLJLWVDUHHTXLYDOHQWWRWKHYDULRXVPRGL¿FDWLRQV UHSUHVHQWHGE\VXI¿[OHWWHUVLQWKH6$(V\VWHPDVJLYHQLQWKH OLVWRIVXI¿[HVLQ7DEOH7KH816GHVLJQDWLRQVIRUIHUURXV PHWDOVDQGDOOR\VDUHGHVFULEHGLQ7DEOH
SURGXFWV &6$ * * *[ * * VSUD\HG PHWDO FRDWLQJV * DQGZHOGLQJFRQVXPDEOHV &6$:[ Most CSA material standards use SI units, although some are DYDLODEOHLQERWK6,DQG,PSHULDOXQLWV IRUH[DPSOH&6$* * :KHQD&6$VWDQGDUGGHVLJQDWLRQLVIROORZHGE\WKH letter “M,” it uses SI units, and if the letter “M” is not present, it may use both units or use only Imperial units. The type of measurement XQLWVDGRSWHGLQ&6$VWDQGDUGVDUHVSHFL¿FLQGXVWU\GULYHQZLWK some industries moving faster toward the exclusive use of SI units than others, and thus the reason for these differences. As far as practicable, rationalization with relevant ISO VWDQGDUGVKDVEHHQDFKLHYHGLQ&6$*6WHHO:LUH5RSHIRU General Purpose and for Mine Hoisting and for Mine Haulage. 6LPLODUO\WKHHGLWLRQRI&6$=6WHHO/LQH3LSHUHIHUHQFHV UHTXLUHPHQWV IRU ,62 ( RQ UDGLRJUDSKLF image indicators for nondestructive testing: principles and idenWL¿FDWLRQDVZHOODV,62 RQQRQGHVWUXFWLYHWHVWLQJ² radiographic examination of metallic materials by X- and gamma rays—basic rules. Introduction to European (EN) Standard Steel Designation System
7KH &RPLWp (XURSpHQ GH 1RUPDOLVDWLRQ &(1 WKH (XURSHDQ &RPPLWWHH IRU 6WDQGDUGL]DWLRQ ZDV IRXQGHG LQ E\ WKH national standards bodies in the European Economic Community DQG(XURSHDQ)UHH7UDGH$VVRFLDWLRQ ()7$ FRXQWULHV7KH&(1 is a system of formal processes to produce standards, shared principally among: Thirty national members and the representative expertise they assemble from each country; these members vote for and implement (XURSHDQ6WDQGDUGV (1
Canadian Standards Association (CSA)
6HYHQDVVRFLDWHPHPEHUVDQGIRXUDI¿OLDWHV
7KH &DQDGLDQ 6WDQGDUGV $VVRFLDWLRQ &6$ KDV HVWDEOLVKHG PHWDO VWDQGDUGV IRU VWUXFWXUDO VWHHOV &6$ * S LSHOLQHVWHHOV &6$= FRUUXJDWHGVWHHOSLSH * ZLUH
The CEN Management Centre, Brussels.
The CEN works closely with the European Committee for (OHFWURWHFKQLFDO 6WDQGDUGL]DWLRQ &(1(/(& WKH (XURSHDQ
Table 1.8 UNS Designations for Ferrous Metals and Alloys UNS Descriptor
Ferrous Metals
Dxxxxx
Specified mechanical properties of steels
Fxxxxx
Cast irons
Gxxxxx
SAE and former AISI carbon and alloy steels (except tool steels)
Hxxxxx
AISI H-steels
Jxxxxx
Cast steels
Kxxxxx
Miscellaneous steels and ferrous alloys
Sxxxxx
Heat and corrosion-resistant (stainless) steels
Txxxxx
Tool steels
UNS Descriptor Wxxxxx
Welding Filler Metals Welding filler metals, covered and tubular electrodes classified by weld deposit composition
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 1
7HOHFRPPXQLFDWLRQV 6WDQGDUGV ,QVWLWXWH (76, DQG WKH ,62 ,W also has close liaisons with European trade and professional organizations. The principal task of CEN is to prepare and issue European VWDQGDUGV (1 GH¿QHGDVDVHWRIWHFKQLFDOVSHFL¿FDWLRQVHVWDElished and approved in collaboration with the parties concerned in the various member countries of CEN. They are established on the principle of consensus and are adopted by the votes of weighted majority. Adopted standards must be implemented in their entirety as national standards by each member country regardless of the ZD\ LQ ZKLFK WKH QDWLRQDO PHPEHU YRWHG DQG DQ\ FRQÀLFWLQJ national standards must be withdrawn. 7KH LGHQWL¿FDWLRQ RI (XURSHDQ VWDQGDUGV LQ HDFK PHPEHU FRXQWU\EHJLQVZLWKWKHUHIHUHQFHOHWWHUVRIWKHFRXQWU\¶VQDWLRQDO standards body—for example, BS for the British Standards ,QVWLWXWLRQ %6, LQ WKH 8QLWHG .LQJGRP ',1 IRU WKH *HUPDQ ,QVWLWXWHIRU6WDQGDUGL]DWLRQ 'HXWVFKHV,QVWLWXWIU1RUPXQJ 1) IRUWKH)UHQFKQDWLRQDORUJDQL]DWLRQIRUVWDQGDUGL]DWLRQ $VVRFLDWLRQ )UDQoDLVHGH1RUPDOLVDWLRQRU$)125 ,WLVIROORZHGE\WKHLQLWLDOV(1DQGDVHTXHQWLDOQXPEHURIXSWR¿YHGLJLWV)RUH[DPSOH BS EN 10025, DIN EN 10025, or NF EN 10025 are all the same EN standard, which is available in English, French, and German. An EN standard may contain one document, or it may be PDGHXSRIVHYHUDOSDUWV)RUH[DPSOH(13DUWVWKURXJK ZKHUHHDFKSDUWVSHFL¿HVDSDUWLFXODUFKDUDFWHULVWLFRIWKHVWHHO product, may not include the word part in the designation but rather LWLVUHSODFHGZLWKDK\SKHQ HJ(1HWF PHDQLQJ3DUW 7KHSUH¿[³SU´SUHFHGLQJWKH(1GHVLJQDWLRQLGHQWL¿HVWKHGRFument as a draft standard that has not yet been approved, HJSU(1HWF EN 10027 Standard Designation System for Steels
The CEN designation system for steels is standardized in EN 10027, which is published in two parts: Part 1—Steel Names Part 2—Numerical System
The steel name is a combination of letters and numbers as described E\(1:LWKLQWKLVV\VWHPVWHHOQDPHVDUHFODVVL¿HGLQWR two groups. The system is similar in some respects to, but is not LGHQWLFDO ZLWK WKDW RXWOLQHG LQ DQ ,62 WHFKQLFDO UHSRUW ,62 76 ²6WHHOQDPHVEDVHGRQOHWWHUV\PEROV Steel Names
Steel Names Group 1, within EN 10027-1, refers to steels that are designated according to their application and mechanical or physical properties. These have names that are comprised of one or more letters related to the application, followed by a number related to properties. For example, the name for structural steels begins with
Introduction to Comparing World Steel Standards
17
the letter S, line pipe steels begin with the letter L, rail steels begin ZLWKWKHOHWWHU5DQGVWHHOVIRUSUHVVXUHSXUSRVHVEHJLQZLWKWKH OHWWHU3VXFKDV(16WHHO1DPH31+ Steel Names Group 2 is used for steels that are designated according to their chemical composition and are further divided into four subgroups, depending on alloy content. Examples of these Group 2 steel names are: (16WHHO1DPH&U0R (16WHHO1DPH;&U1L Numerical System
EN 10027-2 describes the system used for assigning steel numbers, which are complementary to the steel names described earlier. 7KHVHFRQVLVWRID¿[HGVHWRIGLJLWVDQGKHQFHDUHPRUHVXLWDEOH than the name for data processing purposes. The steel numbers are LQWKHIRUP;;;;ZKHUHWKH³´UHIHUVWRVWHHO7KH¿UVWWZR digits following the “1” represent the steel group number. Examples of steel numbers are as follows: (16WHHO1DPH&U0R6WHHO1XPEHU (16WHHO1DPH;&U1L 6WHHO1XPEHU Former National Standards Superseded by CEN Standards
An increasing number of national European and UK standards are being withdrawn and superseded by EN standards. This transition, IURP ROG WR QHZ VWDQGDUGV KDV PDGH LW LQFUHDVLQJO\ GLI¿FXOW WR compare the superseded national standards with current standards from other nations outside of Europe and the UK, let alone to compare them to the new EN standards. For example, if you are looking XSDIRUPHUQDWLRQDOVWDQGDUGVXFKDV',1LWKDVEHHQVXSHUVHGHGE\(1 Superseded national standards may be replaced by more than one new EN standard, and some may have been partially replaced. 6RDVXSHUVHGHGQDWLRQDOVWDQGDUGFRXOGEHUHSODFHGE\RU more new EN standards, or it may be only partially replaced by these new EN standards. Indexes in this Handbook
One of the easiest ways of using this handbook is to refer to one of the four indexes. If a user is looking for a comparable steel, then the information can be found in at least one of the indexes, which are built around the steel designation systems described previously, namely: Steel Grade/Name Index UNS Number Index Steel Number Index 6SHFL¿FDWLRQ'HVLJQDWLRQ,QGH[
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter
2 CARBON AND ALLOY STEELS FOR GENERAL USE
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
20
Carbon and Alloy Steels for General Use – List of Standards
Chapter 2
ASME Standard ASME SA-29/SA-29M
Steel Bars, Carbon and Alloy, Hot-Wrought, General Requirements for
ASTM Standards ASTM A29/A29M-12e1 ASTM A322-13 ASTM A355-89 (2012) ASTM A576-90b (2012)
General Requirements for Steel Bars, Carbon and Alloy, Hot-Wrought Steel Bars, Alloy, Standard Grades Steel Bars, Alloys, for Nitriding Steel Bars, Carbon, Hot-Wrought, Special Quality
EN Standards EN 10083-2:2006 EN 10083-3:2006 C1:2008 EN 10084:2008 EN 10085:2001 EN 10250-2:1999 C1:2000 EN 10263-3:2001 C1:2001 EN 10263-4:2001 C2:2003 EN 10269:2013
Steels for quenching and tempering – Part 2: Technical delivery conditions for non alloy steels Steels for quenching and tempering – Part 3: Technical delivery conditions for alloy steels Case hardening steels – Technical delivery conditions Nitriding steels – Technical delivery conditions Open die steel forgings for general engineering purposes – Part 2: Non-alloy quality and special steels Steel rod, bars and wire for cold heading and cold extrusion – Part 3: Technical delivery conditions for case hardening steels Steel rod, bars and wire for cold heading and cold extrusion – Part 4: Technical delivery conditions for steels for quenching and tempering Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
ISO Standards ISO 683-1:1987 ISO 683-10:1987 ISO 683-11:1987
Heat-Treatable Steels, Alloy Steels and Free-Cutting Steels – Part 1: Direct-Hardening Unalloyed and Low-Alloyed Wrought Steel in Form of Different Black Products Heat-Treatable Steels, Alloy Steels and Free-Cutting Steels – Part 10: Wrought Nitriding Steels Heat-Treatable Steels, Alloy Steels and Free-Cutting Steels – Part 11: Wrought Case-Hardening Steels
EN ISO Standards EN ISO 16120-2:2011 EN ISO 16120-4:2011
Non-alloy steel wire rod for conversion to wire – Part 2: Specific requirements for general-purpose wire rod Non-alloy steel wire rod for conversion to wire – Part 4: Specific requirements for wire rod for special applications
GB Standards GB/T 699-1999 GB 715-89 GB/T 3077-1999 GB/T 3078-94 GB 5216-85 GB 13791-92
Quality Carbon Structural Steels Hot-Rolled Round Carbon Steel Bars for Standard Parts Alloy Structure Steels Technical Requirements for Quality Structural Steel Cold Drawn Bars Technical Requirements for Structural Steel with Specified Hardenability Bands Cold Drawn Special Shaped Steel Bar
JIS Standards JIS G 4051:2009 JIS G 4053:2008 JIS G 7105:2000
Carbon steels for machine structural use Low-alloyed steels for machine structural use Heat-treatable steels, alloy steels and free-cutting steels – Part 18: Bright products of unalloyed and low alloy steels
SAE Standards SAE J403 JUN14 SAE J404 JAN09
Chemical Compositions of SAE Carbon Steels (Long Products Only) Chemical Compositions of SAE Alloy Steels (Hot Rolled and Cold Finished Bars Only)
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter 2
Carbon and Alloy Steels for General Use
21
2.1 Chemical Composition of Carbon Steels for General Use UNS Steel No. No. G10050 --G10050 ----1.0300 --1.1110
C 0.06 0.06 0.06 0.05
Mn 0.35 0.35 0.30-0.60 0.30-0.50
Si ----0.30 0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.20 0.25 0.05 0.020 0.025 0.10 0.10 0.05
SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 EN ISO 16120-2:2011 EN ISO 16120-4:2011
Grade 1005 Grade 1006 Grade 1006 C7D C5D2
G10050 --G10060 --G10060 ----1.0313 --1.1111
0.06 0.08 0.08 0.05-0.09 0.07
0.35 0.25-0.40 0.25-0.40 0.30-0.60 0.30-0.50
------0.30 0.30
0.040 0.040 0.040 0.035 0.020
0.050 0.050 0.050 0.035 0.025
------0.20 0.10
------0.25 0.10
------0.05 0.05
SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
Grade 1006 Grade 1008 Grade 1008 Grade 1008 C9D C8D2
G10060 --G10080 --G10080 --G10080 ----1.0304 --1.1113
0.08 0.10 0.10 0.10 0.10 0.06-0.10
0.25-0.40 0.30-0.50 0.30-0.50 0.30-0.50 0.30-0.60 0.30-0.50
--------0.30 0.30
0.040 0.040 0.040 0.040 0.035 0.020
0.050 0.050 0.050 0.050 0.035 0.025
--------0.20 0.10
--------0.25 0.10
--------0.05 0.05
GB/T 699-1999
Grade 08 Grade 08F Grade 1008 Grade 1010 Grade 1010 Grade 1010 C10E C10R
--------G10080 --G10100 --G10100 --G10100 ----1.1121 --1.1207
0.05-0.11 0.05-0.11 0.10 0.08-0.13 0.08-0.13 0.08-0.13 0.07-0.13 0.07-0.13
0.35-0.65 0.25-0.50 0.30-0.50 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60
0.17-0.37 0.03 --------0.40 0.40
----0.040 0.040 0.040 0.040 0.035 0.035
0.10 0.10 -------------
0.30 0.30 -------------
-----------------
0.20 0.10
0.25 0.10
0.05 0.05
0.15 0.15 --0.15 0.15 --0.20 0.20 ---
0.30 0.30 --0.30 0.30 --0.20 0.20 ---
-------------------
SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN 10084:2008
EN ISO 16120-2:2011 EN ISO 16120-4:2011
C10D C10D2
GB 13791-92 GB/T 3078-94
Grade 10 Grade 10 Grade 10F Grade 10 Grade 10F Type C 10 Symbol S10C Symbol S09CK Grade 1010
GB/T 699-1999 ISO 683-11:1987 JIS G 4051:2009 SAE J403 JUN14
-----
1.0310 1.1114
0.08-0.13 0.08-0.12
0.30-0.60 0.30-0.50
0.30 0.30
0.035 0.020
----0.050 0.050 0.050 0.050 0.035 0.0200.040 0.035 0.025
----------------G10100
-------------------
0.07-0.13 0.07-0.13 0.07-0.13 0.07-0.13 0.07-0.13 0.07-0.13 0.08-0.13 0.07-0.12 0.08-0.13
0.35-0.65 0.35-0.65 0.50 0.35-0.65 0.25-0.50 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60
0.17-0.37 0.17-0.37 0.03 0.17-0.37 0.07 0.15-0.40 0.15-0.35 0.10-0.35 ---
----0.035 ----0.035 0.030 0.025 0.040
----0.035 ----0.035 0.035 0.025 0.050
Others ----Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 ------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 --------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 ------------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 --Cu 0.25 Cu 0.25 --Cu 0.30; (Ni+Cr) 0.35 Cu 0.25; (Ni+Cr) 0.30 ---
Download From http://bbs.infoeach.com
Designation Grade 1005 Grade 1005 C4D C3D2
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 EN ISO 16120-2:2011 EN ISO 16120-4:2011
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
22
2.1 Chemical Composition of Carbon Steels for General Use (Continued) UNS Steel No. No. G10120 --G10120 --G10120 ----1.0311 --1.1124
C 0.10-0.15 0.10-0.15 0.10-0.15 0.10-0.15 0.10-0.15
Mn 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.50
Si ------0.30 0.30
GB 715-89 JIS G 4051:2009 SAE J403 JUN14 ASME SA-29/SA-29M
Grade BL2 Symbol S12C Grade 1012 Grade 1015 Grade 1016 Grade 1015 Grade 1016 Grade 1015 Grade 1016 C15R
--------G10120 --G10150 --G10160 --G10150 --G10160 --G10150 --G10160 ----1.1140
0.09-0.15 0.10-0.15 0.10-0.15 0.13-0.18 0.13-0.18 0.13-0.18 0.13-0.18 0.13-0.18 0.13-0.18 0.12-0.18
0.25-0.55 0.30-0.60 0.30-0.60 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.30-0.60
0.07 0.15-0.35 --------------0.40
0.040 0.030 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.035
ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN 10084:2008
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.20 0.25 0.05 0.020 0.025 0.10 0.10 0.05
C15E C16E C16R
-------
1.1141 1.1148 1.1208
0.12-0.18 0.12-0.18 0.12-0.18
0.30-0.60 0.60-0.90 0.60-0.90
0.40 0.40 0.40
0.035 0.035 0.035
EN ISO 16120-2:2011 EN ISO 16120-4:2011
C15D C15D2
-----
1.0413 1.1126
0.12-0.17 0.13-0.17
0.30-0.60 0.30-0.50
0.30 0.30
0.035 0.020
GB/T 699-1999
Grade 15 Grade 15F Grade 15Mn Grade 15 Grade 15F Grade 15Mn Grade 15 Type C 16 M2
-----------------
-----------------
0.12-0.18 0.12-0.18 0.12-0.18 0.12-0.18 0.12-0.18 0.12-0.18 0.12-0.18 0.12-0.18
0.35-0.65 0.25-0.50 0.70-1.00 0.35-0.65 0.50 0.70-1.00 0.35-0.65 0.60-0.90
0.17-0.37 0.07 0.17-0.37 0.17-0.37 0.07 0.17-0.37 0.17-0.37 0.15-0.40
--------0.035 ----0.035
Type C 16 E4 Type C 15 M2
-----
-----
0.12-0.18 0.12-0.18
0.60-0.90 0.30-0.60
0.15-0.40 0.15-0.40
0.035 0.035
Type C 15 E4 Symbol S15C Symbol S15CK Grade 1015 Grade 1016
------G10150 G10160
-----------
0.12-0.18 0.13-0.18 0.13-0.18 0.13-0.18 0.13-0.18
0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.60-0.90
0.15-0.40 0.15-0.35 0.15-0.35 -----
0.035 0.030 0.025 0.040 0.040
GB/T 3078-94
GB 13791-92 ISO 683-11:1987
JIS G 4051:2009 SAE J403 JUN14
0.040 0.035 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.0200.040 0.035 0.035 0.0200.040 0.035 0.025
--0.20 -----------------
--0.20 -----------------
---------------------
Others ------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 --Cu 0.30; (Ni+Cr) 0.35 -----------------
-------
-------
-------
-------
0.20 0.10
0.25 0.10
0.05 0.05
--------0.035 ----0.0200.040 0.035 0.0200.040 0.035 0.035 0.025 0.050 0.050
0.25 0.25 0.25 0.25 --0.25 0.25 ---
0.30 0.30 0.30 0.30 --0.30 0.30 ---
-----------------
Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 --Cu 0.25 Cu 0.25 ---
-----
-----
-----
-----
--0.20 0.20 -----
--0.20 0.20 -----
-----------
--Cu 0.30; (Ni+Cr) 0.35 Cu 0.25; (Ni+Cr) 0.30 -----
Download From http://bbs.infoeach.com
Designation Grade 1012 Grade 1012 Grade 1012 C12D C12D2
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
23
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification ASME SA-29/SA-29M
ASTM A29/A29M-12e1
ASTM A576-90b (2012)
JIS G 4051:2009 SAE J403 JUN14 ASME SA-29/SA-29M
ASTM A29/A29M-12e1
ASTM A576-90b (2012)
EN 10083-2:2006 EN 10250-2:1999 C1:2000 EN ISO 16120-2:2011 EN ISO 16120-4:2011 GB/T 699-1999
UNS Steel No. No. G10170 --G10180 --G10190 --G10170 --G10180 --G10190 --G10170 --G10180 --G10190 ----1.0416 --1.1129
C 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.15-0.20 0.16-0.20
Mn 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.30-0.50
Si ------------------0.30 0.30
Symbol S17C Grade 1017 Grade 1018 Grade 1020 Grade 1021 Grade 1022 Grade 1020 Grade 1021 Grade 1022 Grade 1020 Grade 1021 Grade 1022 C22R C22E C22 C20D C20D2
--G10170 G10180 G10200 G10210 G10220 G10200 G10210 G10220 G10200 G10210 G10220 -----------
------------------------1.1149 1.1151 1.0402 1.0414 1.1137
0.15-0.20 0.15-0.20 0.15-0.20 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.17-0.24 0.17-0.24 0.17-0.24 0.18-0.23 0.18-0.23
0.30-0.60 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.60-0.90 0.70-1.00 0.40-0.70 0.40-0.70 0.40-0.70 0.30-0.60 0.30-0.50
0.15-0.35 ----------------------0.40 0.40 0.40 0.30 0.30
0.030 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.030 0.030 0.045 0.035 0.020
0.035 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.020-0.040 0.035 0.045 0.035 0.025
0.20 ----------------------0.40 0.40 0.40 0.20 0.10
0.20 ----------------------0.40 0.40 0.40 0.25 0.10
------------------------0.10 0.10 0.10 0.05 0.05
---------------
---------------
0.17-0.23 0.17-0.23 0.14-0.22 0.17-0.23 0.17-0.24 0.17-0.23 0.17-0.23
0.35-0.65 0.70-1.00 0.30-0.60 0.35-0.65 0.50 0.70-1.00 0.35-0.65
0.17-0.37 0.17-0.37 0.07 0.17-0.37 0.07 0.17-0.37 0.17-0.37
----0.040 --0.035 -----
----0.040 --0.035 -----
0.25 0.25 --0.25 --0.25 0.25
0.30 0.30 --0.30 --0.30 0.30
---------------
Grade 20 Grade 20Mn GB 715-89 Grade BL3 GB/T 3078-94 Grade 20 Grade 20F Grade 20Mn GB 13791-92 Grade 20 Note: This section continued on next page
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.20 0.25 0.05 0.020 0.025 0.10 0.10 0.05
Others ------------------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.30; (Ni+Cr) 0.35 ----------------------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 --Cu 0.25 --Cu 0.25 Cu 0.25
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN ISO 16120-2:2011 EN ISO 16120-4:2011
Designation Grade 1017 Grade 1018 Grade 1019 Grade 1017 Grade 1018 Grade 1019 Grade 1017 Grade 1018 Grade 1019 C18D C18D2
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
24
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification JIS G 4051:2009 SAE J403 JUN14
ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011 GB 13791-92 GB/T 3078-94 GB/T 699-1999 ISO 683-1:1987
JIS G 4051:2009 SAE J403 JUN14
Grade 25 Grade 25 Grade 25Mn Grade 25 Grade 25Mn Grade C 25 Grade C 25 E4 Grade C 25 M2 Symbol S25C Grade 1025 Grade 1026
UNS Steel No. No. --------G10200 --G10210 --G10220 --G10230 --G10230 --G10230 ------G10230 --G10250 --G10260 --G10250 --G10260 --G10250 --G10260 ----1.0415 --1.1139
C 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.20-0.25 0.20-0.25 0.20-0.25 0.20-0.25 0.20-0.25 0.22-0.28 0.22-0.28 0.22-0.28 0.22-0.28 0.22-0.28 0.22-0.28 0.24-0.29 0.24-0.29
Mn 0.30-0.60 0.30-0.60 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.50-0.80 0.50-0.70
Si 0.15-0.35 0.15-0.35 ------------0.15-0.35 --------------0.10-0.30 0.10-0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.030 0.035 0.20 0.20 --0.025 0.025 0.20 0.20 --0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.20 0.20 --0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.030 0.20 0.25 0.05 0.020 0.025 0.10 0.10 0.03
-----------------
-----------------
0.22-0.29 0.22-0.29 0.22-0.29 0.22-0.29 0.22-0.29 0.22-0.29 0.22-0.29 0.22-0.29
0.50-0.80 0.50-0.80 0.70-1.00 0.50-0.80 0.70-1.00 0.40-0.70 0.40-0.70 0.40-0.70
0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
----------0.045 0.035 0.035
--G10250 G10260
-------
0.22-0.28 0.22-0.28 0.22-0.28
0.30-0.60 0.30-0.60 0.60-0.90
0.15-0.35 -----
0.030 0.040 0.040
----------0.045 0.035 0.0200.040 0.035 0.050 0.050
0.25 0.25 0.25 0.25 0.25 -------
0.30 0.30 0.30 0.30 0.30 -------
-----------------
Others Cu 0.30; (Ni+Cr) 0.35 Cu 0.25; (Ni+Cr) 0.30 ------------Cu 0.30; (Ni+Cr) 0.35 --------------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 -------
0.20 -----
0.20 -----
-------
Cu 0.30; (Ni+Cr) 0.35 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) JIS G 4051:2009 SAE J403 JUN14 ASME SA-29/SA-29M
Designation Symbol S20C Symbol S20CK Grade 1020 Grade 1021 Grade 1022 Grade 1023 Grade 1023 Grade 1023 Symbol S22C Grade 1023 Grade 1025 Grade 1026 Grade 1025 Grade 1026 Grade 1025 Grade 1026 C26D C26D2
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
25
2.1 Chemical Composition of Carbon Steels for General Use (Continued) UNS Steel No. No. G10290 --G10290 --G10290 ------G10290 --G10300 --G10300 --G10300 -----------------------------------
C 0.25-0.31 0.25-0.31 0.25-0.31 0.25-0.31 0.25-0.31 0.28-0.34 0.28-0.34 0.28-0.34 0.27-0.34 0.27-0.34 0.27-0.34 0.27-0.34 0.27-0.34 0.27-0.34 0.27-0.34 0.27-0.34
Mn 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.50-0.80 0.60 0.70-1.00 0.50-0.80 0.70-1.00 0.50-0.80 0.50-0.80 0.50-0.80
Si ------0.15-0.35 --------0.17-0.37 0.20 0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
JIS G 4051:2009 SAE J403 JUN14 EN ISO 16120-2:2011 EN ISO 16120-4:2011
Symbol S30C Grade 1030 C32D C32D2
----G10300 ----1.0530 --1.1143
0.27-0.33 0.28-0.34 0.30-0.35 0.30-0.34
0.60-0.90 0.60-0.90 0.50-0.80 0.50-0.70
0.15-0.35 --0.10-0.30 0.10-0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.20 0.20 --0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ----------0.25 0.30 --0.035 0.035 ----------0.25 0.30 ------0.25 0.30 ------0.25 0.30 --0.045 0.045 ------0.035 0.035 ------0.035 0.020------0.040 0.030 0.035 0.20 0.20 --0.040 0.050 ------0.030 0.030 0.20 0.25 0.05 0.020 0.025 0.10 0.10 0.03
JIS G 4051:2009
Symbol S33C
0.30-0.36
0.60-0.90
0.15-0.35
0.030
Download From http://bbs.infoeach.com
GB/T 699-1999 ISO 683-1:1987
---
---
0.035
0.20
0.20
---
Others ------Cu: 0.30; (Ni+Cr) 0.35 --------Cu 0.25 --Cu 0.25 Cu 0.25 Cu 0.25 ------Cu 0.30; (Ni+Cr) 0.35 --Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.30; (Ni+Cr) 0.35
Download From http://bbs.infoeach.com
Designation Grade 1029 Grade 1029 Grade 1029 Symbol S28C Grade 1029 Grade 1030 Grade 1030 Grade 1030 Grade 30 Grade 30 Grade 30Mn Grade 30 Grade 30Mn Grade C 30 Grade C 30 E4 Grade C 30 M2
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) JIS G 4051:2009 SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) GB 13791-92 GB/T 3078-94
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
26
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
EN ISO 16120-4:2011
C35E C35 C36D2
-------
1.1181 1.0501 1.1145
0.32-0.39 0.32-0.39 0.34-0.38
0.50-0.80 0.50-0.80 0.50-0.70
0.40 0.40 0.10-0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.0200.40 0.40 0.10 0.040 0.030 0.035 0.40 0.40 0.10 0.045 0.045 0.40 0.40 0.10 0.020 0.025 0.10 0.10 0.03
Grade 35 Grade 35Mn Grade 35 Grade 35Mn Grade 35 Grade C 35 Grade C 35 E4 Grade C 35 M2
-----------------
-----------------
0.32-0.39 0.32-0.39 0.32-0.39 0.32-0.39 0.32-0.39 0.32-0.39 0.32-0.39 0.32-0.39
0.50-0.80 0.70-1.00 0.60 0.70-1.00 0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80
0.17-0.37 0.17-0.37 0.20 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
----0.035 ----0.045 0.035 0.035
ASTM A29/A29M-12e1
ASTM A576-90b (2012)
Download From http://bbs.infoeach.com
GB/T 699-1999
UNS Steel No. No. G10340 --G10350 --G10370 --G10340 --G10350 --G10370 --G10350 --G10370 ----1.1180
C 0.32-0.38 0.32-0.38 0.32-0.38 0.32-0.38 0.32-0.38 0.32-0.38 0.32-0.38 0.32-0.38 0.32-0.39
Mn 0.50-0.80 0.60-0.90 0.70-1.00 0.50-0.80 0.60-0.90 0.70-1.00 0.60-0.90 0.70-1.00 0.50-0.80
Si ----------------0.40
JIS G 4051:2009 SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
Symbol S35C Grade 1035 Grade 1038 Grade 1038 Grade 1038 C38D C38D2
----G10350 --G10380 --G10380 --G10380 ----1.0516 --1.1150
0.32-0.38 0.32-0.38 0.35-0.42 0.35-0.42 0.35-0.42 0.35-0.40 0.36-0.40
0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.50-0.80 0.50-0.70
0.15-0.35 --------0.10-0.30 0.10-0.30
0.030 0.040 0.040 0.040 0.040 0.030 0.020
----0.035 ----0.045 0.035 0.0200.040 0.035 0.050 0.050 0.050 0.050 0.030 0.025
JIS G 4051:2009 SAE J403 JUN14
Symbol S38C Grade 1038
--G10380
0.35-0.41 0.35-0.42
0.60-0.90 0.60-0.90
0.15-0.35 ---
0.030 0.040
0.035 0.050
GB/T 3078-94 GB 13791-92 ISO 683-1:1987
-----
0.25 0.25 --0.25 0.25 -------
0.30 0.30 --0.30 0.30 -------
-----------------
0.20 --------0.20 0.10
0.20 --------0.25 0.10
----------0.05 0.03
0.20 ---
0.20 ---
-----
Others ----------------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 --Cu 0.25 Cu 0.25 ------Cu 0.30; (Ni+Cr) 0.35 --------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.30; (Ni+Cr) 0.35 ---
Download From http://bbs.infoeach.com
EN 10083-2:2006
Designation Grade 1034 Grade 1035 Grade 1037 Grade 1034 Grade 1035 Grade 1037 Grade 1035 Grade 1037 C35R
Specification ASME SA-29/SA-29M
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
27
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN 10083-2:2006
GB 13791-92 GB/T 3078-94 GB/T 699-1999 ISO 683-1:1987
JIS G 4051:2009 SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011 JIS G 4051:2009 SAE J403 JUN14
UNS Steel No. No. G10390 --G10400 --G10390 --G10400 --G10390 --G10400 ----1.1186 --1.1189
C40 C40D2
----
1.0511 1.1153
0.37-0.44 0.38-0.42
0.50-0.80 0.50-0.70
0.40 0.10-0.30
Grade 40 Grade 40 Grade 40Mn Grade 40 Grade 40Mn Grade C 40 Grade C 40 E4 Grade C 40 M2
-----------------
-----------------
0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44
0.50-0.80 0.60 0.70-1.00 0.50-0.80 0.70-1.00 0.50-0.80 0.50-0.80 0.50-0.80
0.17-0.37 0.20 0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
--0.035 ------0.045 0.035 0.035
C 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44
Mn 0.70-1.00 0.60-0.90 0.70-1.00 0.60-0.90 0.70-1.00 0.60-0.90 0.50-0.80 0.50-0.80
Si ------------0.40 0.40
Symbol S40C Grade 1039 Grade 1040 Grade 1042 Grade 1043 Grade 1042 Grade 1043 Grade 1042 Grade 1043 C42D C42D2
----G10390 --G10400 --G10420 --G10430 --G10420 --G10430 --G10420 --G10430 ----1.0541 --1.1154
0.37-0.43 0.37-0.44 0.37-0.44 0.40-0.47 0.40-0.47 0.40-0.47 0.40-0.47 0.40-0.47 0.40-0.47 0.40-0.45 0.40-0.44
0.60-0.90 0.70-1.00 0.60-0.90 0.60-0.90 0.70-1.00 0.60-0.90 0.70-1.00 0.60-0.90 0.70-1.00 0.50-0.80 0.50-0.70
0.15-0.35 ----------------0.10-0.30 0.10-0.30
0.030 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.030 0.020
--0.035 ------0.045 0.035 0.0200.040 0.035 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.030 0.025
Symbol S43C Grade 1042 Grade 1043
--G10420 G10430
0.40-0.46 0.40-0.47 0.40-0.47
0.60-0.90 0.60-0.90 0.70-1.00
0.15-0.35 -----
0.030 0.040 0.040
0.035 0.050 0.050
-------
0.25 --0.25 0.25 0.25 -------
0.30 --0.30 0.30 0.30 -------
-----------------
0.20 ----------------0.20 0.10
0.20 ----------------0.25 0.10
------------------0.05 0.03
0.20 -----
0.20 -----
-------
Others ------------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 --Cu 0.25 Cu 0.25 Cu 0.25 ------Cu 0.30; (Ni+Cr) 0.35 ----------------Al 0.01; Cu 0.30 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.30; (Ni+Cr) 0.35 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN ISO 16120-4:2011
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 0.40 0.10 0.030 0.0200.40 0.40 0.10 0.040 0.045 0.045 0.40 0.40 0.10 0.020 0.025 0.10 0.10 0.03
Designation Grade 1039 Grade 1040 Grade 1039 Grade 1040 Grade 1039 Grade 1040 C40E C40R
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
28
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification ASME SA-29/SA-29M
ASTM A29/A29M-12e1
ASTM A576-90b (2012)
EN ISO 16120-2:2011 EN ISO 16120-4:2011
GB 13791-92 GB/T 699-1999 GB/T 3078-94 ISO 683-1:1987
JIS G 4051:2009 SAE J403 JUN14
C45 C48D C46D2
-------
1.0503 1.0517 1.1162
0.42-0.50 0.45-0.50 0.44-0.48
0.50-0.80 0.50-0.80 0.50-0.70
0.40 0.10-0.30 0.10-0.30
C48D2
---
1.1164
0.46-0.50
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
Grade 45 Grade 45 Grade 45Mn Grade 45 Grade 45Mn Grade C 45 Grade C 45 E4 Grade C 45 M2
-----------------
-----------------
0.42-0.50 0.42-0.50 0.42-0.50 0.42-0.49 0.42-0.50 0.42-0.50 0.42-0.50 0.42-0.50
0.50-0.80 0.50-0.80 0.70-1.00 0.60 0.70-1.00 0.50-0.80 0.50-0.80 0.50-0.80
0.17-0.37 0.17-0.37 0.17-0.37 0.20 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
------0.035 --0.045 0.035 0.035
0.25 0.25 0.25 --0.25 -------
0.30 0.30 0.30 --0.30 -------
-----------------
----G10440 G10450 G10460
-----------
0.42-0.48 0.45-0.51 0.43-0.50 0.43-0.50 0.43-0.50
0.60-0.90 0.60-0.90 0.30-0.60 0.60-0.90 0.70-1.00
0.15-0.35 0.15-0.35 -------
0.030 0.030 0.040 0.040 0.040
------0.035 --0.045 0.035 0.0200.040 0.035 0.035 0.050 0.050 0.050
(Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 Cu 0.25 --Cu 0.25 -------
0.20 0.20 -------
0.20 0.20 -------
-----------
Cu 0.30; (Ni+Cr) 0.35 Cu 0.30; (Ni+Cr) 0.35 -------
Symbol S45C Symbol S48C Grade 1044 Grade 1045 Grade 1046
UNS Steel No. No. G10440 --G10450 --G10460 --G10440 --G10450 --G10460 --G10440 --G10450 --G10460 ----1.1191 --1.1201
C 0.43-0.50 0.43-0.50 0.43-0.50 0.43-0.50 0.43-0.50 0.43-0.50 0.43-0.50 0.43-0.50 0.43-0.50 0.42-0.50 0.42-0.50
Mn 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.60-0.90 0.70-1.00 0.30-0.60 0.60-0.90 0.70-1.00 0.50-0.80 0.50-0.80
Si ------------------0.40 0.40
Others ------------------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10083-2:2006
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 0.40 0.10 0.030 0.0200.40 0.40 0.10 0.040 0.045 0.045 0.40 0.40 0.10 0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
Designation Grade 1044 Grade 1045 Grade 1046 Grade 1044 Grade 1045 Grade 1046 Grade 1044 Grade 1045 Grade 1046 C45E C45R
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
29
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
C50D C50D2
-----
1.0586 1.1171
0.48-0.53 0.48-0.52
0.50-0.80 0.50-0.70
0.10-0.30 0.10-0.30
GB 13791-92
Grade 50 Grade 50Mn Grade 50 Grade 50Mn Grade 50 Grade 50Mn Grade C 50 Grade C 50 E4 Grade C 50 M2
-------------------
-------------------
0.47-0.55 0.48-0.56 0.47-0.55 0.48-0.56 0.47-0.55 0.48-0.56 0.47-0.55 0.47-0.55 0.47-0.55
0.50-0.80 0.70-1.00 0.50-0.80 0.70-1.00 0.50-0.80 0.70-1.00 0.60-0.90 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
------------0.045 0.035 0.035
0.47-0.53 0.46-0.53 0.48-0.55 0.48-0.55 0.50-0.55 0.50-0.54
0.60-0.90 0.60-0.90 0.60-0.90 0.70-1.00 0.50 0.50-0.70
0.15-0.35 ------0.80 0.10-0.30
0.50-0.56
0.60-0.90
0.15-0.35
ASTM A29/A29M-12e1
ASTM A576-90b (2012)
Download From http://bbs.infoeach.com
EN 10083-2:2006
GB/T 3078-94 GB/T 699-1999 ISO 683-1:1987
JIS G 4051:2009 SAE J403 JUN14
Designation Grade 1049 Grade 1050 Grade 1053 Grade 1049 Grade 1050 Grade 1053 Grade 1049 Grade 1050 Grade 1053 C50E C50R
EN ISO 16120-2:2011 EN ISO 16120-4:2011
Symbol S50C Grade 1049 Grade 1050 Grade 1053 C52D C52D2
JIS G 4051:2009
Symbol S53C
UNS Steel No. No. G10490 --G10500 --G10530 --G10490 --G10500 --G10530 --G10490 --G10500 --G10530 ----1.1206 --1.1241
----G10490 --G10500 --G10530 ----1.0588 --1.1202 ---
---
C 0.46-0.53 0.48-0.55 0.48-0.55 0.46-0.53 0.48-0.55 0.48-0.55 0.46-0.53 0.48-0.55 0.48-0.55 0.47-0.55 0.47-0.55
Mn 0.60-0.90 0.60-0.90 0.70-1.00 0.60-0.90 0.60-0.90 0.70-1.00 0.60-0.90 0.60-0.90 0.70-1.00 0.60-0.90 0.60-0.90
Si ------------------0.40 0.40
0.25 0.25 0.25 0.25 0.25 0.25 -------
0.30 0.30 0.30 0.30 0.30 0.30 -------
-------------------
0.030 0.040 0.040 0.040 0.030 0.020
------------0.045 0.035 0.0200.040 0.035 0.050 0.050 0.050 0.030 0.025
0.20 ------0.15 0.10
0.20 ------0.20 0.10
--------0.05 0.03
0.030
0.035
0.20
0.20
---
Others ------------------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 ------Cu 0.30; (Ni+Cr) 0.35 ------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.30; (Ni+Cr) 0.35
Download From http://bbs.infoeach.com
EN ISO 16120-2:2011 EN ISO 16120-4:2011
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 0.40 0.10 0.030 0.0200.40 0.40 0.10 0.040 0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
Specification ASME SA-29/SA-29M
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
30
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
-------
1.0535 1.0518 1.1220
0.52-0.60 0.53-0.58 0.54-0.58
0.60-0.90 0.50-0.80 0.50-0.70
0.40 0.10-0.30 0.10-0.30
GB/T 3078-94 GB/T 699-1999 ISO 683-1:1987
Grade 55 Grade 55 Grade C 55 Grade C 55 E4 Grade C 55 M2
-----------
-----------
0.52-0.60 0.52-0.60 0.52-0.60 0.52-0.60 0.52-0.60
0.50-0.80 0.50-0.80 0.60-0.90 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
----0.045 0.035 0.035
JIS G 4051:2009 SAE J403 JUN14
Symbol S55C Grade 1055
--G10550
-----
0.52-0.58 0.50-0.60
0.60-0.90 0.60-0.90
0.15-0.35 ---
0.030 0.040
Download From http://bbs.infoeach.com
EN ISO 16120-2:2011 EN ISO 16120-4:2011
Designation Grade 1055 Grade 1055 Grade 1055 C55E C55R
UNS Steel No. No. G10550 --G10550 --G10550 ----1.1203 --1.1209
C 0.50-0.60 0.50-0.60 0.50-0.60 0.52-0.60 0.52-0.60
Mn 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90
Si ------0.40 0.40
----0.045 0.035 0.0200.040 0.035 0.050
Others ------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63
0.25 0.25 -------
0.30 0.30 -------
-----------
(Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 -------
0.20 ---
0.20 ---
-----
Cu 0.30; (Ni+Cr) 0.35 ---
Download From http://bbs.infoeach.com
C55 C56D C56D2
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 0.40 0.10 0.030 0.0200.40 0.40 0.10 0.040 0.045 0.045 0.40 0.40 0.10 0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN 10083-2:2006
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
31
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN 10083-2:2006
EN ISO 16120-4:2011
GB 13791-92 GB/T 3078-94 GB/T 699-1999 ISO 683-1:1987
JIS G 4051:2009 SAE J403 JUN14
C60 C58D C60D C58D2
---------
1.0601 1.0609 1.0610 1.1212
0.57-0.65 0.55-0.60 0.58-0.63 0.56-0.60
0.60-0.90 0.50-0.80 0.50-0.80 0.50-0.70
0.40 0.10-0.30 0.10-0.30 0.10-0.30
C60D2
---
1.1228
0.58-0.62
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
Grade 60 Grade 60 Grade 60Mn Grade 60 Grade 60Mn Grade C 60 Grade C 60 E4 Grade C 60 M2
-----------------
-----------------
0.57-0.65 0.57-0.65 0.57-0.65 0.57-0.65 0.57-0.65 0.57-0.65 0.57-0.65 0.57-0.65
0.50-0.80 0.50-0.80 0.70-1.00 0.50-0.80 0.70-1.00 0.60-0.90 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40 0.10-0.40
----------0.045 0.035 0.035
0.25 0.25 0.25 0.25 0.25 -------
0.30 0.30 0.30 0.30 0.30 -------
-----------------
--G10600
-----
0.55-0.61 0.55-0.65
0.60-0.90 0.60-0.90
0.15-0.35 ---
0.030 0.040
----------0.045 0.035 0.0200.040 0.035 0.050
(Cr+Mo+Ni) 0.63 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 -------
0.20 ---
0.20 ---
-----
Cu 0.30; (Ni+Cr) 0.35 ---
Symbol S58C Grade 1060
UNS Steel No. No. G10590 --G10600 --G10590 --G10600 --G10600 ----1.1221 --1.1223
C 0.55-0.65 0.55-0.65 0.55-0.65 0.55-0.65 0.55-0.65 0.57-0.65 0.57-0.65
Mn 0.50-0.80 0.60-0.90 0.50-0.80 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90
Si ----------0.40 0.40
Others ----------(Cr+Mo+Ni) 0.63 (Cr+Mo+Ni) 0.63
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN ISO 16120-2:2011
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 0.40 0.10 0.030 0.0200.40 0.40 0.10 0.040 0.045 0.045 0.40 0.40 0.10 0.030 0.030 0.15 0.20 0.05 0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
Designation Grade 1059 Grade 1060 Grade 1059 Grade 1060 Grade 1060 C60E C60R
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
32
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 EN ISO 16120-2:2011
EN ISO 16120-4:2011
GB/T 699-1999 SAE J403 JUN14 ASME SA-29/SA-29M
ASTM A29/A29M-12e1
ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
Steel No. --------1.0611 1.0612 1.0613 1.1222
C 0.60-0.70 0.60-0.70 0.60-0.70 0.60-0.70 0.60-0.65 0.63-0.68 0.65-0.70 0.60-0.64
Mn 0.50-0.80 0.60-0.90 0.50-0.80 0.60-0.90 0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.70
Si --------0.10-0.30 0.10-0.30 0.10-0.30 0.10-0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.030 0.15 0.20 0.05 0.030 0.030 0.15 0.20 0.05 0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
C68D2
---
1.1232
0.66-0.70
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
C66D2
---
1.1236
0.64-0.68
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
----------------G10650 --G10690 --G10700 ------G10690 --G10700 ------G10700 ----1.0615 --1.0617 --1.1242
0.62-0.70 0.62-0.70 0.62-0.70 0.62-0.70 0.60-0.70 0.65-0.75 0.65-0.75 0.65-0.70 0.65-0.75 0.65-0.75 0.65-0.70 0.65-0.75 0.68-0.73 0.70-0.75 0.70-0.74
0.50-0.80 0.90-1.20 0.50-0.80 0.90-1.20 0.60-0.90 0.40-0.70 0.60-0.90 0.75-1.05 0.40-0.70 0.60-0.90 0.75-1.05 0.60-0.90 0.50-0.80 0.50-0.80 0.50-0.70
0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 ----------------0.10-0.30 0.10-0.30 0.10-0.30
--------0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.030 0.030 0.020
--------0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.050 0.030 0.030 0.025
0.25 0.25 0.25 0.25 ----------------0.15 0.15 0.10
0.30 0.30 0.30 0.30 ----------------0.20 0.20 0.10
------------------------0.05 0.05 0.03
Grade 65 Grade 65Mn Grade 65 Grade 65Mn Grade 1065 Grade 1069 Grade 1070 Grade 1071 Grade 1069 Grade 1070 Grade 1071 Grade 1070 C70D C72D C72D2 C70D2
GB/T 699-1999 SAE J403 JUN14
Grade 70 Grade 70Mn Grade 1070
---
1.1251
0.68-0.72
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
----G10700
-------
0.67-0.75 0.67-0.75 0.65-0.75
0.50-0.80 0.90-1.20 0.60-0.90
0.17-0.37 0.17-0.37 ---
----0.040
----0.050
0.25 0.25 ---
0.30 0.30 ---
-------
Others --------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 Cu 0.25 Cu 0.25 ----------------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 Cu 0.25 ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 3078-94
UNS No. G10640 G10650 G10640 G10650 ---------
Designation Grade 1064 Grade 1065 Grade 1064 Grade 1065 C62D C66D C68D C62D2
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
33
2.1 Chemical Composition of Carbon Steels for General Use (Continued)
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 EN ISO 16120-2:2011 EN ISO 16120-4:2011
ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
C76D2 Grade 75 Grade 1074 Grade 1075 Grade 1078 Grade 1078 Grade 1078 C80D C82D C80D2 C82D2
UNS No. G10740 G10750 G10740 G10750 -------
Steel No. --------1.0614 1.0620 1.1252
C 0.70-0.80 0.70-0.80 0.70-0.80 0.70-0.80 0.73-0.78 0.75-0.80 0.76-0.80
Mn 0.50-0.80 0.40-0.70 0.50-0.80 0.40-0.70 0.50-0.80 0.50-0.80 0.50-0.70
Si --------0.10-0.30 0.10-0.30 0.10-0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.030 0.15 0.20 0.05 0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
---
1.1253
0.74-0.78
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
----G10740 --G10750 --G10780 --G10780 --G10780 ----1.0622 --1.0626 --1.1255
0.72-0.80 0.70-0.80 0.70-0.80 0.72-0.85 0.72-0.85 0.72-0.85 0.78-0.83 0.80-0.85 0.78-0.82
0.50-0.80 0.50-0.80 0.40-0.70 0.30-0.60 0.30-0.60 0.30-0.60 0.50-0.80 0.50-0.80 0.50-0.70
0.17-0.37 ----------0.10-0.30 0.10-0.30 0.10-0.30
--0.040 0.040 0.040 0.040 0.040 0.030 0.030 0.020
--0.050 0.050 0.050 0.050 0.050 0.030 0.030 0.025
0.25 ----------0.15 0.15 0.10
0.30 ----------0.20 0.20 0.10
------------0.05 0.05 0.03
1.1262
0.80-0.84
0.50-0.70
0.10-0.30
0.020
0.025
0.10
0.10
0.03
---
GB/T 699-1999 SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
Grade 80 Grade 1078 Grade 1080 Grade 1080 Grade 1080 C86D C86D2
----G10780 --G10800 --G10800 --G10800 ----1.0616 --1.1265
0.77-0.85 0.72-0.85 0.75-0.88 0.75-0.88 0.75-0.88 0.83-0.88 0.84-0.88
0.50-0.80 0.30-0.60 0.60-0.90 0.60-0.90 0.60-0.90 0.50-0.80 0.50-0.70
0.17-0.37 --------0.10-0.30 0.10-0.30
--0.040 0.040 0.040 0.040 0.030 0.020
--0.050 0.050 0.050 0.050 0.030 0.025
0.25 --------0.15 0.10
0.30 --------0.20 0.10
----------0.05 0.03
SAE J403 JUN14 ASME SA-29/SA-29M
Grade 1080 Grade 1084 Grade 1086 Grade 1084 Grade 1086 Grade 1084 C88D C88D2
G10800 --G10840 --G10860 --G10840 --G10860 --G10840 ----1.0628 --1.0628
0.75-0.88 0.80-0.93 0.80-0.93 0.80-0.93 0.80-0.93 0.80-0.93 0.85-0.90 0.86-0.90
0.60-0.90 0.60-0.90 0.30-0.50 0.60-0.90 0.30-0.50 0.60-0.90 0.50-0.80 0.50-0.70
------------0.10-0.30 0.10-0.30
0.040 0.040 0.040 0.040 0.040 0.040 0.030 0.020
0.050 0.050 0.050 0.050 0.050 0.050 0.030 0.025
------------0.15 0.10
------------0.20 0.10
------------0.05 0.03
Grade 85 Grade 1084 Grade 1086
--G10840 G10860
0.82-0.90 0.80-0.93 0.80-0.93
0.50-0.80 0.60-0.90 0.30-0.50
0.17-0.37 -----
--0.040 0.040
--0.050 0.050
0.25 -----
0.30 -----
-------
ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011 GB/T 699-1999 SAE J403 JUN14
-------
Others --------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 ----------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 --------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 ------------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 Cu 0.25 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 699-1999 SAE J403 JUN14
Designation Grade 1074 Grade 1075 Grade 1074 Grade 1075 C76D C78D C78D2
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
34
2.1 Chemical Composition of Carbon Steels for General Use (Continued) UNS Steel No. No. G10900 --G10900 --G10900 ----1.0618 --1.1282
C 0.85-0.98 0.85-0.98 0.85-0.98 0.90-0.95 0.90-0.94
Mn 0.60-0.90 0.60-0.90 0.60-0.90 0.50-0.80 0.50-0.70
Si ------0.10-0.30 0.10-0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.030 0.15 0.20 0.05 0.020 0.025 0.10 0.10 0.03
SAE J403 JUN14 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-4:2011
Grade 1090 Grade 1095 Grade 1095 Grade 1095 C98D2
G10900 --G10950 --G10950 --G10950 ----1.1283
0.85-0.98 0.90-1.03 0.90-1.03 0.90-1.03 0.96-1.00
0.60-0.90 0.30-0.50 0.30-0.50 0.30-0.50 0.50-0.70
--------0.10-0.30
0.040 0.040 0.040 0.040 0.020
0.050 0.050 0.050 0.050 0.025
--------0.10
--------0.10
--------0.03
SAE J403 JUN14
Grade 1095
G10950
0.90-1.03
0.30-0.50
---
0.040
0.050
---
---
---
Mn 1.10-1.40 1.10-1.40 1.35-1.65 1.10-1.40 1.35-1.65 1.40-1.80 1.40-1.80 1.30-1.65 1.20-1.50 1.20-1.50 1.10-1.40 1.35-1.65 1.30-1.65 1.40-1.80 1.30-1.65 1.20-1.50 1.20-1.50 1.20-1.50 1.40-1.80 1.40-1.80 1.20-1.50 1.20-1.50
Si ----------0.17-0.37 0.17-0.37 0.10-0.40 0.15-0.35 0.15-0.35 ----0.40 0.17-0.37 0.10-0.40 ------0.17-0.37 0.17-0.37 0.15-0.35 ---
---
Others ------Al 0.01; Cu 0.25; (Cu+Sn) 0.25 Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 --------Al 0.01; Cu 0.15; N 0.007; (Cu+Ni+Cr) 0.30; (Cu+Sn) 0.15 ---
2.2 Chemical Composition of High Manganese Carbon Steels for General Use
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) GB/T 3077-1999 GB/T 3078-94 ISO 683-1:1987 JIS G 4053:2008 SAE J403 JUN14 EN 10083-2:2006 GB/T 3077-1999 ISO 683-1:1987 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) GB/T 3077-1999 GB/T 3078-94 JIS G 4053:2008 SAE J403 JUN14
Designation Grade 1522 Grade 1522 Grade 1524 Grade 1522 Grade 1524 Grade 20Mn2 Grade 20Mn2 Grade 22 Mn 6 Symbol SMn420 Symbol SMnC420 Grade 1522 Grade 1524 28Mn6 Grade 30Mn2 Grade 28 Mn 6 Grade 1536 Grade 1536 Grade 1536 Grade 35Mn2 Grade 35Mn2 Symbol SMn433 Grade 1536
UNS Steel No. No. G15220 --G15220 --G15240 --G15220 --G15240 ----------------------G15220 --G15240 ----1.1170 --------G15360 --G15360 --G15360 --------------G15360 ---
C 0.18-0.24 0.18-0.24 0.19-0.25 0.18-0.24 0.19-0.25 0.17-0.24 0.17-0.24 0.19-0.26 0.17-0.23 0.17-0.23 0.18-0.24 0.19-0.25 0.25-0.32 0.27-0.34 0.25-0.32 0.30-0.37 0.30-0.37 0.30-0.37 0.32-0.39 0.32-0.39 0.30-0.36 0.30-0.37
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.035 0.035 ------0.030 0.030 0.35 0.25 --0.030 0.030 0.35-0.70 0.25 --0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 0.40 0.10 0.035 0.035 0.30 0.30 0.15 0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.030 0.030 0.35 0.25 --0.040 0.050 -------
Others ----------Cu 0.30 Cu 0.30 --Cu 0.30 Cu 0.30 ----(Cr+Mo+Ni) 0.63 Cu 0.30 --------Cu 0.30 Cu 0.30 Cu 0.30 ---
Download From http://bbs.infoeach.com
Designation Grade 1090 Grade 1090 Grade 1090 C92D C92D2
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) EN ISO 16120-2:2011 EN ISO 16120-4:2011
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
35
2.2 Chemical Composition of High Manganese Carbon Steels for General Use (Continued)
Designation Grade 1541 Grade 1541 Grade 1541 Grade 40Mn2 Grade 40Mn2 Grade 36 Mn 6 Symbol SMn438 Grade 1541 Grade 42 Mn 6 Symbol SMn443 Grade 1547 Grade 1547 Grade 45Mn2 Grade 45Mn2 Grade 1547 Grade 1552 Grade 1552 Grade 50Mn2 Grade 50Mn2 Grade 1552
UNS Steel No. No. G15410 --G15410 --G15410 ------------------G15410 ----------G15470 --G15470 ----------G15470 --G15520 --G15520 ----------G15520 ---
C 0.36-0.44 0.36-0.44 0.36-0.44 0.37-0.44 0.37-0.44 0.33-0.40 0.35-0.41 0.36-0.44 0.39-0.46 0.40-0.46 0.43-0.51 0.43-0.51 0.42-0.49 0.42-0.49 0.43-0.51 0.47-0.55 0.47-0.55 0.47-0.55 0.47-0.55 0.47-0.55
Mn 1.35-1.65 1.35-1.65 1.35-1.65 1.40-1.80 1.40-1.80 1.30-1.65 1.35-1.65 1.35-1.65 1.30-1.65 1.35-1.65 1.35-1.65 1.35-1.65 1.40-1.80 1.40-1.80 1.35-1.65 1.20-1.50 1.20-1.50 1.40-1.80 1.40-1.80 1.20-1.50
Si ------0.17-0.37 0.17-0.37 0.10-0.40 0.15-0.35 --0.10-0.40 0.15-0.35 ----0.17-0.37 0.17-0.37 ------0.17-0.37 0.17-0.37 ---
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.035 0.035 ------0.030 0.030 0.35 0.25 --0.040 0.050 ------0.035 0.035 ------0.030 0.030 0.35 0.25 --0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.040 0.050 -------
Others ------Cu 0.30 Cu 0.30 --Cu 0.30 ----Cu 0.30 ----Cu 0.30 Cu 0.30 ------Cu 0.30 Cu 0.30 ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A576-90b (2012) GB/T 3077-1999 GB/T 3078-94 ISO 683-1:1987 JIS G 4053:2008 SAE J403 JUN14 ISO 683-1:1987 JIS G 4053:2008 ASTM A29/A29M-12e1 ASTM A576-90b (2012) GB/T 3077-1999 GB/T 3078-94 SAE J403 JUN14 ASTM A29/A29M-12e1 ASTM A576-90b (2012) GB/T 3077-1999 GB/T 3078-94 SAE J403 JUN14
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
36
2.3 Chemical Composition of Alloy Steels for General Use 2.3.1 Chromium (Cr) Steels
C 0.14-0.20
Mn 0.60-0.90
Si 0.40
17Cr3 Grade 15Cr Grade 15CrA Grade 15CrA Symbol SCr415 Grade 5120 Grade 5120 Grade 5120 Grade 20Cr Grade 20CrH Grade 20Cr Grade 20Cr Type 20 CrS 4
--1.7016 ----------------G51200 --G51200 --G51200 -----------------------
0.14-0.20 0.12-0.18 0.12-0.17 0.12-0.17 0.13-0.18 0.17-0.22 0.17-0.22 0.17-0.22 0.18-0.24 0.17-0.23 0.18-0.24 0.18-0.24 0.17-0.23
0.60-0.90 0.40-0.70 0.40-0.70 0.40-0.70 0.60-0.90 0.70-0.90 0.70-0.90 0.70-0.90 0.50-0.80 0.50-0.85 0.50-0.80 0.50-0.80 0.60-0.90
0.40 0.17-0.37 0.17-0.37 0.17-0.37 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.15-0.40
JIS G 4053:2008 SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10084:2008
Type 20 Cr 4 Symbol SCr420 Grade 5120 Grade 5130 Grade 5130 Grade 5130 28Cr4 28CrS4
--------G51200 --G51300 --G51300 --G51300 ----1.7030 --1.7036
0.17-0.23 0.18-0.23 0.17-0.22 0.28-0.33 0.28-0.33 0.28-0.33 0.24-0.31 0.24-0.31
0.60-0.90 0.60-0.90 0.70-0.90 0.70-0.90 0.70-0.90 0.70-0.90 0.60-0.90 0.60-0.90
0.15-0.40 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
GB/T 3077-1999 GB/T 3078-94 JIS G 4053:2008 SAE J404 JAN09
Grade 30Cr Grade 30Cr Symbol SCr430 Grade 5130
------G51300
0.27-0.34 0.27-0.34 0.28-0.33 0.28-0.33
0.50-0.80 0.50-0.80 0.60-0.90 0.70-0.90
0.17-0.37 0.17-0.37 0.15-0.35 0.15-0.35
GB/T 3077-1999
Download From http://bbs.infoeach.com
GB/T 3078-94 JIS G 4053:2008 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 GB 13791-92 GB 5216-85 GB/T 3077-1999 GB/T 3078-94 ISO 683-11:1987
Designation 17CrS3
UNS No. ---
---------
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.0200.70-1.00 ----0.040 0.025 0.035 0.70-1.00 ----0.035 0.035 0.70-1.00 0.30 0.15 0.025 0.025 0.70-1.00 0.30 0.10 0.025 0.025 0.70-1.00 0.30 0.10 0.030 0.030 0.90-1.20 0.25 --0.035 0.040 0.70-0.90 ----0.035 0.040 0.70-0.90 ----0.035 0.040 0.70-0.90 ----0.035 0.035 0.70-1.00 0.30 0.15 0.035 0.035 0.70-1.10 0.30 --0.035 0.035 0.70-1.00 0.30 0.15 0.035 0.035 0.70-1.00 0.30 0.15 0.035 0.0200.90-1.20 ----0.040 0.035 0.035 0.90-1.20 ----0.030 0.030 0.90-1.20 0.25 --0.030 0.040 0.70-0.90 0.25 0.06 0.035 0.040 0.80-1.10 ----0.035 0.040 0.80-1.10 ----0.035 0.040 0.80-1.10 ----0.025 0.035 0.90-1.20 ----0.025 0.0200.90-1.20 ----0.040 0.035 0.035 0.80-1.10 0.30 0.15 0.035 0.035 0.80-1.10 0.30 0.15 0.030 0.030 0.90-1.20 0.25 --0.030 0.040 0.80-1.10 0.25 0.06
Others ----Cu 0.30 Cu 0.25 Cu 0.25 Cu 0.30 ------Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.30 ----Cu 0.30 Cu 0.35 ----------Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.35
Download From http://bbs.infoeach.com
Steel No. 1.7014
Specification EN 10084:2008
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
37
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.1 Chromium (Cr) Steels (Continued) UNS Steel No. No. G51320 --G51320 --G51320 ----1.7033 --1.7037
ISO 683-1:1987
Grade 34 Cr 4 Grade 34 CrS 4
SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008
Grade 5132 Grade 5135 Grade 5135 Grade 5135 37Cr4 37CrS4
GB/T 3077-1999 GB/T 3078-94 ISO 683-1:1987
Grade 35Cr Grade 35Cr Grade 37 Cr 4 Grade 37 CrS 4
JIS G 4053:2008 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008
Symbol SCr435 Grade 5140 Grade 5140 Grade 5140 41Cr4 41CrS4
GB/T 3077-1999 GB/T 3078-94 GB 5216-85 GB 13791-92 ISO 683-1:1987
Grade 40Cr Grade 40Cr Grade 40CrH Grade 40Cr Grade 41 Cr 4 Grade 41 CrS 4
-------------
JIS G 4053:2008 SAE J404 JAN09
Symbol SCr440 Grade 5140
--G51400
-----
C 0.30-0.35 0.30-0.35 0.30-0.35 0.30-0.37 0.30-0.37
Mn 0.60-0.80 0.60-0.80 0.60-0.80 0.60-0.90 0.60-0.90
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
0.30-0.37 0.30-0.37
0.60-0.90 0.60-0.90
0.10-0.40 0.10-0.40
0.30-0.35 0.33-0.38 0.33-0.38 0.33-0.38 0.34-0.41 0.34-0.41
0.60-0.80 0.60-0.80 0.60-0.80 0.60-0.80 0.60-0.90 0.60-0.90
0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
0.32-0.39 0.32-0.39 0.34-0.41 0.34-0.41
0.50-0.80 0.50-0.80 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40
0.33-0.38 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.45 0.38-0.45
0.60-0.90 0.70-0.90 0.70-0.90 0.70-0.90 0.60-0.90 0.60-0.90
0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
-------------
0.37-0.44 0.34-0.42 0.37-0.44 0.37-0.44 0.38-0.45 0.38-0.45
0.50-0.80 0.50-0.80 0.50-0.85 0.50-0.80 0.60-0.90 0.60-0.90
0.17-0.37 0.20 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40
-----
0.38-0.43 0.38-0.43
0.60-0.90 0.70-0.90
0.15-0.35 0.15-0.35
-----
G51320 --G51350 --G51350 --G51350 ----1.7034 --1.7038 ---------
---------
----G51400 --G51400 --G51400 ----1.7035 --1.7039
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.75-1.00 ----0.035 0.040 0.75-1.00 ----0.035 0.040 0.75-1.00 ----0.025 0.035 0.90-1.20 ----0.025 0.0200.90-1.20 ----0.040 0.035 0.035 0.90-1.20 ----0.035 0.0200.90-1.20 ----0.040 0.030 0.040 0.75-1.00 0.25 0.06 0.035 0.040 0.80-1.05 ----0.035 0.040 0.80-1.05 ----0.035 0.040 0.80-1.05 ----0.025 0.035 0.90-1.20 ----0.025 0.0200.90-1.20 ----0.040 0.035 0.035 0.80-1.10 0.30 0.15 0.035 0.035 0.80-1.10 0.30 0.15 0.035 0.035 0.90-1.20 ----0.035 0.0200.90-1.20 ----0.040 0.030 0.030 0.90-1.20 0.25 --0.035 0.040 0.70-0.90 ----0.035 0.040 0.70-0.90 ----0.035 0.040 0.70-0.90 ----0.025 0.035 0.90-1.20 ----0.025 0.0200.90-1.20 ----0.040 0.035 0.035 0.80-1.10 0.30 0.15 0.035 0.035 0.80-1.10 ----0.035 0.035 0.70-1.10 0.30 --0.035 0.035 0.80-1.10 0.30 0.15 0.035 0.035 0.90-1.20 ----0.035 0.0200.90-1.20 ----0.040 0.030 0.030 0.90-1.20 0.25 --0.030 0.040 0.70-0.90 0.25 0.06
Others --------------Cu 0.35 ----------Cu 0.30 Cu 0.30 ----Cu 0.30 -----------
Download From http://bbs.infoeach.com
Designation Grade 5132 Grade 5132 Grade 5132 34Cr4 34CrS4
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008
Cu 0.30 --Cu 0.30 Cu 0.30 ----Cu 0.30 Cu 0.35
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
38
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.1 Chromium (Cr) Steels (Continued)
Designation Grade 5145 Grade 5145 Grade 45CrH Grade 45Cr Grade 45Cr Symbol SCr445 Grade 5150 Grade 5150 Grade 50Cr Grade 5150
UNS Steel No. No. G51450 --G51450 ------------------G51500 --G51500 ------G51500 ---
C 0.43-0.48 0.43-0.48 0.42-0.49 0.42-0.49 0.42-0.49 0.43-0.48 0.48-0.53 0.48-0.53 0.47-0.54 0.48-0.53
Mn 0.70-0.90 0.70-0.90 0.50-0.85 0.50-0.80 0.50-0.80 0.60-0.90 0.70-0.90 0.70-0.90 0.50-0.80 0.70-0.90
Si 0.15-0.35 0.15-0.35 0.17-0.37 0.17-0.37 0.17-0.37 0.15-0.35 0.15-0.35 0.15-0.35 0.17-0.37 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.70-0.90 ----0.035 0.040 0.70-0.90 ----0.035 0.035 0.70-1.10 0.30 --0.035 0.035 0.80-1.10 0.30 0.15 0.035 0.035 0.80-1.10 0.30 0.15 0.030 0.030 0.90-1.20 0.25 --0.035 0.040 0.70-0.90 ----0.035 0.040 0.70-0.90 ----0.035 0.035 0.80-1.10 0.30 0.15 0.030 0.040 0.70-0.90 0.25 0.06
Others ----Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.30 ----Cu 0.30 Cu 0.35
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 GB 5216-85 GB/T 3077-1999 GB/T 3078-94 JIS G 4053:2008 ASTM A29/A29M-12e1 ASTM A322-13 GB/T 3077-1999 SAE J404 JAN09
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
39
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.2 Chromium-Molybdenum (Cr-Mo) Steels
Specification ASME SA-29/SA-29M
ASTM A29/A29M-12e1
EN 10084:2008
GB/T 3077-1999 GB/T 3078-94 GB 5216-85 GB 13791-92 ISO 683-11:1987
JIS G 4053:2008
SAE J404 JAN09
UNS Steel No. No. G41180 --G41200 --G41210 --G41180 --G41200 --G41210 --G41180 --G41200 --G41210 ----1.7243 --1.7244
C 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.18-0.23 0.15-0.21 0.15-0.21
Mn 0.70-0.90 0.90-1.20 0.75-1.00 0.70-0.90 0.90-1.20 0.75-1.00 0.70-0.90 0.90-1.20 0.75- 1.00 0.60-0.90 0.60-0.90
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
20MoCrS3
---
1.7319
0.17-0.23
0.60-0.90
0.40
20MoCr3 20MoCr4 20MoCrS4
-------
1.7320 1.7321 1.7323
0.17-0.23 0.17-0.23 0.17-0.23
0.60-0.90 0.70-1.00 0.70-1.00
0.40 0.40 0.40
22CrMoS3-5
---
1.7333
0.19-0.24
0.70-1.00
0.40
Grade 20CrMnMo Grade 20CrMo Grade 20CrMnMo Grade 20CrMo Grade 20CrMnMoH Grade 20CrMo(A) Type 18 CrMo 4 Type 18 CrMoS 4
-----------------
-----------------
0.17-0.23 0.17-0.24 0.17-0.23 0.17-0.24 0.17-0.23 0.17-0.24 0.15-0.21 0.15-0.21
0.90-1.20 0.40-0.70 0.90-1.20 0.40-0.70 0.85-1.20 0.40-0.70 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.17-0.37 0.15-0.40 0.15-0.40
--------G41180 G41200
-------------
0.16-0.21 0.18-0.23 0.17-0.23 0.20-0.25 0.18-0.23 0.18-0.23
0.60-0.90 0.60-0.90 0.70-1.00 0.60-0.90 0.70-0.90 0.90-1.20
0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35
Symbol SCM418 Symbol SCM420 Symbol SCM421 Symbol SCM822 Grade 4118 Grade 4120
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.40-0.60 --0.08-0.15 0.035 0.040 0.40-0.60 --0.13-0.20 0.035 0.040 0.45-0.65 --0.20-0.30 0.035 0.040 0.40-0.60 --0.08-0.15 0.035 0.040 0.40-0.60 --0.13-0.20 0.035 0.040 0.45-0.65 --0.20-0.30 0.035 0.040 0.40-0.60 --0.08-0.15 0.035 0.040 0.40-0.60 --0.13-0.20 0.035 0.040 0.45-0.65 --0.20-0.30 0.025 0.035 0.90-1.20 --0.15-0.25 0.025 0.0200.90-1.20 --0.15-0.25 0.040 0.025 0.0200.40-0.70 --0.30-0.40 0.040 0.025 0.035 0.40-0.70 --0.30-0.40 0.025 0.035 0.30-0.60 --0.40-0.50 0.025 0.0200.30-0.60 --0.40-0.50 0.040 0.025 0.0200.70-1.00 --0.40-0.50 0.040 0.035 0.035 1.10-1.40 0.30 0.20-0.30 0.035 0.035 0.80-1.10 0.30 0.15-0.25 0.035 0.035 1.10-1.40 0.30 0.20-0.30 0.035 0.035 0.80-1.10 0.30 0.15-0.25 0.035 0.035 1.05-1.40 0.30 0.20-0.30 0.025 0.025 0.80-1.10 0.30 0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.25 0.035 0.0200.90-1.20 --0.15-0.25 0.040 0.030 0.030 0.90-1.20 0.25 0.15-0.25 0.030 0.030 0.90-1.20 0.25 0.15-0.25 0.030 0.030 0.90-1.20 0.25 0.15-0.25 0.030 0.030 0.90-1.20 0.25 0.35-0.45 0.030 0.040 0.40-0.60 0.25 0.08-0.15 0.030 0.040 0.40-0.60 0.25 0.13-0.20
Others --------------------------------Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.25 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A322-13
Designation Grade 4118 Grade 4120 Grade 4121 Grade 4118 Grade 4120 Grade 4121 Grade 4118 Grade 4120 Grade 4121 18CrMo4 18CrMoS4
Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.35 Cu 0.35
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
40
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.2 Chromium-Molybdenum (Cr-Mo) Steels (Continued)
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008
GB/T 3078-94 ISO 683-1:1987
JIS G 4053:2008
SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008
25CrMo4 Grade 30CrMo Grade 30CrMoA Grade 30CrMo Grade 25 CrMo 4 Grade 25 CrMoS 4 Symbol SCM425 Symbol SCM430 Symbol SCM432 Grade 4130 Grade 4137 Grade 4137 Grade 4137 34CrMo4 34CrMoS4
GB 13791-92 GB/T 3077-1999 GB/T 3078-94 ISO 683-1:1987
Grade 35CrMo(A) Grade 35CrMo Grade 35CrMo Grade 34 CrMo 4 Grade 34 CrMoS 4
JIS G 4053:2008 SAE J404 JAN09
Symbol SCM435 Grade 4137
UNS Steel No. No. G41300 --G41300 --G41300 ----1.7213
C 0.28-0.33 0.28-0.33 0.28-0.33 0.22-0.29
Mn 0.40-0.60 0.40-0.60 0.40-0.60 0.60-0.90
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.40
1.7218 -----------
0.22-0.29 0.26-0.34 0.26-0.33 0.26-0.34 0.22-0.29 0.22-0.29
0.60-0.90 0.40-0.70 0.40-0.70 0.40-0.70 0.60-0.90 0.60-0.90
0.40 0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40
------------G41300 --G41370 --G41370 --G41370 ----1.7220 --1.7226
0.23-0.28 0.28-0.33 0.27-0.37 0.28-0.33 0.35-0.40 0.35-0.40 0.35-0.40 0.30-0.37 0.30-0.37
0.60-0.90 0.60-0.90 0.30-0.60 0.40-0.60 0.70-0.90 0.70-0.90 0.70-0.90 0.60-0.90 0.60-0.90
0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
-------------
-----------
-----------
0.32-0.40 0.32-0.40 0.32-0.40 0.30-0.37 0.30-0.37
0.40-0.70 0.40-0.70 0.40-0.70 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40
--G41370
-----
0.33-0.38 0.35-0.40
0.60-0.90 0.70-0.90
0.15-0.35 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.025 0.0200.90-1.20 --0.15-0.30 0.040 0.025 0.035 0.90-1.20 --0.15-0.30 0.035 0.035 0.80-1.10 0.30 0.15-0.25 0.025 0.025 0.80-1.10 0.30 0.15-0.25 0.035 0.035 0.80-1.10 0.30 0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.30 0.035 0.0200.90-1.20 --0.15-0.30 0.040 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.030 1.00-1.50 0.25 0.15-0.30 0.030 0.040 0.80-1.10 0.25 0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.025 0.035 0.90-1.20 --0.15-0.30 0.025 0.0200.90-1.20 --0.15-0.30 0.040 0.025 0.025 0.80-1.10 0.30 0.15-0.25 0.035 0.035 0.80-1.10 0.30 0.15-0.25 0.035 0.035 0.80-1.10 0.30 0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.30 0.035 0.0200.90-1.20 --0.15-0.30 0.040 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.040 0.80-1.10 0.25 0.15-0.25
Others ----------Cu 0.30 Cu 0.25 Cu 0.30 ----Cu 0.30 Cu 0.30 Cu 0.30 Cu 0.35 ----------Cu 0.25 Cu 0.30 Cu 0.30 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 3077-1999
Designation Grade 4130 Grade 4130 Grade 4130 25CrMoS4
Cu 0.30 Cu 0.35
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
41
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.2 Chromium-Molybdenum (Cr-Mo) Steels (Continued)
GB/T 3077-1999 GB/T 3078-94 ISO 683-1:1987
Grade 42CrMo Grade 42CrMo Grade 42 CrMo 4 Grade 42 CrMoS 4
JIS G 4053:2008 SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 JIS G 4053:2008 SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008 ISO 683-1:1987 JIS G 7105:2000 SAE J404 JAN09
Symbol SCM440 Grade 4140 Grade 4145 Grade 4145 Grade 4145 Symbol SCM445 Grade 4145 Grade 4150 Grade 4150 Grade 4150 50CrMo4 Grade 50 CrMo 4 Type 50CrMo4 Grade 4150
UNS Steel No. No. G41400 --G41400 --G41400 ----1.7225 --1.7227 ---------
---------
----G41400 --G41450 --G41450 --G41450 ------G41450 --G41500 --G41500 --G41500 ----1.7228 --------G41500 ---
C 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.45 0.38-0.45
Mn 0.75-1.00 0.75-1.00 0.75-1.00 0.60-0.90 0.60-0.90
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
0.38-0.45 0.38-0.45 0.38-0.45 0.38-0.45
0.50-0.80 0.50-0.80 0.60-0.90 0.60-0.90
0.17-0.37 0.17-0.37 0.10-0.40 0.10-0.40
0.38-0.43 0.38-0.43 0.43-0.48 0.43-0.48 0.43-0.48 0.43-0.48 0.43-0.48 0.48-0.53 0.48-0.53 0.48-0.53 0.46-0.54 0.46-0.54 0.46-0.54 0.48-0.53
0.60-0.90 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.60-0.90 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.50-0.80 0.50-0.80 0.50-0.80 0.75-1.00
0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.10-0.40 0.10-0.40 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.025 0.035 0.90-1.20 --0.15-0.30 0.025 0.0200.90-1.20 --0.15-0.30 0.040 0.035 0.035 0.90-1.20 0.30 0.15-0.25 0.035 0.035 0.90-1.20 0.30 0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.30 0.035 0.0200.90-1.20 --0.15-0.30 0.040 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.040 0.80-1.10 0.25 0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.040 0.80-1.10 0.25 0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.025 0.035 0.90-1.20 --0.15-0.30 0.035 0.035 0.90-1.20 --0.15-0.30 0.035 0.035 0.90-1.20 --0.15-0.30 0.030 0.040 0.80-1.10 0.25 0.15-0.25
C 0.14-0.20 0.10-0.17 0.12-0.18 0.12-0.18 0.27-0.33 0.27-0.35
Mn 0.40-0.70 0.30-0.60 0.35-0.65 0.35-0.65 0.30-0.60 0.35-0.65
Si 0.40 0.17-0.37 0.15-0.40 0.15-0.35 0.17-0.37 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.035 0.60-0.90 3.00-3.50 --0.035 0.035 0.60-0.90 2.75-3.15 --0.035 0.035 0.60-0.90 3.00-3.50 --0.030 0.030 0.60-1.00 3.00-3.50 ------0.60-0.90 2.75-3.15 --0.030 0.030 0.60-1.00 2.50-3.00 ---
Others ----------Cu 0.30 Cu 0.30 ----Cu 0.30 Cu 0.35 ------Cu 0.30 Cu 0.35 ------------Cu 0.35
2.3.3 Chromium-Nickel (Cr-Ni) Steels
Specification EN 10084:2008 GB/T 3077-1999 ISO 683-11:1987 JIS G 4053:2008 GB/T 3077-1999 JIS G 4053:2008
Designation 15NiCr13 Grade 12CrNi3 Type 15 NiCr 13 Symbol SNC815 Grade 30CrNi3 Symbol SNC631
UNS No. -------------
Steel No. 1.5752 -----------
Download From http://bbs.infoeach.com
Designation Grade 4140 Grade 4140 Grade 4140 42CrMo4 42CrMoS4
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008
Others ------Cu 0.30 --Cu 0.30
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
42
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.4 Nickel-Chromium-Molybdenum (Ni-Cr-Mo) Steels
Specification ISO 683-11:1987 JIS G 4053:2008 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10084:2008
ASTM A29/A29M-12e1 ASTM A322-13 GB/T 3077-1999 GB/T 3078-94 JIS G 4053:2008 SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10084:2008
UNS Steel No. No. --------G43200 --G43200 --G43200 ----1.6571
C 0.14-0.20 0.12-0.18 0.17-0.22 0.17-0.22 0.17-0.22 0.16-0.23
Mn 0.60-0.90 0.40-0.70 0.45-0.65 0.45-0.65 0.45-0.65 0.50-0.90
Si 0.15-0.40 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40
Grade 20CrNiMo Symbol SNCM420 Grade 4320 Grade 4340 Grade E4340 Grade 4340 Grade E4340 Grade 4340 Grade E4340 Grade 40CrNiMoA Grade 40CrNiMoA Symbol SNCM439 Grade 4340 Grade E4340 Grade 8620 Grade 8620 Grade 8620 20NiCrMo2-2 20NiCrMoS2-2
--------G43200 --G43400 --G43406 --G43400 --G43406 --G43400 --G43406 --------------G43400 --G43406 --G86200 --G86200 --G86200 ----1.6523 --1.6526
0.17-0.23 0.17-0.23 0.17-0.22 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.37-0.44 0.37-0.44 0.36-0.43 0.38-0.43 0.38-0.43 0.18-0.23 0.18-0.23 0.18-0.23 0.17-0.23 0.17-0.23
0.60-0.95 0.40-0.70 0.45-0.65 0.60-0.80 0.65-0.85 0.60-0.80 0.65-0.85 0.60-0.80 0.65-0.85 0.50-0.80 0.50-0.80 0.60-0.90 0.60-0.80 0.65-0.85 0.70-0.90 0.70-0.90 0.70-0.90 0.65-0.95 0.65-0.95
0.17-0.37 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.17-0.37 0.17-0.37 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40
GB 5216-85 ISO 683-11:1987
Grade 20CrNiMoH Type 20 NiCrMo 2 Type 20 NiCrMoS 2
-------
-------
0.17-0.23 0.17-0.23 0.17-0.23
0.60-0.95 0.65-0.95 0.65-0.95
0.17-0.37 0.15-0.4 0.15-0.4
JIS G 4053:2008 SAE J404 JAN09
Symbol SNCM220 Grade 8620
--G86200
-----
0.17-0.23 0.18-0.23
0.60-0.90 0.70-0.90
0.15-0.35 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.035 0.80-1.10 1.20-1.60 0.15-0.25 0.030 0.030 0.40-0.60 1.60-2.00 0.15-0.30 0.035 0.040 0.40-0.60 1.65-2.00 0.20-0.30 0.035 0.040 0.40-0.60 1.65-2.00 0.20-0.30 0.035 0.040 0.40-0.60 1.65-2.00 0.20-0.30 0.025 0.0200.60-0.90 1.40-1.70 0.25-0.35 0.040 0.035 0.035 0.40-0.70 0.35-0.75 0.20-0.30 0.030 0.030 0.40-0.60 1.60-2.00 0.15-0.30 0.030 0.040 0.40-0.60 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.025 0.025 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.025 0.025 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.025 0.025 0.70-0.90 1.65-2.00 0.20-0.30 0.025 0.025 0.60-0.90 1.25-1.65 0.15-0.25 0.025 0.025 0.60-0.90 1.25-1.65 0.15-0.25 0.030 0.030 0.60-1.00 1.60-2.00 0.15-0.30 0.030 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.025 0.025 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.40-0.60 0.40-0.70 0.15-0.25 0.035 0.040 0.40-0.60 0.40-0.70 0.15-0.25 0.035 0.04 0.40-0.60 0.40-0.70 0.15-0.25 0.025 0.035 0.35-0.70 0.40-0.70 0.15-0.25 0.025 0.0200.35-0.70 0.40-0.70 0.15-0.25 0.040 0.035 0.035 0.35-0.65 0.35-0.75 0.15-0.25 0.035 0.035 0.30-0.65 0.40-0.70 0.15-0.25 0.035 0.0200.30-0.65 0.40-0.70 0.15-0.25 0.040 0.030 0.030 0.40-0.60 0.40-0.70 0.15-0.25 0.030 0.040 0.40-0.60 0.40-0.70 0.15-0.25
Others --Cu 0.30 ----------Cu 0.30 Cu 0.35 ------------Cu 0.25 Cu 0.25 Cu 0.30 Cu 0.35 Cu 0.35 -----------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 3077-1999 JIS G 4053:2008 SAE J404 JAN09 ASME SA-29/SA-29M
Designation Type 17 NiCrMo 6 Symbol SNCM415 Grade 4320 Grade 4320 Grade 4320 20NiCrMoS6-4
Cu 0.30 ----Cu 0.30 Cu 0.35
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
43
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.4 Nickel-Chromium-Molybdenum (Ni-Cr-Mo) Steels (Continued) UNS Steel No. No. G86400 --G86400 --G86400 -----------
C 0.38-0.43 0.38-0.43 0.38-0.43 0.37-0.44 0.37-0.44
Mn 0.75-1.00 0.75-1.00 0.75-1.00 0.70-1.00 0.70-1.00
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.10-0.40 0.10-0.40 0.15-0.35 0.15-0.35 0.15-0.30 0.15-0.30 0.40
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.40-0.60 0.40-0.70 0.15-0.25 0.035 0.040 0.40-0.60 0.40-0.70 0.15-0.25 0.035 0.040 0.40-0.60 0.40-0.70 0.15-0.25 0.035 0.035 0.40-0.60 0.40-0.70 0.15-0.30 0.035 0.0200.40-0.60 0.40-0.70 0.15-0.30 0.040 0.030 0.030 0.40-0.60 0.40-0.70 0.15-0.30 0.030 0.040 0.40-0.60 0.40-0.70 0.15-0.25 0.025 0.025 1.00-1.40 3.00-3.50 0.08-0.15 0.025 0.025 1.00-1.40 3.00-3.50 0.08-0.15 0.025 0.035 0.80-1.10 3.00-3.50 0.20-0.30
JIS G 4053:2008 SAE J404 JAN09 ASME SA-29/SA-29M ASTM A29/A29M-12e1 EN 10084:2008
Symbol SNCM240 Grade 8640 Grade E9310 Grade E9310 14NiCrMo13-4
----G86400 --G93106 --G93106 ----1.6657
0.38-0.43 0.38-0.43 0.08-0.13 0.08-0.13 0.11-0.17
0.70-1.00 0.75-1.00 0.45-0.65 0.45-0.65 0.30-0.60
Cu 0.30 Cu 0.35 -------
C 0.38-0.43 0.28-0.35 0.30-0.37 0.38-0.45 0.30-0.37 0.35-0.42 0.35-0.42 0.38-0.45 0.40-0.50
Mn 0.50-0.70 0.40-0.70 0.40-0.70 0.40-0.70 0.40-0.70 0.30-0.60 0.30-0.60 0.50-0.80 0.60
Si 0.15-0.35 0.40 0.40 0.40 0.40 0.20-0.45 0.20-0.45 0.50 0.15-0.50
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 1.40-1.80 --0.30-0.40 0.025 0.035 1.50-1.80 --0.20-0.40 0.025 0.035 1.00-1.30 --0.15-0.25 0.025 0.035 1.50-1.80 --0.20-0.35 0.025 0.035 1.50-1.80 0.85-1.15 0.15-0.25 0.035 0.035 1.35-1.65 0.30 0.15-0.25 0.025 0.025 1.35-1.65 0.30 0.15-0.25 0.030 0.035 1.50-1.80 --0.15-0.30 0.030 0.030 1.30-1.70 0.25 0.15-0.30
Others Al 0.95-1.30 Al 0.80-1.20 Al 0.80-1.20 Al 0.80-1.20 Al 0.80-1.20 Al 0.70-1.10; Cu 0.30 Al 0.70-1.10; Cu 0.25 Al 0.8-1.20 Al 0.70-1.20; Cu 0.30
Others -----------
2.3.5 Chromium-Molybdenum-Aluminum (Cr-Mo-Al) Steels
Specification ASTM A355-89 (2012) EN 10085:2001
GB/T 3077-1999 GB/T 3078-94 ISO 683-10:1987 JIS G 4053:2008
Designation Class A 32CrAlMo7-10 34CrAlMo5-10 41CrAlMo7-10 34CrAlNi7-10 Grade 38CrMoAl Grade 38CrMoAlA Type 41 CrAlMo 74 Symbol SACM645
UNS No. K24065 -----------------
Steel No. --1.8505 1.8507 1.8509 1.8550 ---------
Download From http://bbs.infoeach.com
Designation Grade 8640 Grade 8640 Grade 8640 Grade 41 CrNiMo 2 Grade 41 CrNiMoS 2
Download From http://bbs.infoeach.com
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 ISO 683-1:1987
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
44
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.6 Boron (B) Steels
Designation Grade 10B18 Grade 18B2 Grade 17B2 Grade 10B18 Grade 10B23 Grade 23B2 Grade 10B23 Grade 10B29 Grade 28B2 Grade 10B29 Grade 10B30 Grade 33B2 Grade 10B30 Grade 10B38 Grade 38B2 Grade 35B2 Grade 10B38 Grade 10B40 Grade 40B Grade 40B Grade 10B40 Grade 10B45 Grade 45B Grade 45B Grade 10B45 Grade 10B50 Grade 50B Grade 50B Grade 50B Grade 10B50 Grade 15B22 Grade 20MnB5 Grade 15B22
UNS No. G10181 ----G10181 G10231 --G10231 G10291 --G10291 G10301 --G10301 G10381 ----G10381 G10401 ----G10401 G10451 ----G10451 G10501 ------G10501 G15221 --G15221
Steel No. --1.5503 1.5502 ----1.5508 ----1.5510 ----1.5514 ----1.5515 1.5511 ------------------------------1.5530 ---
C 0.15-0.20 0.16-0.20 0.15-0.20 0.15-0.20 0.20-0.25 0.20-0.25 0.20-0.25 0.25-0.31 0.25-0.30 0.25-0.31 0.28-0.34 0.30-0.35 0.28-0.34 0.35-0.42 0.35-0.40 0.32-0.39 0.35-0.42 0.37-0.44 0.37-0.44 0.37-0.44 0.37-0.44 0.43-0.50 0.42-0.49 0.42-0.49 0.43-0.50 0.48-0.55 0.47-0.55 0.47-0.55 0.47-0.55 0.48-0.55 0.18-0.24 0.17-0.23 0.18-0.24
Mn 0.60-0.90 0.60-0.80 0.60-0.90 0.60-0.90 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.50-0.80 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 1.10-1.40 1.10-1.40 1.10-1.40
Si --0.30 0.30 ----0.30 ----0.30 ----0.30 ----0.15-0.30 0.40 ----0.17-0.37 0.17-0.37 ----0.17-0.37 0.17-0.37 ----0.17-0.37 0.17-0.37 0.17-0.37 ----0.40 ---
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.050 ------0.025 0.025 ------0.025 0.025 0.30 ----0.040 0.050 -----0.040 0.050 ------0.025 0.025 0.30 ----0.040 0.050 ------0.040 0.050 ------0.025 0.025 0.30 ----0.040 0.050 ------0.040 0.050 ------0.025 0.025 0.30 ----0.040 0.050 ------0.040 0.050 ------0.025 0.025 0.30 ----0.030 0.015 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.040 0.050 ------0.040 0.050 ------0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.035 0.035 0.30 0.30 0.15 0.040 0.050 ------0.040 0.050 ------0.025 0.035 ------0.040 0.050 -------
Others B 0.0005-0.003 B 0.0008-0.005; Cu 0.25 B 0.0008-0.005; Cu 0.25 B 0.0005-0.003 B 0.0005-0.003 B 0.0008-0.005; Cu 0.25 B 0.0005-0.003 B 0.0005-0.003 B 0.0008-0.005; Cu 0.25 B 0.0005-0.003 B0.0005-0.003 B 0.0008-0.005; Cu 0.25 B0.0005-0.003 B 0.0005-0.003 B 0.0008-0.005; Cu 0.25 B 0.0008-0.0050; Al 0.020 min. B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.0035; Cu 0.30 B 0.0005-0.0035 B 0.0005-0.003 B 0.0008-0.0050 B 0.0005-0.003
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASTM A29/A29M-12e1 EN 10263-3:2001 C1:2001 EN 10263-4:2001 C2:2003 SAE J403 JUN14 ASTM A29/A29M-12e1 EN 10263-4:2001 C2:2003 SAE J403 JUN14 ASTM A29/A29M-12e1 EN 10263-4:2001 C2:2003 SAE J403 JUN14 ASTM A29/A29M-12e1 EN 10263-4:2001 C2:2003 SAE J403 JUN14 ASTM A29/A29M-12e1 EN 10263-4:2001 C2:2003 EN 10269:2013 SAE J403 JUN14 ASTM A29/A29M-12e1 GB/T 3077-1999 GB/T 3078-94 SAE J403 JUN14 ASTM A29/A29M-12e1 GB/T 3077-1999 GB/T 3078-94 SAE J403 JUN14 ASTM A29/A29M-12e1 GB 13791-92 GB/T 3077-1999 GB/T 3078-94 SAE J403 JUN14 ASTM A29/A29M-12e1 EN 10083-3:2006 C1:2008 SAE J403 JUN14
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
45
2.3 Chemical Composition of Alloy Steels for General Use (Continued) 2.3.6 Boron (B) Steels (Continued)
Specification ASME SA-29/SA-29M
ASTM A29/A29M-12e1
ASTM A29/A29M-12e1 EN 10263-4:2001 C2:2003 ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 SAE J404 JAN09
UNS Steel No. No. G50441 --G50461 --G50501 --G50441 --G50461 --G50501 --G50441 --G50461 --G50501 --G51351 ----1.7077 G50601 --G51601 --G50601 --G51601 --G50601 --G51601 --G51601 ---
C 0.43-0.48 0.44-0.49 0.48-0.53 0.43-0.48 0.44-0.49 0.48-0.53 0.43-0.48 0.44-0.49 0.48-0.53 0.33-0.38 0.34-0.38 0.56-0.64 0.56-0.64 0.56-0.64 0.56-0.64 0.56-0.64 0.56-0.64 0.56-0.64
Mn 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.60-0.80 0.70-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.30 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.20-0.60 ----0.035 0.040 0.20-0.35 ----0.035 0.040 0.40-0.60 ----0.035 0.040 0.20-0.60 ----0.035 0.040 0.20-0.35 ----0.035 0.040 0.40-0.60 ----0.035 0.040 0.20-0.60 ----0.035 0.040 0.20-0.35 ----0.035 0.040 0.40-0.60 ----0.035 0.040 0.80-1.05 ----0.025 0.025 0.90-1.20 ----0.035 0.040 0.40-0.60 ----0.035 0.040 0.70-0.90 ----0.035 0.040 0.40-0.60 ----0.035 0.040 0.70-0.90 ----0.035 0.040 0.40-0.60 ----0.035 0.040 0.70-0.90 ----0.030 0.040 0.70-0.90 0.25 0.06
Others B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0008-0.005; Cu 0.25 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003 B 0.0005-0.003; Cu 0.35
UNS Steel No. No. G61500 --G61500 --G61500 ----1.8159 --------G61500 ---
C 0.48-0.53 0.48-0.53 0.48-0.53 0.47-0.55 0.47-0.54 0.47-0.50 0.48-0.53
Mn 0.70-0.90 0.70-0.90 0.70-0.90 0.70-1.10 0.50-0.80 0.60-1.00 0.70-0.90
Si 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.17-0.37 0.10-0.40 0.15-0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.80-1.10 ----0.035 0.040 0.80-1.10 ----0.035 0.040 0.80-1.10 ----0.025 0.025 0.90-1.20 ----0.025 0.025 0.80-1.10 0.30 0.10 0.035 0.035 0.80-1.10 ----0.030 0.040 0.80-1.10 0.25 0.06
Others V 0.15 min. V 0.15 min. V 0.15 min. V 0.10-0.25 V 0.10-0.20 V 0.10-0.25 V 0.15 min.; Cu 0.35
2.3.7 Chromium-Vanadium (Cr-V) Steels
Specification ASME SA-29/SA-29M ASTM A29/A29M-12e1 ASTM A322-13 EN 10083-3:2006 C1:2008 GB/T 3077-1999 ISO 683-1:1987 SAE J404 JAN09
Designation Grade 6150 Grade 6150 Grade 6150 51CrV4 Grade 50CrVA Grade 51 CrV 4 Grade 6150
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A322-13
Designation Grade 50B44 Grade 50B46 Grade 50B50 Grade 50B44 Grade 50B46 Grade 50B50 Grade 50B44 Grade 50B46 Grade 50B50 Grade 51B35 Grade 36CrB4 Grade 50B60 Grade 51B60 Grade 50B60 Grade 51B60 Grade 50B60 Grade 51B60 Grade 51B60
Handbook of Comparative World Steel Standards
Chapter 2
Carbon and Alloy Steels for General Use
46
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter
3 STRUCTURAL STEEL PLATES
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
48
Structural Steel Plates – List of Standards
Chapter 3
ASME Standards ASME SA-36/SA-36M ASME SA-283/SA-283M ASME SA-572/SA-572M
Carbon Structural Steel Low and Intermediate Tensile Strength Carbon Steel Plates High-Strength Low-Alloy Columbium-Vanadium Structural Steel Steel, Sheet and Strip, Hot-Rolled, Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with ASME SA-1011/SA-1011M Improved Formability, and Ultra-High Strength
ASTM Standards ASTM A36/A36M-14 ASTM A242/A242M-13 ASTM A283/A283M-13 ASTM A514/A514M-14 ASTM A529/A529M-14 ASTM A572/A572M-15 ASTM A573/A573M-13 ASTM A588/A588M-15 ASTM A606/A606M-09a ASTM A633/A633M-13 ASTM A656/A656M-13 ASTM A709/A709M-13a ASTM A710/A710M-02 (2013) ASTM A871/A871M-14 ASTM A1011/A1011M-14
Carbon Structural Steel High-Strength Low-Alloy Structural Steel Low and Intermediate Tensile Strength Carbon Steel Plates High-Yield-Strength, Quenched and Tempered Alloy Steel Plate, Suitable for Welding High-Strength Carbon-Manganese Steel of Structural Quality High-Strength Low-Alloy Columbium-Vanadium Structural Steel Structural Carbon Steel Plates of Improved Toughness High-Strength Low-Alloy Structural Steel, up to 50 ksi [345 MPa] Minimum Yield Point, with Atmospheric Corrosion Resistance Steel, Sheet and Strip, High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled, with Improved Atmospheric Corrosion Resistance Normalized High-Strength Low-Alloy Structural Steel Plates Hot-Rolled Structural Steel, High-Strength Low-Alloy Plate with Improved Formability Structural Steel for Bridges Precipitation-Strengthened Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium Alloy Structural Steel Plates High-Strength Low-Alloy Structural Steel Plate with Atmospheric Corrosion Resistance Steel, Sheet and Strip, Hot-Rolled, Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with Improved Formability, and Ultra-High Strength
CSA Standard CSA G40.21-13
Structural Quality Steel - Plates, Sheet, Floor Plates, Bars, and Welded Shapes
EN Standard EN 10025-2:2004
Hot rolled products of structural steels – Part 2: Technical delivery conditions for non-alloy structural steels
GB Standards GB 700-88 GB 711-88 GB 712-2000 GB/T 1591-94 GB/T 3524-92 GB 11251-89 GB/T 16270-1996 GB/T 18982-2003
Carbon Structural Steels Hot-Rolled Quality Carbon Structural Steel Plates and Wide Strips Hull Structural Steel High Strength Low Alloy Structural Steels Hot-Rolled Carbon and Low Alloy Structural Steel Strips Hot-Rolled Alloy Structural Steel Plates High Strength Structural Steel Plates and Strips: Products Supplied in the Heat-Treated or Controlled Rolled Condition Corrosion Resistant Steel Plates and Strips for Container
ISO Standards ISO 630:1995 A1:2003 ISO 4950-2:1995 A1:2003 ISO 4950-3:1995 A1:2003 ISO 4952:2006 ISO 5952:2005
Structural Steels - Plates, Wide Flats, Bars, Sections and Profiles High Yield Strength Flat Steel Products, Part 2: Products Supplied in the Normalized or Controlled Rolled Condition High Yield Strength Flat Steel Products – Part 3: Products Supplied in the Heat-Treated (Quenched + Tempered) Condition Structural Steels with Improved Atmospheric Corrosion Resistance - Second Edition Continuously Hot-Rolled Steel Sheet of Structural Quality with Improved Atmospheric Corrosion Resistance
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 3
Structural Steel Plates – List of Standards
49
JIS Standards JIS G 3101:2010 JIS G 3106:2008 JIS G 3114:2008 JIS G 3125:2010 JIS G 3128:2009 JIS G 3136:2012
Rolled steels for general structure Rolled steels for welded structure Hot-rolled atmospheric corrosion resisting steels for welded structure Superior atmospheric corrosion resisting rolled steels High yield strength steel plates for welded structure Rolled steels for building structure
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
50
Structural Steel Plates – Heat Treatment Terms
Chapter 3
Heat Treatment Terms Applicable to this Chapter Standard ASME SA-36/SA-36M ASME SA-283/SA-283M ASME SA-572/SA-572M ASME SA-1011/SA-1011M ASTM A36/A36M-14 ASTM A242/A242M-13 ASTM A283/A283M-13 ASTM A514/A514M-14 ASTM A529/A529M-14 ASTM A572/A572M-15 ASTM A573/A573M-13 ASTM A588/A588M-15 ASTM A606/A606M-09a ASTM A633/A633M-13 ASTM A656/A656M-13 ASTM A709/A709M-13a ASTM A710/A710M-02 (2013) ASTM A871/A871M-14 ASTM A1011/A1011M-14 CSA G40.21-13 EN 10025-2:2004 GB 700-88 GB 711-88 GB 712-2000 GB/T 1591-94 GB/T 3524-92 GB 11251-89 GB/T 16270-1996 GB/T 18982-2003 ISO 630:1995 A1:2003 ISO 4950-2:1995 A1:2003 ISO 4950-3:1995 A1:2003 ISO 4952:2006 ISO 5952:2005 JIS G 3101:2010 JIS G 3106:2008 JIS G 3114:2008 JIS G 3125:2010 JIS G 3128:2009 JIS G 3136:2012
Heat Treatment Terms ------HR: hot-rolled SR: stress relieved ----QT: quenched and tempered; SR: stress relieved --------HR: hot-rolled (as-rolled); CR: cold-rolled; A: annealed; N: normalized; HR+A: hot-rolled and annealed; HR+N: hot rolled and normalized N: normalized; NN: double normalized HR: hot-rolled QT: quenched and tempered; AR: as rolled; CtR: control rolled; TMCP: thermo-mechanical control processed; PHT: precipitation heat treatment; N+PHT: normalized followed by precipitation heat treatment; Q+PHT: quenched followed by precipitation heat treatment N: normalized; QT: quenched and tempered; AR: as rolled HR: hot-rolled AR: as-rolled; QT: quenched and tempered; N: normalized; CtR: control rolled; SR: stress relieved; A: annealed; N: normalized rolled; TMCP: thermos-mechanically rolled; AR: as rolled HR: hot-rolled; CtR: control-rolled; N: normalized HR: hot-rolled; N: normalized; A: annealed; T: tempered N: normalized; TMCP: thermo-mechanically control processed; HR: hot-rolled; CtR: controlled-rolled; QT: quenched and tempered HR: hot-rolled; CtR: control rolled; N: normalized; NT: normalized and tempered; QT: quenched and tempered HR: hot-rolled A: annealed; N: normalized; NT: normalized and tempered; QT: quenched and tempered; CtR: control rolled; N: normalized; QT: quenched and tempered; NT: normalized and tempered HR: hot-rolled; CR: cold-rolled AR: as rolled; N: normalized or equivalent (obtained by controlled rolling); BA: by agreement N: normalized; NT: normalized and tempered; CtR: controlled rolled condition QT: quenched and tempered AR: as rolled; N: normalized or equivalent (obtained by controlled rolling) HR: hot-rolled HR: hot-rolled N: normalized; QHT: quench-hardened and tempered; T: tempered; TMCP: thermo-mechanical control processed N: normalized; QT: quenched and tempered; TMCP: thermo-mechanical control processed; T: tempered CR: cold-rolled; HR: hot-rolled QT: quenched and tempered N: normalized; T: tempered; TMCP: thermo-mechanical control processed
Impact Testing Notes Applicable to this Chapter see standard for supplementary impact testing: the standard includes impact testing as a supplementary requirement (optional to the purchaser). see standard for impact data: impact testing requirements are listed in the standard for multiple test temperatures.
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter 3
Structural Steel Plates
51
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates
Specification ISO 630:1995 A1:2003 ASME SA-283/SA-283M EN 10025-2:2004
Designation Grade E 185 (Fe 310), Quality 0 Grade A S185
Grade Q195
GB 711-88 GB/T 3524-92 GB 711-88
Grade 08F Grade Q195 Grade 08 Grade 10F Grade 10 Symbol SS330
JIS G 3101:2010
Note: This section continued on next page.
Steel No. ---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi 3 ≤ t ≤ 16 --185 --300-540 --16 < t ≤ 25 --175 --300-540 --K01400 ------165 24 310-415 45-60 --1.0035 t 40 ------315-390 ------t ≤ 60 ------315 ----------195 --315-430 ------t ≤ 60 ------325 ------t ≤ 60 ------325 ------t ≤ 60 ------335 ------t ≤ 16 --205 --330-430 --16 < t ≤ 40 --195 --330-430 --40 < t ≤ 100 --175 --330-430 --t > 100 --165 --330-430 ---
Elongation % min. 18 18 30 --18 L, 16 T 18 L, 16 T 17 L, 15 T 16 L, 14 T 16 L, 14 T 15 L, 13 T 15 L, 13 T 15 L, 13 T 33 32 --34 33 33 32 32 see standard see standard see standard see standard
Heat Treatment AR AR --AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP HR, CtR or N HR, CtR or N HR, CtR or N N, A, T or HR HR N, A, T or HR N, A, T or HR N, A, T or HR HR HR HR HR
Other -------------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 700-88
UNS No. ---
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
52
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued) Steel No. ---
Grade Q215B
---
---
ASME SA-1011/SA-1011M
Grade Q215A Grade Q215B Grade 30 [205], SS
-------
-------
ASTM A1011/A1011M-14
Grade 30 [205], SS
---
---
ISO 630:1995 A1:2003
Grade E 235 (Fe 360), Quality A
---
---
Grade E 235 (Fe 360), Quality B Grade E 235 (Fe 360), Quality B NF
---
---
---
---
Download From http://bbs.infoeach.com
GB/T 3524-92
Designation Grade Q215A
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 16 --215 --335-410 --31 16 < t ≤ 40 --205 --335-410 --30 40 < t ≤ 60 --195 --335-410 --29 60 < t ≤ 100 --185 --335-410 --28 100 < t ≤ 150 --175 --335-410 --27 t > 150 --165 --335-410 --26 t ≤ 16 --215 --335-410 --31 16 < t ≤ 40 --205 --335-410 --30 40 < t ≤ 60 --195 --335-410 --29 60 < t ≤ 100 --185 --335-410 --28 100 < t ≤ 150 --175 --335-410 --27 t > 150 --165 --335-410 --26 ----215 --335-450 --31 ----215 --335-450 --31 0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 205 30 340 L 49 L 21 L 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 205 30 340 L 49 L 24 L 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 205 30 340 L 49 L 25 L 0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 205 30 340 L 49 L 21 L 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 205 30 340 L 49 L 24 L 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 205 30 340 L 49 L 25 L 3 ≤ t ≤ 16 --235 --340-470 --26 16 < t ≤ 40 --225 --340-470 --26 40 < t ≤ 63 --215 --340-470 --25 63 < t ≤ 80 --215 --340-470 --24 80 < t ≤ 100 --215 --340-470 --24 100 < t ≤ 150 --195 --340-470 --22 150 < t ≤ 200 --185 --340-470 --21 3 ≤ t ≤ 16 --235 --340-470 --26 16 < t ≤ 25 --225 --340-470 --26 3 ≤ t ≤ 16 --235 --340-470 --26 16 < t ≤ 40 --225 --340-470 --26 40 < t ≤ 63 --215 --340-470 --25 63 < t ≤ 80 --215 --340-470 --24 80 < t ≤ 100 --215 --340-470 --24 100 < t ≤ 150 --195 --340-470 --22 150 < t ≤ 200 --185 --340-470 --21
Heat Treatment HR or CtR HR or CtR HR or CtR HR or CtR HR or CtR HR or CtR HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR HR HR HR HR HR HR HR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR
Other ------------L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C ----------------------------------27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C
Download From http://bbs.infoeach.com
UNS No. ---
Specification GB 700-88
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
53
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued)
Specification ISO 630:1995 A1:2003
Grade E 235 (Fe 360), Quality D
Grade B
UNS No. ---
Steel No. ---
---
---
K01702
---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. 3 ≤ t ≤ 16 --235 --340-470 --26 16 < t ≤ 40 --225 --340-470 --26 40 < t ≤ 63 --215 --340-470 --25 63 < t ≤ 80 --215 --340-470 --24 80 < t ≤ 100 --215 --340-470 --24 100 < t ≤ 150 --195 --340-470 --22 150 < t ≤ 200 --185 --340-470 --21 3 ≤ t ≤ 16 --235 --340-470 --26 16 < t ≤ 40 --225 --340-470 --26 40 < t ≤ 63 --215 --340-470 --25 63 < t ≤ 80 --215 --340-470 --24 80 < t ≤ 100 --215 --340-470 --24 100 < t ≤ 150 --195 --340-470 --22 150 < t ≤ 200 --185 --340-470 --21 ----185 27 345-450 50-65 28
Heat Treatment AR AR AR AR AR AR AR N or BA N or BA N or BA N or BA N or BA N or BA N or BA ---
Other 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-283/SA-283M
Designation Grade E 235 (Fe 360), Quality C
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
54
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued) UNS No. -----
ASTM A1011/A1011M-14
Grade 33 [230], SS
---
S235JR
---
S235J0
---
ASME SA-1011/SA-1011M
Grade 36 [250], Type 1, SS
---
ASTM A1011/A1011M-14
Grade 36 [250], Type 1, SS
---
EN 10025-2:2004
GB 711-88 Grade 15 Note: This section continued on next page.
---
Steel No. -----
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi t ≤ 60 ------355 --0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 230 33 360 L 52 L 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 230 33 360 L 52 L 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 230 33 360 L 52 L --0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 230 33 360 L 52 L 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 230 33 360 L 52 L 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 230 33 360 L 52 L 1.0038 t 150 --185 --375-460 --21 t ≤ 16 --235 --375-460 --26 16 < t ≤ 40 --225 --375-460 --25 40 < t ≤ 60 --215 --375-460 --24 60 < t ≤ 100 --205 --375-460 --23 100 < t ≤ 150 --195 --375-460 --22 t > 150 --185 --375-460 --21 t ≤ 16 --235 --375-460 --26 16 < t ≤ 40 --225 --375-460 --25 40 < t ≤ 60 --215 --375-460 --24 60 < t ≤ 100 --205 --375-460 --23 100 < t ≤ 150 --195 --375-460 --22 t > 150 --185 --375-460 --21 ----235 --375-500 --26 ----235 --375-500 --26 t ≤ 60 ------380 --27 ----205 30 380-515 55-75 25 ----205 30 380-515 55-75 25 0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 275 40 380 L 55 L 15 L 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 275 40 380 L 55 L 20 L 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 275 40 380 L 55 L 21 L 0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 275 40 380 L 55 L 15 L 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 275 40 380 L 55 L 20 L 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 275 40 380 L 55 L 21 L
Heat Treatment HR or CtR HR or CtR HR or CtR HR or CtR HR or CtR HR or CtR HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR HR N, A, T or HR ----HR HR HR HR HR HR
Other ------------L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ -20°C L: 27 J @ -20°C L: 27 J @ -20°C L: 27 J @ -20°C L: 27 J @ -20°C L: 27 J @ -20°C -----------------------
Download From http://bbs.infoeach.com
UNS No. ---
Specification GB 700-88
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
56
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued) Steel No. -------------
Grade SN400B
---
---
Grade SN400C
---
---
JIS G 3101:2010
Symbol SS400
---
---
JIS G 3106:2008
Grade SM400A
---
---
Grade SM400B
---
---
Grade SM400C
---
---
JIS G 3136:2012
Designation Grade 58 [400] Grade A Grade B Grade D Grade E Grade SN400A
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. t ≤ 40 t ≤ 1.5 ----------------6 ≤ t < 16 --16 ≤ t ≤ 40 --40 < t ≤ 100 --6 ≤ t < 12 --12 ≤ t ≤ 16 --16 < t ≤ 40 --40 < t ≤ 100 --6 ≤ t < 16 --16 ≤ t ≤ 40 --40 < t ≤ 100 --t ≤ 16 --16 < t ≤ 40 --40 < t ≤ 100 --t > 100 --t≤5 --5 < t ≤ 16 --16 < t ≤ 40 --40 < t ≤ 100 --100 < t ≤ 160 --160 < t ≤ 200 --t≤5 --5 < t ≤ 16 --16 < t ≤ 40 --40 < t ≤ 100 --100 < t ≤ 160 --160 < t ≤ 200 --t≤5 --5 < t ≤ 16 --16 < t ≤ 40 --40 < t ≤ 100 --100 < t ≤ 200 ---
Yield Strength, min. Tensile Strength, min. MPa ksi MPa ksi 220 32 400-490 58-71 235 --400-520 --235 --400-520 --235 --400-520 --235 --400-520 --235 --400-510 --235 --400-510 --215 --400-510 --235 --400-510 --235-355 --400-510 --235-355 --400-510 --215-335 --400-510 ------400-510 --235-355 --400-510 --215-335 --400-510 --245 --400-510 --235 --400-510 --215 --400-510 --205 --400-510 --245 --400-510 --245 --400-510 --235 --400-510 --215 --400-510 --205 --400-510 --195 --400-510 --245 --400-510 --245 --400-510 --235 --400-510 --215 --400-510 --205 --400-510 --195 --400-510 --245 --400-510 --245 --400-510 --235 --400-510 --215 --400-510 ------400-510 ---
Elongation % min. 24 22 22 22 22 17 21 23 18 18 22 24 18 22 24 see standard see standard see standard see standard 23 18 22 24 24 24 23 18 22 24 24 24 23 18 22 24 24
Heat Treatment --N, TMCP, HR or CtR N, TMCP, HR or CtR N, TMCP, HR or CtR see standard N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP N, T or TMCP HR HR HR HR N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP N, QHT, T or TMCP
Other --see standard for impact data
--------L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C --L: 27 J @ 0°C L: 27 J @ 0°C ----------------------L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C --L: 47 J @ 0°C L: 47 J @ 0°C L: 47 J @ 0°C L: 47 J @ 0°C
Download From http://bbs.infoeach.com
UNS No. K02301 -----------
Specification ASTM A573/A573M-13 GB 712-2000
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
57
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued)
Designation
UNS No. K02595
Steel No. ---
ASME SA-1011/SA-1011M
K02596 K02597 K02598 K02599 Grade 36 [250], Type 2, SS ---
-----------
ASTM A36/A36M-14
---
K02595
---
ASTM A709/A709M-13a
Grade 36 [250]
K02596 K02597 K02598 K02599 ---
-----------
ASTM A1011/A1011M-14
Grade 36 [250], Type 2, SS
---
---
Section Thickness/Diameter Yield Strength, min. mm in. MPa ksi 100 < t ≤ 200 4 200 t>8 220 32 65 < t ≤ 100 2.5 < t ≤ 4 250 36 40 < t ≤ 65 1.5 < t ≤ 2.5 250 36 20 < t ≤ 40 0.75 < t ≤ 1.5 250 36 t ≤ 20 t ≤ 0.75 250 36 0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 250 36 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 250 36 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 250 36 100 < t ≤ 200 4 200 t>8 220 32 65 < t ≤ 100 2.5 < t ≤ 4 250 36 40 < t ≤ 65 1.5 < t ≤ 2.5 250 36 20 < t ≤ 40 0.75 < t ≤ 1.5 250 36 t ≤ 20 t ≤ 0.75 250 36 t ≤ 75 t≤3 250 36 t ≤ 100 t≤4 250 36 t > 75 t>3 250 36 0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 250 36 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 250 36 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 250 36
Tensile Strength, min. Elongation MPa ksi % min. 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 L 58-80 L 16 L 400-550 L 58-80 L 20 L 400-550 L 58-80 L 21 L 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400-550 58-80 23 400 58 21 400-550 58-80 23 400 58 19 400-550 L 58-80 L 16 L 400-550 L 58-80 L 20 L 400-550 L 58-80 L 21 L
Heat Treatment ------------HR HR HR SR or none SR or none SR or none SR or none SR or none SR or none --QT --HR HR HR
Other ------------------------------see standard for impact data -------
Download From http://bbs.infoeach.com
---
Download From http://bbs.infoeach.com
Specification ASME SA-36/SA-36M
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
58
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued)
Specification GB 711-88 GB 700-88
ISO 630:1995 A1:2003
Steel No. -----
Grade Q255B
---
---
Grade Q255A Grade Q255B Grade E 275 (Fe 430), Quality A
-------
-------
Grade E 275 (Fe 430), Quality B
---
---
Grade E 275 (Fe 430), Quality C
---
---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 60 ------410 --28 t ≤ 16 --255 --410-510 --24 16 < t ≤ 40 --245 --410-510 --23 40 < t ≤ 60 --235 --410-510 --22 60 < t ≤ 100 --225 --410-510 --21 100 < t ≤ 150 --215 --410-510 --20 t > 150 --205 --410-510 --19 t ≤ 16 --255 --410-510 --24 16 < t ≤ 40 --245 --410-510 --23 40 < t ≤ 60 --235 --410-510 --22 60 < t ≤ 100 --225 --410-510 --21 100 < t ≤ 150 --215 --410-510 --20 t > 150 --205 --410-510 --19 ----255 --410-550 --24 ----255 --410-550 --24 3 ≤ t ≤ 16 --275 --410-540 --22 16 < t ≤ 40 --265 --410-540 --22 40 < t ≤ 63 --255 --410-540 --21 63 < t ≤ 80 --245 --410-540 --20 80 < t ≤ 100 --235 --410-540 --20 100 < t ≤ 150 --225 --410-540 --18 150 < t ≤ 200 --215 --410-540 --17 3 ≤ t ≤ 16 --275 --410-540 --22 16 < t ≤ 40 --265 --410-540 --22 40 < t ≤ 63 --255 --410-540 --21 63 < t ≤ 80 --245 --410-540 --20 80 < t ≤ 100 --235 --410-540 --20 100 < t ≤ 150 --225 --410-540 --18 150 < t ≤ 200 --215 --410-540 --17 3 ≤ t ≤ 16 --275 --410-540 --22 16 < t ≤ 40 --265 --410-540 --22 40 < t ≤ 63 --255 --410-540 --21 63 < t ≤ 80 --245 --410-540 --20 80 < t ≤ 100 --235 --410-540 --20 100 < t ≤ 150 --225 --410-540 --18 150 < t ≤ 200 --215 --410-540 --17
Heat Treatment N, A, T or HR HR or CtR HR or CtR HR or CtR HR or CtR HR or CtR HR or CtR HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR, CtR or N HR HR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR AR
Other --------------L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C ------------------27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 20°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C 27 J @ 0°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 3524-92
UNS No. -----
Designation Grade 20 Grade Q255A
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
59
3.1 Carbon Steels for Structural Steel Plates 3.1A Mechanical Properties of Carbon Steels for Structural Steel Plates (Continued)
Designation Grade E 275 (Fe 430), Quality D
UNS No. ---
Steel No. ---
Download From http://bbs.infoeach.com
Yield Strength, min. Tensile Strength, min. MPa ksi MPa ksi 275 --410-540 --265 --410-540 --255 --410-540 --245 --410-540 --235 --410-540 --225 --410-540 --215 --410-540 --310 45 410 L 60 L 310 45 410 L 60 L 310 45 410 L 60 L 310 45 410 L 60 L 310 45 410 L 60 L 310 45 410 L 60 L 310-410 45-60 410 L 60 L 310-410 45-60 410 L 60 L 310-410 45-60 410 L 60 L 230 33 415-550 60-80 230 33 415-550 60-80 275 --430-580 --275 --410-560 --265 --410-560 --255 --410-560 --245 --410-560 --235 --410-560 --225 --400-540 --215 --380-540 --205 --380-540 --275 --430-580 --275 --410-560 --265 --410-560 --255 --410-560 --245 --410-560 --235 --410-560 --225 --400-540 --215 --380-540 --205 --380-540 ---
Elongation % min. 22 22 21 20 20 18 17 13 L 18 L 19 L 13 L 18 L 19 L 14 L 19 L 20 L 23 23 --23 L, 21 T 23 L, 21 T 22 L, 20 T 21 L, 19 T 21 L, 19 T 19 L, 19 T 18 L, 18 T 18 L, 18 T --23 L, 21 T 23 L, 21 T 22 L, 20 T 21 L, 19 T 21 L, 19 T 19 L, 19 T 18 L, 18 T 18 L, 18 T
Heat Treatment N or BA N or BA N or BA N or BA N or BA N or BA N or BA HR HR HR HR HR HR HR HR HR ----AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP AR, N or TMCP
Other 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C 27 J @ -20°C ------------------------L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C L: 27 J @ 20°C --L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C L: 27 J @ 0°C
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. 3 ≤ t ≤ 16 --16 < t ≤ 40 --40 < t ≤ 63 --63 < t ≤ 80 --80 < t ≤ 100 --100 < t ≤ 150 --150 < t ≤ 200 --ASME SA-1011/SA-1011M Grade 45 [310], SS ----0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 ASTM A1011/A1011M-14 Grade 45 [310], Type 1, SS ----0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 Grade 45 [310], Type 2, SS ----0.65 ≤ t < 1.6 0.025 ≤ t < 0.064 1.6 ≤ t < 2.5 0.064 ≤ t < 0.097 2.5 ≤ t < 6.0 0.097 ≤ t < 0.230 ASME SA-283/SA-283M Grade D K02702 ------ASTM A283/A283M-13 Grade D K02702 ------EN 10025-2:2004 S275JR --1.0044 t 100 --1.0050 t 1.5
0.17 0.17
0.90 0.90
0.40 0.15-0.40
0.035 0.035
0.04 0.04
-----
-----
-----
-----
Download From http://bbs.infoeach.com
UNS No. ---
Specification ISO 630:1995 A1:2003
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
67
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued) UNS No. -----
Steel No. -----
ASTM A1011/A1011M-14
Grade 33 [230], SS
---
---
EN 10025-2:2004
S235JR
---
1.0038
S235J0
---
ASME SA-1011/SA-1011M
Grade 36 [250], Type 1, SS
---
ASTM A1011/A1011M-14
Grade 36 [250], Type 1, SS
---
---
GB 711-88 GB 700-88
GB 711-88 ASME SA-283/SA-283M
Grade 15 Grade Q235A Grade Q235B Grade Q235C Grade Q235D Grade Q235A Grade Q235B Grade 20F Grade C
----------------K02401
-------------------
ASTM A283/A283M-13
Grade C
K02401
---
ASME SA-1011/SA-1011M
Grade 40 [275], SS
---
ASTM A1011/A1011M-14
Grade 40 [275], SS
ASTM A573/A573M-13
Grade 58 [400]
GB/T 3524-92
GB 712-2000
Grade A Grade B Grade D Grade E Note: This section continued on next page.
Section Thickness mm in. t ≤ 60 ---------
C Mn 0.12-0.19 0.25-0.50 0.25 0.90
Si 0.07 ---
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.25 0.25 --0.035 0.04 0.15 0.20 0.06
---
0.25
0.90
---
0.035
0.04
0.15
0.20
0.06
---------------
0.17 0.20 0.20 0.17 0.17 0.17 0.25
1.40 1.40 1.40 1.40 1.40 1.40 0.90
---------------
0.035 0.035 0.035 0.030 0.030 0.030 0.035
0.035 0.035 0.035 0.030 0.030 0.030 0.04
------------0.15
------------0.20
------------0.06
---
---
0.25
0.90
---
0.035
0.04
0.15
0.20
0.06
---
t ≤ 60 ------------t ≤ 60 t ≤ 40 t > 40 t ≤ 40 t > 40 ---
----------------t ≤ 1.5 t > 1.5 t ≤ 1.5 t > 1.5 ---
0.12-0.19 0.14-0.22 0.12-0.20 0.18 0.17 0.14-0.22 0.12-0.20 0.17-0.24 0.24 0.24 0.24 0.24 0.25
0.035 0.045 0.045 0.040 0.035 0.045 0.045 0.035 0.035 0.035 0.030 0.030 0.035
0.040 0.050 0.045 0.040 0.035 0.050 0.045 0.040 0.04 0.04 0.030 0.030 0.04
0.25 0.30 0.30 0.30 0.30 0.30 0.30 0.25 --------0.15
0.25 0.30 0.30 0.30 0.30 0.30 0.30 0.25 --------0.20
------------------------0.06
---
---
---
---
0.25
0.035
0.04
0.15
0.20
0.06
K02301
---
---------
---------
t ≤ 13 13 < t ≤ 40 ---------
t ≤ 0.5 0.5 < t ≤ 1.5 ---------
0.23 0.23 0.21 0.21 0.21 0.18
0.030 0.030 0.035 0.035 0.035 0.035
0.030 0.030 0.035 0.035 0.035 0.035
----0.20 0.20 0.20 0.20
----0.40 0.40 0.40 0.40
-------------
t ≤ 40 40 < t ≤ 150 150 < t ≤ 250 1.0114 t ≤ 40 40 < t ≤ 150 150 < t ≤ 250 -----
0.35-0.65 0.17-0.37 0.30-0.65 0.30 0.30-0.70 0.30 0.35-0.80 0.30 0.35-0.80 0.30 0.30-0.65 0.30 0.30-0.70 0.30 0.25-0.50 0.07 0.90 0.40 0.90 0.15-0.40 0.90 0.40 0.90 0.15-0.40 0.90 --0.90
---
0.60-0.90 0.10-0.35 0.60-0.90 0.10-0.35 --0.50 0.80-1.20 0.35 0.60-1.20 0.35 0.70-1.20 0.35
Others Cu 0.25; N 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 Cu 0.25; N 0.008 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.25; N 0.008 --------V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 ----Cu 0.35; Mn 2.5xC min. Cu 0.35 Cu 0.35 Cu 0.35
Download From http://bbs.infoeach.com
Designation Grade 15F Grade 33 [230], SS
Download From http://bbs.infoeach.com
Specification GB 711-88 ASME SA-1011/SA-1011M
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
68
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued)
Specification JIS G 3136:2012
Steel No. -----
Grade SN400C
---
---
Symbol SS400 Grade SM400A
-----
-----
Grade SM400B
---
---
ASME SA-1011/SA-1011M
--K02595 K02596 K02597 K02598 K02599 Grade 36 [250], Type 2, SS ---
---------------
ASTM A36/A36M-14
---
ASTM A709/A709M-13a
Grade 36 [250]
K02595 K02596 K02597 K02598 K02599 ---
-------------
ASTM A1011/A1011M-14
Grade 36 [250], Type 2, SS
---
---
ASME SA-36/SA-36M
Grade SM400C ---
Section Thickness mm in. 6 ≤ t ≤ 100 --6 ≤ t ≤ 50 --50 < t ≤ 100 --16 ≤ t ≤ 50 --50 < t ≤ 100 ------t ≤ 50 --50 < t ≤ 200 --t ≤ 50 --50 < t ≤ 200 --t ≤ 100 --t > 100 t>4 65 < t ≤ 100 2.5 < t ≤ 4 40 < t ≤ 65 1.5 < t ≤ 2.5 20 < t ≤ 40 0.75 < t ≤ 1.5 t ≤ 20 t ≤ 0.75 -----
C 0.24 0.20 0.22 0.20 0.22 --0.23 0.25 0.20 0.22 0.18 0.29 0.27 0.26 0.25 0.25 0.25
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo ----0.050 0.050 ------0.60-1.50 0.35 0.030 0.015 ------0.60-1.50 0.35 0.030 0.015 ------0.60-1.50 0.35 0.020 0.008 ------0.60-1.50 0.35 0.020 0.008 ----------0.050 0.050 ----------0.035 0.035 ----------0.035 0.035 ------0.60-1.50 0.35 0.035 0.035 ------0.60-1.50 0.35 0.035 0.035 ------0.60-1.50 0.35 0.035 0.035 ------0.85-1.20 0.15-0.40 0.04 0.05 ------0.85-1.20 0.15-0.40 0.04 0.05 ------0.80-1.20 0.15-0.40 0.04 0.05 ------0.80-1.20 0.40 0.04 0.05 --------0.40 0.04 0.05 ------1.35 --0.035 0.04 0.15 0.20 0.06
t > 100 t>4 65 < t ≤ 100 2.5 < t ≤ 4 40 < t ≤ 65 1.5 < t ≤ 2.5 20 < t ≤ 40 0.75 < t ≤ 1.5 t ≤ 20 t ≤ 0.75 t ≤ 20 t ≤ 0.75 20 < t ≤ 40 0.75 < t ≤ 1.5 40 < t ≤ 65 1.5 < t ≤ 2.5 65 < t ≤ 100 2.5 < t ≤ 4 t ≤ 20 t ≤ 0.75 20 < t ≤ 40 0.75 < t ≤ 1.5 40 < t ≤ 100 1.5 < t ≤ 4 ---------
0.29 0.27 0.26 0.25 0.25 0.25 0.25 0.26 0.27 0.26 0.27 0.28 0.26 0.25
0.85-1.20 0.15-0.40 0.85-1.20 0.15-0.40 0.80-1.20 0.15-0.40 0.80-1.20 0.40 --0.40 --0.40 0.80-1.20 0.40 0.80-1.20 0.15-0.40 0.85-1.20 0.15-0.40 --0.40 0.60-0.90 0.40 0.60-0.90 0.40 --0.40 1.35 ---
0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.04 0.035
0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.05 0.04
--------------------------0.15
--------------------------0.20
--------------------------0.06
Others --------------------------------V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 --------------------------V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 3101:2010 JIS G 3106:2008
UNS No. -----
Designation Grade SN400A Grade SN400B
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
69
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued)
Specification GB 711-88 GB 700-88
Steel No. -------------
---
---
---
Section Thickness mm in. t ≤ 60 ------------------t≥3 ---
ASME SA-1011/SA-1011M ASTM A1011/A1011M-14
Grade 45 [310], Type 1, SS
---
---
---
---
Grade 45 [310], Type 2, SS
---
---
---
---
K02702
---
Grade D32
---
---
Grade E32
---
Grade F32
---
GB/T 3524-92 ISO 630:1995 A1:2003
Download From http://bbs.infoeach.com
ASME SA-283/SA-283M
Grade D
ASTM A283/A283M-13
Grade D
EN 10025-2:2004
S275JR
GB 712-2000
S275J0
Grade A32
C 0.17-0.24 0.18-0.28 0.18-0.28 0.18-0.28 0.18-0.28 0.24
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo 0.35-0.65 0.17-0.37 0.035 0.040 0.25 0.25 --0.40-0.70 0.30 0.045 0.050 0.30 0.30 --0.40-0.70 0.30 0.045 0.045 0.30 0.30 --0.40-0.70 0.30 0.045 0.050 0.30 0.30 --0.40-0.70 0.30 0.045 0.045 0.30 0.30 ------0.050 0.050 -------
Others Cu 0.25; N 0.008 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 ---
---
3 ≤ t ≤ 40 t > 40 t≥3
-------
0.21 0.22 0.20
1.50 1.50 1.50
0.40 0.40 0.40
0.045 0.045 0.040
0.045 0.045 0.040
-------
-------
-------
-------
---
---
t≥3
---
0.20
1.50
0.40
0.035
0.035
---
---
---
---
---
---
---
---
0.25
1.35
---
0.035
0.04
0.15
0.20
0.06
0.25
1.35
---
0.035
0.04
0.15
0.20
0.06
0.60
0.0300.070
0.025
0.15
0.20
0.06
V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.008; Cb 0.008; Al 0.02-0.08; N 0.010-0.030 --------Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05; N 0.009
t ≤ 40 t > 40 K02702 --t ≤ 40 t > 40 --1.0044 t ≤ 40 40 < t ≤ 150 150 < t ≤ 250 --1.0143 t ≤ 40 40 < t ≤ 150 150 < t ≤ 250 -------
0.02-0.08 0.30-1.00
t ≤ 1.5 t > 1.5 t ≤ 1.5 t > 1.5 ---------------
0.27 0.27 0.27 0.27 0.21 0.22 0.22 0.18 0.18 0.18 0.18
0.90 0.40 0.90 0.15-0.40 0.90 0.40 0.90 0.15-0.40 1.50 --1.50 --1.50 --1.50 --1.50 --1.50 --0.90-1.60 0.50
0.035 0.035 0.030 0.030 0.035 0.035 0.035 0.030 0.030 0.030 0.035
0.04 0.04 0.030 0.030 0.035 0.035 0.035 0.030 0.030 0.030 0.035
--------------------0.20
--------------------0.40
--------------------0.08
---
---
0.18
0.90-1.60
0.50
0.035
0.035
0.20
0.40
0.08
---
---
---
0.18
0.90-1.60
0.50
0.035
0.035
0.20
0.40
0.08
---
---
---
0.16
0.90-1.60
0.50
0.025
0.025
0.20
0.8
0.08
Download From http://bbs.infoeach.com
UNS No. -------------
Designation Grade 20 Grade Q255A Grade Q255B Grade Q255A Grade Q255B Grade E 275 (Fe 430), Quality A Grade E 275 (Fe 430), Quality B Grade E 275 (Fe 430), Quality C Grade E 275 (Fe 430), Quality D Grade 45 [310], SS
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
70
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued) UNS Steel No. No. --------K02404 ---
ASTM A529/A529M-14 ASME SA-1011/SA-1011M
Grade 50 [345] Grade 50 [340], SS
K02703 ---
-----
ASTM A1011/A1011M-14
Grade 50 [340], SS
---
---
---
---
0.25
1.35
---
0.035
0.04
0.15
0.20
0.06
ASME SA-1011/SA-1011M
Grade 55 [380], SS
---
---
---
---
0.25
1.35
---
0.035
0.04
0.15
0.20
0.06
ASTM A1011/A1011M-14
Grade 55 [380], SS
---
---
---
---
0.25
1.35
---
0.035
0.04
0.15
0.20
0.06
ASTM A573/A573M-13
Grade 70 [485]
K02701
---
ASTM A529/A529M-14 GB 711-88 JIS G 3136:2012
Grade 55 [380] Grade 25Mn Grade 30 Grade SN490C
K02703 -------
---------
GB 700-88 GB/T 3524-92 JIS G 3101:2010 EN 10025-2:2004 JIS G 3106:2008
Grade Q275 Grade Q275 Symbol SS490 E295 Grade SM490A
-----------
------1.0050 ---
Grade SM490B
---
---
Grade SM490C Grade SN490B
-----
-----
t ≤ 13 13 < t ≤ 40 t ≤ 25 t ≤ 60 t ≤ 60 16 ≤ t ≤ 50 50 < t ≤ 100 ------t ≤ 250 t ≤ 50 50 < t ≤ 200 t ≤ 50 50 < t ≤ 200 t ≤ 100 6 ≤ t ≤ 50 50 < t ≤ 100
t ≤ 0.5 0.5 < t ≤ 1.5 t≤1 -------------------------------
0.27 0.28 0.27 0.22-0.30 0.27-0.35 0.18 0.20 0.28-0.38 0.28-0.38 ----0.20 0.22 0.18 0.20 0.18 0.18 0.20
0.030 0.030 0.04 0.035 0.035 0.020 0.020 0.045 0.045 0.050 0.045 0.035 0.035 0.035 0.035 0.035 0.030 0.030
0.030 0.030 0.05 0.040 0.040 0.008 0.008 0.050 0.050 0.050 0.045 0.035 0.035 0.035 0.035 0.035 0.015 0.015
------0.25 0.25 ----0.30 0.30 -------------------
------0.25 0.25 ----0.30 0.30 -------------------
-------------------------------------
Download From http://bbs.infoeach.com
JIS G 3136:2012
Section Thickness Weight, %max, Unless Otherwise Specified mm in. C Mn Si P S Cr Ni Mo t ≤ 60 --0.17-0.24 0.70-1.00 0.17-0.37 0.035 0.040 0.25 0.25 --t ≤ 60 --0.22-0.30 0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 --t ≤ 13 t ≤ 0.5 0.24 0.85-1.20 0.15-0.40 0.030 0.030 ------13 < t ≤ 40 0.5 < t ≤ 1.5 0.26 0.85-1.20 0.15-0.40 0.030 0.030 ------t ≤ 25 t≤1 0.27 1.35 0.40 0.04 0.05 ----------0.25 1.35 --0.035 0.04 0.15 0.20 0.06
0.85-1.20 0.15-0.40 0.85-1.20 0.15-0.40 1.35 0.40 0.70-1.00 0.17-0.37 0.50-0.80 0.17-0.37 1.65 0.55 1.65 0.55 0.50-0.80 0.35 0.50-0.80 0.35 --------1.65 0.55 1.65 0.55 1.65 0.55 1.65 0.55 1.65 0.55 1.65 0.55 1.65 0.55
Others Cu 0.25; N 0.008 Cu 0.25; N 0.008 ------V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 V 0.008; Cu 0.20 nom.; Ti 0.025; Cb 0.008 ------Cu 0.25; N 0.008 Cu 0.25; N 0.008 ----Cu 0.30; N 0.008; As 0.080 Cu 0.30; N 0.008; As 0.080 --N 0.012 ---------------
Download From http://bbs.infoeach.com
ASTM A573/A573M-13
Designation Grade 20Mn Grade 25 Grade 65 [450]
Specification GB 711-88
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
71
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued)
Specification GB 712-2000
JIS G 3106:2008 GB 11251-89
Steel No. ---
Section Thickness mm in. -----
Grade D36
---
---
---
Grade E36
---
---
Grade F36
---
Grade E 355 (Fe 510), Quality C Grade E 355 (Fe 510), Quality D Grade SM490YA Grade SM490YB Grade 40 B
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.035 0.20 0.40 0.08
C 0.18
Mn 0.90-1.60
Si 0.50
---
0.18
0.90-1.60
0.50
0.035
0.035
0.20
0.40
0.08
---
---
0.18
0.90-1.60
0.50
0.035
0.035
0.20
0.40
0.08
---
---
---
0.16
0.90-1.60
0.50
0.025
0.025
0.20
0.80
0.08
---
---
---
---
-------
-------
3 ≤ t ≤ 30 t > 30 3 ≤ t ≤ 30 t > 30 t ≤ 100 t ≤ 100 ---
---------------
0.040 0.040 0.035 0.035 0.035 0.035 ---
0.040 0.040 0.035 0.035 0.035 0.035 ---
---------------
---------------
---------------
0.20 1.60 0.55 0.22 1.60 0.55 0.20 1.60 0.55 0.22 1.60 0.55 0.20 1.65 0.55 0.20 1.65 0.55 0.37-0.44 0.17-0.37 0.60-0.90
Others V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05; N 0.009 ------------B 0.0005-0.0035
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ISO 630:1995 A1:2003
UNS No. ---
Designation Grade A36
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
72
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued)
Specification EN 10025-2:2004
JIS G 3106:2008 GB 711-88 JIS G 3101:2010 GB 11251-89
UNS No. ---
Steel No. 1.0045
Section Thickness mm in. t ≤ 30 --30 < t ≤ 150 --150 < t ≤ 250 --1.0553 t ≤ 30 --30 < t ≤ 40 --40 < t ≤ 150 --150 < t ≤ 250 ---------
C 0.24 0.24 0.24 0.20 0.22 0.22 0.22 0.18
Mn 1.60 1.60 1.60 1.60 1.60 1.60 1.60 0.90-1.60
Si 0.55 0.55 0.55 0.55 0.55 0.55 0.55 0.50
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.030 0.030 ------0.030 0.030 ------0.030 0.030 ------0.030 0.030 ------0.035 0.035 0.20 0.40 0.08
S355J0
---
Grade A40
---
Grade D40
---
---
---
---
0.18
0.90-1.60
0.50
0.035
0.035
0.20
0.40
0.08
Grade E40
---
---
---
---
0.18
0.90-1.60
0.50
0.035
0.035
0.20
0.40
0.08
Grade F40
---
---
---
---
0.16
0.90-1.60
0.50
0.025
0.025
0.20
0.80
0.08
Grade SM520B Grade SM520C Grade 35 Grade 30Mn Symbol SS540 Grade 45 B Grade 45Mn2 Grade 50 B
-----------------
-----------------
t ≤ 100 t ≤ 100 t ≤ 60 t ≤ 60 ---------
-----------------
0.20 0.20 0.32-0.40 0.27-0.35 0.30 0.42-0.49 0.42-0.49 0.47-0.55
0.035 0.035 0.035 0.035 0.040 0.035 0.035 0.035
0.035 0.035 0.040 0.040 0.040 0.035 0.035 0.035
----0.25 0.25 --0.30 0.30 0.30
----0.25 0.25 --0.30 0.30 0.30
----------0.15 0.15 0.15
1.65 0.55 1.65 0.55 0.50-0.80 0.17-0.37 0.70-1.00 0.17-0.37 1.60 --0.60-0.90 0.17-0.37 1.40-1.80 0.17-0.37 0.60-0.90 0.17-0.37
Others Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 Cu 0.55; N 0.012 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05 V 0.05-0.10; Cu 0.35; Ti 0.02; Nb 0.02-0.05; N 0.009 ----Cu 0.25; N 0.008 Cu 0.25; N 0.008 --Cu 0.30; B 0.0005-0.0035 Cu 0.30 Cu 0.30
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 712-2000
Designation S355JR
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
73
3.1 Carbon Steels for Structural Steel Plates 3.1B Chemical Composition of Carbon Steels for Structural Steel Plates (Continued)
Specification GB 711-88
JIS G 3106:2008 EN 10025-2:2004 GB 711-88
UNS No. -------------------------
Steel No. --------1.0060 ------------1.0070
Section Thickness mm in. t ≤ 60 --t ≤ 60 --t ≤ 60 --t ≤ 100 --t ≤ 250 --t ≤ 60 --t ≤ 60 --t ≤ 60 --t ≤ 60 --t ≤ 60 --t ≤ 60 --t ≤ 250 ---
C 0.37-0.45 0.37-0.45 0.42-0.50 0.18 --0.47-0.55 0.48-0.56 0.52-0.60 0.57-0.65 0.57-0.65 0.62-0.70 ---
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo 0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 --0.70-1.00 0.17-0.37 0.035 0.040 0.25 0.25 --0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 --1.70 0.55 0.035 0.035 ----------0.045 0.045 ------0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 --0.70-1.00 0.17-0.37 0.035 0.040 0.25 0.25 --0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 --0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 --0.70-1.00 0.17-0.37 0.035 0.040 0.25 0.25 --0.50-0.80 0.17-0.37 0.035 0.040 0.25 0.25 ------0.045 0.045 -------
Others Cu 0.25; N 0.008 Cu 0.25; N 0.008 Cu 0.25; N 0.008 --N 0.012 Cu 0.25; N 0.008 Cu 0.25; N 0.008 Cu 0.25; N 0.008 Cu 0.25; N 0.008 Cu 0.25; N 0.008 Cu 0.25; N 0.008 N 0.012
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10025-2:2004
Designation Grade 40 Grade 40Mn Grade 45 Grade SM570 E335 Grade 50 Grade 50Mn Grade 55 Grade 60 Grade 60Mn Grade 65 E360
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
74
3.2 Alloy Steels for Structural Steel Plates 3.2.1A Mechanical Properties of High-Strength Low-Alloy Structural Steel Plates
Specification GB/T 1591-94
ASME SA-1011/SA-1011M
Steel No. ---
Grade Q295B
---
---
Grade 260W (38W)
---
---
Grade 260WT (38WT)
---
---
---
---
---
---
---
---
---
---
----------------------K01802
-------------------------
Grade 45 [310], Class 1, HSLAS ASTM A1011/A1011M-14 Grade 45 [310], Class 1, HSLAS ASME SA-1011/SA-1011M Grade 50 [340], Class 2, HSLAS ASTM A1011/A1011M-14 Grade 50 [340], Class 2, HSLAS ASME SA-572/SA-572M Grade 42 [290], Type 1 Grade 42 [290], Type 2 Grade 42 [290], Type 3 Grade 42 [290], Type 5 ASTM A572/A572M-15 Grade 42 [290], Type 1 Grade 42 [290], Type 2 Grade 42 [290], Type 3 Grade 42 [290], Type 5 ASTM A656/A656M-13 Grade 50 [345], Type 3 Grade 50 [345], Type 7 Grade 50 [345], Type 8 ASTM A633/A633M-13 Grade A Note: This section continued on next page.
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi t ≤ 16 --295 --390-570 --16 < t ≤ 35 --275 --390-570 --35 < t ≤ 50 --255 --390-570 --50 < t ≤ 100 --235 --390-570 --t ≤ 16 --295 --390-570 --16 < t ≤ 35 --275 --390-570 --35 < t ≤ 50 --255 --390-570 --50 < t ≤ 100 --235 --390-570 ------260 38 410-590 60-85 t ≤ 65 t ≤ 2.5 260 38 410-590 60-85 65 < t ≤ 200 2.5 ≤ t ≤ 8 250 36 410-590 60-85 ----260 38 410-590 60-85 t ≤ 65 t ≤ 2.5 260 38 410-590 60-85 65 < t ≤ 200 2.5 < t ≤ 8 250 36 410-590 60-85 t ≤ 2.5 t ≤ 0.097 310 45 410 L 60 L t > 2.5 t > 0.097 310 45 410 L 60 L t ≤ 2.5 t ≤ 0.097 310 45 410 L 60 L t > 2.5 t > 0.097 310 45 410 L 60 L t ≤ 2.5 t ≤ 0.097 340 50 410 L 60 L t > 2.5 t > 0.097 340 50 410 L 60 L t ≤ 2.5 t ≤ 0.097 340 50 410 L 60 L t > 2.5 t > 0.097 340 50 410 L 60 L ----290 42 415 60 ----290 42 415 60 ----290 42 415 60 ----290 42 415 60 ----290 42 415 60 ----290 42 415 60 ----290 42 415 60 ----290 42 415 60 t ≤ 50 t≤2 345 50 415 60 t ≤ 50 t≤2 345 50 415 60 t ≤ 50 t≤2 345 50 415 60 t ≤ 100 t≤4 290 42 430-570 63-83
Elongation % min. 23 23 23 23 23 23 23 23 23 23 L, 21 T 23 L, 21 T 23 23 L, 21 T 23 L, 21 T 23 L 25 L 23 L 25 L 20 L 22 L 20 L 22 L 24 24 24 24 24 24 24 24 23 23 23 23
Heat Treatment HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT AR, N or CtR AR, N or CtR AR, N or CtR AR, N or CtR AR, N or CtR AR, N or CtR HR HR HR HR HR HR HR HR ----------------HR HR HR N
Other --------L: 34 J @ 20°C ------------see standard for impact data -----------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
CSA G40.21-13
UNS No. ---
Designation Grade Q295A
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
75
3.2 Alloy Steels for Structural Steel Plates 3.2.1A Mechanical Properties of High-Strength Low-Alloy Structural Steel Plates (Continued)
Specification CSA G40.21-13
ASTM A1011/A1011M-14 ASME SA-572/SA-572M
ASTM A572/A572M-15
ASTM A709/A709M-13a
CSA G40.21-13
ASME SA-1011/SA-1011M ASTM A1011/A1011M-14
Steel No. ---
Grade 300WT (44WT)
---
---
Grade 50 [340], Class 1, HSLAS Grade 50 [340], Class 1, HSLAS Grade 50 [345], Type 1 Grade 50 [345], Type 2 Grade 50 [345], Type 3 Grade 50 [345], Type 5 Grade 50 [345], Type 1 Grade 50 [345], Type 2 Grade 50 [345], Type 3 Grade 50 [345], Type 5 Grade 50 [345], Type 1 Grade 50 [345], Type 2 Grade 50 [345], Type 3 Grade 50 [345], Type 5 Grade 350W (50W)
---
---
---
---
---------------------------
---------------------------
Grade 55 [380], Class 2, HSLAS Grade 55 [380], Class 2, HSLAS
---
---
---
---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi ----300 44 440-620 64-90 ----300 44 410-590 60-85 t ≤ 65 t ≤ 2.5 300 44 440-620 64-90 65 < t ≤ 200 2.5 ≤ t ≤ 8 280 40 440-620 64-90 ----300 44 440-620 64-90 t ≤ 65 t ≤ 2.5 300 44 440-620 64-90 65 < t ≤ 200 2.5 < t ≤ 8 280 40 440-620 64-90 t ≤ 2.5 t ≤ 0.097 340 50 450 L 65 L t > 2.5 t > 0.097 340 50 450 L 65 L t ≤ 2.5 t ≤ 0.097 340 50 450 L 65 L t > 2.5 t > 0.097 340 50 450 L 65 L ----345 50 450 65 ----345 50 450 65 ----345 50 450 65 ----345 50 450 65 ----345 50 450 65 ----345 50 450 65 ----345 50 450 65 ----345 50 450 65 t ≤ 100 t≤4 345 50 450 65 t ≤ 100 t≤4 345 50 450 65 t ≤ 100 t≤4 345 50 450 65 t ≤ 100 t≤4 345 50 450 65 ----350 50 450-650 65-95 ----350 50 450-620 65-90 t ≤ 65 t ≤ 2.5 350 50 450-650 65-95 65 < t ≤ 200 2.5 ≤ t ≤ 8 320 46 450-650 65-95 t ≤ 2.5 t ≤ 0.097 380 55 450 L 65 L t > 2.5 t > 0.097 380 55 450 L 65 L t ≤ 2.5 t ≤ 0.097 380 55 450 L 65 L t > 2.5 t > 0.097 380 55 450 L 65 L
Elongation % min. 23 23 23 L, 21 T 23 L, 21 T 23 23 L, 21 T 23 L, 21 T 20 L 22 L 20 L 22 L 21 21 21 21 21 21 21 21 21 21 21 21 22 22 22 L, 20 T 22 L, 20 T 18 L 20 L 18 L 20 L
Heat Treatment AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR AR, N or CtR AR, N or CtR AR, N or CtR HR HR HR HR ----------------QT QT QT QT AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR HR HR HR HR
Other --------see standard for impact data ------------------------see standard for impact data
-----------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-1011/SA-1011M
UNS No. ---
Designation Grade 300W (44W)
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
76
3.2 Alloy Steels for Structural Steel Plates 3.2.1A Mechanical Properties of High-Strength Low-Alloy Structural Steel Plates (Continued)
Specification GB/T 1591-94
Steel No. ---
Grade Q345B
---
---
Grade Q345C
---
---
Grade Q345D
---
---
Grade Q345E
---
---
K11510
---
ASTM A242/A242M-13
Type 1
CSA G40.21-13
Grade 350WT (50WT)
---
---
Grade 380W (55W)
---
---
---
---
---
---
ASME SA-1011/SA-1011M
Grade 55 [380], Class 1, HSLAS Grade 60 [410], Class 2, HSLAS Note: This section continued on next page.
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 16 --345 --470-630 --21 16 < t ≤ 35 --325 --470-630 --21 35 < t ≤ 50 --295 --470-630 --21 50 < t ≤ 100 --275 --470-630 --21 t ≤ 16 --345 --470-630 --21 16 < t ≤ 35 --325 --470-630 --21 35 < t ≤ 50 --295 --470-630 --21 50 < t ≤ 100 --275 --470-630 --21 t ≤ 16 --345 --470-630 --22 16 < t ≤ 35 --325 --470-630 --22 35 < t ≤ 50 --295 --470-630 --22 50 < t ≤ 100 --275 --470-630 --22 t ≤ 16 --345 --470-630 --22 16 < t ≤ 35 --325 --470-630 --22 35 < t ≤ 50 --295 --470-630 --22 50 < t ≤ 100 --275 --470-630 --22 t ≤ 16 --345 --470-630 --22 16 < t ≤ 35 --325 --470-630 --22 35 < t ≤ 50 --295 --470-630 --22 50 < t ≤ 100 --275 --470-630 --22 t ≤ 20 t ≤ 0.75 345 50 480 70 21 20 < t ≤ 40 0.75 < t ≤ 1.5 315 46 460 67 21 t ≤ 40 t ≤ 1.5 345 50 485 70 21 40 < t ≤ 50 1.5 < t ≤ 2 315 46 460 67 21 40 < t ≤ 100 1.5 < t ≤ 4 290 42 435 63 21 t > 50 t>2 290 42 435 63 21 ----350 50 450-650 65-95 22 ----350 50 450-620 65-90 22 t ≤ 65 t ≤ 2.5 350 50 450-650 65-95 22 L, 20 T 65 < t ≤ 200 2.5 < t ≤ 8 320 46 450-650 65-95 22 L, 20 T ----380 55 480-650 65-95 21 ----380 55 480-650 70-95 21 t ≤ 65 t ≤ 2.5 380 55 480-650 70-95 21 L 65 < t ≤ 200 2.5 < t ≤ 8 350 50 480-650 70-95 21 L t ≤ 2.5 t ≤ 0.097 380 55 480 L 70 L 18 L t > 2.5 t > 0.097 380 55 480 L 70 L 20 L t ≤ 2.5 t ≤ 0.097 410 60 480 L 70 L 16 L t > 2.5 t > 0.097 410 60 480 L 70 L 18 L
Heat Treatment HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT ------------AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR HR HR HR HR
Other --------L: 34 J @ 20°C --------L: 34 J @ 0°C --------L: 34 J @ -20°C --------L: 27 J @ -40°C ------------see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
UNS No. ---
Designation Grade Q345A
-----------------
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
77
3.2 Alloy Steels for Structural Steel Plates 3.2.1A Mechanical Properties of High-Strength Low-Alloy Structural Steel Plates (Continued)
Specification ASTM A1011/A1011M-14
ASTM A588/A588M-15
ASME SA-572/SA-572M
ASTM A572/A572M-15
ASTM A656/A656M-13
Steel No. ---
---
---
K11947
---
Grade B
K12043
---
Grade K
---
---
Grade C
K12000
---
Grade D
K12037
---
-----------------------
-----------------------
Grade 55 [380], Type 1 Grade 55 [380], Type 2 Grade 55 [380], Type 3 Grade 55 [380], Type 5 Grade 55 [380], Type 1 Grade 55 [380], Type 2 Grade 55 [380], Type 3 Grade 55 [380], Type 5 Grade 60 [415], Type 3 Grade 60 [415], Type 7 Grade 60 [415], Type 8
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 2.5 t ≤ 0.097 380 55 480 L 70 L 18 L t > 2.5 t > 0.097 380 55 480 L 70 L 20 L t ≤ 2.5 t ≤ 0.097 410 60 480 L 70 L 16 L t > 2.5 t > 0.097 410 60 480 L 70 L 18 L ----345 50 485 70 21 t ≤ 100 t≤4 345 50 485 70 21 100 < t ≤ 125 4 0.097 410 60 520 L 75 L t ≤ 2.5 t ≤ 0.097 450 65 520 L 75 L t > 2.5 t > 0.097 450 65 520 L 75 L ----415 60 520 75 ----415 60 520 75 ----415 60 520 75 ----415 60 520 75 ----415 60 520 75 ----415 60 520 75 ----415 60 520 75 ----415 60 520 75 t ≤ 16 --420 --520-680 --16 < t ≤ 35 --400 --520-680 --35 < t ≤ 50 --380 --520-680 --50 < t ≤ 100 --360 --520-680 --t ≤ 16 --420 --520-680 --16 < t ≤ 35 --400 --520-680 --35 < t ≤ 50 --380 --520-680 --50 < t ≤ 100 --360 --520-680 --t ≤ 16 --420 --520-680 --16 < t ≤ 35 --400 --520-680 --35 < t ≤ 50 --380 --520-680 --50 < t ≤ 100 --360 --520-680 ---
Elongation % min. 18 20 18 L, 15 T 18 L, 15 T 20 20 20 L, 17 T 20 L, 17 T 16 L 18 L 14 L 16 L 16 L 18 L 14 L 16 L 18 18 18 18 18 18 18 18 18 18 18 18 18 18 18 18 19 19 19 19
Heat Treatment AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR HR HR HR HR HR HR HR HR ----------------HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT
Other --------see standard for impact data
----------------------------------------L: 34 J @ 20°C --------L: 34 J @ 0°C -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-1011/SA-1011M
UNS No. ---
Designation Grade 400W (60W)
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
79
3.2 Alloy Steels for Structural Steel Plates 3.2.1A Mechanical Properties of High-Strength Low-Alloy Structural Steel Plates (Continued)
Specification GB/T 1591-94
Steel No. ---
Grade Q420E
---
---
Grade Q420C
---
---
Grade Q420D
---
---
Grade Q420E
---
---
K12202
---
-------------------
-------------------
---
---
---------
---------
---
---
ASTM A633/A633M-13
Grade E
ASME SA-572/SA-572M
Grade 65 [450], Type 1 Grade 65 [450], Type 2 Grade 65 [450], Type 3 Grade 65 [450], Type 5 Grade 65 [450], Type 1 Grade 65 [450], Type 2 Grade 65 [450], Type 3 Grade 65 [450], Type 5 Grade 65 [450], Class 1, HSLAS Grade 65 [450], Class 1, HSLAS Grade 70 [485], Type 3 Grade 70 [485], Type 7 Grade 70 [485], Type 8 Grade 70 [480], Class 1, HSLAS Grade 70 [480], Class 1, HSLAS
ASTM A572/A572M-15
ASME SA-1011/SA-1011M ASTM A1011/A1011M-14 ASTM A656/A656M-13
ASME SA-1011/SA-1011M ASTM A1011/A1011M-14
Section Thickness/Diameter Yield Strength, min. mm in. MPa ksi t ≤ 16 --420 --16 < t ≤ 35 --400 --35 < t ≤ 50 --380 --50 < t ≤ 100 --360 --t ≤ 16 --420 --16 < t ≤ 35 --400 --35 < t ≤ 50 --380 --50 < t ≤ 100 --360 --t ≤ 50 --420 --50 < t ≤ 100 --400 --t ≤ 50 --420 --50 < t ≤ 100 --400 --t ≤ 50 --420 --50 < t ≤ 100 --400 --t ≤ 100 t≤4 415 60 100 < t ≤ 150 4 2.5 t > 0.097 450 65 t ≤ 2.5 t ≤ 0.097 450 65 t > 2.5 t > 0.097 450 65 t ≤ 25 t≤1 485 70 t ≤ 25 t≤1 485 70 t ≤ 25 t≤1 485 70 t ≤ 2.5 t ≤ 0.097 480 70 t > 2.5 t > 0.097 480 70 t ≤ 2.5 t ≤ 0.097 480 70 t > 2.5 t > 0.097 480 70
Tensile Strength, min. Elongation MPa ksi % min. 520-680 --19 520-680 --19 520-680 --19 520-680 --19 520-680 --19 520-680 --19 520-680 --19 520-680 --19 520-670 T --18 T 520-670 T --18 T 520-670 T --18 T 520-670 T --18 T 520-670 T --18 T 520-670 T --18 T 550-690 80-100 23 515-655 75-95 23 550 80 17 550 80 17 550 80 17 550 80 17 550 80 17 550 80 17 550 80 17 550 80 17 550 L 80 L 14 L 550 L 80 L 16 L 550 L 80 L 14 L 550 L 80 L 16 L 550 80 17 550 80 17 550 80 17 585 L 85 L 12 L 585 L 85 L 14 L 585 L 85 L 12 L 585 L 85 L 14 L
Heat Treatment HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT N or NN NN ----------------HR HR HR HR HR HR HR HR HR HR HR
Other ----L: 34 J @ -20°C --------L: 27 J @ -40°C see standard for impact data
-------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 16270-1996
UNS No. ---
Designation Grade Q420D
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
80
3.2 Alloy Steels for Structural Steel Plates 3.2.1B Chemical Composition of High-Strength Low-Alloy Structural Steel Plates
Specification GB/T 1591-94
CSA G40.21-13
ASTM A1011/A1011M-14 ASME SA-1011/SA-1011M ASTM A1011/A1011M-14 ASME SA-572/SA-572M
ASTM A572/A572M-15
ASTM A656/A656M-13
ASTM A633/A633M-13 CSA G40.21-13
Steel No. ---
Section Thickness mm in. -----
Grade Q295B
---
---
---
Grade 260W (38W) Grade 260WT (38WT) Grade 45 [310], Class 1, HSLAS Grade 45 [310], Class 1, HSLAS Grade 50 [340], Class 2, HSLAS Grade 50 [340], Class 2, HSLAS Grade 42 [290], Type 1 Grade 42 [290], Type 2 Grade 42 [290], Type 3
-------
-------
---
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.045 0.045 0.30 0.30 ---
C 0.16
Mn 0.80-1.50
Si 0.55
---
0.16
0.80-1.50
0.55
-------
-------
0.20 0.20 0.22
0.50-1.50 0.40 0.80-1.50 0.15-0.40 1.35 ---
---
---
---
0.22
1.35
---
---
---
---
0.15
---
---
---
---
-------
-------
t ≤ 150 t ≤ 150 t ≤ 150
Grade 42 [290], Type 5
---
---
Grade 42 [290], Type 1 Grade 42 [290], Type 2 Grade 42 [290], Type 3
-------
Grade 42 [290], Type 5
0.040
0.040
0.30
0.30
---
0.04 0.03 0.04
0.05 0.04 0.04
----0.15
----0.20
----0.06
---
0.04
0.04
0.15
0.20
0.06
1.35
---
0.04
0.04
0.15
0.20
0.06
0.15
1.35
---
0.04
0.04
0.15
0.20
0.06
t≤6 t≤6 t≤6
0.21 0.21 0.21
0.50-1.35 0.50-1.35 0.50-1.35
0.40 0.40 0.40
0.04 0.04 0.04
0.05 0.05 0.05
-------
-------
-------
t ≤ 150
t≤6
0.21
0.50-1.25
0.40
0.04
0.05
---
---
---
-------
t ≤ 150 t ≤ 150 t ≤ 150
t≤6 t≤6 t≤6
0.21 0.21 0.21
0.50-1.35 0.50-1.35 0.50-1.35
0.40 0.40 0.40
0.030 0.030 0.030
0.030 0.030 0.030
-------
-------
-------
---
---
t ≤ 150
t≤6
0.21
0.50-1.25
0.40
0.030
0.030
---
---
---
Grade 50 [345], Type 3
---
---
t ≤ 50
t≤2
0.18
1.65
0.60
0.025
0.030
---
---
---
Grade 50 [345], Type 7 Grade 50 [345], Type 8
-----
-----
t ≤ 50 t ≤ 50
t≤2 t≤2
0.18 0.18
1.65 1.65
0.60 0.60
0.025 0.025
0.030 0.030
-----
-----
-----
K01802 -------
---------
t ≤ 100 -------
t≤4 -------
0.18 0.22 0.22 0.23
1.00-1.35 0.15-0.50 0.030 0.50-1.50 0.40 0.04 0.80-1.50 0.15-0.40 0.03 1.35 --0.04
0.030 0.05 0.04 0.04
------0.15
------0.20
------0.06
---
---
---
---
0.23
0.04
0.15
0.20
0.06
Grade A Grade 300W (44W) Grade 300WT (44WT) ASME SA-1011/SA-1011M Grade 50 [340], Class 1, HSLAS ASTM A1011/A1011M-14 Grade 50 [340], Class 1, HSLAS Note: This section continued on next page.
1.35
---
0.04
Others V 0.02-0.15; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.15; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 ----V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. Cb 0.005-0.05 V 0.01-0.15 V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02-0.15 V 0.06; Ti 0.006-0.04; N 0.003-0.015 Cb 0.005-0.05 V 0.01-0.15 V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02-0.15 V 0.06; Ti 0.006-0.04; N 0.003-0.015 V 0.08; Cb 0.008-0.10; N 0.030 V 0.15; Cb 0.10; N 0.030 V 0.15; Ti 0.15; Cb 0.10; N 0.030 Cb 0.05 ----V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-1011/SA-1011M
UNS No. ---
Designation Grade Q295A
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
81
3.2 Alloy Steels for Structural Steel Plates 3.2.1B Chemical Composition of High-Strength Low-Alloy Structural Steel Plates (Continued)
Specification ASME SA-572/SA-572M
ASTM A709/A709M-13a
CSA G40.21-13 ASME SA-1011/SA-1011M ASTM A1011/A1011M-14 GB/T 1591-94
UNS No. -------
Steel No. -------
Section Thickness mm in. t ≤ 100 t≤4 t ≤ 100 t≤4 t ≤ 100 t≤4
C 0.23 0.23 0.23
Mn 0.50-1.35 0.50-1.35 0.50-1.35
Si 0.40 0.40 0.40
Grade 50 [345], Type 5
---
---
t ≤ 100
t≤4
0.23
0.50-1.35
0.40
Grade 50 [345], Type 1 Grade 50 [345], Type 2 Grade 50 [345], Type 3
-------
-------
t ≤ 100 t ≤ 100 t ≤ 100
t≤4 t≤4 t≤4
0.23 0.23 0.23
0.50-1.35 0.50-1.35 0.50-1.35
0.40 0.40 0.40
Grade 50 [345], Type 5
---
---
t ≤ 100
t≤4
0.23
0.50-1.35
0.40
Grade 50 [345], Type 1 Grade 50 [345], Type 2 Grade 50 [345], Type 3
-------
-------
t ≤ 100 t ≤ 100 t ≤ 100
t≤4 t≤4 t≤4
0.23 0.23 0.23
0.50-1.35 0.50-1.35 0.50-1.35
0.40 0.40 0.40
Grade 50 [345], Type 5
---
---
t ≤ 100
t≤4
0.23
0.50-1.35
0.40
Grade 350W (50W) Grade 55 [380], Class 2, HSLAS Grade 55 [380], Class 2, HSLAS Grade Q345A
-----
-----
-----
-----
0.23 0.15
0.50-1.50 1.35
0.40 ---
---
---
---
---
0.15
1.35
---
---
---
---
---
0.20
1.00-1.60
0.55
Grade Q345B
---
---
---
---
0.20
1.00-1.60
0.55
Grade Q345C
---
---
---
---
0.20
1.00-1.60
0.55
Grade Q345D
---
---
---
---
0.18
1.00-1.60
0.55
Grade Q345E
---
---
---
---
0.18
1.00-1.60
0.55
K11510
---
t ≤ 100
t≤4
0.15
1.00
---
ASTM A242/A242M-13 Type 1 Note: This section continued on next page.
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.04 0.05 ------Cb 0.005-0.05 0.04 0.05 ------V 0.01-0.15 0.04 0.05 ------V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02-0.15 0.04 0.05 ------V 0.06; Ti 0.006-0.04; N 0.003-0.015 0.030 0.030 ------Cb 0.005-0.05 0.030 0.030 ------V 0.01-0.15 0.030 0.030 ------V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02-0.15 0.030 0.030 ------V 0.06; Ti 0.006-0.04; N 0.003-0.015 0.04 0.05 ------Cb 0.005-0.05 0.04 0.05 ------V 0.01-0.15 0.04 0.05 ------V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02-0.15 0.04 0.05 ------V 0.06; Ti 0.006-0.04; N 0.003-0.015 0.04 0.05 --------0.04 0.04 0.15 0.20 0.06 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. 0.04 0.04 0.15 0.20 0.06 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. 0.045 0.045 0.30 0.30 --V 0.02-0.15; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 0.040 0.040 0.30 0.30 --V 0.02-0.15; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 0.035 0.035 0.30 0.30 --V 0.02-0.15; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 0.030 0.030 0.30 0.30 --V 0.02-0.15; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 0.025 0.025 0.30 0.30 --V 0.02-0.15; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 0.15 0.05 ------Cu 0.20 min.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A572/A572M-15
Designation Grade 50 [345], Type 1 Grade 50 [345], Type 2 Grade 50 [345], Type 3
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
82
3.2 Alloy Steels for Structural Steel Plates 3.2.1B Chemical Composition of High-Strength Low-Alloy Structural Steel Plates (Continued) Steel No. -------
---
---
---
---
0.15
---
---
---
---
0.25
---
---
---
---
0.15
K11947
---
t ≤ 200
t≤8
0.19
Grade B
K12043
---
t ≤ 200
t≤8
0.20
Grade K
---
---
t ≤ 200
t≤8
0.17
ASTM A633/A633M-13
Grade C Grade D
K12000 K12037
-----
ASME SA-572/SA-572M
Grade 55 [380], Type 1 Grade 55 [380], Type 2 Grade 55 [380], Type 3
-------
-------
t ≤ 100 t ≤ 40 40 < t ≤ 100 t ≤ 50 t ≤ 50 t ≤ 50
t≤4 t ≤ 1.5 1.5 < t ≤ 4 t≤2 t≤2 t≤2
0.20 0.20 0.20 0.25 0.25 0.25
Grade 55 [380], Type 5
---
---
t ≤ 50
t≤2
0.25
Grade 55 [380], Type 1 Grade 55 [380], Type 2 Grade 55 [380], Type 3
-------
-------
t ≤ 50 t ≤ 50 t ≤ 50
t≤2 t≤2 t≤2
0.25 0.25 0.25
Grade 55 [380], Type 5
---
---
t ≤ 50
t≤2
0.25
Grade 60 [415], Type 3
---
---
t ≤ 40
t ≤ 1.5
0.18
Grade 60 [415], Type 7 Grade 60 [415], Type 8
-----
-----
t ≤ 40 t ≤ 40
t ≤ 1.5 t ≤ 1.5
0.18 0.18
ASME SA-1011/SA-1011M
Download From http://bbs.infoeach.com
ASTM A1011/A1011M-14
ASTM A588/A588M-15
ASTM A572/A572M-15
ASTM A656/A656M-13
Designation Grade 350WT (50WT) Grade 380W (55W) Grade 55 [380], Class 1, HSLAS Grade 60 [410], Class 2, HSLAS Grade 55 [380], Class 1, HSLAS Grade 60 [410], Class 2, HSLAS Grade A
Section Thickness mm in. -------------
C 0.22 0.23 0.25
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo Others 0.80-1.50 0.15-0.40 0.03 0.04 --------0.50-1.50 0.40 0.04 0.05 --------1.35 --0.04 0.04 0.15 0.20 0.06 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. 1.50 --0.04 0.04 0.15 0.20 0.06 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. 1.35 --0.04 0.04 0.15 0.20 0.06 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. 1.50 --0.04 0.04 0.15 0.20 0.06 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. 0.80-1.25 0.30-0.65 0.030 0.030 0.400.40 --V 0.02-0.10; Cu 0.25-0.40 0.65 0.75-1.35 0.15-0.50 0.030 0.030 0.400.50 --V 0.01-0.10; Cu 0.20-0.40 0.70 0.50-1.20 0.25-0.50 0.030 0.030 0.400.40 0.10 Cu 0.30-0.50; Cb 0.005-0.05 0.70 1.15-1.50 0.15-0.50 0.030 0.030 ------Cb 0.01-0.05 0.70-1.35 0.15-0.50 0.030 0.030 0.25 0.25 0.08 Cu 0.35 1.00-1.60 0.15-0.50 0.030 0.030 0.25 0.25 0.08 Cu 0.35 0.50-1.35 0.40 0.04 0.05 ------Cb 0.005-0.05 0.50-1.35 0.40 0.04 0.05 ------V 0.01-0.15 0.50-1.35 0.40 0.04 0.05 ------V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02-0.15 0.50-1.35 0.40 0.04 0.05 ------V 0.06; Ti 0.006-0.04; N 0.003-0.015 0.50-1.35 0.40 0.030 0.030 ------Cb 0.005-0.05 0.50-1.35 0.40 0.030 0.030 ------V 0.01-0.15 0.50-1.35 0.40 0.030 0.030 ------V 0.01-0.15; Cb 0.005-0.05 (Cb+V) 0.02-0.15 0.50-1.35 0.40 0.030 0.030 ------V 0.06; Ti 0.006-0.04; N 0.003-0.015 1.65 0.60 0.025 0.030 ------V 0.08; Cb 0.008-0.10; N 0.030 1.65 0.60 0.025 0.030 ------V 0.15; Cb 0.10; N 0.030 1.65 0.60 0.025 0.030 ------V 0.15; Ti 0.15; Cb 0.10; N 0.030
Download From http://bbs.infoeach.com
UNS No. -------
Specification CSA G40.21-13
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
83
3.2 Alloy Steels for Structural Steel Plates 3.2.1B Chemical Composition of High-Strength Low-Alloy Structural Steel Plates (Continued) Steel No. -------
---
---
---
---
0.15
1.50
---
0.04
0.04
0.15
0.20
0.06
---
---
---
---
0.26
1.50
---
0.04
0.04
0.15
0.20
0.06
---
---
---
---
0.15
1.50
---
0.04
0.04
0.15
0.20
0.06
-------
-------
t ≤ 32 t ≤ 32 t ≤ 32
t ≤ 1.25 t ≤ 1.25 t ≤ 1.25
0.26 0.26 0.26
0.50-1.35 0.50-1.35 0.50-1.35
0.40 0.40 0.40
0.04 0.04 0.04
0.05 0.05 0.05
-------
-------
-------
Grade 60 [415], Type 5
---
---
t ≤ 32
t ≤ 1.25
0.26
0.50-1.35
0.40
0.04
0.05
---
---
---
Grade 60 [415], Type 1 Grade 60 [415], Type 2 Grade 60 [415], Type 3
-------
-------
t ≤ 32 t ≤ 32 t ≤ 32
t ≤ 1.25 t ≤ 1.25 t ≤ 1.25
0.26 0.26 0.26
0.50-1.35 0.50-1.35 0.50-1.35
0.40 0.40 0.40
0.030 0.030 0.030
0.030 0.030 0.030
-------
-------
-------
Grade 60 [415], Type 5
---
---
t ≤ 32
t ≤ 1.25
0.26
0.50-1.35
0.40
0.030
0.030
---
---
---
Grade Q420A
---
---
---
---
0.20
1.00-1.70
0.55
0.045
0.045
0.40
0.70
---
Grade Q420B
---
---
---
---
0.20
1.00-1.70
0.55
0.040
0.040
0.40
0.70
---
Grade Q420C
---
---
---
---
0.20
1.00-1.70
0.55
0.035
0.035
0.40
0.70
---
Grade Q420D
---
---
---
---
0.20
1.00-1.70
0.55
0.030
0.030
0.40
0.70
---
Grade Q420E
---
---
---
---
0.20
1.00-1.70
0.55
0.025
0.025
0.40
0.70
---
Grade Q420C Grade Q420D Grade Q420E Note: This section continued on next page.
-------
-------
-------
-------
0.20 0.18 0.18
1.00-1.60 1.00-1.60 1.00-1.60
0.55 0.55 0.55
0.035 0.030 0.025
0.035 0.030 0.025
0.30 0.30 0.30
0.70 0.70 0.70
0.20 0.20 0.20
ASME SA-1011/SA-1011M
Download From http://bbs.infoeach.com
ASTM A1011/A1011M-14
ASME SA-572/SA-572M
ASTM A572/A572M-15
GB/T 1591-94
GB/T 16270-1996
Designation Grade 400W (60W) Grade 400WT (60WT) Grade 60 [410], Class 1, HSLAS Grade 65 [450], Class 2, HSLAS Grade 60 [410], Class 1, HSLAS Grade 65 [450], Class 2, HSLAS Grade 60 [415], Type 1 Grade 60 [415], Type 2 Grade 60 [415], Type 3
Section Thickness mm in. -------------
C 0.23 0.22 0.26
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo 0.50-1.50 0.40 0.04 0.05 ------0.80-1.60 0.15-0.40 0.03 0.04 ------1.50 --0.04 0.04 0.15 0.20 0.06
Others ----V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. Cb 0.005-0.05 V 0.01-0.15 V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02 to 0.15 V 0.06; Ti 0.006-0.04; N 0.003-0.015 Cb 0.005-0.05 V 0.01-0.15 V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02 to 0.15 V 0.06; Ti 0.006-0.04; N 0.003-0.015 V 0.02-0.20; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.10; Ti 0.20; Nb 0.06 V 0.10; Ti 0.20; Nb 0.06 V 0.10; Ti 0.20; Nb 0.06
Download From http://bbs.infoeach.com
UNS No. -------
Specification CSA G40.21-13
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
84
3.2 Alloy Steels for Structural Steel Plates 3.2.1B Chemical Composition of High-Strength Low-Alloy Structural Steel Plates (Continued) Steel No. ---
Section Thickness mm in. t ≤ 150 t≤6
C 0.22
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo 1.15-1.50 0.15-0.50 0.030 0.030 -------
Grade 65 [450], Type 1
---
---
Grade 65 [450], Type 2
---
---
Grade 65 [450], Type 3
---
---
13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13 t ≤ 0.5 13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13 t ≤ 0.5 13 < t ≤ 32 0.5 < t ≤ 1.25
0.23 0.26 0.23 0.26 0.23
0.80-1.65 0.50-1.35 0.80-1.65 0.50-1.35 0.80-1.65
0.40 0.40 0.40 0.40 0.40
0.04 0.04 0.04 0.04 0.04
0.05 0.05 0.05 0.05 0.05
-----------
-----------
-----------
0.26
0.50-1.35
0.40
0.04
0.05
---
---
---
0.23
0.80-1.65
0.40
0.04
0.05
---
---
---
0.26
0.50-1.35
0.40
0.04
0.05
---
---
---
0.23 0.26 0.23 0.26 0.23
0.80-1.65 0.50-1.35 0.80-1.65 0.50-1.35 0.80-1.65
0.40 0.40 0.40 0.40 0.40
0.030 0.030 0.030 0.030 0.030
0.030 0.030 0.030 0.030 0.030
-----------
-----------
-----------
0.26
0.50-1.35
0.40
0.030
0.030
---
---
---
0.23
0.80-1.65
0.40
0.030
0.030
---
---
---
Designation Grade E
ASME SA-572/SA-572M
Download From http://bbs.infoeach.com
ASTM A572/A572M-15
ASME SA-1011/SA-1011M ASTM A1011/A1011M-14 ASTM A656/A656M-13
ASME SA-1011/SA-1011M ASTM A1011/A1011M-14
t ≤ 13 Grade 65 [450], Type 5
---
---
13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13
Grade 65 [450], Type 1
---
---
Grade 65 [450], Type 2
---
---
Grade 65 [450], Type 3
---
---
---
---
t ≤ 0.5
13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13 t ≤ 0.5 13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13 t ≤ 0.5 13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13
Grade 65 [450], Type 5
t ≤ 0.5
t ≤ 0.5
13 < t ≤ 32 0.5 < t ≤ 1.25 t ≤ 13
t ≤ 0.5
0.26
0.50-1.35
0.40
0.030
0.030
---
---
---
Grade 65 [450], Class 1, HSLAS Grade 65 [450], Class 1, HSLAS Grade 70 [485], Type 3
---
---
---
---
0.26
1.50
---
0.04
0.04
0.15
0.20
0.06
---
---
---
---
0.26
1.50
---
0.04
0.04
0.15
0.20
0.06
---
---
t ≤ 25
t≤1
0.18
1.65
0.60
0.025
0.030
---
---
---
Grade 70 [485], Type 7 Grade 70 [485], Type 8
-----
-----
t ≤ 25 t ≤ 25
t≤1 t≤1
0.18 0.18
1.65 1.65
0.60 0.60
0.025 0.025
0.030 0.030
-----
-----
-----
Grade 70 [480], Class 1, HSLAS Grade 70 [480], Class 1, HSLAS
---
---
---
---
0.26
1.65
---
0.04
0.04
0.15
0.20
0.06
---
---
---
---
0.26
1.65
---
0.04
0.04
0.15
0.20
0.16
Others V 0.04-0.11; N 0.03; Cb 0.01-0.05 Cb 0.005-0.05 Cb 0.005-0.05 V 0.01-0.15 V 0.01-0.15 V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02 to 0.15 V 0.01-0.15; Cb 0.005-0.05; (Cb+V) 0.02 to 0.15 V 0.06; Ti 0.006-0.04; N 0.003-0.015 V 0.06; Ti 0.006-0.04; N 0.003-0.015 Cb 0.005-0.05 Cb 0.005-0.05 V 0.01-0.15 V 0.01-0.15 V 0.01-0.15; Cb 0.005-0.05 (Cb+V) 0.02 to 0.15 V 0.01-0.15; Cb 0.005-0.05 (Cb+V) 0.02 to 0.15 V 0.06; Ti 0.006-0.04; N 0.003-0.015 V 0.06; Ti 0.006-0.04; N 0.003-0.015 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.08; Cb 0.008-0.10; N 0.030 V 0.15; Cb 0.10; N 0.030 V 0.15; Ti 0.15; Cb 0.10; N 0.030 V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min. V 0.005 min.; Cu 0.20 nom.; Ti 0.005 min.; Cb 0.005 min.
Download From http://bbs.infoeach.com
UNS No. K12202
Specification ASTM A633/A633M-13
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
85
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates
Specification GB 11251-89
ISO 4950-2:1995 A1:2003
Grade E 355, Quality E
Grade 50W [345W], Type A Grade 50W [345W], Type B Note: This section continued on next page.
UNS No. ---------
Steel No. ---------
---
---
-----
-----
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. --------400-600 --21 --------400-650 --20 --------450-700 --21 3 ≤ t ≤ 16 --355 --470-630 --22 16 < t ≤ 35 --345 --470-630 --22 35 < t ≤ 50 --335 --470-630 --22 50 < t ≤ 70 --325 --470-630 --22 70 < t ≤ 100 --305 --450-610 --22 100 < t ≤ 125 --295 --440-600 --22 125 < t ≤ 150 --285 --430-590 --22 3 ≤ t ≤ 16 --355 --470-630 --22 16 < t ≤ 35 --345 --470-630 --22 35 < t ≤ 50 --335 --470-630 --22 50 < t ≤ 70 --325 --470-630 --22 70 < t ≤ 100 --305 --450-610 --22 100 < t ≤ 125 --295 --440-600 --22 125 < t ≤ 150 --285 --430-590 --22 t ≤ 100 t≤4 345 50 485 70 21 t ≤ 100 t≤4 345 50 485 70 21
Heat Treatment A, N or NT A, N or NT A, N or NT N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR N, NT or CtR QT QT
Other ------see standard for impact data
see standard for impact data
see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A709/A709M-13a
Designation Grade 15 Cr Grade 20 Cr Grade 20CrMnSiA Grade E 355, Quality DD
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
86
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates (Continued)
Specification GB/T 1591-94
Steel No. ---
Grade Q390B
---
---
Grade Q390C
---
---
Grade Q390D
---
---
Grade Q390E
---
---
K20747
---
Grade 25CrMnSiA
---
---
Grade 30 Cr
---
---
ASTM A710/A710M-02 (2013) Grade A, Class 2
GB 11251-89
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 16 --390 --490-650 --19 16 < t ≤ 35 --370 --490-650 --19 35 < t ≤ 50 --350 --490-650 --19 50 < t ≤ 100 --330 --490-650 --19 t ≤ 16 --390 --490-650 --19 16 < t ≤ 35 --370 --490-650 --19 35 < t ≤ 50 --350 --490-650 --19 50 < t ≤ 100 --330 --490-650 --19 t ≤ 16 --390 --490-650 --20 16 < t ≤ 35 --370 --490-650 --20 35 < t ≤ 50 --350 --490-650 --20 50 < t ≤ 100 --330 --490-650 --20 t ≤ 16 --390 --490-650 --20 16 < t ≤ 35 --370 --490-650 --20 35 < t ≤ 50 --350 --490-650 --20 50 < t ≤ 100 --330 --490-650 --20 t ≤ 16 --390 --490-650 --20 16 < t ≤ 35 --370 --490-650 --20 35 < t ≤ 50 --350 --490-650 --20 50 < t ≤ 100 --330 --490-650 --20 t ≤ 25 t≤1 450 65 495 72 20 25 < t ≤ 50 14 345 50 415 60 20 --------500-700 --20 --------1000 --10 --------500-700 --19
Heat Treatment HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT HR, CtR, N or NT N+PHT N+PHT N+PHT N+PHT A, N or NT QT A, N or NT
Other --------L: 34 J @ 20°C --------L: 34 J @ 0°C --------L: 34 J @ -20°C --------L: 27 J @ -40°C --------152-221 HB 39 J @ RT ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
UNS No. ---
Designation Grade Q390A
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
87
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates (Continued) Steel No. ---
Grade 35 Cr Grade 27SiMn Grade 40 Cr Grade Q460C
---------
---------
Grade Q460D
---
---
Grade Q460E
---
---
Grade Q460C
---
---
Grade Q460D
---
---
Grade Q460E
---
---
Designation Grade 30CrMnSiA
GB/T 1591-94
Download From http://bbs.infoeach.com
GB/T 16270-1996
Note: This section continued on next page.
Section Thickness/Diameter Yield Strength, min. mm in. MPa ksi ----------------------------------------t ≤ 16 --460 --16 < t ≤ 35 --440 --35 < t ≤ 50 --420 --50 < t ≤ 100 --400 --t ≤ 16 --460 --16 < t ≤ 35 --440 --35 < t ≤ 50 --420 --50 < t ≤ 100 --400 --t ≤ 16 --460 --16 < t ≤ 35 --440 --35 < t ≤ 50 --420 --50 < t ≤ 100 --400 --t ≤ 50 --460 --50 < t ≤ 100 --440 --t ≤ 50 --460 --50 < t ≤ 100 --440 --t ≤ 50 --460 --50 < t ≤ 100 --440 ---
Tensile Strength, min. Elongation MPa ksi % min. 550-750 --19 1100 --10 550-750 --18 550-800 --18 550-800 --16 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-720 --17 550-710 T --17 T 550-710 T --17 T 550-710 T --17 T 550-710 T --17 T 550-710 T --17 T 550-710 T --17 T
Heat Treatment A, N or NT QT A, N or NT A, N or NT A, N or NT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT HR, CtR, N, NT or QT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT
Other 152-221 HB 39 J @ RT --------L: 34 J @ 0°C --------L: 34 J @ -20°C --------L: 27 J @ -40°C see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
UNS No. ---
Specification GB 11251-89
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
88
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates (Continued) Steel No. ---
Grade E 460, Quality E
---
---
Grade HPS 70W [HPS 485W] ASTM A710/A710M-02 (2013) Grade A, Class 3
---
---
K20747
---
Designation Grade E 460, Quality DD
ASTM A709/A709M-13a
Download From http://bbs.infoeach.com
CSA G40.21-13
Grade 480WT (70WT)
---
---
GB 11251-89
Grade 35CrMnSiA
---
---
Section Thickness/Diameter Yield Strength, min. mm in. MPa ksi 3 ≤ t ≤ 50 --460 --50 < t ≤ 70 --440 --3 ≤ t ≤ 50 --460 --50 < t ≤ 70 --440 --t ≤ 100 t≤4 485 70 t ≤ 30 30 < t ≤ 50 50 < t ≤ 100 t > 100 ----t ≤ 65 65 < t ≤ 200 ---
t ≤ 1.25 1.25 < t ≤ 2 24 ----t ≤ 2.5 2.5 < t ≤ 8 ---
550 515 450 415 480 480 480 450 ---
80 75 65 60 70 70 70 65 ---
Tensile Strength, min. Elongation MPa ksi % min. 570-720 T --17 T 570-720 T --17 T 570-720 T --17 T 570-720 T --17 T 585-760 85-110 19 585 585 515 485 590-790 590-790 590-790 590-790 600-800
85 85 75 70 85-115 85-115 85-115 85-115 ---
20 20 20 20 17 17 17 L, 14 T 17 L, 14 T 16
Heat Treatment QT QT QT QT AR, CtR, TMCP or QT Q+PHT Q+PHT Q+PHT Q+PHT AR, N or CtR SR, A or N AR, N or CtR AR, N or CtR A, N or NT
Other see standard for impact data see standard for impact data see standard for impact data --------see standard for impact data
---
Download From http://bbs.infoeach.com
UNS No. ---
Specification ISO 4950-3:1995 A1:2003
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
89
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates (Continued)
Specification GB/T 16270-1996
CSA G40.21-13
Steel No. ---
Grade Q500E
---
---
Grade 550WT (80WT)
---
---
K20747
---
ASTM A710/A710M-02 (2013) Grade A, Class 1
Section Thickness/Diameter Yield Strength, min. mm in. MPa ksi t ≤ 50 --500 --50 < t ≤ 100 --480 --t ≤ 50 --500 --50 < t ≤ 100 --480 ------550 80 t ≤ 65 t ≤ 2.5 550 80 65 < t ≤ 200 2.5 < t ≤ 8 520 75 t≤8 t ≤ 0.3125 585 85 8 < t ≤ 20 0.3125 < t ≤ 550 80 0.75
Tensile Strength, min. Elongation MPa ksi % min. 610-770 T --16 T 610-770 T --16 T 610-770 T --16 T 610-770 T --16 T 620-860 90-125 15 620-860 90-125 15 L, 12 T 620-860 90-125 15 L, 12 T 620 90 20 620 90 20
Heat Treatment CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT SR, A or N AR, N or CtR AR, N or CtR PHT PHT
Other see standard for impact data
see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
UNS No. ---
Designation Grade Q500D
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
90
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates (Continued)
Specification GB/T 16270-1996
Steel No. ---
Grade Q550E
---
---
Grade Q620D
---
---
Grade Q620E
---
---
Grade A
K11856
---
Grade B
K11630
---
Grade E
K21604
---
Grade F
K11576
---
Grade H
K11646
---
Grade P
K21650
---
Grade Q
---
---
Grade S
---
---
Section Thickness/Diameter Yield Strength, min. mm in. MPa ksi t ≤ 50 --550 --50 < t ≤ 100 --530 --t ≤ 50 --550 --50 < t ≤ 100 --530 --t ≤ 50 --620 ---
Tensile Strength, min. Elongation MPa ksi % min. 670-830 T --16 T 670-830 T --16 T 670-830 T --16 T 670-830 T --16 T 720-890 T --15 T
Heat Treatment CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT CtR, N, QT or NT
50 < t ≤ 100
---
600
---
720-890 T
---
15 T
CtR, N, QT or NT
t ≤ 50
---
620
---
720-890 T
---
15 T
CtR, N, QT or NT
50 < t ≤ 100
---
600
---
720-890 T
---
15 T
CtR, N, QT or NT
t ≤ 20 20 < t ≤ 32 t ≤ 20 20 < t ≤ 32 t ≤ 20 20 < t ≤ 65 65 < t ≤ 150 t ≤ 20 20 < t ≤ 65 t ≤ 20 20 < t ≤ 50 t ≤ 20 20 < t ≤ 65 65 < t ≤ 150 t ≤ 20 20 < t ≤ 65 65 < t ≤ 150 t ≤ 20 20 < t ≤ 65
t ≤ 0.75 0.75 < t ≤ 1.25 t ≤ 0.75 0.75 < t ≤ 1.25 t ≤ 0.75 0.75 < t ≤ 2.5 2.5 < t ≤ 6 t ≤ 0.75 0.75 < t ≤ 2.5 t ≤ 0.75 0.75 < t ≤ 2 t ≤ 0.75 0.75 < t ≤ 2.5 2.5 < t ≤ 6 t ≤ 0.75 0.75 < t ≤ 2.5 2.5 < t ≤ 6 t ≤ 0.75 0.75 < t ≤ 2.5
690 690 690 690 690 690 620 690 690 690 690 690 690 620 690 690 620 690 690
100 100 100 100 100 100 90 100 100 100 100 100 100 90 100 100 90 100 100
760-895 760-895 760-895 760-895 760-895 760-895 690-895 760-895 760-895 760-895 760-895 760-895 760-895 690-895 760-895 760-895 690-895 760-895 760-895
110-130 110-130 110-130 110-130 110-130 110-130 100-130 110-130 110-130 110-130 110-130 110-130 110-130 100-130 110-130 110-130 100-130 110-130 110-130
18 L 18 L 18 L 18 L 18 L 18 L 16 L 18 L 18 L 18 L 18 L 18 L 18 L 16 L 18 L 18 L 16 L 18 L 18 L
QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR QT or SR
Other see standard for impact data
see standard for impact data see standard for impact data see standard for impact data see standard for impact data 235-293 HB --235-293 HB --235-293 HB ----235-293 HB --235-293 HB --235-293 HB ----235-293 HB ----235-293 HB ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A514/A514M-14
UNS No. ---
Designation Grade Q550D
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
91
3.2 Alloy Steels for Structural Steel Plates 3.2.2A Mechanical Properties of Alloy Steels for Structural Steel Plates (Continued)
Specification ASTM A709/A709M-13a
CSA G40.21-13
JIS G 3128:2009
UNS No. ---
Steel No. ---
2.5 < t ≤ 4
620
90
690-895
100-130
16
QT
t ≤ 65 65 < t ≤ 100 t ≤ 65 65 < t ≤ 100 t ≤ 50
t ≤ 2.5 2.5 < t ≤ 4 t ≤ 2.5 2.5 < t ≤ 4 ---
700 620 700 620 690
100 90 100 90 ---
760-895 760-895 760-895 760-895 770-940 T
110-130 110-130 110-130 110-130 ---
18 L, 16 T 18 L, 16 T 18 L, 16 T 18 L, 16 T 14 T
QT QT QT QT CtR, N, QT or NT
50 < t ≤ 100
---
670
---
770-940 T
---
14 T
CtR, N, QT or NT
t ≤ 50
---
690
---
770-940 T
---
14 T
CtR, N, QT or NT
50 < t ≤ 100
---
670
---
770-940 T
---
14 T
CtR, N, QT or NT
---
6 ≤ t ≤ 16
---
685
---
780-930 T
---
16 T
QT
---
16 < t ≤ 20 20 < t ≤ 50 50 < t ≤ 100 6 ≤ t ≤ 16
---------
685 685 665 685
---------
780-930 T 780-930 T 760-910 T 780-930 T
---------
24 T 16 T 16 T 16 T
QT QT QT QT
---
16 < t ≤ 20 20 < t ≤ 50 50 < t ≤ 100 6 ≤ t ≤ 16
---------
685 685 665 685
---------
780-930 T 780-930 T 760-910 T 780-930 T
---------
24 T 16 T 16 T 16 T
QT QT QT QT
16 < t ≤ 20 20 < t ≤ 50 50 < t ≤ 100
-------
685 685 665
-------
780-930 T 780-930 T 760-910 T
-------
24 T 16 T 16 T
QT QT QT
---
---
Grade 700QT (100QT)
---
---
Grade Q690D
---
---
Grade SHY685
Grade SHY685N
Grade SHY685NS
---
---
---
---
Heat Treatment QT
65 < t ≤ 100 Grade 700Q (100Q)
Grade Q690E
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 65 t ≤ 2.5 690 100 760-895 110-130 18
---
Other see standard for impact data see standard for impact data ----see standard for impact data see standard for impact data see standard for impact data see standard for impact data see standard for impact data see standard for impact data L: 47 J @ -20°C L: 47 J @ -20°C L: 47 J @ -20°C see standard for impact data L: 47 J @ -20°C L: 47 J @ -20°C L: 47 J @ -20°C see standard for impact data 47 J @ -40°C 47 J @ -40°C see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 16270-1996
Designation Grade HPS 100W [HPS 690W]
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
92
3.2 Alloy Steels for Structural Steel Plates 3.2.2B Chemical Composition of Alloy Steels for Structural Steel Plates
Specification GB 11251-89
ISO 4950-2:1995 A1:2003
GB/T 1591-94
Steel No. ---------
Grade E 355, Quality E
---
---
---
---
0.18
0.9-1.6
0.50
0.025
0.025
Grade 50W [345W], Type A Grade 50W [345W], Type B Grade Q390A
-------
-------
t ≤ 100 t ≤ 100 ---
t≤4 t≤4 ---
0.19 0.20 0.20
0.80-1.25 0.75-1.35 1.00-1.60
0.30-0.65 0.15-0.50 0.55
0.04 0.04 0.045
Grade Q390B
---
---
---
---
0.20
1.00-1.60
0.55
Grade Q390C
---
---
---
---
0.20
1.00-1.60
Grade Q390D
---
---
---
---
0.20
Grade Q390E
---
---
---
---
K20747
---
---
---
-----
-----
-----
-----
ASTM A710/A710M-02 (2013) Grade A, Class 2 GB 11251-89
Grade 25CrMnSiA Grade 30 Cr
Section Thickness mm in. C Mn ----0.12-0.18 0.40-0.70 ----0.18-0.24 0.50-0.80 ----0.17-0.23 0.80-1.10 ----0.18 0.9-1.6
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.17-0.37 0.035 0.035 0.70-1.00 0.30 0.15 0.17-0.37 0.035 0.035 0.70-1.00 0.30 0.15 0.90-1.20 ----------0.50 0.030 0.030 0.25 0.30 0.10
0.30
0.10
0.05 0.40-0.65 0.05 0.40-0.70 0.045 0.30
0.40 0.50 0.70
-------
0.040
0.040
0.30
0.70
---
0.55
0.035
0.035
0.30
0.70
---
1.00-1.60
0.55
0.030
0.030
0.30
0.70
---
0.20
1.00-1.60
0.55
0.025
0.025
0.30
0.70
---
0.07
0.40-0.70
0.40
0.025
--0.17-0.37
-----
0.025 0.60-0.90 0.70-1.00 0.150.25 ----------0.80-1.10 -----
----0.27-0.34 0.50-0.80
0.25
Others Cu 0.30 Cu 0.30 --V 0.02-0.10; Al 0.020 min.; Cu 0.35; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.10; Al 0.020 min.; Cu 0.35; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.10; Cu 0.25-0.40 V 0.01-0.10; Cu 0.20-0.40 V 0.02-0.20; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 Cu 1.00-1.30; Cb 0.02 min. -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A709/A709M-13a
UNS No. ---------
Designation Grade 15 Cr Grade 20 Cr Grade 20CrMnSiA Grade E 355, Quality DD
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
93
3.2 Alloy Steels for Structural Steel Plates 3.2.2B Chemical Composition of Alloy Steels for Structural Steel Plates (Continued)
Specification GB 11251-89
GB/T 1591-94
ISO 4950-3:1995 A1:2003
ASTM A709/A709M-13a
Steel No. -----------
Grade Q460D
---
---
---
---
0.20
1.00-1.70
0.55
0.030
0.030
0.70
0.70
---
Grade Q460E
---
---
---
---
0.20
1.00-1.70
0.55
0.025
0.025
0.70
0.70
---
Grade Q460C Grade Q460D Grade Q460E Grade E 460, Quality DD
---------
---------
---------
---------
0.20 0.18 0.18 0.20
1.00-1.60 1.00-1.60 1.00-1.60 0.7-1.7
0.55 0.55 0.55 0.55
0.035 0.030 0.025 0.035
0.035 0.030 0.025 0.035
0.30 0.30 0.30 2
0.70 0.70 0.70 2
0.20 0.20 0.20 1
Grade E 460, Quality E
---
---
---
---
0.20
0.7-1.7
0.55
0.030
0.030
2
2
1
Grade HPS 70W [HPS 485W]
---
---
---
---
0.11
0.020
0.006 0.45-0.70 0.25-0.40 0.020.08
Note: This section continued on next page.
Section Thickness mm in. ---------------------
C 0.28-0.34 0.32-0.39 0.24-0.32 0.37-0.44 0.20
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo 0.80-1.10 0.90-1.20 ----- 0.80-1.10 ----0.50-0.80 0.17-0.37 ----------1.10-1.40 1.10-1.40 ----------0.50-0.80 0.17-0.37 ----- 0.80-1.10 ----1.00-1.70 0.55 0.035 0.035 0.70 0.70 ---
1.10-1.35 0.30-0.50
Others --------V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.02-0.20; Al 0.015 min.; Cu 0.30; Ti 0.02-0.20; Nb 0.015-0.060 V 0.10; Ti 0.20; Nb 0.06 V 0.10; Ti 0.20; Nb 0.06 V 0.10; Ti 0.20; Nb 0.06 V 0.10; Cu 1.5; Ti 0.20; Nb 0.060; N 0.020; B 0.005; Zr 0.15 V 0.10; Cu 1.5; Ti 0.20; Nb 0.060; N 0.020; B 0.005; Zr 0.15 V 0.04-0.08; Al 0.010-0.040; Cu 0.25-0.40; N 0.015
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 16270-1996
UNS No. -----------
Designation Grade 30CrMnSiA Grade 35 Cr Grade 27SiMn Grade 40 Cr Grade Q460C
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
94
3.2 Alloy Steels for Structural Steel Plates 3.2.2B Chemical Composition of Alloy Steels for Structural Steel Plates (Continued)
Specification Designation ASTM A710/A710M-02 (2013) Grade A, Class 3 CSA G40.21-13 GB 11251-89 GB/T 16270-1996
UNS Steel No. No. K20747 ---
Section Thickness mm in. -----
-------
-------
-------
-------
Grade Q500E
---
---
---
---
--K20747
-----
--t ≤ 20
--t ≤ 0.75
CSA G40.21-13 Grade 550WT (80WT) ASTM A710/A710M-02 (2013) Grade A, Class 1
Mn 0.40-0.70
Si 0.40
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Grade 480WT (70WT) Grade 35CrMnSiA Grade Q500D
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.025 0.025 0.60-0.90 0.70-1.00 0.15- Cu 1.00-1.30; Cb 0.02 min. 0.25 0.26 0.80-1.50 0.15-0.40 0.03 0.04 --------0.32-0.39 0.80-1.10 1.10-1.40 ----- 1.10-1.40 ------0.18 1.00-1.60 0.55 0.030 0.030 0.60 1.00 0.40 V 0.10; Ti 0.20; Nb 0.06; B 0.003 0.18 1.00-1.60 0.55 0.025 0.025 0.60 1.00 0.40 V 0.10; Ti 0.20; Nb 0.06; B 0.003 0.15 1.75 0.15-0.40 0.03 0.04 -------0.07 0.40-0.70 0.40 0.025 0.025 0.60-0.90 0.70-1.00 0.15- Cu 1.00-1.30; Cb 0.02 min. 0.25 C 0.07
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
95
3.2 Alloy Steels for Structural Steel Plates 3.2.2B Chemical Composition of Alloy Steels for Structural Steel Plates (Continued)
Specification GB/T 16270-1996
ASTM A709/A709M-13a
Steel No. ---
Section Thickness mm in. -----
Grade Q550E
---
---
---
Grade Q620D
---
---
Grade Q620E
---
Grade A
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.030 0.030 0.60 1.00 0.40
C 0.18
Mn 1.00-1.60
Si 0.55
---
0.18
1.00-1.60
0.55
0.025
0.025
0.60
1.00
0.40
---
---
0.18
1.00-1.60
0.55
0.030
0.030
0.80
1.20
0.60
---
---
---
0.18
1.00-1.60
0.55
0.025
0.025
0.80
1.20
0.60
K11856
---
t ≤ 32
t ≤ 1.25
0.15-0.21 0.80-1.10 0.40-0.80
0.030
0.030 0.50-0.80
---
Grade B
K11630
---
t ≤ 32
t ≤ 1.25
0.12-0.21 0.70-1.00 0.20-0.35
0.030
0.030 0.40-0.65
---
Grade E
K21604
---
t ≤ 150
t≤6
0.12-0.20 0.40-0.70 0.20-0.40
0.030
0.030 1.40-2.00
---
Grade F
K11576
---
t ≤ 65
t ≤ 2.5
0.10-0.20 0.60-1.00 0.15-0.35
0.030
0.030 0.40-0.65 0.70-1.00
Grade H
K11646
---
t ≤ 50
t≤2
0.12-0.21 0.95-1.30 0.20-0.35
0.030
0.030 0.40-0.65 0.30-0.70
Grade P
K21650
---
t ≤ 150
t≤6
0.12-0.21 0.45-0.70 0.20-0.35
0.030
0.030 0.85-1.20 1.20-1.50
Grade Q
---
---
t ≤ 150
t≤6
0.14-0.21 0.95-1.30 0.15-0.35
0.030
0.030 1.00-1.50 1.20-1.50
Grade S
---
---
t ≤ 65
t ≤ 2.5
0.11-0.21 1.10-1.50 0.15-0.45
0.030
0.020
Grade HPS 100W [HPS 690W]
---
---
t ≤ 100
t≤4
0.015
0.006 0.40-0.65 0.65-0.90
Note: This section continued on next page.
0.08
0.95-1.50 0.15-0.35
---
---
Others V 0.10; Ti 0.20; Nb 0.06; B 0.003 V 0.10; Ti 0.20; Nb 0.06; B 0.003 V 0.10; Ti 0.20; Nb 0.06; B 0.003 V 0.10; Ti 0.20; Nb 0.06; B 0.003 B 0.0025; Zr 0.05-0.15
0.180.28 0.15- V 0.03-0.08; Ti 0.01-0.10; 0.25 B 0.0005-0.005 0.40- Ti 0.01-0.10; B 0.001-0.005 0.60 0.40- V 0.03-0.08; Cu 0.15-0.50; 0.60 B 0.0005-0.006 0.20V 0.03-0.08; 0.30 B 0.0005-0.005 0.45B 0.001-0.005 0.60 0.40V 0.03-0.08 0.60 0.10V 0.06; Cb 0.06; 0.60 B 0.001-0.005 0.40- V 0.04-0.08; Cb 0.01-0.03; 0.65 Cu 0.90-1.20; N 0.015; Al 0.020-0.050
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A514/A514M-14
UNS No. ---
Designation Grade Q550D
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
96
3.2 Alloy Steels for Structural Steel Plates 3.2.2B Chemical Composition of Alloy Steels for Structural Steel Plates (Continued)
Specification CSA G40.21-13 GB/T 16270-1996
Steel No. -------
Section Thickness mm in. -------------
Grade Q690E
---
---
---
Grade SHY685
---
---
Grade SHY685N
---
---
Grade SHY685NS
---
---
6 ≤ t ≤ 50 50 < t ≤ 75 75 < t ≤ 100 6 ≤ t ≤ 50 50 < t ≤ 75 75 < t ≤ 100 6 ≤ t ≤ 50 50 < t ≤ 75 75 < t ≤ 100
C 0.20 0.20 0.18
Weight, %max, Unless Otherwise Specified Mn Si P S Cr Ni Mo 1.50 0.15-0.40 0.03 0.04 ------1.50 0.15-0.40 0.03 0.04 ------1.00-1.60 0.55 0.030 0.030 1.20 1.50 0.60
---
0.18
1.00-1.60
0.55
0.025
0.025
1.20
1.50
0.60
-------------------
0.18 0.18 0.18 0.18 0.18 0.18 0.14 0.14 0.14
1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50
0.55 0.55 0.55 0.55 0.55 0.55 0.55 0.55 0.55
0.030 0.030 0.030 0.030 0.030 0.030 0.015 0.015 0.015
0.025 0.025 0.025 0.025 0.025 0.025 0.015 0.015 0.015
1.20 1.20 1.20 0.80 0.80 0.80 0.80 0.80 0.80
------0.30-1.50 0.30-1.50 0.30-1.50 0.30-1.50 0.30-1.50 0.30-1.50
0.60 0.60 0.60 0.60 0.60 0.60 0.60 0.60 0.60
Others B 0.0005-0.005 B 0.0005-0.005 V 0.10; Ti 0.20; Nb 0.06; B 0.003 V 0.10; Ti 0.20; Nb 0.06; B 0.003 V 0.10; Cu 0.50; B 0.005 V 0.10; Cu 0.50; B 0.005 V 0.10; Cu 0.50; B 0.005 V 0.10; Cu 0.50; B 0.005 V 0.10; Cu 0.50; B 0.005 V 0.10; Cu 0.50; B 0.005 V 0.05; Cu 0.50; B 0.005 V 0.05; Cu 0.50; B 0.005 V 0.05; Cu 0.50; B 0.005
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 3128:2009
UNS No. -------
Designation Grade 700Q (100Q) Grade 700QT (100QT) Grade Q690D
Handbook of Comparative World Steel Standards
Chapter 3
Structural Steel Plates
97
3.3 Structural Steels with Improved Atmospheric Corrosion Resistance 3.3A Mechanical Properties of Structural Steels with Improved Atmospheric Corrosion-Resistance
Specification ISO 4952:2006
GB/T 18982-2003
UNS No. ---
Steel No. ---
Grade S235W, Quality C
---
---
Grade S235W, Quality D
---
---
Grade HSA 235W, Class B
---
---
Grade HSA 235W, Class D
---
---
Grade Q295GNHJ
---
---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. t ≤ 16 --235 --360-520 --26 16 < t ≤ 40 --225 --360-520 --26 40 < t ≤ 63 --215 --360-520 --25 t ≤ 16 --235 --360-520 --26 16 < t ≤ 40 --225 --360-520 --26 40 < t ≤ 63 --215 --360-520 --25 t ≤ 16 --235 --360-520 --26 16 < t ≤ 40 --225 --360-520 --26 40 < t ≤ 63 --215 --360-520 --25 t 1.50 t≤2 t>2 t ≤ 1.50 t > 1.50 --------0.057 ≤ t < 0.089 0.089 ≤ t < 0.145 0.145 ≤ t < 0.270 0.057 ≤ t < 0.089 0.089 ≤ t < 0.145 0.145 ≤ t < 0.270
295 240 240 240 240 240 240 240 240 245 245 245 245 260 260 260 260 260 260
--35 35 35 35 35 35 35 35 --------38 38 38 38 38 38
Tensile Strength, min. Elongation MPa ksi % min. 410-490 T --21 410-490 T --25 415-550 60-80 25 415-550 60-80 25 415-550 60-80 25 415-550 60-80 25 415-550 60-80 25 415-550 60-80 25 415-550 60-80 25 415-550 60-80 25 415-515 T 60-75 T 17 T 415-515 T 60-75 T 18 T 415-515 T 60-75 T 20 T 415-515 T 60-75 T 17 T 415-515 T 60-75 T 18 T 415-515 T 60-75 T 20 T 440 T --26 T
Heat Treatment AR, N, Q+T or TMCP N, Q+T, TMCP AR or N or SR or N+SR N AR or N or SR or N+SR N AR, N, SR or N+SR N AR, N, SR or N+SR N HR HR HR HR HR HR HR, CtR or A
440 L 450-585 450-585 450-585 450-585 450-585 450-585 450-585 450-585 450-590 450-590 450-540 T 450-540 T 450-585 T 450-585 T 450-585 T 450-585 T 450-585 T 450-585 T
HR AR or N or SR or N+SR N AR or N or SR or N+SR N AR, N, SR or N+SR N AR, N, SR or N+SR N AR, N or SR N AR, N, Q+T or TMCP N, Q+T, TMCP HR HR HR HR HR HR
--65-85 65-85 65-85 65-85 65-85 65-85 65-85 65-85 --------65-85 T 65-85 T 65-85 T 65-85 T 65-85 T 65-85 T
26 L 23 23 23 23 23 23 23 23 19 23 19 23 15 T 16 T 18 T 15 T 16 T 18 T
Other --------------------------------see standard for impact data ---------------------------------------
Download From http://bbs.infoeach.com
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi --6 ≤ t ≤ 50 --225 --50 < t ≤ 200 --225 ----t ≤ 50 t≤2 220 32 t > 50 t>2 220 32 --t ≤ 40 t ≤ 1.50 220 32 t > 40 t > 1.50 220 32 --t ≤ 50 t≤2 220 32 t > 50 t>2 220 32 --t ≤ 40 t ≤ 1.50 220 32 t > 40 t > 1.50 220 32 --1.5 ≤ t < 2.2 0.057 ≤ t < 0.089 240 35 2.2 ≤ t < 3.8 0.089 ≤ t < 0.145 240 35 3.8 ≤ t < 7.0 0.145 ≤ t < 0.270 240 35 --1.5 ≤ t < 2.2 0.057 ≤ t < 0.089 240 35 2.2 ≤ t < 3.8 0.089 ≤ t < 0.145 240 35 3.8 ≤ t < 7.0 0.145 ≤ t < 0.270 240 35 ------295 ---
Specification JIS G 3118:2010
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
115
4.1 Carbon Steels for Pressure Vessel Plates 4.1A Mechanical Properties of Carbon Steels for Pressure Vessel Plates (Continued) UNS No. ---
EN 10120:2008 JIS G 3103:2012
P310NB Symbol SB480
-----
JIS G 3118:2010
Symbol SGV480
---
ASME SA-515/SA-515M
Grade 70 [485]
K03101
ASME SA-516/SA-516M
Grade 70 [485]
K02700
ASME SA-537/SA-537M
Class 1
K12437
ASME SA-737/SA-737M ASTM A515/A515M-10
Grade B Grade 70 [485]
K12001 K03101
ASTM A516/A516M-10
Grade 70 [485]
K02700
ASME SA-414/SA-414M
Grade F
K03102
ASTM A414/A414M-14
Grade F
K03102
ASTM A537/A537M-13
Class 1
K12437
ASTM A737/A737M-09 (2013) Grade B Note: This section continued on next page.
K12001
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.0481 t ≤ 16 --295 --16 < t ≤ 40 --290 --40 < t ≤ 60 --285 --60 < t ≤ 100 --260 --100 < t ≤ 150 --235 --150 < t ≤ 250 --220 --1.0437 t≤5 --310 ----6 ≤ t ≤ 50 --265 --50 < t ≤ 200 --265 ----6 ≤ t ≤ 50 --265 --50 < t ≤ 200 --265 ----t ≤ 50 t≤2 260 38 t > 50 t>2 260 38 --t ≤ 40 t ≤ 1.50 260 38 t > 40 t > 1.50 260 38 --t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 310 45 ------345 50 --t ≤ 50 t≤2 260 38 t > 50 t>2 260 38 --t ≤ 40 t ≤ 1.50 260 38 t > 40 t > 1.50 260 38 --1.5 ≤ t < 2.2 0.057 ≤ t < 0.089 290 42 2.2 ≤ t < 3.8 0.089 ≤ t < 0.145 290 42 3.8 ≤ t < 7.0 0.145 ≤ t < 0.270 290 42 --1.5 ≤ t < 2.2 0.057 ≤ t < 0.089 290 42 2.2 ≤ t < 3.8 0.089 ≤ t < 0.145 290 42 3.8 ≤ t < 7.0 0.145 ≤ t < 0.270 290 42 --t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 310 45 ------345 50
Tensile Strength, min. Elongation MPa ksi % min. 460-580 --21 460-580 --21 460-580 --21 460-580 --21 440-570 --21 430-570 --21 460-550 T --28 T 480-620 --17 480-620 --21 480-590 T --17 480-590 T --21 485-620 70-90 21 485-620 70-90 21 485-620 70-90 21 485-620 70-90 21 485-620 70-90 22 450-585 65-85 22 485-620 70-90 23 485-620 70-90 21 485-620 70-90 21 485-620 70-90 21 485-620 70-90 21 485-620 T 70-90 T 13 T 485-620 T 70-90 T 14 T 485-620 T 70-90 T 16 T 485-620 T 70-90 T 13 T 485-620 T 70-90 T 14 T 485-620 T 70-90 T 16 T 485-620 70-90 22 450-585 65-85 22 485-620 70-90 23
Heat Treatment AR, N AR, N AR, N AR, N AR, N AR, N HR or HR+N AR, N or SR N AR, N, Q+T or TMCP N, Q+T, TMCP AR or N or SR or N+SR N AR or N or SR or N+SR N N N N AR, N, SR or N+SR N AR, N, SR or N+SR N HR HR HR HR HR HR N N N
Other see standard for impact data
---------------------------------------------------
Download From http://bbs.infoeach.com
Designation P295GH
Download From http://bbs.infoeach.com
Specification EN 10028-2:2009
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
116
4.1 Carbon Steels for Pressure Vessel Plates 4.1A Mechanical Properties of Carbon Steels for Pressure Vessel Plates (Continued)
Specification ISO 4706:1989
GB 3531-1996
UNS No. ---
alloy steel
---
Grade 16MnDR
---
Symbol SPV315
---
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi --t4 t ≤ 0.5 0.5 < t ≤ 1 t ≤ 0.5 0.5 < t ≤ 1 ---
410 410 390 370 415 415 415 380 315 415 380 315 345 345 345 345 450
--------60 60 60 55 46 60 55 46 50 50 50 50 ---
550-670 550-670 550-670 550-670 550-690 550-690 550-690 515-655 485-620 550-690 515-655 485-620 570-725 560-695 570-725 560-695 570-700
--------80-100 80-100 80-100 75-95 70-90 80-100 75-95 70-90 83-105 81-101 83-105 81-101 ---
16 18 18 18 23 23 22 22 20 22 22 20 22 22 22 22 19
N, Q+T or TMCP N, Q+T or TMCP N, Q+T or TMCP N, Q+T or TMCP N N Q+T Q+T Q+T Q+T Q+T Q+T AR or N or SR or N+SR AR or N or SR or N+SR AR, N, SR or N+SR AR, N, SR or N+SR N or Q+T
-------------
450 450 430 410 415 415
--------60 60
570-700 570-700 570-700 570-700 585-705 585-705
--------85-102 85-102
26 20 20 20 20 20
N or Q+T N or Q+T N or Q+T N or Q+T Q+T Q+T
Other see standard for impact data L: 47 J @ -10°C L: 47 J @ -10°C L: 47 J @ -10°C L: 47 J @ -10°C ------------------------see standard for impact data L: 47 J @ -10°C L: 47 J @ -10°C L: 47 J @ -10°C L: 47 J @ -10°C -----
Download From http://bbs.infoeach.com
K12202 K12202 K02008
Download From http://bbs.infoeach.com
ASME SA-737/SA-737M Grade C ASTM A737/A737M-09 (2013) Grade C ASME SA-738/SA-738M Grade C
16 < t ≤ 40 40 < t ≤ 50 50 < t ≤ 100 100 < t ≤ 150 ----t ≤ 65 65 < t ≤ 100 t > 100 t ≤ 65 65 < t ≤ 100 t > 100 t ≤ 12.5 12.5 < t ≤ 25 t ≤ 12.5 12.5 < t ≤ 25 6 < t ≤ 16
Heat Treatment N, Q+T or TMCP
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
120
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates Steel No. 1.0345
Grade 2 Grade P235GH
-----
-----
-----
EN 10120:2008
P245NB
---
1.0111
ASME SA-414/SA-414M ASTM A414/A414M-14
Grade C Grade C
K02503 K02503
GB 6653-94
Grade HP245
EN 10028-3:2009
Designation P235GH
ISO 4978:1983 ISO 9328-2:2004
Section Thickness mm in -----
Mn 0.60-1.20
-----
0.16 0.16
0.25 min. 0.60-1.20
---
---
0.16
0.30 min.
-----
-----
-----
0.25 0.25
0.90 0.90
---
---
---
---
0.16
0.60
P275NH
---
1.0487
---
---
0.16
0.80-1.50
JIS G 3116:2013 JIS G 3115:2010
Symbol SG255 Symbol SPV235
-----
-----
GB 6654-1996 GB 713-1997
Grade 20R Grade 20g
-----
-----
1.6 ≤ t ≤ 6.0 6 ≤ t ≤ 100 100 < t ≤ 200 -----
-----------
0.20 0.18 0.20 0.20 0.20
0.30 1.40 1.40 0.40-0.90 0.50-0.90
Download From http://bbs.infoeach.com
C 0.16
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.025 0.010 0.30 0.30 0.08 V 0.02; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.020; N 0.012; (Cr+Cu+Mo+Ni) 0.70 0.15 0.035 0.035 ------Al 0.015 min. 0.30 0.025 0.015 0.30 0.30 0.08 V 0.02; Al 0.02; Cu 0.30; Ti 0.03; Nb 0.02; (Cr+Cu+Mo+Ni) 0.70 0.25 0.025 0.015 ------Al 0.020 min.; Ti 0.03; Nb 0.050; N 0.009 0.30 0.035 0.035 ------Al 0.02-0.08 0.30 0.035 0.035 0.30 0.40 0.12 Cu 0.40; Al 0.02-0.08; V 0.03; Ti 0.025; Cb 0.02 0.35 0.035 0.035 0.30 0.30 0.30 V 0.12; Al 0.020 min.; Cu 0.20; Ti 0.20; Nb 0.060; (P+S) 0.060 0.40 0.025 0.010 0.30 0.50 0.08 V 0.05; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.05; (Cr+Cu+Mo) 0.45 --0.020 0.020 --------0.35 0.030 0.030 --------0.35 0.030 0.030 --------0.15-0.30 0.035 0.030 0.30 0.30 --Cu 0.30 0.15-0.30 0.035 0.035 0.30 0.30 0.10 V 0.010; Cu 0.30 Si 0.35
Download From http://bbs.infoeach.com
UNS No. ---
Specification EN 10028-2:2009
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
121
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued) Steel No. 1.0425
P265NB
---
1.0423
---
Grade HP265
---
---
ISO 4978:1983 ISO 9328-2:2004
Grade 3 Grade P265GH
-----
JIS G 3103:2012
Symbol SB410
---
Designation P265GH
EN 10120:2008 GB 6653-94
Download From http://bbs.infoeach.com
JIS G 3118:2010
Symbol SGV410
ASME SA-515/SA-515M* Grade 60 [415]
Section Thickness mm in -----
C 0.20
Mn 0.80-1.40
Si 0.40
---
0.19
0.40 min.
0.25
---
---
0.19
0.80
0.35
-----
-----
-----
0.19 0.20
0.40 min. 0.80-1.40
0.20 0.40
---
6 ≤ t ≤ 25
---
0.24
0.90
0.15-0.40
25 < t ≤ 50
---
0.27
0.90
0.15-0.40
50 < t ≤ 100
---
0.29
0.90
0.15-0.40
100 < t ≤ 200
---
0.30
0.90
0.15-0.40
6 ≤ t ≤ 12.5 12.5 < t ≤ 50 50 < t ≤ 100 100 < t ≤ 200 t ≤ 25
--------t≤1
0.21 0.23 0.25 0.27 0.24
0.85-1.20 0.85-1.20 0.85-1.20 0.85-1.20 0.90
0.15-0.40 0.15-0.40 0.15-0.40 0.15-0.40 0.15-0.40
25 < t ≤ 50
14
0.31
0.90
0.15-0.40
---
---
K02401
---
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.025 0.010 0.30 0.30 0.08 V 0.02; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.020; N 0.012; (Cr+Cu+Mo+Ni) 0.70 0.025 0.015 ------Al 0.020 min.; Ti 0.03; Nb 0.050; N 0.009 0.035 0.035 0.30 0.30 0.30 V 0.12; Al 0.020 min.; Cu 0.20; Ti 0.20; Nb 0.060; (P+S) 0.060 0.035 0.035 ------Al 0.015 min. 0.025 0.015 0.30 0.30 0.08 V 0.02; Al 0.02; Cu 0.30; Ti 0.03; Nb 0.02; (Cr+Cu+Mo+Ni) 0.70 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.030 0.030 --------0.030 0.030 --------0.030 0.030 --------0.030 0.030 --------0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010
Download From http://bbs.infoeach.com
UNS No. ---
Specification EN 10028-2:2009
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
122
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued)
Specification Designation ASME SA-516/SA-516M* Grade 60 [415]
ASTM A516/A516M-10*
Grade 60 [415]
Grade 60 [415]
ASME SA-414/SA-414M ASTM A414/A414M-14
Grade D Grade D
GB 6653-94
Grade HP295
JIS G 3116:2013 Symbol SG295 ASME SA-515/SA-515M* Grade 65 [450]
K02401
K02100
---
---
Section Thickness mm in t ≤ 12.5 t ≤ 0.5
C 0.21
Mn 0.60-0.90
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.035 0.035 0.30 0.40 0.12
12.5 < t ≤ 50
0.5 < t ≤ 2
0.23
0.85-1.20
0.15-0.40 0.035 0.035
0.30
0.40
0.12
50 < t ≤ 100
2 100
t>4
0.27
0.85-1.20
0.15-0.40 0.035 0.035
0.30
0.40
0.12
t ≤ 25
t≤1
0.24
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.12
25 < t ≤ 50
14
0.31
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.12
t ≤ 12.5
t ≤ 0.5
0.21
0.60-0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.12
12.5 < t ≤ 50
0.5 < t ≤ 2
0.23
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
50 < t ≤ 100
2 100
t>4
0.27
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
K02505 K02505
-----
-----
-----
0.25 0.25
1.20 1.20
0.30 0.30
0.035 0.035 0.035 0.035
--0.30
--0.40
--0.12
---
---
---
---
0.20
1.00
0.35
0.035 0.035
0.30
0.30
0.30
--K02800
-----
1.6 ≤ t ≤ 6.0 t ≤ 25
--t≤1
0.20 0.28
1.00 0.90
0.35 0.020 0.020 0.15-0.40 0.035 0.035
--0.30
--0.40
--0.12
25 < t ≤ 50
1 50
t>2
0.33
0.90
0.15-0.40 0.035 0.035
0.30
0.40
0.12
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Al 0.02-0.08 Cu 0.40; Al 0.02-0.08; V 0.03; Ti 0.025; Cb 0.02 V 0.12; Al 0.020 min.; Cu 0.20; Ti 0.20; Nb 0.060; (P+S) 0.060 --V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A515/A515M-10*
UNS Steel No. No. K02100 ---
*: See ASTM A20/A20M-14 for additional information. Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
123
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued)
Specification Designation ASME SA-516/SA-516M* Grade 65 [450]
ASTM A516/A516M-10*
JIS G 3103:2012
Grade 65 [450]
Grade 65 [450]
K02800
K02403
Symbol SB450
JIS G 3118:2010
Symbol SGV450
ASME SA-414/SA-414M ASTM A414/A414M-14
Grade E Grade E
---
---
---
---
---
---
K02704 K02704
-----
Section Thickness mm in t ≤ 12.5 t ≤ 0.5
C 0.24
Mn 0.85-1.20
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.035 0.035 0.30 0.40 0.12
12.5 < t ≤ 50
0.5 < t ≤ 2
0.26
0.85-1.20
0.15-0.40 0.035 0.035
0.30
0.40
0.12
50 < t ≤ 100
2 100
t>4
0.29
0.85-1.20
0.15-0.40 0.035 0.035
0.30
0.40
0.12
t ≤ 25
t≤1
0.28
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.12
25 < t ≤ 50
1 50
t>2
0.33
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.12
t ≤ 12.5
t ≤ 0.5
0.24
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
12.5 < t ≤ 50
0.5 < t ≤ 2
0.26
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
50 < t ≤ 100
2 100
t>4
0.29
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
6 ≤ t ≤ 25
---
0.28
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.12
25 < t ≤ 50
---
0.31
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.12
50 < t ≤ 200
---
0.33
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.12
6 ≤ t ≤ 12.5 12.5 < t ≤ 50 50 < t ≤ 100 100 < t ≤ 200 -----
-------------
0.24 0.26 0.28 0.29 0.27 0.27
0.85-1.20 0.85-1.20 0.85-1.20 0.85-1.20 1.20 1.20
0.15-0.40 0.15-0.40 0.15-0.40 0.15-0.40 0.30 0.30
----------0.30
----------0.40
----------0.12
0.030 0.030 0.030 0.030 0.035 0.035
0.030 0.030 0.030 0.030 0.035 0.035
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 --------Al 0.02-0.08 Cu 0.40; Al 0.02-0.08; V 0.03; Ti 0.025; Cb 0.02
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A515/A515M-10*
UNS Steel No. No. K02403 ---
*: See ASTM A20/A20M-14 for additional information.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
124
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued) Steel No. 1.0481
P310NB
---
1.0437
---
---
0.20
0.70 min.
0.50
Symbol SB480
---
---
6 ≤ t ≤ 25
---
0.31
1.20
0.15-0.40
25 < t ≤ 50
---
0.33
1.20
0.15-0.40
50 < t ≤ 200
---
0.35
1.20
0.15-0.40
6 ≤ t ≤ 12.5 12.5 < t ≤ 50 50 < t ≤ 100 100 < t ≤ 200 t ≤ 25
--------t≤1
0.27 0.28 0.30 0.31 0.31
0.85-1.20 0.85-1.20 0.85-1.20 0.85-1.20 1.20
0.15-0.40 0.15-0.40 0.15-0.40 0.15-0.40 0.15-0.40
25 < t ≤ 50
1 50
t>2
0.35
1.20
0.15-0.40
t ≤ 12.5
t ≤ 0.5
0.27
0.85-1.20
0.15-0.40
12.5 < t ≤ 50
0.5 < t ≤ 2
0.28
0.85-1.20
0.15-0.40
50 < t ≤ 100
2 100
t>4
0.31
0.85-1.20
0.15-0.40
t ≤ 40
t ≤ 1.5
0.24
0.70-1.35
0.15-0.50
40 < t ≤ 100
1.5 < t ≤ 4
0.24
1.00-1.60
0.15-0.50
---
---
0.20
1.15-1.50
0.15-0.50
Designation P295GH
EN 10120:2008 JIS G 3103:2012
Download From http://bbs.infoeach.com
JIS G 3118:2010
Symbol SGV480
ASME SA-515/SA-515M* Grade 70 [485]
ASME SA-516/SA-516M* Grade 70 [485]
ASME SA-537/SA-537M* Class 1
ASME SA-737/SA-737M* Grade B
---
---
K03101
---
K02700
K12437
K12001
---
---
---
Section Thickness mm in -----
C Mn 0.08-0.20 0.90-1.50
Si 0.40
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.025 0.010 0.30 0.30 0.08 V 0.02; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.020; N 0.012; (Cr+Cu+Mo+Ni) 0.70 0.025 0.015 ------Al 0.020 min.; Ti 0.03; Nb 0.050; N 0.009 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.020 0.020 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010; (Cu+Ni+Mo+Cr) 1.00; (Cr+Mo) 0.32 0.030 0.030 --------0.030 0.030 --------0.030 0.030 --------0.030 0.030 --------0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.25 0.25 0.08 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 0.035 0.035 0.25 0.25 0.08 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.05; B 0.0010
Download From http://bbs.infoeach.com
UNS No. ---
Specification EN 10028-2:2009
*: See ASTM A20/A20M-14 for additional information. Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
125
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued)
Specification ASTM A515/A515M-10*
Grade 70 [485]
UNS Steel No. No. K03101 ---
K02700
---
Section Thickness mm in t ≤ 25 t≤1
C 0.31
Mn 1.20
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.40 0.12
25 < t ≤ 50
1 50
t>2
0.35
1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
t ≤ 25
t≤1
0.27
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
25 < t ≤ 50
14
0.31
0.85-1.20
0.15-0.40 0.025 0.025
0.30
0.40
0.12
0.035 0.035 0.035 0.035
--0.30
--0.40
--0.12
ASME SA-414/SA-414M Grade F ASTM A414/A414M-14 Grade F
K03102 K03102
-----
-----
-----
0.31 0.31
1.20 1.20
ASTM A537/A537M-13*
K12437
---
t ≤ 40
t ≤ 1.5
0.24
0.70-1.35
0.15-0.50 0.025 0.025
0.25
0.25
0.08
t > 40
t > 1.5
0.24
1.00-1.60
0.15-0.50 0.025 0.025
0.25
0.25
0.08
0.15-0.50 0.025 0.025
0.30
0.40
0.12
-----
-----
-----
0.25 --0.30
0.40 --0.30
0.08 --0.30
Class 1
ASTM A737/A737M-09 (2013)* ISO 4706:1989
Grade B
0.30 0.30
K12001
---
---
---
0.20
1.15-1.50
carbon steel alloy steel
-----
-----
-----
-----
0.22 0.22
1.60 1.60
GB 3531-1996 JIS G 3115:2010 GB 6653-94
Grade 16MnDR Symbol SPV315 Grade HP325
-------
-------
--6 ≤ t ≤ 150 ---
-------
0.20 0.18 0.20
1.20-1.60 1.60 1.50
JIS G 3116:2013 ISO 4978:1983 EN 10028-3:2009
Symbol SG325 Grade 4 P355N
-------
----1.0562
1.6 ≤ t ≤ 6.0 -----
-------
0.20 0.20 0.18
1.50 0.70 min. 1.10-1.70
0.55 0.45 0.50
0.020 0.020 0.035 0.035 0.025 0.010
----0.30
----0.50
----0.08
P355NH
---
1.0565
---
---
0.18
1.10-1.70
0.50
0.025 0.010
0.30
0.50
0.08
0.45 0.45
0.04 0.04
0.04 0.04
0.15-0.50 0.030 0.025 0.55 0.030 0.030 0.35 0.035 0.035
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Al 0.02-0.08 Cu 0.40; Al 0.02-0.08; V 0.03; Ti 0.025; Cb 0.02 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.05; B 0.0010 (P+S) 0.07 V 0.20; Ti 0.20; Nb 0.08; (P+S) 0.07; (Nb+V) 0.20 Al 0.020 min.; Cu 0.25 --V 0.12; Al 0.020 min.; Cu 0.20; Ti 0.20; Nb 0.060; (P+S) 0.060 --Al 0.015 min. V 0.10; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.12; (Cr+Cu+Mo) 0.45 V 0.10; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.12; (Cr+Cu+Mo) 0.45
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A516/A516M-10*
Designation Grade 70 [485]
*: See ASTM A20/A20M-14 for additional information.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
126
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued)
Specification GB 6654-1996 GB 713-1997
UNS No. ---------
Steel No. ---------
Section Thickness mm in -----------------
P355GH
---
1.0473
---
---
EN 10120:2008
P355NB
---
1.0557
---
---
0.20
0.70 min.
0.50
JIS G 3124:2009 GB 713-1997 ASME SA-414/SA-414M ASTM A414/A414M-14
Symbol SEV245 Grade 22Mng Grade G Grade G
----K03103 K03103
---------
6 ≤ t ≤ 150 -------
---------
0.20 0.30 0.31 0.31
0.80-1.60 0.90-1.50 1.35 1.35
0.15-0.60 0.15-0.40 0.30 0.30
ASME SA-738/SA-738M
Grade A
K12447
---
t ≤ 65
t ≤ 2.5
0.24
1.50
0.15-0.50
65 < t ≤ 150
2.5 < t ≤ 6
0.24
1.60
0.15-0.50
t ≤ 65
t ≤ 2.5
0.24
1.50
0.15-0.50
65 < t ≤ 150
2.5 < t ≤ 6
0.24
1.60
0.15-0.50
ASTM A738/A738M-12a
JIS G 3115:2010 GB 6654-1996 GB 6653-94
Grade A
Symbol SPV355 Grade 15MnVR Grade HP365
JIS G 3116:2013 Symbol SG365 Note: This section continued on next page.
K12447
---
C Mn 0.20 1.20-1.60 0.20 1.20-1.60 0.15-0.22 1.00-1.60 0.20 1.50
Si 0.20-0.55 0.20-0.55 0.30-0.60 0.35
0.10-0.22 1.10-1.70
0.60
-------
-------
6 ≤ t ≤ 150 -----
-------
0.20 0.18 0.20
1.60 1.20-1.60 1.50
0.55 0.20-0.55 0.35
---
---
1.6 ≤ t ≤ 6.0
---
0.20
1.50
0.55
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.035 0.030 0.30 0.30 --Cu 0.30 0.035 0.030 0.30 0.30 0.10 V 0.010; Cu 0.30 0.030 0.025 0.30 0.30 0.10 V 0.010; Cu 0.30 0.035 0.035 0.30 0.30 0.30 V 0.12; Al 0.020 min.; Cu 0.20; Ti 0.20; Nb 0.060; (P+S) 0.060 0.025 0.010 0.30 0.30 0.08 V 0.02; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.040; N 0.012; (Cr+Cu+Mo+Ni) 0.70 0.025 0.015 ------Al 0.020 min.; Ti 0.03; Nb 0.050; N 0.009 0.030 0.030 ----0.35 V 0.10; Cu 0.40; Nb 0.05 0.025 0.025 0.30 0.30 0.10 V 0.010; Cu 0.30 0.035 0.035 ------Al 0.02-0.08 0.035 0.035 0.30 0.40 0.12 Cu 0.40; Al 0.02-0.08; V 0.03; Ti 0.025; Cb 0.02 0.035 0.035 0.25 0.50 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 0.035 0.035 0.25 0.50 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 0.025 0.025 0.25 0.50 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 0.025 0.025 0.25 0.50 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 0.030 0.030 --------0.035 0.030 0.30 0.30 --V 0.04-0.12; Cu 0.30 0.035 0.035 0.30 0.30 0.30 V 0.12; Al 0.020 min.; Cu 0.20; Ti 0.20; Nb 0.060; (P+S) 0.060 0.020 0.020 ---------
Download From http://bbs.infoeach.com
EN 10028-2:2009
Download From http://bbs.infoeach.com
GB 6653-94
Designation Grade 16MnR Grade 16Mng Grade 19Mng Grade HP345
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
127
4.1 Carbon Steels for Pressure Vessel Plates 4.1B Chemical Composition of Carbon Steels for Pressure Vessel Plates (Continued)
Specification Designation ASME SA-537/SA-537M* Class 3
Class 2
Class 3
Class 2
K12437
K12437
K12437
---
---
---
Section Thickness mm in t ≤ 40 t ≤ 1.5
C 0.24
Mn 0.70-1.35
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.50 0.035 0.035 0.25 0.25 0.08
40 < t ≤ 150
1.5 < t ≤ 6
0.24
1.00-1.60
0.15-0.50 0.035 0.035
0.25
0.25
0.08
t ≤ 40
t ≤ 1.5
0.24
0.70-1.35
0.15-0.50 0.035 0.035
0.25
0.25
0.08
40 < t ≤ 150
1.5 < t ≤ 6
0.24
1.00-1.60
0.15-0.50 0.035 0.035
0.25
0.25
0.08
t ≤ 40
t ≤ 1.5
0.24
0.70-1.35
0.15-0.50 0.025 0.025
0.25
0.25
0.08
40 < t ≤ 150
1.5 < t ≤ 6
0.24
1.00-1.60
0.15-0.50 0.025 0.025
0.25
0.25
0.08
t ≤ 40
t ≤ 1.5
0.24
0.70-1.35
0.15-0.50 0.025 0.025
0.25
0.25
0.08
40 < t ≤ 150
1.5 < t ≤ 6
0.24
1.00-1.60
0.15-0.50 0.025 0.025
0.25
0.25
0.08
JIS G 3115:2010 Symbol SPV410 ASME SA-737/SA-737M* Grade C
--K12202
-----
6 ≤ t ≤ 150 ---
-----
0.18 0.22
1.60 1.15-1.50
0.75 0.030 0.030 0.15-0.50 0.025 0.025
--0.30
--0.40
--0.12
ASTM A737/A737M-09 (2013)* ASME SA-738/SA-738M
Grade C
K12202
---
---
---
0.22
1.15-1.50
0.15-0.50 0.025 0.025
0.30
0.40
0.12
Grade C
K02008
---
ASTM A738/A738M-12a
Grade C
K02008
---
ASME SA-612/SA-612M ASTM A612/A612M-12 JIS G 3115:2010 ASME SA-738/SA-738M
----Symbol SPV450 Grade B
---------
---------
t ≤ 65 65 < t ≤ 150 t ≤ 65 65 < t ≤ 150 ----6 ≤ t ≤ 150 t ≤ 40
t ≤ 2.5 2.5 < t ≤ 6 t ≤ 2.5 2.5 < t ≤ 6 ------t ≤ 1.5
0.20 0.20 0.20 0.20 0.25 0.25 0.18 0.20
1.50 1.60 1.50 1.60 1.00-1.50 1.00-1.50 1.60 0.90-1.50
0.15-0.50 0.15-0.50 0.15-0.50 0.15-0.50 0.15-0.50 0.15-0.50 0.75 0.15-0.55
0.025 0.025 0.025 0.025 0.025 0.025 0.030 0.030
0.25 0.25 0.25 0.25 0.25 0.25 --0.30
0.50 0.50 0.50 0.50 0.25 0.25 --0.60
0.08 0.08 0.08 0.08 0.08 0.08 --0.20
40 < t ≤ 65
1.5 < t ≤ 2.5
0.20
0.90-1.50
0.15-0.55 0.030 0.030
0.30
0.60
0.20
65 < t ≤ 100
2.5 < t ≤ 4
0.20
0.90-1.60
0.15-0.55 0.030 0.030
0.30
0.60
0.20
t ≤ 40
t ≤ 1.5
0.20
0.90-1.50
0.15-0.55 0.025 0.025
0.30
0.60
0.20
40 < t ≤ 65
1.5 < t ≤ 2.5
0.20
0.90-1.50
0.15-0.55 0.025 0.025
0.30
0.60
0.20
65 < t ≤ 100
2.5 < t ≤ 4
0.20
0.90-1.60
0.15-0.55 0.025 0.025
0.30
0.60
0.20
ASTM A738/A738M-12a
Grade B
---
---
0.025 0.025 0.025 0.025 0.025 0.025 0.030 0.030
Others V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.35; Ti 0.03; Cb 0.02; B 0.0010 --V 0.04-0.11; Cu 0.40; Ti 0.03; Cb 0.05; N 0.03; B 0.0010 V 0.04-0.11; Cu 0.40; Ti 0.03; Cb 0.05; N 0.03; B 0.0010 V 0.05; Cu 0.35 V 0.05; Cu 0.35 V 0.05; Cu 0.35 V 0.05; Cu 0.35 V 0.08; Cu 0.35 V 0.08; Cu 0.35 --V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08 V 0.07; Cu 0.35; Cb 0.04; (Cb+V) 0.08
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A537/A537M-13*
UNS Steel No. No. K12437 ---
*: See ASTM A20/A20M-14 for additional information. Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
128
4.2 Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C 4.2A Mechanical Properties of Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C
Specification EN 10028-3:2009
P275NL2
Grade A Grade A Symbol SLA235A
Symbol SLA235B
Symbol SLA325A
Symbol SLA325B
UNS No. ---
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.0488 t ≤ 16 --275 --16 < t ≤ 40 --265 --40 < t ≤ 60 --255 --60 < t ≤ 100 --235 --100 < t ≤ 150 --225 --150 < t ≤ 250 --215 ----1.1104 t ≤ 16 --275 --16 < t ≤ 40 --265 --40 < t ≤ 60 --255 --60 < t ≤ 100 --235 --100 < t ≤ 150 --225 --150 < t ≤ 250 --215 --K01701 ------275 40 K01701 ------275 40 ----6 ≤ t ≤ 16 --235 --16 < t ≤ 40 --235 --40 < t ≤ 50 --215 ------6 ≤ t ≤ 16 --235 --16 < t ≤ 40 --235 --40 < t ≤ 50 --215 ------6 ≤ t ≤ 16 --325 --16 < t ≤ 20 --325 --20 < t ≤ 38 --325 ------6 ≤ t ≤ 16 --325 --16 < t ≤ 20 --325 --20 < t ≤ 38 --325 ---
Tensile Strength, min. Elongation MPa ksi % min. 390-510 --24 390-510 --24 390-510 --24 370-490 --23 360-480 --23 350-470 --23 390-510 --24 390-510 --24 390-510 --24 370-490 --23 360-480 --23 350-470 --23 400-540 58-78 23 400-540 58-78 23 400-510 T --18 400-510 T --22 400-510 T --24 400-510 T --18 400-510 T --22 400-510 T --24 440-560 T --22 440-560 T --30 440-560 T --22 440-560 T --22 440-560 T --30 440-560 T --22
Heat Treatment AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N N N N or TMCP N or TMCP N or TMCP N or TMCP N or TMCP N or TMCP N or TMCP N or TMCP N or TMCP Q+T or TMCP Q+T or TMCP Q+T or TMCP
Other see standard for impact data
see standard for impact data
----see standard for impact data see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-662/SA-662M ASTM A662/A662M-12 JIS G 3126:2009
Designation P275NL1
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
129
4.2 Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C 4.2A Mechanical Properties of Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C (Continued)
Specification ASME SA-662/SA-662M
Designation Grade B Grade C
ASTM A662/A662M-12
ASTM A841/A841M-13
EN 10028-3:2009
Grade C Grade A, Class 1 Grade B, Class 1 Grade C, Class 1 Grade A, Class 1 Grade B, Class 1 Grade C, Class 1 P355NL1
P355NL2
JIS G 3126:2009
Symbol SLA365
Tensile Strength, min. Elongation MPa ksi % min. 450-585 65-85 23 450-585 65-85 23 485-620 70-90 22 485-620 70-90 22 450-585 65-85 23 450-585 65-85 23 485-620 70-90 22 485-620 70-90 22 480-620 70-90 22 450-585 65-85 22 480-620 70-90 22 450-585 65-85 22 480-620 70-90 22 450-585 65-85 22 480-620 70-90 22 450-585 65-85 22 480-620 70-90 22 450-585 65-85 22 480-620 70-90 22 450-585 65-85 22 490-630 --22 490-630 --22 490-630 --22 470-610 --21 460-600 --21 450-590 --21 490-630 --22 490-630 --22 490-630 --22 470-610 --21 460-600 --21 450-590 --21 490-610 T --20 490-610 T --28 490-610 T --20
Heat Treatment AR, N, SR or N+SR N AR, N, SR or N+SR N AR, N, SR or N+SR N AR, N, SR or N+SR N TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N AR, N Q+T or TMCP Q+T or TMCP Q+T or TMCP
Other ----------------L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-841/SA-841M
Grade B
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K02203 --t ≤ 40 t ≤ 1.5 275 40 t > 40 t > 1.5 275 40 K02007 --t ≤ 40 t ≤ 1.5 295 43 t > 40 t > 1.5 295 43 K02203 --t ≤ 40 t ≤ 1.5 275 40 t > 40 t > 1.5 275 40 K02007 --t ≤ 40 t ≤ 1.5 295 43 t > 40 t > 1.5 295 43 K02010 --t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 315 45 ----t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 315 45 ----t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 315 45 K02010 --t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 315 45 ----t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 315 45 ----t ≤ 65 t ≤ 2.5 345 50 65 < t ≤ 100 2.5 < t ≤ 4 315 45 --1.0566 t ≤ 16 --355 --16 < t ≤ 40 --345 --40 < t ≤ 60 --335 --60 < t ≤ 100 --315 --100 < t ≤ 150 --305 --150 < t ≤ 250 --295 ----1.1106 t ≤ 16 --355 --16 < t ≤ 40 --345 --40 < t ≤ 60 --335 --60 < t ≤ 100 --315 --100 < t ≤ 150 --305 --150 < t ≤ 250 --295 ------6 ≤ t ≤ 16 --365 --16 < t ≤ 20 --365 --20 < t ≤ 38 --365 ---
see standard for impact data
see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
130
4.2 Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C 4.2A Mechanical Properties of Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C (Continued)
Specification JIS G 3126:2009
Designation Symbol SLA410
ASME SA-841/SA-841M
Grade A, Class 2 Grade B, Class 2
Grade A, Class 2 Grade B, Class 2 Grade C, Class 2
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi --6 ≤ t ≤ 16 --410 --16 < t ≤ 20 --410 --20 < t ≤ 38 --410 --K02010 --t ≤ 65 t ≤ 2.5 415 60 65 < t ≤ 100 2.5 < t ≤ 4 380 55 ----t ≤ 65 t ≤ 2.5 415 60 65 < t ≤ 100 2.5 < t ≤ 4 380 55 ----t ≤ 65 t ≤ 2.5 415 60 65 < t ≤ 100 2.5 < t ≤ 4 380 55 K02010 --t ≤ 65 t ≤ 2.5 415 60 65 < t ≤ 100 2.5 < t ≤ 4 380 55 ----t ≤ 65 t ≤ 2.5 415 60 65 < t ≤ 100 2.5 < t ≤ 4 380 55 ----t ≤ 65 t ≤ 2.5 415 60 65 < t ≤ 100 2.5 < t ≤ 4 380 55
Tensile Strength, min. Elongation MPa ksi % min. 520-640 T --18 520-640 T --26 520-640 T --18 550-690 80-100 22 515-655 75-95 22 550-690 80-100 22 515-655 75-95 22 550-690 80-100 22 515-655 75-95 22 550-690 80-100 22 515-655 75-95 22 550-690 80-100 22 515-655 75-95 22 550-690 80-100 22 515-655 75-95 22
Heat Treatment Q+T or TMCP Q+T or TMCP Q+T or TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP TMCP
Other see standard for impact data L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C L: 20 J @ -40°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A841/A841M-13
Grade C, Class 2
UNS No. ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
131
4.2 Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C 4.2B Chemical Composition of Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C
Specification EN 10028-3:2009
Designation P275NL1
P275NL2
ASME SA-662/SA-662M* Grade A
JIS G 3126:2009
Grade A
Steel No. 1.0488
---
1.1104
---
K01701
---
K01701
Symbol SLA235A --Symbol SLA235B --Symbol SLA325A --Symbol SLA325B --*: See ASTM A20/A20M-14 for additional information.
Section Thickness mm in -----
C 0.16
Mn 0.80-1.50
---
0.16
0.80-1.50
---
---
0.14
0.90-1.35
---
---
---
0.14
0.90-1.35
---------
6 ≤ t ≤ 50 6 ≤ t ≤ 50 6 ≤ t ≤ 38 6 ≤ t ≤ 38
---------
0.15 0.15 0.16 0.16
0.70-1.50 0.70-1.50 0.80-1.60 0.80-1.60
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.025 0.008 0.30 0.50 0.08 V 0.05; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.05; (Cr+Cu+Mo) 0.45 0.40 0.020 0.005 0.30 0.50 0.08 V 0.05; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.05; (Cr+Cu+Mo) 0.45 0.15-0.40 0.025 0.025 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.15-0.40 0.025 0.025 0.30 0.40 0.12 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.30 0.025 0.020 --------0.30 0.025 0.020 --------0.55 0.025 0.020 --------0.55 0.025 0.020 --------Si 0.40
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A662/A662M-12*
UNS No. ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
132
4.2 Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C 4.2B Chemical Composition of Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C (Continued)
Specification Designation ASME SA-662/SA-662M* Grade B
ASTM A662/A662M-12*
C 0.19
Mn 0.85-1.50
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.40 0.12
---
---
---
0.20
1.00-1.60
0.15-0.50 0.025 0.025
0.30
0.40
0.12
Grade B
K02203
---
---
---
0.19
0.85-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.12
Grade C
K02007
---
---
---
0.20
1.00-1.60
0.15-0.50 0.025 0.025
0.30
0.40
0.12
K02010
---
t ≤ 40
t ≤ 1.5
0.20
0.70-1.35
0.15-0.50 0.030 0.030
0.25
0.25
0.08
40 < t ≤ 100
1.5 < t ≤ 4
0.20
1.00-1.60
0.15-0.50 0.030 0.030
0.25
0.25
0.08
t ≤ 40
t ≤ 1.5
0.15
0.70-1.35
0.15-0.50 0.030 0.025
0.25
0.60
0.30
40 < t ≤ 100
1.5 < t ≤ 4
0.15
1.00-1.60
0.15-0.50 0.030 0.025
0.25
0.60
0.30
t ≤ 40
t ≤ 1.5
0.10
0.70-1.60
0.15-0.50 0.030 0.015
0.25
0.25
0.08
40 < t ≤ 100
1.5 < t ≤ 4
0.10
1.00-1.60
0.15-0.50 0.030 0.015
0.25
0.25
0.08
t ≤ 40
t ≤ 1.5
0.20
0.70-1.35
0.15-0.50 0.030 0.030
0.25
0.25
0.08
40 < t ≤ 100
1.5 < t ≤ 4
0.20
1.00-1.60
0.15-0.50 0.030 0.030
0.25
0.25
0.08
t ≤ 40
t ≤ 1.5
0.15
0.70-1.35
0.15-0.50 0.030 0.025
0.25
0.60
0.30
40 < t ≤ 100
1.5 < t ≤ 4
0.15
1.00-1.60
0.15-0.50 0.030 0.025
0.25
0.60
0.30
t ≤ 40
t ≤ 1.5
0.10
0.70-1.60
0.15-0.50 0.030 0.015
0.25
0.25
0.08
40 < t ≤ 100
1.5 < t ≤ 4
0.10
1.00-1.60
0.15-0.50 0.030 0.015
0.25
0.25
0.08
Grade B, Class 1
Grade C, Class 1
Grade A, Class 1
Grade B, Class 1
---
---
K02010
---
---
---
---
---
---
---
P355NL1
---
1.0566
---
---
0.18
1.10-1.70
0.50
0.025 0.008
0.30
0.50
0.08
P355NL2
---
1.1106
---
---
0.18
1.10-1.70
0.50
0.020 0.005
0.30
0.50
0.08
---
6 ≤ t ≤ 38
---
0.18
0.80-1.60
0.55
0.025 0.020
---
---
---
JIS G 3126:2009 Symbol SLA365 --*: See ASTM A20/A20M-14 for additional information.
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 V 0.10; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.12; (Cr+Cu+Mo) 0.45 V 0.10; Al 0.020 min.; Cu 0.30; Ti 0.03; Nb 0.05; N 0.012; (Nb+Ti+V) 0.12; (Cr+Cu+Mo) 0.45 ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
K02007
Grade C, Class 1
EN 10028-3:2009
Section Thickness mm in -----
Grade C
ASME SA-841/SA-841M* Grade A, Class 1
ASTM A841/A841M-13*
UNS Steel No. No. K02203 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
133
4.2 Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C 4.2B Chemical Composition of Carbon Steels for Pressure Vessel Plates – With Impact Testing Below -20°C (Continued)
Specification Designation JIS G 3126:2009 Symbol SLA410 ASME SA-841/SA-841M* Grade A, Class 2
UNS Steel No. No. ----K02010 ---
Grade B, Class 2
Grade C, Class 2
Grade A, Class 2
---
K02010
Grade B, Class 2
Grade C, Class 2
*: See ASTM A20/A20M-14 for additional information.
---
---
---
---
---
---
---
C 0.18 0.20
Mn 0.80-1.60 0.70-1.35
40 < t ≤ 100
1.5 < t ≤ 4
0.20
1.00-1.60
t ≤ 40
t ≤ 1.5
0.15
0.70-1.35
40 < t ≤ 100
1.5 < t ≤ 4
0.15
1.00-1.60
t ≤ 40
t ≤ 1.5
0.10
0.70-1.60
40 < t ≤ 100
1.5 < t ≤ 4
0.10
1.00-1.60
t ≤ 40
t ≤ 1.5
0.20
0.70-1.35
40 < t ≤ 100
1.5 < t ≤ 4
0.20
1.00-1.60
t ≤ 40
t ≤ 1.5
0.15
0.70-1.35
40 < t ≤ 100
1.5 < t ≤ 4
0.15
1.00-1.60
t ≤ 40
t ≤ 1.5
0.10
0.70-1.60
40 < t ≤ 100
1.5 < t ≤ 4
0.10
1.00-1.60
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo Others 0.55 0.025 0.020 --------0.15-0.50 0.030 0.030 0.25 0.25 0.08 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.030 0.25 0.25 0.08 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.025 0.25 0.60 0.30 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.025 0.25 0.60 0.30 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.015 0.25 0.25 0.08 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 0.15-0.50 0.030 0.015 0.25 0.25 0.08 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 0.15-0.50 0.030 0.030 0.25 0.25 0.08 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.030 0.25 0.25 0.08 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.025 0.25 0.60 0.30 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.025 0.25 0.60 0.30 V 0.06; Al 0.020 min.; Cu 0.35; Ti 0.03; Cb 0.03; B 0.0010 0.15-0.50 0.030 0.015 0.25 0.25 0.08 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010 0.15-0.50 0.030 0.015 0.25 0.25 0.08 V 0.06; Cu 0.35; Ti 0.006-0.02; Cb 0.06; B 0.0010
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A841/A841M-13*
---
Section Thickness mm in 6 ≤ t ≤ 38 --t ≤ 40 t ≤ 1.5
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
134
4.3 ½ Mo Alloy Steels for Pressure Vessel Plates 4.3A Chemical Composition of ½Mo Alloy Steels for Pressure Vessel Plates UNS Steel Designation No. No. 18MnMo4-5 --1.5414 16Mo3 --1.5415 GB 713-1997 Grade 13MnNiMoNbg ----ISO 9328-2:2004 Grade 16Mo3 ----ASME SA-204/SA-204M* Grade A K11820 --Specification EN 10028-2:2009
Grade C
Grade A
K12020
K12320
K11820
---
---
---
C 0.20 0.12-0.20 0.15 0.12-0.20 0.18
Mn 0.90-1.50 0.40-0.90 1.00-1.60 0.40-0.90 0.90
Si 0.40 0.35 0.10-0.50 0.35 0.15-0.40
25 < t ≤ 50
14
0.25
0.90
0.15-0.40
t ≤ 25
t≤1
0.20
0.90
0.15-0.40
25 < t ≤ 50
14
0.27
0.90
0.15-0.40
t ≤ 25
t≤1
0.23
0.90
0.15-0.40
25 < t ≤ 50
1 50
t>2
0.28
0.90
0.15-0.40
t ≤ 25
t≤1
0.18
0.90
0.15-0.40
25 < t ≤ 50
14
0.25
0.90
0.15-0.40
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.015 0.005 0.30 0.30 0.45-0.60 Cu 0.30; N 0.012 0.025 0.010 0.30 0.30 0.25-0.35 Cu 0.30; N 0.012 0.025 0.025 0.20-0.40 0.60-1.00 0.20-0.40 V 0.010; Cu 0.30; Nb 0.005-0.020 0.025 0.010 0.30 0.30 0.25-0.35 Cu 0.30 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 0.025 0.025 0.30 0.40 0.45-0.60 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A204/A204M-12*
Grade B
Section Thickness mm in ----------------t ≤ 25 t≤1
*: See ASTM A20/A20M-14 for additional information. Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
135
4.3 ½ Mo Alloy Steels for Pressure Vessel Plates 4.3A Chemical Composition of ½Mo Alloy Steels for Pressure Vessel Plates (Continued)
Specification ASTM A204/A204M-12*
Grade C
Symbol SB450M
Symbol SB480M
UNS Steel No. No. K12020 ---
K12320
---
---
---
---
---
Section Thickness mm in t ≤ 25 t≤1
C 0.20
Mn 0.90
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.40 0.45-0.60
25 < t ≤ 50
14
0.27
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
t ≤ 25
t≤1
0.23
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
25 < t ≤ 50
1 50
t>2
0.28
0.90
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
6 ≤ t ≤ 25
---
0.18
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
25 < t ≤ 50
---
0.21
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
50 < t ≤ 100
---
0.23
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
100 < t ≤ 150
---
0.25
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
6 ≤ t ≤ 25
---
0.20
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
25 < t ≤ 50
---
0.23
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
50 < t ≤ 100
---
0.25
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
100 < t ≤ 150
---
0.27
0.90
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 3103:2012
Designation Grade B
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
136
4.3 ½ Mo Alloy Steels for Pressure Vessel Plates 4.3A Chemical Composition of ½Mo Alloy Steels for Pressure Vessel Plates (Continued)
Specification Designation ASME SA-302/SA-302M* Grade A
JIS G 3119:2013
Grade A
Symbol SBV1A
K12021
---
JIS G 3124:2009 Symbol SEV295 --*: See ASTM A20/A20M-14 for additional information.
---
---
---
Section Thickness mm in t ≤ 25 t≤1
C 0.20
Mn 0.95-1.30
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.40 0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
0.95-1.30
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
t ≤ 25
t≤1
0.20
0.95-1.30
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
0.95-1.30
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
6 ≤ t ≤ 25
---
0.20
0.95-1.30
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
25 < t ≤ 50
---
0.23
0.95-1.30
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
50 < t ≤ 150
---
0.25
0.95-1.30
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
6 ≤ t ≤ 150
---
0.19
0.80-1.60
0.15-0.60 0.030 0.030
---
---
0.10-0.40
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.10; Cu 0.70; Nb 0.05
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A302/A302M-12*
UNS Steel No. No. K12021 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
137
4.3 ½ Mo Alloy Steels for Pressure Vessel Plates 4.3A Chemical Composition of ½Mo Alloy Steels for Pressure Vessel Plates (Continued)
Specification Designation ASME SA-302/SA-302M* Grade B
UNS Steel No. No. K12022 ---
Section Thickness mm in t ≤ 25 t≤1
C 0.20
Mn 1.15-1.50
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.40 0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
Type A, Class 2
K12521
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
Type A, Class 3
K12521
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
Grade B
K12022
---
t ≤ 25
t≤1
0.20
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
ASTM A302/A302M-12*
ASTM A533/A533M-09 (2014)*
GB 6654-1996 JIS G 3119:2013
JIS G 3120:2014
Type A, Class 1
K12521
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
Type A, Class 2
K12521
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
Type A, Class 3
K12521
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40
0.45-0.60
-----
-----
--6 ≤ t ≤ 25
-----
0.22 0.20
1.20-1.60 1.15-1.50
0.15-0.50 0.035 0.030 0.15-0.40 0.020 0.020
0.30 0.30
0.30 0.40
0.45-0.65 0.45-0.60
25 < t ≤ 50
---
0.23
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
50 < t ≤ 150
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
Grade 18MnMoNbR Symbol SBV1B
Symbol SQV1A
---
---
---
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
Symbol SQV1B
---
---
---
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40
0.45-0.60
JIS G 3124:2009 Symbol SEV345 --*: See ASTM A20/A20M-14 for additional information.
---
6 ≤ t ≤ 150
---
0.19
0.80-1.70
0.15-0.60 0.030 0.030
---
---
0.15-0.50
Download From http://bbs.infoeach.com
K12521
Download From http://bbs.infoeach.com
ASME SA-533/SA-533M* Type A, Class 1
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Cu 0.30; Nb 0.025-0.050 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.10; Cu 0.70; Nb 0.05
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
138
4.3 ½Mo Alloy Steels for Pressure Vessel Plates 4.3B Mechanical Properties of ½Mo Alloy Steels for Pressure Vessel Plates
Specification EN 10028-2:2009
Designation 18MnMo4-5
UNS No. ---
GB 713-1997
Grade 13MnNiMoNbg
---
ISO 9328-2:2004
Grade 16Mo3
---
ASME SA-204/SA-204M
Grade A
K11820
Grade B
K12020
Grade C
K12320
Grade A
K11820
Grade B
K12020
Grade C
K12320
ASTM A204/A204M-12
JIS G 3103:2012
Symbol SB450M
---
Symbol SB480M
---
Tensile Strength, min. Elongation MPa ksi % min. 510-650 --20 510-650 --20 480-620 --20 440-590 --22 440-590 --22 440-590 --22 430-580 --22 420-570 --22 410-570 --22 570-740 --18 570-740 --18 570-740 --18 440-590 --22 440-590 --22 440-590 --22 430-580 --22 420-570 --22 410-570 --22 450-585 65-85 23 450-585 65-85 23 485-620 70-90 21 485-620 70-90 21 515-655 75-95 20 515-655 75-95 20 450-585 65-85 23 450-585 65-85 23 485-620 70-90 21 485-620 70-90 21 515-655 75-95 20 515-655 75-95 20 450-590 --19 450-590 --23 480-620 --17 480-620 --21
Heat Treatment N+T N+T Q+T AR, N or N+T AR, N or N+T AR, N or N+T AR, N or N+T AR, N or N+T AR, N or N+T HR, CtR, N or N+T HR, CtR, N or N+T HR, CtR, N or N+T N or BA N or BA N or BA N or BA N or BA N or BA AR or SR or N or SR+N N AR or SR or N or SR+N N AR or SR or N or SR+N N AR, SR, N or SR+N N AR, SR, N or SR+N N AR, SR, N or SR+N N AR, N or SR N AR, N or SR N
Other see standard for impact data see standard for impact data
T: 31 J @ 0°C T: 31 J @ 0°C T: 31 J @ 0°C see standard for impact data
---------------------------------
Download From http://bbs.infoeach.com
---
Download From http://bbs.infoeach.com
16Mo3
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.5414 t ≤ 60 --345 --60 < t ≤ 150 --325 --150 < t ≤ 250 --310 --1.5415 t ≤ 16 --275 --16 < t ≤ 40 --270 --40 < t ≤ 60 --260 --60 < t ≤ 100 --240 --100 < t ≤ 150 --220 --150 < t ≤ 250 --210 ----t ≤ 100 --390 --100 < t ≤ 120 --380 --120 < t ≤ 150 --375 ----t ≤ 16 --275 --16 < t ≤ 40 --270 --40 < t ≤ 60 --260 --60 < t ≤ 100 --240 --100 < t ≤ 150 --220 --150 < t ≤ 250 --210 ----t ≤ 40 t ≤ 1.5 255 37 t > 40 t > 1.5 255 37 --t ≤ 40 t ≤ 1.5 275 40 t > 40 t > 1.5 275 40 --t ≤ 40 t ≤ 1.5 295 43 t > 40 t > 1.5 295 43 --t ≤ 40 t ≤ 1.5 255 37 t > 40 t > 1.5 255 37 --t ≤ 40 t ≤ 1.5 275 40 t > 40 t > 1.5 275 40 --t ≤ 40 t ≤ 1.5 295 43 t > 40 t > 1.5 295 43 --6 ≤ t ≤ 50 --255 --50 < t ≤ 150 --255 ----6 ≤ t ≤ 50 --275 --50 < t ≤ 150 --275 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
139
4.3 ½Mo Alloy Steels for Pressure Vessel Plates 4.3B Mechanical Properties of ½Mo Alloy Steels for Pressure Vessel Plates (Continued)
ASTM A302/A302M-12
Grade A
JIS G 3119:2013
Symbol SBV1A
JIS G 3124:2009
Symbol SEV295
ASME SA-302/SA-302M
Grade B
ASME SA-533/SA-533M
Type A, Class 1 Type A, Class 2 Type A, Class 3 Grade B
ASTM A302/A302M-12
ASTM A533/A533M-09 (2014) Type A, Class 1 Type A, Class 2 Type A, Class 3 GB 6654-1996 Grade 18MnMoNbR JIS G 3119:2013
Symbol SBV1B
JIS G 3120:2014
Symbol SQV1A Symbol SQV1B Symbol SEV345
JIS G 3124:2009
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K12021 --t ≤ 50 t≤2 310 45 t > 50 t>2 310 45 K12021 --t ≤ 50 t≤2 310 45 t > 50 t>2 310 45 ----6 ≤ t ≤ 50 --315 --50 < t ≤ 150 --315 ------6 ≤ t ≤ 50 --420 --50 < t ≤ 100 --400 --100 < t ≤ 125 --390 --125 < t ≤ 150 --380 --K12022 --t ≤ 50 t≤2 345 50 t > 50 t>2 345 50 K12521 --t ≥ 6.5 t ≥ 0.25 345 50 K12521 --t ≥ 6.5 t ≥ 0.25 485 70 K12521 --6.5 ≤ t ≤ 65 0.25 ≤ t ≤ 2.5 570 83 K12022 --t ≤ 50 t≤2 345 50 t > 50 t>2 345 50 K12521 --t ≥ 6.5 t ≥ 0.25 345 50 K12521 --t ≥ 6.5 t ≥ 0.25 485 70 K12521 --6.5 ≤ t ≤ 65 0.25 ≤ t ≤ 2.5 570 83 ----30 < t ≤ 60 --440 --60 < t ≤ 100 --410 ------6 ≤ t ≤ 50 --345 --50 < t ≤ 150 --345 ----------345 ----------480 ------6 ≤ t ≤ 50 --430 --50 < t ≤ 100 --430 --100 < t ≤ 125 --420 --125 < t ≤ 150 --410 ---
Tensile Strength, min. Elongation MPa ksi % min. 515-655 75-95 19 515-655 75-95 19 515-655 75-95 19 515-655 75-95 19 520-660 --15 520-660 --19 540-690 T --15 540-690 T --19 530-680 T --19 520-670 T --19 550-690 80-100 18 550-690 80-100 18 550-690 80-100 18 620-795 90-115 16 690-860 100-125 16 550-690 80-100 18 550-690 80-100 18 550-690 80-100 18 620-795 90-115 16 690-860 100-125 16 590-740 --17 570-720 --17 550-690 --15 550-690 --18 550-690 T --18 620-790 T --16 590-740 T --14 590-740 T --18 580-730 T --18 570-720 T --18
Heat Treatment AR or N or SR or N+SR N AR, N, SR or N+SR N AR, N, A, Q+T or N+A N or Q+T AR, N, N+T or A AR, N, N+T or A AR, N, N+T or A AR, N, N+T or A AR or N or SR or N+SR N Q+T Q+T Q+T AR, N, SR or N+SR N Q+T Q+T Q+T N+T N+T AR, N, A, Q+T or N+A N or Q+T AR, A or Q+T AR, A or Q+T AR, N, N+T or A AR, N, N+T or A AR, N, N+T or A AR, N, N+T or A
Other ------------T: 31 J @ 0°C T: 31 J @ 0°C T: 31 J @ 0°C T: 31 J @ 0°C --------------------T: 34 J @ 20°C T: 34 J @ 20°C ----L: 40 J @ BA°C L: 47 J @ BA°C T: 31 J @ 0°C T: 31 J @ 0°C T: 31 J @ 0°C T: 31 J @ 0°C
Download From http://bbs.infoeach.com
Designation Grade A
Download From http://bbs.infoeach.com
Specification ASME SA-302/SA-302M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
140
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.1A Chemical Composition of ¾Cr-½Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-387/SA-387M* Grade 2, Class 1
ASTM A387/A387M-11*
Section Thickness mm in -----
C Mn 0.05-0.21 0.55-0.80
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.50-0.80 0.40 0.45-0.60
Grade 2, Class 2
S50460
---
---
---
0.05-0.21 0.55-0.80
0.15-0.40 0.025 0.025 0.50-0.80
0.40
0.45-0.60
Grade 2, Class 1
S50460
---
---
---
0.05-0.21 0.55-0.80
0.15-0.40 0.025 0.025 0.50-0.80
0.40
0.45-0.60
Grade 2, Class 2
S50460
---
---
---
0.05-0.21 0.55-0.80
0.15-0.40 0.025 0.025 0.50-0.80
0.40
0.45-0.60
Symbol SCMV1-1
---
---
6 ≤ t ≤ 200
---
0.21
0.55-0.80
0.40
0.020 0.020 0.50-0.80
0.40
0.45-0.60
Symbol SCMV1-2
---
---
6 ≤ t ≤ 200
---
0.21
0.55-0.80
0.40
0.020 0.020 0.50-0.80
0.40
0.45-0.60
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003
*: See ASTM A20/A20M-14 for additional information. 4.4.1B Mechanical Properties of ¾Cr–½Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M ASTM A387/A387M-11 JIS G 4109:2013
Designation Grade 2, Class 1 Grade 2, Class 2 Grade 2, Class 1 Grade 2, Class 2 Symbol SCMV1-1 Symbol SCMV1-2
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi S50460 ------230 33 S50460 ------310 45 S50460 ------230 33 S50460 ------310 45 ----6 ≤ t ≤ 50 --225 --50 < t ≤ 200 --225 ------6 ≤ t ≤ 50 --315 --50 < t ≤ 200 --315 ---
Tensile Strength, min. Elongation MPa ksi % min. 380-550 55-80 22 485-620 70-90 22 380-550 55-80 22 485-620 70-90 22 380-550 T --18 380-550 T --22 480-620 T --18 480-620 T --22
Heat Treatment A, N+T or Q+T A, N+T or Q+T A, N+T or Q+T A, N+T or Q+T A or N+T A or N+T N+T N+T
Other -----------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 4109:2013
UNS Steel No. No. S50460 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
141
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.2A Chemical Composition of 1Cr-½Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-387/SA-387M* Grade 12, Class 1
ASTM A387/A387M-11*
Section Thickness mm in -----
C Mn 0.05-0.17 0.40-0.65
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.80-1.15 0.40 0.45-0.60
Grade 12, Class 2
K11757
---
---
---
0.05-0.17 0.40-0.65
0.15-0.40 0.025 0.025 0.80-1.15
0.40
0.45-0.60
Grade 12, Class 1
K11757
---
---
---
0.05-0.17 0.40-0.65
0.15-0.40 0.025 0.025 0.80-1.15
0.40
0.45-0.65
Grade 12, Class 2
K11757
---
---
---
0.05-0.17 0.40-0.65
0.15-0.40 0.025 0.025 0.80-1.15
0.40
0.45-0.65
13 CrMo 4-5 Grade 15CrMoR Grade 15CrMog Symbol SCMV2-1
---------
1.7335 -------
------6 ≤ t ≤ 200
---------
0.08-0.18 0.12-0.18 0.12-0.18 0.17
0.40-1.00 0.40-0.70 0.40-0.70 0.40-0.65
0.35 0.15-0.40 0.15-0.40 0.40
0.70-1.15 0.80-1.20 0.80-1.20 0.80-1.15
--0.30 0.30 0.40
0.40-0.60 0.45-0.60 0.45-0.60 0.45-0.60
Symbol SCMV2-2
---
---
6 ≤ t ≤ 200
---
0.17
0.40-0.65
0.40
0.020 0.020 0.80-1.15
0.40
0.45-0.60
0.025 0.030 0.030 0.020
0.010 0.030 0.030 0.020
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Cu 0.30; N 0.012 Cu 0.30 V 0.010; Cu 0.30 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003
*: See ASTM A20/A20M-14 for additional information. 4.4.2B Mechanical Properties of 1Cr-½Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M
EN 10028-2:2009
Designation Grade 12, Class 1 Grade 12, Class 2 Grade 12, Class 1 Grade 12, Class 2 13 CrMo 4-5
GB 6654-1996
Grade 15CrMoR
GB 713-1997
Grade 15CrMog
JIS G 4109:2013
Symbol SCMV2-1
ASTM A387/A387M-11
Symbol SCMV2-2
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K11757 ------230 33 K11757 ------275 40 K11757 ------230 33 K11757 ------275 40 --1.7335 t ≤ 16 --300 --15 < t ≤ 60 --290 --60 < t ≤ 100 --270 --100 < t ≤ 150 --255 --150 < t ≤ 250 --245 ------6 < t ≤ 60 --295 --60 < t ≤ 100 --275 ------t ≤ 60 --295 --60 < t ≤ 100 --275 ------6 ≤ t ≤ 50 --225 --50 < t ≤ 200 --225 ------6 ≤ t ≤ 50 --275 --50 < t ≤ 200 --275 ---
Tensile Strength, min. Elongation MPa ksi % min. 380-550 55-80 22 450-585 65-85 22 380-550 55-80 22 450-585 65-85 22 450-600 --19 450-600 --19 440-590 --19 430-580 --19 420-570 --19 450-590 --19 450-590 --18 450-590 --19 450-590 --18 380-550 T --18 380-550 T --22 450-590 T --19 450-590 T --22
Heat Treatment A, N+T or Q+T A, N+T or Q+T A, N+T or Q+T A, N+T or Q+T N+T N+T N+T N+T or Q+T Q+T N+T N+T HR, CtR, N or N+T HR, CtR, N or N+T A or N+T A or N+T N+T N+T
Other --------see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10028-2:2009 GB 6654-1996 GB 713-1997 JIS G 4109:2013
UNS Steel No. No. K11757 ---
T: 31 J @ 20°C T: 31 J @ 20°C T: 31 J @ RT T: 31 J @ RT ---------
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
142
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.3A Chemical Composition of 1¼Cr-½Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-387/SA-387M* Grade 11, Class 1
ASTM A387/A387M-11*
Section Thickness mm in -----
C Mn 0.05-0.17 0.40-0.65
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.50-0.80 0.025 0.025 1.00-1.50 0.40 0.45-0.65
Grade 11, Class 2
K11789
---
---
---
0.05-0.17 0.40-0.65
0.50-0.80 0.025 0.025 1.00-1.50
0.40
0.45-0.65
Grade 11, Class 1
K11789
---
---
---
0.05-0.17 0.40-0.65
0.50-0.80 0.025 0.025 1.00-1.50
0.40
0.45-0.65
Grade 11, Class 2
K11789
---
---
---
0.05-0.17 0.40-0.65
0.50-0.80 0.025 0.025 1.00-1.50
0.40
0.45-0.65
13CrMoSi5-5 Symbol SCMV3-1
-----
1.7336 ---
--6 ≤ t ≤ 200
-----
0.17 0.17
0.40-0.65 0.40-0.65
0.50-0.80 0.015 0.005 1.00-1.50 0.50-0.80 0.020 0.020 1.00-1.50
0.30 0.40
0.45-0.65 0.45-0.60
Symbol SCMV3-2
---
---
6 ≤ t ≤ 200
---
0.17
0.40-0.65
0.50-0.80 0.020 0.020 1.00-1.50
0.40
0.45-0.60
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Cu 0.30; N 0.012 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003
*: See ASTM A20/A20M-14 for additional information. 4.4.3B Mechanical Properties of 1¼Cr–½Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M
EN 10028-2:2009
Designation Grade 11, Class 1 Grade 11, Class 2 Grade 11, Class 1 Grade 11, Class 2 13CrMoSi5-5
JIS G 4109:2013
Symbol SCMV3-1
ASTM A387/A387M-11
Symbol SCMV3-2
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K11789 ------240 35 K11789 ------310 45 K11789 ------240 35 K11789 ------310 45 --1.7336 t ≤ 60 --310 --t ≤ 60 --400 --60 < t ≤ 100 --300 --60 < t ≤ 100 --390 --100 < t ≤ 250 --380 ------6 ≤ t ≤ 50 --235 --50 < t ≤ 200 --235 ------6 ≤ t ≤ 50 --315 --50 < t ≤ 200 --315 ---
Tensile Strength, min. Elongation MPa ksi % min. 415-585 60-85 22 515-690 75-100 22 415-585 60-85 22 515-690 75-100 22 510-690 --20 510-690 --20 480-660 --20 500-680 --20 490-670 --20 410-590 T --19 410-590 T --22 520-690 T --18 520-690 T --22
Heat Treatment A, N+T or Q+T A, N+T or Q+T A, N+T or Q+T A, N+T or Q+T N+T Q+T N+T Q+T Q+T A or N+T A or N+T N+T N+T
Other --------see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10028-2:2009 JIS G 4109:2013
UNS Steel No. No. K11789 ---
---------
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
143
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.4A Chemical Composition of 2¼Cr-1Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-387/SA-387M* Grade 22, Class 1
UNS Steel No. No. K21590 ---
Section Thickness mm in -----
C Mn 0.05-0.15 0.30-0.60
Si 0.50
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.025 2.00-2.50 0.40 0.90-1.10
0.05-0.15 0.30-0.60
0.50
0.025 0.025 2.00-2.50
0.40
0.90-1.10
0.30-0.60
0.50
0.025 0.025 2.00-2.50
0.40
0.90-1.10
K21590
---
---
---
Grade 22L, Class 1
K21590
---
---
---
Grade 22, Class 1
K21590
---
---
---
0.05-0.15 0.30-0.60
0.50
0.025 0.025 2.00-2.50
0.40
0.90-1.10
Grade 22, Class 2
K21590
---
---
---
0.05-0.15 0.30-0.60
0.50
0.025 0.025 2.00-2.50
0.40
0.90-1.10
Grade 22L, Class 1
K21590
---
---
---
0.30-0.60
0.50
0.025 0.025 2.00-2.50
0.40
0.90-1.10
10CrMo9-10 Symbol SCMV4-1
-----
1.7380 ---
--6 ≤ t ≤ 300
-----
0.08-0.14 0.40-0.80 0.17 0.30-0.60
0.50 0.50
0.020 0.010 2.00-2.50 0.020 0.020 2.00-2.50
--0.40
0.90-1.10 0.90-1.10
Symbol SCMV4-2
---
---
6 ≤ t ≤ 300
---
0.17
0.30-0.60
0.50
0.020 0.020 2.00-2.50
0.40
0.90-1.10
JIS G 4110:2008 Symbol SCMQ4E --*: See ASTM A20/A20M-14 for additional information.
---
6 ≤ t ≤ 300
---
0.17
0.30-0.60
0.50
0.015 0.015 2.00-2.50
0.40
0.90-1.10
Download From http://bbs.infoeach.com
ASTM A387/A387M-11*
EN 10028-2:2009 JIS G 4109:2013
0.10
0.10
4.4.4B Mechanical Properties of 2¼Cr–1Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M
ASTM A387/A387M-11
EN 10028-2:2009
JIS G 4109:2013 JIS G 4110:2008
Designation Grade 22, Class 1 Grade 22, Class 2 Grade 22L, Class 1 Grade 22, Class 1 Grade 22, Class 2 Grade 22L, Class 1 10CrMo9-10
Symbol SCMV4-1 Symbol SCMV4-2 Symbol SCMQ4E
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K21590 ------205 30 K21590 ------310 45 K21590 ------205 30 K21590 ------205 30 K21590 ------310 45 K21590 ------205 30 --1.7380 t ≤ 16 --310 --16 < t ≤ 40 --300 --40 < t ≤ 60 --290 --60 < t ≤ 100 --280 --100 < t ≤ 150 --260 --150 < t ≤ 250 --250 ------6 ≤ t ≤ 300 --205 ------6 ≤ t ≤ 300 --315 ------6 ≤ t ≤ 300 --380 ---
Tensile Strength, min. Elongation MPa ksi % min. 415-585 60-85 18 515-690 75-100 18 415-585 60-85 18 415-585 60-85 18 515-690 75-100 18 415-585 60-85 18 480-630 --18 480-630 --18 480-630 --18 470-620 --17 460-610 --17 450-600 --17 410-590 T --18 520-690 T --18 580-760 T --18
Heat Treatment A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T N+T N+T N+T N+T or Q+T Q+T Q+T A or N+T N+T Q+T or N+T
Other ------------see standard for impact data
Download From http://bbs.infoeach.com
Grade 22, Class 2
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Cu 0.30; N 0.012 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Nb 0.02
----T: 54 J @ -18°C
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
144
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.5A Chemical Composition of 3Cr-1Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-387/SA-387M* Grade 21, Class 1
JIS G 4109:2013
Section Thickness mm in -----
C Mn 0.05-0.15 0.30-0.60
Si 0.50
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.025 2.75-3.25 0.40 0.90-1.10
0.05-0.15 0.30-0.60
0.50
0.025 0.025 2.75-3.25
0.40
0.90-1.10
0.30-0.60
0.50
0.025 0.025 2.75-3.25
0.40
0.90-1.10
Grade 21, Class 2
K31545
---
---
---
Grade 21L, Class 1
K31545
---
---
---
Grade 21, Class 1
K31545
---
---
---
0.05-0.15 0.30-0.60
0.50
0.025 0.025 2.75-3.25
0.40
0.90-1.10
Grade 21, Class 2
K31545
---
---
---
0.05-0.15 0.30-0.60
0.50
0.025 0.025 2.75-3.25
0.40
0.90-1.10
Grade 21L, Class 1
K31545
---
---
---
0.10
0.30-0.60
0.50
0.025 0.025 2.75-3.25
0.40
0.90-1.10
Symbol SCMV5-1
---
---
6 ≤ t ≤ 300
---
0.17
0.30-0.60
0.50
0.020 0.020 2.75-3.25
0.40
0.90-1.10
Symbol SCMV5-2
---
---
6 ≤ t ≤ 300
---
0.17
0.30-0.60
0.50
0.020 0.020 2.75-3.25
0.40
0.90-1.10
0.10
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003
*: See ASTM A20/A20M-14 for additional information. 4.4.5B Mechanical Properties of 3Cr–1Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M
ASTM A387/A387M-11
JIS G 4109:2013
Designation Grade 21, Class 1 Grade 21, Class 2 Grade 21L, Class 1 Grade 21, Class 1 Grade 21, Class 2 Grade 21L, Class 1 Symbol SCMV5-1 Symbol SCMV5-2
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K31545 ------205 30 K31545 ------310 45 K31545 ------205 30 K31545 ------205 30 K31545 ------310 45 K31545 ------205 30 ----6 ≤ t ≤ 300 --205 ------6 ≤ t ≤ 300 --315 ---
Tensile Strength, min. Elongation MPa ksi % min. 415-585 60-85 18 515-690 75-100 18 415-585 60-85 18 415-585 60-85 18 515-690 75-100 18 415-585 60-85 18 410-590 T --18 520-690 T --18
Heat Treatment A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A or N+T N+T
Other -----------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A387/A387M-11*
UNS Steel No. No. K31545 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
145
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.6A Chemical Composition of 5Cr-½Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-387/SA-387M* Grade 5, Class 1
ASTM A387/A387M-11*
Section Thickness mm in -----
C 0.15
Mn 0.30-0.60
Si 0.50
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.025 4.00-6.00 0.40 0.45-0.65
Grade 5, Class 2
S50200
---
---
---
0.15
0.30-0.60
0.50
0.025 0.025 4.00-6.00
0.40
0.45-0.65
Grade 5, Class 1
S50200
---
---
---
0.15
0.30-0.60
0.50
0.025 0.025 4.00-6.00
0.40
0.45-0.65
Grade 5, Class 2
S50200
---
---
---
0.15
0.30-0.60
0.50
0.025 0.025 4.00-6.00
0.40
0.45-0.65
X12CrMo5 Symbol SCMV6-1
-----
1.7362 ---
--6 ≤ t ≤ 300
-----
0.10-0.15 0.30-0.60 0.15 0.30-0.60
0.50 0.50
0.020 0.005 4.0-6.0 0.020 0.020 4.00-6.00
0.30 0.40
0.45-0.65 0.45-0.65
Symbol SCMV6-2
---
---
6 ≤ t ≤ 300
---
0.50
0.020 0.020 4.00-6.00
0.40
0.45-0.65
0.15
0.30-0.60
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Cu 0.30; N 0.012 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.003
*: See ASTM A20/A20M-14 for additional information. 4.4.6B Mechanical Properties of 5Cr–½Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M ASTM A387/A387M-11 EN 10028-2:2009
JIS G 4109:2013
Designation Grade 5, Class 1 Grade 5, Class 2 Grade 5, Class 1 Grade 5, Class 2 X12CrMo5
Symbol SCMV6-1 Symbol SCMV6-2
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi S50200 ------205 30 S50200 ------310 45 S50200 ------205 30 S50200 ------310 45 --1.7362 t ≤ 60 --320 --60 < t ≤ 150 --300 --150 < t ≤ 250 --300 ------6 ≤ t ≤ 300 --205 ------6 ≤ t ≤ 300 --315 ---
Tensile Strength, min. Elongation MPa ksi % min. 415-585 60-85 18 515-690 75-100 18 415-585 60-85 18 515-690 75-100 18 510-690 --20 480-660 --20 450-630 --20 410-590 T --18 520-690 T --18
Heat Treatment A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T A, SR, N+T or Q+T N+T N+T Q+T A or N+T N+T
Other --------see standard for impact data -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10028-2:2009 JIS G 4109:2013
UNS Steel No. No. S50200 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
146
4.4 Cr-Mo Alloy Steels for Pressure Vessel Plates 4.4.7A Chemical Composition of 9Cr-1Mo Alloy Steels for Pressure Vessel Plates Section Thickness mm in -----
ASTM A387/A387M-11*
Grade 91, Class 2
K91560
---
---
---
0.08-0.12 0.30-0.60
EN 10028-2:2009
X10CrMoVNb9-1
---
1.4903
---
---
0.08-0.12 0.30-0.60
C Mn 0.08-0.12 0.30-0.60
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo Others 0.20-0.50 0.020 0.010 8.00-9.50 0.40 0.85-1.05 V 0.18-0.25; Al 0.02; Cu 0.40; Ti 0.01; Cb 0.06-0.10; N 0.030-0.070; Zr 0.01; B 0.0010 0.20-0.50 0.020 0.010 8.00-9.50 0.40 0.85-1.05 V 0.18-0.25; Al 0.02; Cu 0.40; Ti 0.01; Cb 0.06-0.10; N 0.030-0.070; Zr 0.01; B 0.0010 0.50 0.020 0.005 8.0-9.5 0.30 0.85-1.05 V 0.18-0.25; Al 0.040; Cu 0.30; Nb 0.06-0.10; N 0.030-0.070
*: See ASTM A20/A20M-14 for additional information. 4.4.7B Mechanical Properties of 9Cr–1Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-387/SA-387M ASTM A387/A387M-11 EN 10028-2:2009
Designation Grade 91, Class 2 Grade 91, Class 2 X10CrMoVNb9-1
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K90901 ------415 60 K91560 ------415 60 --1.4903 t ≤ 60 --445 --60 < t ≤ 150 --435 --150 < t ≤ 250 --435 ---
Tensile Strength, min. Elongation MPa ksi % min. 585-760 85-110 18 585-760 85-110 18 580-760 --18 550-730 --18 520-700 --18
Heat Treatment N+T, A or SR N+T, A or SR N+T N+T Q+T
Other ----see standard for impact data
Download From http://bbs.infoeach.com
UNS Steel No. No. K90901 ---
Download From http://bbs.infoeach.com
Specification Designation ASME SA-387/SA-387M* Grade 91, Class 2
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
147
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.1A Chemical Composition of ½Ni Alloy Steels for Pressure Vessel Plates
Specification EN 10028-4:2009
GB 3531-1996 ISO 9328-4:2004
Steel No. 1.6212
Section Thickness mm in -----
13MnNi6-3
---
1.6217
---
Grade 15MnNiDR Grade 11MnNi5-3
-----
-----
Grade 13MnNi6-3
---
---
C 0.14
Mn 0.70-1.50
---
0.16
0.85-1.70
-----
-----
0.18 0.14
1.20-1.60 0.70-1.50
---
---
0.16
0.85-1.70
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo Others 0.025 0.010 --0.30-0.80 --V 0.050; Al 0.020 min.; Nb 0.05; (Cr+Cu+Mo) 0.50 0.50 0.025 0.010 --0.30-0.85 --V 0.050; Al 0.020 min.; Nb 0.05; (Cr+Cu+Mo) 0.50 0.15-0.50 0.030 0.025 0.25 0.20-0.60 0.08 V 0.06; Al 0.020 min.; Cu 0.25 0.50 0.025 0.015 --0.30-0.80 --V 0.05; Al 0.02-; Nb 0.05; (Cr+Cu+Mo) 0.50 0.50 0.025 0.015 --0.30-0.80 --V 0.05; Al 0.02-; Nb 0.05; (Cr+Cu+Mo) 0.50 Si 0.50
4.5.1B Mechanical Properties of ½ Ni Alloy Steels for Pressure Vessel Plates
Specification EN 10028-4:2009
Designation 11MnNi5-3
UNS No. ---
13MnNi6-3
---
GB 3531-1996
Grade 15MnNiDR
---
ISO 9328-4:2004
Grade 11MnNi5-3
---
Grade 13MnNi6-3
---
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.6212 t ≤ 30 --285 --30 < t ≤ 50 --275 --50 < t ≤ 80 --265 --1.6217 t ≤ 30 --355 --30 < t ≤ 50 --345 --50 < t ≤ 80 --335 ----6 ≤ t ≤ 16 --325 --16 < t ≤ 36 --305 --36 < t ≤ 60 --290 ----t ≤ 30 --285 ---
---
30 < t ≤ 50 50 < t ≤ 80 t ≤ 30 30 < t ≤ 50 50 < t ≤ 80
-----------
275 265 355 345 335
-----------
Tensile Strength, min. Elongation MPa ksi % min. 420-530 --24 420-530 --24 420-530 --24 490-610 --22 490-610 --22 490-610 --22 490-630 --20 470-610 --20 460-600 --20 550, 80 35, 24 T 420-530 T 420-530 T --24 T 420-530 T --24 T 490-610 T --22 T 490-610 T --22 T 490-610 T --22 T
Heat Treatment N+T N+T N+T N+T N+T N+T N or N+T N or N+T N or N+T N or N+T N or N+T N or N+T N or N+T N or N+T N or N+T
Other see standard for impact data see standard for impact data ------see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
UNS No. ---
Designation 11MnNi5-3
see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
148
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.2A Chemical Composition of 1½ Ni Alloy Steels for Pressure Vessel Plates
Specification EN 10028-4:2009 ISO 9328-4:2004
Designation 15NiMn6 Grade 15NiMn6
UNS No. -----
Steel No. 1.6228 ---
Section Thickness mm in ---------
C 0.18 0.18
Mn 0.80-1.50 0.80-1.50
Si 0.35 0.35
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.010 --1.30-1.70 --0.025 0.015 --1.30-1.70 ---
Others V 0.05; (Cr+Cu+Mo) 0.50 V 0.05; (Cr+Cu+Mo) 0.50
4.5.2B Mechanical Properties of 1½ Ni Alloy Steels for Pressure Vessel Plates
ISO 9328-4:2004
Grade 15NiMn6
UNS No. ---
---
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.6228 t ≤ 30 --355 --30 < t ≤ 50 --345 --50 < t ≤ 80 --335 ----t ≤ 30 --355 --30 < t ≤ 50 --345 --50 < t ≤ 80 --335 ---
Tensile Strength, min. Elongation MPa ksi % min. 490-640 --22 490-640 --22 490-640 --22 490-640 T --22 T 490-640 T --22 T 490-640 T --22 T
Heat Treatment N or N+T or Q+T N or N+T or Q+T N or N+T or Q+T N or N+T or Q+T N or N+T or Q+T N or N+T or Q+T
Other see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
Designation 15NiMn6
Download From http://bbs.infoeach.com
Specification EN 10028-4:2009
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
149
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.3A Chemical Composition of 2¼Ni Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-203/SA-203M* Grade A
Grade A
Grade B
K22103
K21703
K22103
JIS G 3127:2013 Symbol SL2N255 --*: See ASTM A20/A20M-14 for additional information.
---
---
---
---
Section Thickness mm in t ≤ 50 t≤2
C 0.17
Mn 0.70
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 2.10-2.50 0.12
50 < t ≤ 100
2 100
t>4
0.23
0.80
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
t ≤ 50
t≤2
0.21
0.70
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
50 < t ≤ 100
2 100
t>4
0.25
0.80
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
t ≤ 50
t≤2
0.17
0.70
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
50 < t ≤ 100
2 100
t>4
0.23
0.80
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
t ≤ 50
t≤2
0.21
0.70
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
50 < t ≤ 100
2 100
t>4
0.25
0.80
0.15-0.40 0.025 0.025
0.30
2.10-2.50
0.12
6 ≤ t ≤ 50
---
0.17
0.70
---
2.10-2.50
---
0.30
0.015 0.015
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A203/A203M-12*
Grade B
UNS Steel No. No. K21703 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
150
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.3B Mechanical Properties of 2¼Ni Alloy Steels for Pressure Vessel Plates
Specification ASME SA-203/SA-203M
Designation Grade A Grade B
ASTM A203/A203M-12
Grade B Symbol SL2N255
16 < t ≤ 20 20 < t ≤ 50
-----
255 255
-----
Tensile Strength, min. Elongation MPa ksi % min. 450-585 65-85 23 450-585 65-85 23 485-620 70-90 21 485-620 70-90 21 450-585 65-85 23 450-585 65-85 23 485-620 70-90 21 485-620 70-90 21 450-590 T --24
Heat Treatment N N N N N N N N N, N+T or TMCP
450-590 T 450-590 T
N, N+T or TMCP N, N+T or TMCP
-----
29 24
Other 27 J @ BA°C 27 J @ BA°C 27 J @ BA°C 27 J @ BA°C 27 J @ BA°C 27 J @ BA°C 27 J @ BA°C 27 J @ BA°C see standard for impact data L: 21 J @ -70°C L: 21 J @ -70°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 3127:2013
Grade A
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K21703 --t ≤ 50 t≤2 255 37 t > 50 t>2 255 37 K22103 --t ≤ 50 t≤2 275 40 t > 50 t>2 275 40 K21703 --t ≤ 50 t≤2 255 37 t > 50 t>2 255 37 K22103 --t ≤ 50 t≤2 275 40 t > 50 t>2 275 40 ----6 ≤ t ≤ 16 --255 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
151
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.4A Chemical Composition of 3½Ni Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-203/SA-203M* Grade D
Grade E
EN 10028-4:2009 JIS G 3127:2013
Grade D
Grade E
Grade F
K32018
---
K31718
K32018
---
12Ni14 --Symbol SL3N255 --Symbol SL3N275 --Symbol SL3N440 --*: See ASTM A20/A20M-14 for additional information.
---
---
---
---
---
1.5637 -------
Section Thickness mm in t ≤ 50 t≤2
C 0.17
Mn 0.70
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 3.25-3.75 0.12
50 < t ≤ 100
22 345 50 K31718 --t ≤ 50 t≤2 255 37 t > 50 t>2 255 37 K32018 --t ≤ 50 t≤2 275 40 t > 50 t>2 275 40 ----t ≤ 50 t≤2 380 55 t > 50 t>2 345 50 --1.5637 t ≤ 30 --355 --30 < t ≤ 50 --345 --50 < t ≤ 80 --335 ------6 ≤ t ≤ 16 --255 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
153
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.5A Chemical Composition of 5Ni Alloy Steels for Pressure Vessel Plates
Specification EN 10028-4:2009 JIS G 3127:2013
Designation X12Ni5 Symbol SL5N590
UNS No. -----
Steel No. 1.5680 ---
Section Thickness mm in ----6 ≤ t ≤ 50 ---
C 0.15 0.13
Mn 0.30-0.80 1.50
Si 0.35 0.30
Weight, %max, Unless Otherwise Specified P S Cr Ni Mo 0.020 0.005 --4.75-5.25 --0.015 0.015 --4.75-6.00 ---
Others V 0.05; (Cr+Cu+Mo) 0.50 ---
4.5.5B Mechanical Properties of 5Ni Alloy Steels for Pressure Vessel Plates
JIS G 3127:2013
Symbol SL5N590
UNS No. -----
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.5680 t ≤ 30 --390 --30 < t ≤ 50 --380 ----6 ≤ t ≤ 16 --590 --16 < t ≤ 20 20 < t ≤ 50
-----
590 590
-----
Tensile Strength, min. Elongation MPa ksi % min. 530-710 --20 530-710 --20 690-830 T --21 690-830 T 690-830 T
-----
Heat Treatment N or N+T or Q+T N or N+T or Q+T Q+T
25 21
Q+T Q+T
Other see standard for impact data see standard for impact data L: 41 J @ -130°C L: 41 J @ -130°C
4.5.6A Chemical Composition of 9Ni Alloy Steels for Pressure Vessel Plates
Specification ASME SA-353/SA-353M* ---
Designation
UNS Steel No. No. K81340 ---
Section Thickness mm in -----
C 0.13
Mn 0.90
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.015 0.015 0.30 8.50-9.50 0.12
ASME SA-553/SA-553M* Type II
K71340
---
---
---
0.13
0.90
0.15-0.40 0.035 0.035
0.30
7.50-8.50
0.12
Type I
K81340
---
---
---
0.13
0.90
0.15-0.40 0.035 0.035
0.30
8.50-9.50
0.12
---
K81340
---
---
---
0.13
0.90
0.15-0.40 0.015 0.015
0.30
8.50-9.50
0.12
Type II
K71340
---
---
---
0.13
0.90
0.15-0.40 0.015 0.015
0.30
7.50-8.50
0.12
Type I
K81340
---
---
---
0.13
0.90
0.15-0.40 0.015 0.015
0.30
8.50-9.50
0.12
---
K81340
---
---
---
0.13
0.90
0.15-0.40 0.015 0.015
0.30
8.50-9.50
0.12
1.5662 1.5663 -----
----6 ≤ t ≤ 50 6 ≤ t ≤ 100
---------
0.10 0.10 0.12 0.12
0.30-0.80 0.30-0.80 0.90 0.90
---------
8.5-10.0 8.5-10.0 8.50-9.50 8.50-9.50
0.10 0.10 -----
ASTM A353/A353M-09 (2014)* ASTM A553/A553M-14*
ASTM A844/A844M-09* EN 10028-4:2009
X8Ni9 --X7Ni9 --JIS G 3127:2013 Symbol SL9N520 --Symbol SL9N590 --*: See ASTM A20/A20M-14 for additional information.
0.35 0.35 0.30 0.30
0.020 0.015 0.015 0.015
0.005 0.005 0.015 0.015
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.05; (Cr+Cu+Mo) 0.50 V 0.01; (Cr+Cu+Mo) 0.50 -----
Download From http://bbs.infoeach.com
Designation X12Ni5
Download From http://bbs.infoeach.com
Specification EN 10028-4:2009
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
154
4.5 Ni Alloy Steels for Pressure Vessel Plates 4.5.6B Mechanical Properties of 9Ni Alloy Steels for Pressure Vessel Plates
Specification ASME SA-353/SA-353M ASME SA-553/SA-553M
Designation
JIS G 3127:2013
X7Ni9
Symbol SL9N520
Symbol SL9N590
---
---
Tensile Strength, min. Elongation MPa ksi % min. 690-825 100-120 20.0 690-825 100-120 20.0 690-825 100-120 20.0 690-825 100-120 20.0 690-825 100-120 20.0 690-825 100-120 20.0 690-825 100-120 20.0 640-840 --18 640-840 --18 680-820 --18 640-840 --18 640-840 --18 680-820 --18 680-820 --18 680-820 --18 680-820 --18 690-830 T --21
Heat Treatment NN+T Q+T Q+T NN+T Q+T Q+T Q+T N or N+T Q+T Q+T N or N+T Q+T Q+T N or N+T or Q+T Q+T Q+T NN+T
16 < t ≤ 20 20 < t ≤ 50 6 ≤ t ≤ 16
-------
520 520 590
-------
690-830 T 690-830 T 690-830 T
-------
25 21 21
NN+T NN+T Q+T
16 < t ≤ 20 20 < t ≤ 100
-----
590 590
-----
690-830 T 690-830 T
-----
25 21
Q+T Q+T
Other --------------see standard for impact data
see standard for impact data see standard for impact data L: 34 J @ -196°C L: 34 J @ -196°C see standard for impact data L: 41 J @ -196°C L: 41 J @ -196°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
--Type II Type I ASTM A353/A353M-09 (2014) --ASTM A553/A553M-14 Type II Type I ASTM A844/A844M-09 --EN 10028-4:2009 X8Ni9
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K81340 ------515 75 K71340 ------585 85 K81340 ------585 85 K81340 ------515 75 K71340 ------585 85 K81340 ------585 85 K81340 --t ≤ 50 t≤2 585 85 --1.5662 t ≤ 30 --490 --t ≤ 30 --490 --t ≤ 30 --585 --30 < t ≤ 50 --480 --30 < t ≤ 50 --480 --30 < t ≤ 50 --575 ----1.5663 t ≤ 15 --585 --15 < t ≤ 30 --585 --30 < t ≤ 50 --575 ------6 ≤ t ≤ 16 --520 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
155
4.6 Ni-Mo Alloy Steels for Pressure Vessel Plates 4.6.1A Chemical Composition of ½Ni-½Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-302/SA-302M* Grade C
UNS Steel No. No. K12039 ---
Section Thickness mm in t ≤ 25 t≤1
C 0.20
Mn 1.15-1.50
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.40-0.70 0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
Type B, Class 2
K12539
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
Type B, Class 3
K12539
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
Grade C
K12039
---
t ≤ 25
t≤1
0.20
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
ASTM A302/A302M-12*
ASTM A533/A533M- 09 (2014)*
EN 10028-2:2009 JIS G 3119:2013
JIS G 3120:2014
Type B, Class 1
K12539
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
Type B, Class 2
K12539
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
Type B, Class 3
K12539
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.40-0.70 0.45-0.60
-----
1.6311 ---
--6 ≤ t ≤ 25
-----
0.15-0.23 1.00-1.50 0.20 1.15-1.50
0.40 0.020 0.010 0.15-0.40 0.020 0.020
0.20 0.30
0.40-0.80 0.45-0.60 0.40-0.70 0.45-0.60
25 < t ≤ 50
---
0.23
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40-0.70 0.45-0.60
50 < t ≤ 150
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40-0.70 0.45-0.60
20MnMoNi4-5 Symbol SBV2
Symbol SQV2A
---
---
---
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40-0.70 0.45-0.60
Symbol SQV2B
---
---
---
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.40-0.70 0.45-0.60
Download From http://bbs.infoeach.com
K12539
Download From http://bbs.infoeach.com
ASME SA-533/SA-533M* Type B, Class 1
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.02; Cu 0.20; N 0.012 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010
*: See ASTM A20/A20M-14 for additional information.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
156
4.6 Ni-Mo Alloy Steels for Pressure Vessel Plates 4.6.1B Mechanical Properties of ½Ni-½Mo Alloys Steels for Pressure Vessel Plates
Specification ASME SA-302/SA-302M
Designation Grade C
ASME SA-533/SA-533M
Type B, Class 1 Type B, Class 2 Type B, Class 3 Grade C
ASTM A302/A302M-12
JIS G 3119:2013
Symbol SBV2
JIS G 3120:2014
Symbol SQV2A Symbol SQV2B
Tensile Strength, min. Elongation MPa ksi % min. 550-690 80-100 20 550-690 80-100 20 550-690 80-100 18 620-795 90-115 16 690-860 100-125 16 550-690 80-100 20 550-690 80-100 20 550-690 80-100 18 620-795 90-115 16 690-860 100-125 16 590-750 --18 590-730 --18 570-710 --18 570-710 --18 560-700 --18 550-690 --17 550-690 --20 550-690 T --18 620-790 T --16
Heat Treatment AR or N or SR or N+SR N Q+T Q+T Q+T AR, N, SR or N+SR N Q+T Q+T Q+T Q+T Q+T Q+T Q+T Q+T AR, N, A, Q+T or N+A N or Q+T AR, A or Q+T AR, A or Q+T
Other --------------------see standard for impact data
----L: 40 J @ BA°C L: 47 J @ BA°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A533/A533M-09 (2014) Type B, Class 1 Type B, Class 2 Type B, Class 3 EN 10028-2:2009 20MnMoNi4-5
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K12039 --t ≤ 50 t≤2 345 50 t > 50 t>2 345 50 K12539 --t ≥ 6.5 t ≥ 0.25 345 50 K12539 --t ≥ 6.5 t ≥ 0.25 485 70 K12539 --6.5 ≤ t ≤ 65 0.25 ≤ t ≤ 2.5 570 83 K12039 --t ≤ 50 t≤2 345 50 t > 50 t>2 345 50 K12539 --t ≥ 6.5 t ≥ 0.25 345 50 K12539 --t ≥ 6.5 t ≥ 0.25 485 70 K12539 --6.5 ≤ t ≤ 65 0.25 ≤ t ≤ 2.5 570 83 --1.6311 t ≤ 40 --470 --40 < t ≤ 60 --460 --60 < t ≤ 100 --450 --100 < t ≤ 150 --440 --150 < t ≤ 250 --400 ------6 ≤ t ≤ 50 --345 --50 < t ≤ 150 --345 ----------345 ----------480 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
157
4.6 Ni Alloys Steels for Pressure Plates 4.6.2A Chemical Composition of ¾Ni-½Mo Alloy Steels for Pressure Vessel Plates
Specification Designation ASME SA-302/SA-302M* Grade D
UNS Steel No. No. K12054 ---
Section Thickness mm in t ≤ 25 t≤1
C 0.20
Mn 1.15-1.50
Weight, %max, Unless Otherwise Specified Si P S Cr Ni Mo 0.15-0.40 0.025 0.025 0.30 0.70-1.00 0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
Type C, Class 2
K12554
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
Type C, Class 3
K12554
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
Grade D
K12054
---
t ≤ 25
t≤1
0.20
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
25 < t ≤ 50
1 50
t>2
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
ASTM A302/A302M-12*
ASTM A533/A533M-09 (2014)*
Type C, Class 1
K12554
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
Type C, Class 2
K12554
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
Type C, Class 3
K12554
---
---
---
0.25
1.15-1.50
0.15-0.40 0.025 0.025
0.30
0.70-1.00 0.45-0.60
0.30
1.00-1.30 0.25-0.50
EN 10028-2:2009
15NiCuMoNb5-6-4
---
1.6368
---
---
0.17
0.80-1.20
0.25-0.50 0.025 0.010
GB 6654-1996 JIS G 3119:2013
Grade 13MnNiMoNbR Symbol SBV3
-----
-----
--6 ≤ t ≤ 25
-----
0.15 0.20
1.20-1.60 1.15-1.50
0.15-0.50 0.025 0.025 0.20-0.40 0.60-1.00 0.20-0.40 0.15-0.40 0.020 0.020 0.30 0.70-1.00 0.45-0.60
25 < t ≤ 50
---
0.23
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.70-1.00 0.45-0.60
50 < t ≤ 150
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.70-1.00 0.45-0.60
JIS G 3120:2014
Symbol SQV3A
---
---
---
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.70-1.00 0.45-0.60
Symbol SQV3B
---
---
---
---
0.25
1.15-1.50
0.15-0.40 0.020 0.020
0.30
0.70-1.00 0.45-0.60
Download From http://bbs.infoeach.com
K12554
Download From http://bbs.infoeach.com
ASME SA-533/SA-533M* Type C, Class 1
Others V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Cb 0.02; B 0.0010 Al 0.015 min.; Cu 0.50-0.80; Nb 0.015-0.045; N 0.020 Cu 0.30; Nb 0.005-0.020 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010 V 0.03; Cu 0.40; Ti 0.03; Nb 0.02; B 0.0010
*: See ASTM A20/A20M-14 for additional information.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
158
4.6 Ni-Mo Alloy Steels for Pressure Vessel Plates 4.6.2B Mechanical Properties of ¾Ni-½Mo Alloy Steels for Pressure Vessel Plates
Specification ASME SA-302/SA-302M
Designation Grade D
ASME SA-533/SA-533M
Type C, Class 1 Type C, Class 2 Type C, Class 3 Grade D
ASTM A302/A302M-12
GB 6654-1996
Grade 13MnNiMoNbR
JIS G 3119:2013
Symbol SBV3
JIS G 3120:2014
Symbol SQV3A Symbol SQV3B
Tensile Strength, min. Elongation MPa ksi % min. 550-690 80-100 20 550-690 80-100 20 550-690 80-100 18 620-795 90-115 16 690-860 100-125 16 550-690 80-100 20 550-690 80-100 20 550-690 80-100 18 620-795 90-115 16 690-860 100-125 16 610-780 --16 610-780 --16 600-760 --16 590-740 --16 580-740 --16 570-720 --18 570-720 --18 550-690 --17 550-690 --20 550-690 T --18 620-790 T --16
Heat Treatment AR or N or SR or N+SR N Q+T Q+T Q+T AR, N, SR or N+SR N Q+T Q+T Q+T N+T N+T N+T N+T or Q+T Q+T N+T N+T AR, N, A, Q+T or N+A N or Q+T AR, A or Q+T AR, A or Q+T
Other --------------------see standard for impact data
T: 31 J @ 0°C T: 31 J @ 0°C ----L: 40 J @ BA°C L: 47 J @ BA°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A533/A533M-09 (2014) Type C, Class 1 Type C, Class 2 Type C, Class 3 EN 10028-2:2009 15NiCuMoNb5-6-4
UNS Steel Section Thickness / Diameter Yield Strength, min. No. No. mm in. MPa ksi K12054 --t ≤ 50 t≤2 345 50 t > 50 t>2 345 50 K12554 --t ≥ 6.5 t ≥ 0.25 345 50 K12554 --t ≥ 6.5 t ≥ 0.25 485 70 K12554 --6.5 ≤ t ≤ 65 0.25 ≤ t ≤ 2.5 570 83 K12054 --t ≤ 50 t≤2 345 50 t > 50 t>2 345 50 K12554 --t ≥ 6.5 t ≥ 0.25 345 50 K12554 --t ≥ 6.5 t ≥ 0.25 485 70 K12554 --6.5 ≤ t ≤ 65 0.25 ≤ t ≤ 2.5 570 83 --1.6368 t ≤ 40 --460 --40 < t ≤ 60 --440 --60 < t ≤ 100 --430 --100 < t ≤ 150 --420 --150 < t ≤ 200 --410 ------t ≤ 100 --390 --100 < t ≤ 120 --380 ------6 ≤ t ≤ 50 --345 --50 < t ≤ 150 --345 ----------345 ----------480 ---
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
159
4.7 Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates 4.7A Chemical Composition of Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates
ASTM A240/A240M-15a
---
EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4312:2011 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014
X2CrNi12 X2CrNi12 Grade X2CrNi12 Symbol SUH409L ----X6CrNiTi12 X6CrNiTi12 X5CrNiMoTi15-2 Grade X6CrNiTi12 ----X3CrNiMo13-4 Grade X3CrNiMo13-4
ISO 9328-7:2004 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004
UNS No S40500 S40500 ------------S40977 S41050 S40977 S41050 --------S42035 S42035 --------S41500 S41500 -----
Steel No ----1.4002 ------------------1.4003 1.4003 --------1.4516 1.4516 1.4589 ------1.4313 ---
C 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.030 0.04 0.030 0.04 0.030 0.030 0.030 0.030 0.08 0.08 0.08 0.08 0.08 0.08 0.05 0.05 0.05 0.05
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.50 1.00 1.50 1.00 1.50 1.50 1.50 1.00 1.00 1.00 1.50 1.50 1.00 1.00 0.50-1.00 0.50-1.00 1.50 0.50-1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.70 0.70 1.00 1.00 0.60 0.60 0.70 0.70
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.040 0.030 11.5-14.5 0.60 0.040 0.030 11.5-14.5 0.60 0.040 0.015 12.0-14.0 --0.035 0.030 11.50-14.50 0.60 0.035 0.030 11.50-14.50 0.60 0.035 0.030 11.50-14.50 0.60 0.040 0.030 11.50-14.50 0.60 0.040 0.030 11.50-14.50 0.60 0.040 0.015 10.5-12.5 0.30-1.00 0.045 0.030 10.5-12.5 0.60-1.10 0.040 0.015 10.5-12.5 0.30-1.00 0.045 0.030 10.5-12.5 0.60-1.10 0.040 0.015 10.5-12.5 0.30-1.00 0.040 0.015 10.5-12.5 0.30-1.00 0.040 0.015 10.5-12.5 0.30-1.10 0.040 0.030 10.50-11.75 0.60 0.045 0.030 13.5-15.5 1.0-2.5 0.045 0.030 13.5-15.5 1.0-2.5 0.040 0.015 10.5-12.5 0.50-1.50 0.040 0.015 10.5-12.5 0.50-1.50 0.040 0.015 13.5-15.5 1.00-2.50 0.040 0.015 10.5-12.5 0.50-1.50 0.030 0.030 11.5-14.0 3.5-5.5 0.030 0.030 11.5-14.0 3.5-5.5 0.040 0.015 12.0-14.0 3.5-4.5 0.040 0.015 12.0-14.0 3.5-4.5
Mo --------------------------------0.2-1.2 0.2-1.2 ----0.20-1.20 --0.50-1.00 0.50-1.00 0.30-0.70 0.30-1.00
Others Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 N 0.030 N 0.10 N 0.030 N 0.10 N 0.030 N 0.030 N 0.030 Ti 6xC to 0.75 Ti 0.30-0.50 Ti 0.30-0.50 Ti 0.05-0.35 Ti 0.05-0.35 Ti 0.30-0.50 Ti 0.05-0.35 ----N 0.020 min. ---
Download From http://bbs.infoeach.com
Designation Type 405 Type 405 X6CrAl13 Grade 0Cr13Al Grade 0Cr13Al Grade 0Cr13Al Symbol SUS405 Symbol SUS405 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
160
4.7 Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates 4.7A Chemical Composition of Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates (Continued)
Specification ASME SA-240/SA-240M
UNS No S43035
Steel No ---
C 0.030
Mn 1.00
Si 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.040 0.030 17.0-19.0 0.50
Mo ---
---
S43932
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
---
S43940
---
0.030
1.00
1.00
0.040
0.015
17.5-18.5
---
---
Type 439
S43035
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
---
S43932
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
---
S43940
---
0.030
1.00
1.00
0.040
0.015
17.5-18.5
---
---
EN 10028-7:2007
X2CrTiNb18
---
1.4509
0.030
1.00
1.00
0.040
0.015
17.5-18.5
---
---
EN 10088-2:2014
X2CrTiNb18
---
1.4509
0.030
1.00
1.00
0.040
0.015
17.5-18.5
---
---
ISO 9328-7:2004
Grade X2CrTiNb18
---
---
0.030
1.00
1.00
0.040
0.015
17.5-18.5
---
---
EN 10028-7:2007
X3CrTi17 X2CrTi17 X3CrTi17 X3CrNb17 X2CrTi17
-----------
1.4510 1.4520 1.4510 1.4511 1.4520
0.05 0.025 0.05 0.05 0.025
1.00 0.50 1.00 1.00 0.50
1.00 0.50 1.00 1.00 0.50
0.040 0.040 0.040 0.040 0.040
0.015 0.015 0.015 0.015 0.015
16.0-18.0 16.0-18.0 16.0-18.0 16.0-18.0 16.0-18.0
-----------
-----------
Grade 00Cr17 Grade X2CrTi17 Grade X3CrTi17 Symbol SUS430LX Symbol SUS430LX
-----------
-----------
0.030 0.025 0.05 0.030 0.030
1.00 0.50 1.00 1.00 1.00
0.75 0.50 1.00 0.75 0.75
0.035 0.040 0.040 0.040 0.040
0.030 0.015 0.015 0.030 0.030
16.00-19.00 16.0-18.0 16.0-19.0 16.00-19.00 16.00-19.00
0.60 ----0.60 0.60
-----------
EN 10088-2:2014
GB 3280-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012
Others Al 0.15; N 0.030; Ti [0.20+4(C+N)] to 1.10 Al 0.15; N 0.030; Ti+Cb [0.20+4(C+N)] to 0.75 Ti 0.10-0.60; Cb [0.30+(3xC)] min. Al 0.15; N 0.030; Ti [0.20+4(C+N)] to 1.10 Al 0.15; N 0.030; Ti+Cb [0.20+4(C+N)] to 0.75 Ti 0.10-0.60; Cb [0.30+(3xC)] min. Ti 0.10-0.60; Nb [3xC+0.30] to 1.00 Ti 0.10-0.60; Nb [3xC+0.30] to 1.00 Ti 0.10-0.60; Nb [(3xC)+0.30] to 1.00 Ti [4x(C+N)+0.15] to 0.80 Ti 0.30-0.60; N 0.015 Ti [4x(C+N)+0.15] to 0.80 Nb 12xC to 1.00 N 0.015; Ti [4x(C+N)+0.15] to 0.80 Ti 0.10-1.00; Nb 0.10-1.00 Ti 0.30-0.60; N 0.015 Ti [4x(C+N)+0.15] to 0.75 Ti 0.10-1.00; Nb 0.10-1.00 Ti 0.10-1.00; Nb 0.10-1.00
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Designation Type 439
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
161
4.7 Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates 4.7A Chemical Composition of Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No S44400
Steel No ---
C 0.025
Mn 1.00
Si 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.030 17.5-19.5 1.00 1.75-2.50
ASTM A240/A240M-15a
Type 444
S44400
---
0.025
1.00
1.00
0.040
0.030
17.5-19.5
1.00
1.75-2.50
EN 10028-7:2007
X2CrMoTi18-2
---
1.4521
0.025
1.00
1.00
0.040
0.015
17.0-20.0
---
1.80-2.50
EN 10088-2:2014
X2CrMoTi18-2
---
1.4521
0.025
1.00
1.00
0.040
0.015
17.0-20.0
---
1.80-2.50
GB 3280-92
Grade 00Cr18Mo2
---
---
0.025
1.00
1.00
0.035
0.030
17.00-20.00
0.60
1.75-2.50
GB 4237-92
Grade 00Cr18Mo2
---
---
0.025
1.00
1.00
0.035
0.030
17.00-20.00
0.60
1.75-2.50
ISO 9328-7:2004
Grade X2CrMoTi18-2
---
---
0.025
1.00
1.00
0.040
0.015
17.0-20.0
---
1.80-2.50
JIS G 4304:2012
Symbol SUS444
---
---
0.025
1.00
1.00
0.040
0.030
17.00-20.00
0.60
1.75-2.50
JIS G 4305:2012
Symbol SUS444
---
---
0.025
1.00
1.00
0.040
0.030
17.00-20.00
0.60
1.75-2.50
Others N 0.035; (Ti+Cb) [0.20+4(C+N)] to 0.80 N 0.035; Ti+Cb [0.20+4(C+N)] to 0.80 N 0.030; Ti [4x(C+N)+0.15] to 0.80 N 0.030; Ti [4x(C+N)+0.15] to 0.80 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 N 0.030; Ti [4x(C+N)+0.15] to 0.80 Ti, Nb, Zr or their combination 8x(C + N) to 0.80; N 0.025 Ti, Nb, Zr or their combination 8x(C + N) to 0.80; N 0.025
Download From http://bbs.infoeach.com
Designation Type 444
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
162
4.7 Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates 4.7B Mechanical Properties of Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates UNS No. S40500
Steel No. ---
ASTM A240/A240M-15a
Type 405
S40500
---
---
---
170
25
415
60
20
see standard
EN 10088-2:2014
X6CrAl13
---
1.4002
GB 3280-92
Grade 0Cr13Al
---
---
t≤8 t ≤ 13.5 t ≤ 25 ---
---------
230 210 210 175
---------
400-600 400-600 400-600 410
---------
17 L, 17 T 17 L, 17 T 17 L, 17 T 20
A A A A
GB 4237-92
Grade 0Cr13Al
---
---
---
---
177
---
410
---
20
A
GB 4238-92
Grade 0Cr13Al
---
---
---
---
175
---
410
---
20
A
JIS G 4304:2012
Symbol SUS405
---
---
---
---
175
---
410
---
20
A
JIS G 4305:2012
Symbol SUS405
---
---
---
---
175
---
410
---
20
A
ASME SA-240/SA-240M
---
S40977
---
---
---
280
41
450
65
18
see standard
S41050
---
---
---
205
30
415
60
22
see standard
S40977
---
---
---
280
41
450
65
18
see standard
S41050
---
---
---
205
30
415
60
22
see standard
t≤8 t ≤ 13.5 t ≤ 25 t≤8 t ≤ 13.5 t ≤ 25 t≤6 t ≤ 12 t ≤ 25 ---
---------------------
280 280 250 280 280 250 280 280 250 175
---------------------
450-650 450-650 450-650 450-650 450-650 450-650 450-650 450-650 450-650 360
---------------------
20 L, 20 T 20 L, 20 T 18 L, 18 T 20 L, 20 T 20 L, 20 T 18 L, 18 T 20 L, 20 T 20 L, 20 T 18 L, 18 T 25
A A A A A A A A A A
ASTM A240/A240M-15a
---
EN 10028-7:2007
X2CrNi12
---
1.4003
EN 10088-2:2014
X2CrNi12
---
1.4003
ISO 9328-7:2004
Grade X2CrNi12
---
---
JIS G 4312:2011
Symbol SUH409L
---
---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----170 25 415 60 20
Heat Treatment see standard
Other 179 max. HB; 88 max. HRB 179 max. HB; 88 max. HRBW ------183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV 180 max. HB; 88 max. HRB 183 max. HB; 89 max. HRB 180 max. HB; 88 max. HRBW 183 max. HB; 89 max. HRBW T: 50 J @ RT T: 50 J @ RT T: 50 J @ RT ------T: 50 J @ 20°C T: 50 J @ 20°C T: 50 J @ 20°C 162 max. HBW; 80 max. HRBW; 175 max. HV
Download From http://bbs.infoeach.com
Designation Type 405
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
163
4.7 Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates 4.7B Mechanical Properties of Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates (Continued) Steel No. ---
ASTM A240/A240M-15a
---
S42035
---
---
---
380
55
550
80
16
see standard
EN 10028-7:2007
X6CrNiTi12
---
1.4516
X6CrNiTi12
---
1.4516
X5CrNiMoTi15-2
---
1.4589
ISO 9328-7:2004
Grade X6CrNiTi12
---
---
ASME SA-240/SA-240M
---
S41500
---
t≤8 t ≤ 13.5 t ≤ 25 t≤8 t ≤ 13.5 t ≤ 25 t≤8 t ≤ 13.5 t≤6 t ≤ 12 t ≤ 25 ---
-------------------------
280 280 250 280 280 250 400 360 280 280 250 620
----------------------90
450-650 450-650 450-650 450-650 450-650 450-650 550-750 500-750 450-650 450-650 450-650 795
----------------------115
23 L, 23 T 23 L, 23 T 20 L, 20 T 23 L, 23 T 23 L, 23 T 20 L, 20 T 16 L, 16 T 14 L, 14 T 23 L, 23 T 23 L, 23 T 20 L, 20 T 15
A A A A A A A A A A A see standard
ASTM A240/A240M-15a
---
S41500
---
---
---
620
90
795
115
15
see standard
EN 10028-7:2007
X3CrNiMo13-4
---
1.4313
t ≤ 75
---
650
---
780-980
---
14 L, 14 T
Q+T
ISO 9328-7:2004
Grade X3CrNiMo13-4
---
---
t ≤ 75
---
650
---
780-980
---
14 L, 14 T
Q+T
ASME SA-240/SA-240M
Type 439
S43035
---
---
---
205
30
415
60
22
see standard
---
S43932
---
---
---
205
30
415
60
22
see standard
S43940
---
---
---
250
36
430
62
18
see standard
Type 439
S43035
---
---
---
205
30
415
60
22
see standard
---
S43932
---
---
---
205
30
415
60
22
see standard
S43940
---
---
---
250
36
430
62
18
see standard
-------
1.4509 1.4509 ---
t≤4 t≤8 t ≤ 2.5
-------
230 230 230
-------
430-630 430-630 430-630
-------
18 L, 18 T 18 L, 18 T 18 L, 18 T
A A A
Download From http://bbs.infoeach.com
EN 10088-2:2014
ASTM A240/A240M-15a
EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004
Designation
X2CrTiNb18 X2CrTiNb18 Grade X2CrTiNb18
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----380 55 550 80 16
Heat Treatment see standard
Other 180 max. HB; 88 max. HRB 180 max. HB; 88 max. HRBW T: 50 J @ RT T: 50 J @ RT T: 50 J @ RT ----------T: 50 J @ 20°C T: 50 J @ 20°C T: 50 J @ 20°C 302 max. HB; 32 max, HRC 302 max. HB; 32 max, HRC see standard for impact data see standard for impact data 183 max. HB; 89 max. HRB 183 max. HB; 89 max. HRB 180 max. HB; 88 max. HRB 183 max. HB; 89 max. HRBW 183 max. HB; 89 max. HRBW 180 max. HB; 88 max. HRBW -------
Download From http://bbs.infoeach.com
---
UNS No. S42035
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
164
4.7 Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates 4.7B Mechanical Properties of Ferritic and Martensitic Stainless Steels for Pressure Vessel Plates (Continued)
Specification EN 10028-7:2007
UNS No. -------
Tensile Strength, min. Elongation MPa ksi % min. 420-600 --23 L, 23 T 380-530 --24 L, 24 T 420-600 --23 L, 23 T 420-600 --23 L, 23 T 420-600 --23 L, 23 T 380-530 --24 L, 24 T 365 --22
GB 3280-92
X3CrNb17 X2CrTi17 Grade 00Cr17
-------
JIS G 4304:2012
Grade X2CrTi17 Grade X3CrTi17 Symbol SUS430LX
-------
-------
t ≤ 2.5 t≤3 ---
-------
180 230 175
-------
380-530 420-600 360
-------
24 L, 24 T 23 L, 23 T 22
A A A
JIS G 4305:2012
Symbol SUS430LX
---
---
---
---
175
---
360
---
22
A
ASME SA-240/SA-240M
Type 444
S44400
---
---
---
275
40
415
60
20
see standard
ASTM A240/A240M-15a
Type 444
S44400
---
---
---
275
40
415
60
20
---
EN 10028-7:2007 EN 10088-2:2014
X2CrMoTi18-2 X2CrMoTi18-2
-----
1.4521 1.4521
GB 3280-92
Grade 00Cr18Mo2
---
---
t≤4 t≤8 t ≤ 12 t ≤ 13.5 ---
-----------
300 300 280 280 245
-----------
420-640 420-640 420-620 400-600 410
-----------
20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20
A A A A A
GB 4237-92
Grade 00Cr18Mo2
---
---
---
---
245
---
410
---
20
A
ISO 9328-7:2004 JIS G 4304:2012
Grade X2CrMoTi18-2 Symbol SUS444
-----
-----
t ≤ 2.5 ---
-----
300 245
-----
420-640 410
-----
20 L, 20 T 20
A A
JIS G 4305:2012
Symbol SUS444
---
---
---
---
245
---
410
---
20
A
Download From http://bbs.infoeach.com
EN 10088-2:2014
ISO 9328-7:2004
Heat Treatment A A A A A A A
Other ------------183 max. HB; 88 max. HRB ----183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV 217 max. HB; 96 max. HRB 217 max. HB; 96 max. HRBW --------217 max. HB; 96 max. HRB 217 max. HB; 96 max. HRB --217 max. HBW; 96 max. HRBW; 230 max. HV 217 max. HBW; 96 max. HRBW; 230 max. HV
Download From http://bbs.infoeach.com
Steel Section Thickness / Diameter Yield Strength, min. No. mm in. MPa ksi 1.4510 t≤4 --230 --1.4520 t≤4 --180 --1.4510 t≤8 --230 --t ≤ 13.5 --230 --1.4511 t≤8 --230 --1.4520 t≤8 --180 --------175 ---
Designation X3CrTi17 X2CrTi17 X3CrTi17
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
165
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8A Chemical Composition of Austenitic Stainless Steels for Pressure Vessel Plates
EN 10088-2:2014 GB 3280-92 GB 4237-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012
Designation Type 301LN Type 301LN Type 301LN Type 301LN X2CrNiN18-7 X2CrNiN18-7 Grade X2CrNiN18-7 Type 304 Type 304 Type 304 Type 304 X5CrNi18-10 X5CrNi18-10 Grade 0Cr18Ni9 Grade 0Cr18Ni9 Grade 0Cr18Ni9 Grade X5CrNi18-9 Symbol SUS304 Symbol SUS304 Type 304H Type 304H X6CrNi18-10 Grade X6CrNi18-10 Type 304L Type 304L Type 304L Type 304L X2CrNi19-11 X2CrNi18-9 X2CrNi19-11 X2CrNi18-9 Grade 00Cr19Ni10 Grade 00Cr19Ni13Mo3 Grade 00Cr19Ni10 Grade X2CrNi18-9 Grade X2CrNi19-11 Symbol SUS304L Symbol SUS304L
UNS No S30153 S30153 S30153 S30153 ------S30400 S30400 S30400 S30400 ----------------S30409 S30409 ----S30403 S30403 S30403 S30403 -----------------------
Steel No --------1.4318 1.4318 ----------1.4301 1.4301 ----------------1.4948 ----------1.4306 1.4307 1.4306 1.4307 ---------------
C 0.03 0.03 0.03 0.03 0.030 0.030 0.030 0.07 0.08 0.07 0.08 0.07 0.07 0.07 0.07 0.07 0.07 0.08 0.08 0.04-0.10 0.04-0.10 0.04-0.08 0.04-0.08 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.00 2.00 2.00 2.00 2.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 1.00 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.045 0.030 16.0-18.0 6.0-8.0 0.045 0.030 16.0-18.0 6.0-8.0 0.045 0.030 16.0-18.0 6.0-8.0 0.045 0.030 16.0-18.0 6.0-8.0 0.045 0.015 16.5-18.5 6.0-8.0 0.045 0.015 16.5-18.5 6.0-8.0 0.045 0.015 16.5-18.5 6.0-8.0 0.045 0.030 17.5-19.5 8.0-10.5 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.030 17.5-19.5 8.0-10.5 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.015 17.5-19.5 8.0-10.5 0.045 0.015 17.5-19.5 8.0-10.5 0.035 0.030 17.00-19.00 8.00-11.00 0.035 0.030 17.00-19.00 8.00-11.00 0.035 0.030 17.00-19.00 8.00-11.00 0.045 0.015 17.5-19.5 8.0-10.5 0.045 0.030 18.00-20.00 8.00-10.50 0.045 0.030 18.00-20.00 8.00-10.50 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.030 18.0-20.0 8.0-10.5 0.035 0.015 17.0-19.0 8.0-11.0 0.035 0.015 17.0-19.0 8.0-11.0 0.045 0.030 17.5-19.5 8.0-12.0 0.045 0.030 18.0-20.0 8.0-12.0 0.045 0.030 17.5-19.5 8.0-12.0 0.045 0.030 18.0-20.0 8.0-12.0 0.045 0.015 18.0-20.0 10.0-12.0 0.045 0.015 17.5-19.5 8.0-10.5 0.045 0.015 18.0-20.0 10.0-12.0 0.045 0.015 17.5-19.5 8.0-10.5 0.035 0.030 18.00-20.00 8.00-12.00 0.035 0.030 18.00-20.00 11.00-15.00 0.035 0.030 18.00-20.00 8.00-12.00 0.045 0.015 17.5-19.5 8.0-10.0 0.045 0.015 18.0-20.0 10.0-12.0 0.045 0.030 18.00-20.00 9.00-13.00 0.045 0.030 18.00-20.00 9.00-13.00
Mo -----------------------------------------------------------------------------
Others N 0.07-0.20 N 0.07-0.20 N 0.07-0.20 N 0.07-0.20 N 0.10-0.20 N 0.10-0.20 N 0.10-0.20 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 ------N 0.11 --------N 0.10 N 0.11 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 ------N 0.11 N 0.11 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
166
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8A Chemical Composition of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
Designation Type 304N Type 304N Type 304N Type 304N X5CrNiN19-9 X5CrNiN19-9 Grade 0Cr19Ni9N Grade 0Cr19Ni9N Grade X5CrNiN18-8 Symbol SUS304N1 Symbol SUS304N1 Type 304LN Type 304LN Type 304LN Type 304LN X2CrNiN18-10 X2CrNiN18-10 Grade 00Cr18Ni10N Grade 00Cr18Ni10N Grade X2CrNiN18-10 Symbol SUS304LN Symbol SUS304LN Type 309H Type 309H X6CrNi23-13 Grade X6CrNi23-13 Type 310H Type 310H X6CrNi25-20 Grade X6CrNi25-20
UNS No S30451 S30451 S30451 S30451 --------------S30453 S30453 S30453 S30453 --------------S30909 S30909 ----S31009 S31009 -----
Steel No --------1.4315 1.4315 ------------------1.4311 1.4311 --------------1.4950 ------1.4951 ---
C 0.08 0.08 0.08 0.08 0.06 0.06 0.08 0.08 0.07 0.08 0.08 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.04-0.10 0.04-0.10 0.04-0.08 0.04-0.08 0.04-0.10 0.04-0.10 0.04-0.08 0.04-0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.50 2.50 2.50 2.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.70 0.70 0.75 0.75 0.70 0.70
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.030 18.0-20.0 8.0-10.5 0.045 0.015 18.0-20.0 8.0-11.0 0.045 0.015 18.0-20.0 8.0-11.0 0.035 0.030 18.00-20.00 7.00-10.50 0.035 0.030 18.00-20.00 7.00-10.50 0.045 0.015 18.0-20.0 8.0-11.0 0.045 0.030 18.00-20.00 7.00-10.50 0.045 0.030 18.00-20.00 7.00-10.50 0.045 0.030 18.0-20.0 8.0-12.0 0.045 0.030 18.0-20.0 8.0-12.0 0.045 0.030 18.0-20.0 8.0-12.0 0.045 0.030 18.0-20.0 8.0-12.0 0.045 0.015 17.5-19.5 8.5-11.5 0.045 0.015 17.5-19.5 8.5-11.5 0.035 0.030 17.00-19.00 8.50-11.50 0.035 0.030 17.00-19.00 8.50-11.50 0.045 0.015 17.5-19.5 8.0-11.5 0.045 0.030 17.00-19.00 8.50-11.50 0.045 0.030 17.00-19.00 8.50-11.50 0.045 0.030 22.0-24.0 12.0-15.0 0.045 0.030 22.0-24.0 12.0-15.0 0.035 0.015 22.0-24.0 12.0-15.0 0.035 0.015 22.0-24.0 12.0-15.0 0.045 0.030 24.0-26.0 19.0-22.0 0.045 0.030 24.0-26.0 19.0-22.0 0.035 0.015 24.0-26.0 19.0-22.0 0.035 0.015 24.0-26.0 19.0-22.0
Mo -------------------------------------------------------------
Others N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.12-0.22 N 0.12-0.22 N 0.10-0.25 N 0.10-0.25 N 0.10-0.16 N 0.10-0.25 N 0.10-0.25 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 ----N 0.10 N 0.11 ----N 0.10 N 0.11
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
167
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8A Chemical Composition of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007
GB 3280-92 GB 4237-92 GB 4238-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007
EN 10088-2:2014
GB 3280-92 GB 4237-92 ISO 9328-7:2004
JIS G 4304:2012 JIS G 4305:2012
UNS No S31600 S31600 S31600 S31600 ----------------------S31603 S31603 S31603 S31603 ---------------------------
Steel No --------1.4401 1.4436 1.4401 1.4436 ----------------------1.4404 1.4432 1.4435 1.4404 1.4432 1.4435 ---------------
C 0.08 0.08 0.08 0.08 0.07 0.05 0.07 0.05 0.08 0.08 0.08 0.05 0.07 0.08 0.08 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.015 16.5-18.5 10.0-13.0 0.045 0.015 16.5-18.5 10.5-13.0 0.045 0.015 16.5-18.5 10.0-13.0 0.045 0.015 16.5-18.5 10.5-13.0 0.035 0.030 16.00-18.00 10.00-14.00 0.035 0.030 16.00-18.00 10.00-14.00 0.035 0.030 16.00-18.00 10.00-14.00 0.045 0.015 16.5-18.5 10.5-13.0 0.045 0.015 16.5-18.5 10.0-13.0 0.045 0.030 16.00-18.00 10.00-14.00 0.045 0.030 16.00-18.00 10.00-14.00 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.015 16.5-18.5 10.0-13.0 0.045 0.015 16.5-18.5 10.5-13.0 0.045 0.015 17.0-19.0 12.5-15.0 0.045 0.015 16.5-18.5 10.0-13.0 0.045 0.015 16.5-18.5 10.5-13.0 0.045 0.015 17.0-19.0 12.5-15.0 0.035 0.030 16.00-18.00 12.00-15.00 0.035 0.030 16.00-18.00 12.00-15.00 0.045 0.015 16.5-18.5 10.0-13.0 0.045 0.015 16.5-18.5 10.5-13.0 0.045 0.015 17.0-19.0 12.5-15.0 0.045 0.030 16.00-18.00 12.00-15.00 0.045 0.030 16.00-18.00 12.00-15.00
Mo 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-2.50 2.50-3.00 2.00-2.50 2.50-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.50-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-2.50 2.50-3.00 2.50-3.00 2.00-2.50 2.50-3.00 2.50-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.50-3.00 2.50-3.00 2.00-3.00 2.00-3.00
Others N 0.10 --N 0.10 --N 0.10 N 0.10 N 0.10 N 0.10 ------N 0.11 N 0.11 ----N 0.10 --N 0.10 --N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 ----N 0.11 N 0.11 N 0.11 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10088-2:2014
Designation Type 316 Type 316 Type 316 Type 316 X5CrNiMo17-12-2 X3CrNiMo17-13-3 X5CrNiMo17-12-2 X3CrNiMo17-13-3 Grade 0Cr17Ni12Mo2 Grade 0Cr17Ni12Mo2 Grade 0Cr17Ni12Mo2 Grade X3CrNiMo17-12-3 Grade X5CrNiMo17-12-2 Symbol SUS316 Symbol SUS316 Type 316L Type 316L Type 316L Type 316L X2CrNiMo17-12-2 X2CrNiMo17-12-3 X2CrNiMo18-14-3 X2CrNiMo17-12-2 X2CrNiMo17-12-3 X2CrNiMo18-14-3 Grade 00Cr17Ni14Mo2 Grade 00Cr17Ni14Mo2 Grade X2CrNiMo17-12-2 Grade X2CrNiMo17-12-3 Grade X2CrNiMo18-14-3 Symbol SUS316L Symbol SUS316L
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
168
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8A Chemical Composition of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
EN 10088-3:2014 GB 3280-92 GB 4237-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 4237-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012
Designation Type 316Ti Type 316Ti X6CrNiMoTi17-12-2 X6CrNiMoTi17-12-2 Grade 0Cr18Ni12Mo2Ti Grade 0Cr18Ni12Mo2Ti Grade X6CrNiMoTi17-12-2 Symbol SUS316Ti Symbol SUS316Ti Type 316Cb Type 316Cb X6CrNiMoNb17-12-2 X6CrNiMoNb17-12-2 Grade X6CrNiMoNb17-12-2 Type 316LN Type 316LN X2CrNiMoN17-11-2 X2CrNiMoN17-13-3 X2CrNiMoN17-11-2 X2CrNiMoN17-13-3 Grade 00Cr17Ni13Mo2N Grade 00Cr17Ni13Mo2N Grade X2CrNiMoN17-11-2 Grade X2CrNiMoN17-13-3 Symbol SUS316LN Symbol SUS316LN Type 317L Type 317L X2CrNiMo18-15-4 X2CrNiMo18-15-4 Grade 00Cr19Ni13Mo3 Grade X2CrNiMo18-15-4 Symbol SUS317L Symbol SUS317L
UNS No S31635 S31635 --------------S31640 S31640 ------S31653 S31653 --------------------S31703 S31703 -------------
Steel No ----1.4571 1.4571 --------------1.4580 1.4580 ------1.4406 1.4429 1.4406 1.4429 ----------------1.4438 1.4438 ---------
C 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.015 16.5-18.5 10.5-13.5 0.045 0.015 16.5-18.5 10.5-13.5 0.035 0.030 16.00-19.00 11.00-14.00 0.035 0.030 16.00-19.00 11.00-14.00 0.045 0.015 16.5-18.5 10.5-13.5 0.045 0.030 16.00-18.00 10.00-14.00 0.045 0.030 16.00-18.00 10.00-14.00 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.015 16.5-18.5 10.5-13.5 0.045 0.015 16.5-18.5 10.5-13.5 0.045 0.015 16.5-18.5 10.5-13.5 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.030 16.0-18.0 10.0-14.0 0.045 0.015 16.5-18.5 10.0-12.5 0.045 0.015 16.5-18.5 11.0-14.0 0.045 0.030 16.5-18.5 10.0-12.5 0.045 0.015 16.5-18.5 11.0-14.0 0.035 0.030 16.50-18.50 10.50-14.50 0.035 0.030 16.50-18.50 10.50-14.50 0.045 0.015 16.5-18.5 10.0-12.5 0.045 0.015 16.5-18.5 11.0-13.0 0.045 0.030 16.50-18.50 10.50-14.50 0.045 0.030 16.50-18.50 10.50-14.50 0.045 0.030 18.0-20.0 11.0-15.0 0.045 0.030 18.0-20.0 11.0-15.0 0.045 0.015 17.5-19.5 13.0-16.0 0.045 0.015 17.5-19.5 13.0-16.0 0.035 0.030 18.00-20.00 11.00-15.00 0.045 0.015 17.5-19.5 13.0-16.0 0.045 0.030 18.00-20.00 11.00-15.00 0.045 0.030 18.00-20.00 11.00-15.00
Mo 2.00-3.00 2.00-3.00 2.00-2.50 2.00-2.50 1.80-2.50 1.80-2.50 2.00-2.50 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-2.50 2.00-2.50 2.00-2.50 2.00-3.00 2.00-3.00 2.00-2.50 2.50-3.00 2.00-2.50 2.50-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.50-3.00 2.00-3.00 2.00-3.00 3.0-4.0 3.0-4.0 3.0-4.0 3.0-4.0 3.00-4.00 3.00-4.0 3.00-4.00 3.00-4.00
Others N 0.10; Ti 5x(C+N) to 0.70 N 0.10; Ti 5x(C+N) to 0.70 Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC to 0.07 Ti 5xC to 0.70 Ti 5xC min Ti 5xC min N 0.10; Cb 10xC to 1.10 N 0.10; Cb 10xC to 1.10 Nb 10xC to 1.00 Nb 10xC to 1.00 Nb 10xC to 1.00 N 0.10-0.16 N 0.10-0.16 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.10 N 0.10 N 0.10 N 0.10 --N 0.11 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-479/SA-479M ASTM A479/A479M-14 EN 10028-7:2007
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
169
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8A Chemical Composition of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
Designation Type 317LN Type 317LN X2CrNiMoN18-12-4 X2CrNiMoN18-12-4 Grade X2CrNiMoN18-12-4 Symbol SUS317LN Symbol SUS317LN Type 317LMN Type 317LMN X2CrNiMoN17-13-5 X2CrNiMoN17-13-5 Grade X2CrNiMoN17-13-5 Type 321 Type 321 X6CrNiTi18-10 X6CrNiTi18-10 Grade 0Cr18Ni10Ti Grade 0Cr18Ni10Ti Grade 0Cr18Ni10Ti Grade X6CrNiTi18-10 Symbol SUS321 Symbol SUS321 Type 347 Type 347 X6CrNiNb18-10 X6CrNiNb18-10 Grade 0Cr18Ni11Nb Grade 0Cr18Ni11Nb Grade 0Cr18Ni11Nb Grade X6CrNiNb18-10 Symbol SUS347 Symbol SUS347
UNS No S31753 S31753 ----------S31726 S31726 ------S32100 S32100 ----------------S34700 S34700 -----------------
Steel No ----1.4434 1.4434 ----------1.4439 1.4439 ------1.4541 1.4541 ----------------1.4550 1.4550 -------------
C 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 1.00 1.00 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.045 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.045 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.045 0.015 16.5-19.5 10.5-14.0 3.0-4.0 0.045 0.015 16.5-19.5 10.5-14.0 3.0-4.0 0.045 0.015 16.5-19.5 10.5-14.0 3.00-4.0 0.045 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.045 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.045 0.030 17.0-20.0 13.5-17.5 4.0-5.0 0.045 0.030 17.0-20.0 13.5-17.5 4.0-5.0 0.045 0.015 16.5-18.5 12.5-14.5 4.0-5.0 0.045 0.015 16.5-18.5 12.5-14.5 4.0-5.0 0.045 0.015 16.5-18.5 12.5-14.5 4.0-5.0 0.045 0.030 17.0-19.0 9.0-12.0 --0.045 0.030 17.0-19.0 9.0-12.0 --0.045 0.015 17.0-19.0 9.0-12.0 --0.045 0.015 17.0-19.0 9.0-12.0 --0.035 0.030 17.00-19.00 9.00-12.00 --0.035 0.030 17.00-19.00 9.00-12.00 --0.035 0.030 17.00-19.00 9.00-12.00 --0.045 0.015 17.0-19.0 9.0-12.0 --0.045 0.030 17.00-19.00 9.00-13.00 --0.045 0.030 17.00-19.00 9.00-13.00 --0.045 0.030 17.0-19.0 9.0-13.0 --0.045 0.030 17.0-19.0 9.0-13.0 --0.045 0.015 17.0-19.0 9.0-12.0 --0.045 0.015 17.0-19.0 9.0-12.0 --0.035 0.030 17.00-19.00 9.00-13.00 --0.035 0.030 17.00-19.00 9.00-13.00 --0.035 0.030 17.00-19.00 9.00-13.00 --0.045 0.015 17.0-19.0 9.0-12.0 --0.045 0.030 17.00-19.00 9.00-13.00 --0.045 0.030 17.00-19.00 9.00-13.00 ---
Others N 0.10-0.22 N 0.10-0.22 N 0.10-0.20 N 0.10-0.20 N 0.10-0.20 N 0.10-0.22 N 0.10-0.22 N 0.10-0.20 N 0.10-0.20 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.10; Ti 5x(C+N) to 0.70 N 0.10; Ti 5x(C+N) to 0.70 Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC min. Ti 5xC min. Ti 5xC min. Ti 5xC to 0.70 Ti 5xC min. Ti 5xC min. Cb 10xC to 1.00 Cb 10xC to 1.00 Nb 10xC to 1.00 Nb 10xC to 1.00 Nb 10xC min. Nb 10xC min. Nb 10xC min. Nb 10xC to 1.00 Nb 10xC min. Nb 10xC min.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
170
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8A Chemical Composition of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
ASTM A240/A240M-15a
Type 800H
EN 10028-7:2007
X8NiCrAlTi32-21
---
1.4959
0.05-0.10
1.50
0.70
0.015
0.010
19.0-22.0
30.0-34.0
---
ISO 9328-7:2004
Grade X8NiCrAlTi32-21
---
---
0.05-0.10
1.50
0.70
0.015
0.010
19.0-22.0
30.0-34.0
---
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Steel No ----1.4539 1.4539 ------------------1.4529 1.4529 ---------
C 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.030 0.020 0.020 0.030 0.020 0.020 0.020 0.020 0.020 0.030 0.030 0.05-0.10
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 3.00 2.00 2.00 3.00 1.00 1.00 2.00 2.00 2.00 1.50
Si 1.00 1.00 0.70 0.70 0.70 1.00 1.00 1.00 0.50 0.50 1.00 0.50 0.50 0.50 0.50 0.75 1.00 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.045 0.035 19.0-23.0 23.0-28.0 0.045 0.035 19.0-23.0 23.0-28.0 0.030 0.010 19.0-21.0 24.0-26.0 0.030 0.010 19.0-21.0 24.0-26.0 0.030 0.010 19.0-21.0 24.0-26.0 0.045 0.030 19.00-23.00 23.00-28.00 0.045 0.030 19.00-23.00 23.00-28.00 0.040 0.030 20.0-22.0 23.5-25.5 0.030 0.010 19.0-21.0 24.0-26.0 0.030 0.010 20.5-23.0 26.0-28.0 0.040 0.030 20.0-22.0 23.5-25.5 0.030 0.010 19.0-21.0 24.0-26.0 0.030 0.010 20.5-23.0 26.0-28.0 0.030 0.010 19.0-21.0 24.0-26.0 0.030 0.010 19.0-21.0 24.0-26.0 0.030 0.010 19.0-21.0 24.0-26.0 0.045 0.030 19.00-24.00 24.00-26.00 0.045 0.030 19.00-24.00 24.00-26.00 0.045 0.015 19.0-23.0 30.0-35.0
N08810
---
0.05-0.10
1.50
1.00
0.045
0.015
19.0-23.0
30.0-35.0
---
Designation Type 904L Type 904L X1NiCrMoCu25-20-5 X1NiCrMoCu25-20-5 Grade X1NiCrMoCu25-20-5 Symbol SUS890L Symbol SUS890L ---
Mo 4.00-5.00 4.00-5.00 4.0-5.0 4.0-5.0 4.0-5.0 4.00-5.00 4.00-5.00 6.0-7.0 6.00-7.00 6.5-8.0 6.0-7.0 6.00-7.00 6.5-8.0 6.0-7.0 6.0-7.0 6.0-7.0 5.00-7.00 5.00-7.00 ---
Others Cu 1.00-2.00; N 0.10 Cu 1.00-2.00; N 0.10 Cu 1.20-2.00; N 0.15 Cu 1.20-2.00; N 0.15 Cu 1.20-2.00; N 0.15 Cu 1.00-2.00 Cu 1.00-2.00 Cu 0.75; N 0.18-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.30-0.40 Cu 0.75; N 0.18-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.30-0.40 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.15-0.25 N 0.25 N 0.25 Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min. Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min. Al 0.25-0.65; Cu 0.50; Ti 0.25-0.65; Co 0.50; N 0.030; (Ni+Co) 30.0 to 34.0 Al 0.25-0.65; Cu 0.50; Ti 0.25-0.65; Co 1.00; N 0.11; (Ni+Co) 30.0 to 34.0
Download From http://bbs.infoeach.com
EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M
UNS No N08904 N08904 ----------N08367 N08926 S31277 --N08367 N08926 S31277 X1NiCrMoCuN25-20-7 --X1NiCrMoCuN25-20-7 --Grade X1NiCrMoCuN25-20-7 --Symbol SUS836L --Symbol SUS836L --Type 800H N08810
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
171
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates UNS No. S30153
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----240 35 550 80 45
ASME SA-666
Type 301LN
S30153
---
---
---
240
35
550 L
80 L
45 L
A
ASTM A240/A240M-15a
Type 301LN
S30153
---
---
---
240
35
550
80
45
SA
ASTM A666-15
Type 301LN
S30153
---
---
---
240
35
550 L
80 L
45 L
A
EN 10028-7:2007
X2CrNiN18-7
---
1.4318
EN 10088-2:2014
X2CrNiN18-7
---
1.4318
ISO 9328-7:2004
Grade X2CrNiN18-7
---
---
ASME SA-240/SA-240M
Type 304
S30400
---
t≤3 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-----------------------
350 350 330 330 350 330 330 350 330 330 205
--------------------30
650-850 650-850 650-850 650-850 650-850 650-850 630-830 650-850 650-850 650-850 515
--------------------75
35 T 40 T 40 T 40 T 40 T 40 T 45 T 40 T 40 T 40 T 40
SA SA SA SA SA SA SA SA SA SA Q+SA
ASME SA-666
Type 304
S30400
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 304
S30400
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 304
S30400
---
---
---
205
30
515 L
75 L
40 L
A
EN 10028-7:2007
X5CrNi18-10
---
1.4301
EN 10088-2:2014
X5CrNi18-10
---
1.4301
GB 3280-92
Grade 0Cr18Ni9
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
230 210 210 230 210 210 205
---------------
540-750 520-720 520-720 540-750 520-720 520-720 520
---------------
45 T 45 T 45 T 45 T 45 T 45 T 40
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni9
---
---
---
---
205
---
520
---
40
ST
Heat Treatment Q+SA
Other 241 max. HB; 100 max. HRB 241 max. HB; 100 max. HRB 241 max. HBW; 100 max. HRBW 241 max. HB; 100 max. HRB see standard for impact data
see standard for impact data --see standard for impact data 201 max. HB; 92 max. HRB 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW 201 max. HB; 92 max. HRB see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 301LN
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
172
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
Designation Grade 0Cr18Ni9
UNS No. ---
Steel No. ---
ISO 9328-7:2004
Grade X5CrNi18-9
---
---
JIS G 4304:2012
Symbol SUS304
---
JIS G 4305:2012
Symbol SUS304
ASME SA-240/SA-240M
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 --520 --40
Heat Treatment ST
---------
230 210 210 205
---------
540-750 520-720 520-720 520
---------
45 T 45 T 45 T 40
SA SA SA ST
---
---
---
---
205
---
520
---
40
ST
Type 304H
S30409
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 304H
S30409
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNi18-10
---
1.4948
ISO 9328-7:2004
Grade X6CrNi18-10
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
-------------
230 210 190 230 210 190
-------------
530-740 510-710 510-710 530-740 510-710 510-710
-------------
45 T 45 T 45 T 45 T 45 T 45 T
SA SA SA SA SA SA
Download From http://bbs.infoeach.com
---
t≤6 t ≤ 12 t ≤ 75 ---
Other 187 max. HB; 90 max. HRB --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW see standard for impact data --see standard for impact data
Download From http://bbs.infoeach.com
Specification GB 4238-92
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
173
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S30403
Steel No. ---
ASME SA-666
Type 304L
S30403
---
---
---
170
25
485 L
70 L
40 L
A
ASTM A240/A240M-15a
Type 304L
S30403
---
---
---
170
25
485
70
40
SA
ASTM A666-15
Type 304L
S30403
---
---
---
170
25
485 L
70 L
40 L
A
EN 10028-7:2007
X2CrNi19-11
---
1.4306
X2CrNi18-9
---
1.4307
X2CrNi19-11
---
1.4306
X2CrNi18-9
---
1.4307
Grade 00Cr19Ni10
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------------------
220 200 200 220 200 200 220 200 200 220 200 200 177
---------------------------
520-700 520-700 500-700 520-700 520-700 500-700 520-700 520-700 500-700 520-700 520-700 500-700 480
---------------------------
45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 40
SA SA SA SA SA SA SA SA SA SA SA SA ST
Grade 00Cr19Ni13Mo3
---
---
---
---
177
---
480
---
40
ST
GB 4237-92
Grade 00Cr19Ni10
---
---
---
---
177
---
480
---
40
ST
ISO 9328-7:2004
Grade X2CrNi18-9
---
---
Grade X2CrNi19-11
---
---
JIS G 4304:2012
Symbol SUS304L
---
---
t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------
220 200 200 220 200 200 175
---------------
520-670 520-670 500-650 520-670 520-670 500-650 480
---------------
45 T 45 T 45 T 45 T 45 T 45 T 40
SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS304L
---
---
---
---
175
---
480
---
40
ST
EN 10088-2:2014
GB 3280-92
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----170 25 485 70 40
Heat Treatment Q+SA
Other 201 max. HB; 92 max. HRB 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW 201 max. HB; 92 max. HRB see standard for impact data see standard for impact data see standard for impact data see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 min. HB; 90 max. HRB --see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Designation Type 304L
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
174
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S30451
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----240 35 550 80 30
ASME SA-666
Type 304N
S30451
---
---
---
240
35
550 L
80 L
30 L
A
ASTM A240/A240M-15a
Type 304N
S30451
---
---
---
240
35
550
80
30
SA
ASTM A666-15
Type 304N
S30451
---
---
---
240
35
550 L
80 L
30 L
A
EN 10028-7:2007
X5CrNiN19-9
---
1.4315
EN 10088-2:2014
X5CrNiN19-9
---
1.4315
GB 3280-92
Grade 0Cr19Ni9N
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
290 270 270 290 270 270 275
---------------
550-750 550-750 550-750 500-750 500-750 500-750 550
---------------
40 T 40 T 40 T 40 T 40 T 40 T 35
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr19Ni9N
---
---
---
---
275
---
550
---
35
ST
ISO 9328-7:2004
Grade X5CrNiN18-8
---
---
JIS G 4304:2012
Symbol SUS304N1
---
---
t≤6 t ≤ 12 t ≤ 75 ---
---------
290 270 270 275
---------
550-750 550-750 550-750 550
---------
40 T 40 T 40 T 35
SA SA SA ST
JIS G 4305:2012
Symbol SUS304N1
---
---
---
---
275
---
550
---
35
ST
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data see standard for impact data 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB --see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Download From http://bbs.infoeach.com
Designation Type 304N
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
175
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S30453
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 30 515 75 40
ASME SA-666
Type 304LN
S30453
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 304LN
S30453
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 304LN
S30453
---
---
---
205
30
515 L
75 L
40 L
A
EN 10028-7:2007
X2CrNiN18-10
---
1.4311
EN 10088-2:2014
X2CrNiN18-10
---
1.4311
GB 3280-92
Grade 00Cr18Ni10N
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
290 270 270 290 270 270 245
---------------
550-750 550-750 550-750 550-750 550-750 550-750 550
---------------
40 T 40 T 40 T 40 T 40 T 40 T 40
SA SA SA SA SA SA ST
GB 4237-92
Grade 00Cr18Ni10N
---
---
---
---
245
---
550
---
40
ST
ISO 9328-7:2004
Grade X2CrNiN18-10
---
---
JIS G 4304:2012
Symbol SUS304LN
---
---
t≤6 t ≤ 12 t ≤ 75 ---
---------
290 270 270 245
---------
550-750 550-750 550-750 550
---------
40 T 40 T 40 T 40
SA SA SA ST
JIS G 4305:2012
Symbol SUS304LN
---
---
---
---
245
---
550
---
40
ST
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data see standard for impact data 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB --see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Download From http://bbs.infoeach.com
Designation Type 304LN
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
176
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S30909
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 30 515 75 40
ASTM A240/A240M-15a
Type 309H
S30909
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNi23-13
---
1.4950
ISO 9328-7:2004
Grade X6CrNi23-13
---
---
ASME SA-240/SA-240M
Type 310H
S31009
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------
220 200 200 220 200 200 205
------------30
530-730 510-710 510-710 530-730 510-710 510-710 515
------------75
35 T 35 T 35 T 35 T 35 T 35 T 40
SA SA SA SA SA SA Q+SA
ASTM A240/A240M-15a
Type 310H
S31009
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNi25-20
---
1.4951
ISO 9328-7:2004
Grade X6CrNi25-20
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
-------------
220 200 200 220 200 200
-------------
530-730 510-710 510-710 530-730 510-710 510-710
-------------
35 T 35 T 35 T 35 T 35 T 35 T
SA SA SA SA SA SA
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data --see standard for impact data 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data --see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 309H
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
177
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S31600
Steel No. ---
ASME SA-666
Type 316
S31600
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 316
S31600
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 316
S31600
---
---
---
205
30
515 L
75 L
40 L
A
EN 10028-7:2007
X5CrNiMo17-12-2
---
1.4401
X3CrNiMo17-13-3
---
1.4436
X5CrNiMo17-12-2
---
1.4401
X3CrNiMo17-13-3
---
1.4436
GB 3280-92
Grade 0Cr17Ni12Mo2
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------------------
240 220 220 240 220 220 240 220 220 240 220 220 205
---------------------------
530-680 530-680 520-670 550-700 550-700 530-730 530-680 530-680 520-670 550-700 550-700 530-730 520
---------------------------
40 T 40 T 45 T 40 T 40 T 40 T 40 T 40 T 45 T 40 T 40 T 40 T 40
SA SA SA SA SA SA SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr17Ni12Mo2
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr17Ni12Mo2
---
---
---
---
205
---
520
---
40
ST
ISO 9328-7:2004
Grade X3CrNiMo17-12-3
---
---
Grade X5CrNiMo17-12-2
---
---
JIS G 4304:2012
Symbol SUS316
---
---
t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------
240 220 220 240 220 220 205
---------------
550-700 550-700 530-730 530-680 530-680 520-670 520
---------------
40 T 40 T 40 T 40 T 40 T 45 T 40
SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS316
---
---
---
---
205
---
520
---
40
ST
EN 10088-2:2014
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 30 515 75 40
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data see standard for impact data see standard for impact data see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB --see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Designation Type 316
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
178
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S31603
Steel No. ---
ASME SA-666
Type 316L
S31603
---
---
---
170
25
485 L
70 L
40 L
A
ASTM A240/A240M-15a
Type 316L
S31603
---
---
---
170
25
485
70
40
SA
ASTM A666-15
Type 316L
S31603
---
---
---
170
25
485 L
70 L
40 L
A
EN 10028-7:2007
X2CrNiMo17-12-2
---
1.4404
X2CrNiMo17-12-3
---
1.4432
X2CrNiMo18-14-3
---
1.4435
X2CrNiMo17-12-2
---
1.4404
X2CrNiMo17-12-3
---
1.4432
X2CrNiMo18-14-3
---
1.4435
GB 3280-92
Grade 00Cr17Ni14Mo2
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------------------------------
240 220 220 240 220 220 240 220 220 240 220 220 240 220 220 240 220 220 177
---------------------------------------
530-680 530-680 520-670 550-700 550-700 520-670 550-700 550-700 520-670 530-680 530-680 520-670 550-700 550-700 520-670 550-700 550-700 520-670 480
---------------------------------------
40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40
SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA ST
GB 4237-92
Grade 00Cr17Ni14Mo2
---
---
---
---
177
---
480
---
40
ST
EN 10088-2:2014
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----170 25 485 70 40
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data see standard for impact data see standard for impact data see standard for impact data see standard for impact data see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB
Download From http://bbs.infoeach.com
Designation Type 316L
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
179
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. ---
Steel No. ---
Grade X2CrNiMo17-12-3
---
---
Grade X2CrNiMo18-14-3
---
---
JIS G 4304:2012
Symbol SUS316L
---
---
JIS G 4305:2012
Symbol SUS316L
---
---
---
---
175
---
480
---
40
ST
ASME SA-240/SA-240M
Type 316Ti
S31635
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 316Ti
S31635
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNiMoTi17-12-2
---
1.4571
EN 10088-2:2014
X6CrNiMoTi17-12-2
---
1.4571
GB 3280-92
Grade 0Cr18Ni12Mo2Ti
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
240 220 220 240 220 220 205
---------------
540-690 540-690 520-670 540-690 540-690 520-670 530
---------------
40 T 40 T 40 T 40 T 40 T 40 T 35
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni12Mo2Ti
---
---
---
---
205
---
530
---
37
ST
ISO 9328-7:2004
Grade X6CrNiMoTi17-122
---
---
JIS G 4304:2012
Symbol SUS316Ti
---
---
t≤6 t ≤ 12 t ≤ 75 ---
---------
240 220 220 205
---------
540-690 540-690 520-670 520
---------
40 T 40 T 40 T 40
SA SA SA ST
JIS G 4305:2012
Symbol SUS316Ti
---
---
---
---
205
---
520
---
40
ST
Download From http://bbs.infoeach.com
Section Thickness / Diameter Yield Strength, min. mm in. MPa ksi t≤6 --240 --t ≤ 12 --220 --t ≤ 75 --220 --t≤6 --240 --t ≤ 12 --220 --t ≤ 75 --220 --t≤6 --240 --t ≤ 12 --220 --t ≤ 75 --220 ------175 ---
Tensile Strength, min. Elongation MPa ksi % min. 530-680 --40 T 530-680 --40 T 520-670 --45 T 550-700 --40 T 550-700 --40 T 520-670 --45 T 550-700 --40 T 550-700 --40 T 520-670 --45 T 480 --40
Heat Treatment SA SA SA SA SA SA SA SA SA ST
Other --see standard for impact data --see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Designation Grade X2CrNiMo17-12-2
Specification ISO 9328-7:2004
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
180
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S31640
Steel No. ---
ASTM A240/A240M-15a
Type 316Cb
S31640
---
---
---
205
30
515
75
30
SA
EN 10028-7:2007
X6CrNiMoNb17-12-2
---
1.4580
t ≤ 75
---
220
---
520-720
---
40 T
SA
EN 10088-2:2014
X6CrNiMoNb17-12-2
---
1.4580
t ≤ 75
---
220
---
520-720
---
40 T
SA
ISO 9328-7:2004
Grade X6CrNiMoNb1712-2 Type 316LN Type 316LN X2CrNiMoN17-11-2
---
---
t ≤ 75
---
220
---
520-720
---
40 T
SA
-----------------------
205 205 300 280 280 300 280 280 280 280 245
30 30 -------------------
515 515 580-780 580-780 580-780 580-780 580-780 580-780 580-800 580-800 550
75 75 -------------------
30 30 40 T 40 T 40 T 35 T 35 T 40 T 40 L 30 T 40
A SA SA SA SA SA SA SA SA SA ST
ASME SA-479/SA-479M ASTM A479/A479M-14 EN 10028-7:2007
S31653 --S31653 ----1.4406
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 30 515 75 30
Heat Treatment Q+SA
X2CrNiMoN17-13-3
---
1.4429
EN 10088-3:2014
X2CrNiMoN17-11-2
---
1.4406
GB 3280-92
Grade 00Cr17Ni13Mo2N
---
---
----t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t ≤ 160 160 < t ≤ 250 ---
GB 4237-92
Grade 00Cr17Ni13Mo2N
---
---
---
---
245
---
550
---
40
ST
ISO 9328-7:2004
Grade X2CrNiMoN17-112
---
---
Grade X2CrNiMoN17-133
---
---
JIS G 4304:2012
Symbol SUS316LN
---
---
t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------
300 280 280 300 280 280 245
---------------
580-780 580-780 580-780 580-780 580-780 580-780 550
---------------
40 T 40 T 40 T 35 T 35 T 40 T 40
SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS316LN
---
---
---
---
245
---
550
---
40
ST
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data see standard for impact data see standard for impact data ----see standard for impact data see standard for impact data 250 max. HBW 250 max. HBW 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB --see standard for impact data --see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Download From http://bbs.infoeach.com
Designation Type 316Cb
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
181
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S31703
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 30 515 75 40
ASTM A240/A240M-15a
Type 317L
S31703
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X2CrNiMo18-15-4
---
1.4438
EN 10088-2:2014
X2CrNiMo18-15-4
---
1.4438
GB 4237-92
Grade 00Cr19Ni13Mo3
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
240 220 220 240 220 220 177
---------------
550-700 550-700 520-720 550-700 550-700 520-720 480
---------------
35 T 35 T 40 T 35 T 35 T 40 T 35
SA SA SA SA SA SA ST
ISO 9328-7:2004
Grade X2CrNiMo18-15-4
---
---
JIS G 4304:2012
Symbol SUS317L
---
---
t≤6 t ≤ 12 t ≤ 75 ---
---------
240 220 220 175
---------
550-700 550-700 520-720 480
---------
35 T 35 T 40 T 40
SA SA SA ST
JIS G 4305:2012
Symbol SUS317L
---
---
---
---
175
---
480
---
40
ST
ASME SA-240/SA-240M
Type 317LN
S31753
---
---
---
240
35
550
80
40
Q+SA
ASTM A240/A240M-15a
Type 317LN
S31753
---
---
---
240
35
550
80
40
SA
EN 10028-7:2007
X2CrNiMoN18-12-4
---
1.4434
EN 10088-2:2014
X2CrNiMoN18-12-4
---
1.4434
ISO 9328-7:2004
Grade X2CrNiMoN18-124
---
---
JIS G 4304:2012
Symbol SUS317LN
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------------
290 270 270 290 270 270 290 270 270 245
---------------------
570-770 570-770 540-740 570-770 570-770 540-740 570-770 570-770 540-740 550
---------------------
35 T 35 T 40 T 35 T 35 T 40 T 35 T 35 T 40 T 40
SA SA SA SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS317LN
---
---
---
---
245
---
550
---
40
ST
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data see standard for impact data 187 max. HB; 90 max. HRB --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 317L
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
see standard for impact data --see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
182
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S31726
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----240 35 550 80 40
ASTM A240/A240M-15a
Type 317LMN
S31726
---
---
---
240
35
550
80
40
SA
EN 10028-7:2007
X2CrNiMoN17-13-5
---
1.4439
EN 10088-2:2014
X2CrNiMoN17-13-5
---
1.4439
ISO 9328-7:2004
Grade X2CrNiMoN17-135
---
---
ASME SA-240/SA-240M
Type 321
S32100
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------------
290 270 270 290 270 270 290 270 270 205
------------------30
580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 515
------------------75
35 T 35 T 40 T 35 T 35 T 40 T 35 T 35 T 40 T 40
SA SA SA SA SA SA SA SA SA Q+SA
ASTM A240/A240M-15a
Type 321
S32100
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNiTi18-10
---
1.4541
EN 10088-2:2014
X6CrNiTi18-10
---
1.4541
GB 3280-92
Grade 0Cr18Ni10Ti
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
220 200 200 220 200 200 205
---------------
520-720 520-720 500-700 520-720 520-720 500-700 520
---------------
40 T 40 T 40 T 40 T 40 T 40 T 40
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni10Ti
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr18Ni10Ti
---
---
---
---
205 max.
---
520
---
40
ST
ISO 9328-7:2004
Grade X6CrNiTi18-10
---
---
JIS G 4304:2012
Symbol SUS321
---
---
t≤6 t ≤ 12 t ≤ 75 ---
---------
220 200 200 205
---------
520-720 520-720 500-700 520
---------
40 T 40 T 40 T 40
SA SA SA ST
JIS G 4305:2012
Symbol SUS321
---
---
---
---
205
---
520
---
40
ST
Heat Treatment Q+SA
Other 223 max. HB; 96 max. HRB 223 max. HBW; 96 max. HRBW see standard for impact data see standard for impact data --see standard for impact data 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Designation Type 317LMN
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
183
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued) UNS No. S34700
Steel No. ---
ASTM A240/A240M-15a
Type 347
S34700
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNiNb18-10
---
1.4550
EN 10088-2:2014
X6CrNiNb18-10
---
1.4550
GB 3280-92
Grade 0Cr18Ni11Nb
---
---
t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
-------------
200 200 220 200 200 205
-------------
520-720 500-700 520-720 520-720 500-700 520
-------------
40 T 40 T 40 T 40 T 40 T 40
SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni11Nb
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr18Ni11Nb
---
---
---
---
205
---
520
---
40
ST
ISO 9328-7:2004
Grade X6CrNiNb18-10
---
---
t ≤ 75
---
200
---
500-700
---
40 T
SA
JIS G 4304:2012
Symbol SUS347
---
---
---
---
205
---
520
---
40
ST
JIS G 4305:2012
Symbol SUS347
---
---
---
---
205
---
520
---
40
ST
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007
Type 904L Type 904L X1NiCrMoCu25-20-5
EN 10088-2:2014
X1NiCrMoCu25-20-5
---
1.4539
ISO 9328-7:2004
Grade X1NiCrMoCu2520-5
---
---
JIS G 4304:2012
Symbol SUS890L
---
---
----t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-------------------------
220 220 240 220 220 240 220 220 240 220 220 215
31 31 ---------------------
490 490 530-730 530-730 520-720 530-730 530-730 520-720 530-730 530-730 520-720 490
71 71 ---------------------
35 35 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35
Q+SA SA SA SA SA SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS890L
---
---
---
---
215
---
490
---
35
ST
N08904 --N08904 ----1.4539
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----205 30 515 75 40
Heat Treatment Q+SA
Other 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW see standard for impact data see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 90 max. HRB 90 max. HRBW see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 347
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
184
4.8 Austenitic Stainless Steels for Pressure Vessel Plates 4.8B Mechanical Properties of Austenitic Stainless Steels for Pressure Vessel Plates (Continued)
---
N08926 S31277 N08367
EN 10028-7:2007
X1NiCrMoCuN25-20-7
N08926 S31277 ---
EN 10088-2:2014
X1NiCrMoCuN25-20-7
---
1.4529
t ≤ 75
---
300
---
650-850
---
40 T
SA
ISO 9328-7:2004
---
---
t ≤ 75
---
300
---
650-850
---
40 T
SA
JIS G 4304:2012
Grade X1NiCrMoCuN2520-7 Symbol SUS836L
---
---
---
---
275
---
640
---
40
ST
JIS G 4305:2012
Symbol SUS836L
---
---
---
---
275
---
640
---
40
ST
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007
Type 800H Type 800H X8NiCrAlTi32-21
----t ≤ 75
-------
170 170 170
25 25 ---
450 450 500-750
65 65 ---
30 30 30 T
Q+SA SA SA
ISO 9328-7:2004
Grade X8NiCrAlTi32-21
t ≤ 75
---
170
---
500-750
---
30 T
SA
ASTM A240/A240M-15a
Designation
Steel No. ---
Download From http://bbs.infoeach.com
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----310 45 655 95 30 ----310 45 690 100 30 ------295 43 650 94 35 ------360 52 770 112 40 ------310 45 655 95 30 ----310 45 690 100 30 ------295 43 650 94 35 ------360 52 770 112 40 1.4529 t ≤ 75 --300 --650-850 --40 T
N08810 --N08810 ----1.4959 ---
---
Heat Treatment Q+SA Q+SA Q+SA Q+SA SA SA SA SA SA
Other 241 max. HB 100 max. HRB ----241 max. HBW 100 max. HRBW ----see standard for impact data see standard for impact data see standard for impact data 217 max. HBW; 96 max. HRBW; 230 max. HV 217 max. HBW; 96 max. HRBW; 230 max. HV ----see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
---
UNS No. N08367
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
185
4.9 Duplex (Ferritic-Austenitic) Stainless Steels for Pressure Vessel Plates 4.9A Chemical Composition of Duplex (Ferritic-Austenitic) Stainless Steels for Pressure Vessel Plates UNS No S32205 S31803 S32205 ----------S32304 S32304 ------S32520 S32520 ------S32750 S32750 ------S32760
Steel No ------1.4462 1.4462 ----------1.4362 1.4362 ------1.4507 1.4507 ------1.4410 1.4410 -----
C 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.50 2.00 2.00 2.00 1.50 1.50 2.00 2.00 2.00 1.20 1.20 2.00 2.00 2.00 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.80 0.80 0.70 0.70 0.70 0.80 0.80 1.00 1.00 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.030 0.020 22.0-23.0 4.5-6.5 0.030 0.020 21.0-23.0 4.5-6.5 0.030 0.020 22.0-23.0 4.5-6.5 0.035 0.015 21.0-23.0 4.5-6.5 0.035 0.015 21.0-23.0 4.5-6.5 0.035 0.015 21.0-23.0 4.5-6.5 0.040 0.030 21.00-24.00 4.50-6.50 0.040 0.030 21.00-24.00 4.50-6.50 0.040 0.030 21.5-24.5 3.0-5.5 0.040 0.030 21.5-24.5 3.0-5.5 0.035 0.015 22.0-24.0 3.5-5.5 0.035 0.015 22.0-24.5 3.5-5.5 0.035 0.015 22.0-24.0 3.5-5.5 0.035 0.020 24.0-26.0 5.5-8.0 0.035 0.020 24.0-26.0 5.5-8.0 0.035 0.015 24.0-26.0 6.0-8.0 0.035 0.015 24.0-26.0 6.0-8.0 0.035 0.015 24.0-26.0 5.0-7.5 0.035 0.020 24.0-26.0 6.0-8.0 0.035 0.020 24.0-26.0 6.0-8.0 0.035 0.015 24.0-26.0 6.0-8.0 0.035 0.015 24.0-26.0 6.0-8.0 0.035 0.015 24.0-26.0 6.0-8.0 0.030 0.010 24.0-26.0 6.0-8.0
ASTM A240/A240M-15a
---
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
EN 10028-7:2007
X2CrNiMoCuWN25-7-4
---
1.4501
0.030
1.00
1.00
0.035
0.015
24.0-26.0
6.0-8.0
3.0-4.0
EN 10088-2:2014
X2CrNiMoCuWN25-7-4
---
1.4501
0.030
1.00
1.00
0.035
0.015
24.0-26.0
6.0-8.0
3.0-4.0
ISO 9328-7:2004
Grade X2CrNiMoCuWN25-7-4
---
---
0.030
1.00
1.00
0.035
0.015
24.0-26.0
6.0-8.0
3.0-4.0
Download From http://bbs.infoeach.com
Mo 3.0-3.5 2.5-3.5 3.0-3.5 2.50-3.5 2.50-3.5 2.5-3.5 2.50-3.50 2.50-3.50 0.05-0.60 0.05-0.60 0.10-0.60 0.10-0.60 0.10-0.60 3.0-4.0 3.0-4.0 3.0-4.0 3.0-4.0 2.5-4.0 3.0-5.0 3.0-5.0 3.0-4.5 3.0-4.5 3.0-4.5 3.0-4.0
Others N 0.14-0.20 N 0.08-0.20 N 0.14-0.20 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 N 0.08-0.20 N 0.08-0.20 Cu 0.05-0.60; N 0.05-0.20 Cu 0.05-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.50-2.00; N 0.20-0.35 Cu 0.50-2.00; N 0.20-0.35 Cu 1.00-2.50; N 0.20-0.30 Cu 1.00-2.50; N 0.20-0.30 Cu 1.00-2.50; N 0.15-0.30 Cu 0.50; N 0.24-0.32 Cu 0.50; N 0.24-0.32 N 0.24-0.35 N 0.24-0.35 N 0.24-0.35 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] = 40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] = 40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30
Download From http://bbs.infoeach.com
EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M
Designation Type 2205 --Type 2205 X2CrNiMoN22-5-3 X2CrNiMoN22-5-3 Grade X2CrNiMoN22-5-3 Symbol SUS329J3L Symbol SUS329J3L Type 2304 Type 2304 X2CrNiN23-4 X2CrNiN23-4 Grade X2CrNiN23-4 ----X2CrNiMoCuN25-6-3 X2CrNiMoCuN25-6-3 Grade X2CrNiMoCuN25-6-3 Type 2507 Type 2507 X2CrNiMoN25-7-4 X2CrNiMoN25-7-4 Grade X2CrNiMoN25-7-4 ---
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
186
4.9 Duplex Stainless Steels for Pressure Vessel Plates 4.9B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels for Pressure Vessel Plates
Designation Type 2205
UNS No. S32205
Steel No. ---
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----450 65 655 95 25
ASTM A240/A240M-15a
---
S31803
---
---
---
450
65
620
90
25
SA
Type 2205
S32205
---
---
---
450
65
655
95
25
SA
---------------------
485 445 445 500 460 460 465 445 445 450
---------------------
700-950 700-950 640-480 700-950 700-950 640-840 660-950 660-950 640-840 620
---------------------
20 L, 20 T 25 L, 25 T 25 L, 25 T 20 L, 20 T 25 L, 25 T 25 L, 25 T 20 L, 20 T 25 L, 25 T 25 L, 25 T 18
SA SA SA SA SA SA SA SA SA ST
Heat Treatment Q+SA
X2CrNiMoN22-5-3
---
1.4462
EN 10088-2:2014
X2CrNiMoN22-5-3
---
1.4462
ISO 9328-7:2004
Grade X2CrNiMoN22-5-3
---
---
JIS G 4304:2012
Symbol SUS329J3L
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
JIS G 4305:2012
Symbol SUS329J3L
---
---
---
---
450
---
620
---
18
ST
ASME SA-240/SA-240M
Type 2304
S32304
---
---
---
400
58
600
87
25
Q+SA
ASTM A240/A240M-15a
Type 2304
S32304
---
---
---
400
58
600
87
25
SA
EN 10028-7:2007
X2CrNiN23-4
---
1.4362
EN 10088-2:2014
X2CrNiN23-4
---
1.4362
ISO 9328-7:2004
Grade X2CrNiN23-4
---
---
t≤8 t ≤ 13.5 t ≤ 50 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
-------------------
405 385 385 450 400 400 405 385 385
-------------------
600-850 600-850 630-800 650-850 650-850 630-800 600-850 600-850 630-800
-------------------
20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T
SA SA SA SA SA SA SA SA SA
Download From http://bbs.infoeach.com
EN 10028-7:2007
Other 293 max. HB; 31 max. HRC 293 max. HBW; 31 max. HRC 293 max. HBW; 31 max. HRC see standard for impact data see standard for impact data --see standard for impact data 302 max. HBW; 32 max. HRC; 320 max. HV 302 max. HBW; 32 max. HRC; 320 max. HV 290 max. HB; 32 max. HRC 290 max. HBW; 32 max. HRC see standard for impact data
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
see standard for impact data --see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
187
4.9 Duplex Stainless Steels for Pressure Vessel Plates 4.9B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels for Pressure Vessel Plates (Continued) Steel No. -----
X2CrNiMoCuN25-6-3
---
1.4507
EN 10088-2:2014
X2CrNiMoCuN25-6-3
---
1.4507
ISO 9328-7:2004
Grade X2CrNiMoCuN256-3
---
---
ASME SA-240/SA-240M
Type 2507
S32750
ASTM A240/A240M-15a
Type 2507
EN 10028-7:2007
Designation -----
EN 10028-7:2007
Section Thickness / Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----550 80 770 112 25 ----550 80 770 112 25
Heat Treatment Q+SA SA
---------------------
495 475 475 550 530 530 495 475 475 550
------------------80
690-940 690-940 690-890 750-1000 750-1000 730-930 690-940 690-940 690-890 795
------------------116
20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 15
SA SA SA SA SA SA SA SA SA Q+SA
S32750
---
---
---
550
80
795
116
15
SA
X2CrNiMoN25-7-4
---
1.4410
EN 10088-2:2014
X2CrNiMoN25-7-4
---
1.4410
ISO 9328-7:2004
Grade X2CrNiMoN25-7-4
---
---
ASME SA-240/SA-240M ASTM A240/A240M-15a
-----
S32760 S32760
-----
t≤8 t ≤ 13.5 t ≤ 50 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 -----
-----------------------
535 515 515 550 530 530 535 515 515 550 550
------------------80 80
750-1000 750-1000 730-930 750-1000 750-1000 730-930 750-1000 750-1000 730-930 750 750
------------------108 108
20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 25 25
SA SA SA SA SA SA SA SA SA Q+SA SA
EN 10028-7:2007
X2CrNiMoCuWN25-7-4
---
1.4501
t ≤ 50
---
515
---
730-930
---
25 L, 25 T
SA
EN 10088-2:2014
X2CrNiMoCuWN25-7-4
---
1.4501
t ≤ 75
---
530
---
730-930
---
25 L, 25 T
SA
ISO 9328-7:2004
Grade X2CrNiMoCuWN25-7-4
---
---
t ≤ 75
---
515
---
730-930
---
25 L, 25 T
SA
Download From http://bbs.infoeach.com
---
t≤8 t ≤ 13.5 t ≤ 50 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
Other 310 max. HB 310 max. HBW; 32 max. HRC see standard for impact data see standard for impact data --see standard for impact data 310 max. HB; 32 max. HRC 310 max. HBW; 32 max. HRC see standard for impact data see standard for impact data --see standard for impact data 270 max. HB 270 max. HBW; 28 max. HRC see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
UNS No. S32520 S32520
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a
Handbook of Comparative World Steel Standards
Chapter 4
Pressure Vessel Steel Plates
188
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter
5 STEEL TUBES AND PIPES
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
190
Steel Tubes and Pipes - List of Standards
Chapter 5
AFNOR Standards AFNOR NF A 49-220:1990 AFNOR NF A 49-647:1979
Grooved Seamless Steel Tubes for Use at High Temperature - Dimensions - Technical Delivery Conditions Structural Welded Tubes, Circular, Square, Rectangular or Oval, in Ferritic or Austenitic Stainless Steels Dimensions - Technical Delivery Conditions
API Standard API 5L - 2012
Specification for Line Pipe
ASME Standards ASME SA-53/SA-53M ASME SA-106/SA-106M ASME SA-135 ASME SA-178/SA-178M ASME SA-179/SA-179M ASME SA-192/SA-192M ASME SA-209/SA-209M ASME SA-210/SA-210M ASME SA-213/SA-213M ASME SA-214/SA-214M ASME SA-249/SA-249M ASME SA-250/SA-250M ASME SA-268/SA-268M ASME SA-312/SA-312M ASME SA-333/SA-333M ASME SA-334/SA-334M ASME SA-335/SA-335M ASME SA-358/SA-358M ASME SA-376/SA-376M ASME SA-409/SA-409M ASME SA-513 ASME SA-556/SA-556M ASME SA-688/SA-688M ASME SA-789/SA-789M ASME SA-803/SA-803M
Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless Seamless Carbon Steel Pipe for High-Temperature Service Electric-Resistance-Welded Steel Pipe Electric-Resistance-Welded Carbon Steel and Carbon-Manganese Steel Boiler and Superheater Tubes Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Cold-Drawn Low-Carbon Steel Heat-Exchanger and Condenser Tubes Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Carbon Steel Boiler Tubes for High-Pressure Service Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Carbon-Molybdenum Alloy-Steel Boiler and Superheater Tubes Seamless Medium-Carbon Steel Boiler and Superheater Tubes Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes Electric-Resistance-Welded Carbon Steel Heat-Exchanger and Condenser Tubes Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes Electric-Resistance-Welded Ferritic Alloy-Steel Boiler and Superheater Tubes Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service Seamless and Welded Austenitic Stainless Steel Pipes Seamless and Welded Steel Pipe for Low-Temperature Service Seamless and Welded Carbon and Alloy-Steel Tubes for Low-Temperature Service Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service Electric-Fusion–Welded Austenitic Chromium-Nickel Alloy Steel Pipe for High-Temperature Service Note: The listed tensile requirements conform to ASTM A240/A240M plate material that is used to make the pipe. See the applicable AWS filler metal specifications listed in ASTM A240/A240M for the weld tensile property requirements. Seamless Austenitic Steel Pipe for High-Temperature Central-Station Service Welded Large Diameter Austenitic Steel Pipe for Corrosive or High-Temperature Service Electric-Resistance-Welded Carbon and Alloy Steel Mechanical Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Cold-Drawn Carbon Steel Feedwater Heater Tubes Welded Austenitic Stainless Steel Feedwater Heater Tubes Seamless and Welded Ferritic/Austenitic Stainless Steel Tubing for General Service Welded Ferritic Stainless Steel Feedwater Heater Tubes
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 5
Steel Tubes and Pipes – List of Standards
191
ASTM Standards ASTM A53/A53M-12 ASTM A106/A106M-14 ASTM A135/A135M-09 (2014) ASTM A139/A139M-04 (2010) ASTM A178/A178M-02 (2012) ASTM A179/A179M-90a (2012) ASTM A192/A192-02 (2012) ASTM A209/A209-03 (2012) ASTM A210/A210M-02 (2012) ASTM A213/A213M-15a ASTM A214/A214M-96 (2012) ASTM A249/A249M-14a ASTM A250/A250M-05 (2014) ASTM A268/A268M-10 ASTM A269/A269M-14e1 ASTM A270/A270M-15 ASTM A312/A312M-15 ASTM A333/A333M-13 ASTM A334/A334M-04a (2010) ASTM A335/A335M-15 ASTM A358/A358M-14a ASTM A376/A376M-14 ASTM A409/A409M-15 ASTM A500/A500M-13 ASTM A501/A501M-14 ASTM A511/A511M-15a ASTM A512-06 (2012) ASTM A513/A513M-15 ASTM A519-06 (2012) ASTM A554-15 ASTM A556/A556M-96 (2012) ASTM A595/A595M-14 ASTM A632-04 (2014) ASTM A688/A688M-15 ASTM A778-01 (2009)e1 ASTM A789/A789M-14 ASTM A803/A803M-12 ASTM A908-03 (2013)
Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless Seamless Carbon Steel Pipe for High-Temperature Service Electric-Resistance-Welded Steel Pipe Electric-Fusion (Arc)-Welded Steel Pipe (NPS 4 and Over) Electric-Resistance-Welded Carbon Steel and Carbon-Manganese Steel Boiler and Superheater Tubes Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Cold-Drawn Low-Carbon Steel Heat-Exchanger and Condenser Tubes Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Carbon Steel Boiler Tubes for High-Pressure Service Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Carbon-Molybdenum Alloy-Steel Boiler and Superheater Tubes Seamless Medium-Carbon Steel Boiler and Superheater Tubes Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes Electric-Resistance-Welded Carbon Steel Heat-Exchanger and Condenser Tubes Welded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes Electric-Resistance-Welded Ferritic Alloy-Steel Boiler and Superheater Tubes Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing for General Service Seamless and Welded Austenitic Stainless Steel Tubing for General Service Seamless and Welded Austenitic and Ferritic/Austenitic Stainless Steel Sanitary Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless, Welded, and Heavily Cold Worked Austenitic Stainless Steel Pipes Seamless and Welded Steel Pipe for Low-Temperature Service and Other Applications with Required Notch Toughness Seamless and Welded Carbon and Alloy-Steel Tubes for Low-Temperature Service Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service Electric-Fusion–Welded Austenitic Chromium-Nickel Stainless Steel Pipe for High-Temperature Service and General Applications Note: The listed tensile requirements conform to ASTM A240/A240M plate material that is used to make the pipe. See the applicable AWS filler metal specifications listed in ASTM A240/A240M for the weld tensile property requirements. Seamless Austenitic Steel Pipe for High-Temperature Service Welded Large Diameter Austenitic Steel Pipe for Corrosive or High-Temperature Service Cold-Formed Welded and Seamless Carbon Steel Structural Tubing in Rounds and Shapes Hot-Formed Welded and Seamless Carbon Steel Structural Tubing Seamless Stainless Steel Mechanical Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Cold-Drawn Buttweld Carbon Steel Mechanical Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Electric-Resistance-Welded Carbon and Alloy Steel Mechanical Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Carbon and Alloy Steel Mechanical Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Data are "typical" values. Welded Stainless Steel Mechanical Tubing Note: Mechanical properties data are supplementary requirements, provided for information only. Seamless Cold-Drawn Carbon Steel Feedwater Heater Tubes Steel Tubes, Low-Carbon or High-Strength Low-Alloy, Tapered for Structural Use Seamless and Welded Austenitic Stainless Steel Tubing (Small-Diameter) for General Service Seamless and Welded Austenitic Stainless Steel Feedwater Heater Tubes Welded, Unannealed Austenitic Stainless Steel Tubular Products Seamless and Welded Ferritic/Austenitic Stainless Steel Tubing for General Service Seamless and Welded Ferritic Stainless Steel Feedwater Heater Tubes Stainless Steel Needle Tubing
BSI Standards BS 3604-2:1991
Steel Pipes and Tubes for Pressure Purposes: Ferritic Alloy Steel with Specified Elevated Temperature Properties – Part 2: Specification for Longitudinally Arc Welded Tubes
CSA Standard CSA Z245.1-14
Steel Pipe
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
192
Steel Tubes and Pipes - List of Standards
Chapter 5
EN Standards EN 10216-1:2013 EN 10216-2:2013 EN 10216-3:2013 EN 10216-4:2013 EN 10216-5:2013 EN 10217-1:2002 A1:2005 EN 10217-2:2002 A1:2005 EN 10217-4:2002 A1:2005 EN 10217-5:2002 A1:2005 EN 10217-6:2002 A1:2005 EN 10217-7:2014 EN 10296-1:2003 EN 10296-2:2005 C2:2007 EN 10297-1:2003 EN 10297-2:2005 C1:2007 EN 10305-1:2010 EN 10305-2:2010 EN 10305-3:2010
Seamless steel tubes for pressure purposes – Technical delivery conditions – Part 1: Non-alloy steel tubes with specified room temperature properties Seamless steel tubes for pressure purposes – Technical delivery conditions – Part 2: Non-alloy and alloy steel tubes with specified elevated temperature properties Seamless steel tubes for pressure purposes – Technical delivery conditions – Part 3: Alloy fine grain steel tubes Seamless steel tubes for pressure purposes – Technical delivery conditions – Part 4: Non-alloy and alloy steel tubes with specified low temperature properties Seamless steel tubes for pressure purposes – Technical delivery conditions – Part 5: Stainless steel tubes Welded steel tubes for pressure purposes – Technical delivery conditions – Part 1: Non-alloy steel tubes with specified room temperature properties Welded steel tubes for pressure purposes – Technical delivery conditions – Part 2: Electric welded non-alloy and alloy steel tubes with specified elevated temperature properties Welded steel tubes for pressure purposes – Technical delivery conditions – Part 4: Electric welded non-alloy steel tubes with specified low temperature properties Welded steel tubes for pressure purposes – Technical delivery conditions – Part 5: Submerged arc welded nonalloy and alloy steel tubes with specified elevated temperature properties Welded steel tubes for pressure purposes – Technical delivery conditions – Part 6: Submerged arc welded nonalloy steel tubes with specified low temperature properties Welded steel tubes for pressure purposes – Technical delivery conditions – Part 7: Stainless steel tubes Welded circular steel tubes for mechanical and general engineering purposes – Technical delivery conditions – Part 1: Non-alloy and alloy steel tubes Welded circular steel tubes for mechanical and general engineering purposes – Technical delivery conditions – Part 2: Stainless steel Seamless circular steel tubes for mechanical and general engineering purposes – Technical delivery conditions – Part 1: Non-alloy and alloy steel tubes Seamless circular steel tubes for mechanical and general engineering purposes – Technical delivery conditions – Part 2: Stainless steel Steel tubes for precision applications – Technical delivery conditions – Part 1: Seamless cold drawn tubes Steel tubes for precision applications – Technical delivery conditions – Part 2: Welded cold drawn tubes Steel tubes for precision applications – Technical delivery conditions – Part 3: Welded cold sized tubes
ISO Standards ISO 2937:1974 ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 ISO 9329-2:1997 ISO 9329-3:1997 ISO 9330-3:1997 ISO 9330-5:2000
Plain End Seamless Steel Tubes for Mechanical Application Plain End Seamless Precision Steel Tubes - Technical Conditions for Delivery Plain End Welded Precision Steel Tubes - Technical Conditions for Delivery Plain End As-Welded and Sized Precision Steel Tubes - Technical Conditions for Delivery Seamless Steel Tubes for Pressure Purposes - Technical Delivery Conditions - Part 2: Unalloyed and Alloyed Steels with Specified Elevated Temperature Properties Seamless Steel Tubes for Pressure Purposes. Technical Delivery Conditions Part 3: Unalloyed and Alloyed Steels with Specified Low Temperature Properties Welded Steel Tubes for Pressure Purposes. Technical Delivery Conditions. Part 3: Electric Resistance and Induction Welded Unalloyed and Alloyed Steel Tubes with Specified Low Temperature Properties Welded Steel Tubes for Pressure Purposes - Technical Delivery Conditions Part 5: Submerged Arc-Welded Unalloyed and Alloyed Steel Tubes with Specified Low Temperature Properties
EN ISO Standard EN ISO 3183:2013
Petroleum and natural gas industries – Steel pipe for pipeline transportation systems
GB Standards GB 3087-1999 GB 5310-1995 GB 6479-2000 GB/T 12770-2002 GB/T 14164:2005 GB/T 14975-2002 GB/T 17396-1998 GB 18248-2000 GB/T 18984-2003
Seamless Steel Tubes for Low and Medium Pressure Seamless Steel Tubes and Pipes for High Pressure Boiler Seamless Steel Tubes for High-Pressure for Chemical Fertilizer Equipments Welded Stainless Steel Tubes for Machine Structures Hot-Rolled Wide Strips for Line Pipe of Petroleum and Natural Gas Stainless Steel Seamless Tubes for Structures Seamless Hot-Rolled Steel Tubes for Hydraulic Pillar Service Seamless Steel Tubes for Gas Cylinder Seamless Steel Tubes for Low-Temperature-Service Piping
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 5
Steel Tubes and Pipes – List of Standards
193
JIS Standards JIS G 3441:2012 JIS G 3444:2010 JIS G 3445:2010 JIS G 3446:2012 JIS G 3452:2014 JIS G 3454:2012 JIS G 3455:2012 JIS G 3456:2014 JIS G 3457:2012 JIS G 3458:2013 JIS G 3459:2012 JIS G 3460:2013 JIS G 3461:2012 JIS G 3462:2014 JIS G 3463:2012 JIS G 3464:2013 JIS G 3467:2013 JIS G 3468:2011 JIS G 3472:2013 JIS G 3473:2013 JIS G 3474:2014
Alloy steel tubes for machine purposes Carbon steel tubes for general structure Carbon steel tubes for machine structure Stainless steel pipes for machine and structural purposes Carbon steel pipes for ordinary piping Carbon steel tubes for pressure service Carbon steel pipes for high pressure service Carbon steel pipes for high temperature service Arc welded carbon steel pipes Alloy steel pipes Stainless steel pipes Steel tubes for low temperature service Carbon steel boiler and heat exchanger tubes Alloy steel tubes for boiler and heat exchanger Stainless steel boiler and heat exchanger tubes Steel heat exchanger tubes for low temperature service Steel tubes for fired heater Large diameter welded stainless steel pipes Electric resistance welded carbon steel tubes for automobile Carbon steel tubes for cylinder barrels High strength steel tubes for steel tower
SAE Standard SAE J526 NOV10
Welded Low-Carbon Steel Tubing Suitable for Bending, Flaring, Beading, Forming and Brazing
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
194
Steel Tubes and Pipes – Heat Treatment Terms
Chapter 5
Heat Treatment Terms Applicable to this Chapter 5.1 Tubes for General and Structural Applications Standard AFNOR NF A 49-647:1979 ASME SA-268/SA-268M ASME SA-513 ASME SA-789/SA-789M ASTM A268/A268M-10 ASTM A269/A269M-14e1 ASTM A270/A270M-15 ASTM A500/A500M-13 ASTM A501/A501M-14 ASTM A511/A511M-15a ASTM A512-06 (2012) ASTM A513/A513M-15 ASTM A519-06 (2012) ASTM A554-15 ASTM A595/A595M-14 ASTM A632-04 (2014) ASTM A778-01 (2009)e1 ASTM A789/A789M-14 EN 10296-1:2003 EN 10296-2:2005 C2:2007 EN 10297-1:2003 EN 10297-2:2005 C1:2007 EN 10305-1:2010 EN 10305-2:2010 EN 10305-3:2010 GB/T 12770-2002 GB/T 14975-2002 GB/T 17396-1998 GB 18248-2000 ISO 2937:1974 ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 JIS G 3441:2012 JIS G 3444:2010 JIS G 3445:2010 JIS G 3446:2012 JIS G 3472:2013 JIS G 3473:2013 JIS G 3474:2014 SAE J526 NOV10
Heat Treatment Terms AM: as manufactured HT: heat treated N: normalized; AW: as-welded; SD: sink-drawn; MD: mandrel-drawn; MD SR: mandrel-drawn stress-relieved ST+Q: solution treated and quenched HT: heat treated HT: heat treated HT+Q: heat treated then quenched with water; RC: rapidly cooled CF: cold formed; SR: stress relieved; A: annealed; HT: heat treated HF: hot formed A: annealed; A+Q: annealed then water quenched; RC: cooled rapidly SA: soft-annealed; SR A: stress relief annealed AW: as-welded; N: normalized; SD: sink-drawn; MD: mandrel-drawn; MD SR: mandrel-drawn stress-relieved HR: hot rolled; CW: cold worked; SR: stress relieved; A: annealed; N: normalized; AM: as manufactured A: annealed; none: not thermally treated RCCM: roll compressed cold on a mandrel HT: heat treated; HT+Q: heat treated then water quenched; RC: cooled rapidly AM: as manufactured ST+Q: solution treated and quenched CR: cold rolled; A: annealed; N: full tube normalized; NW: normalized weld zone; U: see standard AW: as welded; A: annealed; SA: solution annealed AR: as rolled; N: normalized; QT: quenched and tempered; A: annealed A: annealed; SA: solution annealed; Q+T: quenched and tempered; CF: cold finished; HF: hot finished A: annealed; C: cold drawn, hard; LC: cold drawn, soft; N: normalized; SR: cold drawn and stress relieved A: annealed; C: cold drawn, hard; LC: cold drawn, soft; N: normalized; SR: cold drawn and stress relieved A: annealed; N: normalized; CR1: welded and cold sized, suitable for final annealing; CR2: welded and cold sized, not intended for heat treatment after welding and resizing A: annealed; W: as-welded; ST: solution treated BA: by agreement HR: hot-rolled; A: annealed; H+T: hardened and tempered Q+T: quenched and tempered HF: hot finished BK: cold-finished, as drawn; BKW: lightly cold-worked condition; GBK and GZF (A): annealed; NBK and NZF (N): normalized BK: cold-finished, as drawn; BKW: lightly cold-worked condition; GBK and GZF (A): annealed; NBK and NZF (N): normalized KM: as-welded and sized; GKM and GZF (A): annealed; NKM and NZF (N): normalized AM: as manufactured; CF: cold finished; A: annealed AM: as manufactured AM: as manufactured; CF: cold formed; AHT: appropriately heat treated ST: solution treated; AM: as manufactured; A: annealed See standard AM: as manufactured; CF: cold finished; SR: stress relieved annealed AM: as manufactured See standard
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 5
Steel Tubes and Pipes – Heat Treatment Terms
195
Heat Treatment Terms Applicable to this Chapter (Continued) 5.2 Tubes for Heat Transfer Applications Standard ASME SA-178/SA-178M ASME SA-179/SA-179M ASME SA-192/SA-192M ASME SA-209/SA-209M ASME SA-210/SA-210M ASME SA-213/SA-213M ASME SA-214/SA-214M ASME SA-249/SA-249M ASME SA-250/SA-250M ASME SA-556/SA-556M ASME SA-688/SA-688M ASME SA-803/SA-803M ASTM A178/A178M-02 (2012) ASTM A179/A179M-90a (2012) ASTM A192/A192M-02 (2012) ASTM A209/A209M-03 (2012) ASTM A210/A210M-02 (2012) ASTM A213/A213M-15a ASTM A214/A214M-96 (2012) ASTM A249/A249M-14a ASTM A250/A250M-05 (2014) ASTM A556/A556M-96 (2012) ASTM A688/A688M-15 ASTM A803/A803M-12 EN 10216-1:2013 EN 10216-2:2013 EN 10217-1:2002 A1:2005 EN 10217-2:2002 A1:2005 EN 10217-7:2014 JIS G 3461:2012 JIS G 3462:2014 JIS G 3463:2012 JIS G 3467:2013
Heat Treatment Terms See standard HT: heat treated after final cold draw pass at 1200°F (650°C) or higher CF: cold finished HF: hot finished; CF+IA: cold finished and isothermally annealed; FA: fully annealed; N+T: normalized and tempered HF: hot finished; CF+A: cold finished and subcritically annealed; CF+N: cold finished and normalized heat treatment A+N+T+SCA: fully or isothermally annealed, normalized and tempered, and subcritically annealed; A+N+T: fully or isothermally annealed and normalized and tempered; N+T: normalized and tempered; ST+Q: solution treated then water quenched; RC: cooled rapidly See standard ST+Q: solution treated then water quenched; RC: cooled rapidly FA: fully annealed; IA: isothermally annealed; N: normalized; N+T: normalized and tempered HT: heat treated SA+RC: solution annealed then cooled rapidly; SA+Q: solution annealed then quenched rapidly SA: solution-annealed See standard CD + 1200°F min: cold drawn + heat treated at 1200°F or higher HF: hot finished; CF + 1200°F min: cold finished + heat treated at 1200°F or higher See standard HF: hot finished; CF+SA: cold finished and subcritically annealed; A: fully annealed; N: normalized A: annealed; IA: isothermally annealed; NT: normalized and tempered; SA: subcritically annealed; ST+Q: solution treated then water quenched; RC: cooled rapidly See standard ST+Q: solution treated then water quenched; RC: rapidly cooled; SA: solution annealed A: fully annealed; IA: isothermally annealed; N: normalized; NT: normalized and tempered CD + 1200°F min: cold drawn + heat treated to 1200°F or higher SA+RC: solution-annealed then rapidly cooled; SA+Q: solution-annealed then quenched in water SA: solution-annealed HF: hot formed; HFCF: hot formed cold finished; AF: as formed; N: normalized; NF: normalizing formed; I: isothermally annealed; N: normalized; NT: normalized and tempered; QT: quenched and tempered; NF: normalizing formed See standard See standard SA: solution annealed See standard; N: normalized LTA: low temperature annealed; IA: isothermally annealed; A: fully annealed; N: normalized; NT: normalized and tempered A: annealed; ST: solution treated HFS: hot finished seamless; CFS: cold finished seamless; AM: as manufactured; LTA: low temperature annealed; IA: isothermally annealed; A: fully annealed; N: normalized; NT: normalized and tempered; ST: solution treated
5.3 Tubes for Low Temperature Service Standard
Heat Treatment Terms N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered; ASME SA-334/SA-334M NN+T: double normalized and tempered N: normalized; NT: normalized and tempered; QT: quenched and tempered; NNT: double normalized and ASTM A334/A334M-04a (2010) tempered EN 10216-4:2013 N: normalized; NT: normalized and tempered; QT: quenched and tempered EN 10217-4:2002 A1:2005 See standard GB/T 18984-2003 N: normalized ISO 9329-3:1997 N: normalized; QT: quenched and tempered ISO 9330-3:1997 N: normalized; QT: quenched and tempered ISO 9330-5:2000 N: normalized; QT: quenched and tempered N: normalized; NT: normalized and tempered; NNT: double normalized and tempered; JIS G 3464:2013 QT: quenched and tempered
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
196
Steel Tubes and Pipes – Heat Treatment Terms
Chapter 5
Heat Treatment Terms Applicable to this Chapter (Continued) 5.4 Tubes and Pipes for Pressure Service Standard AFNOR NF A 49-220:1990 ASME SA-53/SA-53M ASME SA-106 ASME SA-135 ASME SA-312/SA-312M ASME SA-333/SA-333M ASME SA-335/SA-335M ASME SA-358/SA-358M ASME SA-376/SA-376M ASME SA-409/SA-409M ASTM A53/A53M-12 ASTM A106/A106M-14 ASTM A135/A135M-09 (2012) ASTM A139/A139M-04 (2010) ASTM A312/A312M-15 ASTM A333/A333M-13 ASTM A335/A335M-15
ASTM A358/A358M-14a
ASTM A376/A376M-14
ASTM A409/A409M-15
ASTM A908-03 (2013) BS 3604-2:1991 EN 10216-1:2013 EN 10216-2:2013 EN 10216-3:2013 EN 10216-4:2013 EN 10216-5:2013 EN 10217-1:2002 A1:2005 EN 10217-2:2002 A1:2005 EN 10217-4:2002 A1:2005 EN 10217-7:2014 GB 3087-1999 GB 5310-1995 GB 6479-2000
Heat Treatment Terms See standard; N: normalized; T: tempered --CF+HT: cold finished and heat treated; HF: hot finished --A+Q: annealed then water quenched; RC: cooled rapidly N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered; NN+T: double normalized and tempered A: fully or isothermally annealed; N+T: normalized and tempered; SA: subcritically annealed; Q+T: quenched and tempered H: heated at specified temperature and water quenched or rapidly cooled; HT: a final heat treatment temperature under 1900°F; A+Q: annealed and quenched; ST: solution treated HT+Q: heat treated then water quenched; RC: cooled rapidly; SA+Q: solution annealed then water quenched; SA+RC: solution annealed then cooled rapidly HT+Q: heat treated then water quenched; RC: cooled rapidly AM: as manufactured; T: tempered HF: hot finished; CD + 1200°F min: cold drawn + heat treated at 1200°F or higher AM: as manufactured; T: tempered See standard A+Q: annealed then water quenched; RC: cooled rapidly QT: quenched and tempered; NNT: double normalized and tempered; N: normalized; NT: normalized and tempered FA: fully annealed; IA: isothermally annealed; NT: normalized and tempered; QT: liquid quenched and tempered; SA: subcritically annealed H: heated at specified temperature and water quenched or rapidly cooled; HT: a final heat treatment temperature under 1900°F; HT-O: no final heat treatment of pipe fabricated of plate that has been solution treated at temperatures required by this specification; HT-SO: No final heat treatment of pipe fabricated of plate that has not been heat treated See standard; HT: heat treated H: heated at specified temperature and water quenched or rapidly cooled; HT: a final heat treatment temperature under 1900°F; HT-O: no final heat treatment of pipe fabricated of plate that has been solution treated at temperatures required by this specification; HT-SO: No final heat treatment of pipe fabricated of plate that has not been heat treated --See standard HF: hot formed; HFCF: hot formed cold finished; AF: as formed; N: normalized; NF: normalizing formed; I: isothermally annealed; N: normalized; NT: normalized and tempered; QT: quenched and tempered; NF: normalizing formed N: normalized N: normalized; NT: normalized and tempered; QT: quenched and tempered SA: solution annealed; SA+CF: solution annealed and cold finished; SA+HF: solution annealed and hot finished See standard See standard See standard SA: solution annealed HF: hot finished; CF: cold finished; HT: heat treated N+T: normalized and tempered; N: normalized; ST: solution treated N: normalized; N+T: normalized and tempered; A: annealed
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 5
Steel Tubes and Pipes – Heat Treatment Terms
197
Heat Treatment Terms Applicable to this Chapter (Continued) 5.4 Tubes and Pipes for Pressure Service (Continued) Standard JIS G 3452:2014 JIS G 3454:2012 JIS G 3455:2012 JIS G 3456:2014 JIS G 3457:2012 JIS G 3458:2013 JIS G 3459:2012 JIS G 3460:2013 JIS G 3468:2011
Heat Treatment Terms See Standard AM: as manufactured; CF + A: cold finished and annealed See standard See standard AW: as welded; ACE: as cold expanded LTA: low temperature annealed; IA: isothermally annealed; FA: fully annealed; N: normalized; NT: normalized and tempered ST: solution treated N: normalized; NT: normalized and tempered; QT: quenched and tempered; NNT: double normalized and tempered ST: solution treated
5.5 Line Pipe Steels Standard API 5L - 2012 CSA Z245.1-14 EN ISO 3183:2013 GB/T 14164-2005
Heat Treatment Terms See standard See standard See standard HR: hot-rolled; CtR: control-rolled
Impact Testing Notes Applicable to this Chapter see standard for impact data: impact testing requirements are listed in the standard for multiple test temperatures.
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter 5
Steel Tubes and Pipes
198
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications
Designation
JIS G 3445:2010 JIS G 3452:2014
Symbol STKM11A Symbol SGP
Download From http://bbs.infoeach.com
EN 10305-3:2010 ASTM A513-15* ASTM A512-06 (2012)* ASME SA-513* EN 10305-1:2010 ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 JIS G 3444:2010
E155 E155 E155 Grade 1008 Grade 1008 R28 R28 R28 E155 E155 E155 E190 E190 Grade 1010 Grade MT 1010 Grade 1010 E215 R28 R28 R28 Symbol STK290
EN 10305-3:2010
E155 E195 EN 10305-2:2010 E195 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
UNS No. ------G10080 G10080 ----------------G10100 G10100 G10100 -----------
Steel No. 1.0033 1.0033 1.0033 ----------1.0033 1.0033 1.0033 1.0031 1.0031 ------1.0212 ---------
-----
-----
-------
1.0033 1.0034 1.0034
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi --------260 --------260 ----------260 --------160 260 23 38 ----159 262 23 38 --------270 ----------270 ------------270 ----155 270-410 --------155 270-410 --------155 --270 ------190 --270 ------190 270 --------170 275 25 40 ----138 276 20 40 ----172 276 25 40 ----140 280 --------155 --280 ------155 --280 ----------155 280 d < 40 ----290 ----40 < d ≤350 ----290 ----d > 350 ----290 ----d > 40 ----290 --------290 ----3 40 --305 440 20 L; 15 T ------------305 440 25 ------------305 440 10 ------------355 440 20 ----G10450 --O.D. ≤ 323.8 O.D. ≤ 12.75 241 448 20 35 65 G10350 --O.D. ≤ 323.8 O.D. ≤ 12.75 276 40 448 65 20 G10350 --O.D. ≤ 323.8 O.D. ≤ 12.75 276 448 20 40 65 G10350 ------310 45 448 65 20 G10400 ------310 45 448 65 20 G10200 --O.D. ≤ 323.8 O.D. ≤ 12.75 345 50 448 65 10 G10150 ------379 55 448 65 5 G10200 ------379 55 448 65 10 G10250 ------379 55 448 65 7 G10300 ------276 448 30 40 65 G11100 ------400 434-689 15 58 63-100
Heat Treatment NKM & NZF C SR A A N CR1 LC SR U, NW AM, CF, or AHT AM, CF, or AHT see standard CF and SR see standard A HR N N N SR MD MD SR SD SA SR A
Other --see standard 70-90 HRB see standard see standard see standard see standard see standard ------------72 HRB 72 HRB 72 HRB 88 max HRB 90 max HRB 72 HRB 77 min HRB 75 min HRB 72 min HRB 60 min HRB 70-100 HRB
Grade 1011
G10110
---
---
---
407
59
448-689
65-100
13
SR A
70-100 HRB
ASTM A513-15*
Grade 1035
G10350
---
---
---
310
45
450
65
20
N
88 max HRB
ASTM A513-15*
Grade 1040 Grade 1015
G10400 G10150
-----
-----
-----
310 380
45 55
450 450
65 65
20 5
N MD
90 max HRB 77 min HRB
Grade 1020
G10200
---
---
---
380
55
450
65
10
MD SR
75 min HRB
Grade 1025 G10250 ISO 3304:1985 R37 --R44 --ISO 3305:1985 R37 --R44 --*: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
-----------
-----------
-----------
380 ---------
55 ---------
450 450 450 450 450
65 ---------
7 6 8 6 8
SD BK BKW BK BKW
72 min HRB ---------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10305-3:2010 EN 10305-2:2010
Designation
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
206
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification EN 10305-3:2010 EN 10305-1:2010 EN 10305-2:2010 EN 10297-1:2003
ASME SA-513*
E355 E355 E355 E315
UNS No. ---------
Steel No. 1.0580 1.0580 1.0580 1.0236
E370 E370 Grade A Grade 1035 Grade 1524 Grade 1040 Grade 1035
--1.0261 --1.0261 K02004 --G10350 --G15240 --G10400 --G10350 ---
Grade 1524
G15240
Grade 1040 ASTM A512-06 (2012)* Grade MT 1015 EN 10305-1:2010 C35E ASTM A512-06 (2012)* Grade 1016 Grade MT 1017 ASTM A519-06 (2012)* Grade 1050 ASME SA-513* Grade 1021 ASTM A512-06 (2012)* Grade 1018 JIS G 3445:2010 Symbol STKM15A JIS G 3472:2013 Symbol STAM470G JIS G 3445:2010 Symbol STKM12C ASTM A513-15* Grade 1021 JIS G 3472:2013 Symbol STAM470H ISO 3304:1985 R50 ISO 3305:1985 R50 ISO 3306:1985 R50 EN 10305-1:2010 E235 ASTM A595/A595M-14 Grade B *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi ------450 --------225 450 --------225 450 ----t ≤ 16 315 450 ------305 450 ------16 < t ≤ 40 295 450 ------40 < t ≤ 65 280 420 ------65 < t ≤ 80 270 420 ------80 < t ≤ 100 ----370 450 --------370 450 --------380 55 450 65 ----345 50 66 455 ----345 50 455 66 ----345 50 455 66 ----345 455 50 66 ---
G10400 ----G10150 ------1.1181 --G10160 ----G10170 ----G10500 --O.D. ≤ 323.8 G10210 ----G10180 --------d > 40 ----------d > 40 G10210 ------------------------------1.0308 --K02005 -----
Elongation % min. 22 22 22 21 L; 19 T 21 L; 19 T 21 L; 19 T 21 L; 19 T 21 L; 19 T 15 15 L; 13 T 23 10 10 10 10
Heat Treatment A A A AR, N AR, N AR, N AR, N AR, N CR2 CR RCCM AW AW AW AW
Other see standard see standard see standard ----------see standard ----75 min HRB 75 min HRB 75 min HRB 75 min HRB
---
345
50
455
66
10
AW
75 min HRB
----------O.D. ≤ 12.75 -------------------------
345 414 280 421 427 262 400 427 275 325 355 400 410 ------384 410
50 60 --61 62 38 58 62 ------58 ----------60
455 455-689 460 462-689 462-689 469 469 469-689 470 470 470 470 470 480 480 480 480 480
66 66-100 --67-100 67-100 68 68 68-100 ------68 ----------70
10 14 21 13 13 18 10 13 22 L; 17 T 22 20 L; 15 T 10 18 23 23 23 6 21
AW SR A N SR A SR A A MD SR SR A AM, CF, or AHT see standard AM, CF, or AHT MD SR see standard GBK & GZF GBK & GZF GKM & GZF C RCCM
75 min HRB 70-100 HRB see standard 70-100 HRB 72-100 HRB 74 HRB 75 min HRB 73-100 HRB ------75 min HRB --------see standard ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10305-3:2010 EN 10296-1:2003 ASTM A595/A595M-14 ASTM A513-15*
Designation
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
207
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued) UNS Steel No. No. G10260 --G10200 ---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----380 480 7 55 70 ----415 5 60 480 70
Grade 1025 Grade 1030 Grade 1025 Grade 1020 Grade 1026
G10250 G10300 G10250 G10200 G10260
-----------
----O.D. ≤ 323.8 O.D. ≤ 323.8 ---
----O.D. ≤ 12.75 O.D. ≤ 12.75 ---
415 425 379 414 379
60 62 55 60 55
480 480 483 483 483
70 70 70 70 70
Grade 1020
G10200
---
---
---
414
60
483
70
Grade 1025
G10250
---
---
---
414
60
483
70
EN 10297-1:2003
Grade 1030 E355
G10300 ----1.0580
EN 10296-1:2003 ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 JIS G 3444:2010
E355 R50 R50 R50 Symbol STK490
--t ≤ 16 16 < t ≤ 40 40 < t ≤ 65 65 < t ≤ 80 80 < t ≤ 100 --------d < 40 40 < d ≤350 d > 350 ---------------------------
-----------------------------------------------------
427 355 345 335 315 295 --285 285 285 315 315 315 315 315 285 355 355 355 355 392 420 448 425 427 462
62 ------------------------------------------65 62 62 67
483 490 490 490 470 470 490 490 490 490 490 490 490 490 490 490-610 490 490-630 490-630 490-630 490 490 490-896 495 496 496-896
70 ------------------------------------------71-130 72 72 72-130
7 20 L; 18 T 20 L; 18 T 20 L; 18 T 20 L; 18 T 20 L; 18 T 22 21 21 21 23 L 23 L 18 T 23 L; 18 T 23 L; 18 T 21 22 22 22 22 6 12 11 5 5 11
Download From http://bbs.infoeach.com
ASTM A519-06 (2012)* ASTM A519-06 (2012)* ASME SA-513*
JIS G 3445:2010
Symbol STKM18B Symbol STKM19A ISO 2937:1974 TS 18 EN 10296-1:2003 E355 EN 10305-1:2010 E355 EN 10305-2:2010 E355 EN 10305-3:2010 E355 EN 10305-2:2010 E235 EN 10305-3:2010 E420 ASTM A512-06 (2012)* Grade MT 1020 ASTM A513-15* Grade 1021 ASME SA-513* Grade 1021 ASTM A512-06 (2012)* Grade 1025 *: See "List of Standards" at the beginning of the chapter.
-----------
1.0580 ---------
------------------G10200 G10210 G10210 G10250
------1.0580 1.0580 1.0580 1.0580 1.0308 1.0575 ---------
Heat Treatment SD MD
Other 77 min HRB 80 min HRB
MD SR SD SR CW SD
77 min HRB 78 min HRB 75 HRB 75 HRB 77 min HRB
5
MD
80 min HRB
10
MD SR
77 min HRB
SD AR, N AR, N AR, N AR, N AR, N A NBK & NZF NBK & NZF NKM & NZF AM AM AM AM, CF, or AHT AM, CF, or AHT HF N N N N C CR2 SR A MD MD SR A
78 min HRB --------------------------------see standard see standard see standard see standard see standard 75 HRB-20 HRC 80 min HRB 80 min HRB 78 HRB-20 HRC
10 7 8 5 7
Download From http://bbs.infoeach.com
Designation Grade 1026 Grade 1020
Specification ASTM A513-15*
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
208
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued) Steel No. 1.1151
Symbol STK500
---
---
JIS G 3472:2013 JIS G 3445:2010 JIS G 3472:2013 EN 10305-1:2010 GB/T 17396-1998 JIS G 3445:2010 EN 10305-2:2010
Symbol STAM500G Symbol STKM14B Symbol STAM500H C45E Grade 35 Symbol STKM16A E275
---------------
------1.1191 ----1.0225
JIS G 3445:2010
Symbol STKM13C Symbol STKM18C Symbol STC510A Symbol STC510B Grade 1025 Grade 1026 Grade 1045
--------G10250 G10260 G10450
---------------
G10250 G10260 G10250 G10350 ------------G10500 ---
--------1.0408 1.0509 ------1.0408 --1.1181
C22E
JIS G 3444:2010
Download From http://bbs.infoeach.com
JIS G 3473:2013 ASTM A513-15* ASTM A519-06 (2012)* ASME SA-513*
Designation
Grade 1025 Grade 1026 ASTM A519-06 (2012)* Grade 1025 Grade 1035 EN 10305-1:2010 E255 E410 ISO 3304:1985 R44 ISO 3305:1985 R44 ISO 3306:1985 R50 EN 10305-1:2010 E255 ASTM A519-06 (2012)* Grade 1050 EN 10305-1:2010 C35E *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi t≤8 340 500 ------290 470 ------8 < t ≤ 20 270 440 ------20 < t ≤ 50 260 420 ------50 < t ≤ 80 d < 40 --355 500 ----40 < d ≤350 --355 500 ----d > 350 --355 500 --------355 500 --------355 500 --------430 500 ----------510 --------305 --510 --d > 40 --325 510 --------357 510 --------375 510 ----d > 40 --380 510 ----d > 40 --380 510 --------380 510 --------380 510 --------450 65 515 75 ----450 65 515 75 O.D. ≤ 323.8 O.D. ≤ 12.75 310 45 517 75 O.D. ≤ 323.8 O.D. ≤ 12.75 331 48 517 75 ----448 65 517 75 ----448 65 517 75 O.D. ≤ 323.8 O.D. ≤ 12.75 448 65 517 75 O.D. ≤ 323.8 O.D. ≤ 12.75 448 65 75 517 ------520 ----------520 ------------520 ----------520 ----------520 ------375 520 ----O.D. ≤ 323.8 O.D. ≤ 12.75 345 538 50 78 ----540 -------
Elongation % min. 20 L; 18 T 22 L; 20 T 22 L; 20 T 22 L; 20 15 L 15 L 10 T 18 15 L; 10 T 16 20 17 20 L; 15 T 8 12 15 L; 10 T 15 L; 10 T 10 15 5 10 15 15 5 10 5 8 8 22 5 5 5 12 12 7
Heat Treatment QT QT QT QT AM AM AM see standard AM, CF, or AHT see standard A HR, A or H+T AM, CF, or AHT LC SR AM, CF, or AHT AM, CF, or AHT CF or SR SR MD MD SR HR N MD MD SR CW SR LC A BK BK KM SR N LC
Other --------------------see standard ----see standard see standard --------82 min HRB 80 min HRB 80 HRB 80 HRB 82 min HRB 80 min HRB 80 HRB 80 HRB see standard see standard ------see standard 82 HRB see standard
Download From http://bbs.infoeach.com
UNS No. ---
Specification EN 10297-1:2003
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
209
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued)
Symbol STKM20A Symbol STC540 E355 Symbol STAM540H R50 R50 C35E
JIS G 3445:2010 EN 10305-1:2010 JIS G 3445:2010
Symbol STKM17A E410 Symbol STKM14C Symbol STKM19C Grade 1026 Grade 1030 Grade 1035 Grade 1050 Grade 1030 Grade 1045 Grade 1026 Grade 1030
G10300
Grade 1035 E275 Grade 1050 E255 E355
G10350 ------1.0225 --G10500 --O.D. ≤ 323.8 --1.0408 ----1.0580 --------d > 40
Download From http://bbs.infoeach.com
ASTM A513-15*
ASTM A519-06 (2012)* ASTM A512-06 (2012)* ASTM A519-06 (2012)* ASME SA-513*
EN 10305-2:2010 ASTM A519-06 (2012)* EN 10305-1:2010
Designation C 35 C45E E355 Symbol STK540
JIS G 3445:2010 Symbol STKM15C *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
UNS No. ---------
Steel No. --1.1191 1.0580 ---
---
---
Elongation % min. 20 18 5 20 L 20 L 16 T 23 L; 18 T 20 5 13 7 7 18 L; 16 T 19 L; 17 T 19 L; 17 T 20 L; 15 T 22 15 L; 10 T 15 L; 10 T 5 10 7 10 10 8 5
Heat Treatment HF N CR1 AM AM AM AM, CF, or AHT AM U, NW see standard BKW BKW N N N AM, CF, or AHT N AM, CF, or AHT AM, CF, or AHT MD MD SR SD HR SR A SR MD
Other --see standard see standard ------------------see standard see standard see standard --see standard ----85 min HRB 81 min HRB 82 min HRB 85 HRB 80 HRB-20 HRC 85 HRB 85 min HRB
---
483
70
552
80
10
MD SR
81 min HRB
----O.D. ≤ 12.75 ---------
483 448 483 --406 450 430
70 --70 ---------
552 560 565 580 580 580 580
80 --82 ---------
7 5 6 5 7 10 12 L; 7 T
SD C SR C LC SR AM, CF, or AHT
82 min HRB see standard 86 HRB see standard see standard see standard ---
Download From http://bbs.infoeach.com
JIS G 3445:2010 JIS G 3473:2013 EN 10296-1:2003 JIS G 3472:2013 ISO 3304:1985 ISO 3305:1985 EN 10297-1:2003
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi ----275 540-660 --------340 540 --------378 540 ----d < 40 --390 540 ----40 < d ≤350 --390 540 ----d > 350 --390 540 --------d > 40 --390 540 ------------390 540 ------1.0580 ----400 540 ------------480 540 ----------------550 --------------550 ----1.1181 t ≤ 16 300 550 ------270 520 ------16 < t ≤ 40 270 520 ------40 < t ≤ 80 ----d > 40 --345 550 ------1.0509 ----410 550-700 --------d > 40 --410 550 --------d > 40 --410 550 ----G10260 ------480 70 550 80 G10300 ------480 70 550 80 G10350 ------480 70 550 80 G10500 --O.D. ≤ 323.8 O.D. ≤ 12.75 345 552 50 80 G10300 ------483 552-896 70 80-130 G10450 --O.D. ≤ 323.8 O.D. ≤ 12.75 483 552 70 80 G10260 ------483 552 70 80
Specification ISO 2937:1974 EN 10305-1:2010 EN 10305-3:2010 JIS G 3444:2010
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
210
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification ASTM A513-15*
ASME SA-513*
JIS G 3474:2014 JIS G 3473:2013
Symbol STKT590 Symbol STC590A Symbol STC590B
EN 10297-1:2003
E420J2
ISO 3304:1985 ISO 3305:1985 EN 10305-1:2010 EN 10297-1:2003
JIS G 3445:2010 ASTM A513-15*
R50 R50 E410 C45E
Symbol STKM16C Grade 1035 Grade 1040 Grade 1524 ASTM A519-06 (2012)* Grade 1045 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
UNS Steel Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation No. No. mm in. MPa ksi MPa ksi % min. G10300 ------515 5 75 585 85 G10350 ------515 10 75 585 85 G10400 ------515 10 75 585 85 G15240 ------515 10 75 585 85 G10300 ------517 75 586 85 5 G10350 ------517 75 586 85 10 G10400 ------517 75 586 85 10 G15240 ------517 75 586 85 10 G10350 --O.D. ≤ 323.8 O.D. ≤ 12.75 517 75 586 85 5 --1.1181 ----590 5 --------------335 --590 --14 --1.0580 ----413 590 6 --------435 590 10 ------------440 590-740 20 L; 16 T ------------490 590 10 ------------490 590 15 -------
1.0599
---------
----1.0509 1.1181
--G10350 G10400 G15240 G10450
-----------
Heat Treatment MD MD SR MD SR MD SR MD MD SR MD SR MD SR CW C HR, A or H+T LC SR AM CF or SR SR
t ≤ 16
---
420
---
600
---
19 L; 17 T
N
16 < t ≤ 40
---
400
---
560
---
19 L; 17 T
N
40 < t ≤ 65
---
390
---
530
---
19 L; 17 T
N
65 < t ≤ 80
---
370
---
500
---
19 L; 17 T
N
80 < t ≤ 100
---
360
---
500
---
19 L; 17 T
N
------t ≤ 16 16 < t ≤ 40 40 < t ≤ 80 d > 40 ------O.D. ≤ 323.8
--------------------O.D. ≤ 12.75
------340 305 305 460 550 550 550 552
--------------80 80 80 80
600 600 620 620 580 580 620 620 620 620 621
--------------90 90 90 90
4 4 8 14 L; 12 T 16 L; 14 T 16 L; 14 T 12 L; 7 T 5 5 5 5
BK BK LC N N N AM, CF, or AHT MD MD MD CW
Other 87 min HRB 85 min HRB 85 min HRB 85 min HRB 87 min HRB 85 min HRB 85 min HRB 85 min HRB 88 HRB see standard --see standard see standard ------L: 27J at -20°C T: 20 J at -20°C L: 27J at -20°C T: 20 J at -20°C L: 27J at -20°C T: 20 J at -20°C L: 27J at -20°C T: 20 J at -20°C L: 27J at -20°C T: 20 J at -20°C ----see standard see standard see standard see standard --90 min HRB 90 min HRB 90 min HRB 90 HRB
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A519-06 (2012)* EN 10305-1:2010 GB/T 17396-1998 EN 10305-2:2010
Designation Grade 1030 Grade 1035 Grade 1040 Grade 1524 Grade 1030 Grade 1035 Grade 1040 Grade 1524 Grade 1035 C35E Grade 45 E355
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
211
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification ASME SA-513*
EN 10297-1:2003
Designation Grade 1035
UNS Steel No. No. G10350 ---
Grade 1040
G10400
Grade 1524 C35E
G15240 ----1.1181
---
E355 E355 26Mn5 E470
---------
1.0580 1.0580 1.1161 1.0536
JIS G 3445:2010 EN 10305-1:2010 EN 10297-1:2003
Symbol STKM17C C45E 38Mn6
-------
--1.1191 1.1127
---
1.0509
EN 10305-1:2010 E410 *: See "List of Standards" at the beginning of the chapter.
Heat Treatment MD
Other 90 min HRB
---
---
552
80
621
90
5
MD
90 min HRB
--t≤8 8 < t ≤ 20 20 < t ≤ 50 50 < t ≤ 80 ------t ≤ 16 16 < t ≤ 40 40 < t ≤ 65 65 < t ≤ 80 80 < t ≤ 100 d > 40 --t ≤ 16 16 < t ≤ 40 40 < t ≤ 80 ---
---------------------------------------
552 430 380 320 290 512 512 --470 430 ------480 --400 380 360 590
80 -------------------------------------
621 630 600 550 500 640 640 650 650 600 ------650 670 670 620 570 690
90 -------------------------------------
5 17 L; 15 T 19 L; 17 T 20 L; 18 T 20 L; 18 T 4 4 7 17 L; 15 T 17 L; 15 T 17 L; 15 T 17 L; 15 T 17 L; 15 T 10 L; 5 T 6 14 L; 12 T 15 L; 13 T 16 L; 14 T 12
MD QT QT QT QT C C LC AR AR AR AR AR AM, CF, or AHT LC N N N SR
90 min HRB --------see standard see standard see standard ------------see standard ------see standard
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10305-1:2010 EN 10305-2:2010 EN 10305-1:2010 EN 10297-1:2003
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. ----552 621 5 80 90
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
212
5.1 Carbon Steel Tubes for General and Structural Applications 5.1A Mechanical Properties of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification EN 10305-1:2010 EN 10297-1:2003
GB 18248-2000
Steel No. 1.1161 1.1181
E590K2
---
1.0644
C45E E410 Grade 37Mn
-------
1.1191 1.0509 ---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. mm in. MPa ksi MPa ksi ----700 ------t≤8 490 700 ------430 650 ------8 < t ≤ 20 370 630 ------20 < t ≤ 50 340 600 ------50 < t ≤ 80
Elongation % min. 4 14 L; 12 T 16 L; 14 T 17 L; 15 T 17 L; 15 T
Heat Treatment C QT QT QT QT
t ≤ 16
---
590
---
700
---
16 L; 14 T
QT
16 < t ≤ 40
---
540
---
650
---
16 L; 14 T
QT
40 < t ≤ 65
---
480
---
570
---
16 L; 14 T
QT
65 < t ≤ 80
---
455
---
520
---
16 L; 14 T
QT
80 < t ≤ 100
---
420
---
520
---
16 L; 14 T
QT
-------
-------
----630
-------
720 750 750 L
-------
4 4 16 L
C C Q+T
Other see standard --------L: 40 J at -20°C T: 27 J at -20°C L: 40 J at -20°C T: 27 J at -20°C L: 40 J at -20°C T: 27 J at -20°C L: 40 J at -20°C T: 27 J at -20°C L: 40 J at -20°C T: 27 J at -20°C see standard see standard L: 55 J @ RT
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10305-1:2010
26Mn5 C45E
UNS No. -----
Designation
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
213
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications
Designation
Download From http://bbs.infoeach.com
E155 E155 E155 Grade 1008 Grade 1008 R28 R28 R28 E190 E190 Grade 1010 Grade MT 1010 Grade 1010 E215 Symbol STK290 Symbol STKM11A Symbol SGP E195 E195 --E155 Symbol STAM290GA Symbol STAM290GB ASTM A513-15* Grade 1008 ASME SA-513* Grade 1008 ASTM A512-06 (2012)* Grade MT 1015 *: See "List of Standards" at the beginning of the chapter.
UNS No. ------G10080 G10080 ----------G10100 G10100 G10100 --------------------G10080 G10080 G10150
Steel No. 1.0033 1.0033 1.0033 ----------1.0031 1.0031 ------1.0212 ------1.0034 1.0034 --1.0033 -----------
C 0.11 0.11 0.11 0.10 0.10 0.10 0.13 0.13 0.10 0.10 0.08-0.13 0.05-0.15 0.08-0.13 0.10 --0.12 --0.15 0.15 0.18 0.11 0.12 0.12 0.10 0.10 0.10-0.20
Mn 0.70 0.70 0.70 0.50 0.50 0.30 0.60 0.60 0.70 0.70 0.30-0.60 0.30-0.60 0.30-0.60 0.70 --0.60 --0.70 0.70 0.60 0.70 0.60 0.60 0.50 0.50 0.30-0.60
Si 0.35 0.35 0.35 ----------0.35 0.35 ------0.05 --0.35 --0.35 0.35 --0.35 0.35 0.35 -------
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.045 0.045 ------0.025 0.025 ------0.025 0.025 ------0.035 0.035 ------0.035 0.035 ------0.040 0.040 ------0.050 0.050 ------0.050 0.050 ------0.045 0.045 ------0.025 0.025 ------0.035 0.035 ------0.04 0.045 ------0.035 0.035 ------0.025 0.025 ------0.050 0.050 ------0.040 0.040 ------0.040 0.040 ------0.025 0.025 ------0.025 0.025 ------0.035 0.035 ------0.045 0.045 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.04 0.045 -------
Others --Al 0.015 min. Al 0.015 min. ------------Al 0.015 min. ------Al 0.025 min ------Al 0.015 min. Al 0.015 min. ---------------
Download From http://bbs.infoeach.com
Specification EN 10296-1:2003 EN 10305-3:2010 EN 10305-2:2010 ASTM A513-15* ASME SA-513* ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 EN 10296-1:2003 EN 10305-3:2010 ASTM A513-15* ASTM A512-06 (2012)* ASME SA-513* EN 10305-1:2010 JIS G 3444:2010 JIS G 3445:2010 JIS G 3452:2014 EN 10305-3:2010 EN 10305-2:2010 SAE J526 NOV10 EN 10296-1:2003 JIS G 3472:2013
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
214
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Designation
Download From http://bbs.infoeach.com
E195 R28 Grade 1015 Grade 1015 E220 Grade 1010 Grade 1010 Grade A E220 E235 E235 E235 R33 R33 R33 TS 1 Grade 1015 Grade 1008 ASTM A519-06 (2012)* Grade 1020 ASME SA-513* Grade 1015 Grade 1008 ISO 3304:1985 R37 ISO 3305:1985 R37 ISO 3306:1985 R37 JIS G 3445:2010 Symbol STKM12A JIS G 3472:2013 Symbol STAM340G EN 10296-1:2003 E235 E260 EN 10305-3:2010 E260 ASTM A512-06 (2012)* Grade MT 1020 ASTM A513-15* Grade 1020 Grade 1021 ASME SA-513* Grade 1020 Grade 1021 *: See "List of Standards" at the beginning of the chapter.
UNS No. ----G10150 G10150 --G10100 G10100 K03000 ----------------G10150 G10080 G10200 G10150 G10080 ----------------G10200 G10200 G10210 G10200 G10210
Steel No. 1.0034 ------1.0215 ------1.0215 1.0308 1.0308 1.0308 ----------------------------1.0308 1.0220 1.0220 -----------
C 0.15 0.13 0.13-0.18 0.12-0.18 0.14 0.08-0.13 0.08-0.13 0.26 0.14 0.17 0.17 0.17 0.16 0.16 0.16 0.16 0.13-0.18 0.10 0.18-0.23 0.12-0.18 0.10 0.17 0.17 0.17 0.20 0.20 0.17 0.16 0.16 0.15-0.25 0.18-0.23 0.18-0.23 0.17-0.23 0.17-0.23
Mn 0.70 0.60 0.30-0.60 0.30-0.60 0.70 0.30-0.60 0.30-0.60 1.35 0.70 1.20 1.20 1.20 0.70 0.70 0.70 0.30-0.70 0.30-0.60 0.50 0.30-0.60 0.30-0.60 0.50 0.8 0.8 0.8 0.60 0.60 1.20 1.20 1.20 0.30-0.60 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90
Si 0.35 ------0.35 ------0.35 0.35 0.35 0.35 ------------------0.35 0.35 0.35 0.35 0.35 0.35 0.35 0.35 -----------
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.025 ------0.050 0.050 ------0.035 0.035 ------0.035 0.035 ------0.025 0.025 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.045 0.045 ------0.025 0.025 ------0.025 0.025 ------0.025 0.025 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.035 0.035 ------0.035 0.035 ------0.040 0.050 ------0.035 0.035 ------0.035 0.035 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.040 0.040 ------0.035 0.035 ------0.045 0.045 ------0.045 0.045 ------0.025 0.025 ------0.04 0.045 -----0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 -------
Others Al 0.015 min. ------Al 0.015 min. ----Cu 0.20 min --Al 0.015 min. Al 0.015 min. Al 0.015 min. --------------------------------Al 0.015 min. -----------
Download From http://bbs.infoeach.com
Specification EN 10305-3:2010 ISO 3306:1985 ASTM A513-15* ASME SA-513* EN 10305-3:2010 ASTM A513-15* ASME SA-513* ASTM A500-13 EN 10296-1:2003 EN 10305-3:2010 EN 10305-1:2010 EN 10305-2:2010 ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 ISO 2937:1974 ASTM A513-15*
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
215
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
EN 10296-1:2003
E275K2
ASTM A513-15* ASME SA-513* ASTM A519-06 (2012)* ASTM A512-06 (2012)* ASTM A519-06 (2012)* ASME SA-513*
Designation
Grade 1021 Grade 1021 Grade 1020 Grade MT 1025 Grade 1025 Grade 1025 Grade 1008 Grade 1010 Grade 1015 ASTM A513-15* Grade 1025 Grade 1008 Grade 1010 Grade 1015 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page
UNS No. ------G10200 ----------G10200 G10250 -----------
Steel No. ----1.0033 ----------1.0308 ------------1.0034
C 0.10 0.13 0.11 0.17-0.23 0.17 0.17 0.17 0.17 0.17 0.18-0.23 0.22-0.28 0.16 0.16 0.25 0.25 0.15
Mn 0.30 0.60 0.70 0.30-0.60 0.40-0.80 0.8 0.8 0.8 1.20 0.30-0.60 0.30-0.60 0.70 0.70 0.30-0.90 0.30-0.90 0.70
Si ----0.35 --0.35 0.35 0.35 0.35 0.35 --------0.35 0.35 0.35
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 ------0.050 0.050 ------0.025 0.025 ------0.035 0.035 ------0.045 0.045 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.030 0.035 ------0.035 0.035 ------0.040 0.050 ------0.050 0.050 ------0.050 0.050 ------0.040 0.040 ------0.040 0.040 ------0.025 0.025 -------
--G10210 G10210 G10200 G10250 G10250 G10250 G10080 G10100 G10150 G10250 G10080 G10100 G10150
1.0456
0.20
0.50-1.40
0.40
0.035
0.030
0.30
0.30
0.10
---------------------------
0.18-0.23 0.17-0.23 0.18-0.23 --0.22-0.28 0.22-0.28 0.10 0.08-0.13 0.12-0.18 0.22-0.28 0.10 0.08-0.13 0.13-0.18
0.60-0.90 0.60-0.90 0.30-0.60 --0.30-0.60 0.30-0.60 0.50 0.30-0.60 0.30-0.60 0.30-0.60 0.50 0.30-0.60 0.30-0.60
---------------------------
0.035 0.035 0.040 --0.040 0.035 0.035 0.035 0.035 0.035 0.035 0.035 0.035
0.035 0.035 0.050 --0.050 0.035 0.035 0.035 0.035 0.035 0.035 0.035 0.035
---------------------------
---------------------------
---------------------------
Others ----Al 0.015 min. ------------------------Al 0.015 min. Al 0.020 min; Cu 0.35; N 0.015; Nb 0.050; Ti 0.03; V 0.05 ---------------------------
Download From http://bbs.infoeach.com
R28 R28 E155 Grade 1020 TS 4 R37 R37 R37 E235 Grade 1020 Grade 1025 R33 R33 Symbol STC370 Symbol STKM13A E195
Download From http://bbs.infoeach.com
Specification ISO 3304:1985 ISO 3305:1985 EN 10305-2:2010 ASME SA-513* ISO 2937:1974 ISO 3304:1985 ISO 3305:1985 ISO 3306:1985 EN 10297-1:2003 ASTM A513-15* ASTM A519-06 (2012)* ISO 3304:1985 ISO 3305:1985 JIS G 3473:2013 JIS G 3445:2010 EN 10305-2:2010
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
216
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification EN 10305-1:2010 EN 10296-1:2003 EN 10305-1:2010 EN 10305-3:2010
E215 E275 E255 E275 E235 E275 E235 Symbol STAM390G Symbol STKM12B
UNS No. -------------------
Steel No. 1.0212 1.0225 1.0408 1.0225 1.0308 1.0225 1.0308 -----
C 0.10 0.21 0.21 0.21 0.17 0.21 0.17 0.25 0.20
Mn 0.70 1.40 0.40-1.10 1.40 1.20 1.40 1.20 0.30-0.90 0.60
Si 0.05 0.35 0.35 0.35 0.35 0.35 0.35 0.35 0.35
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.025 ------0.045 0.045 ------0.025 0.025 ------0.025 0.025 ------0.025 0.025 ------0.025 0.025 ------0.045 0.045 ------0.035 0.035 ------0.040 0.040 -------
Others Al 0.025 min ---Al 0.015 min. Al 0.015 min. Al 0.015 min. -------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10305-2:2010 EN 10296-1:2003 JIS G 3472:2013 JIS G 3445:2010
Designation
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
217
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification ISO 3304:1985
Designation
EN 10297-1:2003
E275K2
ISO 3305:1985
Download From http://bbs.infoeach.com
ISO 3306:1985
ISO 2937:1974 JIS G 3445:2010 ASTM A519-06 (2012)* ASME SA-513*
TS 9 Symbol STKM14A Grade 1035 Grade 1026 Grade 1030 Grade 1008 Grade 1010 Grade 1015 Grade 1020 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page.
Steel No. ----------------1.0033 ----------1.0225 1.0225 1.0225 1.0225 1.0237 1.0237
C 0.10 0.17 0.21 0.13 0.17 0.21 0.17 0.21 0.11 0.25 0.26 0.17-0.24 0.26 0.26 0.21 0.21 0.21 0.21 0.20 0.20
Mn 0.30 0.8 1.2 0.60 0.8 1.2 0.8 1.2 0.70 --1.35 0.35-0.65 --1.35 1.40 1.40 1.40 1.40 1.40 1.40
Si --0.35 0.35 --0.35 0.35 0.35 0.35 0.35 ----0.17-0.37 ----0.35 0.35 0.35 0.35 0.35 0.35
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.025 0.025 ------0.040 0.040 ------0.035 0.035 ------0.035 0.035 0.25 0.25 --0.035 0.035 ------0.035 0.035 ------0.045 0.045 ------0.030 0.035 ------0.025 0.025 ------0.025 0.025 ------0.045 0.045 ------0.025 0.025 -------
---
1.0456
0.20
0.50-1.40
0.40
0.030
0.030
0.30
0.30
0.10
----G10350 G10260 G10300 G10080 G10100 G10150 G10200
-------------------
0.21 0.30 0.32-0.38 0.22-0.28 0.27-0.34 0.10 0.08-0.13 0.12-0.18 0.17-0.23
0.40-1.20 0.30-1.00 0.60-0.90 0.60-0.90 0.60-0.90 0.50 0.30-0.60 0.30-0.60 0.30-0.60
0.35 0.35 ---------------
0.045 0.040 0.040 0.035 0.035 0.035 0.035 0.035 0.035
0.045 0.040 0.050 0.035 0.035 0.035 0.035 0.035 0.035
-------------------
-------------------
-------------------
Others ----------------Al 0.015 min. --Cu 0.20 min Cu 0.20 Cu 0.20 min Cu 0.20 min ----Al 0.015 min. Al 0.015 min. --Al 0.015 min. Al 0.020 min; Cu 0.35; N 0.015; Nb 0.05; Ti 0.03; V 0.05 -------------------
Download From http://bbs.infoeach.com
EN 10305-2:2010 JIS G 3444:2010 ASTM A500-13 GB/T 17396-1998 ASTM A501-14 ASTM A500-13 EN 10296-1:2003 EN 10297-1:2003 EN 10305-2:2010 EN 10305-3:2010 EN 10296-1:2003 EN 10305-3:2010
R28 R37 R44 R28 R37 R44 R37 R44 E155 Symbol STK400 Grade D Grade 20 Grade A Grade B E275 E275 E275 E275 E320 E320
UNS No. ------------------------K03000 K03000 -------------
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
218
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification ASTM A513-15*
UNS Steel No. No. G10260 --G10300 --G10080 --G10100 --G10150 --G10200 ------------1.0308
C 0.22-0.28 0.28-0.34 0.10 0.08-0.13 0.13-0.18 0.18-0.23 0.16 0.16 0.17
Mn 0.60-0.90 0.60-0.90 0.50 0.30-0.60 0.30-0.60 0.30-0.60 0.70 0.70 1.20
Si ----------------0.35
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.050 0.050 ------0.050 0.050 ------0.025 0.025 -------
Others ----------------Al 0.015 min.
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Designation Grade 1026 Grade 1030 Grade 1008 Grade 1010 Grade 1015 Grade 1020 ISO 3304:1985 R33 ISO 3305:1985 R33 EN 10305-1:2010 E235 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
219
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Designation
Download From http://bbs.infoeach.com
E195 Grade C Grade 1021 Grade 1021 C22E E215 Grade MT 1010 C35E E255 EN 10305-2:2010 E235 JIS G 3445:2010 Symbol STKM18A Symbol STKM13B JIS G 3472:2013 Symbol STAM440G JIS G 3473:2013 Symbol STC440 JIS G 3472:2013 Symbol STAM440H ASTM A519-06 (2012)* Grade 1045 Grade 1035 ASME SA-513* Grade 1035 Grade 1040 ASTM A519-06 (2012)* Grade 1020 ASME SA-513* Grade 1025 ASTM A512-06 (2012)* Grade MT 1030 Grade 1011 Grade 1110 ASTM A513-15* Grade 1035 Grade 1040 ASTM A513-15* Grade 1025 ISO 3304:1985 R37 R44 ISO 3305:1985 R37 R44 EN 10305-3:2010 E355 EN 10305-1:2010 E355 EN 10305-2:2010 E355 EN 10297-1:2003 E315 EN 10305-3:2010 E370 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page.
UNS No. --K02705 G10210 G10210 ----G10100 ----------------G10450 G10350 G10350 G10400 G10200 G10250 G10300 G10110 G11100 G10350 G10400 G10250 -------------------
Steel No. 1.0034 ------1.1151 1.0212 --1.1181 1.0408 1.0308 ------------------------------------------1.0580 1.0580 1.0580 1.0236 1.0261
C 0.15 0.23 0.18-0.23 0.17-0.23 0.17-0.24 0.10 0.05-0.15 0.32-0.39 0.21 0.17 0.18 0.25 0.25 0.25 0.25 0.43-0.50 0.32-0.38 0.31-0.38 0.36-0.44 0.18-0.23 0.22-0.28 ----0.08-0.13 0.32-0.38 0.37-0.44 0.22-0.28 0.17 0.21 0.17 0.21 0.22 0.22 0.22 0.21 0.21
Mn 0.70 1.35 0.60-0.90 0.60-0.90 0.40-0.70 0.70 0.30-0.60 0.50-0.80 0.40-1.10 1.20 1.50 0.30-0.90 0.30-0.90 0.30-0.90 0.30-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.30-0.60 0.30-0.60 ----0.30-0.60 0.60-0.90 0.60-0.90 0.30-0.60 0.8 1.2 0.8 1.2 1.60 1.60 1.60 1.50 1.60
Si 0.35 ------0.40 0.05 --0.40 0.35 0.35 0.55 0.35 0.35 0.35 0.35 ------------------------0.35 0.35 0.35 0.35 0.55 0.55 0.55 0.30 0.55
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.025 0.025 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 0.40 0.40 0.10 0.025 0.025 ------0.04 0.045 ------0.030 0.035 0.40 --0.10 0.025 0.025 ------0.025 0.025 ------0.040 0.040 ------0.040 0.040 ------0.035 0.035 ------0.040 0.040 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 --------------------------0.040 0.08-0.130 ------0.035 0.035 ------0.040 0.050 ------0.035 0.035 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.025 0.025 ------0.025 0.025 ------0.025 0.025 ------0.030 0.035 ------0.025 0.025 -------
Others Al 0.015 min. Cu 0.20 min ----Cr+Mo+Ni 0.63 Al 0.025 min --Cr+Mo+Ni 0.63 --Al 0.015 min. ------------------------------------------Al 0.020 min. Al 0.020 min. Al 0.020 min. --Al 0.020 min.
Download From http://bbs.infoeach.com
Specification EN 10305-2:2010 ASTM A500-13 ASTM A513-15* ASME SA-513* EN 10297-1:2003 EN 10305-1:2010 ASTM A512-06 (2012)* EN 10305-1:2010
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
220
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification EN 10296-1:2003 ASTM A595/A595M-14 ASTM A513-15*
Designation
Steel No. 1.0261 ----------------1.1181 --------------------------1.0308 -----------------------
C 0.21 0.15-0.25 0.32-0.38 0.19-0.25 0.37-0.44 0.31-0.38 0.18-0.25 0.36-0.44 0.10-0.20 0.32-0.39 0.13-0.18 --0.48-0.55 0.17-0.23 0.15-0.20 0.25-0.35 0.25 0.20 0.18-0.23 0.25 0.23 0.23 0.23 0.17 0.15-0.25 0.22-0.28 0.18-0.23 0.22-0.28 0.28-0.34 0.22-0.28 0.18-0.23 0.22-0.28 0.17-0.23 0.22-0.28 0.27-0.34
Mn 1.60 0.30-0.90 0.60-0.90 1.35-1.65 0.60-0.90 0.60-0.90 1.35-1.65 0.60-0.90 0.30-0.60 0.50-0.80 0.60-0.90 --0.60-0.90 0.60-0.90 0.60-0.90 0.30-1.00 0.30-0.90 0.60 0.60-0.90 0.30-0.90 1.6 1.6 1.6 1.20 0.40-1.35 0.60-0.90 0.30-0.60 0.30-0.60 0.60-0.90 0.30-0.60 0.30-0.60 0.60-0.90 0.30-0.60 0.30-0.60 0.60-0.90
Si 0.55 0.060 --------------0.40 ----------0.35 0.35 0.35 --0.35 0.55 0.55 0.55 0.35 0.060 ---------------------
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.045 0.045 ------0.035 0.035 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.04 0.045 ------0.030 0.035 0.40 --0.10 0.040 0.045 ----------------0.040 0.050 ------0.035 0.035 ------0.040 0.045 ------0.040 0.040 ------0.035 0.035 ------0.040 0.040 ------0.035 0.035 ------0.035 0.035 ------0.050 0.050 ------0.050 0.050 ------0.050 0.050 ------0.025 0.025 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.035 0.035 -------
Others --(Si+Al) 0.020 min --------------Cr+Mo+Ni 0.63 --------------------------Al 0.015 min. (Si+Al) 0.020 min ---------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
E370 Grade A Grade 1035 Grade 1524 Grade 1040 ASME SA-513* Grade 1035 Grade 1524 Grade 1040 ASTM A512-06 (2012)* Grade MT 1015 EN 10305-1:2010 C35E ASTM A512-06 (2012)* Grade 1016 Grade MT 1017 ASTM A519-06 (2012)* Grade 1050 ASME SA-513* Grade 1021 ASTM A512-06 (2012)* Grade 1018 JIS G 3445:2010 Symbol STKM15A JIS G 3472:2013 Symbol STAM470G JIS G 3445:2010 Symbol STKM12C ASTM A513-15* Grade 1021 JIS G 3472:2013 Symbol STAM470H ISO 3304:1985 R50 ISO 3305:1985 R50 ISO 3306:1985 R50 EN 10305-1:2010 E235 ASTM A595/A595M-14 Grade B ASTM A513-15* Grade 1026 Grade 1020 Grade 1025 Grade 1030 ASTM A519-06 (2012)* Grade 1025 ASTM A519-06 (2012)* Grade 1020 ASME SA-513* Grade 1026 Grade 1020 Grade 1025 Grade 1030 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page.
UNS No. --K02004 G10350 G15240 G10400 G10350 G15240 G10400 G10150 --G10160 G10170 G10500 G10210 G10180 ------G10210 ----------K02005 G10260 G10200 G10250 G10300 G10250 G10200 G10260 G10200 G10250 G10300
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
221
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification EN 10297-1:2003 EN 10296-1:2003 JIS G 3444:2010 JIS G 3445:2010
JIS G 3473:2013 ASTM A513-15* ASTM A519-06 (2012)* ASME SA-513* ASTM A519-06 (2012)* EN 10305-1:2010
E355 E355 Symbol STK490 Symbol STKM18B Symbol STKM19A TS 18 E235 E420 Grade MT 1020 Grade 1021 Grade 1021 Grade 1025 C22E Symbol STK500 Symbol STAM500G Symbol STKM14B Symbol STAM500H C45E Grade 35 Symbol STKM16A E275 Symbol STKM13C Symbol STKM18C Symbol STC510A Symbol STC510B Grade 1025 Grade 1026 Grade 1045 Grade 1025 Grade 1026 Grade 1025 Grade 1035 E255 E410
ISO 3304:1985 R44 ISO 3305:1985 R44 *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page.
UNS No. ----------------G10200 G10210 G10210 G10250 --------------------------G10250 G10260 G10450 G10250 G10260 G10250 G10350 ---
Steel No. 1.0580 1.0580 --------1.0308 1.0575 --------1.1151 --------1.1191 ----1.0225 ----------------------1.0408
C 0.22 0.22 0.18 0.18 0.25 0.23 0.17 0.16 0.15-0.25 0.18-0.23 0.17-0.23 0.22-0.28 0.17-0.24 0.24 0.30 0.30 0.30 0.42-0.55 0.32-0.40 0.35-0.45 0.21 0.25 0.18 0.25 0.18 0.22-0.28 0.22-0.28 0.43-0.50 0.22-0.28 0.22-0.28 0.22-0.28 0.32-0.38 0.21
Mn 1.60 1.60 1.65 1.50 1.50 0.80-1.50 1.20 1.70 0.30-0.60 0.60-0.90 0.60-0.90 0.30-0.60 0.40-0.70 0.30-1.30 0.30-1.00 0.30-1.00 0.30-1.00 0.50-0.80 0.50-0.80 0.40-1.00 1.40 0.30-0.90 1.50 0.30-0.90 1.50 0.30-0.60 0.60-0.90 0.60-0.90 0.30-0.60 0.60-0.90 0.30-0.60 0.60-0.90 0.40-1.10
Si 0.55 0.55 0.55 0.55 0.55 0.35 0.35 0.50 --------0.40 0.35 0.35 0.35 0.35 0.40 0.17-0.37 0.40 0.35 0.35 0.55 0.35 0.55 --------------0.35
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.030 0.035 ------0.045 0.045 ------0.035 0.035 ------0.040 0.040 ------0.040 0.040 ------0.045 0.045 ------0.025 0.025 ------0.025 0.025 ------0.04 0.045 ------0.035 0.035 ------0.035 0.035 ------0.040 0.045 ------0.035 0.035 0.40 0.40 0.10 0.040 0.040 ------0.035 0.035 ------0.040 0.040 ------0.035 0.035 ------0.030 0.035 0.40 --0.10 0.035 0.035 0.25 0.25 --0.040 0.040 ------0.025 0.025 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.035 0.035 ------0.035 0.035 ------0.040 0.050 ------0.035 0.035 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.025 0.025 -------
---
1.0509
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
---
---
---
-----
-----
0.21 0.21
1.2 1.2
0.35 0.35
0.050 0.050
0.050 0.050
-----
-----
-----
Others ------------Al 0.015 min. Al 0.020 min. --------Cr+Mo+Ni 0.63 --------Cr+Mo+Ni 0.63 Cu 0.20 --Al 0.015 min. ------------------------V 0.08-0.15; Al 0.010-0.060; Nb 0.07; Ti 0.05; (Nb+V) 0.20 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ISO 2937:1974 EN 10305-2:2010 EN 10305-3:2010 ASTM A512-06 (2012)* ASTM A513-15* ASME SA-513* ASTM A512-06 (2012)* EN 10297-1:2003 JIS G 3444:2010 JIS G 3472:2013 JIS G 3445:2010 JIS G 3472:2013 EN 10305-1:2010 GB/T 17396-1998 JIS G 3445:2010 EN 10305-2:2010 JIS G 3445:2010
Designation
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
222
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
EN 10305-1:2010
E410
JIS G 3445:2010
Designation
Symbol STKM14C Symbol STKM19C ASTM A513-15* Grade 1026 Grade 1030 Grade 1035 ASTM A519-06 (2012)* Grade 1050 ASTM A512-06 (2012)* Grade 1030 ASTM A519-06 (2012)* Grade 1045 ASME SA-513* Grade 1026 Grade 1030 Grade 1035 EN 10305-2:2010 E275 ASTM A519-06 (2012)* Grade 1050 EN 10305-1:2010 E255 E355 ASTM A513-15* Grade 1030 Grade 1035 Grade 1040 Grade 1524 JIS G 3445:2010 Symbol STKM15C *: See "List of Standards" at the beginning of the chapter. Note: This section continued on next page.
UNS No. --G10500 -------------------------
Steel No. ----1.1181 1.0580 --------1.0580 ------1.1181 ---
C 0.23 0.48-0.55 0.32-0.39 0.22 0.32-0.39 0.23 0.25 0.25 0.22 0.30 0.23 0.23 0.32-0.39 0.45-0.55
Mn 1.6 0.60-0.90 0.50-0.80 1.60 0.50-0.80 1.50 1.60 1.60 1.60 0.30-1.00 1.6 1.6 0.50-0.80 0.40-1.00
Si 0.55 --0.40 0.55 0.15-0.40 0.55 0.55 0.55 0.55 0.35 0.55 0.55 0.40 0.40
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.050 0.050 ------0.040 0.050 ------0.030 0.035 0.40 --0.10 0.025 0.025 ------0.035 0.035 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.045 0.045 ------0.035 0.035 ------0.050 0.050 ------0.050 0.050 ------0.035 0.035 0.40 0.40 0.10 0.040 0.040 -------
---
1.0509
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
---
---
---
--------G10260 --G10300 --G10350 --G10500 --G10300 --G10450 --G10260 --G10300 --G10350 ----1.0225 G10500 ----1.0408 --1.0580 G10300 --G10350 --G10400 --G15240 -------
0.30 0.25 0.22-0.28 0.28-0.34 0.32-0.38 0.48-0.55 0.28-0.34 0.43-0.50 0.22-0.28 0.27-0.34 0.31-0.38 0.21 0.48-0.55 0.21 0.22 0.28-0.34 0.32-0.38 0.37-0.44 0.19-0.25 0.25-0.35
0.30-1.00 1.50 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 0.60-0.90 1.40 0.60-0.90 0.40-1.10 1.60 0.60-0.90 0.60-0.90 0.60-0.90 1.35-1.65 0.30-1.00
0.35 0.55 ------------------0.35 --0.35 0.55 --------0.35
0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.035 0.035 0.035 0.025 0.040 0.025 0.025 0.035 0.035 0.040 0.040 0.040
0.040 0.040 0.035 0.035 0.035 0.050 0.045 0.050 0.035 0.035 0.035 0.025 0.050 0.025 0.025 0.035 0.035 0.050 0.050 0.040
-----------------------------------------
-----------------------------------------
-----------------------------------------
Others ----Cr+Mo+Ni 0.63 Al 0.020 min. ----Nb or V 0.15 Nb or V 0.15 --------Cr+Mo+Ni 0.63 --V 0.08-0.15; Al 0.010-0.060; Nb 0.07; Ti 0.05; (Nb+V) 0.20 ----------------------Al 0.015 min. ----Al 0.020 min. -----------
Download From http://bbs.infoeach.com
R50 Grade 1050 C35E E355 C 35 Symbol STK540 Symbol STKM20A Symbol STC540 E355 Symbol STAM540H R50 R50 C35E Symbol STKM17A
Download From http://bbs.infoeach.com
Specification ISO 3306:1985 ASTM A519-06 (2012)* EN 10305-1:2010 EN 10305-3:2010 ISO 2937:1974 JIS G 3444:2010 JIS G 3445:2010 JIS G 3473:2013 EN 10296-1:2003 JIS G 3472:2013 ISO 3304:1985 ISO 3305:1985 EN 10297-1:2003 JIS G 3445:2010
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
223
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification ASME SA-513*
UNS Steel No. No. G10300 --G10350 --G10400 --G15240 --G10350 ----1.1181 ------1.0580 -------------
C 0.27-0.34 0.31-0.38 0.36-0.44 0.18-0.25 0.32-0.38 0.32-0.39 0.42-0.50 0.22 0.12 0.25 0.25
Mn 0.60-0.90 0.60-0.90 0.60-0.90 1.35-1.65 0.60-0.90 0.50-0.80 0.50-0.80 1.60 2.00 0.30-0.90 1.50
Si ----------0.40 0.17-0.37 0.55 0.40 0.35 0.55
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.035 ------0.035 0.035 ------0.040 0.050 ------0.040 0.050 ------0.040 0.050 ------0.030 0.035 0.40 --0.10 0.035 0.035 0.25 0.25 --0.025 0.025 ------0.030 0.030 ------0.040 0.040 ------0.040 0.040 -------
EN 10297-1:2003
E420J2
---
1.0599
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
0.30
0.40
0.08
ISO 3304:1985 ISO 3305:1985
R50 R50
-----
-----
0.23 0.23
1.6 1.6
0.55 0.55
0.050 0.050
0.050 0.050
-----
-----
-----
EN 10305-1:2010
E410
---
1.0509
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
---
---
---
EN 10297-1:2003 JIS G 3445:2010 ASTM A513-15*
EN 10297-1:2003 EN 10305-1:2010 EN 10305-2:2010 EN 10305-1:2010
C45E Symbol STKM16C Grade 1035 Grade 1040 Grade 1524 Grade 1045 Grade 1035 Grade 1040 Grade 1524 C35E E355 E355 26Mn5
----G10350 G10400 G15240 G10450 G10350 G10400 G15240 ---------
1.1191 ----------------1.1181 1.0580 1.0580 1.1161
0.42-0.50 0.35-0.45 0.32-0.38 0.37-0.44 0.19-0.25 0.43-0.50 0.31-0.38 0.36-0.44 0.18-0.25 0.32-0.39 0.22 0.22 0.20-0.30
0.50-0.80 0.40-1.00 0.60-0.90 0.60-0.90 1.35-1.65 0.60-0.90 0.60-0.90 0.60-0.90 1.35-1.65 0.50-0.80 1.60 1.60 1.20-1.50
0.40 0.40 --------------0.40 0.55 0.55 0.40
0.035 0.040 0.035 0.040 0.040 0.040 0.035 0.040 0.040 0.035 0.025 0.025 0.030
0.035 0.040 0.035 0.050 0.050 0.050 0.035 0.050 0.050 0.035 0.025 0.025 0.035
0.40 ----------------0.40 -------
0.40 ----------------0.40 -------
0.10 ----------------0.10 -------
EN 10297-1:2003
E470
---
1.0536
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
---
---
---
JIS G 3445:2010 EN 10305-1:2010 EN 10297-1:2003
Symbol STKM17C C45E 38Mn6
-------
--1.1191 1.1127
0.45-0.55 0.42-0.55 0.34-0.42
0.40-1.00 0.50-0.80 1.40-1.65
0.40 0.40 0.15-0.35
0.040 0.030 0.035
0.040 0.035 0.035
--0.40 0.40
----0.40
--0.10 0.10
EN 10305-1:2010
E410
---
1.0509
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
---
---
---
ASTM A519-06 (2012)* ASME SA-513*
Others ----------Cr+Mo+Ni 0.63 Cu 0.20 Al 0.020 min. (Nb+V) 0.15; B 0.0002 ----Al 0.010 min; Cu 0.30; N 0.020; Nb 0.07; Ti 0.05; V 0.08-0.15; (Nb+V) 0.20 ----V 0.08-0.15; Al 0.010-0.060; Nb 0.07; Ti 0.05; (Nb+V) 0.20 Cr+Mo+Ni 0.63 ----------------Cr+Mo+Ni 0.63 Al 0.020 min. Al 0.020 min. --Al 0.010 min; N 0.020; Nb 0.07; V 0.08-0.15 --Cr+Mo+Ni 0.63 Cr+Mo+Ni 0.63 V 0.08-0.15; Al 0.010-0.060; Nb 0.07; Ti 0.05; (Nb+V) 0.20
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A519-06 (2012)* EN 10305-1:2010 GB/T 17396-1998 EN 10305-2:2010 JIS G 3474:2014 JIS G 3473:2013
Designation Grade 1030 Grade 1035 Grade 1040 Grade 1524 Grade 1035 C35E Grade 45 E355 Symbol STKT590 Symbol STC590A Symbol STC590B
*: See "List of Standards" at the beginning of the chapter. Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
224
5.1 Carbon Steel Tubes for General and Structural Applications 5.1B Chemical Composition of Carbon Steel Tubes for General and Structural Applications (Continued)
Specification EN 10305-1:2010 EN 10297-1:2003
GB 18248-2000
Steel No. 1.1161 1.1181
C 0.20-0.30 0.42-0.50
Mn 1.20-1.50 0.50-0.80
Si 0.40 0.40
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.030 0.035 ------0.035 0.035 0.40 0.40 0.10
E590K2
---
1.0644
0.16-0.22
1.30-1.70
0.10-0.50
0.030
0.035
0.30
0.40
0.08
Grade 37Mn
---
---
0.34-0.40
1.35-1.65
0.10-0.30
0.03
0.03
0.3
0.3
---
Si 0.15-0.35 0.40 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.35 0.40 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.15-0.35 0.40 0.40 0.15-0.35
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.035-0.050 0.20 0.25 0.20-0.30 0.025 0.035 --0.40 0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.040 0.040 0.80-1.10 --0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.30 0.035 0.035 0.80-1.15 --0.15-0.30 0.025 0.035 0.90-1.20 --0.15-0.30 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.040 0.040 0.80-1.10 --0.15-0.25 0.040 0.040 0.80-1.10 --0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.30 0.030 0.030 0.90-1.20 0.25 0.15-0.30 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.040 0.040 0.80-1.10 --0.15-0.25 0.040 0.040 0.80-1.10 --0.15-0.25 0.035 0.035 0.90-1.20 --0.15-0.30 0.025 0.035 0.90-1.20 --0.15-0.30 0.030 0.030 0.90-1.20 0.25 0.15-0.30
Others --Cr+Mo+Ni 0.63 Al 0.010 min; Cu 0.30; N 0.020; Nb 0.07; Ti 0.05; V 0.08-0.15; (Nb+V) 0.20 Cu 0.20; (P+S) 0.055
5.2 Alloy Steel Tubes for General and Structural Applications 5.2A Chemical Composition of Alloy Steel Tubes for General and Structural Applications
Specification ASTM A519-06 (2012)* EN 10305-1:2010 ASME SA-513* ASTM A513-15* ASTM A519-06 (2012)* EN 10297-1:2003
Designation Grade 4028 26Mo2 Grade 4130 Grade 4130 Grade 4130 25CrMo4 30CrMo4 EN 10305-1:2010 25CrMo4 JIS G 3441:2012 Symbol SCM418TK Symbol SCM420TK Symbol SCM430TK ASTM A519-06 (2012)* Grade 4135 Grade 4137 EN 10297-1:2003 34CrMo4 JIS G 3441:2012 Symbol SCM435TK ASME SA-513* Grade 4140 ASTM A513-15* Grade 4140 ASTM A519-06 (2012)* Grade 4140 Grade 4142 EN 10297-1:2003 42CrMo4 EN 10305-1:2010 42CrMo4 JIS G 3441:2012 Symbol SCM440TK *: See "List of Standards" at the beginning of the chapter.
UNS No. G40280 --G41300 G41300 G41300 ------------G41350 G41370 ----G41400 G41400 G41400 G41420 -------
Steel No. --1.5417 ------1.7218 1.7216 1.7218 ----------1.7220 ----------1.7225 1.7225 ---
C 0.25-0.30 0.22-0.29 0.28-0.33 0.28-0.33 0.28-0.33 0.22-0.29 0.27-0.34 0.22-0.29 0.16-0.21 0.18-0.23 0.28-0.33 0.32-0.39 0.35-0.40 0.30-0.37 0.33-0.38 0.38-0.43 0.38-0.43 0.38-0.43 0.40-0.45 0.38-0.45 0.38-0.45 0.38-0.43
Mn 0.70-0.90 1.50 0.40-0.60 0.40-0.60 0.40-0.60 0.60-0.90 0.35-0.60 0.60-0.90 0.60-0.85 0.60-0.85 0.60-0.85 0.65-0.95 0.70-0.90 0.60-0.90 0.60-0.85 0.75-1.00 0.75-1.00 0.75-1.00 0.75-1.00 0.60-0.90 0.60-0.90 0.60-0.85
Others Cu 0.35 --------------Cu 0.30 Cu 0.30 Cu 0.30 ------Cu 0.30 ------------Cu 0.30
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
26Mn5 C45E
UNS No. -----
Designation
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
225
5.2 Alloy Steel Tubes for General and Structural Applications 5.2B Mechanical Properties of Alloy Steel Tubes for General and Structural Applications UNS Steel No. No. G40280 ----1.5417
ASME SA-513*
Grade 4130
G41300
---
ASTM A513-15*
Grade 4130
G41300
---
ASTM A519-06 (2012)*
Grade 4130
G41300
---
EN 10297-1:2003
25CrMo4
---
1.7218
EN 10305-1:2010
JIS G 3441:2012
30CrMo4
25CrMo4
Symbol SCM418TK Symbol SCM420TK Symbol SCM430TK *: See "List of Standards" at the beginning of the chapter.
---
1.7216
Section Thickness/Diameter mm in. ---------
Yield Strength MPa ksi ----------------345 50 379 55 552 80 586 85 345 50 380 55 550 80 585 85 379 55 414 60 483 70 586 85 ----700 ---
Tensile Strength MPa ksi ----720 --670 ------483 70 496 72 621 90 655 95 480 70 495 72 620 90 655 95 517 75 621 90 621 90 724 105 ----900 ---
Elongation %, min. --4 6 --20 10 10 5 20 10 10 5 30 20 20 10 --12 L; 10 T
--------------------------t≤8
-----------------------------
8 < t ≤ 20
---
600
---
800
---
14 L; 12 T
20 < t ≤ 50
---
450
---
700
---
15 L; 13 T
50 < t ≤ 80
---
400
---
650
---
16 L; 14 T
t≤8
---
750
---
950
---
9 L; 7 T
8 < t ≤ 20
---
630
---
850
---
9 L; 7 T
20 < t ≤ 50
---
520
---
750
---
10 L; 8 T
50 < t ≤ 80
---
480
---
700
---
11 L; 9 T
---------------
---------------
--720 670 ---------
---------------
--4 6 ---------
---
1.7218
-----
-----
-------
-------
-------
-------
Heat Treatment A, N, SR, QT, or none C LC SR, or A, or N N AW MD SR MD N AW MD SR MD A N HR SR A QT
QT
A C LC SR, or A, or N AM, CF or A AM, CF or A AM, CF or A
Other --------100 max HRB 80 min HRB 87 min HRB 90 min HRB 100 max HRB 80 min HRB 87 min HRB 90 min HRB 81 HRB 89 HRB 89 HRB 95 HRB 212 HB L: 45 J @ 20°C L: 50 J @ 20°C T: 32 J @ 20°C see standard for impact data see standard for impact data L: 40 J @ 20°C L: 45 J @ 20°C T: 27 J @ 20°C see standard for impact data see standard for impact data 223 HB -------------
Download From http://bbs.infoeach.com
Designation Grade 4028 26Mo2
Download From http://bbs.infoeach.com
Specification ASTM A519-06 (2012)* EN 10305-1:2010
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
226
5.2 Alloy Steel Tubes for General and Structural Applications 5.2B Mechanical Properties of Alloy Steel Tubes for General and Structural Applications (Continued)
Specification ASTM A519-06 (2012)*
Designation Grade 4135 Grade 4137
EN 10297-1:2003
34CrMo4
UNS Steel No. No. G41350 --G41370 -----
1.7220
Section Thickness/Diameter mm in. ---------
Yield Strength MPa ksi ---------
Tensile Strength MPa ksi ---------
Elongation %, min. -----
Heat Treatment AM AM
---
800
---
1000
---
11 L; 9 T
QT
8 < t ≤ 20 20 < t ≤ 50 50 < t ≤ 80 -----
-------------------------------------
650 550 500 ----448 485 655 690 450 485 655 690 414 621 621 689 ---
----------65 70 95 100 65 70 95 100 60 90 90 100 ---
900 800 750 ----621 621 724 758 620 620 725 760 552 855 855 855 ---
----------90 90 105 110 90 90 105 110 80 120 120 120 ---
12 L; 10 T 14 L; 12 T 15 L; 13 T ----20 10 10 5 20 10 10 5 25 15 20 10 ---
A AM, CF or A N AW MD SR MD N AW MD SR MD A HR N SR A, N, SR, QT, or none
JIS G 3441:2012 ASME SA-513*
Symbol SCM435TK Grade 4140
--G41400
-----
ASTM A513-15*
Grade 4140
G41400
---
ASTM A519-06 (2012)*
Grade 4140
G41400
---
Grade 4142
G41420
---
---------------------------
---
1.7225
t≤8
---
900
---
1100
---
10 L; 8 T
QT
8 < t ≤ 20 20 < t ≤ 50 50 < t ≤ 80 -----------
-----------------
750 650 550 -----------
-----------------
1000 900 800 --720 670 -----
-----------------
11 L; 9 T 12 L; 10 T 13 L; 11 T --4 6 -----
A C LC SR, or A, or N AM, CF or A
EN 10297-1:2003
EN 10305-1:2010
42CrMo4
42CrMo4
JIS G 3441:2012 Symbol SCM440TK *: See "List of Standards" at the beginning of the chapter.
---
1.7225
---
---
223 HB --105 max HRB 85 min HRB 90 min HRB 90 min HRB 105 max HRB 85 min HRB 90 min HRB 90 min HRB 85 HRB 100 HRB 100 HRB 100 HRB --see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
t≤8
Other ----see standard for impact data
241 HB ---------
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
227
5.3 Stainless Steel Tubes for General and Structural Applications 5.3.1A Chemical Composition of Ferritic and Martensitic Stainless Steel Tubes for General and Structural Applications UNS No. S40500 S40500 S40500 --S40900 S40900 ------S41000 S41000 S41000 --------------------S43000 S43000 ----------------S43035
Steel No. ------1.4002 ----1.4512 1.4512 --------1.4006 --------------------------1.4016 1.4016 -----------
C 0.08 0.08 0.08 0.08 0.08 0.08 0.030 0.030 0.025 0.15 0.15 0.15 0.08-0.15 0.08 0.15 0.08 0.15 0.15 0.15 0.16-0.25 0.16-0.25 0.10 0.12 0.12 0.12 0.12 0.08 0.08 0.12 0.12 0.12 0.12 0.07
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.80 1.00 1.00 1.00 1.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.0 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.80 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00
Weight, % max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.030 11.5-14.5 0.50 --0.040 0.030 11.5-14.5 0.50 --0.040 0.030 11.5-14.5 0.50 --0.040 0.015 12.0-14.0 ----0.045 0.030 10.5-11.7 0.50 --0.045 0.030 10.5-11.7 0.50 --0.040 0.015 10.5-12.5 ----0.040 0.015 10.5-12.5 ----0.035 0.02 10.5-12.5 ----0.040 0.030 11.5-13.5 ----0.040 0.030 11.5-13.5 ----0.040 0.030 11.5-13.5 0.50 --0.040 0.015 11.5-13.5 0.75 --0.035 0.03 11.50-13.50 0.6 --0.035 0.03 11.50-13.50 0.6 --0.035 0.03 11.50-13.50 0.6 --0.035 0.03 11.50-13.50 0.6 --0.040 0.030 11.50-13.50 0.60 --0.040 0.030 11.50-13.50 0.60 --0.035 0.03 12.00-14.00 0.6 --0.040 0.030 12.00-14.00 0.60 --0.040 0.030 16-18 0.50 --0.040 0.030 16.0-18.0 ----0.040 0.030 16.0-18.0 ----0.040 0.030 16.0-18.0 0.50 --0.040 0.030 16.0-18.0 0.50 --0.040 0.015 16.0-18.0 ----0.040 0.015 16.0-18.0 ----0.035 0.03 16.00-18.00 0.6 --0.035 0.03 16.00-18.00 0.6 --0.040 0.030 16.00-18.00 0.60 --0.040 0.030 16.00-18.00 0.60 --0.040 0.030 17.00-19.00 0.50 ---
ASTM A268/A268M-10
Grade TP439
S43035
---
0.07
1.00
1.00
0.040
0.030
17.00-19.00
0.50
---
EN 10296-2:2005 C2:2007 EN 10297-2:2005 C1:2007
Grade X3CrTi17 Grade X3CrTi17
-----
1.4510 1.4510
0.05 0.05
1.00 1.00
1.00 1.00
0.040 0.040
0.015 0.015
16.0-18.0 16.0-18.0
-----
-----
Download From http://bbs.infoeach.com
GB/T 14975-2002 JIS G 3446:2012 GB/T 14975-2002 JIS G 3446:2012 AFNOR NF A 49-647:1979 ASME SA-268/SA-268M ASTM A268/A268M-10 ASTM A554-15 ASTM A511/A511M-15a EN 10296-2:2005 C2:2007 EN 10297-2:2005 C1:2007 GB/T 12770-2002 GB/T 14975-2002 JIS G 3446:2012
Others Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Ti 6xC to 0.75 Ti 6xC to 0.75 Ti 6x(C+N) to 0.65; N 0.030 Ti 6x(C+N) to 0.65 Ti 6xC to 0.75 ----------------------------------------------Al 0.15; N 0.04; Ti 0.20+4x(C+N) to 1.10 Al 0.15; N 0.04; Ti 0.20+4x(C+N) to 1.10 Ti 4x(C+N)+0.15 to 0.80 Ti 4x(C+N)+0.15 to 0.80
Download From http://bbs.infoeach.com
ASME SA-268/SA-268M
Designation Grade TP405 Grade TP405 Grade MT 405 Grade X6CrAl13 Grade TP409 Grade TP409 Grade X2CrTi12 Grade X2CrTi12 Grade 00Cr12Ti Grade TP410 Grade TP410 Grade MT 410 Grade X12Cr13 Grade 0Cr13 Grade 1Cr13 Grade 0Cr13 Grade 1Cr13 Symbol SUS410TKA Symbol SUS410TKC Grade 2Cr13 Symbol SUS420J1TKA TS Z 8 C 17 Grade TP430 Grade TP430 Grade MT-430 Grade MT 430 Grade X6Cr17 Grade X6Cr17 Grade 1Cr17 Grade 1Cr17 Symbol SUS430TKA Symbol SUS430TKC Grade TP439
Specification ASME SA-268/SA-268M ASTM A268/A268M-10 ASTM A511/A511M-15a EN 10297-2:2005 C1:2007 ASME SA-268/SA-268M ASTM A268/A268M-10 EN 10296-2:2005 C2:2007 EN 10297-2:2005 C1:2007 GB/T 12770-2002 ASME SA-268/SA-268M ASTM A268/A268M-10 ASTM A511/A511M-15a EN 10297-2:2005 C1:2007 GB/T 12770-2002
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
228
5.3 Stainless Steel Tubes for General and Structural Applications 5.3.1B Mechanical Properties of Ferritic and Martensitic Stainless Steel Tubes for General and Structural Applications UNS No. S40500
Steel No. ---
ASTM A268/A268M-10
Grade TP405
S40500
---
t ≥ 0.4
t ≥ 0.015
205
30
415
ASTM A511/A511M-15a*
Grade MT 405
S40500
---
---
---
210
30
EN 10297-2:2005 C1:2007 ASME SA-268/SA-268M
Grade X6CrAl13 Grade TP409
--1.4002 S40900 ---
--t ≥ 0.4
--t ≥ 0.015
210 170
ASTM A268/A268M-10
Grade TP409
S40900
---
t ≥ 0.4
t ≥ 0.015
EN 10296-2:2005 C2:2007 EN 10297-2:2005 C1:2007 GB/T 12770-2002
Grade X2CrTi12 Grade X2CrTi12 Grade 00Cr12Ti
-------
1.4512 1.4512 ---
t ≤ 30 -------
---------
*: See "List of Standards" at the beginning of the chapter.
Section Thickness/Diameter mm in. t ≥ 0.4 t ≥ 0.015
Yield Strength MPa ksi 205 30
Tensile Strength MPa ksi 415 60
Elongation %, min. 20
Heat Treatment HT
60
20
HT
415
60
20
A
--25
400 380
--55
17 L, 17 T 20
A HT
170
25
380
55
20
HT
210 210 -----
---------
380 380 365-460 365-460
---------
25 L, 23 T 25 L, 25 T --35
AW or A A A W
Other 207 max HB; 95 max HRB 207 HB; 95 max HRB 207 max HBW; 95 max HRB --207 max HB; 95 max HRB 207 max HB; 95 max HRB ---------
Download From http://bbs.infoeach.com
Designation Grade TP405
Download From http://bbs.infoeach.com
Specification ASME SA-268/SA-268M
Handbook of Comparative World Steel Standards
Chapter 5
Steel Tubes and Pipes
229
5.3 Stainless Steel Tubes for General and Structural Applications 5.3.1B Mechanical Properties of Ferritic and Martensitic Stainless Steel Tubes for General and Structural Applications (Continued) UNS No. S41000
Steel No. ---
ASTM A268/A268M-10
Grade TP410
S41000
---
t ≥ 0.4
t ≥ 0.015
205
30
415
ASTM A511/A511M-15a*
Grade MT 410
S41000
---
---
---
210
30
EN 10297-2:2005 C1:2007
Grade X12Cr13
---
1.4006
GB/T 12770-2002
Grade 0Cr13
---
---
Grade 1Cr13
---
---
Grade 0Cr13 Grade 1Cr13 Symbol SUS410TKA
-------
-------
Symbol SUS410TKC
---
---
----------------15 205 30 Grade F 348 S34800 --t ≤ 130 t≤5 205 30 t > 130 t>5 205 30 ASTM A403/A403M-15 Grade WP347 S34700 ------205 30 Grade CR347 S34700 ------205 30 ASTM A473-15 Type 347 S34700 ------205 30 ASTM A965/A965M-14 Grade F347 S34700 ------205 30 Grade F348 S34800 ------205 30 EN 10222-5:1999 X6 CrNiNb 18-10 --1.4550 t ≤ 450 --205 --ISO 9327-5:1999 Type X6CrNiNb18-10 ----t ≤ 450 --205 --JIS G 3214:1991 A1:2009 Symbol SUS F 347 ----t < 130 --205 --130 ≤ t ≤ 200 --205 --ASME SA-182/SA-182M Grade F 347H S34709 --t ≤ 130 t≤5 205 30 t > 130 t>5 205 30 ASTM A182/A182M-15 Grade F 347H S34709 --t ≤ 130 t≤5 205 30 t > 130 t>5 205 30 EN 10222-5:1999 X7 CrNiNb 18-10 --1.4912 t ≤ 450 --205 --ISO 9327-5:1999 Type X7CrNiNb18-10 ----t ≤ 450 --205 --JIS G 3214:1991 A1:2009 Symbol SUS F 347H ----t < 130 --205 --130 ≤ t ≤ 200 --205 --EN 10250-4:1999 X1NiCrMoCu25-20-5 --1.4539 t ≤ 250 --230 --ISO 9327-5:1999 Type X2NiCrMoCu25-20-5 ----t ≤ 160 --220 --Specification ASME SA-182/SA-182M
6.3.4A Chemical Composition of Precipitation-Hardening Stainless Steel Forgings
Specification ASME SA-705/SA-705M ASTM A705/A705M-13 EN 10250-4:1999 JIS G 3214:1991 A1:2009
Designation Type 630 Type 630 X5CrNiCuNb16-4 Symbol SUS F 630
UNS Steel No. No. S17400 --S17400 ----1.4542 -----
C 0.07 0.07 0.07 0.07
Mn 1.00 1.00 1.50 1.00
Si 1.00 1.00 0.70 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni 0.040 0.030 15.00-17.50 3.00-5.00 0.040 0.030 15.00-17.50 3.00-5.00 0.040 0.030 15.00-17.00 3.00-5.00 0.040 0.030 15.00-17.50 3.00-5.00
Mo ----0.60 ---
Others Cu 3.00-5.00; (Cb+Ta) 0.15-0.45 Cu 3.00-5.00; (Cb+Ta) 0.15-0.45 Cu 3.00-5.00; Nb 5xC to 0.45 Cu 3.00-5.00; Nb 0.15-0.45
Handbook of Comparative World Steel Standards
Chapter 6
Steel Forgings
380
6.3 Stainless Steel Forgings 6.3.4B Mechanical Properties of Precipitation-Hardening Stainless Steel Forgings
Specification ASME SA-705/SA-705M
EN 10250-4:1999
Type 630
X5CrNiCuNb16-4
JIS G 3214:1991 A1:2009 Symbol SUS F 630
UNS Steel No. No. S17400 ---
S17400
---
---
1.4542
---
---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min. --------------t ≤ 75 t≤3 1170 170 1310 190 10 L t ≤ 75 t≤3 1070 155 1170 170 10 L
Heat Treatment ST AH AH
t ≤ 200
t≤8
1000
145
1070
155
12 L
AH
t ≤ 200
t≤8
860
125
1000
145
13 L
AH
t ≤ 200
t≤8
795
115
965
140
14 L
AH
t ≤ 200
t≤8
725
105
930
135
16 L
AH
t ≤ 200
t≤8
520
75
795
115
18 L
AH
--t ≤ 75 t ≤ 75
--t≤3 t≤3
--1170 1070
--170 155
--1310 1170
--190 170
--10 L 10 L
ST AH AH
t ≤ 200
t≤8
1000
145
1070
155
12 L
AH
t ≤ 200
t≤8
860
125
1000
145
13 L
AH
t ≤ 200
t≤8
795
115
965
140
14 L
AH
t ≤ 200
t≤8
725
105
930
135
16 L
AH
t ≤ 200
t≤8
520
75
795
115
18 L
AH
--t ≤ 250 t ≤ 250 t ≤ 250 t ≤ 200 t ≤ 200 t ≤ 200
---------------
--720 1000 1150 860 795 725
---------------
1200 max. 930 1070 1300 1000 970 930
---------------
--15 L, 12 T 12 L, 10 T 8 L, 6 T 12 L 13 L 15 L
A PH PH PH HT HT HT
Other 363 max HB; 38 max HRC 388 min HB; 40 min HRC 375 min HB; 38 min HRC; L: 6.8 J @ RT 331 min HB; 35 min HRC; L: 20 J @ RT 311 min HB; 32 min HRC; L: 27 J @ RT 302 min HB; 31 min HRC; L: 34 J @ RT 277 min HB; 28 min HRC; L: 41 J @ RT 255 min HB; 24 min HRC; L: 75 J @ RT 363 max HB; 38 max HRC 388 min HB; 40 min HRC 375 min HB; 38 min HRC; L: 6.8 J @ RT 331 min HB; 35 min HRC; L: 20 J @ RT 311 min HB; 32 min HRC; L: 27 J @ RT 302 min HB; 31 min HRC; L: 34 J @ RT 277 min HB; 28 min HRC; L: 41 J @ RT 255 min HB; 24 min HRC; L: 75 J @ RT 360 max HB see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A705/A705M-13
Designation Type 630
--311 min HBW; 27 J @ RT 302 min HBW; 34 J @ RT 277 min HBW; 41 J @ RT
Handbook of Comparative World Steel Standards
Chapter 6
Steel Forgings
381
6.3 Stainless Steel Forgings 6.3.5A Chemical Composition of Duplex (Ferritic-Austenitic) Stainless Steel Forgings
Specification ASME SA-182/SA-182M ASTM A182/A182M-15 EN 10250-4:1999 ASME SA-182/SA-182M ASME SA-815/SA-815M
ASTM A815/A815M-14
EN 10222-5:1999 EN 10250-4:1999 ISO 9327-5:1999 ASME SA-182/SA-182M ASME SA-815/SA-815M ASTM A182/A182M-15 ASTM A815/A815M-14 EN 10222-5:1999 EN 10250-4:1999
UNS No. S31200 S31200 --S31803 S32205 S31803 S31803 S32205 S32205 S31803 S32205 S31803 S31803 S32205 S32205 ------S32750 S32750 S32750 S32750 S32750 S32750 -----
Steel No. ----1.4460 ------------------------1.4462 1.4462 --------------1.4410 1.4410
C 0.030 0.030 0.05 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 1.20 1.20 1.20 1.20 1.20 1.20 2.00 2.00
Si 1.00 1.00 1.00 1.00 1.00 1.0 1.0 1.00 1.00 1.00 1.00 1.0 1.0 1.00 1.00 1.00 1.00 1.00 0.80 0.8 0.8 0.80 0.8 0.8 1.00 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.045 0.030 24.0-26.0 5.5-6.5 1.20-2.00 0.045 0.030 24.0-26.0 5.5-6.5 1.20-2.00 0.035 0.030 25.00-28.00 4.50-6.50 1.30-2.00 0.030 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.030 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.030 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.030 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.030 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.030 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.030 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.030 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.030 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.030 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.030 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.030 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.035 0.015 21.00-23.00 4.50-6.50 2.50-3.50 0.035 0.015 21.00-23.00 4.50-6.50 2.50-3.50 0.035 0.020 21.00-23.00 4.50-6.50 2.50-3.50 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.035 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.035 0.015 24.00-26.00 6.00-8.00 3.00-4.50 0.035 0.015 24.00-26.00 6.00-8.00 3.00-4.50
Others N 0.14-0.20 N 0.14-0.20 N 0.05-0.20 N 0.08-0.20 N 0.14-0.20 N 0.08-0.20 N 0.08-0.20 N 0.14-0.20 N 0.14-0.20 N 0.08-0.20 N 0.14-0.20 N 0.08-0.20 N 0.08-0.20 N 0.14-0.20 N 0.14-0.20 N 0.10-0.22 N 0.10-0.22 N 0.08-0.20 Cu 0.50; N 0.24-0.32 Cu 0.5; N 0.24-0.32 Cu 0.5; N 0.24-0.32 Cu 0.50; N 0.24-0.32 Cu 0.5; N 0.24-0.32 Cu 0.5; N 0.24-0.32 N 0.20-0.35 N 0.20-0.35
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A182/A182M-15
Designation Grade F 50 Grade F 50 X3CrNiMoN27-5-2 Grade F 51 Grade F 60 Grade WPS31803 Grade CRS31803 Grade WPS32205 Grade CRS32205 Grade F 51 Grade F 60 Grade WPS31803 Grade CRS31803 Grade WPS32205 Grade CRS32205 X2 CrNiMoN 22-5-3 X2CrNiMoN22-5-3 Type X2CrNiMoN22-5-3 Grade F 53 Grade WPS32750 Grade CRS32750 Grade F 53 Grade WPS32750 Grade CRS32750 X2 CrNiMoN 25-7-4 X2CrNiMoN25-7-4
Handbook of Comparative World Steel Standards
Chapter 6
Steel Forgings
382
6.3 Stainless Steel Forgings 6.3.5A Chemical Composition of Duplex (Ferritic-Austenitic) Stainless Steel Forgings (Continued) UNS Steel No. No. S32760 ---
C 0.030
Mn 1.00
Si 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.030 0.010 24.0-26.0 6.0-8.0 3.0-4.0
ASME SA-815/SA-815M
Grade WPS32760
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
Grade CRS32760
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
ASTM A182/A182M-15
Grade F 55
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
ASTM A473-15
---
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
ASTM A815/A815M-14
Grade WPS32760
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
Grade CRS32760
S32760
---
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
---
1.4501
0.030
1.00
1.00
0.035
0.015
24.00-26.00
6.00-8.00
3.00-4.00
S32520 S32520 S32550
-------
0.030 0.030 0.04
1.50 1.50 1.50
0.80 0.80 1.00
0.035 0.035 0.040
0.020 0.020 0.030
24.0-26.0 24.0-26.0 24.0-27.0
5.5-8.0 5.5-8.0 4.5-6.5
3.0-5.0 3.0-5.0 2.9-3.9
-------
1.4507 1.4362 ---
0.030 0.030 0.030
2.00 2.00 2.50
0.70 1.00 1.00
0.035 0.035 0.035
0.015 0.015 0.020
24.00-26.00 22.00-24.00 22.00-24.00
5.50-7.50 3.50-5.50 3.50-5.00
2.70-4.00 0.10-0.60 0.60
EN 10250-4:1999
X2CrNiMoCuWN25-7-4
ASME SA-182/SA-182M ASTM A182/A182M-15 ASTM A473-15
Grade F 59 Grade F 59 ---
EN 10250-4:1999 EN 10250-4:1999 ISO 9327-5:1999
X2CrNiMoCuN25-6-3 X2CrNiN23-4 Type X2CrNiN23-4
Others Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-3.00; N 0.20-0.35 Cu 0.50-3.00; N 0.20-0.35 Cu 1.50-2.50; N 0.10-0.25; [Cr+(3.3xMo)+(16xN)] 0.40 min. Cu 1.00-2.50; N 0.15-0.30 Cu 0.10-0.60; N 0.05-0.20 Cu 0.60; N 0.05-0.20
Download From http://bbs.infoeach.com
Designation Grade F 55
Download From http://bbs.infoeach.com
Specification ASME SA-182/SA-182M
Handbook of Comparative World Steel Standards
Chapter 6
Steel Forgings
383
6.3 Stainless Steel Forgings 6.3.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steel Forgings
Specification ASME SA-182/SA-182M ASTM A182/A182M-15 EN 10250-4:1999 ASME SA-182/SA-182M ASME SA-815/SA-815M
ASTM A815/A815M-14
EN 10222-5:1999 EN 10250-4:1999 ISO 9327-5:1999 ASME SA-182/SA-182M ASME SA-815/SA-815M ASTM A182/A182M-15 ASTM A815/A815M-14 EN 10222-5:1999 EN 10250-4:1999
UNS No. S31200 S31200 --S31803 S32205 S31803 S31803 S32205 S32205 S31803 S32205 S31803 S31803 S32205 S32205 ------S32750
Grade WPS32750 Grade CRS32750 Grade F 53
S32750 S32750 S32750
Grade WPS32750 Grade CRS32750 X2 CrNiMoN 25-7-4 X2CrNiMoN25-7-4
S32750 S32750 -----
Steel Section Thickness/Diameter Yield Strength, min. No. mm in. MPa ksi ------450 65 ------450 65 1.4460 t ≤ 160 --460 --------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 ------450 65 1.4462 t ≤ 350 --450 --1.4462 t ≤ 350 --450 ----t ≤ 250 --450 ----t ≤ 50 t≤2 550 80 t > 50 t>2 515 75 ------550 80 ------550 80 --t ≤ 50 t≤2 550 80 t > 50 t>2 515 75 ------550 80 ------550 80 1.4410 t ≤ 160 --500 --1.4410 t ≤ 160 --530 ---
Tensile Strength, min. Elongation MPa ksi % min. 690-900 100-130 25 690-900 100-130 25 620-880 --20 L, 15 T 620 90 25 655 95 25 620 90 20.0 620 90 20.0 655 95 20.0 655 95 20.0 620 90 25 655 95 25 620 90 20.0 620 90 20.0 655 95 20.0 655 95 20.0 680-880 --30 L, 25 T 650-880 --25 L, 20 T 600-860 --25 L, 20 T 800 116 15 730 106 15 800-965 116-140 15.0 800-965 116-140 15.0 800 116 15 730 106 15 800-965 116-140 15.0 800-965 116-140 15.0 800-1000 --30 L, 25 T 730-930 --25 L, 20 T
Heat Treatment ST+Q ST+Q SA ST+Q ST+Q HT+Q or RC HT+Q or RC HT+Q HT+Q ST+Q ST+Q HT+Q or RC HT+Q or RC HT+Q HT+Q ST SA Q+T ST+Q ST+Q HT+Q or RC HT+Q or RC ST+Q ST+Q HT+Q or RC HT+Q or RC ST SA
Other ----see standard for impact data ----290 max HBW 290 max HBW 290 max HBW 290 max HBW ----290 max HBW 290 max HBW 290 max HBW 290 max HBW see standard for impact data see standard for impact data see standard for impact data 310 max HBW 310 max HBW 310 max HBW 310 max HBW 310 max HBW 310 max HBW 310 max HBW 310 max HBW see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A182/A182M-15
Designation Grade F 50 Grade F 50 X3CrNiMoN27-5-2 Grade F 51 Grade F 60 Grade WPS31803 Grade CRS31803 Grade WPS32205 Grade CRS32205 Grade F 51 Grade F 60 Grade WPS31803 Grade CRS31803 Grade WPS32205 Grade CRS32205 X2 CrNiMoN 22-5-3 X2CrNiMoN22-5-3 Type X2CrNiMoN22-5-3 Grade F 53
Handbook of Comparative World Steel Standards
Chapter 6
Steel Forgings
384
6.3 Stainless Steel Forgings 6.3.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steel Forgings (Continued)
Specification ASME SA-182/SA-182M ASME SA-815/SA-815M ASTM A182/A182M-15 ASTM A473-15 ASTM A815/A815M-14
UNS No. S32760 S32760 S32760 S32760 S32760 S32760 S32760 --S32520 S32520 S32550 -------
Steel Section Thickness/Diameter Yield Strength, min. No. mm in. MPa ksi ------550 80 ------550 80 ------550 80 ------550 80 ------550 80 ------550 80 ------550 80 1.4501 t ≤ 160 --530 --------550 80 ------550 80 ------550 80 1.4507 t ≤ 160 --500 --1.4362 t ≤ 160 --400 ----t ≤ 160 --400 ---
Tensile Strength, min. Elongation MPa ksi % min. 750-895 109-130 25 750-895 109-130 25.0 750-895 109-130 25.0 750-895 109-130 25 750 109 25 750-895 109-130 25.0 750-895 109-130 25.0 730-930 --25 L, 20 T 770 112 25 770 112 25 750 109 25.0 700-900 --25 L, 20 T 600-830 --25 L, 20 T 600-820 --25 L, 20 T
Heat Treatment ST+Q HT+Q or RC HT+Q or RC ST+Q A HT+Q or RC HT+Q or RC SA ST+Q ST+Q A+Q or RC SA SA Q+T
Other --270 max HBW 270 max HBW --290 max HB 270 max HBW 270 max HBW see standard for impact data ----290 max HB see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10250-4:1999 ASME SA-182/SA-182M ASTM A182/A182M-15 ASTM A473-15 EN 10250-4:1999 EN 10250-4:1999 ISO 9327-5:1999
Designation Grade F 55 Grade WPS32760 Grade CRS32760 Grade F 55 --Grade WPS32760 Grade CRS32760 X2CrNiMoCuWN25-7-4 Grade F 59 Grade F 59 --X2CrNiMoCuN25-6-3 X2CrNiN23-4 Type X2CrNiN23-4
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter
7 STEEL CASTINGS
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
386
Steel Castings – Heat Treatment Terms
Chapter 7
AFNOR Standards AFNOR NF A 32-058:1984
Cast Steels and White Cast Iron Resistant to Abrasion
ASME Standards ASME SA-216/SA-216M ASME SA-217/SA-217M ASME SA-351/SA-351 ASME SA-352/SA-352M ASME SA-487/SA-487M
Steel Castings, Carbon, Suitable for Fusion Welding for High-Temperature Service Steel Castings, Martensitic Stainless and Alloy, for Pressure-Containing Parts, Suitable for High-Temperature Service Castings, Austenitic, Austenitic-Ferritic (Duplex), for Pressure-Containing Parts Steel Castings, Ferritic and Martensitic, for Pressure-Containing Parts, Suitable for Low-Temperature Service Steel Castings Suitable for Pressure Service
ASTM Standards ASTM A27/A27M-13 ASTM A128/A128M-93 (2012) ASTM A148/A148 M-14 ASTM A216/A216M-14e1 ASTM A217/A217M-14 ASTM A297/A297M-14 ASTM A351/A351M-14 ASTM A352/A352M-06 (2012) ASTM A389/A389M-13 ASTM A447/A447M-11 ASTM A487/A487M-14 ASTM A608/A608M-14 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 ASTM A757/A757M-15 ASTM A958/A958M-14
Steel Castings, Carbon, for General Application Steel Castings, Austenitic Manganese Steel Castings, High Strength, for Structural Purposes Steel Castings, Carbon, Suitable for Fusion Welding, for High-Temperature Service Steel Castings, Martensitic Stainless and Alloy, for Pressure- Containing Parts, Suitable for HighTemperature Service Steel Castings, Iron-Chromium and Iron-Chromium-Nickel, Heat Resistant, for General Application Note: Mechanical properties data are supplementary requirements, provided for information only. Castings, Austenitic, for Pressure-Containing Parts Steel Castings, Ferritic and Martensitic, for Pressure-Containing Parts, Suitable for Low-Temperature Service Steel Castings, Alloy, Specially Heat-Treated, for Pressure-Containing Parts, Suitable for High-Temperature Service Steel Castings, Chromium-Nickel-Iron Alloy (25-12 Class), for High-Temperature Service Steel Castings Suitable for Pressure Service Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures Note: Mechanical properties data are supplementary requirements, provided for information only. Castings, Iron-Chromium, Iron-Chromium-Nickel, Corrosion Resistant, for General Application Note: Mechanical properties data are supplementary requirements, provided for information only. Castings, Iron-Chromium-Nickel, Corrosion Resistant, for Severe Service Note: Mechanical properties data are supplementary requirements, provided for information only. Steel Castings, Ferritic and Martensitic, for Pressure-Containing and Other Applications, for LowTemperature Service Steel Castings, Carbon and Alloy, with Tensile Requirements, Chemical Requirements Similar to Standard Wrought Grades
EN Standards EN 10213:2007 C1:2008 EN 10283:2010 EN 10293:2015 EN 10295:2002
Steel castings for pressure purposes Corrosion resistant steel castings Steel castings – Steel castings for general engineering uses Heat resistant steel castings
GB Standards GB/T 5680-1998 GB 7659-87 GB 11352-89 GB/T 14408-93 GB/T 16253-1996
Austenitic Manganese Steel Castings Carbon Steel Castings Suitable for Welded Structure Carbon Steel Castings for General Engineering Purposes Low Alloy Steel Castings for General Engineering and Structural Purposes Steel Castings for Pressure Purposes
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 7
Steel Castings - List of Standards
387
ISO Standards ISO 3755:1991 ISO 4991:1994 ISO 9477:1992 ISO 11972:1998 ISO 11973:1999 ISO 13521:1999 ISO 14737:2003
Cast Carbon Steels for General Engineering Purposes Steel Castings for Pressure Purposes High Strength Cast Steels for General Engineering and Structural Purposes Corrosion-Resistant Cast Steels for General Applications Heat-Resistant Cast Steels and Alloys for General Applications Austenitic Manganese Steel Castings Cast Non-Alloy and Low Alloy Steels for General Applications
JIS Standards JIS G 5101:1991 JIS G 5102:1991 JIS G 5111:1991 JIS G 5121:2003 JIS G 5122:2003 JIS G 5131:2008 JIS G 5151:1991 JIS G 5152:1991
Carbon steel castings Steel castings for welded structure High tensile strength carbon steel castings and low alloy steel castings for structural purposes Corrosion-resistant cast steels for general applications Heat-resistant cast steels and alloys for general applications High manganese steel castings Steel castings for high temperature and high pressure service Steel castings for low temperature and high pressure service
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
388
Steel Castings – Heat Treatment Terms
Chapter 7
Heat Treatment Terms Applicable to this Chapter Standard AFNOR NF A 32-058:1984 ASME SA-216/SA-216M ASME SA-217/SA-217M ASME SA-351/SA-351 ASME SA-352/SA-352M ASME SA-487/SA-487M ASTM A27/A27M-13 ASTM A128/A128M-93 (2012) ASTM A148/A148 M-14 ASTM A216/A216M-14e1 ASTM A217/A217M-14 ASTM A297/A297M-14 ASTM A351/A351M-14 ASTM A352/A352M-06 (2012) ASTM A389/A389M-13 ASTM A447/A447M-11 ASTM A487/A487M-14 ASTM A608/A608M-14 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 ASTM A757/A757M-15 ASTM A958/A958M-14 EN 10213:2007 C1:2008 EN 10283:2010 EN 10293:2015 EN 10295:2002 GB/T 5680-1998 GB 7659-87 GB 11352-89 GB/T 14408-93 GB/T 16253-1996 ISO 3755:1991 ISO 4991:1994 ISO 9477:1992 ISO 11972:1998 ISO 11973:1999 ISO 13521:1999 JIS G 5101:1991 JIS G 5102:1991 JIS G 5111:1991 JIS G 5121:2003 JIS G 5122:2003 JIS G 5131:2008 JIS G 5151:1991 JIS G 5152:1991
Heat Treatment Terms Q: water quenched A: annealed; N: normalized; N+T: normalized and tempered N+T: normalized and tempered Q: quenched; AC: as-cast N+T: normalized and tempered; Q+T: quenched and tempered N+T: normalized and tempered; Q+T: quenched and tempered FA: full annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered Q: quenched FA: full annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered A: annealed; N: normalized; N+T: normalized and tempered N+T: normalized and tempered AC: as cast; BA: by agreement Q: quenched; AC: as-cast N+T: normalized and tempered; Q+T: quenched and tempered N+T: normalized and tempered --N+T: normalized and tempered; Q+T: quenched and tempered --A: annealed; N+T: normalized and tempered; Q: quenched; AC: as-cast Q: quenched N+T: normalized and tempered; Q+T: quenched and tempered N: normalized; N+T: normalized and tempered; HT+Q+T: heat treated and quenched, then tempered N: normalized; Q+T: quenched and tempered; SA+Q: solution annealed and water quenched Q+T: quenched and tempered; SA+Q: solution annealed and water quenched N: normalized; Q+T: quenched and tempered A: annealed Q: water quenched A: annealed; N: normalized; N+T: normalized and tempered A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered; N+C(A)+T: normalized and rapid air cooled and tempered; ST: solution treated AM: at discretion of the manufacturer A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered; ST: solution treated AM: at discretion of the manufacturer N+T: normalized and tempered; ST+Q: solution treated and quenched A: annealed; AC: as-cast ST+Q: solution treated and water quenched A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered N+T: normalized and tempered; Q+T: quenched and tempered Q+T: quenched and tempered; ST: solution treated A: annealed; AC: as cast; BA: by agreement Q: water toughened A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered A: annealed; N: normalized; N+T: normalized and tempered; Q+T: quenched and tempered
Impact Testing Notes Applicable to this Chapter see standard for impact data: impact testing requirements are listed in the standard for multiple test temperatures.
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter 7
Steel Castings
389
7.1 Cast Carbon Steels 7.1.1A Mechanical Properties of Cast Carbon Steel for General and Structural Applications
Specification JIS G 5101:1991 EN 10293:2015 GB 11352-89 GB 7659-87 ISO 3755:1991
JIS G 5101:1991 GB 11352-89 GB 7659-87 ISO 3755:1991 ASTM A27/A27M-13 ASTM A958/A958M-14
EN 10293:2015
JIS G 5102:1991
UNS No. ------------------J03000 J02500 ----------J03001 J02003 J02508 J03012 ---------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. ----175 --360 --23 1.0420 t ≤ 300 200 --380-530 --25 1.0449 t ≤ 100 200 --380-530 --25 --t ≤ 100 200 --400 --25 ----200 --400 --25 --t ≤ 28 200 --400-550 --25 --t ≤ 28 200 --400-550 --25 ----205 --410 --21 ----235 --410 --21 ----205 30 415 60 24 ----205 30 415 60 22 ----225 --450 --19 --t ≤ 100 230 --450 --22 ----230 --450 --22 --t ≤ 28 230 --450-600 --22 --t ≤ 28 230 --450-600 --22 ----240 35 450 65 24 ----240 35 450 65 24 ----240 35 450 65 24 ----240 35 450 65 24 1.0446 t ≤ 300 240 --450-600 --22 1.0455 t ≤ 100 240 --450-600 --22 1.1131 t ≤ 50 240 --450-600 --24 ----255 --450 --20
Heat Treatment A, N, N+T or Q+T N N A, N, N+T or Q+T A, N or N+T AM AM A, N, N+T or Q+T A, N, N+T or Q+T FA, N, N+T or Q+T --A, N, N+T or Q+T A, N, N+T or Q+T A, N or N+T AM AM FA, N, N+T or Q+T N N N N N Q+T A, N, N+T or Q+T
Other --27 J @ RT 35 J @ RT 30 J @ RT see standard for impact data 30 J @ 23°C ± 5 45 J @ 23°C ± 5 --27 J @ 0°C ------25 J @ RT see standard for impact data 25 J @ 23°C ± 5 45 J @ 23°C ± 5 --------27 J @ RT 31 J @ RT see standard for impact data 27 J @ 0°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 5101:1991 JIS G 5102:1991 ASTM A27/A27M-13
Designation Class SC 360 GE200 GS200 Grade ZG 200-400 Grade ZG200-400H Grade 200-400 Grade 200-400W Class SC 410 Class SCW 410 Grade 60-30 [415-205] Grade U-60-30 [415-205] Class SC 450 Grade ZG 230-450 Grade ZG230-450H Grade 230-450 Grade 230-450W Grade 65-35 [450-240] Grade SC 1020, Class 65/35 Grade SC 1025, Class 65/35 Grade SC 1030, Class 65/35 GE240 GS240 G17Mn5 Class SCW 450
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
390
7.1 Cast Carbon Steels 7.1.1A Mechanical Properties of Cast Carbon Steel for General and Structural Applications (Continued)
Specification JIS G 5101:1991 GB/T 14408-93 ISO 3755:1991
Designation Class SC 480 Grade ZGD270-480 Grade 270-480 Grade 270-480W
ASTM A27/A27M-13
Grade 70-36 [485-250] Grade 70-40 [485-275] Grade SC 1020, Class 70/36 Grade SC 1025, Class 70/36 Grade SC 1030, Class 70/36 Grade SC 1040, Class 70/36 Grade ZG275-485H Grade ZG 270-500 Grade ZGD290-510 Grade ZGD345-570 Class SCC 3A Class SCMn 1A Grade 80-40 [550-275] Grade 80-50 [550-345] Grade SC 1030, Class 80/40 Grade SC 1030, Class 80/50 Grade SC 1040, Class 80/40 Grade SC 1040, Class 80/50 Grade SC 1045, Class 80/40 Grade SC 1045, Class 80/50 Grade 340-550
ASTM A958/A958M-14
GB 7659-87 GB 11352-89 GB/T 14408-93 JIS G 5111:1991 ASTM A148/A148 M-14 ASTM A958/A958M-14
ISO 3755:1991
Grade 340-550W JIS G 5102:1991
Class SCW 550
Steel No. -------
Section Yield Strength, min. Tensile Strength, min. Elongation Thickness, mm MPa ksi MPa ksi % min. --245 --480 --17 --270 --480 --18 t ≤ 28 270 --480-630 --18 28 < t ≤ 40 260 --500-650 --------t ≤ 28 270 --480-630 --18 28 < t ≤ 40 260 --500-650 ----------275 --480 --20 --1.6220 t ≤ 30 300 --480-620 --20 t ≤ 100 300 --500-650 --22 J03501 ----250 36 485 70 22 J02501 ----275 40 485 70 22 J02003 ----250 36 485 70 22 J02508 ----250 36 485 70 22 J03012 ----250 36 485 70 22 J04003 ----250 36 485 70 22 ------275 --485 --20 ----t ≤ 100 270 --500 --18 ------290 --510 --16 ------345 --570 --14 ------265 --520 --13 ------275 --540 --17 D50400 ----275 40 550 80 18 D50500 ----345 50 550 80 22 J03012 ----275 40 550 80 18 J03012 ----345 50 550 80 22 J04003 ----275 40 550 80 18 J04003 ----345 50 550 80 22 J04502 ----275 40 550 80 18 J04502 ----345 50 550 80 22 ----t ≤ 28 340 --550-700 --15 28 < t ≤ 40 300 --570-720 --------t ≤ 28 340 --550-700 --15 28 < t ≤ 40 300 --570-720 ----------355 --550 --18
Heat Treatment A, N, N+T or Q+T A, N, N+T or Q+T AM AM AM AM A, N, N+T or Q+T N Q+T FA, N, N+T or Q+T FA, N, N+T or Q+T N N N+T N+T A, N or N+T A, N, N+T or Q+T A, N, N+T or Q+T A, N, N+T or Q+T N+T N+T FA, N, N+T or Q+T FA, N, N+T or Q+T HT+Q+T HT+Q+T N+T N+T N+T N+T AM AM AM AM A, N, N+T or Q+T
Other ----22 J @ 23°C ± 5 --22 J @ 23°C ± 5 --27 J @ 0°C see standard for impact data ------------see standard for impact data 22 J @ RT ----143 min. HB 143 min. HB ----------------20 J @ 23°C ± 5 --20 J @ 23°C ± 5 --27 J @ 0°C
Download From http://bbs.infoeach.com
Class SCW 480 G20Mn5
Download From http://bbs.infoeach.com
JIS G 5102:1991 EN 10293:2015
UNS No. -------
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
391
7.1 Cast Carbon Steels 7.1.1A Mechanical Properties of Cast Carbon Steel for General and Structural Applications (Continued)
Specification GB 11352-89 JIS G 5111:1991
EN 10293:2015
GB/T 14408-93 ISO 9477:1992 ASTM A148/A148 M-14 ASTM A958/A958M-14 JIS G 5102:1991 GB 11352-89 JIS G 5111:1991
EN 10293:2015
Class SCC 5A Class SCMn 3A Class SCC 3B Class SCSiMn 2B Class SCMn 2B Grade ZGD410-620 Grade 410-620 Grade 90-60 [620-415] Grade SC 1040, Class 90/60 Grade SC 1045, Class 90/60 Class SCW 620 Grade ZG 340-640 Class SCMn 5A Class SCC 5B Class SCMn 3B G24Mn6
G28Mn6
UNS No. -----------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. --t ≤ 100 310 --570 --15 ----345 --590 --16 ----295 --590 --13 ----390 --590 --17 1.0558 t ≤ 30 300 --600-750 --15 30 < t ≤ 100 300 --520-670 --18 ------295 --620 --9 ------370 --640 --13 ------370 --620 --13 ------440 --640 --17 ------440 --640 --16 ------410 --620 --13 ------410 --620-770 --16 D50600 ----415 60 620 90 20 J04003 ----415 60 620 90 18 J04502 ----415 60 620 90 18 ------430 --620 --17 ----t ≤ 100 340 --640 --10 ------390 --690 --9 ------440 --690 --9 ------490 --690 --13 --1.1118 t ≤ 50 550 --700-800 --12 t ≤ 100 500 --650-800 --15 t ≤ 150 400 --600-800 --18 --1.1165 t ≤ 50 550 --700-850 --10 t ≤ 100 450 --600-750 --14 t ≤ 250 260 --520-670 --18
Heat Treatment A, N, N+T or Q+T N+T N+T Q+T N N N+T N+T Q+T Q+T Q+T A, N, N+T or Q+T AM FA, N, N+T or Q+T N+T N+T A, N, N+T or Q+T A, N, N+T or Q+T N+T Q+T Q+T Q+T Q+T Q+T Q+T Q+T N
Other 15 J @ RT 163 min. HB 163 min. HB 170 min. HB 27 J @ RT 31 J @ RT 163 min. HB 170 min. HB 183 min. HB 183 min. HB 183 min. HB --20 J @ 23°C ± 5 ------27 J @ 0°C 10 J @ RT 183 min. HB 201 min. HB 197 min. HB 27 J @ -20°C 27 J @ -30°C 27 J @ -30°C 31 J @ RT 35 J @ RT 27 J @ RT
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 5111:1991
Designation Grade ZG 310-570 Class SCMn 2A Class SCSiMn 2A Class SCMn 1B GE300
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
392
7.1 Cast Carbon Steels 7.1.1A Mechanical Properties of Cast Carbon Steel for General and Structural Applications (Continued)
Designation Grade ZGD535-720 Grade 540-720 Grade 105-85 [725-585] Grade SC 1045, Class 105/85 Class SCMn 5B Grade 115-95 [795-655] Grade 620-820 Grade ZGD650-830 Grade 130-115 [895-795] Grade ZGD730-910 Grade ZGD840-1030 Grade 840-1030 Grade 150-135 [1035-930]
UNS Steel No. No. --------D50850 --J04502 ------D50950 ----------D51150 --------------D51350 ---
Section Yield Strength, min. Tensile Strength, min. Elongation Thickness, mm MPa ksi MPa ksi % min. --535 --720 --12 --540 --720-870 --14 --585 85 725 105 17 --585 85 725 105 17 --540 --740 --9 --655 95 795 115 14 --620 --820-970 --11 --650 --830 --10 --795 115 895 130 11 --730 --910 --8 --840 --1030 --6 --840 --1030-1180 --7 --930 135 1035 150 7
Heat Treatment A, N, N+T or Q+T AM FA, N, N+T or Q+T N+T Q+T FA, N, N+T or Q+T AM A, N, N+T or Q+T FA, N, N+T or Q+T A, N, N+T or Q+T A, N, N+T or Q+T AM FA, N, N+T or Q+T
Other --20 J @ 23°C ± 5 ----212 min. HB --18 J @ 23°C ± 5 --------15 J @ 23°C ± 5 ---
7.1.1B Chemical Composition of Cast Carbon Steel for General and Structural Applications
Specification JIS G 5101:1991 EN 10293:2015
GB 11352-89 GB 7659-87 ISO 3755:1991
UNS No. -----
Steel No. --1.0420
C 0.20 ---
Mn -----
Si -----
GS200
---
1.0449
0.18
1.20
0.60
0.030
0.025
0.30
0.40
0.12
Grade ZG 200-400 Grade ZG200-400H Grade 200-400 Grade 200-400W
---------
---------
0.20 0.20 --0.25
0.80 0.80 --1.00
0.50 0.50 --0.60
0.04 0.04 0.035 0.035
0.04 0.04 0.035 0.035
0.35 0.30 -----
0.30 0.30 -----
0.20 0.15 -----
Designation Class SC 360 GE200
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 ------0.035 0.030 0.30 0.40 0.12
Others --V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.05; Cu 0.30 V 0.05; Cu 0.30 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification GB/T 14408-93 ISO 9477:1992 ASTM A148/A148 M-14 ASTM A958/A958M-14 JIS G 5111:1991 ASTM A148/A148 M-14 ISO 9477:1992 GB/T 14408-93 ASTM A148/A148 M-14 GB/T 14408-93 GB/T 14408-93 ISO 9477:1992 ASTM A148/A148 M-14
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
393
7.1 Cast Carbon Steels 7.1.1B Chemical Composition of Cast Carbon Steel for General and Structural Applications (Continued)
Specification JIS G 5101:1991 JIS G 5102:1991 ASTM A27/A27M-13
ASTM A27/A27M-13 ASTM A958/A958M-14
EN 10293:2015
JIS G 5102:1991 JIS G 5101:1991 GB/T 14408-93 ISO 3755:1991 JIS G 5102:1991 EN 10293:2015 ASTM A27/A27M-13 ASTM A958/A958M-14
GB 7659-87
UNS Steel No. No. C ----0.30 ----0.22 J03000 --0.30 J02500 --0.25 ----0.35 ----0.30 ----0.20 ----------0.25 J03001 --0.30 J02003 --0.18-0.23 J02508 --0.22-0.28 J03012 --0.28-0.34 --1.0446 ---
Si --0.80 0.80 0.80 --0.50 0.50 --0.60 0.80 0.30-0.60 0.30-0.60 0.30-0.60 ---
1.20
0.60
0.030
0.025
0.30
0.40
0.12
GS240
---
1.0455
G17Mn5
---
1.1131 0.15-0.20
1.00-1.60
0.60
0.020
0.020
0.30
0.40
0.12
Class SCW 450 Class SC 480 Grade ZGD270-480 Grade 270-480 Grade 270-480W Class SCW 480 G20Mn5
---------------
--0.22 --0.40 ----------0.25 --0.22 1.6220 0.17-0.23
1.50 ------1.20 1.50 1.00-1.60
0.80 ------0.60 0.80 0.60
0.040 0.040 0.040 0.035 0.035 0.040 0.020
0.040 0.040 0.040 0.035 0.035 0.040 0.020
----------0.50 0.30
----------0.50 0.80
------------0.12
0.70 1.20 0.40-0.80 0.40-0.80 0.50-0.90 0.50-0.90 1.20
0.80 0.80 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.50
0.035 0.035 0.040 0.040 0.040 0.040 0.04
0.035 0.035 0.040 0.040 0.040 0.040 0.04
------------0.30
------------0.30
------------0.15
Grade 70-36 [485-250] Grade 70-40 [485-275] Grade SC 1020, Class 70/36 Grade SC 1025, Class 70/36 Grade SC 1030, Class 70/36 Grade SC 1040, Class 70/36 Grade ZG275-485H
J03501 J02501 J02003 J02508 J03012 J04003 ---
---------------
0.23
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 ------0.040 0.040 ------0.035 0.035 ------0.035 0.035 ------0.040 0.040 ------0.04 0.04 0.35 0.30 0.20 0.04 0.04 0.30 0.30 0.15 0.035 0.035 ------0.035 0.035 ------0.035 0.035 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.035 0.030 0.30 0.40 0.12
Mn --1.50 0.60 0.75 --0.90 1.20 --1.20 0.70 0.40-0.80 0.40-0.80 0.50-0.90 ---
0.35 0.25 0.18-0.23 0.22-0.28 0.28-0.34 0.37-0.44 0.25
Others ----------V 0.05; Cu 0.30 V 0.05; Cu 0.30 ------------V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 ------------V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 ------------V 0.05; Cu 0.30
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 5101:1991 GB 11352-89 GB 7659-87 ISO 3755:1991
Designation Class SC 410 Class SCW 410 Grade 60-30 [415-205] Grade U-60-30 [415-205] Class SC 450 Grade ZG 230-450 Grade ZG230-450H Grade 230-450 Grade 230-450W Grade 65-35 [450-240] Grade SC 1020, Class 65/35 Grade SC 1025, Class 65/35 Grade SC 1030, Class 65/35 GE240
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
394
7.1 Cast Carbon Steels 7.1.1B Chemical Composition of Cast Carbon Steel for General and Structural Applications (Continued)
Specification GB 11352-89 GB/T 14408-93 JIS G 5111:1991 ASTM A148/A148 M-14
ISO 3755:1991 JIS G 5102:1991 GB 11352-89 JIS G 5111:1991
EN 10293:2015 JIS G 5111:1991
GB/T 14408-93 ISO 9477:1992 ASTM A148/A148 M-14 ASTM A958/A958M-14 JIS G 5102:1991 GB 11352-89
UNS Steel No. No. --------------------D50400 --D50500 --J03012 --J03012 --J04003 --J04003 --J04502 --J04502 --------------------------------1.0558
C 0.40 ----0.30-0.40 0.20-0.30 ----0.28-0.34 0.28-0.34 0.37-0.44 0.37-0.44 0.43-0.50 0.43-0.50 --0.25 0.22 0.50 0.25-0.35 0.25-0.35 0.20-0.30 ---
Mn 0.90 ----0.50-0.80 1.00-1.60 ----0.50-0.90 0.50-0.90 0.50-0.90 0.50-0.90 0.50-0.90 0.50-0.90 --1.50 1.50 0.90 1.00-1.60 0.90-1.20 1.00-1.60 ---
Si 0.50 ----0.30-0.60 0.30-0.60 ----0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 --0.60 0.80 0.60 0.30-0.60 0.50-0.80 0.30-0.60 ---
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.04 0.35 0.30 0.20 0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.05 0.06 ------0.05 0.06 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.035 0.035 ------0.035 0.035 ------0.040 0.040 0.50 2.50 0.30 0.04 0.04 0.35 0.30 0.20 0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.035 0.030 0.30 0.40 0.12
Class SCC 5A Class SCMn 3A Class SCC 3B Class SCSiMn 2B Class SCMn 2B Grade ZGD410-620 Grade 410-620 Grade 90-60 [620-415] Grade SC 1040, Class 90/60 Grade SC 1045, Class 90/60 Class SCW 620 Grade ZG 340-640
--------------D50600 J04003 J04502 -----
0.40-0.50 0.30-0.40 0.30-0.40 0.25-0.35 0.25-0.35 ------0.37-0.44 0.43-0.50 0.22 0.60
0.50-0.80 1.00-1.60 0.50-0.80 0.90-1.20 1.00-1.60 ------0.50-0.90 0.50-0.90 1.50 0.90
0.30-0.60 0.30-0.60 0.30-0.60 0.50-0.80 0.30-0.60 --0.60 --0.30-0.60 0.30-0.60 0.80 0.60
0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.05 0.040 0.040 0.040 0.04
-------------------------
0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.06 0.040 0.040 0.040 0.04
--------------------0.50 0.35
--------------------2.50 0.30
--------------------0.30 0.20
Others V 0.05; Cu 0.30 ----------------------------V 0.20 V 0.05; Cu 0.30 ------V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 --------------------V 0.20 V 0.05; Cu 0.30
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A958/A958M-14
Designation Grade ZG 270-500 Grade ZGD290-510 Grade ZGD345-570 Class SCC 3A Class SCMn 1A Grade 80-40 [550-275] Grade 80-50 [550-345] Grade SC 1030, Class 80/40 Grade SC 1030, Class 80/50 Grade SC 1040, Class 80/40 Grade SC 1040, Class 80/50 Grade SC 1045, Class 80/40 Grade SC 1045, Class 80/50 Grade 340-550 Grade 340-550W Class SCW 550 Grade ZG 310-570 Class SCMn 2A Class SCSiMn 2A Class SCMn 1B GE300
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
395
7.1 Cast Carbon Steels 7.1.1B Chemical Composition of Cast Carbon Steel for General and Structural Applications (Continued)
Specification JIS G 5111:1991
EN 10293:2015
Designation Class SCMn 5A Class SCC 5B Class SCMn 3B G24Mn6 G28Mn6 Grade ZGD535-720 Grade 540-720 Grade 105-85 [725-585] Grade SC 1045, Class 105/85 Class SCMn 5B Grade 115-95 [795-655] Grade 620-820 Grade ZGD650-830 Grade 130-115 [895-795] Grade ZGD730-910 Grade ZGD840-1030 Grade 840-1030 Grade 150-135 [1035-930]
------D50850 J04502 --D50950 ----D51150 ------D51350
Steel No. ------1.1118
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 ------0.040 0.040 ------0.040 0.040 ------0.020 0.015 0.30 0.40 0.12
C 0.40-0.50 0.40-0.50 0.30-0.40 0.20-0.25
Mn 1.00-1.60 0.50-0.80 1.00-1.60 1.50-1.80
Si 0.30-0.60 0.30-0.60 0.30-0.60 0.60
1.1165 0.25-0.32
1.20-1.80
0.60
0.035
0.030
0.30
0.40
0.12
------0.50-0.90 1.00-1.60 -----------------
--0.60 --0.30-0.60 0.30-0.60 --0.60 --------0.60 ---
0.040 0.035 0.05 0.040 0.040 0.05 0.035 0.040 0.05 0.035 0.035 0.035 0.05
0.040 0.035 0.06 0.040 0.040 0.06 0.035 0.040 0.06 0.035 0.035 0.035 0.06
---------------------------
---------------------------
---------------------------
---------------------------
------0.43-0.50 0.40-0.50 -----------------
Others ------V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 ---------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 14408-93 ISO 9477:1992 ASTM A148/A148 M-14 ASTM A958/A958M-14 JIS G 5111:1991 ASTM A148/A148 M-14 ISO 9477:1992 GB/T 14408-93 ASTM A148/A148 M-14 GB/T 14408-93 GB/T 14408-93 ISO 9477:1992 ASTM A148/A148 M-14
UNS No. ---------
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
396
7.1 Cast Carbon Steels 7.1.2A Mechanical Properties of Cast Carbon Steel for Pressure Purposes at High Temperatures
GB/T 16253-1996
Grade ZG240-450A Grade ZG240-450AG Grade ZG240-450B Grade ZG240-450BG Type C23-45A Type C23-45AH Type C23-45B Type C23-45BH Class SCPH 2 GP280GH
ISO 4991:1994
JIS G 5151:1991 EN 10213:2007 C1:2008 ASME SA-216/SA-216M ASTM A216/A216M-14e1 GB/T 16253-1996 ISO 4991:1994
Grade WCB Grade WCC Grade WCB Grade WCC Grade ZG280-520 Grade ZG280-520G Type C26-52 Type C26-52H
UNS Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. No. Thickness, mm MPa ksi MPa ksi % min. ------205 --410 --21 J02502 ----205 30 415-585 60-85 24 J02502 ----205 30 415-585 60-85 24 --1.0619 t ≤ 100 240 --420-600 --22 t ≤ 100 240 --420-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------240 --450-600 --22 ------245 --480 --19 --1.0625 t ≤ 100 280 --480-640 --22 t ≤ 100 280 --480-640 --22 J03002 ----250 36 485-655 70-95 22 J02503 ----275 40 485-655 70-95 22 J03002 ----250 36 485-655 70-95 22 J02503 ----275 40 485-655 70-95 22 ------280 --520-670 --18 ------280 --520-670 --18 ------280 --520-670 --18 ------280 --520-670 --18
Heat Treatment A, N, N+T or Q+T A, N or N+T A, N or N+T N Q+T A, N, N+T or Q+T N, N+T or Q+T A, N, N+T or Q+T N, N+T or Q+T A, N, N+T or Q+T N, N+T or Q+T A, N, N+T or Q+T N, N+T or Q+T A, N, N+T or Q+T N Q+T A, N or N+T A, N or N+T A, N or N+T A, N or N+T A, N, N+T or Q+T N, N+T or Q+T A, N, N+T or Q+T N, N+T or Q+T
Other ------27 J @ RT 40 J @ RT 27 J @ RT 27 J @ RT 45 J @ RT 45 J @ RT 27 J @ RT 27 J @ RT 45 J @ RT 45 J @ RT --27 J @ RT 35 J @ RT --------35 J @ RT 35 J @ RT 35 J @ RT 35 J @ RT
Download From http://bbs.infoeach.com
Designation Class SCPH 1 Grade WCA Grade WCA GP240GH
Download From http://bbs.infoeach.com
Specification JIS G 5151:1991 ASME SA-216/SA-216M ASTM A216/A216M-14e1 EN 10213:2007 C1:2008
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
397
7.1 Cast Carbon Steels 7.1.2B Chemical Composition of Cast Carbon Steel for Pressure Purposes at High Temperatures UNS Steel No. No. ----J02502 ---
C 0.25 0.25
Mn 0.70 0.70
Si 0.60 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 0.25 0.50 0.25 0.04 0.045 0.50 0.50 0.20
ASTM A216/A216M-14e1
Grade WCA
J02502
0.25
0.70
0.60
0.035
0.035
0.50
0.50
0.20
EN 10213:2007 C1:2008
GP240GH
---
0.50-1.20
0.60
0.030
0.020
0.30
0.40
0.12
Grade ZG240-450A Grade ZG240-450AG Grade ZG240-450B Grade ZG240-450BG Type C23-45A Type C23-45AH
-------------
-------------
0.25 0.25 0.20 0.20 0.25 0.25
1.20 1.20 1.00-1.60 1.00-1.60 1.20 1.20
0.60 0.60 0.60 0.60 0.60 0.60
0.035 0.035 0.035 0.035 0.035 0.035
0.035 0.035 0.035 0.035 0.035 0.035
0.40 0.40 0.40 0.40 --0.40
0.40 0.40 0.40 0.40 --0.40
0.15 0.15 0.15 0.15 --0.15
Type C23-45B
---
---
0.20
1.00-1.60
0.60
0.035
0.035
0.40
0.40
0.15
Type C23-45BH
---
---
0.20
1.00-1.60
0.60
0.035
0.035
0.40
0.40
0.15
JIS G 5151:1991 EN 10213:2007 C1:2008
Class SCPH 2 GP280GH
-----
1.00 0.80-1.20
0.60 0.60
0.040 0.030
0.040 0.020
0.25 0.30
0.50 0.40
0.25 0.12
ASME SA-216/SA-216M
Grade WCB
J03002
---
0.30
1.00
0.60
0.04
0.045
0.50
0.50
0.20
Grade WCC
J02503
---
0.25
1.20
0.60
0.04
0.045
0.50
0.50
0.20
Grade WCB
J03002
---
0.30
1.00
0.60
0.035
0.035
0.50
0.50
0.20
Grade WCC
J02503
---
0.25
1.20
0.60
0.035
0.035
0.50
0.50
0.20
Grade ZG280-520 Grade ZG280-520G Type C26-52
-------
-------
0.25 0.25 0.25
1.20 1.20 1.20
0.60 0.60 0.60
0.035 0.035 0.035
0.035 0.035 0.035
0.40 0.40 0.40
0.40 0.40 0.40
0.15 0.15 0.15
Type C26-52H
---
---
0.25
1.20
0.60
0.035
0.035
0.40
0.40
0.15
GB/T 16253-1996
ISO 4991:1994
ASTM A216/A216M-14e1
GB/T 16253-1996 ISO 4991:1994
---
1.0619 0.18-0.23
--0.30 1.0625 0.18-0.25
Others Cu 0.50; (Cu+Ni+Cr+Mo) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.40 V 0.03; Cu 0.40 V 0.03; Cu 0.40 V 0.03; Cu 0.40 --(Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40 (Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40 (Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40 Cu 0.50; (Cu+Ni+Cr+Mo) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.40 V 0.03; Cu 0.40 (Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40 (Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40
Download From http://bbs.infoeach.com
Designation Class SCPH 1 Grade WCA
Download From http://bbs.infoeach.com
Specification JIS G 5151:1991 ASME SA-216/SA-216M
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
398
7.1 Cast Carbon Steels 7.1.3A Mechanical Properties of Cast Carbon Steel for Pressure Purposes at Low Temperatures
Specification ASME SA-352/SA-352M
GB/T 16253-1996 ISO 4991:1994 JIS G 5152:1991
Grade ZG240-450BD Grade ZG280-520D Type C23-45BL Type C26-52L Class SCPL 1
UNS Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. No. Thickness, mm MPa ksi MPa ksi % min. J02504 ----205 30.0 415-585 60.0-85.0 24 J03003 ----240 35.0 450-620 65.0-90.0 24 J02505 ----275 40.0 485-655 70.0-95.0 22 J02504 ----205 30.0 415-585 60.0-85.0 24 J03003 ----240 35.0 450-620 65.0-90.0 24 J02505 ----275 40.0 485-655 70.0-95.0 22 J03002 ----240 35 450 65 24 J02503 ----275 40 485 70 22 --1.1131 t ≤ 50 240 --450-600 --24 --1.6220 t ≤ 30 300 --480-620 --20 t ≤ 100 300 --500-650 --22 ------240 --450-600 --22 ------280 --520-670 --18 ------240 --450-600 --22 ------280 --520-670 --18 ------245 --450 --21
Heat Treatment N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T Q+T Q+T Q+T N Q+T N, N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T A, N, N+T or Q+T
Other 18 J @ -32°C 18 J @ -46°C 20 J @ -46°C 18 J @ -32°C 18 J @ -46°C 20 J @ -46°C L: 17 J @ -46°C L: 20 J @ -46°C 27 J @ -40°C 27 J @ -30°C 27 J @ -40°C 27 J @ -40°C 27 J @ -35°C 27 J @ -40°C 27 J @ -35°C see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Designation Grade LCA Grade LCB Grade LCC ASTM A352/A352M-06 (2012) Grade LCA Grade LCB Grade LCC ASTM A757/A757M-15 Grade A1Q Grade A2Q EN 10213:2007 C1:2008 G17Mn5 G20Mn5
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
399
7.1 Cast Carbon Steels 7.1.3B Chemical Composition of Cast Carbon Steel for Pressure Purposes at Low Temperatures UNS Steel No. No. J02504 --J03003 ---
C 0.25 0.30
Mn 0.70 1.00
Si 0.60 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.045 0.50 0.50 0.20 0.04 0.045 0.50 0.50 0.20
Grade LCC
J02505
---
0.25
1.20
0.60
0.04
0.045
0.50
0.50
0.20
ASTM A352/A352M-06 (2012) Grade LCA Grade LCB
J02504 J03003
-----
0.25 0.30
0.70 1.00
0.60 0.60
0.04 0.04
0.045 0.045
0.50 0.50
0.50 0.50
0.20 0.20
Grade LCC
J02505
---
0.25
1.20
0.60
0.04
0.045
0.50
0.50
0.20
Grade A1Q
J03002
---
0.30
1.00
0.60
0.025
0.025
0.40
0.50
0.25
Grade A2Q
J02503
---
0.25
1.20
0.60
0.025
0.025
0.40
0.50
0.25
Download From http://bbs.infoeach.com
ASTM A757/A757M-15
EN 10213:2007 C1:2008
GB/T 16253-1996 ISO 4991:1994
JIS G 5152:1991
G17Mn5
---
1.1131 0.15-0.20
1.00-1.60
0.60
0.020
0.020
0.30
0.40
0.12
G20Mn5 Grade ZG240-450BD Grade ZG280-520D Type C23-45BL
---------
1.6220 0.17-0.23 --0.20 --0.25 --0.20
1.00-1.60 1.00-1.60 1.20 1.00-1.60
0.60 0.60 0.60 0.60
0.020 0.030 0.030 0.030
0.020 0.030 0.030 0.030
0.30 0.40 0.40 0.40
0.80 0.40 0.40 0.40
0.12 0.15 0.15 0.15
Type C26-52L
---
---
0.25
1.20
0.60
0.030
0.030
0.40
0.40
0.15
Class SCPL 1
---
---
0.30
1.00
0.60
0.040
0.040
0.25
0.50
---
Others V 0.03; Cu 0.30; (Cr+Ni+V) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+V) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.30; (Cr+Ni+Mo+V+Cu) 1.00 V 0.03; Cu 0.50; (V+Cr+Ni+Mo+Cu+P+S) 1.00 V 0.03; Cu 0.50; (V+Cr+Ni+Mo+Cu+P+S) 1.00 V 0.03; Cu 0.30; (Cr+Mo+Ni+V+Cu) 1.00 V 0.03; Cu 0.30 V 0.03; Cu 0.40 V 0.03; Cu 0.40 (Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40 (Cr+Mo+Ni+V+Cu) 1.00; V 0.03; Cu 0.40 Cu 0.50; (Cr+Ni+Cu) 1.00
Download From http://bbs.infoeach.com
Designation Grade LCA Grade LCB
Specification ASME SA-352/SA-352M
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
400
7.2 Cast Manganese Steels 7.2A Chemical Composition of Cast Manganese Steels
Specification AFNOR NF A 32-058:1984 ASTM A128/A128M-93 (2012) ISO 13521:1999 AFNOR NF A 32-058:1984
Designation Grade Z 100 MD 6 1-M Grade F Grade GX120MnMo7-1 Grade Z 120 M 12-M
C 0.8-1.2 1.05-1.35 1.05-1.35 1.1-1.4
Mn 5-7 6.0-8.0 6.00-8.00 11-14
Si 1 1.00 0.30-0.90 1
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.08 0.03 ----0.8-1.2 0.07 ------0.9-1.2 0.060 0.045 ----0.90-1.20 0.08 0.03 -------
J91109 J91119 J91129 J91139 J91149 ------------------J91309 --------J91459 ----J91249 ----J91339 -------
1.05-1.35 0.9-1.05 1.05-1.2 1.12-1.28 1.2-1.35 1.00-1.45 0.90-1.35 0.95-1.35 0.90-1.05 1.05-1.35 0.90-1.30 0.90-1.20 0.90-1.20 1.1-1.4 1.05-1.35 0.90-1.30 1.05-1.35 0.90-1.30 0.7-1.3 0.7-1.3 1.05-1.35 0.8-1.3 0.7-1.3 0.75-1.30 0.75-1.35 1.05-1.45 0.70-1.00 1.1-1.4 1.05-1.35
11.0 min. 11.5-14.0 11.5-14.0 11.5-14.0 11.5-14.0 11.00-14.00 11.00-14.00 11.00-14.00 11.00-14.00 11.00-14.00 11.00-14.00 11.00-14.00 11.00-14.00 11-14 11.5-14.0 11.00-14.00 11.00-14.00 11.00-14.00 12-15 11.5-14.0 11.00-14.00 11-14 11.5-14.0 11.00-14.00 11.00-14.00 11.5-14.0 13.00-15.00 16-18 16.00-19.00
1.00 1.00 1.00 1.00 1.00 0.30-1.00 0.30-1.00 0.30-0.80 0.30-0.90 0.30-0.90 --0.80 0.30-0.80 1 1.00 0.30-0.80 0.30-0.90 0.80 1 1.00 0.30-0.90 1 1.00 0.30-1.00 0.30-0.90 1.00 0.30-0.60 1 0.30-0.90
0.07 0.07 0.07 0.07 0.07 0.090 0.070 0.070 0.060 0.060 0.100 0.070 0.050 0.08 0.07 0.070 0.060 0.070 0.08 0.07 0.060 0.08 0.07 0.070 0.060 0.07 0.070 0.08 0.060
-----------------------------------------------------------
----------0.040 0.040 0.035 0.045 0.045 0.050 0.040 0.035 0.03 --0.040 0.045 0.040 0.03 --0.045 0.03 --0.040 0.045 --0.045 0.03 0.045
--------------------------1-2.5 1.5-2.5 1.50-2.50 1.50-2.50 1.50-2.50 ------------------1.8-2.3 1.50-2.50
------------------------------------2-5 3.0-4.0 3.00-4.00 -----------------
------------------------------------------0.8-1.2 0.9-1.2 0.90-1.20 0.90-1.20 1.8-2.1 1.00-1.80 -----
Others ------[(Mn-2)/10] Cmax.; C (Mn/10)max. -----------------------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A128/A128M-93 (2012) Grade A Grade B-1 Grade B-2 Grade B-3 Grade B-4 GB/T 5680-1998 Grade ZGMn13-1 Grade ZGMn13-2 Grade ZGMn13-3 ISO 13521:1999 Grade GX100Mn13 Grade GX120Mn13 JIS G 5131:2008 Class SCMnH 1 Class SCMnH 2 Class SCMnH 3 AFNOR NF A 32-058:1984 Grade Z 120 MC 12-M ASTM A128/A128M-93 (2012) Grade C GB/T 5680-1998 Grade ZGMn13-4 ISO 13521:1999 Grade GX120MnCr13-2 JIS G 5131:2008 Class SCMnH 11 AFNOR NF A 32-058:1984 Grade Z 100 MN 13 4-M ASTM A128/A128M-93 (2012) Grade D ISO 13521:1999 Grade GX120MnNi13-3 AFNOR NF A 32-058:1984 Grade Z 110 MD 12 1-M ASTM A128/A128M-93 (2012) Grade E-1 GB/T 5680-1998 Grade ZGMn13-5 ISO 13521:1999 Grade GX110MnMo13-1 ASTM A128/A128M-93 (2012) Grade E-2 ISO 13521:1999 Grade GX90MnMo14 AFNOR NF A 32-058:1984 Grade Z 120MC 17 2-M ISO 13521:1999 Grade GX120MnCr17-2
UNS Steel No. No. ----J91340 -----------
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
401
7.2 Cast Manganese Steels 7.2B Mechanical Properties of Cast Manganese Steels
Specification AFNOR NF A 32-058:1984 ASTM A128/A128M-93 (2012) ISO 13521:1999 AFNOR NF A 32-058:1984 ASTM A128/A128M-93 (2012)
ISO 13521:1999 JIS G 5131:2008
AFNOR NF A 32-058:1984 ASTM A128/A128M-93 (2012) GB/T 5680-1998 ISO 13521:1999 JIS G 5131:2008 AFNOR NF A 32-058:1984 ASTM A128/A128M-93 (2012) ISO 13521:1999 AFNOR NF A 32-058:1984 ASTM A128/A128M-93 (2012) ISO 13521:1999 ASTM A128/A128M-93 (2012) ISO 13521:1999 AFNOR NF A 32-058:1984 ISO 13521:1999
UNS Steel No. No. ----J91340 ----------J91109 --J91119 --J91129 --J91139 --J91149 --------------------------------------J91309 ------------------J91459 ----------J91249 ------J91339 ---------------
Section Yield Strength, min. Tensile Strength, min. Elongation Thickness, mm MPa ksi MPa ksi % min. t ≤ 100 ----------------------------------t ≤ 200 ----------------------------------------------------------------------------635 --20 ------685 --25 ------735 --30 ------------------------------------------740 --35 ------740 --35 t ≤ 100 ------------------------390 --735 --20 --------------390 --740 --20 t > 100 ----------------------------------t ≤ 200 ----------------------------------------------------------t ≤ 100 -----------------------
Heat Treatment Q Q ST+Q Q Q Q Q Q Q Q Q Q ST+Q ST+Q Q Q Q Q Q Q ST+Q Q Q Q ST+Q Q Q ST+Q Q ST+Q Q ST+Q
Other 55 - 58 HRC; 200 - 230 HBW ----45 - 50 HRC; 180 - 250 HBW --------------------------45 - 50 HRC; 180 - 250 HBW --------45 - 50 HRC; 180 - 250 HBW ----45 - 50 HRC; 180 - 250 HBW --------45 - 50 HRC; 180 - 250 HBW ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB/T 5680-1998
Designation Grade Z 100 MD 6 1-M Grade F Grade GX120MnMo7-1 Grade Z 120 M 12-M Grade A Grade B-1 Grade B-2 Grade B-3 Grade B-4 Grade ZGMn13-1 Grade ZGMn13-2 Grade ZGMn13-3 Grade GX100Mn13 Grade GX120Mn13 Class SCMnH 1 Class SCMnH 2 Class SCMnH 3 Grade Z 120 MC 12-M Grade C Grade ZGMn13-4 Grade GX120MnCr13-2 Class SCMnH 11 Grade Z 100 MN 13 4-M Grade D Grade GX120MnNi13-3 Grade Z 110 MD 12 1-M Grade E-1 Grade GX110MnMo13-1 Grade E-2 Grade GX90MnMo14 Grade Z 120MC 17 2-M Grade GX120MnCr17-2
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
402
7.3 Cast Alloy Steels 7.3.1A Chemical Composition of Cast Alloy Steels for General and Structural Purposes
Specification EN 10293:2015 ISO 14737:2003 JIS G 5111:1991 ASTM A958/A958M-14
EN 10293:2015 ISO 14737:2003
UNS Steel No. No. --1.7221 --------J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 ----------J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --J14045 --1.7231 -------
C 0.22-0.29 0.20-0.29 0.20-0.30 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.33 0.28-0.35 0.30-0.40 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.43 0.38-0.45 0.38-0.45
Mn 0.50-0.80 0.50-0.80 0.50-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.50-0.80 0.50-0.80 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.70-1.10 0.60-1.00 0.60-0.90
Si 0.60 0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.60 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.40 0.025 0.020 0.80-1.20 0.15-0.30 0.40 0.025 0.020 0.80-1.20 0.15-0.25 0.040 0.040 0.80-1.20 --0.15-0.35 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.025 0.020 0.80-1.20 0.40 0.15-0.25 0.040 0.040 0.80-1.20 --0.15-0.35 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.035 0.040 0.80-1.10 --0.15-0.25 0.025 0.020 0.80-1.20 0.40 0.15-0.30 0.40 0.025 0.020 0.80-1.20 0.15-0.25
Others V 0.05; Cu 0.30 V 0.05; Cu 0.30 ----------------------V 0.05; Cu 0.30 --------------------------V 0.05; Cu 0.30 V 0.05; Cu 0.30
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ISO 14737:2003 JIS G 5111:1991 ASTM A958/A958M-14
Designation G26CrMo4 Grade G25CrMo4 Class SCCrM 1A Grade SC 4130, Class 65/35 Grade SC 4130, Class 70/36 Grade SC 4130, Class 80/40 Grade SC 4130, Class 80/50 Grade SC 4130, Class 90/60 Grade SC 4130, Class 105/85 Grade SC 4130, Class 115/95 Grade SC 4130, Class 130/115 Grade SC 4130, Class 135/125 Grade SC 4130, Class 150/135 Grade G32CrMo4 Class SCCrM 3A Grade SC 4140, Class 65/35 Grade SC 4140, Class 70/36 Grade SC 4140, Class 80/40 Grade SC 4140, Class 80/50 Grade SC 4140, Class 90/60 Grade SC 4140, Class 105/85 Grade SC 4140, Class 115/95 Grade SC 4140, Class 130/115 Grade SC 4140, Class 135/125 Grade SC 4140, Class 150/135 Grade SC 4140, Class 160/145 Grade SC 4140, Class 165/150 G42CrMo4 Grade G42CrMo4
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
403
7.3 Cast Alloy Steels 7.3.1A Chemical Composition of Cast Alloy Steels for General and Structural Purposes (Continued)
Specification ASTM A958/A958M-14
UNS Steel No. No. C Mn J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 J23259 --0.28-0.33 0.60-0.90 ----0.25-0.35 0.90-1.50 --1.6570 0.28 - 0.35 0.60 - 1.00 ----0.28 - 0.35 0.60 - 1.00
Si 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.60 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.035 0.040 0.70-0.90 1.65-2.00 0.20-0.30 0.040 0.040 0.30-0.90 1.60-2.00 0.15-0.35 0.020 0.015 1.00 - 1.40 1.60 - 2.10 0.30 - 0.50 0.020 0.015 1.00 - 1.40 1.60 - 2.10 0.30 - 0.50
Others ----------------------------V 0.05; Cu 0.30 V 0.05; Cu 0.30
7.3.1B Mechanical Properties of Cast Alloy Steels for General and Structural Purposes UNS No. ---
Specification EN 10293:2015
Designation G26CrMo4
ISO 14737:2003
Grade G25CrMo4
---
JIS G 5111:1991
Class SCCrM 1A
---
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. 1.7221 t ≤ 100 550 --700-850 --10 t ≤ 100 450 --600-750 --16 100 < t ≤ 250 300 --550-700 --14 --t ≤ 100 450 --600-750 --16 t ≤ 100 550 --700-850 --10 100 < t ≤ 250 300 --550-700 --14 ----390 --590 --13
Heat Treatment Q+T Q+T Q+T Q+T Q+T Q+T N+T
Other 18 J @ RT 40 J @ RT 27 J @ RT 40 J @ RT 18 J @ RT 27 J @ RT 170 min. HB
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 5111:1991 EN 10293:2015 ISO 14737:2003
Designation Grade SC 4330, Class 65/35 Grade SC 4330, Class 70/36 Grade SC 4330, Class 80/40 Grade SC 4330, Class 80/50 Grade SC 4330, Class 90/60 Grade SC 4330, Class 105/85 Grade SC 4330, Class 115/95 Grade SC 4330, Class 130/115 Grade SC 4330, Class 135/125 Grade SC 4330, Class 150/135 Grade SC 4330, Class 160/145 Grade SC 4330, Class 165/150 Grade SC 4330, Class 210/180 Class SCNCrM 2A G32NiCrMo8-5-4 Grade G32NiCrMo8-5-4
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
404
7.3 Cast Alloy Steels 7.3.1B Mechanical Properties of Cast Alloy Steels for General and Structural Purposes (Continued) UNS Steel No. No. J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 --J13502 -------
EN 10293:2015
Class SCCrM 3A Grade SC 4140, Class 65/35 Grade SC 4140, Class 70/36 Grade SC 4140, Class 80/40 Grade SC 4140, Class 80/50 Grade SC 4140, Class 90/60 Grade SC 4140, Class 105/85 Grade SC 4140, Class 115/95 Grade SC 4140, Class 130/115 Grade SC 4140, Class 135/125 Grade SC 4140, Class 150/135 Grade SC 4140, Class 160/145 Grade SC 4140, Class 165/150 G42CrMo4
--J14045 J14045 J14045 J14045 J14045 J14045 J14045 J14045 J14045 J14045 J14045 J14045 ---
ISO 14737:2003
Grade G42CrMo4
Download From http://bbs.infoeach.com
ISO 14737:2003
JIS G 5111:1991 ASTM A958/A958M-14
---
Section Yield Strength, min. Tensile Strength, min. Elongation Thickness, mm MPa ksi MPa ksi % min. --240 35 450 65 24 --250 36 485 70 22 --275 40 550 80 18 --345 50 550 80 22 --415 60 620 90 18 --585 85 725 105 17 --655 95 795 115 14 --795 115 895 130 11 --860 125 930 135 9 --930 135 1035 150 7 t ≤ 100 270 --630-780 --16 t ≤ 100 540 --700-850 --12 t ≤ 100 650 --800-950 --10 100 < t ≤ 150 480 --620-770 --10 150 < t ≤ 250 330 --620-770 --10 ----440 --690 --9 ----240 35 450 65 24 ----250 36 485 70 22 ----275 40 550 80 18 ----345 50 550 80 22 ----415 60 620 90 18 ----585 85 725 105 17 ----655 95 795 115 14 ----795 115 895 130 11 ----860 125 930 135 9 ----930 135 1035 150 7 ----1000 145 1105 160 6 ----1035 150 1140 165 5 1.7231 t ≤ 100 700 --850-1000 --10 t ≤ 100 600 --800-950 --12 100 < t ≤ 150 550 --700-850 --10 150 < t ≤ 250 350 --650-800 --10 --t ≤ 100 300 --700-850 --15 t ≤ 100 600 --780-930 --12 t ≤ 100 700 --850-1000 --10 100 < t ≤ 150 550 --700-850 --10 150 < t ≤ 250 350 --650-800 --10
Heat Treatment N+T N+T N+T N+T N+T; or HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T N+T Q+T Q+T Q+T Q+T N+T N+T N+T N+T N+T N+T N+T; or HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T Q+T Q+T Q+T Q+T N+T Q+T Q+T Q+T Q+T
Other --------------------10 J @ RT 35 J @ RT 18 J @ RT 27 J @ RT 16 J @ RT 201 min. HB ------------------------27 J @ RT 31 J @ RT 27 J @ RT 16 J @ RT 10 J @ RT 31 J @ RT 16 J @ RT 27 J @ RT 16 J @ RT
Download From http://bbs.infoeach.com
Designation Grade SC 4130, Class 65/35 Grade SC 4130, Class 70/36 Grade SC 4130, Class 80/40 Grade SC 4130, Class 80/50 Grade SC 4130, Class 90/60 Grade SC 4130, Class 105/85 Grade SC 4130, Class 115/95 Grade SC 4130, Class 130/115 Grade SC 4130, Class 135/125 Grade SC 4130, Class 150/135 Grade G32CrMo4
Specification ASTM A958/A958M-14
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
405
7.3 Cast Alloy Steels 7.3.1B Mechanical Properties of Cast Alloy Steels for General and Structural Purposes (Continued)
Specification ASTM A958/A958M-14
Grade G32NiCrMo8-5-4
UNS Steel Section Yield Strength, min. No. No. Thickness, mm MPa ksi J23259 ----240 35 J23259 ----250 36 J23259 ----275 40 J23259 ----345 50 J23259 ----415 60 J23259 ----585 85 J23259 ----655 95 J23259 ----795 115 J23259 ----860 125 J23259 ----930 135 J23259 ----1000 145 J23259 ----1035 150 J23259 ----1240 180 ------590 ----1.6570 t ≤ 100 950 --t ≤ 100 700 --100 < t ≤ 250 650 ----1.6570 t ≤ 100 950 --t ≤ 100 700 --100 < t ≤ 250 650 ---
Tensile Strength, min. Elongation MPa ksi % min. 450 65 24 485 70 22 550 80 18 550 80 22 620 90 18 725 105 17 795 115 14 895 130 11 930 135 9 1035 150 7 1105 160 6 1140 165 5 1450 210 4 780 --9 1050-1200 --10 850-1000 --16 820-970 --14 1050-1200 --10 850-1000 --16 820-970 --14
Heat Treatment N+T N+T N+T N+T N+T; or HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T HT+Q+T N+T Q+T Q+T Q+T Q+T Q+T Q+T
Other --------------------------223 min. HB 35 J @ RT 50 J @ RT 35 J @ RT 35 J @ RT 50 J @ RT 35 J @ RT
Download From http://bbs.infoeach.com
ISO 14737:2003
Download From http://bbs.infoeach.com
JIS G 5111:1991 EN 10293:2015
Designation Grade SC 4330, Class 65/35 Grade SC 4330, Class 70/36 Grade SC 4330, Class 80/40 Grade SC 4330, Class 80/50 Grade SC 4330, Class 90/60 Grade SC 4330, Class 105/85 Grade SC 4330, Class 115/95 Grade SC 4330, Class 130/115 Grade SC 4330, Class 135/125 Grade SC 4330, Class 150/135 Grade SC 4330, Class 160/145 Grade SC 4330, Class 165/150 Grade SC 4330, Class 210/180 Class SCNCrM 2A G32NiCrMo8-5-4
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
406
7.3 Cast Alloy Steels 7.3.2A Chemical Composition of Cast Alloy Steels for Pressure Purposes at High Temperatures UNS Steel No. No. J12524 ---
C 0.25
Mn 0.50-0.80
Si 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.045 0.35 0.50 0.45-0.65
ASTM A217/A217M-14
Grade WC1
J12524
0.25
0.50-0.80
0.60
0.04
0.045
0.35
0.50
0.45-0.65
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991
G20Mo5 Grade ZG19MoG Type C28H Class SCPH 11
0.50-1.00 0.50-1.00 0.50-1.00 0.50-0.80
0.60 0.30-0.60 0.30-0.60 0.60
0.025 0.035 0.035 0.040
0.020 0.035 0.035 0.040
0.30 0.030 0.30 0.35
0.40 ----0.50
0.40-0.60 0.40-0.60 0.40-0.60 0.45-0.65
ASME SA-217/SA-217M
Grade WC6
J12072
---
0.05-0.20
0.50-0.80
0.60
0.04
0.045
1.00-1.50
0.50
0.45-0.65
ASTM A217/A217M-14
Grade WC6
J12072
---
0.05-0.20
0.50-0.80
0.60
0.035
0.035
1.00-1.50
0.50
0.45-0.65
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991 ASTM A389/A389M-13 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991
G17CrMo5-5 Grade ZG15Cr1MoG Type C32H Class SCPH 21 Grade C24 G17CrMoV5-10 Grade ZG17Cr1Mo1VG Type C35BH Class SCPH 23
--1.7357 0.15-0.20 ----0.10-0.20 ----0.10-0.20 ----0.20 J12092 --0.20 --1.7706 0.15-0.20 ----0.13-0.20 ----0.13-0.20 ----0.20
0.50-1.00 0.50-0.80 0.50-0.80 0.50-0.80 0.30-0.80 0.50-0.90 0.50-0.80 0.50-0.80 0.50-0.80
0.60 0.30-0.60 0.30-0.60 0.60 0.60 0.60 0.30-0.60 0.30-0.60 0.60
0.020 0.035 0.035 0.040 0.035 0.020 0.035 0.035 0.040
0.020 0.035 0.035 0.040 0.035 0.015 0.035 0.035 0.040
1.00-1.50 1.00-1.50 1.00-1.50 1.00-1.50 0.80-1.25 1.20-1.50 1.20-1.60 1.20-1.60 1.00-1.50
0.40 ----0.50 --0.40 ----0.50
0.45-0.65 0.45-0.65 0.45-0.65 0.45-0.65 0.90-1.20 0.90-1.10 0.90-1.20 0.90-1.20 0.90-1.20
ASME SA-217/SA-217M
Grade WC9
J21890
---
0.05-0.18
0.40-0.70
0.60
0.04
0.045
2.00-2.75
0.50
0.90-1.20
ASME SA-487/SA-487M
Grade 8, Class A
J22091
---
0.05-0.20
0.50-0.90
0.80
0.04
0.045
2.00-2.75
---
0.90-1.10
Grade 8, Class B
J22091
---
0.05-0.20
0.50-0.90
0.80
0.04
0.045
2.00-2.75
---
0.90-1.10
Grade 8, Class C
J22091
---
0.05-0.20
0.50-0.90
0.80
0.04
0.045
2.00-2.75
---
0.90-1.10
ASTM A217/A217M-14
Grade WC9
J21890
---
0.05-0.18
0.40-0.70
0.60
0.035
0.035
2.00-2.75
0.50
0.90-1.20
ASTM A487/A487M-14
Grade 8, Class A
J22091
---
0.05-0.20
0.50-0.90
0.80
0.035
0.035
2.00-2.75
---
0.90-1.10
Grade 8, Class B
J22091
---
0.05-0.20
0.50-0.90
0.80
0.035
0.035
2.00-2.75
---
0.90-1.10
Grade 8, Class C
J22091
---
0.05-0.20
0.50-0.90
0.80
0.035
0.035
2.00-2.75
---
0.90-1.10
---------
---
1.5419 0.15-0.23 --0.15-0.23 --0.15-0.23 --0.25
Others Cu 0.50; W 0.10; (Cu+Ni+Cr+W) 1.00 Cu 0.50; W 0.10; (Cu+Ni+Cr+W) 1.00 V 0.05; Cu 0.30 ----Cu 0.50; W 0.10; (Cu+Ni+Cr+W) 1.00 Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 V 0.05; Cu 0.30 ----Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 V 0.15-0.25 V 0.20-0.30; Cu 0.30; Sn 0.025 V 0.15-0.35 V 0.15-0.35 V 0.15-0.25; Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; V 0.03; (Cu+W+V) 0.60 Cu 0.50; W 0.10; V 0.03; (Cu+W+V) 0.60 Cu 0.50; W 0.10; V 0.03; (Cu+W+V) 0.60 Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; V 0.03; (Cu+W+V) 0.60 Cu 0.50; W 0.10; V 0.03; (Cu+W+V) 0.60 Cu 0.50; W 0.10; V 0.03; (Cu+W+V) 0.60
Download From http://bbs.infoeach.com
Designation Grade WC1
Download From http://bbs.infoeach.com
Specification ASME SA-217/SA-217M
Note: This section continued on next page. Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
407
7.3 Cast Alloy Steels 7.3.2A Chemical Composition of Cast Alloy Steels for Pressure Purposes at High Temperatures (Continued) UNS Steel No. No. --1.7379 --------------------J42045 ---
ASTM A217/A217M-14
Grade C5
J42045
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991 EN 10295:2002 ISO 11973:1999 ASME SA-217/SA-217M
GX15CrMo5 Grade ZG16Cr5MoG Type C37H Class SCPH 61 GX30CrSi7 Grade GX30CrSi7 Grade C12
ASTM A217/A217M-14
Grade C12
GB/T 16253-1996 ISO 4991:1994 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994
Grade ZG14Cr9Mo1G Type C38H G12MoCrV5-2 Grade ZG14MoVG Type C33H
ISO 4991:1994
Download From http://bbs.infoeach.com
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.020 0.020 2.00-2.50 0.40 0.90-1.20 0.035 0.035 2.00-2.50 --0.90-1.20 0.035 0.035 2.00-2.50 --0.90-1.20 0.035 0.035 2.00-2.50 --0.90-1.20 0.035 0.035 2.00-2.50 --0.90-1.20 0.040 0.040 2.00-2.75 0.50 0.90-1.20 0.04 0.045 4.00-6.50 0.50 0.45-0.65
C 0.13-0.20 0.08-0.15 0.13-0.20 0.08-0.15 0.13-0.20 0.20 0.20
Mn 0.50-0.90 0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80 0.40-0.70
Si 0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.30-0.60 0.60 0.75
0.20
0.40-0.70
0.75
0.04
0.045
4.00-6.50
0.50
0.45-0.65
--1.7365 0.12-0.19 ----0.12-0.19 ----0.12-0.19 ----0.20 --1.4710 0.20-0.35 ----0.20-0.35 J82090 --0.20
0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80 0.50-1.00 0.50-1.00 0.35-0.65
0.80 0.80 0.80 0.75 1.00-2.50 1.00-2.5 1.00
0.025 0.035 0.035 0.040 0.035 0.040 0.04
0.025 0.035 0.035 0.040 0.030 0.040 0.045
4.00-6.00 4.00-6.00 4.00-6.00 4.00-6.50 6.00-8.00 6.0-8.0 8.00-10.00
------0.50 0.50 0.50 0.50
0.45-0.65 0.45-0.65 0.45-0.65 0.45-0.65 0.15 0.5 0.90-1.20
J82090
---
0.20
0.35-0.65
1.00
0.035
0.035
8.00-10.00
0.50
0.90-1.20
-----------
----1.7720 -----
0.10-0.17 0.10-0.17 0.10-0.15 0.10-0.17 0.10-0.17
0.50-0.80 0.50-0.80 0.40-0.70 0.40-0.70 0.40-0.70
0.80 0.80 0.45 0.30-0.60 0.30-0.60
0.035 0.035 0.030 0.035 0.035
0.035 0.035 0.020 0.035 0.035
8.00-10.0 8.00-10.00 0.30-0.50 0.30-0.60 0.30-0.60
----0.40 0.40 0.40
1.00-1.30 1.00-1.30 0.40-0.60 0.40-0.60 0.40-0.60
---
Others V 0.05; Cu 0.30 --------Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 V 0.05; Cu 0.30 ----Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 ----Cu 0.50; W 0.10; (Cu+Ni+W) 1.00 Cu 0.50; W 0.10; Cb 0.03; V 0.06; (Cu+Ni+W) 1.00 ----V 0.22-0.30; Cu 0.30; Sn 0.025 V 0.22-0.32 V 0.22-0.32
7.3.2B Mechanical Properties of Cast Alloy Steels for Pressure Purposes at High Temperatures
Specification Designation ASME SA-217/SA-217M Grade WC1 ASTM A217/A217M-14 Grade WC1 EN 10213:2007 C1:2008 G20Mo5 GB/T 16253-1996 Grade ZG19MoG ISO 4991:1994 Type C28H JIS G 5151:1991 Class SCPH 11 ASME SA-217/SA-217M Grade WC6 ASTM A217/A217M-14 Grade WC6 Note: This section continued on next page.
UNS Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. No. Thickness, mm MPa ksi MPa ksi % min. J12524 ----240 35 450-620 65-90 24 J12524 ----240 35 450-620 65-90 24 --1.5419 t ≤ 100 245 --440-590 --22 ------250 --450-600 --21 ------250 --450-600 --21 ------245 --450 --22 J12072 ----275 40 485-655 70-95 20 J12072 ----275 40 485-655 70-95 20
Heat Treatment N+T N+T Q+T N+T or Q+T N+T or Q+T A, N, N+T or Q+T N+T N+T
Download From http://bbs.infoeach.com
JIS G 5151:1991 ASME SA-217/SA-217M
Designation G17CrMo9-10 Grade ZG12Cr2Mo1G Grade ZG16Cr2Mo1G Type C34AH Type C34BH Class SCPH 32 Grade C5
Specification EN 10213:2007 C1:2008 GB/T 16253-1996
Other ----27 J @ RT 25 J @ RT 25 J @ RT -------
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
408
7.3 Cast Alloy Steels 7.3.2B Mechanical Properties of Cast Alloy Steels for Pressure Purposes at High Temperatures (Continued)
ASTM A217/A217M-14 ASTM A487/A487M-14
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991 ASME SA-217/SA-217M ASTM A217/A217M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991 EN 10295:2002 ISO 11973:1999 ASME SA-217/SA-217M ASTM A217/A217M-14 GB/T 16253-1996 ISO 4991:1994 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994
Designation G17CrMo5-5 Grade ZG15Cr1MoG Type C32H Class SCPH 21 Grade C24 G17CrMoV5-10 Grade ZG17Cr1Mo1VG Type C35BH Class SCPH 23 Grade WC9 Grade 8, Class A Grade 8, Class B Grade 8, Class C Grade WC9 Grade 8, Class A Grade 8, Class B Grade 8, Class C G17CrMo9-10 Grade ZG12Cr2Mo1G Grade ZG16Cr2Mo1G Type C34AH Type C34BH Class SCPH 32 Grade C5 Grade C5 GX15CrMo5 Grade ZG16Cr5MoG Type C37H Class SCPH 61 GX30CrSi7 Grade GX30CrSi7 Grade C12 Grade C12 Grade ZG14Cr9Mo1G Type C38H G12MoCrV5-2 Grade ZG14MoVG Type C33H
UNS No. --------J12092 --------J21890 J22091 J22091 J22091 J21890 J22091 J22091 J22091 ------------J42045 J42045 ------------J82090 J82090 -----------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. 1.7357 t ≤ 100 315 --490-690 --20 ----290 --490-640 --18 ----290 --490-640 --18 ----275 --480 --17 ----345 50 552 80 15.0 1.7706 t ≤ 150 440 --590-780 --15 ----420 --590-740 --15 ----420 --590-740 --15 ----345 --550 --13 ----275 40 485-655 70-95 20 ----380 55 585-760 85-110 20 ----585 85 725 105 17 ----515 75 690 100 17 ----275 40 485-655 70-95 20 ----380 55 585-760 85-110 20 ----585 85 725 105 17 ----515 75 690 100 17 1.7379 t ≤ 150 400 --590-740 --18 ----280 --510-660 --18 ----390 --600-750 --18 ----280 --510-660 --18 ----390 --600-750 --18 ----275 --480 --17 ----415 60 620-795 90-115 18 ----415 60 620-795 90-115 18 1.7365 t ≤ 150 420 --630-760 --16 ----420 --630-780 --16 ----420 --630-780 --16 ----410 --620 --17 1.4710 ------------------------------415 60 620-795 90-115 18 ----415 60 620-795 90-115 18 ----420 --630-780 --16 ----420 --630-780 --16 1.7720 t ≤ 100 295 --510-660 --17 ----320 --500-650 --17 ----320 --500-650 --17
Heat Treatment Q+T N+T or Q+T N+T or Q+T A, N, N+T or Q+T N+T Q+T N+T or Q+T N+T or Q+T A, N, N+T or Q+T N+T N+T Q+T Q+T N+T N+T Q+T Q+T Q+T N+T N+T or Q+T N+T N+T or Q+T A, N, N+T or Q+T N+T N+T Q+T N+T N+T A, N, N+T or Q+T A A or AC N+T N+T N+T N+T Q+T N+T N+T
Other 27 J @ RT 27 J @ RT 27 J @ RT ----27 J @ RT 24 J @ RT 24 J @ RT --------235 max HB; 22 max HRC ------235 max HB; 22 max HRC 40 J @ RT 25 J @ RT 40 J @ RT 25 J @ RT 40 J @ RT ------27 J @ RT 25 J @ RT 25 J @ RT --300 max HB ------20 J @ RT 20 J @ RT 27 J @ RT 13 J @ RT 13 J @ RT
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991 ASTM A389/A389M-13 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5151:1991 ASME SA-217/SA-217M ASME SA-487/SA-487M
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
409
7.3 Cast Alloy Steels 7.3.3A Chemical Composition of Cast Alloy Steels for Pressure Purposes at Low Temperatures
EN 10213:2007 C1:2008 JIS G 5152:1991 ASME SA-352/SA-352M ASTM A352/A352M-06 (2012) ASTM A757/A757M-15
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 JIS G 5152:1991
Designation Grade LC1 Grade LC1 G18Mo5 Class SCPL 11 Grade LC2 Grade LC2 Grade B2N
UNS Steel No. No. C J12522 --0.25 J12522 --0.25 --1.5422 0.15-0.20 ----0.25 J22500 --0.25 J22500 --0.25 J22501 --0.25
Mn 0.50-0.80 0.50-0.80 0.80-1.20 0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80
Si 0.60 0.60 0.60 0.60 0.60 0.60 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.045 ----0.45-0.65 0.04 0.045 ----0.45-0.65 0.020 0.020 0.30 0.40 0.45-0.65 0.040 0.040 0.35 --0.45-0.65 0.04 0.045 --2.00-3.00 --0.04 0.045 --2.00-3.00 --0.025 0.025 0.40 2.0-3.0 0.25
Grade B2Q
J22501
0.50-0.80
0.60
0.025
0.025
0.40
2.0-3.0
0.25
G9Ni10 Class SCPL 21 Grade LC3 Grade LC3 Grade B3N
--1.5636 0.06-0.12 ----0.25 J31550 --0.15 J31550 --0.15 J31500 --0.15
0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80
0.60 0.60 0.60 0.60 0.60
0.020 0.040 0.04 0.04 0.025
0.015 0.040 0.045 0.045 0.025
0.30 0.35 ----0.40
2.00-3.00 2.00-3.00 3.00-4.00 3.00-4.00 3.0-4.0
0.20 ------0.25
Grade B3Q
J31500
0.50-0.80
0.60
0.025
0.025
0.40
3.0-4.0
0.25
0.50-0.80 0.50-0.80 0.50-0.80 0.50-0.80
0.60 0.30-0.60 0.30-0.60 0.60
0.020 0.030 0.030 0.040
0.015 0.030 0.030 0.040
0.30 ----0.35
3.00-4.00 3.00-4.00 3.00-4.00 3.00-4.00
0.20 -------
G9Ni14 Grade ZG14Ni4D Type C43L Class SCPL 31
---------
---
---
0.25
0.15
1.5638 0.06-0.12 --0.14 --0.14 --0.15
Others ----V 0.05; Cu 0.30 Cu 0.50 ----V 0.03; Cu 0.50; (V+Cu+Cr+Mo+P+S) 1.00 V 0.03; Cu 0.50; (V+Cu+Cr+Mo+P+S) 1.00 V 0.05; Cu 0.30 Cu 0.50 ----V 0.03; Cu 0.50; (V+Cu+Cr+Mo+P+S) 1.00 V 0.03; Cu 0.50; (V+Cu+Cr+Mo+P+S) 1.00 V 0.05; Cu 0.30 ----Cu 0.50
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-352/SA-352M ASTM A352/A352M-06 (2012) EN 10213:2007 C1:2008 JIS G 5152:1991 ASME SA-352/SA-352M ASTM A352/A352M-06 (2012) ASTM A757/A757M-15
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
410
7.3 Cast Alloy Steels 7.3.3A Chemical Composition of Cast Alloy Steels for Pressure Purposes at Low Temperatures (Continued)
C 0.22 0.22 0.22
Mn 0.55-0.75 0.55-0.75 0.50-0.80
Si 0.50 0.50 0.60
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.045 1.35-1.85 2.50-3.50 0.30-0.60 0.04 0.045 1.35-1.85 2.50-3.50 0.30-0.60 0.025 0.025 1.35-1.85 2.5-3.5 0.35-0.60
Grade E2N1
J42065
---
0.20
0.40-0.70
0.60
0.020
0.020
1.50-2.0
2.75-3.90
0.40-0.60
Grade E2N2
J42065
---
0.20
0.40-0.70
0.60
0.020
0.020
1.50-2.0
2.75-3.90
0.40-0.60
Grade E2N3
J42065
---
0.20
0.40-0.70
0.60
0.020
0.020
1.50-2.0
2.75-3.90
0.40-0.60
Grade E2Q1
J42065
---
0.20
0.40-0.70
0.60
0.020
0.020
1.50-2.0
2.75-3.90
0.40-0.60
Grade E2Q2
J42065
---
0.20
0.40-0.70
0.60
0.020
0.020
1.50-2.0
2.75-3.90
0.40-0.60
Grade E2Q3
J42065
---
0.20
0.40-0.70
0.60
0.020
0.020
1.50-2.0
2.75-3.90
0.40-0.60
G17NiCrMo13-6 Grade ZG22Ni3Cr2MoAD Grade ZG22Ni3Cr2MoBD Type C43E2aL Type C43E2bL Grade ZG29Cr1MoD Type C31L Grade D1N1
--1.6781 0.15-0.19 ----0.22 ----0.22 ----0.22 ----0.22 ----0.29 ----0.29 J22092 --0.20
0.55-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.40-0.80 0.50-0.80 0.50-0.80 0.40-0.80
0.50 0.60 0.60 0.60 0.60 0.30-0.60 0.30-0.60 0.60
0.015 0.030 0.030 0.030 0.030 0.030 0.030 0.025
0.015 0.030 0.030 0.030 0.030 0.030 0.030 0.025
1.30-1.80 1.35-2.00 1.50-2.00 1.35-2.00 1.50-2.00 0.90-1.20 0.90-1.20 2.0-2.75
3.00-3.50 2.50-3.50 2.75-3.90 2.50-3.50 2.75-3.90 ----0.50
0.45-0.65 0.35-0.60 0.35-0.60 0.35-0.60 0.35-0.60 0.15-0.30 0.15-0.30 0.90-1.20
Grade D1N2
J22092
---
0.20
0.40-0.80
0.60
0.025
0.025
2.0-2.75
0.50
0.90-1.20
Grade D1N3
J22092
---
0.20
0.40-0.80
0.60
0.025
0.025
2.0-2.75
0.50
0.90-1.20
Grade D1Q1
J22092
---
0.20
0.40-0.80
0.60
0.025
0.025
2.0-2.75
0.50
0.90-1.20
Grade D1Q2
J22092
---
0.20
0.40-0.80
0.60
0.025
0.025
2.0-2.75
0.50
0.90-1.20
Grade D1Q3
J22092
---
0.20
0.40-0.80
0.60
0.025
0.025
2.0-2.75
0.50
0.90-1.20
GB/T 16253-1996 ISO 4991:1994 ASTM A757/A757M-15
Grade ZG20Cr2Mo1D Type C34BL Grade C1Q
----J12582
-------
0.20 0.20 0.25
0.50-0.80 0.50-0.80 1.20
0.30-0.60 0.30-0.60 0.60
0.030 0.030 0.025
0.030 0.030 0.025
2.00-2.50 2.00-2.50 0.40
----1.5-2.0
0.90-1.20 0.90-1.20 0.15-0.30
GB/T 16253-1996 ISO 4991:1994
Grade ZG24Ni2MoD Type C43C1L
-----
-----
0.24 0.24
0.80-1.20 0.80-1.20
0.30-0.60 0.30-0.60
0.030 0.030
0.030 0.030
-----
1.50-2.00 1.50-2.00
0.15-0.30 0.15-0.30
Download From http://bbs.infoeach.com
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 GB/T 16253-1996 ISO 4991:1994 ASTM A757/A757M-15
Others ----V 0.03; Cu 0.50; (V+Cu+P+S) 0.70 V 0.03; Cu 0.50; W 0.10; (V+Cu+W+P+S) 0.70 V 0.03; Cu 0.50; W 0.10; (V+Cu+W+P+S) 0.70 V 0.03; Cu 0.50; W 0.10; (V+Cu+W+P+S) 0.70 V 0.03; Cu 0.50; W 0.10; (V+Cu+W+P+S) 0.70 V 0.03; Cu 0.50; W 0.10; (V+Cu+W+P+S) 0.70 V 0.03; Cu 0.50; W 0.10; (V+Cu+W+P+S) 0.70 V 0.05; Cu 0.30 ------------V 0.03; Cu 0.50; W 0.10; (V+Ni+Cu+W+P+S) 1.00 V 0.03; Cu 0.50; W 0.10; (V+Ni+Cu+W+P+S) 1.00 V 0.03; Cu 0.50; W 0.10; (V+Ni+Cu+W+P+S) 1.00 V 0.03; Cu 0.50; W 0.10; (V+Ni+Cu+W+P+S) 1.00 V 0.03; Cu 0.50; W 0.10; (V+Ni+Cu+W+P+S) 1.00 V 0.03; Cu 0.50; W 0.10; (V+Ni+Cu+W+P+S) 1.00 ----V 0.03; Cu 0.50; (Cr+V+Cu+P+S) 1.00 -----
Download From http://bbs.infoeach.com
UNS Steel No. No. J42215 --J42215 --J42220 ---
Specification Designation ASME SA-352/SA-352M Grade LC2-1 ASTM A352/A352M-06 (2012) Grade LC2-1 ASTM A757/A757M-15 Grade E1Q
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
411
7.3 Cast Alloy Steels 7.3.3B Mechanical Properties of Cast Alloy Steels for Pressure Purposes at Low Temperatures UNS No. J12522 J12522 ----J22500 J22500 J22501 J22501 ----J31550 J31550 J31500 J31500 ---------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. ----240 35.0 450-620 65.0-90.0 24 ----240 35.0 450-620 65.0-90.0 24 1.5422 t ≤ 100 240 --440-790 --23 ----245 --450 --21 ----275 40.0 485-655 70.0-95.0 24 ----275 40.0 485-655 70.0-95.0 24 ----275 40 485 70 24 ----275 40 485 70 24 1.5636 t ≤ 35 280 --480-630 --24 ----275 --480 --21 ----275 40.0 485-655 70.0-95.0 24 ----275 40.0 485-655 70.0-95.0 24 ----275 40 485 70 24 ----275 40 485 70 24 1.5638 t ≤ 35 360 --500-650 --20 ----300 --460-610 --20 ----300 --460-610 --20 ----275 --480 --21
Heat Treatment N+T or Q+T N+T or Q+T Q+T A, N, N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T Q+T A, N, N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T Q+T Q+T Q+T A, N, N+T or Q+T
Other 18 J @ -59°C 18 J @ -59°C 27 J @ -45°C see standard for impact data 20 J @ -73°C 20 J @ -73°C L: 20 J @ -73°C L: 20 J @ -73°C 27 J @ -70°C see standard for impact data 20 J @ -101°C 20 J @ -101°C L: 20 J @ -101°C L: 20 J @ -101°C 27 J @ -90°C 27 J @ -70°C 27 J @ -70°C see standard for impact data
Download From http://bbs.infoeach.com
Designation Grade LC1 Grade LC1 G18Mo5 Class SCPL 11 Grade LC2 Grade LC2 Grade B2N Grade B2Q EN 10213:2007 C1:2008 G9Ni10 JIS G 5152:1991 Class SCPL 21 ASME SA-352/SA-352M Grade LC3 ASTM A352/A352M-06 (2012) Grade LC3 ASTM A757/A757M-15 Grade B3N Grade B3Q EN 10213:2007 C1:2008 G9Ni14 GB/T 16253-1996 Grade ZG14Ni4D ISO 4991:1994 Type C43L JIS G 5152:1991 Class SCPL 31
Download From http://bbs.infoeach.com
Specification ASME SA-352/SA-352M ASTM A352/A352M-06 (2012) EN 10213:2007 C1:2008 JIS G 5152:1991 ASME SA-352/SA-352M ASTM A352/A352M-06 (2012) ASTM A757/A757M-15
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
412
7.3 Cast Alloy Steels 7.3.3B Mechanical Properties of Cast Alloy Steels for Pressure Purposes at Low Temperatures (Continued) Tensile Strength, min. Elongation MPa ksi % min. 725-895 105.0-130.0 18 725-895 105.0-130.0 18 620 90 22 620-825 90-120 18 725-930 105-135 15 795-1000 115-145 13 620-825 90-120 18 725-930 105-135 15 795-1000 115-145 13 750-900 --15 620-800 --16 800-950 --13 620-800 --16 800-950 --13 550-700 --16 550-700 --16 585-795 85-115 20 655-860 95-125 18 725-930 105-135 15 585-795 85-115 20 655-860 95-125 18 725-930 105-135 15 600-750 --18
ISO 4991:1994 ASTM A757/A757M-15 GB/T 16253-1996 ISO 4991:1994
--J12582 -----
600-750 515 520-670 520-670
Type C34BL Grade C1Q Grade ZG24Ni2MoD Type C43C1L
---------
---------
390 380 380 380
--55 -----
--75 -----
18 22 20 20
Heat Treatment N+T or Q+T N+T or Q+T Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T, N+C(A)+T, Q+T N+T or Q+T Q+T Q+T Q+T
Other 41 J @ -73°C 41 J @ -73°C L: 41 J @ -73°C L: 41 J @ -73°C L: 27 J @ -73°C L: 20 J @ -73°C L: 41 J @ -73°C L: 27 J @ -73°C L: 20 J @ -73°C 27 J @ -80°C 27 J @ -80°C 27 J @ -60°C 27 J @ -80°C 27 J @ -60°C 27 J @ -45°C 27 J @ -45°C L: BA J @ BA°C L: BA J @ BA°C L: BA J @ BA°C L: BA J @ BA°C L: BA J @ BA°C L: BA J @ BA°C 27 J @ -50°C 27 J @ 50°C L: 20 J @ -46°C 27 J @ -35°C 27 J @ -35°C
Download From http://bbs.infoeach.com
UNS Steel Section Yield Strength, min. No. No. Thickness, mm MPa ksi J42215 ----550 80.0 J42215 ----550 80.0 J42220 ----450 65 J42065 ----485 70 J42065 ----585 85 J42065 ----690 100 J42065 ----485 70 J42065 ----585 85 J42065 ----690 100 --1.6781 t ≤ 200 600 --------450 --------655 --------450 --------655 --------370 --------370 --J22092 ----380 55 J22092 ----515 75 J22092 ----585 85 J22092 ----380 55 J22092 ----515 75 J22092 ----585 85 ------390 ---
Download From http://bbs.infoeach.com
Specification Designation ASME SA-352/SA-352M Grade LC2-1 ASTM A352/A352M-06 (2012) Grade LC2-1 ASTM A757/A757M-15 Grade E1Q Grade E2N1 Grade E2N2 Grade E2N3 Grade E2Q1 Grade E2Q2 Grade E2Q3 EN 10213:2007 C1:2008 G17NiCrMo13-6 GB/T 16253-1996 Grade ZG22Ni3Cr2MoAD Grade ZG22Ni3Cr2MoBD ISO 4991:1994 Type C43E2aL Type C43E2bL GB/T 16253-1996 Grade ZG29Cr1MoD ISO 4991:1994 Type C31L ASTM A757/A757M-15 Grade D1N1 Grade D1N2 Grade D1N3 Grade D1Q1 Grade D1Q2 Grade D1Q3 GB/T 16253-1996 Grade ZG20Cr2Mo1D
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
413
7.4 Cast Stainless Steels 7.4.1 Cast Stainless Steels for General and Corrosion Resistant Applications 7.4.1.1A Chemical Composition of Martensitic and Ferritic Stainless Steels for General and Corrosion Resistant Applications
EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1 JIS G 5121:2003 EN 10283:2010 ISO 11972:1998
Designation Grade CA15 GX12Cr12 Grade GX 12 Cr 12 Class SCS 1 Grade CA15M GX7CrNiMo12-1 Grade GX 8 CrNiMo 12 1 Class SCS 3 Grade CA40 Class SCS 2 Class SCS 2A GX4CrNi13-4 Grade GX 4 CrNi 12 4 (QT1) Grade GX 4 CrNi 12 4 (QT2) Class SCS 5 Grade CA6NM Class SCS 6 GX4CrNiMo16-5-1 Grade GX 4 CrNiMo 16 5 1
UNS No. J91150 ------J91151 ------J91153 ------------J91540 -------
Steel No. C --0.15 1.4011 0.15 --0.15 --0.15 --0.15 1.4008 0.10 --0.10 --0.15 --0.20-0.40 --0.16-0.24 --0.25-0.40 1.4317 0.06 --0.06 --0.06 --0.06 --0.06 --0.06 1.4405 0.06 --0.06
Mn 1.00 1.00 0.80 1.00 1.00 1.00 0.80 1.00 1.00 1.00 1.00 1.00 1.50 1.50 1.00 1.00 1.00 1.00 0.80
Si 1.50 1.00 0.80 1.50 0.65 1.00 0.80 1.00 1.50 1.50 1.50 1.00 1.00 1.00 1.00 1.00 1.00 0.80 0.80
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.04 11.5-14.0 1.00 0.50 0.035 0.025 11.50-13.50 1.00 0.50 0.035 0.025 11.5-13.5 1.00 0.50 0.040 0.040 11.50-14.00 1.00 0.50 0.040 0.040 11.5-14.0 1.0 0.15-1.0 0.035 0.025 12.00-13.50 1.00-2.00 0.20-0.50 0.035 0.025 11.5-13.0 0.80-1.80 0.20-0.50 0.040 0.040 11.50-14.00 0.50-1.50 0.15-1.00 0.04 0.04 11.5-14.0 1.0 0.5 0.040 0.040 11.50-14.00 1.00 0.50 0.040 0.040 11.50-14.00 1.00 0.50 0.035 0.025 12.00-13.50 3.50-5.00 0.70 0.035 0.025 11.5-13.0 3.50-5.00 1.00 0.035 0.025 11.5-13.0 3.5-5.00 1.00 0.040 0.040 11.50-14.00 3.50-4.50 --0.04 0.03 11.5-14.0 3.5-4.5 0.40-1.0 0.040 0.030 11.50-14.00 3.50-4.50 0.40-1.00 0.035 0.025 15.00-17.00 4.00-6.00 0.70-1.50 0.035 0.025 15.0-17.0 4.00-6.00 0.70-1.50
Others --V 0.08; Cu 0.30 ------V 0.08; Cu 0.30 ----------V 0.08; Cu 0.30 ----------V 0.08; Cu 0.30 ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASTM A743/A743M-13ae1 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1 JIS G 5121:2003
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
414
7.4 Cast Stainless Steels 7.4.1 Cast Stainless Steels for General and Corrosion Resistant Applications 7.4.1.1B Mechanical Properties of Martensitic and Ferritic Stainless Steels for General and Corrosion Resistant Applications
Specification ASTM A743/A743M-13ae1* EN 10283:2010 ISO 11972:1998 JIS G 5121:2003
EN 10283:2010
ISO 11972:1998
Grade CA15M GX7CrNiMo12-1 Grade GX 8 CrNiMo 12 1 Class SCS 3 Grade CA40 Class SCS 2 Class SCS 2A GX4CrNi13-4
Grade GX 4 CrNi 12 4 (QT1) Grade GX 4 CrNi 12 4 (QT2) JIS G 5121:2003 Class SCS 5 ASTM A743/A743M-13ae1* Grade CA6NM JIS G 5121:2003 Class SCS 6 EN 10283:2010 GX4CrNiMo16-5-1 ISO 11972:1998 Grade GX 4 CrNiMo 16 5 1 *: See "List of Standards" at the beginning of the chapter.
UNS Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. No. Thickness, mm MPa ksi MPa ksi % min. J91150 ----450 65 620 90 18 --1.4011 t ≤ 150 450 --620 --15 ----t ≤ 150 450 --620 --14 ------345 --540 --18 --450 --620 --16 J91151 ----450 65 620 90 18 --1.4008 t ≤ 300 440 --590 --15 ----t ≤ 300 440 --590 --15 ------440 --590 --16 J91153 ----485 70 690 100 15 ------390 --590 --16 ------485 --690 --15 --1.4317 t ≤ 300 550 --760 --15 t ≤ 300 830 --900 --12 t ≤ 300 500 --700 --16 ----t ≤ 300 550 --750 --15 ----t ≤ 300 830 --900 --12 ------540 --740 --13 J91540 ----550 80 755 110 15 ------550 --750 --15 --1.4405 t ≤ 300 540 --760 --15 ----t ≤ 300 540 --760 --15
Heat Treatment N+T or A Q+T N+T Q+T Q+T N+T or A Q+T N+T Q+T N+T or A Q+T Q+T Q+T Q+T Q+T N+T N+T Q+T N+T Q+T Q+T N+T
Other --20 J @ RT 20 J @ RT 163-229 HB 179-241 HB --27 J @ RT 27 J @ RT 170-235 HB --170-235 HB 269 max. HB 50 J @ RT 35 J @ RT 50 J @ RT 45 J @ RT 35 J @ RT 217-277 HB --285 max. HB 60 J @ RT 60 J @ RT
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A743/A743M-13ae1* EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1* JIS G 5121:2003
Designation Grade CA15 GX12Cr12 Grade GX 12 Cr 12 Class SCS 1
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
415
7.4 Cast Stainless Steels 7.4.1 Cast Stainless Steels for General and Corrosion Resistant Applications 7.4.1.2A Chemical Composition of Austenitic Stainless Steels for General and Corrosion Resistant Applications
ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003
Designation Grade CF20 Class SCS 12 Grade CF8 Grade CF8 GX5CrNi19-10 Grade GX 5 CrNi 19 9 Class SCS 13 Class SCS 13A Grade CF3 Grade CF3 GX2CrNi19-11 Grade GX 2 CrNi 18 10 Class SCS 19A Class SCS 19 Grade CF8C Grade CF8C GX5CrNiNb19-11 Grade GX 6 CrNiNb 19 10 Class SCS 21 Grade CF8M Grade CF8M GX5CrNiMo19-11-2 Grade GX 5 CrNiMo 19 11 2 Grade GX 5 CrNiMo 19 11 3 Class SCS 14 Class SCS 14A GX5CrNiMoNb19-11-2 Grade GX 6 CrNiMoNb 19 11 2 Class SCS 22 Grade CF3M Grade CF3M GX2CrNiMo19-11-2 Grade GX 2 CrNiMo 19 11 2 Class SCS 16A
UNS No. J92602 --J92600 J92600 --------J92500 J92500 --------J92710 J92710 ------J92900 J92900 ----------------J92800 J92800 -------
Steel No. --------1.4308 ----------1.4309 ----------1.4552 --------1.4408 --------1.4581 --------1.4409 -----
C 0.20 0.20 0.08 0.08 0.07 0.07 0.08 0.08 0.03 0.03 0.030 0.03 0.03 0.03 0.08 0.08 0.07 0.08 0.08 0.08 0.08 0.07 0.07 0.07 0.08 0.08 0.07 0.08 0.08 0.03 0.03 0.030 0.03 0.03
Mn 1.50 2.00 1.50 1.50 1.50 1.50 2.00 1.50 1.50 1.50 2.00 1.50 1.50 2.00 1.50 1.50 1.50 1.50 2.00 1.50 1.50 1.50 1.50 1.50 2.00 1.50 1.50 1.50 2.00 1.50 1.50 2.00 1.50 1.50
Si 2.00 2.00 2.00 2.0 1.50 1.50 2.00 2.00 2.00 2.0 1.50 1.50 2.00 2.00 2.00 2.0 1.50 1.50 2.00 2.00 2.0 1.50 1.50 1.50 2.00 1.50 1.50 1.50 2.00 1.50 1.50 1.50 1.50 1.50
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.04 18.0-21.0 8.0-11.0 --0.040 0.040 18.00-21.00 8.00-11.00 --0.04 0.04 18.0-21.0 8.0-11.0 --0.04 0.04 18.0-21.0 8.0-11.0 --0.040 0.030 18.00-20.00 8.00-11.00 --0.040 0.030 18.0-21.0 8.00-11.00 --0.040 0.040 18.00-21.00 8.00-11.00 --0.040 0.040 18.00-21.00 8.00-11.00 --0.04 0.04 17.0-21.0 8.0-12.0 --0.04 0.04 17.0-21.0 8.0-12.0 --0.035 0.025 18.00-20.00 9.00-12.00 --0.040 0.030 17.0-19.0 9.00-12.00 --0.040 0.040 17.00-21.00 8.00-12.00 --0.040 0.040 17.00-21.00 8.00-12.00 --0.04 0.04 18.0-21.0 9.0-12.0 --0.04 0.04 18.0-21.0 9.0-12.0 --0.040 0.030 18.00-20.00 9.00-12.00 --0.040 0.030 18.0-21.0 9.00-12.00 --0.040 0.040 18.00-21.00 9.00-12.00 --0.04 0.04 18.0-21.0 9.0-12.0 2.0-3.0 0.04 0.04 18.0-21.0 9.0-12.0 2.0-3.0 0.040 0.030 18.00-20.00 9.00-12.00 2.00-2.50 0.040 0.030 17.0-20.0 9.00-12.00 2.00-2.50 0.040 0.030 17.0-20.0 9.00-12.00 3.00-3.50 0.040 0.040 17.00-20.00 10.00-14.00 2.00-3.00 0.040 0.040 18.00-21.00 9.00-12.00 2.00-3.00 0.040 0.030 18.00-20.00 9.00-12.00 2.00-2.50 0.040 0.030 17.0-20.0 9.00-12.00 2.00-2.50 0.040 0.040 17.00-20.00 10.00-14.00 2.00-3.00 0.04 0.04 17.0-21.0 9.0-13.0 2.0-3.0 0.04 0.04 17.0-21.0 9.0-13.0 2.0-3.0 0.035 0.025 18.00-20.00 9.00-12.00 2.00-2.50 0.040 0.030 17.0-20.0 9.00-12.00 2.00-2.50 0.040 0.040 17.00-21.00 9.00-13.00 2.00-3.00
Others --------Cu 0.50 ----------N 0.20; Cu 0.50 ------Cb 8xC to 1.0 Cb 8xC to 1.0 (Nb+Ta) 8xC to 1.00; Cu 0.50 Nb 8xC to 1.00 Nb 10xC to 1.35 ----Cu 0.50 --------(Nb+Ta) 8xC to 1.00; Cu 0.50 Nb 8xC to 1.00 Nb 10xC to 1.35 ----N 0.20; Cu 0.50 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASTM A743/A743M-13ae1 JIS G 5121:2003 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ISO 11972:1998 JIS G 5121:2003
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
416
7.4 Cast Stainless Steels 7.4.1 Cast Stainless Steels for General and Corrosion Resistant Applications 7.4.1.2A Chemical Composition of Austenitic Stainless Steels for General and Corrosion Resistant Applications (Continued)
Specification ASTM A743/A743M-13ae1 EN 10283:2010 ISO 11972:1998
JIS G 5121:2003 ASTM A743/A743M-13ae1 EN 10283:2010 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 EN 10283:2010 GB/T 2100-2002 ISO 11972:1998 JIS G 5121:2003 EN 10283:2010 GB/T 2100-2002 ISO 11972:1998 JIS G 5121:2003
UNS No. J92804 ------J93000 J93000 --J92999 J92999 --J93402 --N08007 N08007 ------J94652 --J94651 J94651 --J93254 J93254 ---------------------
Steel No. --1.4446 --------1.4412 --------------1.4458 1.4527 ----1.4416 ----1.4588 ----1.4557 1.4517 ------1.4468 ---------
C 0.03 0.030 0.03 0.03 0.08 0.08 0.07 0.03 0.03 0.03 0.20 0.20 0.07 0.07 0.030 0.06 0.07 0.03 0.030 0.03 0.03 0.025 0.025 0.025 0.025 0.030 0.03 0.03 0.03 0.030 0.03 0.03 0.03 0.03
Mn 1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50 2.00 1.50 1.50 2.00 1.50 2.00 2.0 1.00 2.00 2.00 2.00 1.20 1.20 1.20 1.50 1.5 1.50 1.50 2.00 1.5 1.50 1.50 1.50
Si 1.50 1.00 1.50 1.50 1.50 1.50 1.50 1.50 1.50 1.50 2.00 2.00 1.50 1.50 1.00 1.50 2.00 1.0 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.0 1.00 1.00 1.00 1.0 1.00 1.50 1.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 17.0-22.0 9.0-13.0 2.00-3.00 0.040 0.030 16.50-18.50 12.50-14.50 4.00-4.50 0.040 0.030 17.0-20.0 9.00-12.00 2.00-2.50 0.040 0.030 17.0-20.0 9.00-12.00 3.00-3.50 0.04 0.04 18.0-21.0 9.0-13.0 3.0-4.0 0.04 0.04 18.0-21.0 9.0-13.0 3.0-4.0 0.040 0.030 18.00-20.00 10.00-13.00 3.00-3.50 0.04 0.04 18.0-21.0 9.0-13.0 3.0-4.0 0.04 0.04 18.0-21.0 9.0-13.0 3.0-4.0 0.040 0.030 17.0-20.0 9.00-12.00 3.00-3.50 0.04 0.04 22.0-26.0 12.0-15.0 --0.040 0.040 22.00-26.00 12.00-15.00 --0.04 0.04 19.0-22.0 27.5-30.5 2.0-3.0 0.04 0.04 19.0-22.0 27.5-30.5 2.0-3.0 0.035 0.025 19.00-22.00 26.00-30.00 2.00-2.50 0.040 0.030 19.00-22.00 27.50-30.50 2.00-3.00 0.040 0.040 19.00-22.00 27.50-30.00 2.00-3.00 0.03 0.03 20.0-22.0 23.0-27.0 4.50-5.50 0.035 0.020 19.00-21.00 24.00-26.00 4.50-5.50 0.040 0.010 20.0-22.0 23.5-25.5 6.0-7.0 0.040 0.010 20.0-22.0 23.5-25.5 6.00-7.00 0.035 0.020 19.00-21.00 24.00-26.00 6.00-7.00 0.045 0.010 19.5-20.5 17.5-19.5 6.0-7.0 0.045 0.010 19.5-20.5 17.5-19.5 6.0-7.0 0.030 0.010 19.50-20.50 17.50-19.50 6.00-7.00 0.035 0.025 24.50-26.50 5.00-7.00 2.50-3.50 0.035 0.025 25.0-27.0 4.5-6.5 2.5-3.5 0.035 0.025 25.0-27.0 4.50-6.50 2.50-3.50 0.035 0.025 25.00-27.00 4.50-6.50 2.50-3.50 0.035 0.025 24.50-26.50 5.50-7.00 2.50-3.50 0.035 0.025 25.0-27.0 4.5-6.5 2.5-3.5 0.035 0.025 25.0-27.0 4.50-6.50 2.50-3.50 0.040 0.030 21.00-26.00 4.50-8.50 2.50-4.00 0.035 0.025 25.00-27.00 4.50-6.50 2.50-3.50
Others N 0.10-0.20 N 0.12-0.22; Cu 0.50 N 0.10-0.20 N 0.10-0.20 ----------------Cu 3.0-4.0 Cu 3.0-4.0 Cu 2.00; N 0.20 Cu 3.00-4.00 Cu 3.00-4.00 --N 0.12-0.20; Cu 0.50 Cu 0.75; N 0.18-0.26 Cu 0.75; N 0.18-0.26 Cu 0.50-1.50; N 0.10-0.25 Cu 0.50-1.00; N 0.180-0.240 Cu 0.50-1.00; N 0.180-0.240 Cu 0.50-1.00; N 0.18-0.24 Cu 2.75-3.50; N 0.12-0.22 Cu 2.4-3.5; N 0.12-0.25 Cu 2.50-3.50; N 0.12-0.25 Cu 2.50-3.50; N 0.12-0.25 N 0.12-0.25; Cu 0.50 N 0.12-0.25 N 0.12-0.25 N 0.08-0.30 N 0.12-0.25
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 ISO 11972:1998 ASTM A743/A743M-13ae1 JIS G 5121:2003 ASTM A743/A743M-13ae1 ASTM A744/A744M-13 EN 10283:2010
Designation Grade CF3MN GX2CrNiMoN17-13-4 Grade GX 2 CrNiMoN 19 11 2 Grade GX 2 CrNiMoN 19 11 3 Grade CG8M Grade CG8M GX5CrNiMo19-11-3 Grade CG3M Grade CG3M Grade GX 2 CrNiMo 19 11 3 Grade CH20 Class SCS 17 Grade CN7M Grade CN7M GX2NiCrMo28-20-2 GX4NiCrCuMo30-20-4 Class SCS 23 Grade CN3M GX2NiCrMoN25-20-5 Grade CN3MN Grade CN3MN GX2NiCrMoCuN25-20-6 Grade CK3MCuN Grade CK3MCuN GX2CrNiMoCuN20-18-6 GX2CrNiMoCuN25-6-3-3 Grade ZG03Cr26Ni5Cu3Mo3N Grade GX 2 CrNiCuMoN 26 5 3 3 Class SCS 32 GX2CrNiMoN25-6-3 Grade ZG03Cr26Ni5Mo3N Grade GX 2 CrNiMoN 26 5 3 Class SCS 10 Class SCS 33
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
417
7.4 Cast Stainless Steels 7.4.1 Cast Stainless Steels for General and Corrosion Resistant Applications 7.4.1.2B Mechanical Properties of Austenitic Stainless Steels for General and Corrosion Resistant Applications UNS No. J92602 --J92600 J92600 --------J92500 J92500 --------J92710 J92710 ------J92900 J92900 ----------------J92800 J92800 -------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. ----205 30 485 70 30 ----205 --480 --28 ----205 30 485 70 35 ----205 30 485 70 35 1.4308 t ≤ 150 175 --440 --30 --t ≤ 150 180 --440 --30 ----185 --440 --30 ----205 --480 --33 ----205 30 485 70 35 ----205 30 485 70 35 1.4309 t ≤ 150 185 --440 --30 --t ≤ 150 180 --440 --30 ----205 --480 --33 ----185 --390 --33 ----205 30 485 70 30 ----205 30 485 70 30 1.4552 t ≤ 150 175 --440 --25 --t ≤ 150 180 --440 --25 ----205 --480 --28 ----205 30 485 70 30 ----205 30 485 70 30 1.4408 t ≤ 150 185 --440 --30 --t ≤ 150 180 --440 --30 --t ≤ 150 180 --440 --30 ----185 --440 --28 ----205 --480 --33 1.4581 t ≤ 150 185 --440 --25 --t ≤ 150 180 --440 --25 ----205 --440 --28 ----205 30 485 70 30 ----205 30 485 70 30 1.4409 t ≤ 150 195 --440 --30 --t ≤ 150 180 --440 --30 ----205 --480 --33
Heat Treatment Q ST Q Q SA+Q ST+Q ST ST AC or Q Q SA+Q ST+Q ST ST Q Q SA+Q ST+Q ST Q Q SA+Q ST+Q ST+Q ST ST SA+Q ST+Q ST AC or Q Q SA+Q ST+Q ST
Other --183 max HB ----60 J @ RT 60 J @ RT 183 max HB 183 max HB ----80 J @ RT 80 J @ RT 183 max HB 183 max HB ----40 J @ RT 40 J @ RT 183 max HB ----60 J @ RT 60 J @ RT 60 J @ RT 183 max HB 183 max HB 40 J @ RT 40 J @ RT 183 max HB ----80 J @ RT 80 J @ RT 183 max HB
Download From http://bbs.infoeach.com
Designation Grade CF20 Class SCS 12 Grade CF8 Grade CF8 GX5CrNi19-10 Grade GX 5 CrNi 19 9 Class SCS 13 Class SCS 13A ASTM A743/A743M-13ae1* Grade CF3 ASTM A744/A744M-13* Grade CF3 EN 10283:2010 GX2CrNi19-11 ISO 11972:1998 Grade GX 2 CrNi 18 10 JIS G 5121:2003 Class SCS 19A Class SCS 19 ASTM A743/A743M-13ae1* Grade CF8C ASTM A744/A744M-13* Grade CF8C EN 10283:2010 GX5CrNiNb19-11 ISO 11972:1998 Grade GX 6 CrNiNb 19 10 JIS G 5121:2003 Class SCS 21 ASTM A743/A743M-13ae1* Grade CF8M ASTM A744/A744M-13* Grade CF8M EN 10283:2010 GX5CrNiMo19-11-2 ISO 11972:1998 Grade GX 5 CrNiMo 19 11 2 Grade GX 5 CrNiMo 19 11 3 JIS G 5121:2003 Class SCS 14 Class SCS 14A EN 10283:2010 GX5CrNiMoNb19-11-2 ISO 11972:1998 Grade GX 6 CrNiMoNb 19 11 2 JIS G 5121:2003 Class SCS 22 ASTM A743/A743M-13ae1* Grade CF3M ASTM A744/A744M-13* Grade CF3M EN 10283:2010 GX2CrNiMo19-11-2 ISO 11972:1998 Grade GX 2 CrNiMo 19 11 2 JIS G 5121:2003 Class SCS 16A *: See "List of Standards" at the beginning of the chapter.
Download From http://bbs.infoeach.com
Specification ASTM A743/A743M-13ae1* JIS G 5121:2003 ASTM A743/A743M-13ae1* ASTM A744/A744M-13* EN 10283:2010 ISO 11972:1998 JIS G 5121:2003
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
418
7.4 Cast Stainless Steels 7.4.1 Cast Stainless Steels for General and Corrosion Resistant Applications 7.4.1.2B Mechanical Properties of Austenitic Stainless Steels for General and Corrosion Resistant Applications (Continued)
Specification ASTM A743/A743M-13ae1* EN 10283:2010 ISO 11972:1998
UNS No. J92804 ------J93000 J93000 --J92999 J92999 --J93402 --N08007 N08007 ------J94652 --J94651 J94651 --J93254 J93254 ---------------------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. ----255 37 515 75 35 1.4446 t ≤ 150 210 --440 --20 --t ≤ 150 230 --510 --30 --t ≤ 150 230 --510 --30 ----240 35 520 75 25 ----240 35 520 75 25 1.4412 t ≤ 150 205 --440 --30 ----240 35 515 75 25 ----240 35 515 75 25 --t ≤ 150 180 --440 --30 ----205 30 485 70 30 ----205 --480 --28 ----170 25 425 62 35 ----170 25 425 62 35 1.4458 t ≤ 150 165 --430 --30 1.4527 t ≤ 150 170 --430 --35 ----165 --390 --30 ----170 25 435 63 30 1.4416 t ≤ 150 185 --450 --30 ----260 38 550 80 35 ----260 38 550 80 35 1.4588 t ≤ 50 210 --480 --30 ----260 38 550 80 35 ----260 38 550 80 35 1.4557 t ≤ 50 260 --500 --35 1.4517 t ≤ 150 480 --650 --22 --t ≤ 150 450 --650 --18 --t ≤ 150 450 --650 --18 ----450 --650 --18 1.4468 t ≤ 150 480 --650 --22 --t ≤ 150 450 --650 --18 --t ≤ 150 450 --650 --18 ----390 --620 --15 ----450 --650 --18
Heat Treatment AC or Q SA+Q ST+Q ST+Q Q Q SA+Q Q Q ST+Q Q ST Q Q SA+Q SA+Q ST Q SA+Q Q Q SA+Q Q Q SA+Q SA+Q SA+Q SA+Q ST SA+Q ST+Q SA+Q ST ST
Other --50 J @ RT 80 J @ RT 80 J @ RT ----60 J @ RT ----80 J @ RT --183 max. HB ----60 J @ RT 60 J @ RT 183 max. HB --60 J @ RT ----60 J @ RT ----50 J @ RT 50 J @ RT 50 J 50 J @ RT 50 J @ 20°C 50 J @ RT 50 J 50 J @ RT
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Designation Grade CF3MN GX2CrNiMoN17-13-4 Grade GX 2 CrNiMoN 19 11 2 Grade GX 2 CrNiMoN 19 11 3 ASTM A743/A743M-13ae1* Grade CG8M ASTM A744/A744M-13* Grade CG8M EN 10283:2010 GX5CrNiMo19-11-3 ASTM A743/A743M-13ae1* Grade CG3M ASTM A744/A744M-13* Grade CG3M ISO 11972:1998 Grade GX 2 CrNiMo 19 11 3 ASTM A743/A743M-13ae1* Grade CH20 JIS G 5121:2003 Class SCS 17 ASTM A743/A743M-13ae1* Grade CN7M ASTM A744/A744M-13* Grade CN7M EN 10283:2010 GX2NiCrMo28-20-2 GX4NiCrCuMo30-20-4 JIS G 5121:2003 Class SCS 23 ASTM A743/A743M-13ae1* Grade CN3M EN 10283:2010 GX2NiCrMoN25-20-5 ASTM A743/A743M-13ae1* Grade CN3MN ASTM A744/A744M-13* Grade CN3MN EN 10283:2010 GX2NiCrMoCuN25-20-6 ASTM A743/A743M-13ae1* Grade CK3MCuN ASTM A744/A744M-13* Grade CK3MCuN EN 10283:2010 GX2CrNiMoCuN20-18-6 EN 10283:2010 GX2CrNiMoCuN25-6-3-3 GB/T 2100-2002 Grade ZG03Cr26Ni5Cu3Mo3N ISO 11972:1998 Grade GX 2 CrNiCuMoN 26 5 3 3 JIS G 5121:2003 Class SCS 32 EN 10283:2010 GX2CrNiMoN25-6-3 GB/T 2100-2002 Grade ZG03Cr26Ni5Mo3N ISO 11972:1998 Grade GX 2 CrNiMoN 26 5 3 JIS G 5121:2003 Class SCS 10 Class SCS 33 *: See "List of Standards" at the beginning of the chapter.
302 max. HB
50 J @ 20°C
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
419
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.1A Chemical Composition of Martensitic and Ferritic Stainless Steels for Pressure Purposes UNS Steel No. No. J91150 --J91150 ---
C 0.15 0.15
Mn 1.00 1.00
Si 1.50 1.50
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 11.5-14.0 1.00 0.50 0.040 0.040 11.5-14.0 1.00 0.50
Grade CA15, Class B
J91150
---
0.15
1.00
1.50
0.040
0.040
11.5-14.0
1.00
0.50
Grade CA15, Class C
J91150
---
0.15
1.00
1.50
0.040
0.040
11.5-14.0
1.00
0.50
Grade CA15, Class D
J91150
---
0.15
1.00
1.50
0.040
0.040
11.5-14.0
1.00
0.50
Grade CA15 Grade CA15, Class A
J91150 J91150
-----
0.15 0.15
1.00 1.00
1.50 1.50
0.040 0.035
0.025 0.035
11.5-14.0 11.5-14.0
1.00 1.00
0.50 0.50
Grade CA15, Class B
J91150
---
0.15
1.00
1.50
0.035
0.035
11.5-14.0
1.00
0.50
Grade CA15, Class C
J91150
---
0.15
1.00
1.50
0.035
0.035
11.5-14.0
1.00
0.50
Grade CA15, Class D
J91150
---
0.15
1.00
1.50
0.035
0.035
11.5-14.0
1.00
0.50
Grade ZG14Cr12Ni1MoG Type C39CH GX4CrNi13-4 GX3CrNi13-4 Grade ZG08Cr12Ni4Mo1D Grade ZG08Cr12Ni4Mo1G Type C39NiH Type C39NiL Grade CA6NM Grade CA6NM, Class A
----0.10-0.17 ----0.10-0.17 --1.4317 0.06 --1.6982 0.05 ----0.08 ----0.08 ----0.08 ----0.08 J91540 --0.06 J91540 --0.06
1.00 1.00 1.00 1.00 1.50 1.50 1.50 1.50 1.00 1.00
0.80 0.80 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
0.035 0.035 0.035 0.035 0.030 0.035 0.035 0.030 0.04 0.04
0.035 0.035 0.025 0.015 0.030 0.035 0.035 0.030 0.03 0.03
11.5-13.5 11.50-13.50 12.00-13.50 12.00-13.50 11.5-13.5 11.5-13.5 11.50-13.50 11.50-13.50 11.5-14.0 11.5-14.0
1.00 1.00 3.50-5.00 3.50-5.00 3.50-5.00 3.50-5.00 3.50-5.00 3.50-5.00 3.5-4.5 3.5-4.5
0.50 0.50 0.70 0.70 1.00 1.00 1.00 1.00 0.4-1.0 0.4-1.0
Grade CA6NM, Class B
J91540
---
0.06
1.00
1.00
0.04
0.03
11.5-14.0
3.5-4.5
0.4-1.0
ASTM A352/A352M-06 (2012) Grade CA6NM ASTM A487/A487M-14 Grade CA6NM, Class A
J91540 J91540
-----
0.06 0.06
1.00 1.00
1.00 1.00
0.04 0.035
0.03 0.03
11.5-14.0 11.5-14.0
3.5-4.5 3.5-4.5
0.4-1.0 0.4-1.0
Grade CA6NM, Class B
J91540
---
0.06
1.00
1.00
0.035
0.03
11.5-14.0
3.5-4.5
0.4-1.0
Grade E3N
J91550
---
0.06
1.00
1.00
0.030
0.030
11.5-14.0
3.5-4.5
0.40-1.0
Download From http://bbs.infoeach.com
ASTM A217/A217M-14 ASTM A487/A487M-14
GB/T 16253-1996 ISO 4991:1994 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-352/SA-352M ASME SA-487/SA-487M
ASTM A757/A757M-15
Others --Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 --Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 ----V 0.08; Cu 0.30 V 0.08; Cu 0.30 ----------Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 --Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; V 0.05; (Cu+W+V) 0.50 Cu 0.50; W 0.10; (Cu+W+P+S) 0.50
Download From http://bbs.infoeach.com
Designation Grade CA15 Grade CA15, Class A
Specification ASME SA-217/SA-217M ASME SA-487/SA-487M
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
420
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.1A Chemical Composition of Martensitic and Ferritic Stainless Steels for Pressure Purposes (Continued)
Designation GX23CrMoV12-1 Grade ZG23Cr12Mo1NiVG Type C40H GX8CrNi12 Grade ZG08Cr12Ni1MoG Type C39CNiH
UNS No. -------------
Steel No. 1.4931 ----1.4107 -----
C 0.20-0.26 0.20-0.26 0.20-0.26 0.10 0.05-0.10 0.05-0.10
Mn 0.50-0.80 0.50-0.70 0.50-0.70 0.50-0.80 0.40-0.80 0.40-0.80
Si 0.40 0.20-0.40 0.20-0.40 0.40 0.80 0.80
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.030 0.020 11.30-12.20 1.00 1.00-1.20 0.035 0.035 11.3-12.3 0.70-1.00 1.00-1.20 0.035 0.035 11.30-12.30 0.70-1.00 1.00-1.20 0.030 0.020 11.50-12.50 0.80-1.50 0.50 0.035 0.035 11.5-13.0 0.80-1.80 0.20-0.50 0.035 0.035 11.50-13.00 0.80-1.80 0.20-0.50
Others V 0.25-0.35; Cu 0.30; W 0.50 V 0.25-0.35 V 0.25-0.35 V 0.08; Cu 0.30 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
421
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.1B Mechanical Properties of Martensitic and Ferritic Stainless Steels for Pressure Purposes
Specification ASME SA-217/SA-217M ASME SA-487/SA-487M
GB/T 16253-1996 ISO 4991:1994
Grade ZG08Cr12Ni1MoG Type C39CNiH
UNS No. J91150 J91150 J91150 J91150 J91150 J91150 J91150 J91150 J91150 J91150 ----------------J91540 J91540 J91540 J91540 J91540 J91540 J91550 -------------
Steel Section Yield Strength, min. No. Thickness, mm MPa ksi ----450 65 ----760-895 110-130 ----450 65 ----415 60 ----515 75 ----450 65 ----760-895 110-130 ----450 65 ----415 60 ----515 75 ----450 ------450 --1.4317 t ≤ 300 550 --1.6982 t ≤ 300 500 ------550 ------550 ------550 ------550 ------550 80.0 ----550 80 ----515 75 ----550 80.0 ----550 80 ----515 75 ----550 80 1.4931 t ≤ 150 540 ------540 ------540 --1.4107 t ≤ 300 355 --t ≤ 300 500 ------360 ------360 ---
Tensile Strength, min. Elongation MPa ksi % min. 620-795 90-115 18 965-1170 140-170 10 620-795 90-115 18 620 90 18 690 100 17 620-795 90-115 18 965-1170 140-170 10 620-795 90-115 18 620 90 18 690 100 17 620-770 --14 620-770 --14 760-960 --15 700-900 --15 750-900 --15 750-900 --15 750-900 --15 750-900 --15 760-930 110.0-135.0 15 760-930 110-135 15 690 100 17 760-930 110.0-135.0 15 760-930 110-135 15 690 100 17 760 110 15 740-880 --15 740-880 --15 740-880 --15 540-690 --18 600-800 --16 540-690 --18 540-690 --18
Heat Treatment N+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T N+T or Q+T N+T or Q+T N+T or Q+T N+T or Q+T N+T N+T Q+T Q+T N+T N+T N+T N+T N+T N+T or Q+T N+T or Q+T N+T N+T or Q+T N+T or Q+T N+T Q+T N+T N+T Q+T Q+T N+T N+T
Other ------235 max HB; 22 max HRC 235 max HB; 22 max HRC ------235 max HB; 22 max HRC 235 max HB; 22 max HRC 20 J @ RT 20 J @ RT 50 J @ RT 27 J @ -120°C 27 J @ -80°C 45 J @ RT 45 J @ RT 27 J @ -80°C 27 J @ -73°C --255 max HB; 23 max HRC 27 J @ -73°C --255 max HB; 23 max HRC L: 27 J @ -73°C 27 J @ RT 21 J @ RT 21 J @ RT 45 J @ RT 40 J @ RT 35 J @ RT 35 J @ RT
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Designation Grade CA15 Grade CA15, Class A Grade CA15, Class B Grade CA15, Class C Grade CA15, Class D ASTM A217/A217M-14 Grade CA15 ASTM A487/A487M-14 Grade CA15, Class A Grade CA15, Class B Grade CA15, Class C Grade CA15, Class D GB/T 16253-1996 Grade ZG14Cr12Ni1MoG ISO 4991:1994 Type C39CH EN 10213:2007 C1:2008 GX4CrNi13-4 GX3CrNi13-4 GB/T 16253-1996 Grade ZG08Cr12Ni4Mo1D Grade ZG08Cr12Ni4Mo1G ISO 4991:1994 Type C39NiH Type C39NiL ASME SA-352/SA-352M Grade CA6NM ASME SA-487/SA-487M Grade CA6NM, Class A Grade CA6NM, Class B ASTM A352/A352M-06 (2012) Grade CA6NM ASTM A487/A487M-14 Grade CA6NM, Class A Grade CA6NM, Class B ASTM A757/A757M-15 Grade E3N EN 10213:2007 C1:2008 GX23CrMoV12-1 GB/T 16253-1996 Grade ZG23Cr12Mo1NiVG ISO 4991:1994 Type C40H EN 10213:2007 C1:2008 GX8CrNi12
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
422
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.2A Chemical Composition of Austenitic Stainless Steels for Pressure Purposes
Specification ASME SA-351/SA-351M ASTM A351/A351M-14
ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994
UNS No. J92600 J92600 J92600 J92600 ------J92700 J92700 J92700 J92700 ------J92710 J92710 ------J92900 J92900 -----------------
Steel No. --------1.4308 ------------1.4309 --------1.4552 --------1.4408 --------1.4581 -----
C 0.08 0.08 0.08 0.08 0.07 0.07 0.07 0.03 0.03 0.03 0.03 0.030 0.03 0.03 0.08 0.08 0.07 0.08 0.08 0.08 0.08 0.07 0.07 0.07 0.07 0.07 0.07 0.08 0.08
Mn 1.50 1.50 1.50 1.50 1.50 2.00 2.00 1.50 1.50 1.50 1.50 2.00 2.00 2.00 1.50 1.50 1.50 2.00 2.00 1.50 1.50 1.50 2.00 2.00 2.00 2.00 1.50 2.00 2.00
Si 2.00 2.00 2.00 2.00 1.50 2.00 2.00 2.00 2.00 2.00 2.00 1.50 2.00 2.00 2.00 2.00 1.50 2.00 2.00 1.50 1.50 1.50 2.00 2.00 2.00 2.00 1.50 2.00 2.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 18.0-21.0 8.0-11.0 0.50 0.040 0.040 18.0-21.0 8.0-11.0 0.50 0.040 0.040 18.0-21.0 8.0-11.0 0.50 0.040 0.040 18.0-21.0 8.0-11.0 0.50 0.040 0.030 18.00-20.00 8.00-11.00 --0.045 0.035 18.0-21.0 8.0-11.0 --0.045 0.035 18.00-21.00 8.00-11.00 --0.040 0.040 17.0-21.0 8.0-12.0 0.50 0.040 0.040 17.0-21.0 8.0-12.0 0.50 0.040 0.040 17.0-21.0 8.0-12.0 0.50 0.040 0.040 17.0-21.0 8.0-12.0 0.50 0.035 0.025 18.00-20.00 9.00-12.00 --0.045 0.035 17.0-19.0 9.0-12.0 --0.045 0.035 17.00-19.00 9.00-12.00 --0.040 0.040 18.0-21.0 9.0-12.0 0.50 0.040 0.040 18.0-21.0 9.0-12.0 0.50 0.040 0.030 18.00-20.00 9.00-12.00 --0.045 0.035 18.0-21.0 9.0-12.0 --0.045 0.035 18.00-21.00 9.00-12.00 --0.040 0.040 18.0-21.0 9.0-12.0 2.0-3.0 0.040 0.040 18.0-21.0 9.0-12.0 2.0-3.0 0.040 0.030 18.00-20.00 9.00-12.00 2.00-2.50 0.045 0.035 17.0-21.0 9.0-13.0 2.0-2.5 0.045 0.035 17.0-21.0 9.0-13.0 2.5-3.0 0.045 0.035 17.00-21.00 9.00-13.00 2.00-2.50 0.045 0.035 17.00-21.00 9.00-13.00 2.50-3.00 0.040 0.030 18.00-12.00 9.00-12.00 2.00-2.50 0.045 0.035 17.0-21.0 9.0-13.0 2.0-2.5 0.045 0.035 17.00-21.00 9.00-13.00 2.00-2.50
Others --------Cu 0.50 ------------N 0.20; Cu 0.50 ----Cb 8xC to 1.00 Cb 8xC to 1.00 Nb 8xC to 1.00; Cu 0.50 Nb 8xC to 1.0 Nb 8xC to 1.0 ----Cu 0.50 --------Nb 8xC to 1.00; Cu 0.50 Nb 8xC to 1.0 Nb 8xC to 1.0
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M
Designation Grade CF8 Grade CF8A Grade CF8 Grade CF8A GX5CrNi19-10 Grade ZG07Cr20Ni10 Type C47 Grade CF3 Grade CF3A Grade CF3 Grade CF3A GX2CrNi19-11 Grade ZG03Cr18Ni10 Type C46 Grade CF8C Grade CF8C GX5CrNiNb19-11 Grade ZG08Cr20Ni10Nb Type C50 Grade CF8M Grade CF8M GX5CrNiMo19-11-2 Grade ZG07Cr19Ni11Mo2 Grade ZG07Cr19Ni11Mo3 Type C60 Type C61 GX5CrNiMoNb19-11-2 Grade ZG08Cr19Ni11Mo2Nb Type C60Nb
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
423
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.2A Chemical Composition of Austenitic Stainless Steels for Pressure Purposes (Continued)
Specification ASME SA-351/SA-351M ASTM A351/A351M-14
ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 GB/T 16253-1996 ISO 4991:1994 GB/T 16253-1996 ISO 4991:1994
UNS Steel No. No. J92800 --J92800 --J92800 --J92800 ----1.4409 ----------------N08007 --N08007 ----1.4458 --------J92901 --J92901 -------------------
C 0.03 0.03 0.03 0.03 0.030 0.03 0.03 0.03 0.03 0.07 0.07 0.030 0.04-0.10 0.04-0.10 0.04-0.10 0.04-0.10 0.04-0.10 0.04-0.10 0.07 0.07
Mn 1.50 1.50 1.50 1.50 2.00 2.00 2.00 2.00 2.00 1.50 1.50 2.00 2.00 2.00 1.50 1.50 2.00 2.00 2.00 2.00
Si 1.50 1.50 1.50 1.50 1.50 2.00 2.00 2.00 2.00 1.50 1.50 1.00 2.00 2.00 1.50 1.50 2.00 2.00 2.00 2.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.040 17.0-21.0 9.0-13.0 2.0-3.0 0.040 0.040 17.0-21.0 9.0-13.0 2.0-3.0 0.040 0.040 17.0-21.0 9.0-13.0 2.0-3.0 0.040 0.040 17.0-21.0 9.0-13.0 2.0-3.0 0.035 0.025 18.00-20.00 9.00-12.00 2.00-2.50 0.045 0.035 17.0-21.0 9.0-13.0 2.0-2.5 0.045 0.035 17.0-21.0 9.0-13.0 2.5-3.0 0.045 0.035 17.00-21.00 9.00-13.00 2.00-2.50 0.045 0.035 17.00-21.00 9.00-13.00 2.50-3.00 0.040 0.040 19.0-22.0 27.5-30.5 2.0-3.0 0.040 0.040 19.0-22.0 27.5-30.5 2.0-3.0 0.035 0.025 19.00-22.00 26.00-30.00 2.00-2.50 0.045 0.035 18.0-21.0 8.0-12.0 --0.045 0.035 18.00-21.00 8.00-12.00 --0.040 0.040 18.0-21.0 9.0-12.0 2.0-3.0 0.040 0.040 18.0-21.0 9.0-12.0 2.0-3.0 0.045 0.035 17.0-21.0 9.0-13.0 2.0-2.5 0.045 0.035 17.00-21.00 9.00-13.00 2.00-2.50 0.045 0.035 17.0-20.0 9.0-12.0 --0.045 0.035 17.00-20.00 9.00-12.00 ---
Others --------N 0.20; Cu 0.50 --------Cu 3.0-4.0 Cu 3.0-4.0 N 0.20; Cu 2.00 -----------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10213:2007 C1:2008 GB/T 16253-1996
Designation Grade CF3M Grade CF3MA Grade CF3M Grade CF3MA GX2CrNiMo19-11-2 Grade ZG03Cr19Ni11Mo2 Grade ZG03Cr19Ni11Mo3 Type C57 Type C61LC Grade CN7M Grade CN7M GX2NiCrMo28-20-2 Grade ZG07Cr20Ni10G Type C47H Grade CF10M Grade CF10M Grade ZG07Cr19Ni11Mo2G Type C60H Grade ZG07Cr18Ni10D Type C47L
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
424
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.2B Mechanical Properties of Austenitic Stainless Steels for Pressure Purposes
Specification ASME SA-351/SA-351M ASTM A351/A351M-14
ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994
UNS No. J92600 J92600 J92600 J92600 ------J92700 J92700 J92700 J92700 ------J92710 J92710 ------J92900 J92900 -----------------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. ----205 30 485 70 35.0 ----240 35 530 77 35.0 ----205 30 485 70 35.0 ----240 35 530 77 35.0 1.4308 t ≤ 150 200 --440-640 --30 ----210 --440-640 --30 ----210 --440-640 --30 ----205 30 485 70 35.0 ----240 35 530 77 35.0 ----205 30 485 70 35.0 ----240 35 530 77 35.0 1.4309 t ≤ 150 210 --440-640 --30 ----210 --440-640 --30 ----210 --440-640 --30 ----205 30 485 70 30.0 ----205 30 485 70 30.0 1.4552 t ≤ 150 200 --440-640 --25 ----210 --440-640 --25 ----210 --440-640 --25 ----205 30 485 70 30.0 ----205 30 485 70 30.0 1.4408 t ≤ 150 210 --440-640 --30 ----210 --440-640 --30 ----210 --440-640 --30 ----210 --440-640 --30 ----210 --440-640 --30 1.4581 t ≤ 150 210 --440-640 --25 ----210 --440-640 --25 ----210 --440-640 --25
Heat Treatment Q Q Q Q SA+Q ST ST Q Q Q Q SA+Q ST ST Q Q SA+Q ST ST Q Q SA+Q ST ST ST ST SA+Q ST ST
Other --------60 J @ -196°C ------------70 J @ -196°C --------40 J @ RT --------60 J @ -196°C --------40 J @ RT -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M
Designation Grade CF8 Grade CF8A Grade CF8 Grade CF8A GX5CrNi19-10 Grade ZG07Cr20Ni10 Type C47 Grade CF3 Grade CF3A Grade CF3 Grade CF3A GX2CrNi19-11 Grade ZG03Cr18Ni10 Type C46 Grade CF8C Grade CF8C GX5CrNiNb19-11 Grade ZG08Cr20Ni10Nb Type C50 Grade CF8M Grade CF8M GX5CrNiMo19-11-2 Grade ZG07Cr19Ni11Mo2 Grade ZG07Cr19Ni11Mo3 Type C60 Type C61 GX5CrNiMoNb19-11-2 Grade ZG08Cr19Ni11Mo2Nb Type C60Nb
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
425
7.4 Cast Stainless Steels 7.4.2 Cast Stainless Steels for Pressure Purposes 7.4.2.2B Mechanical Properties of Austenitic Stainless Steels for Pressure Purposes (Continued)
Specification ASME SA-351/SA-351M ASTM A351/A351M-14
ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 EN 10213:2007 C1:2008 GB/T 16253-1996 ISO 4991:1994 ASME SA-351/SA-351M ASTM A351/A351M-14 GB/T 16253-1996 ISO 4991:1994 GB/T 16253-1996 ISO 4991:1994
UNS Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. No. Thickness, mm MPa ksi MPa ksi % min. J92800 ----205 30 485 70 30.0 J92800 ----255 37 550 80 30.0 J92800 ----205 30 485 70 30.0 J92800 ----255 37 550 80 30.0 --1.4409 t ≤ 150 220 --440-640 --30 ------210 --440-620 --30 ------210 --440-640 --30 ------210 --440-620 --30 ------210 --440-640 --30 N08007 ----170 25 425 62 35.0 N08007 ----170 25 425 62 35.0 --1.4458 t ≤ 150 190 --430-630 --30 ------230 --470-670 --30 ------230 --470-670 --30 J92901 ----205 30 485 70 30.0 J92901 ----205 30 485 70 30.0 ------230 --470-670 --30 ------230 --470-670 --30 ------210 --440-640 --30 ------210 --440-640 --30
Heat Treatment Q Q Q Q SA+Q ST ST ST ST Q Q SA+Q ST ST Q Q ST ST ST ST
Other --------70 J @ -196°C ------------60 J @ -196°C ------------45 J @ -195°C 45 J @ -195°C
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10213:2007 C1:2008 GB/T 16253-1996
Designation Grade CF3M Grade CF3MA Grade CF3M Grade CF3MA GX2CrNiMo19-11-2 Grade ZG03Cr19Ni11Mo2 Grade ZG03Cr19Ni11Mo3 Type C57 Type C61LC Grade CN7M Grade CN7M GX2NiCrMo28-20-2 Grade ZG07Cr20Ni10G Type C47H Grade CF10M Grade CF10M Grade ZG07Cr19Ni11Mo2G Type C60H Grade ZG07Cr18Ni10D Type C47L
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
426
7.5 Cast Heat Resistant Steels 7.5A Chemical Composition of Cast Heat Resistant Steels
Specification EN 10295:2002 ISO 11973:1999 JIS G 5122:2003
ISO 11973:1999 JIS G 5122:2003 EN 10295:2002 ISO 11973:1999
UNS No. ------------------------J92605 J92613 --J93005 J93015 ------J93403 J93413 --J92603 J92803 ---------------
Steel No. 1.4729 ------1.4740 --1.4745 --1.4776 --1.4777 ------------1.4823 --------------1.4825 1.4826 ------1.4832 ---
C 0.30-0.50 0.30-0.50 0.40 0.20-0.40 0.30-0.50 0.30-0.50 0.30-0.50 0.30-0.50 0.30-0.50 0.30-0.50 1.20-1.40 1.20-1.40 0.50 0.25-0.35 0.40 0.50 0.45-0.55 0.30-0.50 0.30-0.50 0.40 0.20-0.50 0.30-0.40 0.20-0.50 0.20-0.40 0.25-0.35 0.15-0.35 0.30-0.50 0.15-0.35 0.30-0.50 0.20-0.40 0.15-0.35 0.15-0.35
Mn 1.00 0.50-1.00 1.00 1.00 1.00 0.50-1.00 1.00 0.50-1.00 1.00 0.50-1.00 0.50-1.00 0.50-1.00 1.00 0.5-1.0 1.00 1.50 1.50 1.50 1.50 1.00 2.00 1.50 2.00 2.00 1.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 1.00-2.50 1.00-2.5 2.00 1.50-3.00 1.00-2.50 1.00-2.5 1.00-2.50 1.00-2.5 1.00-2.50 1.00-2.5 1.00-2.50 1.00-2.5 2.00 0.50-2.00 2.00 2.00 0.50-2.00 1.00-2.50 1.00-2.5 2.00 2.00 0.50-2.00 2.00 2.00 0.50-2.00 0.50-2.50 1.00-2.50 1.00-2.5 1.00-2.5 2.00 0.50-2.50 1.00-2.5
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.040 0.030 12.00-14.00 1.00 0.50 0.040 0.030 12.0-14.0 1.00 0.5 0.040 0.040 12.00-15.00 1.00 0.50 0.040 0.040 12.00-15.00 1.00 0.50 0.040 0.030 16.00-19.00 1.00 0.50 0.040 0.030 16.0-19.0 1.00 0.5 0.040 0.030 23.00-26.00 1.00 0.50 0.040 0.030 23.0-26.0 1.00 0.5 0.040 0.030 27.00-30.00 1.00 0.50 0.040 0.030 27.0-30.0 1.00 0.5 0.035 0.030 27.00-30.00 1.00 0.50 0.040 0.030 27.0-30.0 1.00 0.5 0.04 0.04 26.0-30.0 4.00 0.50 0.04 0.04 26-30 4.0 0.50 0.040 0.040 25.00-28.00 1.00 0.50 0.04 0.04 26.0-30.0 4.0-7.0 0.50 0.04 0.04 26-30 4-7 0.50 0.040 0.030 25.00-28.00 3.00-6.00 0.50 0.040 0.030 25.0-28.0 3.00-6.00 0.5 0.040 0.040 24.00-28.00 4.00-6.00 0.50 0.04 0.04 26.0-30.0 8.0-11.0 0.50 0.04 0.04 26-30 8-11 0.50 0.040 0.040 26.00-30.00 8.00-11.00 0.50 0.04 0.04 18.0-23.0 8.0-12.0 0.50 0.04 0.04 19-23 9-12 0.50 0.040 0.030 17.00-19.00 8.00-10.00 0.50 0.040 0.030 21.00-23.00 9.00-11.00 0.50 0.040 0.030 17.0-19.0 8.00-10.00 0.5 0.040 0.030 21.0-23.0 9.00-11.00 0.5 0.040 0.040 18.00-23.00 8.00-12.00 0.50 0.040 0.030 19.00-21.00 13.00-15.00 0.50 0.040 0.030 19.0-21.0 13.00-15.00 0.5
Others -----------------------------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 ASTM A297/A297M-14 ASTM A608/A608M-14 JIS G 5122:2003 ASTM A297/A297M-14 ASTM A608/A608M-14 EN 10295:2002 ISO 11973:1999 JIS G 5122:2003 ASTM A297/A297M-14 ASTM A608/A608M-14 JIS G 5122:2003 ASTM A297/A297M-14 ASTM A608/A608M-14 EN 10295:2002
Designation GX40CrSi13 Grade GX40CrSi13 Class SCH 3 Class SCH 1 GX40CrSi17 Grade GX40CrSi17 GX40CrSi24 Grade GX40CrSi24 GX40CrSi28 Grade GX40CrSi28 GX130CrSi29 Grade GX130CrSi29 Grade HC Grade HC30 Class SCH 2 Grade HD Grade HD50 GX40CrNiSi27-4 Grade GX40CrNiSi27-4 Class SCH 11 Grade HE Grade HE35 Class SCH 17 Grade HF Grade HF30 GX25CrNiSi18-9 GX40CrNiSi22-10 Grade GX25CrNiSi18-9 Grade GX40CrNiSi22-10 Class SCH 12 GX25CrNiSi20-14 Grade GX25 CrNiSi 20-14
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
427
7.5 Cast Heat Resistant Steels 7.5A Chemical Composition of Cast Heat Resistant Steels (Continued)
Specification ASTM A297/A297M-14 ASTM A447/A447M-11 ASTM A608/A608M-14
ASTM A297/A297M-14 ASTM A608/A608M-14 JIS G 5122:2003 ASME SA-351/SA-351M ASTM A297/A297M-14 ASTM A351/A351M-14 ASTM A608/A608M-14 JIS G 5122:2003 ASME SA-351/SA-351M ASTM A351/A351M-14 ASTM A608/A608M-14 EN 10295:2002 ISO 11973:1999 JIS G 5122:2003 ASTM A297/A297M-14 ASTM A608/A608M-14 JIS G 5122:2003
Grade HH Type I Type II Grade HH30 Grade HH33 GX40CrNiSi25-12 Grade GX40CrNiSi25-12 Class SCH 13 Class SCH 13A Grade HI Grade HI35 Class SCH 18 Grade HK30 Grade HK Grade HK30 Grade HK30 Class SCH 21 Grade HK40 Grade HK40 Grade HK40 GX40CrNiSi25-20 Grade GX40CrNiSi25-20 Class SCH 22 Grade HL Grade HL30 Grade HL40 Class SCH 23
UNS Steel No. No. J93503 --J93303 --J93303 --J93513 --J93633 ----1.4837 ------------J94003 --J94013 ------J94203 --J94224 --J94203 --J94203 ------J94204 --J94204 --J94204 ----1.4848 --------N08604 --N08613 --N08614 -------
C 0.20-0.50 0.20-0.45 0.20-0.45 0.25-0.35 0.28-0.38 0.30-0.50 0.30-0.50 0.20-0.50 0.25-0.50 0.20-0.50 0.30-0.40 0.20-0.50 0.25-0.35 0.20-0.60 0.25-0.35 0.25-0.35 0.25-0.35 0.35-0.45 0.35-0.45 0.35-0.45 0.30-0.50 0.30-0.50 0.35-0.45 0.20-0.60 0.25-0.35 0.35-0.45 0.20-0.60
Mn 2.00 2.50 2.50 1.50 1.50 2.00 2.00 2.00 2.50 2.00 1.50 2.00 1.50 2.00 1.50 1.50 1.50 1.50 1.50 1.50 2.00 2.00 1.50 2.00 1.50 1.50 2.00
Si 2.00 1.75 1.75 0.50-2.00 0.50-2.00 1.00-2.50 1.00-2.5 2.00 1.75 2.00 0.50-2.00 2.00 1.75 2.00 1.75 0.50-2.00 1.75 1.75 1.75 0.50-2.00 1.00-2.50 1.00-2.5 1.75 2.00 0.50-2.00 0.50-2.00 2.00
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.04 24.0-28.0 11.0-14.0 0.50 0.030 0.030 23.00-28.00 10.00-14.00 --0.030 0.030 23.00-28.00 10.00-14.00 --0.04 0.04 24-28 11-14 0.50 0.04 0.04 24-26 12-14 0.50 0.040 0.030 24.00-27.00 11.00-14.00 0.50 0.040 0.030 24.0-27.0 11.00-14.00 0.5 0.040 0.040 24.00-28.00 11.00-14.00 0.50 0.040 0.040 23.00-26.00 12.00-14.00 0.50 0.04 0.04 26.0-30.0 14.0-18.0 0.50 0.04 0.04 26-30 14-18 0.50 0.040 0.040 26.00-30.00 14.00-18.00 0.50 0.040 0.040 23.0-27.0 19.0-22.0 0.50 0.04 0.04 24.0-28.0 18.0-22.0 0.50 0.040 0.040 23.0-27.0 19.0-22.0 0.50 0.04 0.04 23-27 19-22 0.50 0.040 0.040 23.00-27.00 19.00-22.00 0.50 0.040 0.040 23.0-27.0 19.0-22.0 0.50 0.040 0.040 23.0-27.0 19.0-22.0 0.50 0.04 0.04 23-27 19-22 0.50 0.040 0.030 24.00-27.00 19.00-22.00 0.50 0.040 0.030 24.0-27.0 19.00-22.00 0.5 0.040 0.040 23.00-27.00 19.00-22.00 0.50 0.04 0.04 28.0-32.0 18.0-22.0 0.50 0.04 0.04 28-32 18-22 0.50 0.04 0.04 28-32 18-22 0.50 0.040 0.040 28.00-32.00 18.00-22.00 0.50
Others --N 0.20 N 0.20 -------------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10295:2002 ISO 11973:1999 JIS G 5122:2003
Designation
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
428
7.5 Cast Heat Resistant Steels 7.5A Chemical Composition of Cast Heat Resistant Steels (Continued)
ISO 11973:1999 JIS G 5122:2003 ASTM A297/A297M-14 ASTM A608/A608M-14 EN 10295:2002 ISO 11973:1999 JIS G 5122:2003 ASME SA-351/SA-351M ASTM A351/A351M-14 JIS G 5122:2003 ASTM A297/A297M-14 ASTM A608/A608M-14 EN 10295:2002
ISO 11973:1999 JIS G 5122:2003 EN 10295:2002 ISO 11973:1999
Designation Grade HN Grade HN40 GX35NiCrSi25-21 Class SCH 19 GX40CrNiSiNb24-24 Grade GX40CrNiSiNb24-24 Grade HP GX40NiCrSiNb35-26 GX40NiCrSi35-26 Grade GX40NiCrSi35-26 Grade GX40NiCrSiNb35-26 Class SCH 24 Grade HT Grade HT50 GX40NiCrSi35-17 Grade GX40NiCrSi35-17 Class SCH 15 Grade HT30 Grade HT30 Class SCH 16 Grade HU Grade HU50 GX40NiCrSiNb35-18 GX40NiCrSiNb38-19 GX40NiCrSi38-19 Grade GX40NiCrSi38-19 Grade GX40NiCrSiNb38-19 Class SCH 20 G-NiCr50Nb Grade GX10NiCrNb50-50
UNS No. J94213 J94214 --------N08705 ----------N08605 N08050 ------N08030 N08030 --N08004 N08005 -----------------
Steel No. ----1.4805 --1.4855 ----1.4852 1.4857 ----------1.4806 --------------1.4807 1.4849 1.4865 ------2.4680 ---
C 0.20-0.50 0.35-0.45 0.20-0.50 0.20-0.50 0.30-0.50 0.25-0.50 0.35-0.75 0.30-0.50 0.30-0.50 0.30-0.50 0.30-0.50 0.35-0.75 0.35-0.75 0.40-0.60 0.30-0.50 0.30-0.50 0.35-0.70 0.25-0.35 0.25-0.35 0.20-0.35 0.35-0.75 0.40-0.60 0.30-0.50 0.30-0.50 0.30-0.50 0.30-0.50 0.3-0.50 0.35-0.75 0.10 0.10
Mn 2.00 1.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 1.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 1.50 2.00 2.00 2.00 2.00 2.00 2.00 0.50 0.50
Si 2.00 0.50-2.00 1.00-2.00 2.00 1.00-2.50 1.00-2.5 2.50 1.00-2.50 1.00-2.50 1.00-2.50 1.00-2.50 2.00 2.50 0.50-2.00 1.00-2.50 1.00-2.50 2.50 2.50 2.50 2.50 2.50 0.50-2.00 1.00-2.50 1.00-2.50 1.00-2.50 1.00-2.50 1.00-2.50 2.50 1.00 0.50
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.04 19.0-23.0 23.0-27.0 0.50 0.04 0.04 19-23 23-27 0.50 0.040 0.030 19.00-23.00 23.00-27.00 0.50 0.040 0.040 19.00-23.00 23.00-27.00 0.50 0.040 0.030 23.00-25.00 23.00-25.00 0.50 0.040 0.030 23.0-25.0 23.00-25.00 0.5 0.04 0.04 24-28 33-37 0.50 0.040 0.030 24.00-27.00 33.00-36.00 0.50 0.040 0.030 24.00-27.00 33.00-36.00 0.50 0.040 0.030 24.0-27.0 33.00-36.00 0.50 0.040 0.030 24.0-27.0 33.00-36.00 0.50 0.040 0.040 24.00-28.00 33.00-37.00 0.50 0.04 0.04 15.0-19.0 33.0-37.0 0.50 0.04 0.04 15-19 33-37 0.50 0.040 0.030 16.00-18.00 34.00-36.00 0.50 0.040 0.030 16.0-18.0 34.00-36.00 0.50 0.040 0.040 15.00-19.00 33.00-37.00 0.50 0.040 0.040 13.0-17.0 33.0-37.0 0.50 0.040 0.040 13.0-17.0 33.0-37.0 0.50 0.040 0.040 13.00-17.00 33.00-37.00 0.50 0.04 0.04 17.0-21.0 37.0-41.0 0.50 0.04 0.04 17-21 37-41 0.50 0.040 0.030 17.00-20.00 34.00-36.00 0.50 0.040 0.030 18.00-21.00 36.00-39.00 0.50 0.040 0.030 18.00-21.00 36.00-39.00 0.50 0.040 0.030 18.0-21.0 36.00 0.50 0.040 0.030 18.0-21.0 36.00-39.00 0.50 0.040 0.040 17.00-21.00 37.00-41.00 0.50 0.020 0.020 48.00-52.00 --0.50 0.020 0.020 47.0-52.0 --0.50
Others --------Nb 0.80-1.80 Nb 1.20-1.80 --Nb 0.80-1.80 ----Nb 0.80-1.80 ----------------------Nb 1.00-1.80 Nb 1.20-1.80 ----Nb 1.20-1.80 --Nb 1.00-1.80; N 0.16; Fe 1.00 Nb 1.40-1.70; N 0.16
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASTM A297/A297M-14 ASTM A608/A608M-14 EN 10295:2002 JIS G 5122:2003 EN 10295:2002 ISO 11973:1999 ASTM A297/A297M-14 EN 10295:2002
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
429
7.5 Cast Heat Resistant Steels 7.5A Chemical Composition of Cast Heat Resistant Steels (Continued) UNS No. N08001 N06006 N08006 N06050 ---------------
Steel No. --------2.4815 --2.4778 --2.4879 --1.4874
C 0.35-0.75 0.35-0.75 0.40-0.60 0.40-0.60 0.35-0.65 0.35-0.65 0.05-0.25 0.50 0.35-0.55 0.35-0.55 0.35-0.65
Mn 2.00 2.00 1.50 1.50 2.00 1.30 1.50 1.00 1.50 1.50 2.00
Si 2.50 2.50 0.50-2.00 0.50-2.00 1.00-2.50 2.00 0.50-1.50 1.00 1.00-2.00 1.00-2.50 1.00
ISO 11973:1999
Grade GX40NiCrCo20-20-20
---
---
0.35-0.60
2.00
1.0
ASTM A608/A608M-14
Download From http://bbs.infoeach.com
Weight, %, max, Unless Otherwise Specified P S Cr Ni Mo 0.04 0.04 10.0-14.0 58.0-62.0 0.50 0.04 0.04 15.0-19.0 64.0-68.0 0.50 0.04 0.04 10-14 58-62 0.50 0.04 0.04 15-19 64-68 0.50 0.040 0.030 12.00-18.00 58.00-66.00 1.00 0.040 0.030 13.0-19.0 64.00-69.00 --0.040 0.030 27.00-30.00 4.00 0.50 0.040 0.030 25.0-30.0 1.00 0.50 0.040 0.030 27.00-30.00 47.00-50.00 0.50 0.040 0.030 27.0-30.0 47.00-50.00 --0.040 0.030 19.00-22.00 18.00-22.00 2.50-3.00 0.040
0.030
19.0-22.0
18.00-22.00
2.50-3.00
Others ------------Co 48.0-52.0; Nb 0.50 Co 48.00-52.00; Fe 20.0 W 4.00-6.00 W 4.00-6.00 W 2.00-3.00; Co 18,50-22.00; Nb 0.75-1.25 W 2.00-3.00; Co 18.00-22.00
Download From http://bbs.infoeach.com
EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 EN 10295:2002
Designation Grade HW Grade HX Grade HW50 Grade HX50 G-NiCr15 Grade GX50NiCr65-15 G-CoCr28 Grade GX30CoCr50-28 G-NiCr28W Grade GX45NiCrWSi48-28-5 GX50NiCrCo20-20-20
Specification ASTM A297/A297M-14
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
430
7.5 Cast Heat Resistant Steels 7.5B Mechanical Properties of Cast Heat Resistant Steels UNS No. ------------------------J92605 J92613
JIS G 5122:2003 ASTM A297/A297M-14* ASTM A608/A608M-14*
Class SCH 2 Grade HD Grade HD50
--J93005 J93015
EN 10295:2002 ISO 11973:1999 JIS G 5122:2003 ASTM A297/A297M-14* JIS G 5122:2003 ASTM A297/A297M-14* ASTM A608/A608M-14*
GX40CrNiSi27-4 Grade GX40CrNiSi27-4 Class SCH 11 Grade HE Class SCH 17 Grade HF Grade HF30
------J93403 --J92603 J92803
Download From http://bbs.infoeach.com
EN 10295:2002
GX25CrNiSi18-9 GX40CrNiSi22-10 ISO 11973:1999 Grade GX25CrNiSi18-9 Grade GX40CrNiSi22-10 JIS G 5122:2003 Class SCH 12 EN 10295:2002 GX25CrNiSi20-14 ISO 11973:1999 Grade GX25 CrNiSi 20-14 *: See "List of Standards" at the beginning of the chapter.
---------------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. 1.4729 ----------------------------------490 ------------490 ----1.4740 --------------------------1.4745 --------------------------1.4776 --------------------------1.4777 ----------------------------------380 55 ----------11 1.6 40 ------20.4 2.96 50 ------36 5.3 40 --------340 --------240 35 515 75 8 --------6.2 0.91 --------17.8 2.58 --------51.4 7.45 --1.4823 --250 --550 --3 ----250 --400 --3 --------590 --------275 40 585 85 9 ----275 --540 --5 ----240 35 485 70 25 --------100 14.5 9.0 ------180 26 7.0 1.4825 --230 --450 --15 1.4826 --230 --450 --8 ----230 --450 --15 ----230 --450 --8 ----235 --490 --23 1.4832 --230 --450 --10 ----230 --450 --10
Heat Treatment A A A A A A --A --A --A AC or BA ------A AC or BA ----------AC or BA AC or BA AC or BA AC or BA ------------AC or BA -----
Other 300 max HB 300 max HB ----300 max HB 300 max HB --300 max HB --320 max HB --400 max HB --------------------400 max HB ---------------------------
Download From http://bbs.infoeach.com
EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 EN 10295:2002 ISO 11973:1999 ASTM A297/A297M-14* ASTM A608/A608M-14*
Designation GX40CrSi13 Grade GX40CrSi13 Class SCH 3 Class SCH 1 GX40CrSi17 Grade GX40CrSi17 GX40CrSi24 Grade GX40CrSi24 GX40CrSi28 Grade GX40CrSi28 GX130CrSi29 Grade GX130CrSi29 Grade HC Grade HC30
Specification EN 10295:2002 ISO 11973:1999 JIS G 5122:2003
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
431
7.5 Cast Heat Resistant Steels 7.5B Mechanical Properties of Cast Heat Resistant Steels (Continued)
Specification ASTM A297/A297M-14* ASTM A447/A447M-11 ASTM A608/A608M-14*
Designation Grade HH Type I Type II Grade HH30 Grade HH33
ASTM A297/A297M-14* ASTM A608/A608M-14*
GX40CrNiSi25-12 Grade GX40CrNiSi25-12 Class SCH 13 Class SCH 13A Grade HI Grade HI35
JIS G 5122:2003 ASME SA-351/SA-351M ASTM A297/A297M-14* ASTM A351/A351M-14 ASTM A608/A608M-14*
Class SCH 18 Grade HK30 Grade HK Grade HK30 Grade HK30
JIS G 5122:2003 ASME SA-351/SA-351M ASTM A351/A351M-14 ASTM A608/A608M-14*
Class SCH 21 Grade HK40 Grade HK40 Grade HK40
EN 10295:2002 GX40CrNiSi25-20 ISO 11973:1999 Grade GX40CrNiSi25-20 JIS G 5122:2003 Class SCH 22 ASTM A297/A297M-14* Grade HL JIS G 5122:2003 Class SCH 23 *: See "List of Standards" at the beginning of the chapter.
Section Yield Strength, min. Tensile Strength, min. Elongation Thickness, mm MPa ksi MPa ksi % min. --240 35 515 75 10 ------550 80 9 ------550 80 4 ------24.2 3.51 16.0 ------52.7 7.65 12.0 J93633 --------28 4 20.0 ------56 8.2 12.0 ------138 20 8.0 --1.4837 --220 --450 --6 ------220 --450 --6 ------235 --490 --8 ------235 --490 --8 J94003 ----240 35 485 70 10 J94013 --------56 8.2 12.0 ------138 20 8.0 ------235 --490 --8 J94203 ----240 35 450 65 10.0 J94224 ----240 35 450 65 10 J94203 ----240 35 450 65 10.0 J94203 --------25 3.6 24.0 ------52 7.5 18.0 ------97 14 9.0 ------180 26 --------235 --440 --8 J94204 ----240 35 425 62 10.0 J94204 ----240 35 425 62 10.0 J94204 --------29 4.2 22.0 ------61 8.8 15.0 ------114 16.5 6.0 ------200 29 7.0 --1.4848 --220 --450 --8 ------220 --450 --6 ------235 --440 --8 N08604 ----240 35 450 65 10 ------245 --450 --8
Heat Treatment AC or BA ------------------AC or BA AC or BA AC or BA ----AC or BA AC AC or BA AC --------AC or BA AC AC ------------AC or BA AC or BA AC or BA
Other -----------------------------------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10295:2002 ISO 11973:1999 JIS G 5122:2003
UNS Steel No. No. J93503 --J93303 --J93303 --J93513 ---
Handbook of Comparative World Steel Standards
Chapter 7
Steel Castings
432
7.5 Cast Heat Resistant Steels 7.5B Mechanical Properties of Cast Heat Resistant Steels (Continued)
Designation
Download From http://bbs.infoeach.com
Grade HN GX35NiCrSi25-21 Class SCH 19 GX40CrNiSiNb24-24 Grade GX40CrNiSiNb24-24 Grade HP GX40NiCrSiNb35-26 GX40NiCrSi35-26 ISO 11973:1999 Grade GX40NiCrSi35-26 Grade GX40NiCrSiNb35-26 JIS G 5122:2003 Class SCH 24 ASTM A297/A297M-14* Grade HT EN 10295:2002 GX40NiCrSi35-17 ISO 11973:1999 Grade GX40NiCrSi35-17 JIS G 5122:2003 Class SCH 15 ASME SA-351/SA-351M Grade HT30 ASTM A351/A351M-14 Grade HT30 JIS G 5122:2003 Class SCH 16 ASTM A297/A297M-14* Grade HU EN 10295:2002 GX40NiCrSiNb35-18 GX40NiCrSiNb38-19 GX40NiCrSi38-19 ISO 11973:1999 Grade GX40NiCrSi38-19 Grade GX40NiCrSiNb38-19 JIS G 5122:2003 Class SCH 20 EN 10295:2002 G-NiCr50Nb ISO 11973:1999 Grade GX10NiCrNb50-50 ASTM A297/A297M-14* Grade HW Grade HX EN 10295:2002 G-NiCr15 ISO 11973:1999 Grade GX50NiCr65-15 EN 10295:2002 G-CoCr28 ISO 11973:1999 Grade GX30CoCr50-28 EN 10295:2002 G-NiCr28W ISO 11973:1999 Grade GX45NiCrWSi48-28-5 EN 10295:2002 GX50NiCrCo20-20-20 ISO 11973:1999 Grade GX40NiCrCo20-20-20 *: See "List of Standards" at the beginning of the chapter.
UNS No. J94213 --------N08705 ----------N08605 ------N08030 N08030 --N08004 ----------------N08001 N06006 -----------------
Steel Section Yield Strength, min. Tensile Strength, min. Elongation No. Thickness, mm MPa ksi MPa ksi % min. --------435 63 8 1.4805 --220 --430 --8 --------390 --5 1.4855 --220 --450 --4 ----220 --400 --4 ----235 34 430 62.5 4.5 1.4852 --220 --440 --4 1.4857 --220 --440 --6 ----220 --440 --6 ----220 --440 --4 ----235 --440 --5 --------450 65 4 1.4806 --220 --420 --6 ----220 --420 --6 --------440 --4 ----195 28 450 65 15.0 ----195 28 450 65 15.0 ----195 --440 --13 --------450 65 4 1.4807 --220 --420 --4 1.4849 --220 --420 --4 1.4865 --220 --420 --6 ----220 --420 --6 ----220 --420 --4 --------390 --4 2.4680 --230 --540 --8 ----230 --540 --8 --------415 60 ----------415 60 --2.4815 --200 --400 --3 ----200 --400 --3 2.4778 --235 --490 --6 --------------2.4879 --240 --440 --3 ----220 --400 --3 1.4874 --320 --420 --6 ----320 --400 --6
Heat Treatment AC or BA --AC or BA ----AC or BA --------AC or BA AC or BA ----AC or BA AC AC AC or BA AC or BA ----------AC or BA ----AC or BA AC or BA -----------------
Other ---------------------------------------------------------------------------
Download From http://bbs.infoeach.com
Specification ASTM A297/A297M-14* EN 10295:2002 JIS G 5122:2003 EN 10295:2002 ISO 11973:1999 ASTM A297/A297M-14* EN 10295:2002
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter
8 WROUGHT STAINLESS STEELS
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
434
Wrought Stainless Steels – List of Standards
Chapter 8
Plate, Sheet, Strip ASME Standards ASME SA-240/SA-240M ASME SA-666 ASME SA-693
Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications Annealed or Cold-Worked Austenitic Stainless Steel, Sheet, Strip, Plate, and Flat Bar Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip
ASTM Standards ASTM A240/A240M-15a ASTM A666-15 ASTM A693–13 ASTM B688-96 (2014)
Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip Chromium-Nickel-Molybdenum-Iron (UNS N08366 and UNS N08367) Plate, Sheet, and Strip
DIN Standard DIN 5512-3:2004
Materials for rail vehicles – Steels – Part 3: Stainless steel flat products; Selected standard
EN Standards EN 10028-7:2007 EN 10088-2:2014 EN 10095:1999 EN 10151:2002 EN 10302:2008
Flat products made of steels for pressure purposes – Part 7: Stainless steels Stainless steels – Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes Heat resisting steels and nickel alloys Stainless steel strip for springs – Technical delivery conditions Creep resisting steels, nickel and cobalt alloys
GB Standards GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91
Cold Rolled Stainless Steel Sheets and Plates Hot Rolled Stainless Steel Sheets and Plates Heat-Resisting Steel Sheets and Plates Cold Rolled Stainless Steel and Heat Resisting Steel Strips
ISO Standards ISO 4955:2005 ISO 9328-7:2004 ISO 16143-1:2004
Heat-Resistant Steels Steel Flat Products for Pressure Purposes – Technical Delivery Conditions – Part 7: Stainless Steels Stainless Steels for General Purposes – Part 1: Flat Products
JIS Standards JIS G 4304:2012 JIS G 4305:2012 JIS G 4312:2011
Hot-rolled stainless steel plate, sheet and strip Cold-rolled stainless steel plate, sheet and strip Heat-resisting steel plate, sheet and strip
SAE Standard SAE J405 JUN98
Chemical Compositions of SAE Wrought Stainless Steels
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 8
Wrought Stainless Steels – List of Standards
435
Bars ASME Standards ASME SA-276 ASME SA-453/SA-453M ASME SA-479/SA-479M ASME SA-564/SA-564M
Stainless Steel Bars and Shapes High-Temperature Bolting Materials with Expansion Coefficients Comparable to Austenitic Stainless Steels Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
ASTM Standards ASTM A276/A276M-15 ASTM A314-13a ASTM A453/A453M-12 ASTM A479/A479M-14 ASTM A564/A564M-13 ASTM A565/A565M-10 ASTM A582/A582M-12e1 ASTM A955/A955M-15 ASTM A1028-03 (2015) ASTM B691-02 (2013)
Stainless Steel Bars and Shapes Stainless Steel Billets and Bars for Forging High-Temperature Bolting, with Expansion Coefficients Comparable to Austenitic Stainless Steels Stainless Steel Bars and Shapes for Use in Boilers and Other Pressure Vessels Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes Martensitic Stainless Steel Bars for High-Temperature Service Free-Machining Stainless Steel Bars Deformed and Plain Stainless-Steel Bars for Concrete Reinforcement Stainless Steel Bars for Compressor and Turbine Airfoils Iron-Nickel-Chromium-Molybdenum Alloys (UNS N08366 and UNS N08367) Rod, Bar, and Wire
EN Standards EN 10088-3:2014 EN 10090:1998 EN 10095:1999 EN 10263-5:2001 EN 10269:2013 EN 10272:2007 EN 10294-2:2012 EN 10302:2008
Stainless steels – Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes Valve steels and alloys for internal combustion engines Heat resisting steels and nickel alloys Steel rod, bars and wire for cold heading and cold extrusion – Part 5: Technical delivery conditions for stainless steels Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties Stainless steel bars for pressure purposes Hollow bars for machining – Technical delivery conditions – Part 2: Stainless steels with specified machinability properties Creep resisting steels, nickel and cobalt alloys
GB Standards GB 1220-92 GB 1221-92 GB 4226-84
Stainless Steel Bars Heat Resisting Steel Bars Cold Finished Stainless Steel Bars
ISO Standards ISO 683-15:1992 ISO 4954:1993 ISO 4955:1994 ISO 16143-2:2004
Heat-Treatable Steels, Alloy Steels and Free-Cutting Steels – Part 15: Valve Steels for Internal Combustion Engines Steels for Cold Heading and Cold Extruding Heat-Resisting Steels and Alloys Stainless Steels for General Purposes – Part 2: Semi-Finished Products, Bars, Rods and Sections
JIS Standards JIS G 4303:2012 JIS G 4311:2011 JIS G 4318:1998 A1:2007
Stainless steel bars Heat-resisting steel bars and wire rods Cold finished stainless steel bars
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
436
Wrought Stainless Steels – Heat Treatment Terms
Chapter 8
Heat Treatment Terms Applicable to this Chapter Standard ASME SA-240/SA-240M ASME SA-276 ASME SA-453/SA-453M ASME SA-479/SA-479M ASME SA-564/SA-564M ASME SA-666 ASME SA-693 ASTM A240/A240M-15a ASTM A276/A276M-15 ASTM A314-13a ASTM A453/A453M-12 ASTM A479/A479M-14 ASTM A564/A564M-13 ASTM A565/A565M-10 ASTM A582/A582M-12e1 ASTM A666-15 ASTM A693-13 ASTM A955/A955M-15 ASTM A1028-03 (2015) ASTM B688-96 (2014) ASTM B691-02 (2013) DIN 5512-3:2004 EN 10028-7:2007 EN 10088-2:2014 EN 10088-3:2014 EN 10090:1998 EN 10095:1999 EN 10151:2002 EN 10263-5:2001 EN 10269:2013 EN 10272:2007 EN 10294-2:2012 EN 10302:2008 GB 1220-92 GB 1221-92 GB 3280-92 GB 4226-84 GB 4237-92 GB 4238-92 GB 4239-91
Heat Treatment Terms See standard; SA: solution annealed; Q+SA: quenched in water and solution annealed A: annealed; HF: hot finished; CF: cold finished; CW: cold worked; H+T: hardened and tempered; H+CW+CF: strain hardened, lightly cold worked and cold finished S+H: solution treated, then hardened A: annealed; N+T: normalized and tempered; T: tempered; Q+T: quenched and tempered; H: strain-hardened SA: solution annealed; PH: precipitation hardened A: annealed PH: precipitation hardened; ST: solution treated; CR: cold rolled; CR+PH: cold rolled and precipitation hardened SA: solution annealed A+HF: annealed and hot finished; A+CF: annealed and cold finished; H+T: hardened and tempered; HF: hot finished; CF: cold finished; CW+CF: cold worked and cold finished; H+CF: strain hardened and cold finished --S+H: solution treated, then hardened A: annealed; N+T: normalized and tempered; Q+T: liquid quenched and tempered; SA: solution annealed; H: strain hardened; T: tempered SA: solution annealed; PH: precipitation hardened A: annealed; HT: heat treated A: annealed; T: intermediate temper; H: hard temper A: annealed PH: precipitation hardened; ST: solution treated; CR: cold rolled; CR+PH: cold rolled and precipitation hardened A: annealed; HR: hot rolled; SH: strain hardened A+Q+G: austenitized, then quenched followed by being aged --CFA: cold-finished-annealed; HFA: hot-finished-annealed HR: hot rolled; CR: cold rolled A: annealed; SA: solution annealed; Q+T: quenched and tempered; See standard; A: annealed; Q+T: quenched and tempered; SA: solution annealed; PH: precipitation hardened (with specified temperature) A: annealed; A+PH: annealed and precipitation hardened; Q+T: quenched and tempered; SA: solution annealed; CW: cold work hardened; PH: precipitation hardened Q: quenched; CTC: control cooled A: annealed; SA: solution annealed CW: cold worked CD+A: cold drawn and soft annealed; A: soft annealed; CD+SA: cold drawn and solution annealed; SA: solution annealed Q+T: quenched and tempered; A: soft annealed; CW: cold work hardened; SA: solution annealed SA: solution annealed SA: solution annealed Q+T: quenched and tempered; SA: solution annealed; PH: precipitation hardened; A: annealed A: annealed; ST: solution treated; Q+T: quenched and tempered A: annealed; ST: solution treated; Q+T: quenched and tempered A: annealed; ST: solution treated; Q+T: quenched and tempered; WH: work hardened --A: annealed; ST: solution treated See standard; A: annealed; ST: solution treated A: annealed; ST: solution treated; Q+T: quenched and tempered; WH: work hardened
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Chapter 8
Wrought Stainless Steels – Heat Treatment Terms
437
Heat Treatment Terms Applicable to this Chapter (continued) Standard ISO 683-15:1992 ISO 4954:1993
Heat Treatment Terms CTC: controlled cooled; Q: quenched See standard; CW: cold worked; A: annealed; Q: quenched; CD: cold drawn
ISO 4955:2005
A: annealed; SA: solution annealed
ISO 9328-7:2004 ISO 16143-1:2004
A: annealed; Q+T: quenched and tempered; SA: solution annealed A: annealed; Q+T: quenched and tempered; SA: solution annealed; PH: precipitation-hardened ST: solution treated; A: annealed; Q+T: quenched and tempered; PH: precipitation hardened at specified temperature ST: solution treated; A: annealed; Q+T: quenched and tempered; PH: precipitation hardening treatment at specified temperature ST: solution treated; A: annealed; Q+T: quenched and tempered T: temper rolled for hardening; PH: precipitation hardening treatment at specified temperature See standard; A: annealed; Q+T: quenched and tempered; ST: solution treated See standard; A: annealed; ST: solution treated -----
JIS G 4303:2012 JIS G 4304:2012 JIS G 4305:2012 JIS G 4311:2011 JIS G 4312:2011 JIS G 4318:1998 A1:2007 SAE J405 JUN98
Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
Chapter 8
Wrought Stainless Steels
438
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.1A Chemical Composition of Martensitic Stainless Steels
Designation Type 403 Grade 1Cr12 Grade 1Cr12 Grade 1Cr12 Grade 1Cr12 Symbol SUS403 Symbol SUS403 X12Cr13 Grade 1Cr13 Grade 1Cr13 Grade 1Cr13 Grade 1Cr13 X12Cr13 Symbol SUS410 Symbol SUS410 Type 410 Grade 00Cr12 Grade 00Cr12 Grade 00Cr12 Grade 00Cr12 Symbol SUS410L Symbol SUS410L Type 410S Type 410S X6Cr13 Grade 0Cr13 Grade 0Cr13 Grade 0Cr13 Symbol SUS410S Symbol SUS410S Type 410S X6Cr13
UNS Steel No No C S40300 --0.15 ----0.15 ----0.15 ----0.15 ----0.15 ----0.15 ----0.15 --1.4006 0.08-0.15 ----0.15 ----0.15 ----0.15 ----0.15 ----0.08-0.15 ----0.15 ----0.15 S41000 --0.15 ----0.030 ----0.030 ----0.03 ----0.030 ----0.030 ----0.030 S41008 --0.08 S41008 --0.08 --1.4000 0.08 ----0.08 ----0.08 ----0.08 ----0.08 ----0.08 S41008 --0.08 ----0.08
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.50 1.00 1.00 1.00 1.00 1.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Si 0.50 0.50 0.50 0.50 0.50 0.50 0.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
P 0.040 0.035 0.035 0.035 0.035 0.040 0.040 0.040 0.035 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 11.5-13.0 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.015 11.5-13.5 0.75 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.5-13.5 0.75 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.75 --0.030 11.00-13.50 0.60 --0.030 11.00-13.50 0.60 --0.030 11.00-13.00 0.60 --0.030 11.00-13.50 0.60 --0.030 11.00-13.50 0.60 --0.030 11.00-13.50 0.60 --0.030 11.5-13.5 0.60 --0.030 11.5-13.5 0.60 --0.015 12.0-14.0 ----0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 12.0-14.0 1.00 ---
Others ------Cu 0.30 ------------Cu 0.30 -------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASTM A240/A240M-15a GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ISO 4955:2005
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
439
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.1A Chemical Composition of Martensitic Stainless Steels (Continued)
Designation Type 420 X20Cr13 Grade 2Cr13 Grade 2Cr13 Grade 2Cr13 X20Cr13 Symbol SUS420J1 Symbol SUS420J1 X30Cr13 Grade 3Cr13 Grade 3Cr13 Grade 3Cr13 X30Cr13 Symbol SUS420J2 Symbol SUS420J2 ----X3CrNiMo13-4 Grade X3CrNiMo13-4 --X39Cr13 Grade 4Cr13 Grade 4Cr13 X39Cr13 X4CrNiMo16-5-1 X4CrNiMo16-5-1 Grade X4CrNiMo16-5-1 Grade 7Cr17 Grade 7Cr17 Grade 7Cr17 Symbol SUS440A Symbol SUS440A
UNS No S42000 ----------------------------S41500 S41500 ----S41500 -------------------------
Steel No --1.4021 ------------1.4028 ----------------1.4313 ----1.4031 ------1.4418 1.4418 -------------
C 0.15 min. 0.16-0.25 0.16-0.25 0.16-0.25 0.16-0.25 0.16-0.25 0.16-0.25 0.16-0.25 0.26-0.35 0.26-0.35 0.26-0.35 0.26-0.40 0.26-0.35 0.26-0.40 0.26-0.40 0.05 0.05 0.05 0.05 0.05 0.36-0.42 0.36-0.45 0.36-0.45 0.36-0.42 0.06 0.06 0.06 0.60-0.75 0.60-0.75 0.60-0.75 0.60-0.75 0.60-0.75
Mn 1.00 1.50 1.00 1.00 1.00 1.50 1.00 1.00 1.50 1.00 1.00 1.00 1.50 1.00 1.00 0.50-1.00 0.50-1.00 1.50 0.50-1.00 0.5-1.0 1.00 0.80 0.80 1.00 1.50 1.50 1.50 1.00 1.00 1.00 1.00 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.60 0.60 0.70 0.70 0.60 1.00 0.80 0.80 1.00 0.70 0.70 0.70 1.00 1.00 1.00 1.00 1.00
P 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.030 0.030 0.040 0.040 0.030 0.040 0.035 0.035 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 12.0-14.0 0.75 0.50 0.015 12.0-14.0 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.0-14.0 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.015 12.0-14.0 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.0-14.0 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 11.5-14.0 3.5-5.5 0.50-1.00 0.030 11.5-14.0 3.5-5.5 0.50-1.00 0.015 12.0-14.0 3.5-4.5 0.30-0.70 0.015 12.0-14.0 3.5-4.5 0.30-1.00 0.030 11.5-14.0 3.5-5.5 0.5-1.0 0.015 12.5-14.5 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.5-14.5 ----0.015 15.0-17.0 4.0-6.0 0.80-1.50 0.015 15.0-17.0 4.0-6.0 0.80-1.50 0.015 15.0-17.0 4.0-6.0 0.80-1.50 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 0.60 0.75
Others ----------------------------------N 0.020 min. ------------N 0.020 min. N 0.020 min. N 0.020 min. -----------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004 SAE J405 JUN98 EN 10088-2:2014 GB 3280-92 GB 4237-92 ISO 16143-1:2004 EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
440
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.1B Mechanical Properties of Martensitic Stainless Steels
Specification ASTM A240/A240M-15a
Designation Type 403
UNS Steel No No S40300 ---
Section Thickness/Diameter mm in. t ≤ 1.27 t ≤ 0.050
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 485 70 20
Heat Treatment ---
t > 1.27
t > 0.050
205
30
485
70
25
---
---
---
---
---
205
---
440
---
20
A
GB 4237-92
Grade 1Cr12
---
---
---
---
205
---
440
---
20
A
GB 4238-92
Grade 1Cr12
---
---
---
---
205
---
440
---
20
A
GB 4239-91 JIS G 4304:2012
Grade 1Cr12 Symbol SUS403
-----
-----
-----
-----
205 205
-----
440 440
-----
20 20
A A
JIS G 4305:2012
Symbol SUS403
---
---
---
---
205
---
440
---
20
A
EN 10088-2:2014
X12Cr13
---
1.4006
t≤8
---
---
---
600 max.
---
20 L, 20 T
A
t ≤ 13.5
---
---
---
600 max.
---
20 L, 20 T
A
-------
450 400 205
-------
650-850 550-750 440
-------
12 L, 12 T 15 L, 15 T 20
Q+T Q+T A
GB 3280-92
Grade 1Cr13
---
---
t ≤ 75 t ≤ 75 ---
GB 4237-92
Grade 1Cr13
---
---
---
---
225
---
440
---
20
A
GB 4238-92
Grade 1Cr13
---
---
---
---
205
---
440
---
20
A
GB 4239-91 ISO 16143-1:2004
Grade 1Cr13 X12Cr13
-----
-----
JIS G 4304:2012
Symbol SUS410
---
---
--t≤8 t ≤ 13.5 t ≤ 75 t ≤ 75 ---
-------------
205 ----400 450 205
-------------
440 440-600 440-600 550-750 650-850 440
-------------
20 20 20 15 12 20
A A A Q+T Q+T A
JIS G 4305:2012
Symbol SUS410
---
---
---
---
205
---
440
---
20
A
Download From http://bbs.infoeach.com
Grade 1Cr12
Download From http://bbs.infoeach.com
GB 3280-92
Other 217 max. HBW; 96 max. HRBW 217 max. HBW; 96 max. HRBW 200 max. HB; 93 max. HRB 200 max. HB; 93 max. HRB 200 max. HB; 93 max. HRB 93 max. HRB 201 max. HBW; 93 max. HRBW; 210 max. HV 201 max. HBW; 93 max. HRBW; 210 max. HV 200 max. HBW; 90 max. HRB 200 max. HBW; 90 max. HRB BA J @ RT BA J @ RT 183 max. HB; 88 max. HRB 200 max. HB; 93 max. HRB 200 max. HB; 93 max. HRB 93 max. HRB --------201 max. HBW; 93 max. HRBW; 210 max. HV 201 max. HBW; 93 max. HRBW; 210 max. HV
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
441
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.1B Mechanical Properties of Martensitic Stainless Steels (Continued) Steel No ---
Grade 00Cr12
---
---
---
---
196
---
370
---
22
A
GB 4238-92
Grade 00Cr12
---
---
---
---
195
---
365
---
22
A
GB 4239-91 JIS G 4304:2012
Grade 00Cr12 Symbol SUS410L
-----
-----
-----
-----
195 195
-----
365 360
-----
22 22
A A
JIS G 4305:2012
Symbol SUS410L
---
---
---
---
195
---
360
---
22
A
ASME SA-240/SA-240M
Type 410S
S41008
---
t ≤ 1.27
t ≤ 0.050
205
30
415
60
20
see standard
t > 1.27
t > 0.050
205
30
415
60
22
see standard
t ≤ 1.27
t ≤ 0.050
205
30
415
60
20
---
t > 1.27
t > 0.050
205
30
415
60
22
---
---------
240 220 220 205
---------
400-600 400-600 400-600 440
---------
19 L, 19 T 19 L, 19 T 19 L, 19 T 20
A A A A
Designation Grade 00Cr12
GB 4237-92
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Type 410S
S41008
---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 190 --365 --22
Heat Treatment A
EN 10088-2:2014
X6Cr13
---
1.4000
GB 3280-92
Grade 0Cr13
---
---
t≤8 t ≤ 13.5 t ≤ 25 ---
GB 4237-92
Grade 0Cr13
---
---
---
---
205
---
410
---
20
A
GB 4239-91 JIS G 4304:2012
Grade 0Cr13 Symbol SUS410S
-----
-----
-----
-----
205 205
-----
410 410
-----
20 20
A A
JIS G 4305:2012
Symbol SUS410S
---
---
---
---
205
---
410
---
20
A
ISO 4955:2005
X6Cr13
---
---
0.5 ≤ t < 3 3 ≤ t ≤ 12 5 ≤ t ≤ 15 5 ≤ t ≤ 25 1.5 ≤ t ≤ 25
-----------
230 230 230 230 230
-----------
400-630 400-630 400-630 400-630 400-630
-----------
18 L, 18 T 20 L, 18 T 20 20 20
A A A A A
Other 183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 88 max. HRB 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HB; 89 max. HRB 183 max. HB; 89 max. HRB 183 max. HBW; 89 max. HRBW 183 max. HBW; 89 max. HRBW ------200 max. HB; 93 max. HRB 183 max. HB; 88 max. HRB 88 max. HRB 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV 197 max. HB 197 max. HB 197 max. HB 197 max. HB 197 max. HB
Download From http://bbs.infoeach.com
UNS No ---
Specification GB 3280-92
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
442
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.1B Mechanical Properties of Martensitic Stainless Steels (Continued)
Specification ASTM A240/A240M-15a
Designation Type 420
EN 10088-2:2014
X20Cr13
UNS Steel No No S42000 -----
1.4021
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min ----690 max. 100 max. 15
Heat Treatment ---
---
---
---
---
---
---
Q+T
t≤8
---
---
---
700 max.
---
15 L, 15 T
A
t ≤ 13.5
---
---
---
700 max.
---
15 L, 15 T
A
-------
550 450 225
-------
750-950 650-850 520
-------
10 L, 10 T 12 L, 12 T 18
Q+T Q+T A
GB 3280-92
Grade 2Cr13
---
---
t ≤ 75 t ≤ 75 ---
GB 4237-92
Grade 2Cr13
---
---
---
---
225
---
520
---
18
A
GB 4239-91 ISO 16143-1:2004
Grade 2Cr13 X20Cr13
-----
-----
JIS G 4304:2012
Symbol SUS420J1
---
---
--t≤3 t≤8 t ≤ 13.5 t ≤ 75 t ≤ 75 ---
---------------
225 ------450 550 225
---------------
520 --520-700 520-700 650-850 750-950 520
---------------
18 --15 15 12 10 18
A Q+T A A Q+T Q+T A
JIS G 4305:2012
Symbol SUS420J1
---
---
---
---
225
---
520
---
18
A
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
t≤3
Other 217 max. HBW; 96 max. HRBW 44-50 HRC; 440-530 HV 225 max. HBW; 95 max. HRB 225 max. HBW; 95 max. HRB BA J @ RT BA J @ RT 223 max. HB; 97 max. HRB 223 max. HB; 97 max. HRB 97 max. HRB ----------223 max. HBW; 97 max. HRBW; 234 max. HV 223 max. HBW; 97 max. HRBW; 234 max. HV
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
443
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.1B Mechanical Properties of Martensitic Stainless Steels (Continued)
Specification EN 10088-2:2014
Designation X30Cr13
UNS No ---
Steel No 1.4028
Section Thickness/Diameter mm in. t≤3 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min -----------
Heat Treatment Q+T
t≤8
---
---
---
740 max.
---
15 L, 15 T
A
t ≤ 13.5
---
---
---
740 max.
---
15 L, 15 T
A
---
---
t ≤ 75 ---
-----
600 225
-----
800-1000 540
-----
10 L, 10 T 18
Q+T A
GB 4237-92
Grade 3Cr13
---
---
-----
-----
--225
-----
--540
-----
--18
Q+T A
GB 4239-91
Grade 3Cr13
---
---
ISO 16143-1:2004
X30Cr13
---
---
JIS G 4304:2012
Symbol SUS420J2
---
---
----t≤3 t≤8 t ≤ 13.5 t ≤ 75 -----
-----------------
225 --------600 --225
-----------------
540 ----540-740 540-740 800-1000 --540
-----------------
18 ----15 15 10 --18
A Q+T Q+T A A Q+T Q+T A
JIS G 4305:2012
Symbol SUS420J2
---
---
---
---
225
---
540
---
18
A
ASME SA-240/SA-240M
---
S41500
---
-----
-----
--620
--90
--795
--115
--15
Q+T see standard
ASTM A240/A240M-15a
---
S41500
---
---
---
620
90
795
115
15
---
EN 10028-7:2007
X3CrNiMo13-4
---
1.4313
t ≤ 75
---
650
---
780-980
---
14 L, 14 T
Q+T
ISO 9328-7:2004
Grade X3CrNiMo13-4
---
---
t ≤ 75
---
650
---
780-980
---
14 L, 14 T
Q+T
Download From http://bbs.infoeach.com
Grade 3Cr13
Download From http://bbs.infoeach.com
GB 3280-92
Other 45-51 HRC; 450-550 HV 235 max. HBW; 97 max. HRB 235 max. HBW; 97 max. HRB --235 max. HB; 99 max. HRB --235 max. HB; 99 max. HRB 99 max. HRB ----------40 min. HRC 235 max. HBW; 99 max. HRBW; 247 max. HV 235 max. HBW; 99 max. HRBW; 247 max. HV 40 min. HRC 302 max. HB; 32 max. HRC 302 max. HBW; 32 max. HRC see standard for impact data see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
444
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.1B Mechanical Properties of Martensitic Stainless Steels (Continued)
Specification EN 10088-2:2014
Designation X39Cr13
UNS No ---
Steel No 1.4031
Section Thickness/Diameter mm in. t≤3 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min -----------
Heat Treatment Q+T
---
---
---
760 max.
---
12 L, 12 T
A
t ≤ 13.5
---
---
---
760 max.
---
12 L, 12 T
A
---------------
225 ----------680
---------------
590 --590 --760 max. 760 max. 840-980
---------------
15 --15 max. --12 12 14 L, 14 T
A Q+T A Q+T A A Q+T
Grade 4Cr13
---
---
GB 4237-92 ISO 16143-1:2004
Grade 4Cr13 X39Cr13
-----
-----
EN 10028-7:2007
X4CrNiMo16-5-1
---
1.4418
------t≤3 t≤8 t ≤ 13.5 t ≤ 75
EN 10088-2:2014 ISO 9328-7:2004
X4CrNiMo16-5-1 Grade X4CrNiMo16-5-1
-----
1.4418 ---
t ≤ 75 t ≤ 75
-----
660 680
-----
840-1100 840-980
-----
14 L, 14 T 14 L, 14 T
Q+T Q+T
GB 3280-92
Grade 7Cr17
---
---
GB 4237-92 GB 4239-91
Grade 7Cr17 Grade 7Cr17
-----
-----
JIS G 4304:2012
Symbol SUS440A
---
---
---------------
---------------
245 --245 245 ----245
---------------
590 --590 590 ----590
---------------
15 --15 15 ----15
A Q+T A A Q+T Q+T A
JIS G 4305:2012
Symbol SUS440A
---
---
---
---
245
---
590
---
15
A
---
---
---
---
---
---
---
Q+T
Download From http://bbs.infoeach.com
GB 3280-92
Download From http://bbs.infoeach.com
t≤8
Other 47-53 HRC; 480-580 HV 240 max. HBW; 98 max. HRB 240 max. HBW; 98 max. HRB ------------see standard for impact data 55 J @ RT see standard for impact data 255 max. HB --255 max. HB ----40 min. HRC 255 max. HBW; 25 max. HRC; 269 max. HV 255 max. HBW; 25 max. HRC; 269 max. HV 40 min. HRC
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
445
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.2A Chemical Composition of Ferritic Stainless Steels
Designation
ASTM A240/A240M-15a
---
EN 10088-2:2014 ISO 16143-1:2004 ISO 4955:2005 SAE J405 JUN98 EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4312:2011 ASME SA-240/SA-240M ASTM A240/A240M-15a DIN 5512-3:2004 EN 10088-2:2014
X2CrTi12 X2CrTi12 X2CrTi12 --X6CrNiTi12 X6CrNiTi12 Grade X6CrNiTi12 Symbol SUH409 ----X5CrNiMoTi15-2 X5CrNiMoTi15-2
Download From http://bbs.infoeach.com
EN 10028-7:2007 EN 10088-2:2014 JIS G 4312:2011 ISO 16143-1:2004 ISO 9328-7:2004 SAE J405 JUN98 ASME SA-240/SA-240M
Type 405 Type 405 X6CrAl13 Grade 0Cr13Al Grade 0Cr13Al Grade 0Cr13Al Grade 0Cr13Al Symbol SUS405 Symbol SUS405 Type 405 --------X2CrNi12 X2CrNi12 Symbol SUH409L X2CrNi12 Grade X2CrNi12 -----
ASTM A240/A240M-15a
UNS No S40500 S40500 --------------S40500 S40977 S41050 S40977 S41050 ----------S41050 S40945 S40975 S40945 S40975 ------S40945 --------S42035 S42035 -----
Steel No ----1.4002 ----------------------1.4003 1.4003 ----------------1.4512 ------1.4516 1.4516 --------1.4589 1.4589
C 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.030 0.04 0.030 0.04 0.030 0.030 0.030 0.030 0.030 0.040 0.030 0.030 0.030 0.030 0.030 0.030 0.03 0.030 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.50 1.00 1.50 1.00 1.50 1.50 1.00 1.50 1.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.50 1.50 1.00 1.00 1.00 1.00 1.0 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.70 0.70 1.00 1.00 1.00 1.00 1.0 1.00
P 0.040 0.040 0.040 0.035 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.045 0.040 0.045 0.040 0.040 0.040 0.040 0.040 0.045 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.045 0.045 0.045 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 11.5-14.5 0.60 --0.030 11.5-14.5 0.60 --0.015 12.0-14.0 ----0.030 11.50-14.50 0.60 --0.030 11.50-14.50 0.60 --0.030 11.50-14.50 0.60 --0.030 11.50-14.50 0.60 --0.030 11.50-14.50 0.60 --0.030 11.50-14.50 0.60 --0.030 11.50-14.50 0.60 --0.015 10.5-12.5 0.30-1.00 --0.030 10.5-12.5 0.60-1.10 --0.015 10.5-12.5 0.30-1.00 --0.030 10.5-12.5 0.60-1.10 --0.015 10.5-12.5 0.30-1.00 --0.015 10.5-12.5 0.30-1.00 --0.030 10.50-11.75 0.60 --0.015 10.5-12.5 0.30-1.10 --0.015 10.5-12.5 0.30-1.10 --0.030 10.50-12.50 0.60-1.10 --0.030 10.5-11.7 0.50 --0.030 10.5-11.7 0.50-1.00 --0.030 10.5-11.7 0.50 --0.030 10.5-11.7 0.50-1.00 --0.015 10.5-12.5 ----0.030 10.5-12.5 0.50 --0.015 10.5-12.5 ----0.030 10.50-11.75 0.50 --0.015 10.5-12.5 0.50-1.50 --0.015 10.5-12.5 0.50-1.50 --0.015 10.5-12.5 0.50-1.50 --0.030 10.50-11.75 0.60 --0.030 13.5-15.5 1.0-2.5 0.2-1.2 0.030 13.5-15.5 1.0-2.5 0.2-1.2 0.03 13.5-15.5 1.0-2.5 0.2-1.2 0.015 13.5-15.5 1.00-2.50 0.20-1.20
Others Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 Al 0.10-0.30 N 0.030 N 0.10 N 0.030 N 0.10 N 0.030 N 0.030 Ti 6xC to 0.75 N 0.030 N 0.030 N 0.10 Ti 0.05-0.20; Cb 0.18-0.40; N 0.030 N 0.030; Ti 6x(C+N) to 0.75 Ti 0.05-0.20; Cb 0.18-0.40; N 0.030 N 0.030; Ti 6x(C+N) to 0.75 Ti 6x(C+N) to 0.65 Ti 6x(C+N) to 0.65 Ti 6x(C+N) to 0.65 Ti 0.05-0.20; Cb 0.18-0.40; N 0.030 Ti 0.05-0.35 Ti 0.05-0.35 Ti 0.05-0.35 Ti 6xC to 0.75 Ti 0.30-0.50 Ti 0.30-0.50 Ti 0.3-0.5 Ti 0.30-0.50
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
446
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.2A Chemical Composition of Ferritic Stainless Steels (Continued)
EN 10088-2:2014
GB 3280-92 GB 4239-91 ISO 16143-1:2004 ISO 4955:2005 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012
Designation Type 429 Type 429 Grade 1Cr15 Grade 1Cr15 Grade 1Cr15 Symbol SUS429 Symbol SUS429 Type 429 Type 430 Type 430 X6Cr17 Grade 1Cr17 Grade 1Cr17 Grade 1Cr17 Grade 1Cr17 X6Cr17 Symbol SUS430 Symbol SUS430 Type 430 X3CrTi17 X2CrTi17 X3CrTi17 X3CrNb17 X2CrTi17 Grade 00Cr17 Grade 00Cr17 X3CrTi17 X3CrNb17 X3CrTi17 Grade X2CrTi17 Grade X3CrTi17 Symbol SUS430LX Symbol SUS430LX
UNS No S42900 S42900 ----------S42900 S43000 S43000 ----------------S43000 -----------------------------
Steel No --------------------1.4016 ----------------1.4510 1.4520 1.4510 1.4511 1.4520 -------------------
C 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.08 0.12 0.12 0.12 0.12 0.08 0.12 0.12 0.12 0.05 0.025 0.05 0.05 0.025 0.030 0.030 0.05 0.05 0.05 0.025 0.05 0.030 0.030
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.50 1.00 1.00 0.50 1.00 1.00 1.00 1.00 1.00 0.50 1.00 1.00 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 0.75 0.75 1.00 1.00 0.50 1.00 1.00 0.50 0.75 0.75 1.00 1.00 1.00 0.50 1.00 0.75 0.75
P 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.035 0.040 0.040 0.040 0.040 0.040 0.040 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 14.0-16.0 ----0.030 14.0-16.0 ----0.030 14.00-16.00 0.60 --0.030 14.00-16.00 0.60 --0.030 14.00-16.00 0.60 --0.030 14.00-16.00 0.60 --0.030 14.00-16.00 0.60 --0.030 14.00-16.00 ----0.030 16.0-18.0 0.75 --0.030 16.0-18.0 0.75 --0.015 16.0-18.0 ----0.030 16.00-18.00 0.60 --0.030 16.00-18.00 0.60 --0.030 16.00-18.00 0.60 --0.030 16.00-18.00 0.60 --0.030 16.0-18.0 ----0.030 16.00-18.00 0.60 --0.030 16.00-18.00 0.60 --0.030 16.00-18.00 0.75 --0.015 16.0-18.0 ----0.015 16.0-18.0 ----0.015 16.0-18.0 ----0.015 16.0-18.0 ----0.015 16.0-18.0 ----0.030 16.00-19.00 0.60 --0.030 16.00-19.00 0.60 --0.030 16.0-19.0 ----0.015 16.0-18.0 ----0.015 16.0-18.0 ----0.015 16.0-18.0 ----0.015 16.0-19.0 ----0.030 16.00-19.00 0.60 --0.030 16.00-19.00 0.60 ---
Others --------------------------------------Ti [4x(C+N)+0.15] to 0.80 Ti 0.30-0.60; N 0.015 Ti [4x(C+N)+0.15] to 0.80 Nb 12xC to 1.00 Ti [4x(C+N)+0.15] to 0.80; N 0.015 Ti 0.10-1.00; Nb 0.10-1.00 Ti 0.10-1.00; Nb 0.10-1.00 Ti [4x(C+N)+0.20] to 0.75 Nb 12xC to 1.00 Ti [4x(C+N)+0.15] to 0.80 Ti 0.30-0.60; N 0.015 Ti [4x(C+N)+0.15] to 0.75 Ti 0.10-1.00; Nb 0.10-1.00 Ti 0.10-1.00; Nb 0.10-1.00
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 EN 10028-7:2007
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
447
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.2A Chemical Composition of Ferritic Stainless Steels (Continued)
C 0.12 0.12 0.08 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.12 0.08 0.12 0.030
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
P 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040
---
S43932
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
Type 439
S43035
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
---
S43932
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
SAE J405 JUN98
---
S43932
---
0.030
1.00
1.00
0.040
0.030
17.0-19.0
0.50
---
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ISO 4955:2005
----X2CrTiNb18 X2CrTiNb18 Grade X2CrTiNb18 X2CrTiNb18
S43940 --S43940 ----1.4509 --1.4509 ---------
0.030 0.030 0.030 0.030 0.030 0.03
1.00 1.00 1.00 1.00 1.00 1.00
1.00 1.00 1.00 1.00 1.00 1.00
0.040 0.040 0.040 0.040 0.040 0.040
0.015 0.015 0.015 0.015 0.015 0.015
17.5-18.5 17.5-18.5 17.5-18.5 17.5-18.5 17.5-18.5 17.5-18.5
-------------
-------------
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Designation
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 16.0-18.0 --0.75-1.25 0.030 16.0-18.0 --0.75-1.25 0.015 16.0-18.0 --0.90-1.40 0.030 16.00-18.00 0.60 0.75-1.25 0.030 16.00-18.00 0.60 0.75-1.25 0.030 16.00-18.00 0.60 0.75-1.25 0.030 16.00-18.00 0.60 0.75-1.25 0.030 16.00-18.00 0.60 0.75-1.25 0.030 16.00-18.00 --0.75-1.25 0.030 16.0-18.0 --0.75-1.25 0.030 16.0-18.0 --0.75-1.25 0.015 16.0-18.0 --0.80-1.40 0.030 16.00-18.00 --0.75-1.25 0.030 17.0-19.0 0.50 ---
Others ------------------Cb 5xC to 0.80 Cb 5xC to 0.80 Nb [7x(C+N)+0.10] to 1.00; N 0.040 Cb 5xC to 0.80 Ti [0.20+4(C+N)] to 1.10; Al 0.15; N 0.030 (Ti+Cb) [0.20+4(C+N)] to 0.75; Al 0.15; N 0.030 Ti [0.20+4(C+N)] to 1.10; Al 0.15; N 0.030 (Ti+Cb) [0.20+4(C+N)] to 0.75; Al 0.15; N 0.030 (Ti+Cb) [0.20 +4x(C+N)] to 0.75; Al 0.15; N 0.030 Cb [0.30+(3xC)] min.; Ti 0.10-0.60 Cb [0.30+(3xC)] min.; Ti 0.10-0.60 Nb [3xC+0.30] to 1.00; Ti 0.10-0.60 Nb [3xC+0.30] to 1.00; Ti 0.10-0.60 Nb [3xC+0.30] to 1.00; Ti 0.10-0.60 Nb [3xC+0.30] to 1.00; Ti 0.10-0.60
Download From http://bbs.infoeach.com
Type 434 Type 434 X6CrMo17-1 Grade 1Cr17Mo Grade 1Cr17Mo Grade 1Cr17Mo Symbol SUS434 Symbol SUS434 --Type 436 Type 436 X6CrMoNb17-1 --Type 439
UNS Steel No No S43400 --S43400 ----1.4113 --------------------S43400 --S43600 --S43600 ----1.4526 S43600 --S43035 ---
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 SAE J405 JUN98 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
448
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.2A Chemical Composition of Ferritic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92
Designation Type 444 Type 444 X2CrMoTi18-2 X2CrMoTi18-2 Grade 00Cr18Mo2
UNS Steel No No S44400 --S44400 ----1.4521 --1.4521 -----
C 0.025 0.025 0.025 0.025 0.025
Mn 1.00 1.00 1.00 1.00 1.00
Si 1.00 1.00 1.00 1.00 1.00
Grade 00Cr18Mo2
---
---
0.025
1.00
1.00
GB 4239-91
Grade 00Cr18Mo2
---
---
0.025
1.00
1.00
ISO 9328-7:2004 JIS G 4304:2012
Grade X2CrMoTi18-2 Symbol SUS444
-----
-----
0.025 0.025
1.00 1.00
1.00 1.00
JIS G 4305:2012
Symbol SUS444
---
---
0.025
1.00
1.00
SAE J405 JUN98
Type 444
S44400
---
0.025
1.00
1.00
GB 4238-92 JIS G 4312:2011 ASTM A240/A240M-15a GB 4238-92 ISO 4955:2005 JIS G 4312:2011 ASME SA-240/SA-240M
Grade 1Cr19Al3 Symbol SUH21 Type 446 Grade 2Cr25N X15CrN26 Symbol SUH446 Type XM-27
----S44600 ------S44627
---------------
0.10 0.10 0.20 0.20 0.20 0.20 0.010
1.00 1.00 1.50 1.50 1.00 1.50 0.40
1.50 1.50 1.00 1.00 1.00 1.00 0.40
ASTM A240/A240M-15a
Type XM-27
S44627
---
0.010
0.40
0.40
GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98
Grade 00Cr27Mo Grade 00Cr27Mo Grade 00Cr27Mo Symbol SUSXM27 Symbol SUSXM27 Type SM-27
----------S44627
-------------
0.010 0.010 0.010 0.010 0.010 0.010
0.40 0.40 0.40 0.40 0.40 0.40
0.40 0.40 0.40 0.40 0.40 0.40
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 4237-92
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo Others 0.030 17.5-19.5 1.00 1.75-2.50 (Ti+Cb) [0.20+4x(C+N)] to 0.80; N 0.035 0.030 17.5-19.5 1.00 1.75-2.50 (Ti+Cb) [0.20+4x(C+N)] to 0.80; N 0.035 0.015 17.0-20.0 --1.80-2.50 Ti [4x(C+N)+0.15] to 0.80; N 0.030 0.015 17.0-20.0 --1.80-2.50 Ti [4x(C+N)+0.15] to 0.80; N 0.030 0.030 17.00-20.00 0.60 1.75-2.50 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 0.035 0.030 17.00-20.00 0.60 1.75-2.50 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 0.035 0.030 17.00-20.00 0.60 1.75-2.50 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 0.040 0.015 17.0-20.0 --1.80-2.50 Ti [4x(C+N)+0.15] to 0.80; N 0.030 0.040 0.030 17.00-20.00 0.60 1.75-2.50 Ti, Nb, Zr or their combination 8x(C + N) to 0.80; N 0.025 0.040 0.030 17.00-20.00 0.60 1.75-2.50 Ti, Nb, Zr or their combination 8x(C + N) to 0.80; N 0.025 0.040 0.030 17.5-19.5 1.00 1.75-2.50 (Ti+Cb) [0.20 +4x(C+N)] to 0.80; N 0.035 0.035 0.030 17.00-21.00 0.60 --Al 2.00-4.00 0.040 0.030 17.00-21.00 0.60 --Al 2.00-4.00 0.040 0.030 23.0-27.0 0.75 --N 0.25 0.035 0.030 23.00-27.00 0.60 --Cu 0.30; N 0.25 0.040 0.030 24.0-28.0 1.00 --N 0.15-0.25 0.040 0.030 23.00-27.00 0.60 --N 0.25 0.020 0.020 25.0-27.5 0.50 0.75-1.50 (Ni+Cu) 0.50; Cu 0.20; Cb 0.05-0.20; N 0.015 0.020 0.020 25.0-27.5 0.50 0.75-1.50 (Ni+Cu) 0.50; Cu 0.20; Cb 0.05-0.20; N 0.015 0.030 0.020 25.00-27.50 0.50 0.75-1.50 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 0.030 0.020 25.00-27.00 0.50 0.75-1.50 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 0.030 0.020 25.00-27.50 0.50 0.75-1.50 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 0.030 0.020 25.00-27.50 0.50 0.75-1.50 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 0.030 0.020 25.00-27.50 0.50 0.75-1.50 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 0.020 0.020 25.00-27.50 0.50 0.75-1.50 (Ni+Cu) 0.50; Cu 0.20; Cb 0.05-0.20; N 0.015 P 0.040 0.040 0.040 0.040 0.035
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
449
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.2A Chemical Composition of Ferritic Stainless Steels (Continued) UNS Steel No No --------------------S44735 ---
C 0.010 0.010 0.010 0.010 0.010 0.030
Mn 0.40 0.40 0.40 0.40 0.40 1.00
Si 0.40 0.40 0.40 0.40 0.40 1.00
P 0.030 0.030 0.030 0.030 0.030 0.040
ASTM A240/A240M-15a
---
S44735
0.030
1.00
1.00
0.040
0.030
28.0-30.0
1.00
3.6-4.2
EN 10088-2:2014 SAE J405 JUN98
X2CrMoTi29-4 ---
--1.4592 S44735 ---
0.025 0.030
1.00 1.00
1.00 1.00
0.030 0.040
0.010 0.030
28.0-30.0 28.00-30.00
--1.00
3.5-4.5 3.60-4.20
Download From http://bbs.infoeach.com
---
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.020 28.50-32.00 0.50 1.50-2.50 0.020 28.00-32.00 0.50 1.50-2.50 0.020 28.50-32.00 0.50 1.50-2.50 0.020 28.50-32.00 0.50 1.50-2.50 0.020 28.50-32.00 0.50 1.50-2.50 0.030 28.0-30.0 1.00 3.6-4.2
Others (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 (Ni+Cu) 0.50 max.; Cu 0.20; N 0.015 (Ti+Cb) 6x(C+N) min.; (Ti+Cb) 0.20 to 1.00; N 0.045 (Ti+Cb) 6x(C+N) min.; (Ti+Cb) 0.20 to 1.00; N 0.045 Ti [4x(C+N)+0.15] to 0.80; N 0.045 (Ti+Cb) 0.20 to 1.00; (Ti+Cb) [6x(C+N)] min.; N 0.045
Download From http://bbs.infoeach.com
Designation Grade 00Cr30Mo2 Grade 00Cr30Mo2 Grade 00Cr30Mo2 Symbol SUS447J1 Symbol SUS447J1 ---
Specification GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
450
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels
ASTM A240/A240M-15a
Type 405
S40500
---
---
---
170
25
415
60
20
---
EN 10088-2:2014
X6CrAl13
---
1.4002
GB 3280-92
Grade 0Cr13Al
---
---
t≤8 t ≤ 13.5 t ≤ 25 ---
---------
230 210 210 175
---------
400-600 400-600 400-600 410
---------
17 L, 17 T 17 L, 17 T 17 L, 17 T 20
A A A A
GB 4237-92
Grade 0Cr13Al
---
---
---
---
177
---
410
---
20
A
GB 4238-92
Grade 0Cr13Al
---
---
---
---
175
---
410
---
20
A
GB 4239-91 JIS G 4304:2012
Grade 0Cr13Al Symbol SUS405
-----
-----
-----
-----
175 175
-----
410 410
-----
20 20
A A
JIS G 4305:2012
Symbol SUS405
---
---
---
---
175
---
410
---
20
A
Designation
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 170 25 415 60 20 see standard
Other 179 max. HB; 88 max. HRB 179 max. HBW; 88 max. HRBW ------183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 88 max. HRB 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Type 405
UNS Steel No No S40500 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
451
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M
ASTM A240/A240M-15a
Designation ---
---
UNS Steel No No S40977 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 280 41 450 65 18 see standard
---
---
---
205
30
415
60
22
see standard
S40977
---
---
---
280
41
450
65
18
---
S41050
---
---
---
205
30
415
60
22
---
t≤8 t ≤ 13.5 t ≤ 25 t≤8 t ≤ 13.5 t ≤ 25 ---
---------------
280 280 250 280 280 250 175
---------------
450-650 450-650 450-650 450-650 450-650 450-650 360
---------------
20 L, 20 T 20 L, 20 T 18 L, 18 T 20 L, 20 T 20 L, 20 T 18 L, 18 T 25
A A A A A A A
-----------------
320 300 280 280 280 250 205 275
------------30 40
450 450 430 450-650 450-650 450-650 380 415
------------55 60
20 L, 20 T A 20 L, 20 T A 20 L, 20 T A 20 L, 20 T A 20 L, 20 T A 18 L, 18 T A 22 see standard 20 see standard
EN 10028-7:2007
X2CrNi12
---
1.4003
EN 10088-2:2014
X2CrNi12
---
1.4003
JIS G 4312:2011
Symbol SUH409L
---
---
ISO 16143-1:2004
X2CrNi12
---
---
ISO 9328-7:2004
Grade X2CrNi12
---
---
ASME SA-240/SA-240M
---
S40945 S40975
-----
t≤6 t ≤ 12 t ≤ 25 t≤6 t ≤ 12 t ≤ 25 -----
ASTM A240/A240M-15a
---
S40945 S40975
-----
-----
-----
205 275
30 40
380 415
55 60
22 20
-----
EN 10088-2:2014
X2CrTi12
---
1.4512
ISO 16143-1:2004
X2CrTi12
---
---
ISO 4955:2005
X2CrTi12
---
---
t≤8 t ≤ 13.5 t≤6 t≤6 t ≤ 12 t ≤ 12 0.5 ≤ t < 3 3 ≤ t ≤ 12 5 ≤ t ≤ 15 5 ≤ t ≤ 25 1.5 ≤ t ≤ 25
-----------------------
210 210 220 175 200 175 210 210 210 210 210
-----------------------
380-560 380-560 380 360 380 360 390-590 390-590 390-590 390-590 390-590
-----------------------
25 L, 25 T 25 L, 25 T 25 L, 25 T 25 L, 25 T 25 L, 25 T 25 L, 25 T 25 L, 25 T 25 L, 25 T -------
A A A A A A A A A A A
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
S41050
Other 180 max. HB; 88 max. HRB 183 max. HB; 89 max. HRB 180 max. HBW; 88 max. HRBW 183 max. HBW; 89 max. HRBW T: 50 J @ RT T: 50 J @ RT T: 50 J @ RT ------162 max. HBW; 80 max. HRBW; 175 max. HV ------T: 50 J @ 20°C T: 50 J @ 20°C T: 50 J @ 20°C 80 max. HRB 197 max. HB; 92 max. HRB 80 max. HRBW 197 max. HBW; 92 max. HRBW -----------------------
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
452
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued) Steel No 1.4516
X6CrNiTi12
---
1.4516
ISO 9328-7:2004
Grade X6CrNiTi12
---
---
JIS G 4312:2011
Symbol SUH409
---
---
ASME SA-240/SA-240M
---
S42035
---
---
---
380
55
550
80
16
see standard
ASTM A240/A240M-15a
---
S42035
---
---
---
380
55
550
80
16
---
DIN 5512-3:2004
X5CrNiMoTi15-2
1.4589
EN 10088-2:2014
X5CrNiMoTi15-2
ASME SA-240/SA-240M
Type 429
--t 1.27
t > 0.050
205
30
450
65
22
see standard
t ≤ 1.27
t ≤ 0.050
205
30
450
65
20
---
t > 1.27
t > 0.050
205
30
450
65
22
---
Designation X6CrNiTi12
EN 10088-2:2014
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Type 429
---
1.4589
S42900
---
S42900
---
Section Thickness/Diameter mm in. t≤8 --t ≤ 13.5 --t ≤ 25 --t≤8 --t ≤ 13.5 --t ≤ 25 --t≤6 --t ≤ 12 --t ≤ 25 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 280 --450-650 --23 L, 23 T 280 --450-650 --23 L, 23 T 250 --450-650 --20 L, 20 T 280 --450-650 --23 L, 23 T 280 --450-650 --23 L, 23 T 250 --450-650 --20 L, 20 T 280 --450-650 --23 L, 23 T 280 --450-650 --23 L, 23 T 250 --450-650 --20 L, 20 T 175 --360 --22
Heat Treatment A A A A A A A A A A
16 T HR 14 T CR 16 T CR 16 L, 16 T A 14 L, 14 T A 20 see standard
GB 3280-92
Grade 1Cr15
---
---
---
---
205
---
450
---
22
A
GB 4237-92
Grade 1Cr15
---
---
---
---
205
---
450
---
22
A
GB 4239-91 JIS G 4304:2012
Grade 1Cr15 Symbol SUS429
-----
-----
-----
-----
205 205
-----
450 450
-----
22 22
A A
JIS G 4305:2012
Symbol SUS429
---
---
---
---
205
---
450
---
22
A
Other T: 50 J @ RT T: 50 J @ RT T: 50 J @ RT ------T: 50 J @ 20°C T: 50 J @ 20°C T: 50 J @ 20°C 162 max. HBW; 80 max. HRBW; 175 max. HV 180 max. HB; 88 max. HRB 180 max. HBW; 88 max. HRBW ----------183 max. HB; 89 max. HRB 183 max. HB; 89 max. HRB 183 max. HBW; 89 max. HRBW 183 max. HBW; 89 max. HRBW 183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 88 max. HRB 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
UNS No ---
Specification EN 10028-7:2007
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
453
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M
ASTM A240/A240M-15a
Designation Type 430
Type 430
UNS Steel No No S43000 ---
S43000
---
Section Thickness/Diameter mm in. t ≤ 1.27 t ≤ 0.050
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 205 30 450 65 20 see standard
t > 0.050
205
30
450
65
22
see standard
t ≤ 1.27
t ≤ 0.050
205
30
450
65
20
---
t > 1.27
t > 0.050
205
30
450
65
22
---
---------
260 240 240 205
---------
430-600 430-600 430-630 450
---------
20 L, 20 T 18 L, 18 T 20 L, 20 T 22
A A A A
EN 10088-2:2014
X6Cr17
---
1.4016
GB 3280-92
Grade 1Cr17
---
---
t≤8 t ≤ 13.5 t ≤ 25 ---
GB 4237-92
Grade 1Cr17
---
---
---
---
205
---
450
---
22
A
GB 4238-92
Grade 1Cr17
---
---
---
---
205
---
450
---
22
A
GB 4239-91 ISO 16143-1:2004
Grade 1Cr17 X6Cr17
-----
-----
JIS G 4304:2012
Symbol SUS430
---
---
--t≤6 t≤6 t ≤ 12 t ≤ 12 t ≤ 25 ---
---------------
205 250 205 230 205 230 205
---------------
450 450 450 450 450 430 420
---------------
22 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 22
A A A A A A A
JIS G 4305:2012
Symbol SUS430
---
---
---
---
205
---
420
---
22
A
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
t > 1.27
Other 183 max. HB; 89 max. HRB 183 max. HB; 89 max. HRB 183 max. HBW; 89 max. HRBW 183 max. HBW; 89 max. HRBW ------183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 88 max. HRB ----------183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
454
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued)
Specification EN 10028-7:2007
UNS No -------
Steel No 1.4510 1.4520 1.4510
-------
1.4511 1.4520 ---
GB 4239-91 ISO 16143-1:2004
Grade 00Cr17 X3CrTi17
-----
-----
ISO 4955:2005
X3CrNb17 X3CrTi17
-----
-----
JIS G 4304:2012
Grade X2CrTi17 Grade X3CrTi17 Symbol SUS430LX
-------
JIS G 4305:2012
Symbol SUS430LX
---
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014
Type 434 Type 434 X6CrMo17-1
GB 3280-92
Grade 1Cr17Mo
---
GB 4237-92
Grade 1Cr17Mo
GB 4239-91 JIS G 4304:2012
JIS G 4305:2012
ISO 9328-7:2004
Section Thickness/Diameter mm in. t≤4 --t≤4 --t≤8 --t ≤ 13.5 --t≤8 --t≤8 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 230 --420-600 --23 L, 23 T 180 --380-530 --24 L, 24 T 230 --420-600 --23 L, 23 T 230 --420-600 --23 L, 23 T 230 --420-600 --23 L, 23 T 180 --380-530 --24 L, 24 T 175 --365 --22
Heat Treatment A A A A A A A
-------
--t≤6 t≤6 t ≤ 12 t ≤ 12 t≤6 0.5 ≤ t ≤ 12 5 ≤ t ≤ 15 1.5 ≤ t ≤ 25 5 ≤ t ≤ 25 t ≤ 2.5 t≤3 ---
---------------------------
175 240 175 220 175 230 230 230 230 230 180 230 175
---------------------------
365 420 360 420 360 420 --------380-530 420-600 360
---------------------------
22 23 L, 23 T 23 L, 23 T 23 L, 23 T 23 L, 23 T 23 L, 23 T 23 L, 23 T ------24 L, 24 T 23 L, 23 T 22
A A A A A A A A A A A A A
---
---
---
175
---
360
---
22
A
---
----t≤8 t ≤ 13.5 ---
-----------
240 240 260 260 205
35 35 -------
450 450 450-630 450-630 450
65 65 -------
---
---
---
---
205
---
450
---
22
A
Grade 1Cr17Mo Symbol SUS434
-----
-----
-----
-----
205 205
-----
450 450
-----
22 22
A A
Symbol SUS434
---
---
---
---
205
---
450
---
22
A
S43400 --S43400 ----1.4113
22 see standard 22 --18 L, 18 T A 18 L, 18 T A 22 A
Other ------------183 max. HB; 88 max. HRB 88 max. HRB ----------------------183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV 89 max. HRB 89 max. HRBW ----183 max. HB; 88 max. HRB 183 max. HB; 88 max. HRB 88 max. HRB 183 max. HBW; 88 max. HRBW; 200 max. HV 183 max. HBW; 88 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
GB 3280-92
X3CrNb17 X2CrTi17 Grade 00Cr17
Download From http://bbs.infoeach.com
EN 10088-2:2014
Designation X3CrTi17 X2CrTi17 X3CrTi17
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
455
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued)
---
S43932
---
---
---
205
30
415
60
22
see standard
Type 439
S43035
---
---
---
205
30
415
60
22
---
---
S43932
---
---
---
205
30
415
60
22
---
ASME SA-240/SA-240M
---
S43940
---
---
---
250
36
430
62
18
see standard
ASTM A240/A240M-15a
---
S43940
---
---
---
250
36
430
62
18
---
EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ISO 4955:2005
X2CrTiNb18 X2CrTiNb18 Grade X2CrTiNb18 X2CrTiNb18
---------
1.4509 1.4509 -----
t≤4 t≤8 t ≤ 2.5 0.5 ≤ t ≤ 12 5 ≤ t ≤ 15 1.5 ≤ t ≤ 25 5 ≤ t ≤ 25
---------------
230 230 230 230 230 230 230
---------------
430-630 430-630 430-630 ---------
---------------
18 L, 18 T 18 L, 18 T 18 L, 18 T 18 L, 18 T 18 18 18
A A A A A A A
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Designation
Section Thickness/Diameter mm in. --------t≤8 -------
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 240 35 450 65 22 see standard 240 35 450 65 22 --280 --480-560 --25 L, 25 T A 205 30 415 60 22 see standard
Other 89 max. HRB 89 max. HRBW --183 max. HB; 89 max. HRB 183 max. HB; 89 max. HRB 183 max. HBW; 89 max. HRBW 183 max. HBW; 89 max. HRBW 180 max. HB; 88 max. HRB 180 max. HBW; 88 max. HRBW ---------------
Download From http://bbs.infoeach.com
Type 436 Type 436 X6CrMoNb17-1 Type 439
UNS Steel No No S43600 --S43600 ----1.4526 S43035 ---
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
456
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued)
ASTM A240/A240M-15a
Type 444
S44400
---
---
---
275
40
415
60
20
---
EN 10028-7:2007 EN 10088-2:2014
X2CrMoTi18-2 X2CrMoTi18-2
-----
1.4521 1.4521
GB 3280-92
Grade 00Cr18Mo2
---
---
t≤4 t≤8 t ≤ 12 t ≤ 13.5 ---
-----------
300 300 280 280 245
-----------
420-640 420-640 420-620 400-600 410
-----------
20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20
A A A A A
GB 4237-92
Grade 00Cr18Mo2
---
---
---
---
245
---
410
---
20
A
GB 4239-91 ISO 9328-7:2004 JIS G 4304:2012
Grade 00Cr18Mo2 Grade X2CrMoTi18-2 Symbol SUS444
-------
-------
--t ≤ 2.5 ---
-------
245 300 245
-------
410 420-640 410
-------
20 20 L, 20 T 20
A A A
JIS G 4305:2012
Symbol SUS444
---
---
---
---
245
---
410
---
20
A
GB 4238-92
Grade 1Cr19Al3
---
---
---
---
245
---
440
---
15
A
JIS G 4312:2011
Symbol SUH21
---
---
---
---
245
---
440
---
15
A
ASTM A240/A240M-15a
Type 446
S44600
---
---
---
275
40
515
65
20
---
GB 4238-92
Grade 2Cr25N
---
---
---
---
275
---
510
---
20
A
ISO 4955:2005
X15CrN26
---
---
JIS G 4312:2011
Symbol SUH446
---
---
0.5 ≤ t < 3 3 ≤ t ≤ 12 5 ≤ t ≤ 15 5 ≤ t ≤ 25 1.5 ≤ t ≤ 25 ---
-------------
280 280 280 280 280 275
-------------
500-700 500-700 500-700 500-700 500-700 510
-------------
13 L, 13 T 15 L, 15 T 15 15 15 20
A A A A A A
Designation
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 275 40 415 60 20 see standard
Other 217 max. HB; 96 max. HRB 217 max. HBW; 96 max. HRBW --------217 max. HB; 96 max. HRB 217 max. HB; 96 max. HRB 96 max. HRB --217 max. HBW; 96 max. HRBW; 230 max. HV 217 max. HBW; 96 max. HRBW; 230 max. HV 210 max. HB; 95 max. HRB 210 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 96 max. HRBW 201 max. HB; 95 max. HRB 212 max. HB 212 max. HB 212 max. HB 212 max. HB 212 max. HB 201 max. HBW; 95 max. HRBW; 210 max. HV
Download From http://bbs.infoeach.com
Type 444
UNS Steel No No S44400 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
457
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.2B Mechanical Properties of Ferritic Stainless Steels (Continued) UNS Steel No No S44627 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 275 40 450 65 22 see standard
ASTM A240/A240M-15a
Type XM-27
S44627
---
---
---
275
40
450
65
22
---
GB 3280-92
Grade 00Cr27Mo
---
---
---
---
245
---
410
---
22
A
GB 4237-92
Grade 00Cr27Mo
---
---
---
---
245
---
410
---
22
A
GB 4239-91 JIS G 4304:2012
Grade 00Cr27Mo Symbol SUSXM27
-----
-----
-----
-----
245 245
-----
410 410
-----
22 22
A A
JIS G 4305:2012
Symbol SUSXM27
---
---
---
---
245
---
410
---
22
A
GB 3280-92
Grade 00Cr30Mo2
---
---
---
---
295
---
450
---
22
A
GB 4237-92
Grade 00Cr30Mo2
---
---
---
---
295
---
450
---
22
A
GB 4239-91 JIS G 4304:2012
Grade 00Cr30Mo2 Symbol SUS447J1
-----
-----
-----
-----
295 295
-----
450 450
-----
22 22
A A
JIS G 4305:2012
Symbol SUS447J1
---
---
---
---
295
---
450
---
22
A
ASME SA-240/SA-240M
---
S44735
---
---
---
415
60
550
80
18
see standard
ASTM A240/A240M-15a
---
S44735
---
---
---
415
60
550
80
18
---
EN 10088-2:2014
X2CrMoTi29-4
---
1.4592
t≤8
---
430
---
550-700
---
20 L, 20 T
A
Other 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW 190 max. HB; 90 max. HRB 190 max. HB; 90 max. HRB 90 max. HRB 192 max. HBW; 90 max. HRBW; 200 max. HV 192 max. HBW; 90 max. HRBW; 200 max. HV 209 max. HB; 95 max. HRB 209 max. HB; 95 max. HRB 95 max. HRB 207 max. HBW; 95 max. HRBW; 220 max. HV 207 max. HBW; 95 max. HRBW; 220 max. HV 255 max. HB; 25 max. HRC 255 max. HBW; 25 max. HRC ---
Download From http://bbs.infoeach.com
Designation Type XM-27
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
458
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a
EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10088-2:2014 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 SAE J405 JUN98
UNS No S20100 S20100 S20100 S20100 S20100 S20100 S20100 S20100 ----------S20100 S20103 S20103 S20103 S20103 --S20103 S20153 S20153 S20153 S20153 S20153 S20200 S20200 S20200 S20200 --------S20200
Steel No ----------------1.4372 ------------------1.4371 --------------------1.4373 ---------
C 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.03 0.03 0.03 0.03 0.030 0.03 0.03 0.03 0.03 0.03 0.03 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15
Mn 5.50-7.50 5.50-7.50 5.5-7.5 5.5-7.5 5.50-7.50 5.50-7.50 5.5-7.5 5.5-7.5 5.5-7.5 5.50-7.50 5.50-7.50 5.50-7.50 5.5-7.5 5.50-7.50 5.50-7.50 5.5-7.5 5.50-7.50 5.5-7.5 6.0-8.0 5.50-7.50 6.40-7.50 6.4-7.5 6.40-7.50 6.4-7.5 6.40-7.50 7.50-10.00 7.5-10.0 7.50-10.00 7.5-10.0 7.5-10.5 7.50-10.00 7.50-10.00 7.50-10.00 7.50-10.0
Si 1.00 1.00 0.75 0.75 1.00 1.00 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 0.75 0.75 0.75 0.75 0.75 0.75 1.00 0.75 1.00 0.75 1.00 1.00 1.00 1.00 1.00
P 0.060 0.060 0.060 0.060 0.060 0.060 0.060 0.060 0.045 0.060 0.060 0.060 0.045 0.060 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.060 0.060 0.060 0.060 0.045 0.060 0.060 0.060 0.060
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.015 16.0-18.0 3.5-5.5 --0.030 16.00-18.00 3.50-5.50 --0.030 16.00-18.00 3.50-5.50 --0.030 16.00-18.00 3.50-5.50 --0.030 16.0-18.0 3.5-5.5 --0.030 16.00-18.00 3.50-5.50 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.030 16.0-18.0 3.5-5.5 --0.015 16.0-17.5 3.5-5.5 --0.030 16.00-18.00 3.50-5.50 --0.015 16.0-17.5 4.0-5.0 --0.015 16.0-17.5 4.0-5.0 --0.015 16.0-17.5 4.0-5.0 --0.015 16.0-17.5 4.0-5.0 --0.015 16.00-17.50 4.00-5.00 --0.030 17.0-19.0 4.0-6.0 --0.030 17.0-19.0 4.0-6.0 --0.030 17.0-19.0 4.0-6.0 --0.030 17.0-19.0 4.0-6.0 --0.015 17.0-19.0 4.0-6.0 --0.030 17.00-19.00 4.00-6.00 --0.030 17.00-19.00 4.00-6.00 --0.030 17.00-19.00 4.00-6.00 --0.030 17.00-19.00 4.00-6.00 ---
Others N 0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.05-0.25 N 0.25 N 0.25 N 0.25 N 0.05-0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.15-0.25; Cu 1.00 N 0.25 Cu 1.00; N 0.10-0.25 Cu 1.00; N 0.10-0.25 Cu 1.00; N 0.10-0.25 Cu 1.00; N 0.10-0.25 Cu 1.00; N 0.10-0.25 N 0.25 N 0.25 N 0.25 N 0.25 N 0.05-0.25 N 0.25 N 0.25 N 0.25 N 0.25
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A666-15
Designation Type 201-1 Type 201-2 Type 201-1 Type 201-2 Type 201-1 Type 201-2 Type 201-1 Type 201-2 X12CrMnNiN17-7-5 Grade 1Cr17Mn6Ni5N Grade 1Cr17Mn6Ni5N Grade 1Cr17Mn6Ni5N X12CrMnNiN17-7-5 Type 201 Type 201L Type 201L Type 201L Type 201L X2CrMnNiN17-7-5 --Type 201LN Type 201LN Type 201LN Type 201LN --Type 202 Type 202 Type 202 Type 202 X12CrMnNiN18-9-5 Grade 1Cr18Mn8Ni5N Grade 1Cr18Mn8Ni5N Grade 1Cr18Mn8Ni5N Type 202
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
459
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (continued)
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10088-2:2014
GB 4239-91 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 JIS G 4304:2012 SAE J405 JUN98
Type 301 Type 301 Type 301 Type 301 X10CrNi18-8 X5CrNi17-7 Grade 1Cr17Ni7 Grade 1Cr17Ni8 Grade 1Cr17Ni7 Grade 1Cr17Ni8 X10CrNi18-8 Symbol SUS301 Symbol SUS301J1 Symbol SUS301 Symbol SUS301J1 Type 301 Type 301L Type 301L Type 301L Type 301L Symbol SUS301L Symbol SUS301L Type 301LN Type 301LN Type 301LN Type 301LN X2CrNiN18-7 X2CrNiN18-7 Grade X2CrNiN18-7 Type 302 Type 302 Type 302 Type 302 Symbol SUS303 Type 302
UNS No S30100 S30100 S30100 S30100 ----------------------S30100 S30103 S30103 S30103 S30103 ----S30153 S30153 S30153 S30153 ------S30200 S30200 S30200 S30200 --S30200
Steel No --------1.4310 1.4319 ----------------------------------------1.4318 1.4318 ---------------
C 0.15 0.15 0.15 0.15 0.05-0.15 0.07 0.15-0.25 0.03-0.12 0.15 0.08-0.12 0.05-0.15 0.15 0.08-0.12 0.15 0.08-0.12 0.15 0.03 0.03 0.03 0.03 0.030 0.030 0.03 0.03 0.03 0.03 0.030 0.030 0.030 0.15 0.15 0.15 0.15 0.15 0.15
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 1.00 1.00 1.00 1.00 2.00 1.00 1.00 1.00 1.00 1.00 2.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 0.75
P 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.20 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.015 16.0-19.0 6.0-9.5 0.80 0.030 16.0-18.0 6.0-8.0 --0.030 16.00-18.00 6.00-8.00 --0.030 16.00-18.00 7.00-9.00 --0.030 16.00-18.00 6.00-8.00 --0.030 16.00-18.00 7.00-9.00 --0.030 16.0-19.0 6.0-9.5 0.80 0.030 16.00-18.00 6.00-8.00 --0.030 16.00-18.00 7.00-9.00 --0.030 16.00-18.00 6.00-8.00 --0.030 16.00-18.00 7.00-9.00 --0.030 16.00-18.00 6.00-8.00 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.00-18.00 6.00-8.00 --0.030 16.00-18.00 6.00-8.00 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.030 16.0-18.0 6.0-8.0 --0.015 16.5-18.5 6.0-8.0 --0.015 16.5-18.5 6.0-8.0 --0.015 16.5-18.5 6.0-8.0 --0.030 17.0-19.0 8.0-10.0 --0.030 17.0-19.0 8.0-10.0 --0.030 17.0-19.0 8.0-10.0 --0.030 17.0-19.0 8.0-10.0 --0.15 17.00-19.00 8.00-10.00 0.60 0.030 17.00-19.00 8.00-10.00 ---
Others N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 --------N 0.11 --------N 0.10 N 0.20 N 0.20 N 0.20 N 0.20 N 0.20 N 0.20 N 0.07-0.20 N 0.07-0.20 N 0.07-0.20 N 0.07-0.20 N 0.10-0.20 N 0.10-0.20 N 0.10-0.20 N 0.10 --N 0.10 ----N 0.10
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 3280-92
Designation
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
460
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (continued)
Designation Grade 1Cr18Ni9Si3 Grade 1Cr18Ni9Si3 Grade 1Cr18Ni9Si3 Grade 1Cr18Ni9Si3 Symbol SUS302B Symbol SUS302B Type 304 Type 304 Type 304 Type 304 X5CrNi18-10 X5CrNi18-10 Grade 0Cr18Ni9 Grade 0Cr18Ni9 Grade 0Cr18Ni9 Grade 0Cr18Ni9 X5CrNi18-9 Grade X5CrNi18-9 Symbol SUS304 Symbol SUS304 Type 304 X6CrNiCu17-8-2 Symbol SUS304J1 Symbol SUS304J1
UNS Steel No No ------------------------S30400 --S30400 --S30400 --S30400 ----1.4301 --1.4301 --------------------------------S30400 ---------------
C 0.15 0.15 0.15 0.15 0.15 0.15 0.07 0.08 0.07 0.08 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.07 0.08 0.08 0.08 0.08 0.08 0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 3.00 3.00 3.00
Si 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 2.00-3.00 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 1.70 1.70 1.70
P 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.5-19.5 8.0-10.5 --0.030 18.0-20.0 8.0-10.5 --0.030 17.5-19.5 8.0-10.5 --0.030 18.0-20.0 8.0-10.5 --0.015 17.5-19.5 8.0-10.5 --0.015 17.5-19.5 8.0-10.5 --0.030 17.00-19.00 8.00-11.00 --0.030 17.00-19.00 8.00-11.00 --0.030 17.00-19.00 8.00-11.00 --0.030 17.00-19.00 8.00-11.00 --0.030 17.5-19.5 8.0-10.5 --0.015 17.5-19.5 8.0-10.5 --0.030 18.00-20.00 8.00-10.50 --0.030 18.00-20.00 8.00-10.50 --0.030 18.00-20.00 8.00-10.50 --0.030 15.0-18.0 6.0-9.0 --0.030 15.00-18.00 6.00-9.00 --0.030 15.00-18.00 6.00-9.00 ---
Others ------------N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 --------N 0.11 N 0.11 ----N 0.10 Cu 1.00-3.00 Cu 1.00-3.00 Cu 1.00-3.00
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
461
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007
GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004 ISO 4955:2005 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98
UNS No S30403 S30403 S30403 S30403 ----------------------------S30403 S30409 S30409 ------S30409 S30451 S30451 S30451 S30451 ----------------S30451
Steel No --------1.4306 1.4307 1.4306 1.4307 --------------------------1.4948 --------------1.4315 1.4315 ---------------
C 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.04-0.10 0.04-0.10 0.04-0.08 0.04-0.08 0.04-0.10 0.04-0.10 0.08 0.08 0.08 0.08 0.06 0.06 0.08 0.08 0.08 0.07 0.08 0.08 0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.50 2.50 2.50 2.50 2.50 2.00
Si 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 0.75 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75
P 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 17.5-19.5 8.0-12.0 --0.030 18.0-20.0 8.0-12.0 --0.030 17.5-19.5 8.0-12.0 --0.030 18.0-20.0 8.0-12.0 --0.015 18.0-20.0 10.0-12.0 --0.015 17.5-19.5 8.0-10.5 --0.015 18.0-20.0 10.0-12.0 --0.015 17.5-19.5 8.0-10.5 --0.030 18.00-20.00 8.00-12.00 --0.030 18.00-20.00 11.00-15.00 --0.030 18.00-20.00 8.00-12.00 --0.030 18.00-20.00 8.00-12.00 --0.030 17.5-19.5 8.0-10.0 --0.030 18.0-20.0 10.0-12.0 --0.015 17.5-19.5 8.0-10.0 --0.015 18.0-20.0 10.0-12.0 --0.030 18.00-20.00 9.00-13.00 --0.030 18.00-20.00 9.00-13.00 --0.030 18.00-20.00 8.00-12.00 --0.030 18.0-20.0 8.0-10.5 --0.030 18.0-20.0 8.0-10.5 --0.015 17.0-19.0 8.0-11.0 --0.015 17.0-19.0 8.0-11.0 --0.030 17.0-19.0 8.0-11.0 --0.030 18.00-20.00 8.00-10.50 --0.030 18.0-20.0 8.0-10.5 --0.030 18.0-20.0 8.0-10.5 --0.030 18.0-20.0 8.0-10.5 --0.030 18.0-20.0 8.0-10.5 --0.015 18.0-20.0 8.0-11.0 --0.015 18.0-20.0 8.0-11.0 --0.030 18.00-20.00 7.00-10.50 --0.030 18.00-20.00 7.00-10.50 --0.030 18.00-20.00 7.00-10.50 --0.015 18.0-20.0 8.0-11.0 --0.030 18.00-20.00 7.00-10.50 --0.030 18.00-20.00 7.00-10.50 --0.030 18.00-20.00 8.00-10.50 ---
Others N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 --------N 0.11 N 0.11 N 0.11 N 0.11 ----N 0.10 ----N 0.10 N 0.11 ----N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.12-0.22 N 0.12-0.22 N 0.10-0.25 N 0.10-0.25 N 0.10-0.25 N 0.10-0.16 N 0.10-0.25 N 0.10-0.25 N 0.10-0.16
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10088-2:2014
Designation Type 304L Type 304L Type 304L Type 304L X2CrNi19-11 X2CrNi18-9 X2CrNi19-11 X2CrNi18-9 Grade 00Cr19Ni10 Grade 00Cr19Ni13Mo3 Grade 00Cr19Ni10 Grade 00Cr19Ni10 X2CrNi18-9 X2CrNi19-11 Grade X2CrNi18-9 Grade X2CrNi19-11 Symbol SUS304L Symbol SUS304L Type 304L Type 304H Type 304H X6CrNi18-10 Grade X6CrNi18-10 X7CrNi18-9 Type 304H Type 304N Type 304N Type 304N Type 304N X5CrNiN19-9 X5CrNiN19-9 Grade 0Cr19Ni9N Grade 0Cr19Ni9N Grade 0Cr19Ni9N Grade X5CrNiN18-8 Symbol SUS304N1 Symbol SUS304N1 Type 304N
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
462
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Specification GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012
UNS No ------------S30453 S30453 S30453 S30453 ------------------S30453 S30500 S30500 ------------S30500 S30600 S30600 --S30600 -----
Steel No --------------------1.4311 1.4311 --------------------1.4303 ----------------1.4361 -------
C 0.08 0.08 0.08 0.08 0.08 0.08 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.12 0.12 0.06 0.12 0.12 0.12 0.12 0.12 0.12 0.018 0.018 0.015 0.018 0.20 0.20
Mn 2.50 2.50 2.50 2.50 2.50 2.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 0.75 3.7-4.3 3.7-4.3 3.7-4.5 3.7-4.3 1.00 1.00
P 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.020 0.020 0.025 0.020 0.035 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 18.00-20.00 7.50-10.50 --0.030 18.00-20.00 7.50-10.50 --0.030 18.00-20.00 7.50-10.50 --0.030 18.00-20.00 7.50-10.50 --0.030 18.00-20.00 7.50-10.50 --0.030 18.00-20.00 7.50-10.50 --0.030 18.0-20.0 8.0-12.0 --0.030 18.0-20.0 8.0-12.0 --0.030 18.0-20.0 8.0-12.0 --0.030 18.0-20.0 8.0-12.0 --0.015 17.5-19.5 8.5-11.5 --0.015 17.5-19.5 8.5-11.5 --0.030 17.00-19.00 8.50-11.50 --0.030 17.00-19.00 8.50-11.50 --0.030 17.00-19.00 8.50-11.50 --0.030 17.5-19.5 8.0-10.0 --0.015 17.5-19.5 8.0-11.5 --0.030 17.00-19.00 8.50-11.50 --0.030 17.00-19.00 8.50-11.50 --0.030 18.00-20.00 8.00-12.00 --0.030 17.0-19.0 10.5-13.0 --0.030 17.0-19.0 10.5-13.0 --0.015 17.0-19.0 11.0-13.0 --0.030 17.00-19.00 10.50-13.00 --0.030 17.00-19.00 10.50-13.00 --0.030 17.00-19.00 10.50-13.00 --0.030 17.00-19.00 10.50-13.00 --0.030 17.00-19.00 10.50-13.00 --0.030 17.00-19.00 10.50-13.00 --0.020 17.0-18.5 14.0-15.5 0.20 0.020 17.0-18.5 14.0-15.5 0.20 0.010 16.5-18.5 14.0-16.0 0.20 0.020 17.0-18.5 14.0-15.5 0.20 0.030 22.00-24.00 12.00-15.00 --0.030 22.00-24.00 12.00-15.00 ---
Others Nb 0.15; N 0.15-0.30 Nb 0.15; N 0.15-0.30 Nb 0.15; N 0.15-0.30 Nb 0.15; N 0.15-0.30 Nb 0.15; N 0.15-0.30 Nb 0.15; N 0.15-0.30 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.10-0.16 ----N 0.10 ------------Cu 0.50 Cu 0.50 N 0.10 Cu 0.50 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 4305:2012 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 SAE J405 JUN98 GB 4238-92 JIS G 4312:2011
Designation Grade 0Cr19Ni10NbN Grade 0Cr19Ni10NbN Grade 0Cr19Ni10NbN Symbol SUS304N2 Symbol SUS304N2-X Symbol SUS304N2 Type 304LN Type 304LN Type 304LN Type 304LN X2CrNiN18-10 X2CrNiN18-10 Grade 00Cr18Ni10N Grade 00Cr18Ni10N Grade 00Cr18Ni10N X2CrNiN18-9 Grade X2CrNiN18-10 Symbol SUS304LN Symbol SUS304LN Type 304LN Type 305 Type 305 X4CrNi18-12 Grade 1Cr18Ni12 Grade 1Cr18Ni12 Grade 1Cr18Ni12 Symbol SUS305 Symbol SUS305 Type 305 ----X1CrNiSi18-15-4 --Grade 2Cr23Ni13 Symbol SUH309
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
463
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
JIS G 4312:2011 EN 10095:1999 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10095:1999 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 4955:2005 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004 SAE J405 JUN98
Designation Type 309S Type 309S X12CrNi23-13 Grade 0Cr23Ni13 Grade 0Cr23Ni13 Grade 0Cr23Ni13 Grade 0Cr23Ni13 X12CrNi23-13 Symbol SUS309S Symbol SUS309S Type 309S Type 309H Type 309H X6CrNi23-13 Grade X6CrNi23-13 Type 309H Grade 1Cr25Ni20Si2 Grade 2Cr25Ni20 Symbol SUH310 X15CrNiSi25-21 Type 310S Type 310S X8CrNi25-21 Grade 0Cr25Ni20 Grade 0Cr25Ni20 Grade 0Cr25Ni20 Grade 0Cr25Ni20 X8CrNi25-21 Symbol SUS310S Symbol SUS310S Type 310S Type 310H Type 310H X6CrNi25-20 Grade X6CrNi25-20 Type 310H
UNS No S30908 S30908 ----------------S30908 S30909 S30909 ----S30909 --------S31008 S31008 ----------------S31008 S31009 S31009 ----S31009
Steel No ----1.4833 --------------------1.4950 ----------1.4841 ----1.4845 --------------------1.4951 -----
C 0.08 0.08 0.15 0.08 0.08 0.08 0.08 0.15 0.08 0.08 0.08 0.04-0.10 0.04-0.10 0.04-0.08 0.04-0.08 0.04-0.10 0.20 0.25 0.25 0.20 0.08 0.08 0.10 0.08 0.08 0.08 0.08 0.10 0.08 0.08 0.08 0.04-0.10 0.04-0.10 0.04-0.08 0.04-0.08 0.04-0.10
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 1.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 1.00 1.50 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 0.70 0.70 0.75 1.50-2.50 1.50 1.50 1.50-2.50 1.50 1.50 1.50 1.00 1.00 1.00 1.50 1.50 1.50 1.50 1.50 0.75 0.75 0.70 0.70 0.75
P 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.045 0.035 0.035 0.040 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 22.0-24.0 12.0-15.0 --0.030 22.0-24.0 12.0-15.0 --0.015 22.00-24.00 12.00-14.00 --0.030 22.00-24.00 12.00-15.00 --0.030 22.00-24.00 12.00-15.00 --0.030 22.00-24.00 12.00-15.00 --0.030 22.00-24.00 12.00-15.00 --0.015 22.0-24.0 12.0-14.0 --0.030 22.00-24.00 12.00-15.00 --0.030 22.00-24.00 12.00-15.00 --0.030 22.00-24.00 12.00-15.00 --0.030 22.0-24.0 12.0-15.0 --0.030 22.0-24.0 12.0-15.0 --0.015 22.0-24.0 12.0-15.0 --0.015 22.0-24.0 12.0-15.0 --0.030 22.00-24.00 12.00-15.00 --0.030 24.00-27.00 18.00-21.00 --0.030 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.015 24.00-26.00 19.00-22.00 --0.030 24.0-26.0 19.0-22.0 --0.030 24.0-26.0 19.0-22.0 --0.015 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.015 24.0-26.0 19.0-22.0 --0.030 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.030 24.00-26.00 19.00-22.00 --0.030 24.0-26.0 19.0-22.0 --0.030 24.0-26.0 19.0-22.0 --0.015 24.0-26.0 19.0-22.0 --0.015 24.0-26.0 19.0-22.0 --0.030 24.00-26.00 19.00-22.00 ---
Others ----N 0.11 --------N 0.11 ----------N 0.10 N 0.11 --------N 0.11 ----N 0.11 --------N 0.11 ----------N 0.10 N 0.11 ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10095:1999 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 4955:2005 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 ISO 9328-7:2004 SAE J405 JUN98 GB 4238-92
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
464
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98
Designation Type 310 MoLN Type 310 MoLN X1CrNiMoN25-22-2 X1CrNiMoN25-22-2 X1CrNiMoN25-22-2 Grade X1CrNiMoN25-22-2 Type 310 MoLN ----X1CrNiMoCuN20-18-7 X1CrNiMoCuN20-18-7 Grade X1CrNiMoCuN20-18-7 Symbol SUS312L Symbol SUS312L --Type 316 Type 316 Type 316 Type 316 X5CrNiMo17-12-2 X3CrNiMo17-13-3 X5CrNiMo17-12-2 X3CrNiMo17-13-3 Grade 0Cr17Ni12Mo2 Grade 0Cr17Ni12Mo2 Grade 0Cr17Ni12Mo2 Grade 0Cr17Ni12Mo2 X5CrNiMo17-12-2 X3CrNiMo17-12-3 Grade X3CrNiMo17-12-3 Grade X5CrNiMo17-12-2 Symbol SUS316 Symbol SUS316 Type 316
UNS No S31050 S31050 --------S31050 S31254 S31254 ----------S31254 S31600 S31600 S31600 S31600 ----------------------------S31600
Steel No ----1.4466 1.4466 ----------1.4547 1.4547 ----------------1.4401 1.4436 1.4401 1.4436 -----------------------
C 0.020 0.020 0.020 0.020 0.020 0.020 0.030 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.08 0.08 0.08 0.08 0.07 0.05 0.07 0.05 0.08 0.08 0.08 0.08 0.07 0.05 0.05 0.07 0.08 0.08 0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.50 0.50 0.70 0.70 0.70 0.70 0.50 0.80 0.80 0.70 0.70 0.70 0.80 0.80 0.80 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75
P 0.030 0.030 0.025 0.025 0.025 0.025 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.010 24.0-26.0 20.5-23.5 1.60-2.60 0.010 24.0-26.0 20.5-23.5 1.60-2.60 0.010 24.0-26.0 21.0-23.0 2.00-2.50 0.010 24.0-26.0 21.0-23.0 2.00-2.50 0.010 24.0-26.0 21.0-23.0 2.00-2.50 0.010 24.0-26.0 21.0-23.0 2.00-2.50 0.010 24.00-26.00 21.00-23.00 2.00-3.00 0.010 19.5-20.5 17.5-18.5 6.0-6.5 0.010 19.5-20.5 17.5-18.5 6.0-6.5 0.010 19.5-20.5 17.5-18.5 6.0-7.0 0.010 19.5-20.5 17.5-18.5 6.0-7.0 0.010 19.5-20.5 17.5-18.5 6.0-7.0 0.015 19.00-21.00 17.50-19.50 6.00-7.00 0.015 19.00-21.00 17.50-19.50 6.00-7.00 0.010 19.50-20.50 17.50-18.50 6.00-6.50 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.015 16.5-18.5 10.0-13.0 2.00-2.50 0.015 16.5-18.5 10.5-13.0 2.50-3.00 0.015 16.5-18.5 10.0-13.0 2.00-2.50 0.015 16.5-18.5 10.5-13.0 2.50-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.5-18.5 10.0-13.0 2.00-3.00 0.030 16.5-18.5 10.5-13.0 2.50-3.00 0.015 16.5-18.5 10.5-13.0 2.50-3.00 0.015 16.5-18.5 10.0-13.0 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00
Others N 0.09-0.15 N 0.09-0.15 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 Cu 0.50-1.00; N 0.18-0.22 Cu 0.50-1.00; N 0.18-0.25 Cu 0.50-1.00; N 0.18-0.25 Cu 0.50-1.00; N 0.18-0.25 Cu 0.50-1.00; N 0.18-0.25 Cu 0.50-1.00; N 0.16-0.25 Cu 0.50-1.00; N 0.16-0.25 Cu 0.50-1.00; N 0.18-0.22 N 0.10 --N 0.10 --N 0.10 N 0.10 N 0.10 N 0.10 --------N 0.11 N 0.11 N 0.11 N 0.11 ----N 0.10
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
465
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10028-7:2007
GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004
ISO 9328-7:2004
JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012
UNS No S31603 S31603 S31603 S31603 ----------------------------------S31603 -------------------
Steel No --------1.4404 1.4432 1.4435 1.4404 1.4432 1.4435 -------------------------------------------
C 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.08 0.08 0.08 0.08 0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
P 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.045 0.045 0.035 0.035 0.035 0.045 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.015 16.5-18.5 10.0-13.0 2.00-2.50 0.015 16.5-18.5 10.5-13.0 2.50-3.00 0.015 17.0-19.0 12.5-15.0 2.50-3.00 0.015 16.5-18.5 10.0-13.0 2.00-2.50 0.015 16.5-18.5 10.5-13.0 2.50-3.00 0.015 17.0-19.0 12.5-15.0 2.50-3.00 0.030 16.00-18.00 12.00-15.00 2.00-3.00 0.030 16.00-18.00 12.00-15.00 2.00-3.00 0.030 16.00-18.00 12.00-15.00 2.00-3.00 0.030 16.5-18.5 10.0-13.0 2.00-3.00 0.030 16.5-18.5 10.5-13.0 2.50-3.00 0.015 17.0-19.0 12.5-15.0 2.50-3.00 0.015 16.5-18.5 10.0-13.0 2.00-3.00 0.015 16.5-18.5 10.5-13.0 2.50-3.00 0.015 17.0-19.0 12.5-15.0 2.50-3.00 0.030 16.00-18.00 12.00-15.00 2.00-3.00 0.030 16.00-18.00 12.00-15.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 17.00-19.00 12.00-16.00 1.20-2.75 0.030 17.00-19.00 12.00-16.00 1.20-2.75 0.030 17.00-19.00 12.00-16.00 1.20-2.75 0.030 17.00-19.00 12.00-16.00 1.20-2.75 0.030 17.00-19.00 10.00-14.00 1.20-2.75 0.030 17.00-19.00 10.00-14.00 1.20-2.75 0.030 17.00-19.00 10.00-14.00 1.20-2.75 0.030 17.00-19.00 10.00-14.00 1.20-2.75 0.030 17.00-19.00 10.00-14.00 1.20-2.75
Others N 0.10 --N 0.10 --N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 N 0.10 ------N 0.11 N 0.11 N 0.11 N 0.11 N 0.11 N 0.11 ----N 0.10 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50 Cu 1.00-2.50
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10088-2:2014
Designation Type 316L Type 316L Type 316L Type 316L X2CrNiMo17-12-2 X2CrNiMo17-12-3 X2CrNiMo18-14-3 X2CrNiMo17-12-2 X2CrNiMo17-12-3 X2CrNiMo18-14-3 Grade 00Cr17Ni14Mo2 Grade 00Cr17Ni14Mo2 Grade 00Cr17Ni14Mo2 X2CrNiMo17-12-2 X2CrNiMo17-12-3 X2CrNiMo18-14-3 Grade X2CrNiMo17-12-2 Grade X2CrNiMo17-12-3 Grade X2CrNiMo18-14-3 Symbol SUS316L Symbol SUS316L Type 316L Grade 00Cr18Ni12Mo2Cu2 Grade 00Cr18Ni14Mo2Cu2 Symbol SUS316J1L Symbol SUS316J1L Grade 0Cr18Ni12Mo2Cu2 Grade 0Cr18Ni12Mo2Cu2 Grade 0Cr18Ni12Mo2Cu2 Symbol SUS316J1 Symbol SUS316J1
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
466
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Designation Type 316Ti Type 316Ti X6CrNiMoTi17-12-2 X6CrNiMoTi17-12-2 Grade 0Cr18Ni12Mo2Ti Grade 0Cr18Ni12Mo2Ti X6CrNiMoTi17-12-2 Grade X6CrNiMoTi17-12-2 Symbol SUS316Ti Symbol SUS316Ti Type 316Ti Type 316Cb Type 316Cb X6CrNiMoNb17-12-2 X6CrNiMoNb17-12-2 Grade X6CrNiMoNb17-12-2 Type 316Cb Type 316N Type 316N Type 316N Type 316N Grade 0Cr17Ni12Mo2N Grade 0Cr17Ni12Mo2N Grade 0Cr17Ni12Mo2N Symbol SUS316N Symbol SUS316N Type 316N
UNS No S31635 S31635 ----------------S31635 S31640 S31640 ------S31640 S31651 S31651 S31651 S31651 ----------S31651
Steel No ----1.4571 1.4571 ------------------1.4580 1.4580 -------------------------
C 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 0.75 0.75 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 0.75
P 0.045 0.045 0.045 0.045 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.015 16.5-18.5 10.5-13.5 2.00-2.50 0.015 16.5-18.5 10.5-13.5 2.00-2.50 0.030 16.00-19.00 11.00-14.00 1.80-2.50 0.030 16.00-19.00 11.00-14.00 1.80-2.50 0.030 16.5-18.5 10.5-13.5 2.00-2.50 0.015 16.5-18.5 10.5-13.5 2.00-2.50 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.0-3.0 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.015 16.5-18.5 10.5-13.5 2.00-2.50 0.015 16.5-18.5 10.5-13.5 2.00-2.50 0.015 16.5-18.5 10.5-13.5 2.00-2.50 0.030 16.00-18.00 10.00-14.00 2.0-3.0 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00
Others Ti 5x(C+N) to 0.70; N 0.10 Ti 5x(C+N) to 0.70; N 0.10 Ti [5xC] to 0.70 Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC to 0.07 Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC min Ti 5xC min Ti [5x(C+N)] to 0.70; N 0.10 Cb 10xC to 1.10; N 0.10 Cb 10xC to 1.10 ; N 0.10 Nb 10xC to 1.00 Nb 10xC to 1.00 Nb 10xC to 1.00 Cb 10xC to 1.10; N 0.10 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.16 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 N 0.10-0.16
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 SAE J405 JUN98 ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
467
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014
JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 4237-92 GB 4239-91 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98
UNS No S31653 S31653 ------------------------S31653 S31700 S31700 ------------S31700 ----------S31703 S31703 --------------S31703
Steel No ----1.4406 1.4429 1.4406 1.4429 --------------------------------------------------1.4438 1.4438 -------------
C 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.040 0.040 0.040 0.040 0.040 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.50 2.50 2.50 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 0.75 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75
P 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.045 0.045 0.045 0.045
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.030 16.0-18.0 10.0-14.0 2.00-3.00 0.015 16.5-18.5 10.0-12.5 2.00-2.50 0.015 16.5-18.5 11.0-14.0 2.50-3.00 0.015 16.5-18.5 10.0-12.5 2.00-2.50 0.015 16.5-18.5 11.0-14.0 2.50-3.00 0.030 16.50-18.50 10.50-14.50 2.00-3.00 0.030 16.50-18.50 10.50-14.50 2.00-3.00 0.030 16.50-18.50 10.50-14.50 2.00-3.00 0.030 16.5-18.5 10.5-13.0 2.50-3.00 0.015 16.5-18.5 10.0-12.5 2.00-3.00 0.015 16.5-18.5 11.0-13.0 2.50-3.00 0.030 16.50-18.50 10.50-14.50 2.00-3.00 0.030 16.50-18.50 10.50-14.50 2.00-3.00 0.030 16.00-18.00 10.00-14.00 2.00-3.00 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 16.00-19.00 15.00-17.00 4.00-6.00 0.030 16.00-19.00 15.00-17.00 4.00-6.00 0.030 16.00-19.00 15.00-17.00 4.00-6.00 0.030 16.00-19.00 15.00-17.00 4.00-6.00 0.030 16.00-19.00 15.00-17.00 4.00-6.00 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.015 17.5-19.5 13.0-16.0 3.0-4.0 0.015 17.5-19.5 13.0-16.0 3.0-4.0 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.015 17.5-19.5 13.0-16.0 3.00-4.0 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00
Others N 0.10-0.16 N 0.10-0.16 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.10-0.16 N 0.10 N 0.10 ------------N 0.10 ----------N 0.10 N 0.10 N 0.10 N 0.10 ----N 0.11 ----N 0.10
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 3280-92 GB 4237-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004
Designation Type 316LN Type 316LN X2CrNiMoN17-11-2 X2CrNiMoN17-13-3 X2CrNiMoN17-11-2 X2CrNiMoN17-13-3 Grade 00Cr17Ni13Mo2N Grade 00Cr17Ni13Mo2N Grade 00Cr17Ni13Mo2N X2CrNiMoN17-12-3 Grade X2CrNiMoN17-11-2 Grade X2CrNiMoN17-13-3 Symbol SUS316LN Symbol SUS316LN Type 316LN Type 317 Type 317 Grade 0Cr19Ni13Mo3 Grade 0Cr19Ni13Mo3 Grade 0Cr19Ni13Mo3 Grade 0Cr19Ni13Mo3 Symbol SUS317 Symbol SUS317 Type 317 Grade 0Cr18Ni16Mo5 Grade 0Cr18Ni16Mo5 Grade 0Cr18Ni16Mo5 Symbol SUS317J1 Symbol SUS317J1 Type 317L Type 317L X2CrNiMo18-15-4 X2CrNiMo18-15-4 Grade 00Cr19Ni13Mo3 Grade 00Cr19Ni13Mo3 Grade X2CrNiMo18-15-4 Symbol SUS317L Symbol SUS317L Type 317L
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
468
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Designation Type 317LMN Type 317LMN X2CrNiMoN17-13-5 X2CrNiMoN17-13-5 Grade X2CrNiMoN17-13-5 --Type 317LN Type 317LN X2CrNiMoN18-12-4 X2CrNiMoN18-12-4 Grade X2CrNiMoN18-12-4 Symbol SUS317LN Symbol SUS317LN Type 317LN Type 321 Type 321 X6CrNiTi18-10 X6CrNiTi18-10 Grade 0Cr18Ni10Ti Grade 0Cr18Ni10Ti Grade 0Cr18Ni10Ti Grade 0Cr18Ni10Ti X6CrNiTi18-10 Grade X6CrNiTi18-10 Symbol SUS321 Symbol SUS321 Type 321 Type 321H Type 321H Grade 1Cr18Ni9 Grade 1Cr18Ni9 Grade 1Cr18Ni9 X7CrNiTi18-10 Type 321H X12NiCrSi35-16 Grade 1Cr16Ni35 Symbol SUH330
UNS No S31726 S31726 ------S31726 S31753 S31753 ----------S31753 S32100 S32100 --------------------S32100 S32109 S32109 --------S32109 -------
Steel No ----1.4439 1.4439 --------1.4434 1.4434 ------------1.4541 1.4541 --------------------------------1.4864 -----
C 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.04-0.10 0.04-0.10 0.15 0.15 0.15 0.04-0.10 0.04-0.10 0.15 0.15 0.15
Mn 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.75 0.75 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.75 0.75 1.00 1.00 1.00 1.00 0.75 1.00-2.00 1.50 1.50
P 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.045 0.045 0.045 0.035 0.035 0.035 0.045 0.045 0.045 0.035 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 17.0-20.0 13.5-17.5 4.0-5.0 0.030 17.0-20.0 13.5-17.5 4.0-5.0 0.015 16.5-18.5 12.5-14.5 4.0-5.0 0.015 16.5-18.5 12.5-14.5 4.0-5.0 0.015 16.5-18.5 12.5-14.5 4.0-5.0 0.030 17.00-20.00 13.50-17.50 4.0-5.0 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.030 18.0-20.0 11.0-15.0 3.0-4.0 0.015 16.5-19.5 10.5-14.0 3.0-4.0 0.015 16.5-19.5 10.5-14.0 3.0-4.0 0.015 16.5-19.5 10.5-14.0 3.00-4.0 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 18.00-20.00 11.00-15.00 3.00-4.00 0.030 17.0-19.0 9.0-12.0 --0.030 17.0-19.0 9.0-12.0 --0.015 17.0-19.0 9.0-12.0 --0.015 17.0-19.0 9.0-12.0 --0.030 17.00-19.00 9.00-12.00 --0.030 17.00-19.00 9.00-12.00 --0.030 17.00-19.00 9.00-12.00 --0.030 17.00-19.00 9.00-12.00 --0.030 17.0-19.0 9.0-12.0 --0.015 17.0-19.0 9.0-12.0 --0.030 17.00-19.00 9.00-13.00 --0.030 17.00-19.00 9.00-13.00 --0.030 17.00-19.00 9.00-12.00 --0.030 17.0-19.0 9.0-12.0 --0.030 17.0-19.0 9.0-12.0 --0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.00-19.00 8.00-10.00 --0.030 17.0-19.0 9.0-12.0 --0.030 17.00-19.00 9.00-12.00 --0.015 15.00-17.00 33.00-37.00 --0.030 14.00-17.00 33.00-37.00 --0.030 14.00-17.00 33.00-37.00 ---
Others N 0.10-0.20 N 0.10-0.20 N 0.12-0.22 N 0.12-0.22 N 0.12-0.22 N 0.10-0.20 N 0.10-0.22 N 0.10-0.22 N 0.10-0.20 N 0.10-0.20 N 0.10-0.20 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 Ti 5x(C+N) to 0.70; N 0.10 Ti 5x(C+N) to 0.70 ; N 0.10 Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC min. Ti 5xC min. Ti 5xC min. Ti 5xC min. Ti 5xC to 0.70 Ti 5xC to 0.70 Ti 5xC min. Ti 5xC min. Ti 5x(C+N) to 0.70; N 0.10 Ti 4x(C+N) to 0.70 Ti 4x(C+N) to 0.70 Ti 5x(C-0.02) to 0.80 Ti 5x(C-0.02) to 0.80 Ti 5x(C-0.02) to 0.80 Ti 5xC to 0.80 Ti 4x(C+N) to 0.70 N 0.11 -----
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a GB 3280-92 GB 4237-92 GB 4239-91 ISO 4955:2005 SAE J405 JUN98 EN 10095:1999 GB 4238-92 JIS G 4312:2011
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
469
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued) Steel No 1.4513 ---
C 0.025 0.025
Mn 1.00 1.00
Si 1.00 1.00
Grade 00Cr17Mo
---
---
0.025
1.00
1.00
GB 4239-91
Grade 00Cr17Mo
---
---
0.025
1.00
1.00
JIS G 4304:2012
Symbol SUS436L
---
---
0.025
1.00
1.00
JIS G 4305:2012
Symbol SUS436L
---
---
0.025
1.00
1.00
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 EN 10088-2:2014 EN 10151:2002 ISO 16143-1:2004 EN 10028-7:2007 EN 10302:2008 ISO 9328-7:2004 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012
Type 347 Type 347 X6CrNiNb18-10 X6CrNiNb18-10 Grade 0Cr18Ni11Nb Grade 0Cr18Ni11Nb Grade 0Cr18Ni11Nb Grade 0Cr18Ni11Nb X6CrNiNb18-10 Grade X6CrNiNb18-10 Symbol SUS347 Symbol SUS347 Type 347 X11CrNiMnN19-8-6 X11CrNiMnN19-8-6 X11CrNiMnN19-8-6 X6CrNiTiB18-10 X6CrNiTiB18-10 Grade X6CrNiTiB18-10 Grade 0Cr18Ni13Si4 Grade 0Cr18Ni13Si4 Grade 0Cr18Ni13Si4 Grade 0Cr18Ni13Si4 Symbol SUSXM15J1 Symbol SUSXM15J1
S34700 S34700 --------------------S34700 -------------------------
----1.4550 1.4550 ------------------1.4369 1.4369 --1.4941 1.4941 ---------------
0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.07-0.15 0.07-0.15 0.07-0.15 0.04-0.08 0.04-0.08 0.04-0.08 0.08 0.08 0.08 0.08 0.08 0.08
2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 5.0-7.5 5.0-7.5 5.0-7.5 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
0.75 0.75 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.75 0.50-1.00 0.50-1.00 0.50-1.00 1.00 1.00 1.00 3.00-5.00 3.00-5.00 3.00-5.00 3.00-5.00 3.00-5.00 3.00-5.00
Designation X2CrMoTi17-1 Grade 00Cr17Mo
GB 4237-92
Download From http://bbs.infoeach.com
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo Others 0.015 16.0-18.0 --0.80-1.40 Ti [4x(C+N)+0.15] to 0.80; N 0.020 0.030 16.00-19.00 0.60 0.75-1.25 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 0.035 0.030 16.00-19.00 0.60 0.75-1.25 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 0.035 0.030 16.00-19.00 0.60 0.75-1.25 Ti 8x(C+N) to 0.80; Nb 8x(C+N) to 0.80; Zr 8x(C+N) to 0.80; (Ti+Nb+Zr) 8x(C+N) to 0.80; N 0.025 0.040 0.030 16.00-19.00 0.60 0.75-1.50 Ti, Nb, Zr or their combination 8x(C + N) to 0.80; N 0.025 0.040 0.030 16.00-19.00 0.60 0.75-1.50 Ti, Nb, Zr or their combination 8x(C + N) to 0.80; N 0.025 0.045 0.030 17.0-19.0 9.0-13.0 --Cb 10xC to 1.00 0.045 0.030 17.0-19.0 9.0-13.0 --Cb 10xC to 1.00 0.045 0.015 17.0-19.0 9.0-12.0 --Nb 10xC to 1.00 0.045 0.015 17.0-19.0 9.0-12.0 --Nb 10xC to 1.00 0.035 0.030 17.00-19.00 9.00-13.00 --Nb 10xC min. 0.035 0.030 17.00-19.00 9.00-13.00 --Nb 10xC min. 0.035 0.030 17.00-19.00 9.00-13.00 --Nb 10xC min. 0.035 0.030 17.00-19.00 9.00-13.00 --Nb 10xC min. 0.045 0.030 17.0-19.0 9.0-12.0 --Nb 10xC to 1.00 0.045 0.015 17.0-19.0 9.0-12.0 --Nb 10xC to 1.00 0.045 0.030 17.00-19.00 9.00-13.00 --Nb 10xC min. 0.045 0.030 17.00-19.00 9.00-13.00 --Nb 10xC min. 0.045 0.030 17.00-19.00 9.00-13.00 --Cb 10xC to 1.00 0.030 0.015 17.5-19.5 6.5-8.5 --N 0.20-0.30 0.030 0.015 17.5-19.5 6.5-8.5 --N 0.20-0.30 0.030 0.015 17.5-19.5 6.5-8.5 --N 0.20-0.30 0.035 0.015 17.0-19.0 9.0-12.0 --Ti 5xC to 0.70; B 0.0015-0.0050 0.035 0.015 17.0-19.0 9.0-12.0 --Ti 5xC to 0.80; B 0.0015-0.0050 0.035 0.015 17.0-19.0 9.0-12.0 --Ti 5xC to 0.70; B 0.0015-0.0050 0.035 0.030 15.00-20.00 11.50-15.00 ----0.035 0.030 15.00-20.00 11.50-15.00 ----0.035 0.030 15.00-20.00 11.50-15.00 ----0.035 0.030 15.00-20.00 11.50-15.00 ----0.045 0.030 15.00-20.00 11.50-15.00 ----0.045 0.030 15.00-20.00 11.50-15.00 ----P 0.040 0.035
Download From http://bbs.infoeach.com
UNS No -----
Specification EN 10088-2:2014 GB 3280-92
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
470
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued) UNS Steel No No C --1.4597 0.10 ----0.10 S31060 --0.05-0.10
ASTM A240/A240M-15a
---
S31060
---
EN 10302:2008
X8CrNiNb16-13 X6CrNiMoTiB17-13 X1CrNi25-21 X1CrNi25-21 X1CrNi25-21 Grade X1CrNi25-21 ----X2CrNiMnMoN25-18-6-5 X2CrNiMnMoN25-18-6-5 ------X1CrNiMoCuNW24-22-6 ------X1CrNiMoCuN24-22-8 X1CrNiMoCuN24-22-8 --X8CrNiTi18-10 Grade 1Cr18Ni9Ti Grade 1Cr18Ni9Ti Grade 1Cr18Ni9Ti Grade 1Cr18Ni9Ti Type 347H Type 347H X7CrNiNb18-10 Type 347H X3CrNiMoBN17-13-3 X3CrNiMoBN17-13-3 Grade X3CrNiMoBN17-13-3
------------S34565 S34565 ----S34565 S31266 S31266 --S31266 S32654 S32654 ----S32654 ----------S34709 S34709 --S34709 -------
1.4961 1.4983 1.4335 1.4335 --------1.4565 --------1.4659 ------1.4652 ----1.4878 ----------------1.4910 1.4910 ---
EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 ISO 16143-1:2004 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014 ISO 16143-1:2004 SAE J405 JUN98 EN 10095:1999 GB 3280-92 GB 4237-92 GB 4238-92 GB 4239-91 ASME SA-240/SA-240M ASTM A240/A240M-15a ISO 4955:2005 SAE J405 JUN98 EN 10028-7:2007 EN 10302:2008 ISO 9328-7:2004
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 15.0-18.0 3.00 1.00 0.030 16.0-18.0 2.00 1.00 0.030 22.0-24.0 10.0-12.5 ---
Mn 6.5-9.0 6.5-8.5 1.00
Si 2.00 2.00 0.50
P 0.040 0.040 0.040
0.05-0.10
1.00
0.50
0.040
0.030
22.0-24.0
10.0-12.5
---
0.04-0.10 0.04-0.08 0.020 0.020 0.02 0.020 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.020 0.030 0.020 0.020 0.020 0.020 0.020 0.10 0.12 0.12 0.12 0.12 0.04-0.10 0.04-0.10 0.04-0.10 0.04-0.10 0.04 0.04 0.04
1.50 2.00 2.00 2.00 2.00 2.00 5.00-7.00 5.00-7.00 5.0-7.0 5.0-7.0 5.00-7.00 2.00-4.00 2.00-4.00 2.00-4.0 2.00-4.00 2.00-4.00 2.00-4.00 2.00-4.0 2.0-4.0 2.00-4.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
0.30-0.60 0.75 0.25 0.25 0.25 0.25 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.70 1.00 0.50 0.50 0.50 0.50 0.50 1.00 1.00 1.00 1.00 1.00 0.75 0.75 1.00 0.75 0.75 0.75 0.75
0.035 0.035 0.025 0.025 0.025 0.025 0.030 0.030 0.030 0.030 0.030 0.035 0.035 0.030 0.035 0.030 0.030 0.030 0.030 0.030 0.045 0.035 0.035 0.035 0.035 0.045 0.045 0.045 0.045 0.035 0.035 0.035
0.015 0.015 0.010 0.010 0.010 0.010 0.010 0.010 0.015 0.010 0.010 0.020 0.020 0.010 0.020 0.005 0.005 0.005 0.005 0.005 0.015 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.015 0.015 0.015
15.0-17.0 16.0-18.0 24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0 23.0-25.0 23.0-25.0 24.0-26.0 24.0-26.0 23.00-25.00 23.0-25.0 23.0-25.0 23.0-25.0 23.00-25.00 24.0-25.0 24.0-25.0 23.0-25.0 23.0-25.0 24.00-25.00 17.00-19.00 17.00-19.00 17.00-19.00 17.00-19.00 17.00-19.00 17.0-19.0 17.0-19.0 17.0-19.0 17.00-19.00 16.0-18.0 16.0-18.0 16.0-18.0
12.0-14.0 12.0-14.0 20.0-22.0 20.0-22.0 20.0-22.0 20.0-22.0 16.0-18.0 16.0-18.0 16.0-19.0 16.0-19.0 16.00-18.00 21.0-24.0 21.0-24.0 21.0-23.0 21.00-24.00 21.0-23.0 21.0-23.0 21.0-23.0 21.0-23.0 21.00-23.00 9.00-12.00 8.00-11.00 8.00-11.00 8.00-11.00 8.00-11.00 9.0-13.0 9.0-13.0 9.0-12.0 9.00-13.00 12.0-14.0 12.0-14.0 12.0-14.0
--2.00-2.50 0.20 0.20 0.20 0.20 4.0-5.0 4.0-5.0 4.0-5.0 4.0-5.0 4.00-5.00 5.2-6.2 5.2-6.2 5.5-6.5 5.00-7.00 7.0-8.0 7.0-8.0 7.0-8.0 7.0-8.0 7.00-8.00 ------------------2.00-3.00 2.00-3.00 2.00-3.00
Others Cu 2.00-3.5; N 0.10-0.30 Cu 2.00-3.5; N 0.15-0.30 B 0.001-0.01; N 0.18-0.25; (Ce+La) 0.025-0.070 B 0.001-0.010; N 0.18-0.25; (Ce+La) 0.025-0.070 Nb 10xC to 1.20 B 0.0015-0.0060; Ti 5xC to 0.80 N 0.10 N 0.10 N 0.11 N 0.11 Cb 0.10; N 0.40-0.60 Cb 0.10; N 0.40-0.60 Nb 0.15; N 0.30-0.60 Nb 0.15; N 0.30-0.60 Cb 0.10; N 0.40-0.60 Cu 1.00-2.50; W 1.50-2.50; N 0.35-0.60 Cu 1.00-2.50; W 1.50-2.50; N 0.35-0.60 Cu 1.00-2.00; W 1.50-2.50; N 0.35-0.50 Cu 0.50-3.00; W 1.00-3.00; N 0.35-0.60 Cu 0.30-0.60; N 0.45-0.55 Cu 0.30-0.60; N 0.45-0.55 Cu 0.30-0.60; N 0.45-0.55 Cu 0.30- 0.60; N 0.45-0.55 Cu 0.30-0.60; N 0.45-0.55 Ti 5xC to 0.80 Ti 5x(C-0.02) to 0.80 Ti 5x(C-0.02) to 0.80 Ti 5x(C-0.02) to 0.80 Ti 5x(C-0.02) to 0.80 Cb 8xC to 1.00 Cb 8xC to 1.00 Nb 10xC to 1.20 Cb 8xC to 1.00 N 0.10-0.18; B 0.0015-0.0050 N 0.10-0.18; B 0.0015-0.0050 N 0.10-0.18; B 0.0015-0.0050
Download From http://bbs.infoeach.com
Designation X8CrMnCuN17-8-3 X8CrMnCuN17-8-3 ---
Download From http://bbs.infoeach.com
Specification EN 10088-2:2014 ISO 16143-1:2004 ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
471
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued) UNS No -------
Steel No C 1.4961 0.04-0.10 --0.04-0.10 --0.08
JIS G 4312:2011
Symbol SUH660
---
EN 10302:2008
X6NiCrTiMoVB25-15-2
---
1.4980 0.030-0.08 1.00-2.00
1.00
EN 10028-7:2007
X5NiCrAlTi31-20
---
1.4958 0.03-0.08
1.50
0.70
EN 10302:2008
X5NiCrAlTi31-20
---
1.4958 0.030-0.08
1.50
0.70
ISO 9328-7:2004
Grade X5NiCrAlTi31-20
---
0.03-0.08
1.50
0.70
EN 10302:2008
X12CrCoNi21-20
---
1.4971 0.08-0.16
2.00
1.00
JIS G 4312:2011
Symbol SUH661
---
---
0.08-0.16
1.00-2.00
1.00
ASME SA-240/SA-240M
Type 800
N08800
---
0.10
1.50
1.00
ASTM A240/A240M-15a
Type 800
N08800
---
0.10
1.50
1.00
EN 10095:1999 SAE J405 JUN98 ASME SA-240/SA-240M
X10NiCrAlTi32-21 --Type 800H
--1.4876 0.12 N08800 --0.10 N08810 --0.05-0.10
2.00 1.50 1.50
1.00 1.00 1.00
---
N08811
---
0.06-0.10
1.50
1.00
Type 800H
N08810
---
0.05-0.10
1.50
1.00
---
N08811
---
0.06-0.10
1.50
1.00
1.4959 0.05-0.10
1.50
0.70
ASTM A240/A240M-15a
---
---
0.08
Mn 1.50 1.50 2.00
Si 0.30-0.60 0.30-0.60 1.00
2.00
1.00
EN 10028-7:2007
X8NiCrAlTi32-21
---
ISO 4955:2005 ISO 9328-7:2004
X8NiCrAlTi32-21 Grade X8NiCrAlTi32-21
-----
-----
0.05-0.10 0.05-0.10
1.50 1.50
1.00 0.70
SAE J405 JUN98
---
N08810
---
0.05-0.10
1.50
1.00
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo Others 0.015 15.0-17.0 12.0-14.0 --Nb 10xC to 1.20 0.050 15.0-17.0 12.0-14.0 --Nb 10xC to 1.20 0.030 13.00-16.00 24.00-27.00 1.00-1.50 V 0.10-0.50; Al 0.35 min.; Ti 1.90-2.35; B 0.001-0.010 0.040 0.030 13.50-16.00 24.00-27.00 1.00-1.50 V 0.10-0.50; Al 0.35; Ti 1.90-2.35; B 0.001-0.010 0.025 0.015 13.5-16.0 24.0-27.0 1.00-1.50 V 0.10-0.50; Al 0.35; Ti 1.90-2.30; B 0.0030-0.010 0.015 0.010 19.0-22.0 30.0-32.5 --(Al+Ti) 0.70 max.; (Ni+Co) 30.0 to 32.5; Al 0.20-0.50; Cu 0.50; Ti 0.20-0.50; Co 0.50; Nb 0.10; N 0.030 0.015 0.010 19.0-22.0 30.0-32.5 --Al 0.20-0.50; Cu 0.50; Ti 0.20-0.50; Nb 0.10 0.015 0.010 19.0-22.0 30.0-32.5 --(Al+Ti) 0.70 max.; (Ni+Co) 30.0 to 32.5; Al 0.20-0.50; Cu 0.50; Ti 0.20-0.50; Co 1.00; Nb 0.10; N 0.11 0.035 0.015 20.0-22.5 19.0-21.0 2.50-3.5 W 2.00-3.00; Co 18.5-21.0; Nb 0.75-1.25; N 0.10-0.20 0.040 0.030 20.00-22.50 19.00-21.00 2.50-3.50 W 2.00-3.00; Co 18.50-21.00; Nb 0.75-1.25; N 0.10-0.20 0.045 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min. 0.045 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min 0.030 0.015 19.00-23.00 30.00-34.00 --Al 0.15-0.60; Ti 0.15-0.60 0.045 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60 0.045 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min. 0.040 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min.; (Al+Ti) 0.85-1.20 0.045 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min. 0.040 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60; Fe 39.5 min.; (Al+Ti) 0.85-1.20 0.015 0.010 19.0-22.0 30.0-34.0 --(Ni+Co) 30.0 to 34.0; Al 0.25-0.65; Cu 0.50; Ti 0.25-0.65; Co 0.50; N 0.030 0.015 0.015 19.0-23.0 30.0-34.0 --Al 0.15-0.60; Cu 0.70; Ti 0.15-0.60 0.015 0.010 19.0-22.0 30.0-34.0 --(Ni+Co) 30.0 to 34.0; Al 0.25-0.65; Cu 0.50; Ti 0.25-0.65; Co 1.00; N 0.11 0.045 0.015 19.0-23.0 30.0-35.0 --Al 0.15-0.60; Cu 0.75; Ti 0.15-0.60 P 0.035 0.035 0.035
Download From http://bbs.infoeach.com
Designation X8CrNiNb16-13 Grade X8CrNiNb16-13 Grade 0Cr15Ni25Ti2MoAlVB
Download From http://bbs.infoeach.com
Specification EN 10028-7:2007 ISO 9328-7:2004 GB 4238-92
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
472
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.3A Chemical Composition of Austenitic Stainless Steels (Continued)
Specification EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 ASME SA-240/SA-240M
ASTM B688-96 (2014) EN 10028-7:2007 EN 10088-2:2014 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004
UNS No ------N08367 N08926 S31277 N08367 N08926 S31277 N08366 N08367 ----------N08367 N08926 N08904 N08904 ------------N08904 ---------
Steel No 1.4537 1.4537 ------------------1.4529 1.4529 --------------1.4539 1.4539 ----------1.4563 1.4563 -----
C 0.020 0.020 0.020 0.030 0.020 0.020 0.030 0.020 0.020 0.035 0.030 0.020 0.020 0.020 0.030 0.030 0.030 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020 0.020
Mn 2.00 2.00 2.00 2.00 2.00 3.00 2.00 2.00 3.00 2.00 2.00 1.00 1.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00
Si 0.70 0.70 0.70 1.00 0.50 0.50 1.00 0.50 0.50 1.00 1.00 0.50 0.50 0.75 1.00 1.00 1.00 0.50 1.00 1.00 0.70 0.70 0.75 0.70 1.00 1.00 1.00 0.70 0.70 0.70 0.70
P 0.030 0.030 0.030 0.040 0.030 0.030 0.040 0.030 0.030 0.040 0.040 0.030 0.030 0.030 0.045 0.045 0.040 0.030 0.045 0.045 0.030 0.030 0.035 0.030 0.045 0.045 0.045 0.030 0.030 0.030 0.030
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.010 24.0-26.0 24.0-27.0 4.7-5.7 0.010 24.0-26.0 24.0-27.0 4.7-5.7 0.010 24.0-26.0 24.0-27.0 4.7-5.7 0.030 20.0-22.0 23.5-25.5 6.0-7.0 0.010 19.0-21.0 24.0-26.0 6.00-7.00 0.010 20.5-23.0 26.0-28.0 6.5-8.0 0.030 20.0-22.0 23.5-25.5 6.0-7.0 0.010 19.0-21.0 24.0-26.0 6.00-7.00 0.010 20.5-23.0 26.0-28.0 6.5-8.0 0.030 20.00-22.00 23.50-25.50 6.00-7.00 0.030 20.00-22.00 23.50-25.50 6.00-7.00 0.010 19.0-21.0 24.0-26.0 6.0-7.0 0.010 19.0-21.0 24.0-26.0 6.0-7.0 0.010 19.0-21.0 24.0-26.0 6.0-7.0 0.030 19.00-24.00 24.00-26.00 5.00-7.00 0.030 19.00-24.00 24.00-26.00 5.00-7.00 0.030 20.00-22.00 23.50-25.50 6.00-7.00 0.010 19.00-21.00 24.00-26.00 6.0-7.0 0.035 19.0-23.0 23.0-28.0 4.00-5.00 0.035 19.0-23.0 23.0-28.0 4.00-5.00 0.010 19.0-21.0 24.0-26.0 4.0-5.0 0.010 19.0-21.0 24.0-26.0 4.0-5.0 0.015 19.0-22.0 23.5-26.0 4.0-5.0 0.010 19.0-21.0 24.0-26.0 4.0-5.0 0.030 19.00-23.00 23.00-28.00 4.00-5.00 0.030 19.00-23.00 23.00-28.00 4.00-5.00 0.035 19.00-23.00 23.00-28.00 4.0-5.0 0.010 26.0-28.0 30.0-32.0 3.0-4.0 0.010 26.0-28.0 30.0-32.0 3.0-4.0 0.010 26.0-28.0 30.0-32.0 3.0-4.0 0.010 26.0-28.0 30.0-32.0 3.00-4.0
Others Cu 1.00-2.00; N 0.17-0.25 Cu 1.00-2.00; N 0.17-0.25 Cu 1.00-2.00; N 0.17-0.25 Cu 0.75; N 0.18-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.30-0.40 Cu 0.75; N 0.18-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.30-0.40 --Cu 0.75; N 0.18-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.15-0.25 Cu 0.50-1.50; N 0.15-0.25 N 0.25 N 0.25 Cu 0.75; N 0.18-0.25 Cu 0.5-1.5; N 0.15-0.25 Cu 1.00-2.00; N 0.10 Cu 1.00-2.00; N 0.10 Cu 1.20-2.00; N 0.15 Cu 1.20-2.00; N 0.15 Cu 1.20-2.00; N 0.15 Cu 1.20-2.00; N 0.15 Cu 1.00-2.00 Cu 1.00-2.00 Cu 1.0-2.0; N 0.10 Cu 0.70-1.50; N 0.10 Cu 0.70-1.50; N 0.10 Cu 0.70- 1.50; N 0.11 Cu 0.70-1.50; N 0.11
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Designation X1CrNiMoCuN25-25-5 X1CrNiMoCuN25-25-5 Grade X1CrNiMoCuN25-25-5 ----------------X1NiCrMoCuN25-20-7 X1NiCrMoCuN25-20-7 Grade X1NiCrMoCuN25-20-7 Symbol SUS836L Symbol SUS836L ----Type 904L Type 904L X1NiCrMoCu25-20-5 X1NiCrMoCu25-20-5 X1NiCrMoCu25-20-5 Grade X1NiCrMoCu25-20-5 Symbol SUS890L Symbol SUS890L Type 904L X1NiCrMoCu31-27-4 X1NiCrMoCu31-27-4 X1NiCrMoCu31-27-4 Grade X1NiCrMoCu31-27-4
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
473
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels
Specification ASME SA-240/SA-240M
ASME SA-666
ASTM A666-15
UNS Steel No No S20100 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 260 38 515 75 40
Heat Treatment Q+SA
Type 201-2
S20100
---
---
---
310
45
655
95
40
Q+SA
Type 201-1
S20100
---
---
---
260
38
515 L
75 L
40 L
A
Type 201-2
S20100
---
---
---
310
45
655 L
95 L
40 L
A
Type 201-1
S20100
---
---
---
260
38
515
75
40
SA
Type 201-2
S20100
---
---
---
310
45
655
95
40
SA
Type 201-1
S20100
---
---
---
260
38
515 L
75 L
40 L
A
Type 201-2
S20100
---
---
---
310
45
655 L
95 L
40 L
A
---------
350 330 330 245
---------
680-880 680-880 680-880 635
---------
45 T 45 T 40 T 40
SA SA SA ST
EN 10088-2:2014
X12CrMnNiN17-7-5
---
1.4372
GB 3280-92
Grade 1Cr17Mn6Ni5N
---
---
t≤8 t ≤ 13.5 t ≤ 75 ---
GB 4237-92
Grade 1Cr17Mn6Ni5N
---
---
---
---
245
---
635
---
40
ST
GB 4239-91 ISO 16143-1:2004
Grade 1Cr17Mn6Ni5N X12CrMnNiN17-7-5
-----
-----
--t≤8 t ≤ 13.5 t ≤ 75
---------
245 350 330 330
---------
635 750-950 750-950 750-950
---------
40 45 T 45 T 40 T
ST SA SA SA
Other 217 max. HB; 95 max. HRB 241 max. HB; 100 max. HRB 217 max. HB; 95 max. HRB 241 max. HB; 100 max. HRB 217 max. HBW; 95 max. HRBW 241 max. HBW; 100 max. HRBW 217 max. HB; 95 max. HRB 241 max. HB; 100 max. HRB --see standard for impact data 241 max. HB; 100 max. HRB 241 max. HB; 100 max. HRB 100 max. HRB -------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Designation Type 201-1
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
474
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S20103 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 260 38 655 95 40
Heat Treatment Q+SA
ASME SA-666
Type 201L
S20103
---
---
---
260
38
655 L
95 L
40 L
A
ASTM A240/A240M-15a
Type 201L
S20103
---
---
---
260
38
655
95
40
SA
ASTM A666-15
Type 201L
S20103
---
---
---
260
38
655 L
95 L
40 L
A
EN 10088-2:2014
X2CrMnNiN17-7-5
---
1.4371
ASME SA-240/SA-240M
Type 201LN
S20153
---
t≤8 t ≤ 13.5 t ≤ 75 ---
---------
300 280 280 310
------45
650-850 650-850 630-830 655
------95
45 T 45 T 35 T 45
SA SA SA Q+SA
ASME SA-666
Type 201LN
S20153
---
---
---
310
45
655 L
95 L
45 L
A
ASTM A240/A240M-15a
Type 201LN
S20153
---
---
---
310
45
655
95
45
SA
ASTM A666-15
Type 201LN
S20153
---
---
---
310
45
655 L
95 L
45 L
A
ASME SA-240/SA-240M ASME SA-666 ASTM A240/A240M-15a ASTM A666-15 EN 10088-2:2014
Type 202 Type 202 Type 202 Type 202 X12CrMnNiN18-9-5
S20200 --S20200 --S20200 --S20200 ----1.4373
GB 3280-92
Grade 1Cr18Mn8Ni5N
---
---
--------t≤8 t ≤ 13.5 t ≤ 75 ---
-----------------
260 260 260 260 340 320 320 245
38 38 38 38 ---------
620 620 L 620 620 L 680-880 680-880 600-800 590
90 90 L 90 90 L ---------
40 40 L 40 40 L 45 T 45 T 35 T 40
Q+SA A SA A SA SA SA ST
GB 4237-92
Grade 1Cr18Mn8Ni5N
---
---
---
---
245
---
590
---
40
ST
GB 4239-91
Grade 1Cr18Mn8Ni5N
---
---
---
---
245
---
590
---
40
ST
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB --see standard for impact data 241 max. HB; 100 max. HRB 241 max. HB; 100 max. HRB 241 max. HBW; 100 max. HRBW 241 max. HB; 100 max. HRB 241 max. HB 241 max. HB 241 max. HB 241 max. HB --see standard for impact data 207 max. HB; 95 max. HRB 207 max. HB; 95 max. HRB 95 max. HRB
Download From http://bbs.infoeach.com
Designation Type 201L
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
475
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASME SA-666
Type 301
S30100
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 301
S30100
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 301
S30100
---
---
---
205
30
515 L
75 L
40 L
A
EN 10088-2:2014
X10CrNi18-8 X5CrNi17-7
-----
1.4310 1.4319
GB 3280-92
Grade 1Cr17Ni7
---
---
t≤8 t≤3 t≤6 ---
---------
250 230 230 205
---------
600-950 550-750 550-750 520
---------
40 T 45 T 45 T 40
SA SA SA ---
--t < 0.4 t < 0.4 t < 0.4 t < 0.4 t < 0.4 0.4 < t < 0.8 t > 0.4 t ≥ 0.8 ---
---------------------
510 755 930 960 960 960 930 755 930 205
---------------------
865 1030 1210 1270 1270 1270 1210 1030 1210 570
---------------------
25 9 3 3 4 5 5 10 7 45
WH WH WH WH WH WH WH WH WH ST
----t < 0.4 t < 0.4 t < 0.4 0.4 ≤ t < 0.8 0.4 ≤ t < 0.8 t ≥ 0.4 t ≥ 0.8 t ≥ 0.8 ---
-----------------------
205 510 755 930 960 930 960 755 930 960 205
-----------------------
520 865 1030 1205 1275 1205 1275 1030 1205 1275 570
-----------------------
40 25 9 3 3 5 4 10 7 5 45
ST WH WH WH WH WH WH WH WH WH ST
Designation
Grade 1Cr17Ni8
---
---
Grade 1Cr17Ni7
---
---
Grade 1Cr17Ni8 Note: This section continued on next page
---
---
GB 4239-91
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 40
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB ------187 max. HB; 90 max. HRB ------------------187 max. HB; 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB
Download From http://bbs.infoeach.com
Type 301
UNS Steel No No S30100 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
476
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
Symbol SUS301
---
---
Symbol SUS301J1
---
---
---
---
205
---
570
---
45
ST
Symbol SUS301
---
---
---
---
205
---
520
---
40
ST
---
---
t < 0.4 t < 0.4 t < 0.4 t < 0.4 0.4 ≤ t < 0.8 0.4 ≤ t < 0.8 0.4 ≤ t < 0.8 0.4 ≤ t < 0.8 t ≥ 0.8 t ≥ 0.8 t ≥ 0.8 t ≥ 0.8 ---
---------------------------
510 755 930 960 510 755 930 960 510 755 930 960 205
---------------------------
860 1030 1210 1270 860 1030 1210 1270 860 1030 1210 1270 570
---------------------------
25 9 3 3 25 10 5 4 25 10 7 5 45
T T T T T T T T T T T T ST
Designation X10CrNi18-8
JIS G 4304:2012
Download From http://bbs.infoeach.com
JIS G 4305:2012
Symbol SUS301J1
Section Thickness/Diameter mm in. t≤8 --t ≤ 13.5 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 250 --600-800 --40 T 230 --600-800 --40 T 205 --520 --40
Heat Treatment SA SA ST
ASME SA-240/SA-240M
Type 301L
S30103
---
---
---
220
32
550
80
45
Q+SA
ASME SA-666
Type 301L
S30103
---
---
---
220
32
550 L
80 L
45 L
A
ASTM A240/A240M-15a
Type 301L
S30103
---
---
---
220
32
550
80
45
SA
ASTM A666-15
Type 301L
S30103
---
---
---
220
32
550 L
80 L
45 L
A
JIS G 4304:2012
Symbol SUS301L
---
---
---
---
215
---
550
---
45
ST
Other ----207 max. HBW; 95 max. HRBW; 218 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 207 max. HBW; 95 max. HRBW; 218 max. HV ------------------------187 max. HBW; 90 max. HRBW; 200 max. HV 241 max. HB; 100 max. HRB 241 max. HB; 100 max. HRB 241 max. HBW; 100 max. HRBW 241 max. HB; 100 max. HRB 207 max. HBW; 95 max. HRBW; 218 max. HV
Download From http://bbs.infoeach.com
UNS No ---
Specification ISO 16143-1:2004
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
477
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification JIS G 4305:2012
Designation Symbol SUS301L
UNS No ---
Steel No ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 215 --550 --45
Heat Treatment ST
-----------
345 410 480 685 240
--------35
690 760 820 930 550
--------80
40 35 25 20 45
T T T T Q+SA
S30153
---
ASME SA-666
Type 301LN
S30153
---
---
---
240
35
550 L
80 L
45 L
A
ASTM A240/A240M-15a
Type 301LN
S30153
---
---
---
240
35
550
80
45
SA
ASTM A666-15
Type 301LN
S30153
---
---
---
240
35
550 L
80 L
45 L
A
EN 10028-7:2007
X2CrNiN18-7
---
1.4318
EN 10088-2:2014
X2CrNiN18-7
---
1.4318
ISO 9328-7:2004
Grade X2CrNiN18-7
---
---
ASME SA-240/SA-240M
Type 302
S30200
---
t≤3 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-----------------------
350 350 330 330 350 330 330 350 330 330 205
--------------------30
650-850 650-850 650-850 650-850 650-850 650-850 630-830 650-850 650-850 650-850 515
--------------------75
35 T 40 T 40 T 40 T 40 T 40 T 45 T 40 T 40 T 40 T 40
SA SA SA SA SA SA SA SA SA SA Q+SA
ASME SA-666
Type 302
S30200
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 302
S30200
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 302
S30200
---
---
---
205
30
515 L
75 L
40 L
A
JIS G 4304:2012
Symbol SUS303
---
---
---
---
205
---
520
---
35
ST
--see standard for impact data --see standard for impact data 201 max. HB; 92 max. HRB 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW 201 max. HB; 92 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Type 301LN
Download From http://bbs.infoeach.com
ASME SA-240/SA-240M
-----------
Other 207 max. HBW; 95 max. HRBW; 218 max. HV --------241 max. HB; 100 max. HRB 241 max. HB; 100 max. HRB 241 max. HBW; 100 max. HRBW 241 max. HB; 100 max. HRB see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
478
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
Grade 1Cr18Ni9Si3
---
---
---
---
205
---
502
---
40
ST
GB 4238-92
Grade 1Cr18Ni9Si3
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 JIS G 4304:2012
Grade 1Cr18Ni9Si3 Symbol SUS302B
-----
-----
-----
-----
205 205
-----
520 520
-----
40 40
ST ST
JIS G 4305:2012
Symbol SUS302B
---
---
---
---
205
---
520
---
40
ST
ASME SA-240/SA-240M
Type 304
S30400
---
---
---
205
30
515
75
40
Q+SA
ASME SA-666
Type 304
S30400
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 304
S30400
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 304
S30400
---
---
---
205
30
515 L
75 L
40 L
A
EN 10028-7:2007
X5CrNi18-10
---
1.4301
EN 10088-2:2014
X5CrNi18-10
---
1.4301
GB 3280-92
Grade 0Cr18Ni9
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
230 210 210 230 210 210 205
---------------
540-750 520-720 520-720 540-750 520-720 520-720 520
---------------
45 T 45 T 45 T 45 T 45 T 45 T 40
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni9
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr18Ni9
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 ISO 16143-1:2004
Grade 0Cr18Ni9 X5CrNi18-9
-----
-----
ISO 9328-7:2004
Grade X5CrNi18-9
---
---
--t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
---------------
205 230 210 210 230 210 210
---------------
520 540-740 540-740 520-720 540-750 520-720 520-720
---------------
40 45 T 45 T 45 T 45 T 45 T 45 T
ST SA SA SA SA SA SA
Designation Grade 1Cr18Ni9Si3
GB 4237-92
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 --520 --40
Heat Treatment ST
Download From http://bbs.infoeach.com
Other 207 max. HB; 95 max. HRB 207 max. HB; 95 max. HRB 207 max. HB; 95 max. HRB 95 max. HRB 207 max. HBW; 95 max. HRBW; 218 max. HV 207 max. HBW; 95 max. HRBW; 218 max. HV 201 max. HB; 92 max. HRB 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW 201 max. HB; 92 max. HRB see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB --------see standard for impact data
Download From http://bbs.infoeach.com
UNS No ---
Specification GB 3280-92
Note: This section continued on next page Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
479
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
Symbol SUS304
---
---
---
---
205
---
520
---
40
ST
X6CrNiCu17-8-2
---
---
JIS G 4304:2012
Symbol SUS304J1
---
---
t≤8 t ≤ 13.5 t ≤ 75 ---
---------
155 155 155 155
---------
450 450 450 450
---------
40 T 40 T 40 T 40
SA SA SA ST
JIS G 4305:2012
Symbol SUS304J1
---
---
---
---
155
---
450
---
40
ST
ASME SA-240/SA-240M
Type 304L
S30403
---
---
---
170
25
485
70
40
Q+SA
ASME SA-666
Type 304L
S30403
---
---
---
170
25
485 L
70 L
40 L
A
ASTM A240/A240M-15a
Type 304L
S30403
---
---
---
170
25
485
70
40
SA
ASTM A666-15
Type 304L
S30403
---
---
---
170
25
485 L
70 L
40 L
A
EN 10028-7:2007
X2CrNi19-11
---
1.4306
X2CrNi18-9
---
1.4307
X2CrNi19-11
---
1.4306
X2CrNi18-9
---
1.4307
Grade 00Cr19Ni10
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------------------
220 200 200 220 200 200 220 200 200 220 200 200 177
---------------------------
520-670 520-670 500-650 520-670 520-670 500-650 520-700 520-700 500-700 520-700 520-700 500-700 480
---------------------------
45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 40
SA SA SA SA SA SA SA SA SA SA SA SA ST
Grade 00Cr19Ni13Mo3
---
---
---
---
177
---
480
---
40
ST
Designation Symbol SUS304
JIS G 4305:2012
ISO 16143-1:2004
Download From http://bbs.infoeach.com
EN 10088-2:2014
GB 3280-92
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 --520 --40
Heat Treatment ST
Other 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV ------187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 201 max. HB; 92 max. HRB 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW 201 max. HB; 92 max. HRB see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
UNS No ---
Specification JIS G 4304:2012
--see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
480
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
Grade 00Cr19Ni10 X2CrNi18-9
-----
-----
X2CrNi19-11
---
---
Grade X2CrNi18-9
---
---
Grade X2CrNi19-11
---
---
JIS G 4304:2012
Symbol SUS304L
---
JIS G 4305:2012
Symbol SUS304L
ASME SA-240/SA-240M
Designation Grade 00Cr19Ni10
GB 4239-91 ISO 16143-1:2004
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 177 --480 --40
Heat Treatment ST
-------------------------------
175 220 175 200 200 220 200 200 220 200 200 220 200 200 175
-------------------------------
480 520-720 480-680 520-720 500-700 520-720 520-720 500-700 520-670 520-670 500-650 520-670 520-670 500-650 480
-------------------------------
40 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 45 T 40
ST SA SA SA SA SA SA SA SA SA SA SA SA SA ST
---
---
---
---
175
---
480
---
40
ST
Type 304H
S30409
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 304H
S30409
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNi18-10
---
1.4948
ISO 9328-7:2004
Grade X6CrNi18-10
---
---
ISO 4955:2005
X7CrNi18-9
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160
-----------------------
230 210 190 230 210 190 195 195 195 195 195
-----------------------
530-740 510-710 510-710 530-740 510-710 510-710 500-700 500-700 500-700 500-700 500-700
-----------------------
45 T 45 T 45 T 45 T 45 T 45 T 37 L, 37 T 40 40 L, 40 T 40 40
SA SA SA SA SA SA SA SA SA SA SA
Download From http://bbs.infoeach.com
---
--t≤8 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
ISO 9328-7:2004
Other 187 min. HB; 90 max. HRB 90 max. HRB ----------------see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW see standard for impact data
Download From http://bbs.infoeach.com
UNS No ---
Specification GB 4237-92
--see standard for impact data 192 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
481
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S30451 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 240 35 550 80 30
Heat Treatment Q+SA
ASME SA-666
Type 304N
S30451
---
---
---
240
35
550 L
80 L
30 L
A
ASTM A240/A240M-15a
Type 304N
S30451
---
---
---
240
35
550
80
30
SA
ASTM A666-15
Type 304N
S30451
---
---
---
240
35
550 L
80 L
30 L
A
EN 10028-7:2007
X5CrNiN19-9
---
1.4315
EN 10088-2:2014
X5CrNiN19-9
---
1.4315
GB 3280-92
Grade 0Cr19Ni9N
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
290 270 270 290 270 270 275
---------------
550-750 550-750 550-750 500-750 500-750 500-750 550
---------------
40 T 40 T 40 T 40 T 40 T 40 T 35
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr19Ni9N
---
---
---
---
275
---
550
---
35
ST
GB 4239-91 ISO 9328-7:2004
Grade 0Cr19Ni9N Grade X5CrNiN18-8
-----
-----
JIS G 4304:2012
Symbol SUS304N1
---
---
--t≤6 t ≤ 12 t ≤ 75 ---
-----------
275 290 270 270 275
-----------
550 550-750 550-750 550-750 550
-----------
35 40 T 40 T 40 T 35
ST SA SA SA ST
JIS G 4305:2012
Symbol SUS304N1
---
---
---
---
275
---
550
---
35
ST
GB 3280-92
Grade 0Cr19Ni10NbN
---
---
---
---
345
---
685
---
35
ST
GB 4237-92
Grade 0Cr19Ni10NbN
---
---
---
---
345
---
685
---
35
ST
GB 4239-91 JIS G 4304:2012
Grade 0Cr19Ni10NbN Symbol SUS304N2
-----
-----
-----
-----
345 345
-----
685 690
-----
35 35
ST ST
JIS G 4305:2012
Symbol SUS304N2-X Symbol SUS304N2
-----
-----
-----
-----
450 345
-----
720 690
-----
25 35
ST ST
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data see standard for impact data 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 95 max. HRB --see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV 250 max. HB; 100 max. HRB 250 max. HB; 100 max. HRB 100 max. HRB 248 max. HBW; 100 max. HRBW; 260 max. HV 230-325 HBW 248 max. HBW; 100 max. HRBW; 260 max. HV
Download From http://bbs.infoeach.com
Designation Type 304N
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
482
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S30453 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 40
Heat Treatment Q+SA
ASME SA-666
Type 304LN
S30453
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 304LN
S30453
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 304LN
S30453
---
---
---
205
30
515 L
75 L
40 L
A
EN 10028-7:2007
X2CrNiN18-10
---
1.4311
EN 10088-2:2014
X2CrNiN18-10
---
1.4311
GB 3280-92
Grade 00Cr18Ni10N
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
290 270 270 290 270 270 245
---------------
550-750 550-750 550-750 550-750 550-750 550-750 550
---------------
40 T 40 T 40 T 40 T 40 T 40 T 40
SA SA SA SA SA SA ST
GB 4237-92
Grade 00Cr18Ni10N
---
---
---
---
245
---
550
---
40
ST
GB 4239-91 ISO 16143-1:2004
Grade 00Cr18Ni10N X2CrNiN18-9
-----
-----
ISO 9328-7:2004
Grade X2CrNiN18-10
---
---
JIS G 4304:2012
Symbol SUS304LN
---
---
--t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-----------------
245 290 270 270 290 270 270 245
-----------------
550 550-750 550-750 530-730 550-750 550-750 550-750 550
-----------------
40 40 T 40 T 40 T 40 T 40 T 40 T 40
ST SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS304LN
---
---
---
---
245
---
550
---
40
ST
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data --see standard for impact data 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 95 max. HRB --------see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Download From http://bbs.infoeach.com
Designation Type 304LN
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
483
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASTM A240/A240M-15a
Type 305
S30500
---
---
---
170
25
485
70
40
SA
EN 10088-2:2014 GB 3280-92
X4CrNi18-12 Grade 1Cr18Ni12
-----
1.4303 ---
t≤8 ---
-----
220 177
-----
500-650 480
-----
45 T 40
SA ST
GB 4237-92
Grade 1Cr18Ni12
---
---
---
---
177
---
480
---
40
ST
GB 4239-91 JIS G 4304:2012
Grade 1Cr18Ni12 Symbol SUS305
-----
-----
-----
-----
175 175
-----
480 480
-----
40 40
ST ST
JIS G 4305:2012
Symbol SUS305
---
---
---
---
175
---
480
---
40
ST
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014
----X1CrNiSi18-15-4
----t ≤ 75
-------
240 240 220
35 35 ---
540 540 530-730
78 78 ---
40 40 40 T
Q+SA SA SA
GB 4238-92
Grade 2Cr23Ni13
---
---
---
---
205
---
560
---
40
ST
JIS G 4312:2011
Symbol SUH309
---
---
---
---
205
---
560
---
40
ST
Designation
S30600 --S30600 ----1.4361
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 170 25 485 70 40
Heat Treatment Q+SA
Other 183 max. HB; 88 max. HRB 183 max. HBW; 88 max. HRBW --187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV ----see standard for impact data 201 max. HB; 95 max. HRB 201 max. HBW; 95 max. HRBW; 210 max. HV
Download From http://bbs.infoeach.com
Type 305
UNS Steel No No S30500 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
484
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S30908 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 40
Heat Treatment Q+SA
ASTM A240/A240M-15a
Type 309S
S30908
---
---
---
205
30
515
75
40
SA
EN 10095:1999
X12CrNi23-13
---
1.4833
GB 3280-92
Grade 0Cr23Ni13
---
---
0.5 ≤ t < 3 t ≤ 25 3 ≤ t ≤ 75 t ≤ 160 ---
-----------
210 210 210 210 205
-----------
500-700 500-700 L 500-700 500-700 L 520
-----------
33 L, 33 T 35 L 35 L, 35 T 35 L 40
SA SA SA SA ST
GB 4237-92
Grade 0Cr23Ni13
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr23Ni13
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 ISO 4955:2005
Grade 0Cr23Ni13 X12CrNi23-13
-----
-----
JIS G 4304:2012
Symbol SUS309S
---
---
--0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160 ---
---------------
205 210 210 210 210 210 205
---------------
520 ----------520
---------------
40 33 L, 33 T 35 35 L, 35 T 35 35 40
ST SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS309S
---
---
---
---
205
---
520
---
40
ST
ASME SA-240/SA-240M
Type 309H
S30909
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 309H
S30909
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNi23-13
---
1.4950
ISO 9328-7:2004
Grade X6CrNi23-13
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
-------------
220 200 200 220 200 200
-------------
530-730 510-710 510-710 530-730 510-710 510-710
-------------
35 T 35 T 35 T 35 T 35 T 35 T
SA SA SA SA SA SA
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 192 max. HB 192 max. HB 192 max. HB 192 max. HB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 192 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 309S
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
--see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
485
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No -----
Symbol SUH310
---
---
---
---
205
---
590
---
35
ST
EN 10095:1999
X15CrNiSi25-21
---
1.4841
ASME SA-240/SA-240M
Type 310S
S31008
---
0.5 ≤ t < 3 t ≤ 25 3 ≤ t ≤ 75 t ≤ 160 ---
-----------
230 230 230 230 205
--------30
550-750 550-750 L 550-750 550-750 L 515
--------75
28 L, 28 T 30 L 30 L, 30 T 30 L 40
SA SA SA SA Q+SA
ASTM A240/A240M-15a
Type 310S
S31008
---
---
---
205
30
515
75
40
SA
EN 10095:1999
X8CrNi25-21
---
1.4845
GB 3280-92
Grade 0Cr25Ni20
---
---
0.5 ≤ t < 3 t ≤ 25 3 ≤ t ≤ 75 t ≤ 160 ---
-----------
210 210 210 210 205
-----------
500-700 500-700 L 500-700 500-700 L 520
-----------
33 L, 33 T 35 L 35 L, 35 T 35 L 40
SA SA SA SA ST
GB 4237-92
Grade 0Cr25Ni20
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr25Ni20
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 ISO 4955:2005
Grade 0Cr25Ni20 X8CrNi25-21
-----
-----
JIS G 4304:2012
Symbol SUS310S
---
---
--0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160 ---
---------------
205 210 210 210 210 210 205
---------------
520 ----------520
---------------
40 33 L, 33 T 35 35 L, 35 T 35 35 40
ST SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS310S
---
---
---
---
205
---
520
---
40
ST
Designation Grade 1Cr25Ni20Si2 Grade 2Cr25Ni20
JIS G 4312:2011
Section Thickness/Diameter mm in. ---------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min ----540 --35 205 --590 --35
Heat Treatment ST ST
Download From http://bbs.infoeach.com
Other --201 max. HB; 95 max. HRB 201 max. HBW; 95 max. HRBW; 210 max. HV 223 max. HB 223 max. HB 223 max. HB 223 max. HB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 192 max. HB 192 max. HB 192 max. HB 192 max. HB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 192 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
UNS No -----
Specification GB 4238-92
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
486
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S31009 ---
ASTM A240/A240M-15a
Type 310H
S31009
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNi25-20
---
1.4951
ISO 9328-7:2004
Grade X6CrNi25-20
---
---
ASME SA-240/SA-240M
Type 310 MoLN
S31050
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
------------t ≤ 0.25
220 200 200 220 200 200 270
------------39
530-730 510-710 510-710 530-730 510-710 510-710 580
------------84
35 T 35 T 35 T 35 T 35 T 35 T 25
SA SA SA SA SA SA Q+SA
---
t > 0.25
255
37
540
78
25
Q+SA
---
t ≤ 0.25
270
39
580
84
25
SA
---
t > 0.25
255
37
540
78
25
SA
ASTM A240/A240M-15a
Type 310 MoLN
S31050
---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 40
Heat Treatment Q+SA
EN 10028-7:2007
X1CrNiMoN25-22-2
---
1.4466
t ≤ 75
---
250
---
540-740
---
40 T
SA
EN 10088-2:2014
X1CrNiMoN25-22-2
---
1.4466
t ≤ 75
---
250
---
540-740
---
40 T
SA
ISO 16143-1:2004 ISO 9328-7:2004
X1CrNiMoN25-22-2 Grade X1CrNiMoN25-22-2
-----
-----
t ≤ 75 t ≤ 75
-----
250 250
-----
540-740 540-740
-----
40 T 40 T
SA SA
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data --see standard for impact data 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HBW; 95 max. HRBW see standard for impact data see standard for impact data --see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 310H
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
487
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M
ASTM A240/A240M-15a
Designation ---
---
UNS Steel No No S31254 ---
S31254
---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 310 45 690 100 35
Heat Treatment Q+SA
---
310
45
655
95
35
Q+SA
---
---
310
45
690
100
35
SA
---
---
310
45
655
95
35
SA
---------------------
320 300 300 320 300 300 320 300 300 300
---------------------
650-850 650-850 650-850 650-850 650-850 650-850 650-850 650-850 650-850 650
---------------------
35 T 35 T 40 T 35 T 35 T 40 T 35 T 35 T 40 T 35
SA SA SA SA SA SA SA SA SA ST
EN 10028-7:2007
X1CrNiMoCuN20-18-7
---
1.4547
EN 10088-2:2014
X1CrNiMoCuN20-18-7
---
1.4547
ISO 9328-7:2004
Grade X1CrNiMoCuN20-18-7
---
---
JIS G 4304:2012
Symbol SUS312L
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
JIS G 4305:2012
Symbol SUS312L
---
---
---
---
300
---
650
---
35
ST
ASME SA-240/SA-240M
Type 316
S31600
---
---
---
205
30
515
75
40
Q+SA
ASME SA-666
Type 316
S31600
---
---
---
205
30
515 L
75 L
40 L
A
ASTM A240/A240M-15a
Type 316
S31600
---
---
---
205
30
515
75
40
SA
ASTM A666-15
Type 316
S31600
---
---
---
205
30
515 L
75 L
40 L
A
EN 10028-7:2007
X5CrNiMo17-12-2
---
1.4401
X3CrNiMo17-13-3
---
1.4436
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75
-------------
240 220 220 240 220 220
-------------
530-680 530-680 520-670 550-700 550-700 530-730
-------------
40 T 40 T 45 T 40 T 40 T 40 T
SA SA SA SA SA SA
--see standard for impact data --see standard for impact data 223 max. HBW; 96 max. HRBW; 230 max. HV 223 max. HBW; 96 max. HRBW; 230 max. HV 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
---
Other 223 max. HB; 96 max. HRB 223 max. HB; 96 max. HRB 223 max. HBW; 96 max. HRBW 223 max. HBW; 96 max. HRBW see standard for impact data
see standard for impact data
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
488
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4401
X3CrNiMo17-13-3
---
1.4436
GB 3280-92
Grade 0Cr17Ni12Mo2
---
---
GB 4237-92
Grade 0Cr17Ni12Mo2
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr17Ni12Mo2
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 ISO 16143-1:2004
Grade 0Cr17Ni12Mo2 X5CrNiMo17-12-2
-----
-----
X3CrNiMo17-12-3
---
---
Grade X3CrNiMo17-12-3
---
---
Grade X5CrNiMo17-12-2
---
---
JIS G 4304:2012
Symbol SUS316
---
---
--t≤8 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-------------------------------
205 240 205 220 220 240 220 220 240 220 220 240 220 220 205
-------------------------------
520 530-730 520-720 530-730 510-710 530-730 530-730 510-710 550-700 550-700 530-730 530-680 530-680 520-670 520
-------------------------------
40 40 T 40 T 40 T 40 T 40 T 40 T 40 T 40 T 40 T 40 T 40 T 40 T 45 T 40
ST SA SA SA SA SA SA SA SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS316
---
---
---
---
205
---
520
---
40
ST
Download From http://bbs.infoeach.com
ISO 9328-7:2004
Designation X5CrNiMo17-12-2
Section Thickness/Diameter mm in. t≤8 --t ≤ 13.5 --t ≤ 75 --t≤8 --t ≤ 13.5 --t ≤ 75 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 240 --530-680 --40 T 220 --530-680 --40 T 220 --520-670 --45 T 240 --550-700 --40 T 220 --550-700 --40 T 220 --530-730 --40 T 205 --520 --40
Heat Treatment SA SA SA SA SA SA ST
Other --see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB ----------------see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
UNS No ---
Specification EN 10088-2:2014
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
489
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S31603 ---
ASME SA-666
Type 316L
S31603
---
---
---
170
25
485 L
70 L
40 L
A
ASTM A240/A240M-15a
Type 316L
S31603
---
---
---
170
25
485
70
40
SA
ASTM A666-15
Type 316L
S31603
---
---
---
170
25
485 L
70 L
40 L
A
EN 10028-7:2007
X2CrNiMo17-12-2
---
1.4404
X2CrNiMo17-12-3
---
1.4432
X2CrNiMo18-14-3
---
1.4435
X2CrNiMo17-12-2
---
1.4404
X2CrNiMo17-12-3
---
1.4432
X2CrNiMo18-14-3
---
1.4435
GB 3280-92
Grade 00Cr17Ni14Mo2
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------------------------------
240 220 220 240 220 220 240 220 220 240 220 220 240 220 220 240 220 220 177
---------------------------------------
530-680 530-680 520-670 550-700 550-700 520-670 550-700 550-700 520-670 530-680 530-680 520-670 550-700 550-700 520-670 550-700 550-700 520-670 480
---------------------------------------
40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40 T 40 T 45 T 40
SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA ST
GB 4237-92
Grade 00Cr17Ni14Mo2
---
---
---
---
177
---
480
---
40
ST
GB 4239-91 Grade 00Cr17Ni14Mo2 Note: This section continued on next page
---
---
---
---
175
---
480
---
40
ST
EN 10088-2:2014
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 170 25 485 70 40
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB see standard for impact data see standard for impact data see standard for impact data --see standard for impact data --see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB
Download From http://bbs.infoeach.com
Designation Type 316L
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
490
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
X2CrNiMo17-12-3
---
---
X2CrNiMo18-14-3
---
---
Grade X2CrNiMo17-12-2
---
---
Grade X2CrNiMo17-12-3
---
---
Grade X2CrNiMo18-14-3
---
---
JIS G 4304:2012
Symbol SUS316L
---
---
JIS G 4305:2012
Symbol SUS316L
---
---
---
---
175
---
480
---
40
ST
GB 4237-92
Grade 00Cr18Ni12Mo2Cu2
---
---
---
---
177
---
480
---
35
ST
GB 4239-91 JIS G 4304:2012
Grade 00Cr18Ni14Mo2Cu2 Symbol SUS316J1L
-----
-----
-----
-----
175 175
-----
480 480
-----
40 40
ST ST
JIS G 4305:2012
Symbol SUS316J1L
---
---
---
---
175
---
480
---
40
ST
GB 3280-92
Grade 0Cr18Ni12Mo2Cu2
---
---
---
---
205
---
520
---
40
ST
GB 4237-92
Grade 0Cr18Ni12Mo2Cu2
---
---
---
---
205
---
520
---
35
ST
GB 4239-91 Grade 0Cr18Ni12Mo2Cu2 Note: This section continued on next page
---
---
---
---
205
---
520
---
40
ST
Download From http://bbs.infoeach.com
ISO 9328-7:2004
Designation X2CrNiMo17-12-2
Section Thickness/Diameter mm in. t≤8 --t≤8 --t ≤ 13.5 --t ≤ 75 --t≤8 --t ≤ 13.5 --t ≤ 75 --t≤6 --t ≤ 12 --t ≤ 75 --t≤6 --t ≤ 12 --t ≤ 75 --t≤6 --t ≤ 12 --t ≤ 75 --t≤6 --t ≤ 12 --t ≤ 75 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 240 --530-730 --40 T 175 --480-680 --40 T 220 --530-730 --40 T 220 --510-710 --40 T 240 --530-730 --40 T 220 --530-730 --40 T 220 --510-710 --40 T 240 --550-750 --40 T 220 --550-750 --40 T 220 --520-720 --45 T 240 --530-680 --40 T 220 --530-680 --40 T 220 --520-670 --45 T 240 --550-700 --40 T 220 --550-700 --40 T 220 --520-670 --45 T 240 --550-700 --40 T 220 --550-700 --40 T 220 --520-670 --45 T 175 --480 --40
Heat Treatment SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA ST
Other ----------------------see standard for impact data --see standard for impact data --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HB; 90 max. HRB 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB
Download From http://bbs.infoeach.com
UNS No ---
Specification ISO 16143-1:2004
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
491
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
---
---
---
---
205
---
520
---
40
ST
Type 316Ti
S31635
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 316Ti
S31635
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNiMoTi17-12-2
---
1.4571
EN 10088-2:2014
X6CrNiMoTi17-12-2
---
1.4571
GB 3280-92
Grade 0Cr18Ni12Mo2Ti
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
240 220 220 240 220 220 205
---------------
540-690 540-690 520-670 540-690 540-690 520-670 530
---------------
40 T 40 T 40 T 40 T 40 T 40 T 35
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni12Mo2Ti
---
---
---
---
205
---
530
---
37
ST
ISO 16143-1:2004
X6CrNiMoTi17-12-2
---
---
ISO 9328-7:2004
Grade X6CrNiMoTi17-12-2
---
---
JIS G 4304:2012
Symbol SUS316Ti
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
---------------
240 220 220 240 220 220 205
---------------
530-730 530-730 510-710 540-690 540-690 520-670 520
---------------
40 T 40 T 40 T 40 T 40 T 40 T 40
SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS316Ti
---
---
---
---
205
---
520
---
40
ST
ASME SA-240/SA-240M
Type 316Cb
S31640
---
---
---
205
30
515
75
30
Q+SA
ASTM A240/A240M-15a
Type 316Cb
S31640
---
---
---
205
30
515
75
30
SA
EN 10028-7:2007
X6CrNiMoNb17-12-2
---
1.4580
t ≤ 75
---
220
---
520-720
---
40 T
SA
EN 10088-2:2014
X6CrNiMoNb17-12-2
---
1.4580
t ≤ 75
---
220
---
520-720
---
40 T
SA
ISO 9328-7:2004
Grade X6CrNiMoNb17-12-2
---
---
t ≤ 75
---
220
---
520-720
---
40 T
SA
Designation Symbol SUS316J1
JIS G 4305:2012
Symbol SUS316J1
ASME SA-240/SA-240M
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 --520 --40
Heat Treatment ST
Download From http://bbs.infoeach.com
Other 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB --------see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
UNS No ---
Specification JIS G 4304:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
492
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S31651 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 240 35 550 80 35
Heat Treatment Q+SA
ASME SA-666
Type 316N
S31651
---
---
---
240
35
550 L
80 L
35 L
A
ASTM A240/A240M-15a
Type 316N
S31651
---
---
---
240
35
550
80
35
SA
ASTM A666-15
Type 316N
S31651
---
---
---
240
35
550 L
80 L
35 L
A
GB 3280-92
Grade 0Cr17Ni12Mo2N
---
---
---
---
275
---
550
---
35
ST
GB 4237-92
Grade 0Cr17Ni12Mo2N
---
---
---
---
275
---
550
---
35
ST
GB 4239-91 JIS G 4304:2012
Grade 0Cr17Ni12Mo2N Symbol SUS316N
-----
-----
-----
-----
275 275
-----
550 550
-----
35 35
ST ST
JIS G 4305:2012
Symbol SUS316N
---
---
---
---
275
---
550
---
35
ST
Other 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 95 max. HRB 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Download From http://bbs.infoeach.com
Designation Type 316N
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
493
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S31653 ---
ASTM A240/A240M-15a
Type 316LN
S31653
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X2CrNiMoN17-11-2
---
1.4406
X2CrNiMoN17-13-3
---
1.4429
X2CrNiMoN17-11-2
---
1.4406
X2CrNiMoN17-13-3
---
1.4429
GB 3280-92
Grade 00Cr17Ni13Mo2N
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------------------
300 280 280 300 280 280 300 280 280 300 280 280 245
---------------------------
580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 550
---------------------------
40 T 40 T 40 T 35 T 35 T 40 T 40 T 40 T 40 T 35 T 35 T 40 T 40
SA SA SA SA SA SA SA SA SA SA SA SA ST
GB 4237-92
Grade 00Cr17Ni13Mo2N
---
---
---
---
245
---
550
---
40
ST
GB 4239-91 ISO 16143-1:2004
Grade 00Cr17Ni13Mo2N X2CrNiMoN17-12-3
-----
-----
ISO 9328-7:2004
Grade X2CrNiMoN17-11-2
---
---
Grade X2CrNiMoN17-13-3
---
---
JIS G 4304:2012
Symbol SUS316LN
---
---
--t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-----------------------
245 300 280 280 300 280 280 300 280 280 245
-----------------------
550 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780 550
-----------------------
40 35 T 35 T 40 T 40 T 40 T 40 T 35 T 35 T 40 T 40
ST SA SA SA SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS316LN
---
---
---
---
245
---
550
---
40
ST
EN 10088-2:2014
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 40
Heat Treatment Q+SA
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data see standard for impact data --see standard for impact data --see standard for impact data 217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 95 max. HRB --------see standard for impact data --see standard for impact data 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV
Download From http://bbs.infoeach.com
Designation Type 316LN
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
494
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASTM A240/A240M-15a
Type 317
S31700
---
---
---
205
30
515
75
35
SA
GB 3280-92
Grade 0Cr19Ni13Mo3
---
---
---
---
205
---
520
---
40
ST
GB 4237-92
Grade 0Cr19Ni13Mo3
---
---
---
---
205
---
520
---
35
ST
GB 4238-92
Grade 0Cr19Ni13Mo3
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 JIS G 4304:2012
Grade 0Cr19Ni13Mo3 Symbol SUS317
-----
-----
-----
-----
205 205
-----
520 520
-----
40 40
ST ST
JIS G 4305:2012
Symbol SUS317
---
---
---
---
205
---
520
---
40
ST
GB 3280-92
Grade 0Cr18Ni16Mo5
---
---
---
---
177
---
480
---
40
ST
GB 4237-92
Grade 0Cr18Ni16Mo5
---
---
---
---
177
---
480
---
35
ST
GB 4239-91 JIS G 4304:2012
Grade 0Cr18Ni16Mo5 Symbol SUS317J1
-----
-----
-----
-----
175 175
-----
480 480
-----
40 40
ST ST
JIS G 4305:2012
Symbol SUS317J1
---
---
---
---
175
---
480
---
40
ST
ASME SA-240/SA-240M
Type 317L
S31703
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 317L
S31703
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X2CrNiMo18-15-4
---
1.4438
EN 10088-2:2014
X2CrNiMo18-15-4
---
1.4438
GB 4237-92
Grade 00Cr19Ni13Mo3
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
240 220 220 240 220 220 177
---------------
550-700 550-700 520-720 550-700 550-700 520-720 480
---------------
35 T 35 T 40 T 35 T 35 T 40 T 35
SA SA SA SA SA SA ST
GB 4239-91 Grade 00Cr19Ni13Mo3 Note: This section continued on next page
---
---
---
---
175
---
480
---
40
ST
Designation
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 35
Heat Treatment SA
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data
Download From http://bbs.infoeach.com
Type 317
UNS Steel No No S31700 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
--see standard for impact data 187 max. HB; 90 max. HRB 90 max. HRB
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
495
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
Symbol SUS317L
---
---
JIS G 4305:2012
Symbol SUS317L
---
---
---
---
175
---
480
---
40
ST
ASME SA-240/SA-240M
Type 317LMN
S31726
---
---
---
240
35
550
80
40
Q+SA
ASTM A240/A240M-15a
Type 317LMN
S31726
---
---
---
240
35
550
80
40
SA
EN 10028-7:2007
X2CrNiMoN17-13-5
---
1.4439
EN 10088-2:2014
X2CrNiMoN17-13-5
---
1.4439
ISO 9328-7:2004
Grade X2CrNiMoN17-13-5
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12
-----------------
290 270 270 290 270 270 290 270
-----------------
580-780 580-780 580-780 580-780 580-780 580-780 580-780 580-780
-----------------
35 T 35 T 40 T 35 T 35 T 40 T 35 T 35 T
SA SA SA SA SA SA SA SA
t ≤ 75
---
270
---
580-780
---
40 T
SA
Designation Grade X2CrNiMo18-15-4
JIS G 4304:2012
Section Thickness/Diameter mm in. t≤6 --t ≤ 12 --t ≤ 75 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 240 --550-700 --35 T 220 --550-700 --35 T 220 --520-720 --40 T 175 --480 --40
Heat Treatment SA SA SA ST
Download From http://bbs.infoeach.com
ASME SA-240/SA-240M
Type 317LN
S31753
---
---
---
240
35
550
80
40
Q+SA
ASTM A240/A240M-15a
Type 317LN
S31753
---
---
---
240
35
550
80
40
SA
EN 10028-7:2007
X2CrNiMoN18-12-4
---
1.4434
EN 10088-2:2014
X2CrNiMoN18-12-4
---
1.4434
ISO 9328-7:2004
Grade X2CrNiMoN18-12-4
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
-------------------
290 270 270 290 270 270 290 270 270
-------------------
570-770 570-770 540-740 570-770 570-770 540-740 570-770 570-770 540-740
-------------------
35 T 35 T 40 T 35 T 35 T 40 T 35 T 35 T 40 T
SA SA SA SA SA SA SA SA SA
Other --see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV 223 max. HB; 96 max. HRB 223 max. HBW; 96 max. HRBW see standard for impact data --see standard for impact data --see standard for impact data see standard for impact data 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data
Download From http://bbs.infoeach.com
UNS No ---
Specification ISO 9328-7:2004
--see standard for impact data --see standard for impact data
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
496
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No ---
---
---
---
---
245
---
550
---
40
ST
Type 321
S32100
---
---
---
205
30
515
75
40
Q+SA
ASTM A240/A240M-15a
Type 321
S32100
---
---
---
205
30
515
75
40
SA
EN 10028-7:2007
X6CrNiTi18-10
---
1.4541
EN 10088-2:2014
X6CrNiTi18-10
---
1.4541
GB 3280-92
Grade 0Cr18Ni10Ti
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
---------------
220 200 200 220 200 200 205
---------------
520-720 520-720 500-700 520-720 520-720 500-700 520
---------------
40 T 40 T 40 T 40 T 40 T 40 T 40
SA SA SA SA SA SA ST
GB 4237-92
Grade 0Cr18Ni10Ti
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr18Ni10Ti
---
---
---
---
205 max.
---
520
---
40
ST
GB 4239-91 ISO 16143-1:2004
Grade 0Cr18Ni10Ti X6CrNiTi18-10
-----
-----
ISO 9328-7:2004
Grade X6CrNiTi18-10
---
---
JIS G 4304:2012
Symbol SUS321
---
---
--t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-----------------
205 220 200 200 220 200 200 205
-----------------
520 520-720 520-720 500-700 520-720 520-720 500-700 520
-----------------
40 40 T 40 T 40 T 40 T 40 T 40 T 40
ST SA SA SA SA SA SA ST
JIS G 4305:2012
Symbol SUS321
---
---
---
---
205
---
520
---
40
ST
Designation Symbol SUS317LN
JIS G 4305:2012
Symbol SUS317LN
ASME SA-240/SA-240M
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 245 --550 --40
Heat Treatment ST
Download From http://bbs.infoeach.com
Other 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HBW; 95 max. HRBW; 220 max. HV 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW see standard for impact data --see standard for impact data 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB --------see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
UNS No ---
Specification JIS G 4304:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
497
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S32109 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 40
Heat Treatment Q+SA
ASTM A240/A240M-15a
Type 321H
S32109
---
---
---
205
30
515
75
40
SA
GB 3280-92
Grade 1Cr18Ni9
---
---
---
---
205
---
520
---
40
ST
GB 4237-92
Grade 1Cr18Ni9
---
---
---
---
205
---
520
---
40
ST
GB 4239-91
Grade 1Cr18Ni9
---
---
ISO 4955:2005
X7CrNiTi18-10
---
---
EN 10095:1999
X12NiCrSi35-16
---
1.4864
GB 4238-92
Grade 1Cr16Ni35
---
---
--------0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160 0.5 ≤ t < 3 t ≤ 25 3 ≤ t ≤ 75 t ≤ 160 ---
-----------------------------
205 ------190 190 190 190 190 230 230 230 230 205
-----------------------------
520 785 980 1130 510-710 510-710 510-710 510-710 510-710 550-750 550-750 L 550-750 550-750 L 560
-----------------------------
40 20 10 5 40 L, 40 T 40 40 L, 40 T 40 40 28 L, 28 T 30 L 30 L, 30 T 30 L 35
ST WH WH WH SA SA SA SA SA SA SA SA SA ST
JIS G 4312:2011
Symbol SUH330
---
---
---
---
205
---
560
---
35
ST
Other 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 215 max. HB 215 max. HB 215 max. HB 215 max. HB 215 max. HB 223 max. HB 223 max. HB 223 max. HB 223 max. HB 201 max. HB; 95 max. HRB 201 max. HBW; 95 max. HRBW; 210 max. HV
Download From http://bbs.infoeach.com
Designation Type 321H
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
498
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4513 ---
Grade 00Cr17Mo
---
---
---
---
245
---
410
---
GB 4239-91 JIS G 4304:2012
Grade 00Cr17Mo Symbol SUS436L
-----
-----
-----
-----
245 245
-----
410 410
-----
JIS G 4305:2012
Symbol SUS436L
---
---
---
---
245
---
410
---
ASME SA-240/SA-240M
Type 347
S34700
---
---
---
205
30
515
75
ASTM A240/A240M-15
Type 347
S34700
---
---
---
205
30
515
75
EN 10028-7:2007
X6CrNiNb18-10
---
1.4550
EN 10088-2:2014
X6CrNiNb18-10
---
1.4550
GB 3280-92
Grade 0Cr18Ni11Nb
---
---
t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 ---
-------------
200 200 220 200 200 205
-------------
520-720 500-700 520-720 520-720 500-700 520
-------------
GB 4237-92
Grade 0Cr18Ni11Nb
---
---
---
---
205
---
520
---
GB 4238-92
Grade 0Cr18Ni11Nb
---
---
---
---
205
---
520
---
GB 4239-91 ISO 16143-1:2004
Grade 0Cr18Ni11Nb X6CrNiNb18-10
-----
-----
ISO 9328-7:2004
Grade X6CrNiNb18-10
---
---
--t≤8 t ≤ 13.5 t ≤ 75 t ≤ 75
-----------
205 220 200 200 200
-----------
520 520-720 520-720 500-700 500-700
-----------
JIS G 4304:2012
Symbol SUS347
---
---
---
---
205
---
520
---
JIS G 4305:2012
Symbol SUS347
---
---
---
---
205
---
520
---
EN 10088-2:2014 EN 10151:2002 ISO 16143-1:2004
X11CrNiMnN19-8-6 X11CrNiMnN19-8-6 X11CrNiMnN19-8-6
-------
1.4369 1.4369 ---
t≤4 0.05 ≤ t ≤ 1.00 t≤4
-------
340 --340
-------
750-950 700-1700 750-950
-------
Designation X2CrMoTi17-1 Grade 00Cr17Mo
GB 4237-92
Section Thickness/Diameter mm in. t≤8 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 200 --400-550 --23 L, 23 T 245 --410 --20
Heat Treatment A A
Download From http://bbs.infoeach.com
Other --217 max. HB; 96 max. HRB 20 A 217 max. HB; 96 max. HRB 20 A 96 max. HRB 20 A 217 max. HBW; 96 max. HRBW; 230 max. HV 20 A 217 max. HBW; 96 max. HRBW; 230 max. HV 40 Q+SA 201 max. HB; 92 max. HRB 40 SA 201 max. HBW; 92 max. HRBW 40 T SA see standard for 40 T SA impact data 40 T SA --40 T SA see standard for 40 T SA impact data 40 ST 187 max. HB; 90 max. HRB 40 ST 187 max. HB; 90 max. HRB 40 ST 187 max. HB; 90 max. HRB 40 ST 90 max. HRB 40 T SA --40 T SA --40 T SA --40 T SA see standard for impact data 40 ST 187 max. HBW; 90 max. HRBW; 200 max. HV 40 ST 187 max. HBW; 90 max. HRBW; 200 max. HV 35 T SA ----CW 300-475 HV 35 T SA --Handbook of Comparative World Steel Standards
Download From http://bbs.infoeach.com
UNS No -----
Specification EN 10088-2:2014 GB 3280-92
Chapter 8
Wrought Stainless Steels
499
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS No ---
Steel No 1.4941
Section Thickness/Diameter mm in. t≤8 --t ≤ 13.5 --t ≤ 75 ------t≤6 --t ≤ 12 --t ≤ 75 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 220 --510-710 --40 T 200 --510-710 --40 T 200 --490-690 --40 T 195 --490-680 --35 220 --510-710 --40 T 200 --510-710 --40 T 200 --490-690 --40 T 205 --520 --40
Heat Treatment SA SA SA SA SA SA SA ST
EN 10302:2008 ISO 9328-7:2004
X6CrNiTiB18-10 Grade X6CrNiTiB18-10
-----
1.4941 ---
GB 3280-92
Grade 0Cr18Ni13Si4
---
---
GB 4237-92
Grade 0Cr18Ni13Si4
---
---
---
---
205
---
520
---
40
ST
GB 4238-92
Grade 0Cr18Ni13Si4
---
---
---
---
205
---
520
---
40
ST
GB 4239-91 JIS G 4304:2012
Grade 0Cr18Ni13Si4 Symbol SUSXM15J1
-----
-----
-----
-----
205 205
-----
520 520
-----
40 40
ST ST
JIS G 4305:2012
Symbol SUSXM15J1
---
---
---
---
205
---
520
---
40
ST
EN 10088-2:2014
X8CrMnCuNB17-8-3
---
1.4597
t≤8 t ≤ 13.5
-----
300 300
-----
580-780 580-780
-----
40 T 40 T
SA SA
ISO 16143-1:2004
X8CrMnCuN17-8-3
---
---
ASME SA-240/SA-240M
---
S31060
---
t≤8 t ≤ 13.5 ---
-------
300 300 280
----41
580-780 580-780 600
----87
40 T 40 T 40
SA SA Q+SA
ASTM A240/A240M-15a
---
S31060
---
---
---
280
41
600
87
40
SA
EN 10302:2008
X8CrNiNb16-13 X6CrNiMoTiB17-13
-----
1.4961 1.4983
-----
-----
200 205
-----
510-690 530-730
-----
35 35
SA SA
Other see standard for impact data ----see standard for impact data 207 max. HB; 95 max. HRB 207 max. HB; 95 max. HRB 207 max. HB; 95 max. HRB 95 max. HRB 207 max. HBW; 95 max. HRBW; 218 max. HV 207 max. HBW; 95 max. HRBW; 218 max. HV --see standard for impact data ----217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW -----
Download From http://bbs.infoeach.com
Designation X6CrNiTiB18-10
Download From http://bbs.infoeach.com
Specification EN 10028-7:2007
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
500
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS No ---
Steel No 1.4335
X1CrNi25-21
---
1.4335
t ≤ 75
---
200
---
470-670
---
40 T
SA
X1CrNi25-21 Grade X1CrNi25-21
-----
-----
t ≤ 75 t ≤ 75
-----
200 200
-----
470-670 470-670
-----
40 T 40 T
SA SA
Specification EN 10028-7:2007
Designation X1CrNi25-21
EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004
Section Thickness/Diameter mm in. t ≤ 75 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 200 --470-670 --40 T
Heat Treatment SA
---
S34565
---
---
---
415
60
795
115
35
Q+SA
ASTM A240/A240M-15a
---
S34565
---
---
---
415
60
795
115
35
SA
EN 10088-2:2014
X2CrNiMnMoN25-18-6-5
---
1.4565
ISO 16143-1:2004
X2CrNiMnMoN25-18-6-5
---
---
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014
----X1CrNiMoCuNW24-22-6
S31266 --S31266 ----1.4659
t≤6 t ≤ 10 t ≤ 40 t≤6 t ≤ 10 t ≤ 40 ----t ≤ 75
-------------------
420 420 420 420 420 420 420 420 420
------------61 61 ---
800-950 800-950 800-950 800-1000 800-1000 800-1000 750 750 800-1000
------------109 109 ---
30 T 30 T 30 T 35 T 35 T 35 T 35 35 40 T
SA SA SA SA SA SA Q+SA SA SA
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014
----X1CrNiMoCuN24-22-8
S32654 --S32654 ----1.4652
ISO 16143-1:2004
X1CrNiMoCuN24-22-8
----t≤8 t ≤ 13.5 t ≤ 15 t≤8 t ≤ 13.5 t ≤ 75
-----------------
430 430 430 430 430 430 430 430
62 62 -------------
750 750 750-1000 750-1000 750-1000 750-950 750-950 750-950
109 109 -------------
40 40 40 T 40 T 40 T 40 T 40 T 40 T
Q+SA SA SA SA SA SA SA SA
---
---
----------see standard for impact data 250 max. HB 250 max. HBW --see standard for impact data -------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-240/SA-240M
Other see standard for impact data see standard for impact data --see standard for impact data 241 max. HB; 100 max. HRB 241 max. HBW; 100 max. HRBW see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
501
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4878
Grade 1Cr18Ni9Ti
---
---
GB 3280-92
Grade 1Cr18Ni9Ti
---
---
---
---
205
---
520
---
40
ST
GB 4237-92
Grade 1Cr18Ni9Ti
---
---
---
---
205
---
520
---
40
ST
GB 4239-91
Grade 1Cr18Ni9Ti
---
---
ASME SA-240/SA-240M
Type 347H
S34709
---
---------
---------
205 ----205
------30
540 735 885 515
------75
40 20 7 40
ST WH WH Q+SA
ASTM A240/A240M-15a
Type 347H
S34709
---
---
---
205
30
515
75
40
SA
ISO 4955:2005
X7CrNiNb18-10
---
---
EN 10028-7:2007
X3CrNiMoBN17-13-3
---
1.4910
EN 10302:2008 ISO 9328-7:2004
X3CrNiMoBN17-13-3 Grade X3CrNiMoBN17-13-3
-----
1.4910 ---
0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160 t≤3 t≤8 t ≤ 13.5 t ≤ 75 --t≤6 t ≤ 12
-------------------------
205 205 205 205 205 300 300 260 260 260 300 260
-------------------------
510-710 510-710 510-710 510-710 510-710 580-780 580-780 550-750 550-750 550-750 580-780 550-750
-------------------------
28 L, 28 T 30 30 L, 30 T 30 30 35 T 40 T 40 T 40 T 35 40 T 40 T
SA SA SA SA SA SA SA SA SA SA SA SA
t ≤ 75
---
260
---
550-750
---
40 T
SA
Designation X8CrNiTi18-10
GB 4238-92
Section Thickness/Diameter mm in. 0.5 ≤ t < 3 --t ≤ 25 --3 ≤ t ≤ 75 --t ≤ 160 -------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 190 --500-720 --40 L, 40 T 190 --500-720 L --40 L 190 --500-720 --40 L, 40 T 190 --500-720 L --40 L 205 --520 --40
Heat Treatment SA SA SA SA ST
Download From http://bbs.infoeach.com
EN 10028-7:2007
X8CrNiNb16-13
---
1.4961
t ≤ 75
---
200
---
510-690
---
35 T
SA
ISO 9328-7:2004
Grade X8CrNiNb16-13
---
---
t ≤ 75
---
200
---
510-690
---
35 T
SA
Other 215 max. HB 215 max. HB 215 max. HB 215 max. HB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 187 max. HB; 90 max. HRB 90 max. HRB 90 max. HRB 90 max. HRB 201 max. HB; 92 max. HRB 201 max. HBW; 92 max. HRBW 192 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB see standard for impact data
----see standard for impact data see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
UNS No ---
Specification EN 10095:1999
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
502
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification GB 4238-92
JIS G 4312:2011
Designation Grade 0Cr15Ni25Ti2MoAlVB
Symbol SUH660
UNS No ---
---
Steel No ---
---
X6NiCrTiMoVB25-15-2 X5NiCrAlTi31-20
-----
1.4980 1.4958
EN 10302:2008
X5NiCrAlTi31-20
---
1.4958
ISO 9328-7:2004
Grade X5NiCrAlTi31-20
---
---
EN 10302:2008 JIS G 4312:2011
X12CrCoNi21-20 Symbol SUH661
-----
1.4971 ---
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10095:1999
Type 800 Type 800 X10NiCrAlTi32-21
N08800 --N08800 ----1.4876
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min ----725 max. --25
Heat Treatment ST
---
---
590
---
900
---
15
see standard
---
---
---
---
730
---
25
ST
---
---
590
---
900
---
15
see standard
--t ≤ 75 t ≤ 75 ----t ≤ 75 t ≤ 75 -----
-------------------
600 170 210 170 210 170 210 300 315
-------------------
900-1150 500-750 500-750 500-750 500-750 500-750 500-750 690-900 690
-------------------
15 30 T 30 T 35 35 30 T 30 T 30 35
PH SA A SA A SA A SA ST
---
---
345
---
760
---
30
see standard
t > 0.50 t > 0.50 0.5 ≤ t < 3 t ≤ 25 3 ≤ t ≤ 75 t ≤ 160
t > 0.020 t > 0.020 ---------
205 205 170 170 170 170
30 30 ---------
520 520 450-680 450-680 L 450-680 450-680 L
75 75 ---------
30 30 28 L, 28 T 30 L 30 L, 30 T 30 L
Q+SA SA SA SA SA SA
Other 192 max. HB; 91 max. HRB 248 min. HB; 101 min. HRB 192 max. HBW; 91 max. HRBW; 202 max. HV 248 min. HBW; 24 min. HRC; 261 min. HV --see standard for impact data ----see standard for impact data --248 max. HBW; 100 max. HRBW; 261 max. HV 192 min. HBW; 91 min. HRBW; 202 min. HV ----192 max. HB 192 max. HB 192 max. HB 192 max. HB
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10302:2008 EN 10028-7:2007
Section Thickness/Diameter mm in. -----
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
503
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification ASME SA-240/SA-240M
UNS Steel No No N08810 --N08811 --N08810 --N08811 ----1.4959
ISO 4955:2005
X8NiCrAlTi32-21
---
---
ISO 9328-7:2004
Grade X8NiCrAlTi32-21
---
EN 10028-7:2007
X1CrNiMoCuN25-25-5
EN 10088-2:2014
ASTM A240/A240M-15a
Section Thickness/Diameter mm in. t > 0.50 t > 0.020 ----t > 0.50 t > 0.020 ----t ≤ 75 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 170 25 450 65 30 170 25 450 65 30 170 25 450 65 30 170 25 450 65 30 170 --500-750 --30 T
Heat Treatment Q+SA Q+SA SA SA SA
-------------
170 170 170 170 170 170
-------------
450-680 450-680 450-680 450-680 450-680 500-750
-------------
28 L, 28 T 30 30 L, 30 T 30 30 30 T
SA SA SA SA SA SA
---
1.4537
t ≤ 75
---
290
---
600-800
---
40 T
SA
X1CrNiMoCuN25-25-5
---
1.4537
t ≤ 75
---
290
---
600-800
---
40 T
SA
ISO 9328-7:2004
Grade X1CrNiMoCuN25-25-5
---
---
t ≤ 75
---
290
---
600-800
---
40 T
SA
ASME SA-240/SA-240M
---
N08367
---
ASTM A240/A240M-15a
-------
N08926 S31277 N08367
-------
ASTM B688-96 (2014)
-------
N08926 S31277 N08366
-------
---
N08367
---
----------------0.015 ≤ t ≤ 0.1875 t > 0.1875 0.015 ≤ t ≤ 0.1875 t > 0.1875 ---
310 310 295 360 310 310 295 360 240 240 310 310 300
45 45 43 52 45 45 43 52 35 35 45 45 ---
655 690 650 770 690 655 650 770 515 L 515 L 690 L 655 L 650-850
95 100 94 112 100 65 94 112 75 L 75 L 100 L 95 L ---
30 30 35 40 30 30 35 40 30 30 30 30 40 T
Q+SA Q+SA Q+SA Q+SA SA SA SA SA --------SA
Download From http://bbs.infoeach.com
---
0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160 t ≤ 75
EN 10028-7:2007
X1NiCrMoCuN25-20-7
---
1.4529
----------------0.40 ≤ t ≤ 4.8 t > 4.8 0.40 ≤ t ≤ 4.8 t > 4.8 t ≤ 75
EN 10088-2:2014
X1NiCrMoCuN25-20-7
---
1.4529
t ≤ 75
---
300
---
650-850
---
40 T
SA
ISO 9328-7:2004
Grade X1NiCrMoCuN25-20-7
---
---
t ≤ 75
---
300
---
650-850
---
40 T
SA
Other --------see standard for impact data 192 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB see standard for impact data see standard for impact data see standard for impact data see standard for impact data 241 max. HB 100 max. HRB ----100 max. HRBW 241 max. HBW ----95 max. HRB 212 max. HBN 100 max. HRB 240 max. HBN see standard for impact data see standard for impact data see standard for impact data
Download From http://bbs.infoeach.com
EN 10028-7:2007
Designation Type 800H --Type 800H --X8NiCrAlTi32-21
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
504
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS No ---
Steel No ---
---
---
Designation Symbol SUS836L
JIS G 4305:2012
Symbol SUS836L
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007
Type 904L Type 904L X1NiCrMoCu25-20-5
EN 10088-2:2014
X1NiCrMoCu25-20-5
---
1.4539
ISO 16143-1:2004
X1NiCrMoCu25-20-5
---
---
ISO 9328-7:2004
Grade X1NiCrMoCu25-20-5
---
---
JIS G 4304:2012
Symbol SUS890L
---
JIS G 4305:2012
Symbol SUS890L
EN 10028-7:2007
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 275 --640 --40
Heat Treatment ST
---
275
---
640
---
40
ST
---
----t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
-------------------------------
220 220 240 220 220 240 220 220 240 220 220 240 220 220 215
31 31 ---------------------------
490 490 530-730 530-730 520-720 530-730 530-730 520-720 530-730 530-730 510-710 530-730 530-730 520-720 490
71 71 ---------------------------
35 35 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35 T 35
Q+SA SA SA SA SA SA SA SA SA SA SA SA SA SA ST
---
---
---
---
215
---
490
---
35
ST
X1NiCrMoCu31-27-4
---
1.4563
t ≤ 75
---
220
---
500-700
---
40 T
SA
EN 10088-2:2014
X1NiCrMoCu31-27-4
---
1.4563
t ≤ 75
---
220
---
500-700
---
40 T
SA
ISO 16143-1:2004 ISO 9328-7:2004
X1NiCrMoCu31-27-4 Grade X1NiCrMoCu31-27-4
-----
-----
t ≤ 75 t ≤ 75
-----
220 220
-----
500-700 500-700
-----
40 T 40 T
SA SA
Download From http://bbs.infoeach.com
---
N08904 --N08904 ----1.4539
Other 217 max. HBW; 96 max. HRBW; 230 max. HV 217 max. HBW; 96 max. HRBW; 230 max. HV 90 max. HRB 90 max. HRBW see standard for impact data --see standard for impact data --------see standard for impact data 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HBW; 90 max. HRBW; 200 max. HV see standard for impact data see standard for impact data --see standard for impact data
Download From http://bbs.infoeach.com
Specification JIS G 4304:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
505
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.4A Chemical Composition of Precipitation-Hardening Stainless Steels
Designation Type 630 Type 630 X5CrNiCuNb16-4 Symbol SUS630 Symbol SUS630 Type 631 Type 631 X7CrNiAl17-7 Grade 0Cr17Ni7Al Grade 0Cr17Ni7Al Grade 0Cr17Ni7Al X7CrNiAl17-7 Symbol SUS631 Symbol SUS631
UNS Steel No No S17400 --S17400 ----1.4542 --------S17700 --S17700 ----1.4568 -------------------------
C 0.07 0.07 0.07 0.07 0.07 0.09 0.09 0.09 0.09 0.09 0.09 0.09 0.09 0.09
Mn 1.00 1.00 1.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Si 1.00 1.00 0.70 1.00 1.00 1.00 1.00 0.70 1.00 1.00 1.00 0.70 1.00 1.00
P 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 15.00-17.50 3.00-5.00 --0.030 15.0-17.5 3.0-5.0 --0.015 15.0-17.0 3.0-5.0 0.60 0.030 15.00-17.50 3.00-5.00 --0.030 15.00-17.50 3.00-5.00 --0.030 16.00-18.00 6.50-7.75 --0.030 16.0-18.0 6.5-7.7 --0.015 16.0-18.0 6.5-7.8 --0.030 16.00-18.00 6.50-7.75 --0.030 16.00-18.00 6.50-7.75 --0.030 16.00-18.00 6.50-7.75 --0.015 16.0-18.0 6.5-7.8 --0.030 16.00-18.00 6.50-7.75 --0.030 16.00-18.00 6.50-7.75 ---
Others (Cb+Ta) 0.15 to 0.45; Cu 3.00-5.00 (Cb+Ta) 0.15 to 0.45; Cu 3.0-5.0 Nb 5xC to 0.45; Cu 3.0-5.0 Nb 0.15-0.45; Cu 3.00-5.00 Nb 0.15-0.45; Cu 3.00-5.00 Al 0.75-1.50 Al 0.75-1.50 Al 0.70-1.50 Al 0.75-1.50 Al 0.75-1.50; Cu 0.50 Al 0.75-1.00 Al 0.70-1.50 Al 0.75-1.50 Al 0.75-1.50
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-693 ASTM A693-13 EN 10088-2:2014 JIS G 4304:2012 JIS G 4305:2012 ASME SA-693 ASTM A693-13 EN 10088-2:2014 GB 4237-92 GB 4238-92 GB 4239-91 ISO 16143-1:2004 JIS G 4304:2012 JIS G 4305:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
506
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels
Specification ASME SA-693
Designation Type 630
UNS Steel No No S17400 ---
Section Thickness/Diameter mm in. 0.38 ≤ t ≤ 102 0.015 ≤ t ≤ 4.0 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875
Heat Treatment ST
1170 1070 1000 860 790 725 515
170 155 145 125 115 105 75
1310 L 1170 L 1070 L 1000 L 965 L 930 L 790 L
190 L 170 L 155 L 145 L 140 L 135 L 115 L
5T 5T 5T 5T 5T 8T 9T
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1170
170
1310 L
190 L
8T
PH 900°F/482°C PH 925°F/496°C PH 1025°F/552°C PH 1075°F/579°C PH 1100°F/593°C PH 1150°F/621°C PH 1400°F+1150°F/ 760°C+621°C PH 900°F/482°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1070
155
1170 L
170 L
8T
PH 925°F/496°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1000
145
1070 L
155 L
8T
PH 1025°F/552°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
860
125
1000 L
145 L
9T
PH 1075°F/579°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
790
115
965 L
140 L
10 T
PH 1100°F/593°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
725
105
930 L
135 L
10 T
PH 1150°F/621°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
515
75
790 L
115 L
11 T
15.90 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
1170
170
1310 L
190 L
10 T
PH 1400°F+1150°F/ 760°C+621°C PH 900°F/482°C
15.90 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
1070
155
1170 L
170 L
10 T
PH 925°F/496°C
15.90 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
1000
145
1070 L
155 L
12 T
PH 1025°F/552°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
860
125
1000 L
145 L
13 T
PH 1075°F/579°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
790
115
965 L
140 L
14 T
PH 1100°F/593°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
725
105
930 L
135 L
16 T
PH 1150°F/621°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
515
75
790 L
115 L
18 T
PH 1400°F+1150°F/ 760°C+621°C)
Other 363 max. HB; 38 max. HRC 40-48 HRC 38-48 HRC 35-43 HRC 31-40 HRC 31-40 HRC 28-38 HRC 255-331 HB; 26-36 HRC 388-477 HB; 40-48 HRC 375-477 HB; 38-47 HRC 321-415 HB; 33-42 HRC 293-375 HB; 29-38 HRC 293-375 HB; 29-38 HRC 269-352 HB; 26-36 HRC 248-321 HB; 24-34 HRC 388-477 HB; 40-48 HRC 375-477 HB; 38-47 HRC 321-415 HB; 33-42 HRC 293-375 HB; 29-38 HRC 293-375 HB; 29-38 HRC 269-352 HB; 26-36 HRC 248-321 HB; 24-34 HRC
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
t < 4.762 t < 4.762 t < 4.762 t < 4.762 t < 4.762 t < 4.762 t < 4.762
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min -----------
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
507
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)
Specification ASTM A693-13
Designation Type 630
UNS Steel No No S17400 ---
Section Thickness/Diameter mm in. 0.38 ≤ t ≤ 102 0.015 ≤ t ≤ 4.0 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875 t < 0.1875
Heat Treatment ST
1170 1070 1000 860 790 725 515
170 155 145 125 115 105 75
1310 L 1170 L 1070 L 1000 L 965 L 930 L 790 L
190 L 170 L 155 L 145 L 140 L 135 L 115 L
5T 5T 5T 5T 5T 8T 9T
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1170
170
1310 L
190 L
8T
PH 900°F/482°C PH 925°F/496°C PH 1025°F/552°C PH 1075°F/579°C PH 1100°F/593°C PH 1150°F/621°C PH 1400°F+1150°F/ 760°C+621°C PH 900°F/482°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1070
155
1170 L
170 L
8T
PH 925°F/496°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1000
145
1070 L
155 L
8T
PH 1025°F/552°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
860
125
1000 L
145 L
9T
PH 1075°F/579°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
790
115
965 L
140 L
10 T
PH 1100°F/593°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
725
105
930 L
135 L
10 T
PH 1150°F/621°C
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
515
75
790 L
115 L
11 T
15.90 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
1170
170
1310 L
190 L
10 T
PH 1400°F+1150°F/ 760°C+621°C PH 900°F/482°C
15.90 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
1070
155
1170 L
170 L
10 T
PH 925°F/496°C
15.90 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
1000
145
1070 L
155 L
12 T
PH 1025°F/552°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
860
125
1000 L
145 L
13 T
PH 1075°F/579°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
790
115
965 L
140 L
14 T
PH 1100°F/593°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
725
105
930 L
135 L
16 T
PH 1150°F/621°C
15.88 ≤ t ≤ 102
0.626 ≤ t ≤ 4.0
515
75
790 L
115 L
18 T
PH 1400°F+1150°F/ 760°C+621°C)
Other 363 max. HB; 38 max. HRC 40-48 HRC 38-46 HRC 35-43 HRC 31-40 HRC 31-40 HRC 28-38 HRC 255-331 HB; 26-36 HRC 388-477 HB; 40-48 HRC 375-477 HB; 38-47 HRC 321-415 HB; 33-42 HRC 293-375 HB; 29-38 HRC 293-375 HB; 29-38 HRC 269-352 HB; 26-36 HRC 248-321 HB; 24-34 HRC 388-477 HB; 40-48 HRC 375-477 HB; 38-47 HRC 321-415 HB; 33-42 HRC 293-375 HB; 29-38 HRC 293-375 HB; 29-38 HRC 269-352 HB; 26-36 HRC 248-321 HB; 24-34 HRC
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
t < 4.762 t < 4.762 t < 4.762 t < 4.762 t < 4.762 t < 4.762 t < 4.762
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min -----------
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
508
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)
Specification EN 10088-2:2014
Symbol SUS630
UNS No ---
Steel No 1.4542
---
---
Section Thickness/Diameter mm in. t≤8 --t≤8 --t≤8 --t ≤ 50 --t ≤ 50 --t ≤ 50 --t ≤ 50 -------
Yield Strength, min. MPa ksi 700 --1150 ----------800 --600 --1000 -------
Tensile Strength, min. Elongation MPa ksi % min 900 --6 L, 6 T 1300 --3 L, 3 T 1275 max. --5 L, 5 T 1050 max. ----950-1150 --12 L, 12 T 850-1050 --14 L, 14 T 1070-1270 --10 L, 10 T -------
Heat Treatment PH (P900) PH (P1300) SA see standard PH (P950) PH (P850) PH (P1070) PH (S)
t≤5
---
725
---
930
---
8
PH (H1150)
t≤5
---
860
---
1000
---
5
PH (H1075)
t≤5
---
1000
---
1070
---
5
PH (H1025)
t≤5
---
1175
---
1310
---
5
PH (H900)
5 < t ≤ 15
---
725
---
930
---
10
PH (H1150)
5 < t ≤ 15
---
860
---
1000
---
9
PH (H1075)
5 < t ≤ 15
---
1000
---
1070
---
8
PH (H1025)
5 < t ≤ 15
---
1175
---
1310
---
8
PH (H900)
t > 15
---
725
---
930
---
16
PH (H1150)
t > 15
---
860
---
1000
---
13
PH (H1075)
t > 15
---
1000
---
1070
---
12
PH (H1025)
t > 15
---
1175
---
1310
---
10
PH (H900)
Other --------------363 max. HBW; 38 max. HRC 277 min. HBW; 28 min. HRC 302 min. HBW; 31 min. HRC 331 min. HBW; 35 min. HRC 375 min. HBW; 40 min. HRC 277 min. HBW; 28 min. HRC 302 min. HBW; 31 min. HRC 331 min. HBW; 35 min. HRC 375 min. HBW; 40 min. HRC 277 min. HBW; 28 min. HRC 302 min. HBW; 31 min. HRC 331 min. HBW; 35 min. HRC 375 min. HBW; 40 min. HRC
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
JIS G 4304:2012
Designation X5CrNiCuNb16-4
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
509
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)
Specification JIS G 4305:2012
Designation Symbol SUS630
UNS No ---
Steel No ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min -----------
Heat Treatment PH (S)
-------
1175 1000 860
-------
1310 1070 1000
-------
5 5 5
PH (H900) PH (H1025) PH (H1075)
t≤5
---
725
---
930
---
8
PH (H1150)
5 < t ≤ 15 5 < t ≤ 15 5 < t ≤ 15
-------
1175 1000 860
-------
1310 1070 1000
-------
8 8 9
PH (H900) PH (H1025) PH (H1075)
5 < t ≤ 15
---
725
---
930
---
10
PH (H1150)
t > 15 t > 15 t > 15
-------
1175 1000 860
-------
1310 1070 1000
-------
10 12 13
PH (H900) PH (H1025) PH (H1075)
t > 15
---
725
---
930
---
16
PH (H1150)
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
t≤5 t≤5 t≤5
Other 363 max. HBW; 38 max. HRC 375 min. HBW 331 min. HBW 302 min. HBW; 31 min. HRC 277 min. HBW; 28 min. HRC 375 min. HBW 331 min. HBW 302 min. HBW; 31 min. HRC 277 min. HBW; 28 min. HRC 375 min. HBW 331 min. HBW 302 min. HBW; 31 min. HRC 277 min. HBW; 28 min. HRC
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
510
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)
Specification ASME SA-693
Designation Type 631
UNS Steel No No S17700 ---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min 0.038 ≤ t ≤ 0.124 0.0015 ≤ t ≤ 0.0049 1035 150 1240 L 180 L 3T
1310
190
1450 L
210 L
1T
0.127 ≤ t ≤ 0.251 0.0050 ≤ t ≤ 0.0099
1035
150
1240 L
180 L
4T
0.127 ≤ t ≤ 0.251 0.0050 ≤ t ≤ 0.0099
1310
190
1450 L
210 L
2T
t ≤ 0.25 0.25 ≤ t ≤ 0.505
t ≤ 0.010 450 max. 65 max. 1035 max. L 150 max. L 0.010 ≤ t ≤ 0.0199 1035 150 1240 L 180 L
--5T
0.25 ≤ t ≤ 0.505
0.010 ≤ t ≤ 0.0199
1310
190
1450 L
210 L
3T
0.038 ≤ t ≤ 1.27 0.038 ≤ t ≤ 1.27
0.0015 ≤ t ≤ 0.050 0.0015 ≤ t ≤ 0.050
1205 1580
175 230
1380 L 1655 L
200 L 240 L
1T 1T
0.51 ≤ t ≤ 4.760
0.020 ≤ t ≤ 0.1874
1035
150
1240 L
180 L
6T
0.51 ≤ t ≤ 4.760
0.020 ≤ t ≤ 0.1874
1310
190
1450 L
210 L
4T
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
965
140
1170 L
170 L
7T
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
1240
180
1380 L
200 L
6T
0.25 < t ≤ 102
0.010 < t ≤ 4.0
380 max. 55 max. 1035 max. L 150 max. L
20
Other 38 min. HRC
44 min. HRC
38 min. HRC
44 min. HRC
--38 min. HRC
44 min. HRC
41 min. HRC 46 min. HRC 38 min. HRC
44 min. HRC
352 min. HB; 38 min. HRC
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
0.038 ≤ t ≤ 0.124 0.0015 ≤ t ≤ 0.0049
Heat Treatment PH 1400°F+55°F+ 1050°F/760°C+15°C +566°C PH 1750°F+(-100)°F +950°F/954°C+ (-73)°C+510°C PH 1400°F+55°F+ 1050°F/760°C+15°C +566°C PH 1750°F+(-100)°F +950°F/954°C+ (-73)°C+510°C ST PH 1400°F+55°F+ 1050°F/760°C+ 15°C+566°C PH 1750°F+(-100)°F +950°F/954°C +(-73)°C+510°C CR CR+PH 900°F/482°C PH 1400°F+55°F +1050°F/760°C +15°C+566°C PH 1750°F+(-100)°F +950°F/954°C +(-73)°C+510°C PH 1400°F+55°F +1050°F/760°C +15°C+566°C PH 1750°F+(-100)°F +950°F/954°C +(-73)°C+510°C ST
401 min. HB; 43 min. HRC 92 max. HRB
Note: This section continued on next page.
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
511
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)
Specification ASTM A693-13
Designation Type 631
UNS Steel No No S17700 ---
Section Thickness/Diameter Yield Strength, min. Tensile Strength, min. Elongation mm in. MPa ksi MPa ksi % min 0.038 ≤ t ≤ 0.124 0.0015 ≤ t ≤ 0.0049 1035 150 1240 L 180 L 3T
Other 38 min. HRC
0.038 ≤ t ≤ 0.124 0.0015 ≤ t ≤ 0.0049
44 min. HRC
0.127 ≤ t ≤ 0.251 0.0050 ≤ t ≤ 0.0099
t ≤ 0.25 0.25 ≤ t ≤ 0.505
t ≤ 0.010 0.010 ≤ t ≤ 0.0199
0.25 ≤ t ≤ 0.505
0.010 ≤ t ≤ 0.0199
0.038 ≤ t ≤ 1.27 0.038 ≤ t ≤ 1.27
0.0015 ≤ t ≤ 0.050 0.0015 ≤ t ≤ 0.050
0.51 ≤ t ≤ 4.760
0.020 ≤ t ≤ 0.1874
0.51 ≤ t ≤ 4.760
0.020 ≤ t ≤ 0.1874
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
4.762 ≤ t ≤ 15.88 0.1875 ≤ t ≤ 0.625
EN 10088-2:2014
X7CrNiAl17-7
---
1.4568
0.25 < t ≤ 102 t≤8 t≤8
0.010 < t ≤ 4.0 -----
38 min. HRC
44 min. HRC
--38 min. HRC
44 min. HRC
41 min. HRC 46 min. HRC 38 min. HRC
44 min. HRC
352 min. HB; 38 min. HRC
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
0.127 ≤ t ≤ 0.251 0.0050 ≤ t ≤ 0.0099
Heat Treatment PH 1400°F+55°F+ 1050°F/760°C+15°C +566°C 1310 190 1450 L 210 L 1T PH 1750°F+(-100)°F +950°F/954°C+ (-73)°C+510°C 1035 150 1240 L 180 L 4T PH 1400°F+55°F+ 1050°F/760°C+15°C +566°C 1310 190 1450 L 210 L 2T PH 1750°F+(-100)°F +950°F/954°C+ (-73)°C+510°C 450 max. 65 max. 1035 max. L 150 max. L --ST 1035 150 1240 L 180 L 5T PH 1400°F+55°F+ 1050°F/760°C+ 15°C+566°C 1310 190 1450 L 210 L 3T PH 1750°F+(-100)°F +950°F/954°C +(-73)°C+510°C 1205 175 1380 L 200 L 1T CR 1580 230 1655 L 240 L 1T CR+PH 900°F/482°C 1035 150 1240 L 180 L 6T PH 1400°F+55°F +1050°F/760°C +15°C+566°C 1310 190 1450 L 210 L 4T PH 1750°F+(-100)°F +950°F/954°C +(-73)°C+510°C 965 140 1170 L 170 L 7T PH 1400°F+55°F +1050°F/760°C +15°C+566°C 1240 180 1380 L 200 L 6T PH 1750°F+(-100)°F +950°F/954°C +(-73)°C+510°C 380 max. 55 max. 1035 max. L 150 max. L 20 ST ----1030 max. --19 L, 19 T SA 1310 --1450 --2 L, 2 T PH (P1450)
401 min. HB; 43 min. HRC 92 max. HRB -----
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
512
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.4B Mechanical Properties of Precipitation-Hardening Stainless Steels (Continued)
Specification GB 4237-92
Grade 0Cr17Ni7Al
UNS No ---
---
Steel No ---
---
GB 4239-91
Grade 0Cr17Ni7Al
---
---
ISO 16143-1:2004
X7CrNiAl17-7
---
---
JIS G 4304:2012
Symbol SUS631
---
---
JIS G 4305:2012
Symbol SUS631
---
---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 380 max. --1030 max. --20
Heat Treatment ST
t≤3 t≤3 t>3 t>3 ---
-----------
960 1030 960 1030 380 max.
-----------
1140 1230 1140 1230 1030 max.
-----------
3 --5 4 20
ST ST ST ST ST
t≤3 t≤3 t>3 t>3 --t≤3 t≤3 t>3 t>3 t≤8 t≤8 t≤8 ---
---------------------------
960 1030 960 1030 380 max. 960 1030 960 1030 --1200 1310 380 max.
---------------------------
1140 1230 1140 1230 1030 max. 1140 --1140 1225, 1225 1030 max. 1300 1450 1030 max.
---------------------------
3 --5 4 20 3 --5 4 19 --2 20
ST ST ST ST ST ST ST ST ST SA PH (+P1300) PH (+P1450) PH (S)
t≤3
---
1030
---
1230
---
---
PH (RH950)
t≤3
---
960
---
1140
---
3
PH (TH1050)
t>3
---
1030
---
1230
---
4
PH (RH950)
t>3
---
960
---
1140
---
5
PH (TH1050)
---
---
380 max.
---
1030 max.
---
20
PH (S)
t≤3
---
960
---
1140
---
3
PH (TH1050)
t≤3
---
1030
---
1230
---
---
PH (RH950)
t>3
---
960
---
1140
---
5
PH (TH1050)
t>3
---
1030
---
1230
---
4
PH (RH950)
Other 190 max. HB; 92 max. HRB --------190 max. HB; 92 max. HRB --------92 max. HRB --------------192 max. HBW; 92 max. HRBW 40 min. HRC; 392 min. HV 35 min. HRC; 345 min. HV 40 min. HRC; 392 min. HV 35 min. HRC; 345 min. HV 192 max. HBW; 92 max. HRBW 35 min. HRC; 345 min. HV 40 min. HRC; 392 min. HV 35 min. HRC; 345 min. HV 40 min. HRC; 392 min. HV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 4238-92
Designation Grade 0Cr17Ni7Al
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
513
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.5A Chemical Composition of Duplex (Ferritic-Austenitic) Stainless Steels
Specification EN 10088-2:2014 GB 3280-92 GB 4237-92 ASME SA-240/SA-240M ASTM A240/A240M-15a
ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 SAE J405 JUN98 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012
UNS No ------S31803 S32205 S31803 S32205 ------------S31803 S32205 S32304 S32304 --------S32304 S32520 S32520 --------S32520 -------
Steel No 1.4424 ------------1.4462 1.4462 ----------------1.4362 1.4362 ----------1.4507 1.4507 -------------
C 0.030 0.03 0.03 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.03 0.030 0.030
Mn 1.20-2.00 1.00-2.00 1.00-2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.00 2.50 2.50 2.00 2.00 2.00 2.00 2.50 1.50 1.50 2.00 2.00 2.00 2.00 1.50 1.50 1.50 1.50
Si 1.40-2.00 1.30-2.00 1.30-2.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.80 0.80 0.70 0.70 0.70 0.70 0.80 1.00 1.00 1.00
P 0.035 0.030 0.030 0.030 0.030 0.030 0.030 0.035 0.035 0.035 0.035 0.040 0.040 0.030 0.030 0.040 0.040 0.035 0.035 0.035 0.035 0.040 0.035 0.035 0.035 0.035 0.035 0.035 0.035 0.040 0.040 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.015 18.0-19.0 4.5-5.2 2.50-3.0 0.030 18.00-19.50 4.50-5.50 2.50-3.00 0.030 18.0-19.5 4.5-5.5 2.5-3.0 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.020 21.0-23.0 4.5-6.5 2.5-3.5 0.020 22.0-23.0 4.5-6.5 3.0-3.5 0.015 21.0-23.0 4.5-6.5 2.50-3.5 0.015 21.0-23.0 4.5-6.5 2.50-3.5 0.015 21.0-23.0 4.5-6.5 2.5-3.5 0.015 21.0-23.0 4.5-6.5 2.5-3.5 0.030 21.00-24.00 4.50-6.50 2.50-3.50 0.030 21.00-24.00 4.50-6.50 2.50-3.50 0.020 21.0-23.0 4.50-6.50 2.50-3.50 0.020 22.0-23.0 4.50-6.50 3.00-3.50 0.030 21.5-24.5 3.0-5.5 0.05-0.60 0.030 21.5-24.5 3.0-5.5 0.05-0.60 0.015 22.0-24.0 3.5-5.5 0.10-0.60 0.015 22.0-24.5 3.5-5.5 0.10-0.60 0.015 22.0-24.0 3.5-5.5 0.10-0.60 0.015 22.0-24.0 3.5-5.5 0.10-0.60 0.030 21.5-24.5 3.00-5.00 0.05-0.60 0.020 24.0-26.0 5.5-8.0 3.0-4.0 0.020 24.0-26.0 5.5-8.0 3.0-4.0 0.015 24.0-26.0 6.0-8.0 3.0-4.0 0.015 24.0-26.0 6.0-8.0 3.0-4.0 0.015 24.0-26.0 5.0-7.5 2.5-4.0 0.015 24.0-26.0 5.0-7.5 2.5-4.0 0.020 24.00-26.00 5.50-8.00 3.00-5.00 0.030 22.00-26.00 4.50-7.50 2.50-4.00 0.030 24.00-26.00 5.50-7.50 2.50-3.50 0.030 24.00-26.00 5.50-7.50 2.50-3.50
Others N 0.05-0.10 N 0.10 N 0.10 N 0.08-0.20 N 0.14-0.20 N 0.08-0.20 N 0.14-0.20 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 N 0.10-0.22 N 0.08-0.20 N 0.08-0.20 N 0.08-0.20 N 0.14-0.20 Cu 0.05-0.60; N 0.05-0.20 Cu 0.05-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.10-0.60; N 0.05-0.20 Cu 0.05-3.00; N 0.05-0.20 Cu 0.50-2.00; N 0.20-0.35 Cu 0.50-2.00; N 0.20-0.35 Cu 1.00-2.50; N 0.20-0.30 Cu 1.00-2.50; N 0.20-0.30 Cu 1.00-2.50; N 0.15-0.30 Cu 1.00-2.50; N 0.15-0.30 Cu 0.50-3.00; N 0.20-0.35 N 0.08-0.30 N 0.08-0.30 N 0.08-0.30
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98
Designation X2CrNiMoSi18-5-3 Grade 00Cr18Ni5Mo3Si2 Grade 00Cr18Ni5Mo3Si2 --Type 2205 --Type 2205 X2CrNiMoN22-5-3 X2CrNiMoN22-5-3 X2CrNiMoN22-5-3 Grade X2CrNiMoN22-5-3 Symbol SUS329J3L Symbol SUS329J3L ----Type 2304 Type 2304 X2CrNiN23-4 X2CrNiN23-4 X2CrNiN23-4 Grade X2CrNiN23-4 ------X2CrNiMoCuN25-6-3 X2CrNiMoCuN25-6-3 X2CrNiMoCuN25-6-3 Grade X2CrNiMoCuN25-6-3 --Grade 00Cr24Ni6Mo3N Symbol SUS329J4L Symbol SUS329J4L
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
514
8.1 Stainless Steels: Plates, Sheet and Strip 8.1.5A Chemical Composition of Duplex (Ferritic-Austenitic) Stainless Steels (Continued) UNS Steel No No S32750 --S32750 ---
C 0.030 0.030
Mn 1.20 1.20
Si 0.80 0.80
P 0.035 0.035
EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 SAE J405 JUN98 ASME SA-240/SA-240M
X2CrNiMoN25-7-4 X2CrNiMoN25-7-4 X2CrNiMoN25-7-4 Grade X2CrNiMoN25-7-4 -----
--1.4410 --1.4410 --------S32750 --S32760 ---
0.030 0.030 0.030 0.030 0.030 0.030
2.00 2.00 2.00 2.00 1.20 1.00
1.00 1.00 1.00 1.00 0.80 1.00
0.035 0.035 0.035 0.035 0.035 0.030
0.015 0.015 0.015 0.015 0.020 0.010
24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0
6.0-8.0 6.0-8.0 6.0-8.0 6.0-8.0 6.00-8.00 6.0-8.0
3.0-4.5 3.0-4.5 3.0-4.5 3.0-4.5 3.00-5.00 3.0-4.0
ASTM A240/A240M-15a
---
S32760
0.030
1.00
1.00
0.030
0.010
24.0-26.0
6.0-8.0
3.0-4.0
EN 10028-7:2007 EN 10088-2:2014 ISO 16143-1:2004 ISO 9328-7:2004 SAE J405 JUN98
X2CrNiMoCuWN25-7-4 --1.4501 X2CrNiMoCuWN25-7-4 --1.4501 X2CrNiMoCuWN25-7-4 ----Grade X2CrNiMoCuWN25-7-4 ------S32760 ---
0.030 0.030 0.030 0.030 0.030
1.00 1.00 1.00 1.00 1.00
1.00 1.00 1.00 1.00 1.00
0.035 0.035 0.035 0.035 0.030
0.015 0.015 0.015 0.015 0.010
24.0-26.0 24.0-26.0 24.0-26.0 24.0-26.0 24.00-26.00
6.0-8.0 6.0-8.0 6.0-8.0 6.0-8.0 6.00-8.00
3.0-4.0 3.0-4.0 3.0-4.0 3.0-4.0 3.00-4.00
ASME SA-240/SA-240M ASTM A240/A240M-15a GB 3280-92 GB 4237-92 GB 4239-91 JIS G 4304:2012 JIS G 4305:2012 SAE J405 JUN98 ASME SA-240/SA-240M ASTM A240/A240M-15a EN 10088-2:2014
Type 329 Type 329 Grade 0Cr26Ni5Mo2 Grade 0Cr26Ni5Mo2 Grade 0Cr26Ni5Mo2 Symbol SUS329J1 Symbol SUS329J1 Type 329 ----X2CrNiMoN29-7-2
0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.08 0.030 0.030 0.030
1.00 1.00 1.50 1.50 1.50 1.50 1.50 1.00 0.80-1.50 0.80-1.50 0.80-1.50
0.75 0.75 1.00 1.00 1.00 1.00 1.00 0.75 0.80 0.80 0.50
0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.030 0.030 0.030
0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.030 0.015
23.0-28.0 23.0-28.0 23.00-28.00 23.00-28.00 23.00-28.00 23.00-28.00 23.00-28.00 23.00-28.00 28.0-30.0 28.0-30.0 28.0-30.0
2.0-5.00 2.0-5.00 3.00-6.00 3.00-6.00 3.00-6.00 3.00-6.00 3.00-6.00 2.50-5.00 5.8-7.5 5.8-7.5 5.8-7.5
1.00-2.00 1.00-2.00 1.00-3.00 1.00-3.00 1.00-3.00 1.00-3.00 1.00-3.00 1.0-2.0 1.50-2.60 1.50-2.60 1.50-2.60
---
S32900 --S32900 ----------------------S32900 --S32906 --S32906 ----1.4477
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.020 24.0-26.0 6.0-8.0 3.0-5.0 0.020 24.0-26.0 6.0-8.0 3.0-5.0
Others Cu 0.50; N 0.24-0.32 Cu 0.50; N 0.24-0.32; [Cr+(3.3xMo)+(16xN)] = 41 min. N 0.24-0.35 N 0.24-0.35 N 0.24-0.35 N 0.24-0.35 Cu 0.50; N 0.24-0.32 [Cr+(3.3xMo)+(16xN)] = 40 min.; Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 [Cr+(3.3xMo)+(16xN)] = 40 min; Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 [Cr+(3.3xMo)+(16xN)] 40 min.; Cu 0.50-1.00; W 0.50-1.00; N 0.20-0.30 ----------------Cu 0.80; N 0.30-0.40 Cu 0.80; N 0.30-0.40 Cu 0.80; N 0.30-0.40
Download From http://bbs.infoeach.com
Designation Type 2507 Type 2507
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M ASTM A240/A240M-15a
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
515
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels Steel No 1.4424
Grade 00Cr18Ni5Mo3Si2 Grade 00Cr18Ni5Mo3Si2 ---
----S31803
-------
Type 2205
S32205
---
---
---
450
65
655
95
25
Q+SA
---
S31803
---
---
---
450
65
620
90
25
SA
Type 2205
S32205
---
---
---
450
65
655
95
25
SA
---------------------------
485 445 445 500 460 460 480 460 460 465 445 445 450
---------------------------
700-950 700-950 640-480 700-950 700-950 640-840 660 660 640 660-950 660-950 640-840 620
---------------------------
20 L, 20 T 25 L, 25 T 25 L, 25 T 20 L, 20 T 25 L, 25 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 25 L, 25 T 18
SA SA SA SA SA SA SA SA SA SA SA SA ST
---
450
---
620
---
18
ST
Designation X2CrNiMoSi18-5-3
GB 3280-92 GB 4237-92 ASME SA-240/SA-240M
Download From http://bbs.infoeach.com
ASTM A240/A240M-15a
Section Thickness/Diameter mm in. t≤8 --t ≤ 13.5 --t ≤ 75 ---------------
EN 10028-7:2007
X2CrNiMoN22-5-3
---
1.4462
EN 10088-2:2014
X2CrNiMoN22-5-3
---
1.4462
ISO 16143-1:2004
X2CrNiMoN22-5-3
---
---
ISO 9328-7:2004
Grade X2CrNiMoN22-5-3
---
---
JIS G 4304:2012
Symbol SUS329J3L
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 ---
JIS G 4305:2012
Symbol SUS329J3L
---
---
---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 450 --700-900 --25 L, 25 T 450 --700-900 --25 L, 25 T 400 --680-900 --25 L, 25 T 390 --590 --20 390 --590 --20 450 65 620 90 25
Heat Treatment SA SA SA ST ST Q+SA
Other see standard for impact data 30 max. HRB --293 max. HB; 31 max. HRC 293 max. HB; 31 max. HRC 293 max. HBW; 31 max. HRC 293 max. HBW; 31 max. HRC see standard for impact data --see standard for impact data --------see standard for impact data 302 max. HBW; 32 max. HRC; 320 max. HV 302 max. HBW; 32 max. HRC; 320 max. HV
Download From http://bbs.infoeach.com
UNS No ---
Specification EN 10088-2:2014
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
516
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels (Continued) UNS Steel No No S32304 ---
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 400 58 600 87 25
Heat Treatment Q+SA
ASTM A240/A240M-15a
Type 2304
S32304
---
---
---
400
58
600
87
25
SA
EN 10028-7:2007
X2CrNiN23-4
---
1.4362
EN 10088-2:2014
X2CrNiN23-4
---
1.4362
ISO 16143-1:2004
X2CrNiN23-4
---
---
ISO 9328-7:2004
Grade X2CrNiN23-4
---
---
ASME SA-240/SA-240M ASTM A240/A240M-15a
-----
S32520 S32520
-----
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 -----
-----------------------------
405 385 385 450 400 400 420 400 400 405 385 385 550 550
------------------------80 80
600-850 600-850 630-800 650-850 650-850 630-800 600 600 630 600-850 600-850 630-800 770 770
------------------------112 112
20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 25 25
SA SA SA SA SA SA SA SA SA SA SA SA Q+SA SA
EN 10028-7:2007
X2CrNiMoCuN25-6-3
---
1.4507
EN 10088-2:2014
X2CrNiMoCuN25-6-3
---
1.4507
ISO 16143-1:2004
X2CrNiMoCuN25-6-3
---
---
ISO 9328-7:2004
Grade X2CrNiMoCuN25-6-3
---
---
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75
-------------------------
495 475 475 550 530 530 550 530 530 495 475 475
-------------------------
690-940 690-940 690-890 750-1000 750-1000 730-930 750 750 730 690-940 690-940 690-890
-------------------------
20 L, 20 T 20 L, 20 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T 17 L, 17 T 17 L, 17 T 25 L, 25 T 20 L, 20 T 20 L, 20 T 25 L, 25 T
SA SA SA SA SA SA SA SA SA SA SA SA
Other 290 max. HB; 32 max. HRC 290 max. HBW; 32 max. HRC see standard for impact data --see standard for impact data --------see standard for impact data 310 max. HB 310 max. HBW; 32 max. HRC see standard for impact data --see standard for impact data --------see standard for impact data
Download From http://bbs.infoeach.com
Designation Type 2304
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
517
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels (Continued)
Specification GB 4239-91 JIS G 4304:2012
Designation Grade 00Cr24Ni6Mo3N Symbol SUS329J4L
JIS G 4305:2012
Symbol SUS329J4L
UNS No -----
Steel No -----
Section Thickness/Diameter mm in. ---------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 450 --620 --18 450 --620 --18
Heat Treatment ST ST
---
---
---
---
450
---
620
---
18
ST
Type 2507
S32750
---
---
---
550
80
795
116
15
Q+SA
ASTM A240/A240M-15a
Type 2507
S32750
---
---
---
550
80
795
116
15
SA
EN 10028-7:2007
X2CrNiMoN25-7-4
---
1.4410
EN 10088-2:2014
X2CrNiMoN25-7-4
---
1.4410
ISO 16143-1:2004
X2CrNiMoN25-7-4
---
---
ISO 9328-7:2004
Grade X2CrNiMoN25-7-4
---
---
ASME SA-240/SA-240M ASTM A240/A240M-15a
-----
S32760 S32760
-----
t≤8 t ≤ 13.5 t ≤ 75 t≤8 t ≤ 13.5 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 t≤6 t ≤ 12 t ≤ 75 -----
-----------------------------
535 515 515 550 530 530 550 530 530 535 515 515 550 550
------------------------80 80
750-1000 750-1000 730-930 750-1000 750-1000 730-930 750 750 730 750-1000 750-1000 730-930 750 750
------------------------108 108
20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 15 L, 15 T 15 L, 15 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 20 L, 20 T 25 25
SA SA SA SA SA SA SA SA SA SA SA SA Q+SA SA
EN 10028-7:2007
X2CrNiMoCuWN25-7-4
---
1.4501
t ≤ 75
---
515
---
730-930
---
25 L, 25 T
SA
EN 10088-2:2014
X2CrNiMoCuWN25-7-4
---
1.4501
t ≤ 75
---
530
---
730-930
---
25 L, 25 T
SA
ISO 16143-1:2004 ISO 9328-7:2004
X2CrNiMoCuWN25-7-4 Grade X2CrNiMoCuWN25-7-4
-----
-----
t ≤ 75 t ≤ 75
-----
530 515
-----
730 730-930
-----
25 L, 25 T 25 L, 25 T
SA SA
--see standard for impact data --------see standard for impact data 270 max. HB 270 max. HBW; 28 max. HRC see standard for impact data see standard for impact data --see standard for impact data
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-240/SA-240M
Other --302 max. HBW; 32 max. HRC; 320 max. HV 302 max. HBW; 32 max. HRC; 320 max. HV 310 max. HB; 32 max. HRC 310 max. HBW; 32 max. HRC see standard for impact data
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
518
8.1 Stainless Steels: Plate, Sheet and Strip 8.1.5B Mechanical Properties of Duplex (Ferritic-Austenitic) Stainless Steels (Continued)
ASTM A240/A240M-15a
Type 329
S32900
---
---
---
485
70
620
90
15
SA
GB 3280-92
Grade 0Cr26Ni5Mo2
---
---
---
---
390
---
590
---
18
ST
GB 4237-92 GB 4239-91 JIS G 4304:2012
Grade 0Cr26Ni5Mo2 Grade 0Cr26Ni5Mo2 Symbol SUS329J1
-------
-------
-------
-------
390 390 390
-------
590 590 590
-------
18 18 18
ST ST ST
JIS G 4305:2012
Symbol SUS329J1
---
---
---
---
390
---
590
---
18
ST
ASME SA-240/SA-240M
---
S32906
---
t < 10.0
t < 0.4
650
94
800
166
25.0
Q+SA
t ≥ 10.0
t ≥ 0.4
550
80
750
109
25.0
Q+SA
t < 10.0
t < 0.4
650
94
800
166
25.0
SA
t ≥ 10.0
t ≥ 0.4
550
80
750
109
25.0
SA
t≤8 t ≤ 13.5 t ≤ 75
-------
650 550 550
-------
800-1050 750-1000 750-1000
-------
20 L, 20 T 20 L, 20 T 20 L, 20 T
SA SA SA
ASTM A240/A240M-15a
EN 10088-2:2014
Designation
---
X2CrNiMoN29-7-2
S32906
---
---
1.4477
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 485 70 620 90 15
Heat Treatment Q+SA
Other 269 max. HB; 28 max. HRC 269 max. HBW; 28 max. HRC 277 max. HB; 29 max. HRB 277 max. HB --277 max. HBW; 29 max. HRC; 292 max. HV 277 max. HBW; 29 max. HRC; 292 max. HV 310 max. HB; 32 max. HRC 310 max. HB; 32 max. HRC 310 max. HBW; 32 max. HRC 310 max. HBW; 32 max. HRC --see standard for impact data
Download From http://bbs.infoeach.com
Type 329
UNS Steel No No S32900 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
519
8.2 Stainless Steels: Bar 8.2.1A Chemical Composition of Martensitic Stainless Steels
Designation Type 403 Type 403 Type 403 Type 403 Grade 1Cr12 Grade 1Cr12 Symbol SUS403 Symbol SUS403 Type 410 Type 410 Type 410 Type 410 Type 410 Type 410 X12Cr13 X12Cr13 Grade 1Cr13 Grade 1Cr13 Grade 1Cr13 Type X 12 Cr 13 E Symbol SUS410 Symbol SUS410 Grade 1Cr13Mo Grade 1Cr13Mo Symbol SUS410J1 Type 416 Grade Y1Cr13 Grade Y1Cr13 Symbol SUS416 Symbol SUS416 X12CrS13
UNS No S40300 S40300 S40300 S40300 --------S41000 S41000 S41000 S41000 S41000 S41000 ----------------------S41600 -----------
Steel No ----------------------------1.4006 1.4006 ----------------------------1.4005
C 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.08-0.15 0.15 0.15 0.08-0.15 0.08-0.15 0.15 0.08-0.15 0.08-0.15 0.15 0.15 0.15 0.09-0.15 0.15 0.15 0.08-0.18 0.08-0.18 0.08-0.18 0.15 0.15 0.15 0.15 0.15 0.06-0.15
Mn 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.50 1.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.25 1.25 1.25 1.25 1.25 1.50
Si 0.50 0.50 0.50 0.50 0.50 0.50 0.50 0.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.60 0.60 0.60 1.00 1.00 1.00 1.00 1.00 1.00
P 0.040 0.040 0.040 0.040 0.035 0.035 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.040 0.035 0.035 0.040 0.06 0.060 0.060 0.060 0.060 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 11.50-13.00 ----0.030 11.5-13.0 ----0.030 11.5-13.0 ----0.030 11.5-13.0 ----0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.50-13.00 0.60 --0.030 11.5-13.5 0.75 --0.030 11.50-13.50 ----0.030 11.5-13.5 ----0.030 11.5-13.5 0.75 --0.030 11.5-13.5 ----0.030 11.5-13.5 ----0.030 11.5-13.5 0.75 --0.030 11.50-13.50 0.75 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.5-13.5 1.0 --0.030 11.50-13.50 0.60 --0.030 11.50-13.50 0.60 --0.030 11.50-14.00 0.60 0.30-0.60 0.030 11.50-14.00 0.60 --0.030 11.50-14.00 0.60 0.30-0.60 0.15 min. 12.0-14.0 ----0.15 min. 12.00-14.00 0.60 0.60 0.15 12.00-14.00 0.60 0.60 0.15 min. 12.00-14.00 0.60 0.60 0.15 min. 12.00-14.00 0.60 0.60 0.15-0.35 12.0-14.0 --0.60
Others ----------------------------------------------Cu 0.30 ---------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-276 ASME SA-479/SA-479M ASTM A276/A276M-15 ASTM A479/A479M-14 GB 1220-92 GB 4226-84 JIS G 4303:2012 JIS G 4318:1998 A1:2007 ASME SA-240/SA-240M ASME SA-276 ASME SA-479/SA-479M ASTM A240/A240M-15a ASTM A276/A276M-15 ASTM A479/A479M-14 EN 10088-3:2014 EN 10263-5:2001 GB 1220-92 GB 1221-92 GB 4226-84 ISO 4954:1993 JIS G 4303:2012 JIS G 4318:1998 A1:2007 GB 1220-92 GB 1221-92 JIS G 4303:2012 ASTM A582/A582M-12e1 GB 1220-92 GB 4226-84 JIS G 4303:2012 JIS G 4318:1998 A1:2007 EN 10088-3:2014
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
520
8.2 Stainless Steels: Bar 8.2.1A Chemical Composition of Martensitic Stainless Steels (Continued)
Designation Type 420 Type 420 X20Cr13 Grade 2Cr13 Grade 2Cr13 Grade 2Cr13 Symbol SUS420J1 Symbol SUS420J1 Type 420F X30Cr13 Grade 3Cr13 Grade 3Cr13 Symbol SUS420J2 Symbol SUS420J2 X29CrS13 Grade Y3Cr13 Grade Y3Cr13 Symbol SUS420F Symbol SUS420F Type 431 Type 431 Type 431 Type 431 X17CrNi16-2 Type X 19 CrNi 16 2 E Symbol SUS431 Type 440A Type 440A X70CrMo15 Grade 7Cr17 Symbol SUS440A Type 440B Type 440B Grade 8Cr17 Symbol SUS440B
UNS No S42000 S42000 ------------S42020 --------------------S43100 S43100 S43100 S43100 ------S44002 S44002 ------S44003 S44003 -----
Steel No ----1.4021 ------------1.4028 --------1.4029 ----------------1.4057 --------1.4109 -------------
C 0.15 min. 0.15 min. 0.16-0.25 0.16-0.25 0.16-0.25 0.16-1.25 0.16-0.25 0.16-0.25 0.30-0.40 0.26-0.35 0.26-0.35 0.26-0.40 0.26-0.40 0.26-0.40 0.25-0.32 0.26-0.40 0.26-0.40 0.26-0.40 0.26-0.40 0.20 0.20 0.20 0.20 0.12-0.22 0.14-0.23 0.20 0.60-0.75 0.60-0.75 0.60-0.75 0.60-0.75 0.60-0.75 0.75-0.95 0.75-0.95 0.75-0.95 0.75-0.95
Mn 1.00 1.00 1.50 1.00 1.00 1.00 1.00 1.00 1.25 1.50 1.00 1.00 1.00 1.00 1.50 1.25 1.25 1.25 1.25 1.00 1.00 1.00 1.00 1.50 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.70 1.00 1.00 1.00 1.00 1.00 1.00
P 0.040 0.040 0.040 0.035 0.035 0.035 0.040 0.040 0.06 0.040 0.035 0.035 0.040 0.040 0.040 0.060 0.060 0.060 0.060 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.040 0.035 0.040 0.040 0.040 0.035 0.040
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo 0.030 12.00-14.00 ----0.030 12.0-14.0 ----0.030 12.0-14.0 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.15 min. 12.0-14.0 0.50 --0.030 12.0-14.0 ----0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.030 12.00-14.00 0.60 --0.15-0.25 12.0-13.5 --0.60 0.15 min. 12.00-14.00 0.60 0.60 0.15 min. 12.00-14.00 0.60 0.60 0.15 min. 12.00-14.00 0.60 0.60 0.15 min. 12.00-14.00 0.60 0.60 0.030 15.00-17.00 1.25-2.50 --0.030 15.0-17.0 1.25-2.50 --0.030 15.0-17.0 1.25-2.50 --0.030 15.0-17.0 1.25-2.50 --0.030 15.0-17.0 1.50-2.50 --0.030 15.0-17.5 1.5-2.5 --0.030 15.00-17.00 1.25-2.50 --0.030 16.00-18.00 --0.75 0.030 16.0-18.0 --0.75 0.030 14.0-16.0 --0.40-0.80 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 --0.75 0.030 16.0-18.0 --0.75 0.030 16.00-18.00 0.60 0.75 0.030 16.00-18.00 0.60 0.75
Others ----------------Cu 0.60 -----------------------------------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Specification ASME SA-276 ASTM A276/A276M-15 EN 10088-3:2014 GB 1220-92 GB 1221-92 GB 4226-84 JIS G 4303:2012 JIS G 4318:1998 A1:2007 ASTM A582/A582M-12e1 EN 10088-3:2014 GB 1220-92 GB 4226-84 JIS G 4303:2012 JIS G 4318:1998 A1:2007 EN 10088-3:2014 GB 1220-92 GB 4226-84 JIS G 4303:2012 JIS G 4318:1998 A1:2007 ASME SA-276 ASME SA-479/SA-479M ASTM A276/A276M-15 ASTM A479/A479M-14 EN 10088-3:2014 ISO 4954:1993 JIS G 4303:2012 ASME SA-276 ASTM A276/A276M-15 EN 10088-3:2014 GB 1220-92 JIS G 4303:2012 ASME SA-276 ASTM A276/A276M-15 GB 1220-92 JIS G 4303:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
521
8.2 Stainless Steels: Bar 8.2.1A Chemical Composition of Martensitic Stainless Steels (Continued) UNS No S44004 S44004 ----------S64152 -------
Steel No ------------1.4125 --1.4938 1.4938 1.4913
GB 1221-92 JIS G 4311:2011
Grade 2Cr12MoVNbN Symbol SUH600
-----
-----
ASTM A565/A565M-10 GB 1221-92 JIS G 4311:2011 ASME SA-276 ASME SA-479/SA-479M ASTM A276/A276M-15 ASTM A479/A479M-14 EN 10088-3:2014 ISO 16143-2:2004 EN 10088-3:2014 GB 1220-92 ASTM A582/A582M-12e1 GB 1220-92 JIS G 4303:2012 EN 10088-3:2014 GB 1220-92 GB 1221-92 JIS G 4311:2011
Grade 616 Grade 2Cr12NiMoWV Symbol SUH616 --------X3CrNiMo13-4 X3CrNiMo13-4 X39Cr13 Grade 4Cr13 Type 440F Grade Y11Cr17 Symbol SUS440F X90CrMoV18 Grade 9Cr18MoV Grade 8Cr20Si2Ni Symbol SUH4
C Mn 0.95-1.20 1.00 0.95-1.20 1.00 0.95-1.20 1.00 0.95-1.20 1.00 0.95-1.20 1.00 0.95-1.20 1.00 0.95-1.20 1.00 0.08-0.15 0.50-0.90 0.08-0.15 0.40-0.90 0.08-0.15 0.40-0.90 0.17-0.23 0.40-0.90
Si 1.00 1.00 1.00 1.00 1.00 1.00 1.00 0.35 0.50 0.50 0.50
0.15-0.20 0.15-0.20
0.50 0.50
0.50-1.00 0.50-1.00
S42200 --0.20-0.25 0.50-1.00 ----0.20-0.25 0.50-1.00 ----0.20-0.25 0.50-1.00 S41500 --0.05 0.50-1.00 S41500 --0.05 0.50-1.00 S41500 --0.05 0.50-1.00 S41500 --0.05 0.50-1.00 --1.4313 0.05 1.50 ----0.05 0.50-1.00 --1.4031 0.36-0.42 1.00 ----0.36-0.45 0.80 S44020 --0.95-1.20 1.25 ----0.95-1.20 1.25 ----0.95-1.20 1.25 --1.4112 0.85-0.95 1.00 ----0.85-0.95 0.80 ----0.75-0.85 0.20-0.60 ----0.75-0.85 0.20-0.60
0.50 0.50 0.50 0.60 0.60 0.60 0.60 0.70 0.70 1.00 0.60 1.00 1.00 1.00 1.00 0.80 1.75-2.25 1.75-2.25
Weight, %, max, Unless Otherwise Specified S Cr Ni Mo Others 0.030 16.00-18.00 --0.75 --0.030 16.0-18.0 --0.75 --0.030 16.00-18.00 0.60 0.75 --0.030 16.00-18.00 0.60 0.75 --0.030 16.00-18.00 0.60 0.75 --0.030 16.00-18.00 0.60 0.75 --0.030 16.0-18.0 --0.40-0.80 --0.025 11.00-12.50 2.00-3.00 1.50-2.00 V 0.25-0.40; N 0.01-0.05 0.015 11.0-12.5 2.00-3.00 1.50-2.00 V 0.25-0.40; N 0.020-0.040 0.015 11.0-12.5 2.00-3.00 1.50-2.00 V 0.25-0.40; N 0.020-0.040 0.015 10.0-11.5 0.20-0.60 0.50-0.80 V 0.10-0.30; Nb 0.25-0.55; N 0.05-0.10; Al 0.020; B 0.0015 0.035 0.030 10.00-13.00 0.60 0.30-0.90 V 0.10-0.40; Nb 0.20-0.60; N 0.05-0.10 0.040 0.030 10.00-13.00 0.60 0.30-0.90 V 0.10-0.40; Nb 0.20-0.60; N 0.05-0.10; Cu 0.30 0.025 0.025 11.00-12.50 0.50-1.00 0.90-1.25 V 0.20-0.30; W 0.90-1.25 0.035 0.030 11.00-13.00 0.50-1.00 0.75-1.25 V 0.20-0.40; W 0.70-1.25 0.040 0.030 11.00-13.00 0.50-1.00 0.75-1.25 V 0.20-0.30; Cu 0.30; W 0.75-1.25 0.030 0.030 11.50-14.00 3.50-5.50 0.50-1.00 --0.030 0.030 11.5-14.0 3.5-5.5 0.50-1.00 --0.030 0.030 11.5-14.0 3.5-5.5 0.50-1.00 --0.030 0.030 11.5-14.0 3.5-5.5 0.50-1.00 --0.040 0.015 12.0-14.0 3.5-4.5 0.30-0.70 N 0.020 min. 0.040 0.015 12.0-14.0 3.5-4.5 0.30-1.00 --0.040 0.030 12.5-14.5 ------0.035 0.030 12.00-14.00 0.60 ----0.06 0.15 min. 16.0-18.0 0.50 --Cu 0.60 0.060 0.15 min. 16.00-18.00 0.60 0.75 --0.060 0.15 min. 16.00-18.00 0.60 0.75 --0.040 0.030 17.0-19.0 --0.90-1.30 V 0.07-0.12 0.035 0.030 17.00-19.00 0.60 1.00-1.30 V 0.07-0.12 0.030 0.030 19.00-20.50 1.15-1.65 ----0.030 0.030 19.00-20.50 1.15-1.65 --Cu 0.30
P 0.040 0.040 0.035 0.035 0.040 0.040 0.040 0.025 0.025 0.025 0.025
Download From http://bbs.infoeach.com
Designation Type 440C Type 440C Grade 11Cr17 Grade 11Cr17 Symbol SUS440C Symbol SUS440C X105CrMo17 Grade XM-32 X12CrNiMoV12-3 X12CrNiMoV12-3 X19CrMoNbVN11-1
Download From http://bbs.infoeach.com
Specification ASME SA-276 ASTM A276/A276M-15 GB 1220-92 GB 4226-84 JIS G 4303:2012 JIS G 4318:1998 A1:2007 EN 10088-3:2014 ASTM A565/A565M-10 EN 10269:2013 EN 10302:2008 EN 10269:2013
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
522
8.2 Stainless Steels: Bar 8.2.1B Mechanical Properties of Martensitic Stainless Steels
ASME SA-479/SA-479M
Type 403
S40300
---
ASTM A276/A276M-15
Type 403
S40300
---
ASTM A479/A479M-14
Type 403
S40300
---
GB 1220-92
Grade 1Cr12
---
---
JIS G 4303:2012
Symbol SUS403
---
---
Designation
Section Thickness/Diameter mm in. --------------------------------------------------------------------------------t ≤ 75 ---
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 275 40 480 70 20 A and HF 275 40 480 70 16 A and CF 550 80 690 100 15 H+T and HF 550 80 690 100 12 H+T and CF 620 90 830 120 12 H+T and HF 620 90 830 120 12 H+T and CF 275 40 485 70 20 A 275 40 485 70 20 T 585 85 760 110 15 T 690 100 895 130 12 T 275 40 480 70 20 A+HF 275 40 480 70 16 A+CF 550 80 690 100 15 H+T and HF 550 80 690 100 12 H+T and CF 620 90 830 120 12 H+T and HF 620 90 830 120 12 H+T and CF 275 40 485 70 20 A 275 40 485 70 20 T 585 85 760 110 15 T 690 100 895 130 12 T 390 --590 --25 Q+T
t ≤ 75 d ≤ 75
-----
-----
-----
-----
-----
-----
A A
d ≤ 75
---
390
---
590
---
25
Q+T
Other ------------223 max. HB 223 max. HB 269 max. HB 331 max. HB ------------223 max. HB 223 max. HB 269 max. HB 331 max. HB 170 min. HB; 118 J @ RT 200 max. HB 200 max. HBW; 93 max. HRBW; 210 max. HV 170 min. HBW; 87 min. HRBW; 178 min. HV
Download From http://bbs.infoeach.com
Type 403
UNS Steel No No S40300 ---
Download From http://bbs.infoeach.com
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
523
8.2 Stainless Steels: Bar 8.2.1B Mechanical Properties of Martensitic Stainless Steels (Continued)
ASME SA-276
Type 410
S41000
---
ASME SA-479/SA-479M
Type 410
S41000
---
ASTM A240/A240M-15a
Type 410
S41000
---
ASTM A276/A276M-15
Type 410
S41000
---
ASTM A479/A479M-14
Type 410
S41000
---
Designation
Note: This section continued on next page
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 205 30 450 65 20 see standard
-----------------------
-----------------------
275 275 550 550 620 620 275 275 585 690 205
40 40 80 80 90 90 40 40 85 100 30
480 480 690 690 830 830 485 485 760 895 450
70 70 100 100 120 120 70 70 110 130 65
20 16 15 12 12 12 20 20 15 12 20
A and HF A and CF H+T and HF H+T and CF H+T and HF H+T and CF A T T T ---
---------------------
---------------------
275 275 550 550 620 620 275 275 585 690
40 40 80 80 90 90 40 40 85 100
480 480 690 690 830 830 485 485 760 895
70 70 100 100 120 120 70 70 110 130
20 16 15 12 12 12 20 20 15 12
A+HF A+CF H+T and HF H+T and CF H+T and HF H+T and CF A T T T
Other 217 max. HB; 96 max. HRB ------------223 max. HB 223 max. HB 269 max. HB 331 max. HB 217 max. HBW; 96 max. HRBW ------------223 max. HB 223 max. HB 269 max. HB 331 max. HB
Download From http://bbs.infoeach.com
Type 410
UNS Steel No No S41000 ---
Download From http://bbs.infoeach.com
Specification ASME SA-240/SA-240M
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
524
8.2 Stainless Steels: Bar 8.2.1B Mechanical Properties of Martensitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X12Cr13
UNS No ---
Steel No 1.4006
Yield Strength, min. MPa ksi --------------------550 ------500 ----------450 ------450 --450 ------450 -----------------------------------------------
Tensile Strength, min. Elongation MPa ksi % min 730 max. ----1100 max. --10 1050 max. --10 1000 max. --10 880 ----700-1000 --9L 880 ----700-1000 --9L 950 max. --15 800 ----650-930 --10 L 760 ----650-880 --10 L 650-850 --15 L 730 ----650-850 --15 L 500-700 ----600-800 ----700-900 ----800-1000 ----900-1100 ----1000-1250 ----1100-1350 ----1200-1450 ----1400-1700 ----1600-1900 ----1800-2100 -----
Heat Treatment A A+PH A+PH A+PH A Q+T A Q+T A+PH A Q+T A Q+T Q+T A Q+T -----------------------
Other 220 max. HBW ------280 max. HB --280 max. HB ----250 max. HB L: 25 J @ RT 230 max. HB L: 25 J @ RT L: 25 J @ RT 220 max. HB L: 25 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. ----0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --t ≤ 10 --10 < t ≤ 16 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --16 < t ≤ 40 --40 < t ≤ 63 --40 < t ≤ 63 --t ≤ 160 --63 < t ≤ 160 --63 < t ≤ 160 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
525
8.2 Stainless Steels: Bar 8.2.1B Mechanical Properties of Martensitic Stainless Steels (Continued)
Specification EN 10263-5:2001
Designation X12Cr13
UNS No ---
Steel No 1.4006
Grade 1Cr13
---
---
GB 1221-92
Grade 1Cr13
---
---
ISO 4954:1993
Type X 12 Cr 13 E
---
---
JIS G 4303:2012
Symbol SUS410
---
---
Yield Strength, min. MPa ksi ----------------------------------------345 ---
Tensile Strength, min. Elongation MPa ksi % min 600 max. L ----660 max. L ----600 max. L ----720 max. L ----600 max. L ----640 max. L ----600 max. L ----700 max. L ----600 max. L ----600 max. L ----540 --25
Heat Treatment CD+A CD+A A A CD+A CD+A A A CD+A A Q+T
t ≤ 75 t ≤ 75
-----
--345
-----
--540
-----
--25
A Q+T
t ≤ 75 2 ≤ d ≤ 100 2 ≤ d ≤ 100 d ≤ 75
---------
---------
---------
--600 max. 640 max. ---
---------
---------
A A, CW A, CW A
d ≤ 75
---
345
---
540
---
25
Q+T
GB 1220-92
Grade 1Cr13Mo
---
---
t ≤ 75
---
490
---
685
---
20
Q+T
GB 1221-92
Grade 1Cr13Mo
---
---
t ≤ 75 t ≤ 75
-----
--490
-----
--685
-----
--20
A Q+T
JIS G 4303:2012
Symbol SUS410J1
---
---
t ≤ 75 d ≤ 75
-----
-----
-----
-----
-----
-----
A A
d ≤ 75
---
490
---
690
---
20
Q+T
Other --------------------159 min. HB; 78 J @ RT 200 max. HB 159 min. HB; 78 J @ RT 200 max. HB ----200 max. HBW; 93 max. HRBW; 210 max. HV 159 min. HBW; 84 min. HRBW; 166 min. HV 192 min. HB; 78 J @ RT 200 max. HB 192 min. HB; 78 J @ RT 200 max. HB 200 max. HBW; 93 max. HRBW; 210 max. HV 192 min. HBW; 92 min. HRBW; 200 min. HV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
GB 1220-92
Section Thickness/Diameter mm in. 2 12.70 t > 0.5 ----2 ≤ d ≤ 50 --2 ≤ d ≤ 50 --d ≤ 180 ---
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 205 30 515 75 30 A and HF 310 45 620 90 30 A and CF 690 100 860 125 12 CW and CF 550 80 795 115 15 CW and CF 450 65 725 105 20 CW and CF 345 50 690 100 24 CW and CF 310 45 655 95 28 CW and CF 205 30 515 75 40 A and HF 205 30 515 75 30 A and CF 205 30 515 75 30 A 205 30 515 75 30 A+HF 310 45 620 90 30 A+CF 690 100 860 125 12 CW+CF 550 80 795 115 15 CW+CF 450 65 725 105 20 CW+CF 345 50 690 100 24 CW+CF 310 45 655 95 28 CW+CF 205 30 515 75 40 A+HF 205 30 515 75 30 A+CF 205 30 515 75 30 SA ----660 max. ----Q, CD ----720 max. ----see standard 205 --520 --40 ST
Other --------------------------------------------187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Type 302
UNS Steel No No S30200 ---
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
554
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification Designation ASTM A582/A582M-12e1 Type 303 EN 10088-3:2014 X8CrNiS18-9
UNS Steel No No S30300 ----1.4305
Yield Strength, min. MPa ksi ----350 --500 --------------------------400 --400 ------190 --190 --190 --190 ----------------------------------------------190 --205 ---
Tensile Strength, min. Elongation MPa ksi % min ------700-850 --20 800-1000 --12 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-950 --15 L 600-950 --15 L 800 max. --35 500-850 --20 L 500-850 --20 L 500-750 --35 L 500-750 --35 L 500-700 ----600-800 ----700-900 ----800-1000 ----900-1100 ----1000-1250 ----1100-1350 ----1200-1450 ----1400-1700 ----1600-1900 ----1800-2100 ----500-700 --35 L; 30 T 520 --40
Heat Treatment A CW CW SA SA SA SA SA SA SA SA SA SA SA SA SA ----------------------SA ST
EN 10294-2:2012 GB 1220-92
X8CrNiS18-9 Grade Y1Cr18Ni9
-----
JIS G 4303:2012
Symbol SUS303
---
---
d ≤ 180
---
205
---
520
---
40
ST
S30323 ---
-----
--t ≤ 180
-----
--205
-----
--520
-----
--40
A ST
---
---
d ≤ 180
---
205
---
520
---
40
ST
ASTM A582/A582M-12e1 Type 303Se GB 1220-92 Grade Y1Cr18Ni9Se JIS G 4303:2012
Symbol SUS303Se
Other 262 max. HBW --------------------------230 max. HBW --------------------------187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 262 max. HBW 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. ------------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 --63 < t ≤ 160 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --1.4305 ------t ≤ 180 ---
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
555
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASME SA-479/SA-479M
Type 304
S30400
---
ASME SA-666
Type 304
S30400
---
ASTM A276/A276M-15
Type 304
S30400
---
ASTM A479/A479M-14
Type 304
S30400
---
ASTM A666-15
Type 304
S30400
---
Designation
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t ≤ 19.05 t ≤ 0.75 19.05 < t ≤ 25.40 0.75 < t ≤ 1 25.40 < t ≤ 31.75 1 < t ≤ 1.25 31.75 < t ≤ 38.10 1.25 < t ≤ 1.5 38.10 < t ≤ 44.45 1.5 < t ≤ 1.75 t ≤ 50.8 t≤2 50.8 < t ≤ 63.5 2 < t ≤ 2.5 63.5 < t ≤ 76.2 2.5 < t ≤ 3 t > 12.5 t > 0.5 t > 12.70 t > 0.5 --------t ≤ 50.8 t≤2 50.8 < t ≤ 63.5 2 < t ≤ 2.5 63.5 < t ≤ 76.2 2.5 < t ≤ 3 ----t ≤ 12.5 t ≤ 12.70 t ≤ 19.05 19.05 < t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 t > 12.5 t > 12.70 ----t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 ---
t ≤ 0.5 t ≤ 0.5 t ≤ 0.75 0.75 < t ≤ 1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 t > 0.5 t > 0.5 ----t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 ---
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 205 30 515 75 30 A and HF 310 45 620 90 30 A and CF 690 100 860 125 12 CW and CF 550 80 795 115 15 CW and CF 450 65 725 105 20 CW and CF 345 50 690 100 24 CW and CF 310 45 655 95 28 CW and CF 515 75 650 95 25 H+CW+CF 450 65 620 90 30 H+CW+CF 380 55 550 80 30 H+CW+CF 205 30 515 75 40 A and HF 205 30 515 75 30 A and CF 205 30 515 75 30 A 450 65 585 85 30 H 515 75 655 95 25 H 450 65 620 90 30 H 380 55 550 80 30 H 205 30 515 75 40 A 205 310 690 550 450 345 310 515 450 380 205 205 205 450 515 450 380 205
30 45 100 80 65 50 45 75 65 55 30 30 30 65 75 65 55 30
515 620 860 795 725 690 655 650 620 550 515 515 515 585 655 620 550 515
75 90 125 115 105 100 95 95 90 80 75 75 75 85 95 90 80 75
30 30 12 15 20 24 28 25 30 30 40 30 30 30 25 30 30 40
A+HF A+CF CW+CF CW+CF CW+CF CW+CF CW+CF H+CF H+CF H+CF A+HF A+CF SA H H H H A
Other ----------------------------------201 max. HB; 92 max. HRB ----------------------------------201 max. HB; 92 max. HRB
Download From http://bbs.infoeach.com
Type 304
UNS Steel No No S30400 ---
Specification ASME SA-276
Note: This section continued on next page Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
556
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification ASTM A955/A955M-15 EN 10088-3:2014
Designation Grade 60 [420], Type 304 Grade 75 [520], Type 304 X5CrNi18-10
UNS Steel No No S30400 --S30400 ----1.4301
Yield Strength, min. MPa ksi 420 60 520 75 350 --500 --------------------------400 --400 ------190 --190 --190 ---
Tensile Strength, min. Elongation Heat MPa ksi % min Treatment 620 90 20 A, HR or SH 690 100 20 A, HR or SH 700-850 --20 CW 800-1000 --12 CW 1100 max. --20 SA 1050 max. --20 SA 1000 max. --30 SA 950 max. --30 SA 900 max. --30 SA 850 max. --35 SA 600-950 --25 L SA 600-950 --25 L SA 800 max. --35 SA 600-850 --30 L SA 580-850 --30 L SA 500-700 --45 L SA
63 < t ≤ 160 160 < t ≤ 250
-----
190 190
-----
500-700 500-700
-----
45 L 35 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
190 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
35 T -----------------------
SA -----------------------
Other --------------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. ----------------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
557
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10263-5:2001
Designation X5CrNi18-10
UNS No ---
Steel No 1.4301
X5CrNi18-10 Grade 0Cr18Ni9
-----
1.4301 ---
GB 1221-92 ISO 4954:1993
Grade 0Cr18Ni9 Type X 5 CrNi 18 9 E
-----
-----
JIS G 4303:2012
Symbol SUS304
---
---
t ≤ 180 2 ≤ d ≤ 50 2 ≤ d ≤ 50 d ≤ 180
---------
Yield Strength, min. MPa ksi ----------------------------------------195 --205 --205 ----205
---------
Tensile Strength, min. Elongation MPa ksi % min 700 max. L ----750 max. L ----650 max. L ----820 max. L ----650 max. L ----700 max. L ----650 max. L ----780 max. L ----650 max. L ----650 max. L ----500-700 --40 L; 35 T 520 --40 520 650 max. 710 max. 520
---------
40 ----40
Heat Treatment CD+SA CD+SA SA CD+SA CD+SA CD+SA SA CD+SA CD+SA SA SA ST ST Q, CD see standard ST
Other ----------------------187 max. HB; 90 max. HRB 187 max. HB ----187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10294-2:2012 GB 1220-92
Section Thickness/Diameter mm in. 2 0.5 t > 12.70 t > 0.5 --------t ≤ 50.8 t≤2 50.8 < t ≤ 63.5 2 < t ≤ 2.5 63.5 < t ≤ 76.2 2.5 < t ≤ 3 ----t ≤ 12.5 t ≤ 12.70 t ≤ 19.05 19.05 < t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 t > 12.5 t > 12.70 ----t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 ---
t ≤ 0.5 t ≤ 0.5 t ≤ 0.75 0.75 < t ≤ 1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 t > 0.5 t > 0.5 ----t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 170 25 485 70 30 310 45 620 90 30 170 25 485 70 40 170 25 485 70 30 170 25 485 70 30 450 65 585 85 30 515 75 655 95 25 450 65 620 90 30 380 55 550 80 30 170 25 485 70 40 170 310 690 550 450 345 310 515 450 380 170 170 170 450 515 450 380 170
25 45 100 80 65 50 45 75 65 55 25 25 25 65 75 65 55 25
485 620 860 795 725 690 655 650 620 550 485 485 485 585 655 620 550 485
70 90 125 115 105 100 95 95 90 80 70 70 70 85 95 90 80 70
30 30 12 15 20 24 28 25 30 30 40 30 30 30 25 30 30 40
Heat Treatment A and HF A and CF A and HF A and CF SA H H H H A A+HF A+CF CW+CF CW+CF CW+CF CW+CF CW+CF H+CF H+CF H+CF A+HF A+CF SA H H H H A
Other ------------------201 max. HB; 92 max. HRB ----------------------------------201 max. HB; 92 max. HRB
Download From http://bbs.infoeach.com
Designation Type 304L
Download From http://bbs.infoeach.com
Specification ASME SA-276
Note This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
559
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X2CrNi18-9
UNS No ---
Steel No 1.4307
Yield Strength, min. MPa ksi 350 --500 --------------------------400 --380 ------175 --175 --175 ---
Tensile Strength, min. Elongation MPa ksi % min 700-850 --20 800-1000 --12 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-930 --25 L 600-930 --25 L 800 max. --35 500-830 --30 L 500-830 --30 L 500-700 --45 L
Heat Treatment CW CW SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
175 175
-----
500-700 500-700
-----
45 L 35 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
175 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
35 T -----------------------
SA -----------------------
Other ----------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. --------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
560
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4307
GB 1220-92
X2CrNi18-9 X2CrNi19-11 Grade 00Cr19Ni10
-------
1.4307 1.4306 ---
ISO 4954:1993
Type X 2 CrNi 18 10 E
---
---
JIS G 4303:2012
Symbol SUS304L
---
ASME SA-276
Type 304N
S30451
Download From http://bbs.infoeach.com
EN 10294-2:2012
ASME SA-479/SA-479M ASME SA-666
Designation X2CrNi18-9
Type 304N Type 304N
S30451 S30451
Section Thickness/Diameter mm in. 2 12.70 -----
t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 -----
205 310 205 205 205 205
30 45 30 30 30 30
515 620 515 515 515 515
75 90 75 75 75 75
30 30 40 30 30 40
A and HF A and CF A and HF A and CF A A
ASTM A276/A276M-15
Type 304LN
S30453
---
ASTM A479/A479M-14 ASTM A666-15
Type 304LN Type 304LN
S30453 S30453
-----
t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 -----
t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 -----
205 310 205 205 205 205
30 45 30 30 30 30
515 620 515 515 515 515
75 90 75 75 75 75
30 30 40 30 30 40
A+HF A+CF A+HF A+CF SA A
EN 10088-3:2014
X2CrNiN18-10
---
1.4311
t ≤ 160
---
270
---
550-760
---
40 L
SA
160 < t ≤ 250
---
270
---
550-760
---
30 T
SA
t ≤ 180
---
245
---
550
---
40
ST
Download From http://bbs.infoeach.com
S30451 S30451
t ≤ 19.05 19.05 < t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 -----
ASTM A479/A479M-14 ASTM A666-15
Type 304N Type 304N
GB 1220-92
GB 1220-92
Grade 00Cr18Ni10N
---
---
Other --------------------217 max. HB; 95 max. HRB 217 max. HB; 95 max. HRB 217 max. HBW; 95 max. HRBW; 220 max. HV 215 max. HBW; L: 100 J @ RT ----------217 max. HB; 95 max. HRB ----------217 max. HB; 95 max. HRB 230 max. HBW; L: 100 J @ RT 230 max. HBW; T: 60 J @ RT 217 max. HB; 95 max. HRB
Download From http://bbs.infoeach.com
t ≤ 0.75 0.75 < t ≤ 1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 -----
Heat Treatment A+HF or A+CF CW+CF CW+CF CW+CF CW+CF CW+CF H+CF H+CF H+CF SA A
Note: This section continued on the next page Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
562
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS No ---
Steel No ---
ASME SA-479/SA-479M ASTM A479/A479M-14 EN 10088-3:2014 ISO 4955:2005
Type 304H Type 304H X9CrNi18-9 X7CrNi18-9
S30409 --S30409 ----1.4325 -----
ASME SA-276
Type XM-21
S30452
ASTM A276/A276M-15
Type XM-21
S30452
Section Thickness/Diameter mm in. d ≤ 180 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 245 --550 --40
Heat Treatment ST
---
----t ≤ 40 0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160 ---
-------------------
205 205 190 195 195 195 195 195 345
30 30 ------------50
515 515 550-750 500-700 500-700 500-700 500-700 500-700 620
75 75 ------------90
30 30 40 L 37 L, 37 T 40 40 L, 40 T 40 40 30
---
t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 ---
t≤1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 ---
860 795 725 690 345
125 115 105 100 50
1000 930 895 860 620
145 135 135 125 90
15 16 17 18 30
t≤1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 ---
860 795 725 690 345
125 115 105 100 ---
1000 930 895 860 685
145 135 135 125 ---
15 16 17 18 35
A SA SA SA SA SA SA SA A and HF or A and CF CW and CF CW and CF CW and CF CW and CF A+HF or A+CF CW+CF CW+CF CW+CF CW+CF ST
GB 1220-92
Grade 0Cr19Ni10NbN
---
---
t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 t ≤ 180
JIS G 4303:2012
Symbol SUS304N2
---
---
d ≤ 180
---
345
---
690
---
35
ST
ASME SA-276
Type 305
S30500
---
ASTM A276/A276M-15
Type 305
S30500
---
GB 1220-92
Grade 1Cr18Ni12
---
---
t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 t ≤ 180
t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 ---
205 310 205 205 205 310 205 205 177
30 45 30 30 30 45 30 30 ---
515 620 515 515 515 620 515 515 480
75 90 75 75 75 90 75 75 ---
30 30 40 30 30 30 40 30 40
A and HF A and CF A and HF A and CF A+HF A+CF A+HF A+CF ST
JIS G 4303:2012
Symbol SUS305
---
---
d ≤ 180
---
175
---
480
---
40
ST
Other 217 max. HBW; 95 max. HRBW; 220 max. HV ----215 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB 192 max. HB --------------------250 max. HB; 100 max. HRB 250 max. HBW; 100 max. HRBW; 260 max. HV ----------------187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Designation Symbol SUS304LN
Download From http://bbs.infoeach.com
Specification JIS G 4303:2012
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
563
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X4CrNi18-12
UNS No ---
Steel No 1.4303
X4CrNi18-12
---
1.4303
EN 10269:2013
X4CrNi18-12
---
1.4303
ISO 4954:1993
Type X 5 CrNi 18 12 E
---
---
Yield Strength, min. MPa ksi ----------------------------190 ---
Tensile Strength, min. Elongation MPa ksi % min 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 800 max. --35 500-700 --45 L
Heat Treatment SA SA SA SA SA SA SA SA
160 < t ≤ 250
---
190
---
500-700
---
35 T
SA
d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 2 12.70 t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 t ≤ 180 t ≤ 180
t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 -----
205 310 205 205 205 310 205 205 205 205
30 45 30 30 30 45 30 30 -----
515 620 515 515 515 620 515 515 590 590
75 90 75 75 75 90 75 75 -----
30 30 40 30 30 30 40 30 40 40
A and HF A and CF A and HF A and CF A+HF A+CF A+HF A+CF ST ST
Designation
Section Thickness/Diameter mm in. t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 t ≤ 180 --t ≤ 180 --t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 ----t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 ----t ≤ 180 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 --560 --45 205 --560 --45 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 --520 --40
Heat Treatment A and HF A and CF A and HF A and CF A+HF A+CF A+HF A+CF ST ST A and HF A and CF A and HF A and CF A A+HF A+CF A+HF A+CF SA ST
Other ----------------201 max. HB 201 max. HBW --------------------187 max. HB; 90 max. HRB 187 max. HB 187 max. HBW; 90 max. HRBW; 200 max. HV ----------------201 max. HB 201 max. HBW
Download From http://bbs.infoeach.com
Type 309
UNS Steel No No S30900 ---
Download From http://bbs.infoeach.com
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
565
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued) UNS Steel No No S31008 ---
ASME SA-479/SA-479M ASTM A276/A276M-15
Type 310S Type 310S
S31008 S31008
-----
ASTM A479/A479M-14 GB 1220-92
Type 310S Grade 0Cr25Ni20
S31008 ---
-----
GB 1221-92 JIS G 4303:2012
Grade 0Cr25Ni20 Symbol SUS310S
-----
-----
Section Thickness/Diameter mm in. t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 ----t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 ----t ≤ 180 --t ≤ 180 d ≤ 180
-----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 --520 --40 205 205
-----
520 520
-----
40 40
Heat Treatment A and HF A and CF A and HF A and CF A A+HF A+CF A+HF A+CF SA ST ST ST
Other --------------------187 max. HB; 90 max. HRB 187 max. HB 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Designation Type 310S
Download From http://bbs.infoeach.com
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
566
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASME SA-479/SA-479M ASTM A276/A276M-15
-----
S31254 S31254
ASTM A479/A479M-14 EN 10088-3:2014
--X1CrNiMoCuN20-18-7
S31254 ----1.4547
Designation
-----
Section Thickness/Diameter mm in. -----
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 300 44 650 95 35 A and HF or A and CF 305 44 655 95 35 A 300 44 650 95 35 A+HF or A+CF 305 44 655 95 35 SA ----1100 max. --20 SA ----1050 max. --20 SA ----1000 max. --30 SA ----950 max. --30 SA ----900 max. --30 SA ----850 max. --35 SA ----800 max. --35 SA 300 --650-850 --35 L SA
-----
-----
--0.05 < d ≤ 0.10 0.10 < d ≤ 0.20 0.20 < d ≤ 0.50 0.50 < d ≤ 1.00 1.00 < d ≤ 3.00 3.00 < d ≤ 5.00 5.00 < d ≤ 16.00 t ≤ 160
-------------------
160 < t ≤ 250
---
300
---
650-850
---
30 T
SA
-------------------------
----------------------300
-------------------------
500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100 650
-------------------------
----------------------35
----------------------ST
JIS G 4303:2012
Symbol SUS312L
---
---
d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≤ 180
EN 10088-3:2014
X1CrNiMoCuNW24-22-6
---
1.4659
t ≤ 160
---
420
---
800-1000
---
50 L
SA
ISO 16143-2:2004 ASTM A276/A276M-15
X1CrNiMoCuNW24-22-6 ---
--S32654
-----
t ≤ 160 ---
-----
420 430
--62
800-1000 750
--109
50 L 40
ASTM A479/A479M-14 EN 10088-3:2014
--X1CrNiMoCuN24-22-8
S32654 ----1.4652
--t ≤ 50
-----
430 430
62 ---
750 750-1000
109 ---
40 40 L
SA A+HF or A+CF SA SA
ISO 16143-2:2004
X1CrNiMoCuN24-22-8
t ≤ 50
---
430
---
750-1000
---
40 L
SA
---
---
Other ----------------------260 max. HBW; L: 100 J @ RT 260 max. HBW; T: 60 J @ RT ----------------------223 max. HBW; 96 max. HRBW; 230 max. HV 290 max. HBW; L: 90 J @ RT --250 max. HBW
Download From http://bbs.infoeach.com
---
UNS Steel No No S31254 ---
Download From http://bbs.infoeach.com
Specification ASME SA-276
250 max. HB 310 max. HBW; L: 100 J @ RT ---
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
567
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASTM A276/A276M-15
Type 314
S31400
---
-----
--1.4841
GB 1221-92 EN 10095:1999
Designation
Grade 1Cr25Ni20Si2 X15CrNiSi25-21
Section Thickness/Diameter mm in. t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 t ≤ 180 --0.5 ≤ t < 3 --t ≤ 25 --3 ≤ t ≤ 75 --t ≤ 160 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 295 --590 --35 230 --550-750 --28 L, 28 T 230 --550-750 L --30 L 230 --550-750 --30 L, 30 T 230 --550-750 L --30 L
Heat Treatment A and HF A and CF A and HF A and CF A+HF A+CF A+HF A+CF ST SA SA SA SA
Other ----------------187 max. HB 223 max. HB 223 max. HB 223 max. HB 223 max. HB
Download From http://bbs.infoeach.com
Type 314
UNS Steel No No S31400 ---
Download From http://bbs.infoeach.com
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
568
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
ASME SA-479/SA-479M
Type 316
S31600
---
ASME SA-666
Type 316
S31600
---
ASTM A276/A276M-15
Type 316
S31600
---
ASTM A479/A479M-14
Type 316
S31600
---
ASTM A666-15
Type 316
S31600
---
Designation
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t ≤ 19.05 t ≤ 0.75 19.05 < t ≤ 25.40 0.75 < t ≤ 1 25.40 < t ≤ 31.75 1 < t ≤ 1.25 31.75 < t ≤ 38.10 1.25 < t ≤ 1.5 38.10 < t ≤ 44.45 1.5 < t ≤ 1.75 t ≤ 50.8 t≤2 50.8 < t ≤ 63.5 2 < t ≤ 2.5 63.5 < t ≤ 76.2 2.5 < t ≤ 3 t > 12.5 t > 0.5 t > 12.70 t > 0.5 --------t ≤ 50.8 t≤2 50.8 < t ≤ 63.5 2 < t ≤ 2.5 63.5 < t ≤ 76.2 2.5 < t ≤ 3 ----t ≤ 12.5 t ≤ 12.70 t ≤ 19.05 19.05 < t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 t > 12.5 t > 12.70 ----t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 ---
t ≤ 0.5 t ≤ 0.5 t ≤ 0.75 0.75 < t ≤ 1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 t > 0.5 t > 0.5 ----t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 ---
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment 205 30 515 75 30 A and HF 310 45 620 90 30 A and CF 690 100 860 125 12 CW and CF 550 80 795 115 15 CW and CF 450 65 725 105 20 CW and CF 345 50 690 100 24 CW and CF 310 45 655 95 28 CW and CF 515 75 650 95 25 H+CW+CF 450 65 620 90 30 H+CW+CF 380 55 550 80 30 H+CW+CF 205 30 515 75 40 A and HF 205 30 515 75 30 A and CF 205 30 515 75 30 A 450 65 585 85 30 H 515 75 655 95 30 H 450 65 620 90 30 H 380 55 550 80 30 H 205 30 515 75 40 A 205 310 690 550 450 345 310 515 450 380 205 205 205 450 515 450 380 205
30 45 100 80 65 50 45 75 65 55 30 30 30 65 75 65 55 30
515 620 860 795 725 690 655 650 620 550 515 515 515 585 655 620 550 515
75 90 125 115 105 100 95 95 90 80 75 75 75 85 95 90 80 75
30 30 12 15 20 24 28 25 30 30 40 30 30 30 25 30 30 40
A+HF A+CF CW+CF CW+CF CW+CF CW+CF CW+CF H+CF H+CF H+CF A+HF A+CF SA H H H H A
Other ----------------------------------217 max. HB; 95 max. HRB ----------------------------------217 max. HB; 95 max. HRB
Download From http://bbs.infoeach.com
Type 316
UNS Steel No No S31600 ---
Specification ASME SA-276
Note: This section continued on next page Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
569
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X5CrNiMo17-12-2
UNS No ---
Steel No 1.4401
Yield Strength, min. MPa ksi 350 --500 --------------------------400 --380 ------200 --200 --200 ---
Tensile Strength, min. Elongation MPa ksi % min 700-850 --20 800-1000 --12 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-950 --25 L 580-950 --25 L 800 max. --35 500-850 --30 L 500-850 --30 L 500-700 --40 L
Heat Treatment CW CW SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
200 200
-----
500-700 500-700
-----
40 L 30 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
200 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
30 T -----------------------
SA -----------------------
Other ----------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. --------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
570
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X3NiCrMo17-13-3
UNS No ---
Steel No 1.4436
Yield Strength, min. MPa ksi ------------------------400 --400 ------200 --190 --200 ---
Tensile Strength, min. Elongation MPa ksi % min 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-950 --25 L 600-950 --25 L 800 max. --35 500-850 --30 L 500-850 --30 L 500-700 --40 L
Heat Treatment SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
200 200
-----
500-700 500-700
-----
40 L 30 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
200 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
30 T -----------------------
SA -----------------------
Other ------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. 0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
571
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4401
X3CrNiMo17-13-3
---
1.4436
EN 10294-2:2012 GB 1220-92
X5CrNiMo17-12-2 Grade 0Cr17Ni12Mo2
-----
1.4401 ---
GB 1221-92 ISO 4954:1993
Grade 0Cr17Ni12Mo2 Type X 5 CrNiMo 17 12 2 E
-----
-----
JIS G 4303:2012
Symbol SUS316
---
---
Designation X5CrNiMo17-12-2
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. 2 0.5 --------t ≤ 50.8 t≤2 50.8 < t ≤ 63.5 2 < t ≤ 2.5 63.5 < t ≤ 76.2 2.5 < t ≤ 3 -----
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 170 25 485 70 30 310 45 620 90 30 170 25 485 70 40 170 25 485 70 30 170 25 485 70 30 450 65 585 85 30 515 75 655 95 25 450 65 620 90 30 380 55 550 80 30 170 25 485 70 40
Heat Treatment A and HF A and CF A and HF A and CF A H H H H A
---
t ≤ 12.5 t ≤ 12.70 t ≤ 19.05 19.05 < t ≤ 25.40 25.40 < t ≤ 31.75 31.75 < t ≤ 38.10 38.10 < t ≤ 44.45 t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 t > 12.5 t > 12.70 ----t ≤ 50.8 50.8 < t ≤ 63.5 63.5 < t ≤ 76.2 ---
t ≤ 0.5 t ≤ 0.5 t ≤ 0.75 0.75 < t ≤ 1 1 < t ≤ 1.25 1.25 < t ≤ 1.5 1.5 < t ≤ 1.75 t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 t > 0.5 t > 0.5 ----t≤2 2 < t ≤ 2.5 2.5 < t ≤ 3 ---
170 310 690 550 450 345 310 515 450 380 170 170 170 450 515 450 380 170
25 45 100 80 65 50 45 75 65 55 25 25 25 65 75 65 55 25
485 620 860 795 725 690 655 650 620 550 485 485 485 585 655 620 550 485
70 90 125 115 105 100 95 95 90 80 70 70 70 85 95 90 80 70
30 30 12 15 20 24 28 25 30 30 40 30 30 30 25 30 30 40
A+HF A+CF CW+CF CW+CF CW+CF CW+CF CW+CF H+CF H+CF H+CF A+HF A+CF SA H H H H A
-----
-----
-----
420 520
60 75
620 690
90 100
20 20
A, HR or SH A, HR or SH
Other ------------------217 max. HB; 95 max. HRB ----------------------------------217 max. HB; 95 max. HRB -----
Download From http://bbs.infoeach.com
Designation Type 316L
Download From http://bbs.infoeach.com
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
573
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X2CrNiMo17-12-2
UNS No ---
Steel No 1.4404
Yield Strength, min. MPa ksi 350 --500 --------------------------400 --380 ------200 --200 --200 ---
Tensile Strength, min. Elongation MPa ksi % min 700-850 --20 800-1000 --12 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-930 --25 L 580-930 --25 L 800 max. --35 500-830 --30 L 500-830 --30 L 500-700 --40 L
Heat Treatment CW CW SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
200 200
-----
500-700 500-700
-----
40 L 30 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
200 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
30 T -----------------------
SA -----------------------
Other ----------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. --------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
574
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X2CrNiMo17-12-3
UNS No ---
Steel No 1.4432
Yield Strength, min. MPa ksi ------------------------400 --380 ------200 --200 --200 ---
Tensile Strength, min. Elongation MPa ksi % min 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-930 --25 L 600-880 --25 L 800 max. --35 500-850 --30 L 500-850 --30 L 500-700 --40 L
Heat Treatment SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
200 200
-----
500-700 500-700
-----
40 L 30 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
200 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
30 T -----------------------
SA -----------------------
Other ------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. 0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
575
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X2CrNiMo18-14-3
UNS No ---
Steel No 1.4435
Yield Strength, min. MPa ksi ------------------------400 --400 ------235 --235 --200 ---
Tensile Strength, min. Elongation MPa ksi % min 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-950 --25 L 600-950 --25 L 800 max. --35 500-850 --30 L 500-850 --30 L 500-700 --40 L
Heat Treatment SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
235 200
-----
500-700 500-700
-----
40 L 30 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
235 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
30 T -----------------------
SA -----------------------
Other ------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. 0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continue on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
576
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4404
X2CrNiMo17-12-3
---
1.4432
ISO 4954:1993
X2CrNiMo17-12-2 X2CrNiMo18-14-3 Type X 2 CrNiMo 17 13 3 E
-------
1.4404 1.4435 ---
ASME SA-276
Type 316Ti
S31635
---
ASME SA-479/SA-479M ASTM A276/A276M-15
Type 316Ti Type 316Ti
S31635 S31635
-----
S31635
---
Download From http://bbs.infoeach.com
EN 10294-2:2012
Designation X2CrNiMo17-12-2
ASTM A479/A479M-14 Type 316Ti Note: This section continued on next page
Section Thickness/Diameter mm in. 2 0.5 ----t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 -----
Yield Strength, min. MPa ksi --------------------------------------------------------------------------------190 --190 ----------205 30 310 45 205 30 205 30 205 30 205 30 310 45 205 30 205 30 205 30
Tensile Strength, min. Elongation Heat MPa ksi % min Treatment 670 max. L ----CD+SA 720 max. L ----CD+SA 650 max. L ----SA 780 max. L ----CD+SA 650 max. L ----CD+SA 700 max. L ----CD+SA 650 max. L ----SA 750 max. L ----CD+SA 650 max. L ----CD+SA 650 max. L ----SA 670 max. L ----CD+SA 720 max. L ----CD+SA 650 max. L ----SA 780 max. L ----CD+SA 650 max. L ----CD+SA 700 max. L ----CD+SA 650 max. L ----SA 750 max. L ----CD+SA 650 max. L ----CD+SA 650 max. L ----SA 490-690 --40 L; 30 T SA 490-690 --40 L; 30 T SA 680 max. ----Q, CD 730 max. ----see standard 515 75 30 A and HF 620 90 30 A and CF 515 75 40 A and HF 515 75 30 A and CF 515 75 30 A 515 75 30 A+HF 620 90 30 A+CF 515 75 40 A+HF 515 75 30 A+CF 515 75 30 SA
Other ---------------------------------------------------------------------
Download From http://bbs.infoeach.com
UNS No ---
Specification EN 10263-5:2001
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
577
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X6CrNiMoTi17-12-2
UNS No ---
Steel No 1.4571
Yield Strength, min. MPa ksi 350 --500 --------------------------400 --380 ------200 --200 --200 ---
Tensile Strength, min. Elongation MPa ksi % min 700-850 --20 800-1000 --12 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-950 --25 L 580-950 --25 L 800 max. --35 500-850 --30 L 500-850 --30 L 500-700 --40 L
Heat Treatment CW CW SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
200 200
-----
500-700 500-700
-----
40 L 30 T
SA SA
160 < t ≤ 250 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-------------------------
200 -----------------------
-------------------------
500-700 500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-------------------------
30 T -----------------------
SA -----------------------
Other ----------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. --------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
578
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10263-5:2001
Designation X6CrNiMoTi17-12-2
UNS No ---
Steel No 1.4571
X6CrNiMoTi17-12-2 Type X 6 CrNiMoTi 17 12 2 E
-----
1.4571 ---
JIS G 4303:2012
Symbol SUS316Ti
---
---
ASME SA-276
Type 316Cb
S31640
---
ASME SA-479/SA-479M ASTM A276/A276M-15
Type 316Cb Type 316Cb
S31640 S31640
-----
ASTM A479/A479M-14 EN 10088-3:2014
Type 316Cb X6CrNiMoNb17-12-2
S31640 ----1.4580
Yield Strength, min. MPa ksi ----------------------------------------190 ----------205 ---
Tensile Strength, min. Elongation Heat MPa ksi % min Treatment 720 max. L ----CD+SA 770 max. L ----CD+SA 680 max. L ----SA 850 max. L ----CD+SA 680 max. L ----CD+SA 730 max. L ----CD+SA 680 max. L ----SA 810 max. L ----CD+SA 680 max. L ----CD+SA 680 max. L ----SA 490-690 --35 L; 30 T SA 680 max. ----Q, CD 730 max. ----see standard 520 --40 ST
t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 --t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 --t ≤ 160
t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 --t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 -----
205 310 205 205 205 205 310 205 205 205 215
30 45 30 30 30 30 45 30 30 30 ---
515 620 515 515 515 515 620 515 515 515 510-740
75 90 75 75 75 75 90 75 75 75 ---
30 30 40 30 30 30 30 40 30 30 35 L
A and HF A and CF A and HF A and CF A A+HF A+CF A+HF A+CF SA SA
160 < t ≤ 250
---
215
---
510-740
---
30 T
SA
GB 1220-92
Grade 0Cr18Ni12Mo2Cu2
---
---
t ≤ 180
---
205
---
520
---
40
ST
JIS G 4303:2012
Symbol SUS316J1
---
---
d ≤ 180
---
205
---
520
---
40
ST
GB 1220-92
Grade 00Cr17Ni14Mo2
---
---
t ≤ 180
---
177
---
480
---
40
ST
JIS G 4303:2012
Symbol SUS316L
---
---
d ≤ 180
---
175
---
480
---
40
ST
Other --------------------------187 max. HBW; 90 max. HRBW; 200 max. HV --------------------230 max. HBW; L: 100 J @ RT 230 max. HBW; T: 60 J @ RT 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
EN 10294-2:2012 ISO 4954:1993
Section Thickness/Diameter mm in. 2 12.70 --t ≤ 12.5 t ≤ 12.70 t > 12.5 t > 12.70 --t ≤ 160
t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 --t ≤ 0.5 t ≤ 0.5 t > 0.5 t > 0.5 -----
205 310 205 205 205 205 310 205 205 205 280
30 45 30 30 30 30 45 30 30 30 ---
515 620 515 515 515 515 620 515 515 515 580-800
75 90 75 75 75 75 90 75 75 75 ---
30 30 40 30 30 30 30 40 30 30 40 L
A and HF A and CF A and HF A and CF A A+HF A+CF A+HF A+CF SA SA
160 < t ≤ 250
---
280
---
580-800
---
30 T
SA
t ≤ 160
---
280
---
580-800
---
40 L
SA
160 < t ≤ 250
---
280
---
580-800
---
30 T
SA
2 0.5 t > 12.70 t > 0.5 ----t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 ----t ≤ 180 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 --520 --40
Heat Treatment A and HF A and CF A and HF A and CF A A+HF A+CF A+HF A+CF SA ST
GB 1220-92
Grade 00Cr19Ni13Mo3
---
---
t ≤ 180
---
177
---
480
---
40
ST
JIS G 4303:2012
Symbol SUS317L
---
---
d ≤ 180
---
175
---
480
---
40
ST
EN 10088-3:2014
X2CrNiMoN17-13-5
---
1.4439
t ≤ 160
---
280
---
580-800
---
35 L
SA
160 < t ≤ 250
---
280
---
580-800
---
30 T
SA
GB 1220-92
Grade 0Cr18Ni16Mo5
---
---
t ≤ 180
---
177
---
480
---
40
ST
JIS G 4303:2012
Symbol SUS317J1
---
---
d ≤ 180
---
175
---
480
---
40
ST
Other --------------------187 max. HB; 90 max. HRB 187 max. HB 187 max. HBW; 90 max. HRBW; 200 max. HV 215 max. HBW; L: 100 J @ RT 215 max. HBW; T: 60 J @ RT 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV 250 max. HBW; L: 100 J @ RT 250 max. HBW; T: 60 J @ RT 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV
Download From http://bbs.infoeach.com
Type 317
UNS Steel No No S31700 ---
Download From http://bbs.infoeach.com
Specification ASME SA-276
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
582
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification ASME SA-276
ASME SA-479/SA-479M
ASTM A479/A479M-14
Type 321 Type 321H Type 321
S32100 S32109 S32100
-------
S32100 S32109
-----
Type 321 Type 321H Note: This section continued on next page
Section Thickness/Diameter mm in. t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 --------t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 ---------
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30
Heat Treatment A and HF A and CF A and HF A and CF A A A+HF A+CF A+HF A+CF SA SA
Other -------------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASTM A276/A276M-15
Type 321
UNS Steel No No S32100 ---
Designation
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
583
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X6CrNiTi18-10
UNS No ---
Steel No 1.4541
Yield Strength, min. MPa ksi 350 --500 --------------------------400 --380 ------190 --190 --190 ---
Tensile Strength, min. Elongation MPa ksi % min 700-850 --20 800-1000 --12 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-950 --25 L 580-950 --25 L 800 max. --35 500-850 --30 L 500-850 --30 L 500-700 --40 L
Heat Treatment CW CW SA SA SA SA SA SA SA SA SA SA SA SA
63 < t ≤ 160 160 < t ≤ 250
-----
190 190
-----
500-700 500-700
-----
40 L 30 T
SA SA
d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05 d ≥ 0.05
-----------------------
-----------------------
-----------------------
500-700 600-800 700-900 800-1000 900-1100 1000-1250 1100-1350 1200-1450 1400-1700 1600-1900 1800-2100
-----------------------
-----------------------
-----------------------
Other ----------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW; L: 100 J @ RT L: 100 J @ RT 215 max. HBW; T: 60 J @ RT -----------------------
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
Section Thickness/Diameter mm in. --------0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 ---
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
584
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued) Steel No 1.4541
Grade 0Cr18Ni10Ti
---
---
Grade 1Cr18Ni9
---
---
t ≤ 180
---
205
---
520
---
40
ST
GB 1221-92 ISO 4954:1993
Grade 0Cr18Ni10Ti Type X 6 CrNiTi 18 10 E
-----
-----
JIS G 4303:2012
Symbol SUS321
---
---
t ≤ 180 2 ≤ d ≤ 50 2 ≤ d ≤ 50 d ≤ 180
---------
205 ----205
---------
520 680 max. 730 max. 520
---------
40 ----40
ST Q, CD see standard ST
Download From http://bbs.infoeach.com
GB 1220-92
Designation X6CrNiTi18-10
Section Thickness/Diameter mm in. 2 12.70 t > 0.5 t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 --------t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 t ≤ 12.5 t ≤ 0.5 t ≤ 12.70 t ≤ 0.5 t > 12.5 t > 0.5 t > 12.70 t > 0.5 --------t ≤ 160 ---
Yield Strength, min. Tensile Strength, min. Elongation MPa ksi MPa ksi % min 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 310 45 620 90 30 205 30 515 75 40 205 30 515 75 30 205 30 515 75 30 205 30 515 75 30 205 --510-740 --40 L
Heat Treatment A and HF A and CF A and HF A and CF A and HF A and CF A and HF A and CF A A A+HF A+CF A+HF A+CF A+HF A+CF A+HF A+CF SA SA SA
160 < t ≤ 250
---
205
---
510-740
---
30 T
SA
GB 1220-92
Grade 0Cr18Ni11Nb
---
---
t ≤ 180
---
205
---
520
---
40
ST
JIS G 4303:2012
Symbol SUS347
---
---
d ≤ 180
---
205
---
520
---
40
ST
ASME SA-276
---
S30815
---
---
---
310
45
600
87
40
ASME SA-479/SA-479M ASTM A276/A276M-15
-----
S30815 S30815
-----
-----
-----
310 310
45 45
600 600
87 87
40 40
ASTM A479/A479M-14 ISO 4955:2005
--X7CrNiSiNCe21-11
S30815 ---
-----
--0.5 ≤ t < 3 1.5 ≤ t ≤ 25 3 ≤ t ≤ 75 t ≤ 100 5 ≤ t ≤ 160
-------------
310 310 310 310 310 310
45 -----------
600 650-850 650-850 650-850 650-850 650-850
87 -----------
40 37 L, 37 T 40 40 L, 40 T 40 40
A and HF or A and CF A A+HF or A+CF SA SA SA SA SA SA
Other ----------------------------------------230 max. HBW; L: 100 J @ RT 230 max. HBW; T: 60 J @ RT 187 max. HB; 90 max. HRB 187 max. HBW; 90 max. HRBW; 200 max. HV ---
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ASME SA-479/SA-479M
Type 347
UNS Steel No No S34700 ---
Designation
------210 max. HB 210 max. HB 210 max. HB 210 max. HB 210 max. HB
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
587
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10088-3:2014
Designation X6CrNiCuS18-9-2
UNS No ---
X6CrNiCuS18-9-2 X53CrMnNiNbN21-9
-----
ISO 683-15:1992
Grade X 53CrMnNiNbN 21 9
---
GB 1221-92 JIS G 4311:2011
Grade 5Cr21Mn9Ni4N Symbol SUH35
-----
Section Thickness/Diameter mm in. 0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 --63 < t ≤ 160 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 ----t ≤ 160 --1.4870 --------------------t ≤ 25 ----t ≤ 25 ---
Yield Strength, min. Tensile Strength, min. Elongation Heat MPa ksi MPa ksi % min Treatment ----1100 max. --20 SA ----1050 max. --20 SA ----1000 max. --30 SA ----950 max. --30 SA ----900 max. --30 SA ----850 max. --35 SA 400 --600-950 --15 L SA 400 --600-950 --15 L SA ----800 max. --35 SA 185 --500-910 --20 L SA 185 --500-910 --20 L SA 185 --500-710 --35 L SA 185 --500-710 --35 L SA ----500-700 ----------600-800 ----------700-900 ----------800-1000 ----------900-1100 ----------1000-1250 ----------1100-1350 ----------1200-1450 ----------1400-1700 ----------1600-1900 ----------1800-2100 ------185 --500-710 --35 L SA ----1300 approx. ----CTC ----1300 max. ----Q ----------CTC ----1300 max. ----Q 560 --885 --8 ST 560 --880 --8 see standard
Other ----------------------215 max. HBW --------------------------385 HB approx. 385 max. HB --385 max. HB 302 min. HB 302 min. HBW
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com
ISO 16143-2:2004 EN 10090:1998
Steel No 1.4570
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
588
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Designation
UNS Steel No No S35315 --S35315 ----1.4854
ISO 4955:2005
X6NiCrSiNCe35-25
---
EN 10088-3:2014
X3CrNiCu18-9-4
---
Section Thickness/Diameter mm in. --------0.5 ≤ t ≤ 3 --t ≤ 25 --3 ≤ t ≤ 75 --t ≤ 160 ----1.5 ≤ t ≤ 25 --0.5 ≤ t ≤ 75 --t ≤ 100 --5 ≤ t ≤ 160 --1.4567 0.05 < d ≤ 0.10 --0.10 < d ≤ 0.20 --0.20 < d ≤ 0.50 --0.50 < d ≤ 1.00 --1.00 < d ≤ 3.00 --3.00 < d ≤ 5.00 --t ≤ 10 --10 < t ≤ 16 --5.00 < d ≤ 16.00 --16 < t ≤ 40 --40 < t ≤ 63 --t ≤ 160 --63 < t ≤ 160 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 --d ≥ 0.05 ---
Yield Strength, min. MPa ksi 270 39 270 39 300 --300 --300 --300 --300 --300 --300 --300 --------------------------400 --340 ------175 --175 --175 --175 -----------------------------------------------
Tensile Strength, min. Elongation MPa ksi % min 650 94 40 650 94 40 650-850 --40 L, 40 T 650-850 L --40 L 650-850 --40 L, 40 T 650-850 L --40 L ----40 ----40 L, 40 T ----40 ----40 1100 max. --20 1050 max. --20 1000 max. --30 950 max. --30 900 max. --30 850 max. --35 600-850 --25 L 600-850 --25 L 800 max. --35 450-800 --30 L 450-800 --30 L 450-650 --45 L 450-650 --40 L 500-700 ----600-800 ----700-900 ----800-1000 ----900-1100 ----1000-1250 ----1100-1350 ----1200-1450 ----1400-1700 ----1600-1900 ----1800-2100 -----
Heat Treatment A SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA SA -----------------------
Other ----210 max. HB 210 max. HB 210 max. HB 210 max. HB 210 max. HB 210 max. HB 210 max. HB 210 max. HB ------------------L: 100 J @ RT L: 100 J @ RT 215 max. HBW L: 100 J @ RT -----------------------
Download From http://bbs.infoeach.com
----X6NiCrSiNCe35-25
Download From http://bbs.infoeach.com
Specification ASME SA-479/SA-479M ASTM A479/A479M-14 EN 10095:1999
Note: This section continued on next page
Handbook of Comparative World Steel Standards
Chapter 8
Wrought Stainless Steels
589
8.2 Stainless Steels: Bar 8.2.3B Mechanical Properties of Austenitic Stainless Steels (Continued)
Specification EN 10263-5:2001
Designation X3CrNiCu18-9-4
UNS No ---
Steel No 1.4567
Yield Strength, min. MPa ksi ----------------------------------------350 --175 --177 --------------175 ---
Tensile Strength, min. Elongation Heat MPa ksi % min Treatment 600 max. L ----CD+SA 650 max. L ----CD+SA 590 max. L ----SA 740 max. L ----CD+SA 590 max. L ----CD+SA 640 max. L ----CD+SA 590 max. L ----SA 700 max. L ----CD+SA 590 max. L ----CD+SA 590 max. L ----SA 700-850 L --20 L CW 450-650 L --45 L SA 480 --40 ST 450-650 ----SA 590 max. ----Q, CD 620 max. ----see standard 480 --40 ST
EN 10269:2013
X3CrNiCu18-9-4
---
1.4567
GB 1220-92 ISO 16143-2:2004 ISO 4954:1993
Grade 0Cr18Ni9Cu3 X3CrNiCu18-9-4 Type X 3 CrNiCu 18 9 3 E
-------
-------
JIS G 4303:2012
Symbol SUSXM7
---
---
GB 1220-92
Grade 0Cr18Ni13Si4
---
---
t ≤ 180
---
205
---
520
---
40
ST
GB 1221-92 JIS G 4303:2012
Grade 0Cr18Ni13Si4 Symbol SUSXM15J1
-----
-----
t ≤ 180 d ≤ 180
-----
205 205
-----
520 520
-----
40 40
ST ST
GB 1221-92 JIS G 4311:2011
Grade 2Cr21Ni12N Symbol SUH37
-----
-----
t ≤ 25 t ≤ 25
-----
430 390
-----
820 780
-----
26 35
ST see standard
Other --------------------L: 80 J @ 20°C L : 100 J @ 20°C --------187 max. HBW; 90 max. HRBW; 200 max. HV 207 max. HB; 95 max. HRB 207 max. HB 207 max. HBW; 95 max. HRBW; 218 max. HV 269 max. HB 248 max. HBW
Download From http://bbs.infoeach.com
Download From http://bbs.infoeach.com